By R. A. Marriot

The steam-generating plant at the Garfield smelter of The American Smelting and Refining Co. consists of two divisions in which the boilers are classed as direct-fired or waste-heat. The direct-fired boiler plant consists of eight 330-boiler hp. type K-19 and S-I 7 Stirling boilers located in the boiler room adjacent to the power house, and two 330-boiler hp. Stirling type K-19 boilers in the reverberatory building, which formerly were connected to a reverberatory furnace but now are arranged for direct firing. All direct-fired boilers are now fired with natural gas. The waste-heat boiler plant consists of all units connected to reverberatory furnaces, and receiving heat from the exit gases therefrom. In this classification there are two 490-boiler hp. Erie City vertical water-tube boilers, and six 330-boiler hp. type K-19 Stirling water-tube waste-heat boilers. Each furnace has boilers arranged in battery setting. The boilers are directly in front of the furnace and connection is made through a short uptake and flue (Fig. 1). The Stirling boiler settings rest on concrete foundations at ground level, with the furnace uptake and flue at a low elevation. The Erie boilers are carried on steelwork some 15 ft. above ground level, and stand against the face of the uptake with no connecting flue. The constructional requirements of a larger furnace dictated this type of setting.

Jan 1, 1934

By Arthur Wade

The most important development in connection with the search for oil in Australia during 1940 was on the legislative side. Prior to 1939 legislative enactments in the various states with regard to prospecting for petroleum were such as to prohibit large-scale effort and to bar the major oil companies from operating. The preparation of the Wade Model Bill for the Commonwealth Government in 1939 and the acceptance of the Bill in principle by all States, has gone far to remove these obstacles. Amending Acts, largely based on the Alodel Bill, have now been passed by all States with the exception of New South Wales and Tasmania. In New South Wales an Amending Bill is being drafted, while the Govern-ment of Tasmania is preparing to introduce an Amending Bill provided there is any demand for it. Noteworthy developments followed immediately on the passing of these Amending Acts. The Shell Company (1)1 and the Superior Oil Company of California (2) too$ up large areas in Queensland and com-menced work during 1940. Caltex acquired a big tract of country in the Kimberley district of Western Australia (3) and has made application for an area in the Territory of Papua. An Australian company, The Phoenix Oil Extraction Co., has obtained a permit to prospect over an extensive area bordering the south coast of Western Australia (4). Other developments are foreshadowed. The Shell Company is making an intensive examination of its area in Queensland (I). Geological, geophysical and aerial surveys are in progress. Caltex has three geological parties in the held in Western Australia while Superior Oil Company of California has done some geological work in the interior of Queensland (2). None of these concerns envisages a drilling campaign in the near future. Much exploratory work is necessary. Further work has been done by the companies that were already operating in 1939, though an important Australian company - Oil Search—has abandoned the work of prospecting in Australia. This company has subleased its holdings, at North West Cape in Western Australia (;), to Caltex on a royalty basis. The company also maintains its holdings in, and connection with, the Australasian Petroleum Company Proprietary Limited, which is a combination of Standard Oil (New Jersey), Anglo-Iranian and Oil Search. This company is operating in the territories of Papua and New Guinea. Drilling Victoria.—Although a good deal of drilling was done in the LaBes Entrance Tertiary Basin of Victoria (7), no appreciable production of oil was obtained. In order to test the extent and possibilities of the oil-bearing sand in this region, the Commonwealth and State Governments jointly put down six scout boreholes to depths of between 1200 and I500 it. The results were nega tive. A deeper exploratory horehole put down by the Governments at Seacornbe, or 26

Jan 1, 1941

By Arthur Wade

The most important development in connection with the search for oil in Australia during 1940 was on the legislative side. Prior to 1939 legislative enactments in the various states with regard to prospecting for petroleum were such as to prohibit large-scale effort and to bar the major oil companies from operating. The preparation of the Wade Model Bill for the Commonwealth Government in 1939 and the acceptance of the Bill in principle by all States, has gone far to remove these obstacles. Amending Acts, largely based on the Alodel Bill, have now been passed by all States with the exception of New South Wales and Tasmania. In New South Wales an Amending Bill is being drafted, while the Govern-ment of Tasmania is preparing to introduce an Amending Bill provided there is any demand for it. Noteworthy developments followed immediately on the passing of these Amending Acts. The Shell Company (1)1 and the Superior Oil Company of California (2) too$ up large areas in Queensland and com-menced work during 1940. Caltex acquired a big tract of country in the Kimberley district of Western Australia (3) and has made application for an area in the Territory of Papua. An Australian company, The Phoenix Oil Extraction Co., has obtained a permit to prospect over an extensive area bordering the south coast of Western Australia (4). Other developments are foreshadowed. The Shell Company is making an intensive examination of its area in Queensland (I). Geological, geophysical and aerial surveys are in progress. Caltex has three geological parties in the held in Western Australia while Superior Oil Company of California has done some geological work in the interior of Queensland (2). None of these concerns envisages a drilling campaign in the near future. Much exploratory work is necessary. Further work has been done by the companies that were already operating in 1939, though an important Australian company - Oil Search—has abandoned the work of prospecting in Australia. This company has subleased its holdings, at North West Cape in Western Australia (;), to Caltex on a royalty basis. The company also maintains its holdings in, and connection with, the Australasian Petroleum Company Proprietary Limited, which is a combination of Standard Oil (New Jersey), Anglo-Iranian and Oil Search. This company is operating in the territories of Papua and New Guinea. Drilling Victoria.—Although a good deal of drilling was done in the LaBes Entrance Tertiary Basin of Victoria (7), no appreciable production of oil was obtained. In order to test the extent and possibilities of the oil-bearing sand in this region, the Commonwealth and State Governments jointly put down six scout boreholes to depths of between 1200 and I500 it. The results were nega tive. A deeper exploratory horehole put down by the Governments at Seacornbe, or 26

Jan 1, 1941

By Donald L. Ball

The equilibrium of boron nitride, gaseous nitrogen, and solute boron was investigated in Fe, Fe-C, and Fe-Si rnelts by the Sieverts technique. The free ellergy of dissociation of boron nitride, involving -the implied standard states, was evaluated in the range 1400" to 1600°C as: ?Fo = 38,000 - 23.5T, cal ber mole The solute-solute interaction coefficients eBB, ecB , and eg were determined as 0.058, 0.22, and 0.078, respectively. BORON is an important ingredient in some types of steel and cast iron. It was employed at a particularly high level, 0.01 wt pet, in the as-cast malleable iron "CentraSteel".1 In this material, the boron concentration was critical in order to assure graphite, and avoid primary cementite, in the as-cast structure. One possible function of the boron in this alloy was the nucleation of graphite through the agency of boron nitride, which, conceivably, precipitated from the melt during cooling. A research program was instituted to assess the validity of this proposed mechanism. The first undertaking, reported here, was a determination of the thermodynamic possibility of boron nitride precipitation. Data available in the literature on the activity coefficient of solute boron in iron-base melts are inadequate for the present purpose. They will be reviewed briefly, however, so that comparison can be made, when

Jan 1, 1968

By Oswald J. Heinrich

(Read at the Philadelphia Meeting, February, 1878.) DURING the last twenty years much has been done to investigate and define the Mesozoic formation of the United States along the Atlantic States, as well as in the Territories. The investigations of Professors Hitchcock, Emmons, Hayden, H. D. Rogers, and those now in progress in connection with the geological surveys of Penn-

Jan 1, 1878

By W. E. D. Jr. Stokes

THE application of aviation to mining and petroleum operations, on the basis of economy and attainment, has become a demonstrated fact. According to Dominion Government records, 30. Canadian companies engaged in air transportation with northland mining camps, carried 13,000 tons of freight in 1935, and in 1936 carried 16,000 tons. In addition, many mining companies used planes to transport prospectors with canoes, outboard motors, gasoline drums and supplies to remote locations, and one company maintained a plane to take radium-bearing ore from its mine on Great Bear Lake nearly 1000 miles south to the rail-way at Waterways, Alberta. Heavy pieces of mining machinery weighing 2 tons are being carried by Ford trimotor planes over the Andes, at an altitude of not less than 15,000 feet. At Bulolo, New Guinea, 17,500 tons of disassembled gold-dredging equipment has been flown over inaccessible terrain, while supplies and building materials for a, community of 1000 whites have been transported by airplane. A 3 1/2-ton shaft was carried on one notable trip, while at another time an automobile, 2 tons of rice and a large safe went over the mountains in one plane. Fig. 1 shows an electric generator that was carried by plane to Bulolo.

Jan 1, 1937

By William E. Ford, Edward Salisbury Dana

Normal phosphoric acid is H3P04, and consequently normal phosphates have the formulas R3PO4, R3(P04)2 and RPO4, and similarly for the arsenates, etc. Only a comparatively small number of species conform to this simple formula. Most species contain more than one metallic element, and in the prominent Apatite Group the radical (CaF), (CaCI) or (PbCI) enters; in in the Wagnerite Group we have similarly (RF) or (ROH).

Jan 1, 1922

By L. N. Brown

The use of sheet and strip metal has increascd rapidly during the last few years and manufacturers have been called upon for an ever-increasing tonnage, better drawing quality, and better surface. The automobile industry is probably the most insistent in striving for a better product and a desire to reduce costs. Confronted by these demands, the mills have directed their efforts toward the delivery of material. Their personnel has been occupied largely with the problems incident to production, as any increase forced the use of new sources of raw material with their problems. These problems, combined with those met in the daily routine, have demanded immediate attention, with the result that the standardizing of heat treatments, quality, or temper, etc., have been neglected. Considerable work in standardizing has been done by many companies, but no acceptable method has been developed. The following method, therefore, is given with the hope that some method that can be accepted by the manufacturers and users may be developed. The problem of selecting a material with such properties that the losses in processing are a minimum is interesting and difficult. A description of the properties required is likewise difficult, largely because of loose terms. Another handicap is the number of methods of testing which have not been standardized and concerning which little information is available. In the selection of drawing or forming stock, it is advisable to eliminate as many variables as possible; consequently the method of testing the material is of the utmost importance. The method should be rapid and comparatively easy of application, as it is more important that a large percentage of the stock be tested with reasonable accuracy than that

Jan 1, 1923

By L. N. Brown

The use of sheet and strip metal has increascd rapidly during the last few years and manufacturers have been called upon for an ever-increasing tonnage, better drawing quality, and better surface. The automobile industry is probably the most insistent in striving for a better product and a desire to reduce costs. Confronted by these demands, the mills have directed their efforts toward the delivery of material. Their personnel has been occupied largely with the problems incident to production, as any increase forced the use of new sources of raw material with their problems. These problems, combined with those met in the daily routine, have demanded immediate attention, with the result that the standardizing of heat treatments, quality, or temper, etc., have been neglected. Considerable work in standardizing has been done by many companies, but no acceptable method has been developed. The following method, therefore, is given with the hope that some method that can be accepted by the manufacturers and users may be developed. The problem of selecting a material with such properties that the losses in processing are a minimum is interesting and difficult. A description of the properties required is likewise difficult, largely because of loose terms. Another handicap is the number of methods of testing which have not been standardized and concerning which little information is available. In the selection of drawing or forming stock, it is advisable to eliminate as many variables as possible; consequently the method of testing the material is of the utmost importance. The method should be rapid and comparatively easy of application, as it is more important that a large percentage of the stock be tested with reasonable accuracy than that

Jan 1, 1923

By Herbert Clark Hoover, Lou Henry Hoover

PREVIOUSLY I have given much information concerning the miners, also I have discussed the choice of localities for mining, for washing sands, and for evaporating waters; further, I described the method of searching for veins. With such matters I was occupied in the second book; now I come to the third book, which is about veins and stringers, and the seams in the rocks1. The term "vein" is sometimes used to indicate canales in the earth, but very often elsewhere by this name I have described that which may be put in vessels2; I now attach a second significance to these words, for by them I mean to designate any mineral substances which the earth keeps hidden within her own deep receptacles.

Jan 1, 1950

By G. W. Healy, W. D. Forgeng, N. R. Griffing

The liquidus surface of the C-Cr-Fe system to 1900°C has been mapped from carbon solubility and freezing point measurements, metallographic observations, and published data. In the graphite field, the surface drops precipitously to meet a slope descending from the Cr3C2-C join through the mixed carbide fields to a meandering eutectic valley; this flows from the Cr-C to the Fe-C edge. On the low-cavbon side of the valley, the surface rises to the chromium corner. 1 HE purpose of this inquiry was to gain a more complete knowledge of the C-Cr-Fe liquidus surface. This required an extensive study of carbon and chromium-rich alloys which, in the past, have received the least attention. Sanbongi el al.1 measured the solubility of carbon in liquid alloys containing up to 25 wt pct Cr at temperatures of 1460" and 1545°C and found that it increased with chromium content and temperature. Lucas and wentrup2 also made solubility experiments in graphite crucibles, but at higher chromium contents in the range of 38 to 80 pct and at temperatures of 1550" to 1700°C; however, their experiments were relatively few, and the effect of temperature was not consistent. The present investigation included compsitions ranging from 0 to 94 pct Cr and 1.4 to 11.7 pct C at temperatures up to 1800°C. Saturation experiments in graphite crucibles, thermal analyses during freezing, and metallographic and X-ray diffraction studies were employed to obtain desired information which, together with published data from other investigations about the binary edges and the ternary system at lower carbon levels, made possible the construction of a comprehensive C-Cr-Fe liquidus surface. C-CR-FE LIQUIDUS SURFACE The derived ternary liquidus surface is shown in Fig. 1 where the solid curves are liquidus isotherms. The dashed curves and the binary edges are the liquidus field boundaries of the primary crystals, the arrows along these boundaries indicating their direction with decreasing temperature. Each intersection of three internal boundaries is the composition of liquid involved in four-phase isothermal equilibrium with the three primary crystals whose liquidus fields touch there. It may be observed that a total of six four-phase equilibria occur at melt temperatures. The general topography of the liquidus surface consists of a eutectic valley sloping down from the Cr-C edge at 3.2 pct C to the Fe-C edge at 4.25 pct C. The liquidus surface rises in two directions from the valley, one hillside terminating at the Cr-Fe edge while the opposing hillside rises toward the carbon corner out beyond the top edge of Fig. 1. Both hillsides are interrupted by intersections of surfaces or joints representing the liquid colmpositions of various three-phase equilibria. Seven primary crystals occur, namely a(bcc), ?(fcc), graphite, (Fe, Cr)3C capable of dissolving as much as 15 pct Cr, and three different chromium carbides in which iron is partially soluble by substitution for chromium. The composition ranges of the primary l~hases at melt temperatures are shown

Jan 1, 1962

By Cyril Wells, Robert F. Mehl

The purpose of this investigation was to prepare high-purity iron-carbon alloys, to determine as precisely as possible the A3(GOS), the Acm(SE), and the A1(PSK) transformation temperatures in the meta-stable iron-iron carbide system (up to 1.4 per cent C), and to study the influence of carefully controlled and constant rates of heating and cooling (1/8 to 2o C. per minute) upon the transformation temperature and upon the resulting microstructure. Apart from the general metallurgical importance attending the completion of such a task, it will be noted that highly precise transformation temperatures are of interest and importance in the thermodynamic study of this system1. Several determinations of the iron-iron carbide diagram have been made2. These suffer generally from the low purity of the alloys used, and from the application of methods of investigation of low sensitivity. Attempts to compare and weight the many data available in an effort to construct as accurate a diagram as possible have, in the main, been unsuccessful. In general, the wide differences in the results of different workers, the lack of complete analytical data, the omission of important details relating to the heat-treatment of the alloys, and the meager description of the methods of investigation applied, render such a process of averaging nearly meaningless. It may be seen from the summaries by Epstein2 and Körber and Oelsenl that variations as great as 30' C. exist in the reported data on the A3 temperatures in iron-carbon alloys. Fortunately, the Aa temperature in pure iron is now known to be 910" C. ± 1° C.3 The best recent work on iron-carbon alloys is that of Esser4 on hypoeutectoid steels and that of Sato5 on both hypoeutectoid and hyper-eutectoid steels. Esser made a dilatometric and magnetic study of iron and iron-carbon alloys containing 0.06 to 0.86 per cent C, for which a high purity is claimed. Presumably the electrolytic iron was reasonably pure, but the alloys contained considerable impurities, on the average totaling 0.35 per

Jan 1, 1937

By Leonard Grimshaw

DIFFUSION Of carbon from gases into iron has been the object of much research, because of its long recognized importance in carburizing processes, but the direct diffusion of carbon from steel into iron has received relatively little attention. Because of the increasing use of clad metals in industry, direct diffusion from steel into iron is becoming of practical importance. Therefore, the object of this investigation was to study the diffusion of carbon from several different kinds of steel directly into relatively pure iron, realizing that elements in the steels other than carbon might influence the rate of carbon diffusion. The previous work on diffusion of carbon into iron has been consider-able, and includes many reports in foreign languages. This work has recently been well reviewed by Mehl1 and Krynitsky,2 and the reader is referred to their excellent bibliographies.

Jan 1, 1937

By Walter V. Knopp, Laurence Delisle

INTRODUCTION THE aim of this work was the preparation of nickel-steels from elemental metal powders by powder metallurgy techniques. It was known that plain carbon steels could be made from a mixture of iron powder and graphite and that the effect of carbon on iron in powder form was of the same nature as that produced in fusion metallurgy. The problem in making nickel steels from elemental powders consisted therefore in finding out whether sufficient diffusion of the nickel and other incidental metals normally present in such steels could be induced in the solid state to modify the properties of plain carbon steels made from powders and produce the beneficial effect of alloying. The composition selected originally was that of an S.A.E. 2330 steel. Metal powders, in the proportion corresponding to that composition, were mixed with graphite, pressed, and heated at different temperatures for different periods of time, to produce bonding of the metal particles and mutual diffusion of the various elements without melting. Temperatures up to 1325°C and sintering periods as long as 6 hr were first investigated because it was expected that such conditions would produce maximum diffusion with an accompanying improvement in the properties of the alloy. It was found that, although diffusion proceeded to a large extent under the conditions investigated, it would not be complete unless sintering were carried out at a high temperature for much longer than 6 hr. Relatively high temperatures and long sintering times are objectionable from a practical point of view, particularly when a low cost material is to be produced, because they necessitate the use of special, costly equipment. Work could be done to improve the diffusion of iron and nickel by changing conditions other than the sintering temperature and time, i.e., finer primary or alloy powders could be used. However, a marked change in the properties of the steel had been observed even with only partial diffusion. It was thought, therefore, that instead of trying to improve the diffusion, advantage might be taken of its incompleteness to produce a special structure consisting, in the unquenched condition, of a hard constituent, rich in nickel, dispersed in a tough pearlitic matrix. Steels with such a structure, not readily obtainable by fusion, should have desirable mechanical properties. Besides, it should be possible to prepare them from elemental powders under economical conditions. This latter alternative was therefore adopted for the second phase of this work. This report is divided into four parts: 1. General Procedure. 2. Effect of Sintering Temperature. 3. Effect of Varying the Nickel Content. 4. Effect of Alloying Elements. GENERAL PROCEDURE The general technique of cold pressing as used in powder metallurgy was applied.

Jan 1, 1948

By Ivan E. Goodner, Charles H. Fulton

The subject of the constitution of copper-iron mattes has received considerable attention in recent years by Keller,' Belles,2 Hofman,3 and Gibb and Philp.4 Still more recently Friedrich, Röntgen, Wiedmann, Heyn and Bauer, and Leroux have published, in some instances, elaborate researches on the various systems of the sulphides, and the snlphides and their respective metals, which enter into the constitution of mattes, and have added very greatly to the knowledge of the subject. The work of Friedrich has been especially fruitful. But to' date no effort has been made to correlate the data obtained in the latter researches and apply them to the study of the product called " matte," which is made in such large quantities by copper- and lead-smelters. In this paper we propose to determine, by metallographic and chemical means, the constitution of copper-iron and copper-lead-iron mattes in the light of the recent data above mentioned. We do not discuss copper-nickel mattes or speisses (artificial arsenides). The paper is divided into three sections: I. A review and discussion of the various binary systems of the metallic sulphides, and the binary systems of various metals and their respective sulphides entering into the constitution of mattes; also a discussion of the physical properties of these sulphides. II. A description of the results obtained from the chemical and microscopic examinations of the samples of copper-iron and copper-lead-iron matte obtained from various plants.

Jan 1, 1909

By Albert A. Smith

The creep properties of metals have assumed increasing importance in recent years and many investigations have been made on various phases of the problem. In the past year the annual lectures of the Institute of Metals Division1 and the Iron and Steel Division2 were concerned with this subject, and are excellent reviews. For many years the creep properties of lead and lead alloys have been investigated at the Central Research Laboratories of the American Smelting and Refining Co., and it is hoped that the present paper will contribute knowledge of some of the factors that influence creep. Lead, being a metal that recrys-tallizes readily at room temperature, is an excellent material upon which to investigate creep phenomena because of the simplicity of the apparatus needed, and it might be expected that results would apply to some extent to elevated-temperature tests of other metals. Material The creep tests of this investigation were all made on high-purity lead (99.9998+ Pb) in which the only impurity that could be detected by spectrographic and chemical means was approximately 0.0001 per cent Fe. Flat strips, 0.750 in. wide by 0. 100 in. thick, were prepared by extruding 2-in. dia. cast billets at a temperature of 250°C. This gave a material of 2 to 3 mm. average grain size with a tensile strength of j.400 lb. per sq. in. when tested at a straining rate of 5 per cent per minute. With this extremely soft material, great care was necessary in handling the specimens, to avoid distortion and subsequent recrystallization. The creep tests at 30°C. were conducted in a constant-temperature room, specially built for the purpose in the basement of an office building in which there was no moving machinery, and no vibration was detectable under the most severe conditions of shock in the adjacent surroundings. The room was well insulated and heated electrically, control being by means of a de Khotinsky regulator operating a relay. Maximum temperature variation over a period of several years has been ± 1/2°C. Specimens of the extruded strip, 16 in. long, were used for test purposes with no reduced gauge section, thus eliminating any distortion due to machining. The method of clamping and supporting the specimens is shown diagrammatically in Fig. 1. The gauge marker for the measurement of extension consisted of an aluminum strip, 0.050 in. thick by 0.75 in. wide, one end of which was ground and sanded to a precise knife-edge and fastened to the specimen by suitable pins. After the strip was fastened in place a fine scratch was inscribed just below the knife-edge by means of a sharp teasing needle. Just below this gauge scratch a short vertical mark was made so that the same point could be located and read each time. Several hundred specimens have been prepared by this method, and it was found that with experi-

Jan 1, 1941

By Albert A. Smith

The creep properties of metals have assumed increasing importance in recent years and many investigations have been made on various phases of the problem. In the past year the annual lectures of the Institute of Metals Division1 and the Iron and Steel Division2 were concerned with this subject, and are excellent reviews. For many years the creep properties of lead and lead alloys have been investigated at the Central Research Laboratories of the American Smelting and Refining Co., and it is hoped that the present paper will contribute knowledge of some of the factors that influence creep. Lead, being a metal that recrys-tallizes readily at room temperature, is an excellent material upon which to investigate creep phenomena because of the simplicity of the apparatus needed, and it might be expected that results would apply to some extent to elevated-temperature tests of other metals. Material The creep tests of this investigation were all made on high-purity lead (99.9998+ Pb) in which the only impurity that could be detected by spectrographic and chemical means was approximately 0.0001 per cent Fe. Flat strips, 0.750 in. wide by 0. 100 in. thick, were prepared by extruding 2-in. dia. cast billets at a temperature of 250°C. This gave a material of 2 to 3 mm. average grain size with a tensile strength of j.400 lb. per sq. in. when tested at a straining rate of 5 per cent per minute. With this extremely soft material, great care was necessary in handling the specimens, to avoid distortion and subsequent recrystallization. The creep tests at 30°C. were conducted in a constant-temperature room, specially built for the purpose in the basement of an office building in which there was no moving machinery, and no vibration was detectable under the most severe conditions of shock in the adjacent surroundings. The room was well insulated and heated electrically, control being by means of a de Khotinsky regulator operating a relay. Maximum temperature variation over a period of several years has been ± 1/2°C. Specimens of the extruded strip, 16 in. long, were used for test purposes with no reduced gauge section, thus eliminating any distortion due to machining. The method of clamping and supporting the specimens is shown diagrammatically in Fig. 1. The gauge marker for the measurement of extension consisted of an aluminum strip, 0.050 in. thick by 0.75 in. wide, one end of which was ground and sanded to a precise knife-edge and fastened to the specimen by suitable pins. After the strip was fastened in place a fine scratch was inscribed just below the knife-edge by means of a sharp teasing needle. Just below this gauge scratch a short vertical mark was made so that the same point could be located and read each time. Several hundred specimens have been prepared by this method, and it was found that with experi-

Jan 1, 1941

By Robert F. Mehl, Gerhard Derge

The gamma-alpha transformation in iron and iron-rich alloys is of such practical and theoretical importance that many papers have been published upon the subject relating to critical temperatures, transformation rates and accompanying property changes. Although crystallo-graphic studies are of less immediate practical usefulness, the opportunities which these offer to furnish data on the basic atomic movements which characterize the transformation are not to be neglected1. The early work on the crystallography of this transformation has been reviewed in the fourth paper of this series2; since then several important papers have appeared. Our present knowledge may be briefly summarized as follows. Kurdjumow and Sachs, working with a 1.4 per cent carbon steel3, established the orientation relationships subsisting between the face-centered gamma and the metastable tetragonal lattices in freshly quenched martensite, and between the face-centered gamma and the body-centered alpha lattices in tempered martensite. The orientation relationship observed in the latter case may be stated in terms of planes and directions observed to lie parallel in the two lattices: {111} ?//{110}a [110] ?// [111]a (This notation is used throughout as the most descriptive means of expressing the fact that any (111) plane of the gamma phase may be parallel to any (110) plane of the alpha phase, and that a [110] direction in a particular (111)? plane is parallel to a [Ill] direction in the corresponding (110)a plane.) From these relationships the atomic movements that transform the gamma lattice into the alpha may be inferred. In the present experiment these may be considered as consisting primarily in a shear of the atoms parallel to the {111} planes in [110]? Directions

Jan 1, 1937

By W. P. Saunders, W. R. Hibbard, G. H. Eichelman

Interest in the various products of the austenite eutectoid transformation in iron-carbon alloys, particularly as produced by the isothermal sub-critical techniques introduced by Davenport and Bain,' has resulted in the application of similar heat treatments to other eutectoid transformations. Studies o f the beta copper-aluminum alloy eutectoid transformation revealed microstructures very similar to those found in iron-carbon alloys. Investigations5t6 of the kappa phase in the copper-silicon alloy system have established the eutectoid type transformation of this phase into terminal alpha and intermediate gamma phases. This transformation has been reported5 as forming a eutectoid type structure in a very sluggish manner by a long time isothermal treatment. The purpose of the present investigation is to study the products of the kappa eutectoid transformation as affected by transformation temperatures by means of microscopic and hardness methods. Preparation of Alloys The copper-silicon alloy equilibrium diagram is shown in Fig 1. The kappa field converges to a minimum silicon solubility at the eutectoid composition and all other completely kappa alloys are hypereutec-toid. Thus, kappa decomposition involves first the proeutectoid precipitation of gamma, followed by the eutectoid transformation of a lower silicon content kappa (5.2 pct) Smith6 has indicated that alloys containing between 5.4 and 5.7 pct silicon could be hot rolled, but that the latter composition was desirable in order to permit a wider kappa temperature range. The alloy was prepared by adding Baker's commercially pure silicon to an ingot of copper-silicon alloy containing 2.34 pct silicon remaining from the investigation of Brick, Martin and Angier.' Following the casting techniques of Krynitsky, Saunders and Stern,s the ingot was melted under a heavy layer of dried charcoal in a clay-graphite crucible in a gas-fired pot furnace. Small lumps of silicon were held under thc melt surface with a graphite rod. After the silicon had dissolved, the alloy was chill-cast and then remelted without a cover, stirred thoroughly, skimmed and poured into a preheated cast iron mold. The cast microstructure is shown in Fig 2. The casting, 10 X 4 X K in., was annealed at 750°C for 21 hr and furnace cooled, About }{& in. was milled from all surfaces. The plate was cut in half longitudinally and the bottom half analyzed by A.S.T.M. and The composition by weight was as follows: copper 94.24 pct, silicon 5.56 pct, iron 0.11 pct.

Jan 1, 1949

By R. W. Kraft

A back- reflection precession-type X-yay camera for determining the crystallographic orientation of the crystallites of both phases in small areas of thick specimens of polyphase alloys is described ad the geometry, advantages, and limitations of the apparatus are discussed. Metallographic obseg-vations of interfacial angles (or habit planes or growth direction are made on the same specimen so that the crystallographic and metallographzc orientation data call be directly correlated. An example of the application of tile technique to a unidi-~~ectionally solidified CuA12-A1 eutectic specimen is presented. The interfacial planes ad growth directions of each phase were established, and the orientation relationship between the phases was observed and found to be approximately intermediate between two previously reported relationships. The crystallographic interfacial relationship between two solid phases is an important parameter in a variety of metallurgical phenomena because of the energy associated with the interface and because this energy is at least partly associated with the way in which the two space lattices are in contact along the interface. In order to describe the interfacial planes in the crystallites of both phases it is necessary to determine the crystallographic orientation of each phase in a specimen relative to each other, and to directly correlate these data with met-allographic measurements from which the interfacial planes can be determined on the same specimen. The back-reflection Laue technique is the easiest way to determine the orientation of thick single crystals or large grains and the method can be combined with metallographic techniques to provide the necessary data, provided the reflections from each phase can be distinguished from one another. However, if the crystallites are small or of varying orientation or if one or both phases has a unit cell with less than the maximum symmetry, many overlapping and complex Laue patterns are recorded simultaneously and it becomes impractical if not impossible to interpret the photographs. All of these complexities were present in a unidirectionally so- lidified A1-CuA12 eutectic alloy1 for which a crystallographic analysis was desired. Consequently the method described here was developed since no known X-ray or electron diffraction technique had all of the following attributes which were required. 1) Method should yield data from which the crys-tallographic orientation of every crystallite or diffracting unit in the irradiated area can be determined. 2) Method should be adaptable to the study of small areas. Depending upon the degree of preferred orientation in the specimens, it should be possible to obtain reliable data in a reasonable length of time on irradiated areas as small as 1.0 or even 0.1 mm in diam. 3) Method should permit direct correlation of crystallographic data with microscopic orientation data pertaining to crystallite axes, habit, morphology, and growth directions as determined by optical microscopy. 4) method should be such that selected areas of large specimens can be easily studied. Trepanning of a small specimen (such as an electron microscope specimen) from larger specimens was undesirable since it would greatly increase the problem of correlating the crystallographic and microscopic directional data. Requirements 3 and 4 dictated that an X-ray back-reflection pinhole technique should be used on large samples, such as metallographic specimens which had previously been examined and analyzed for their microscopic characteristics. Similarly, requirement 2 could be satisfied by choosing a collimator of appropriately small diameter. Exposure times would not be excessive provided the detector were close enough to the specimen. Because of space limitations film was chosen in preference to a Geiger counter. Requirement 1 was fulfilled by using monochromatic radiation and providing enough additional degrees of freedom in specimen rotation to compensate for Bragg law restrictions on diffracted beams. DESCRIPTION OF APPARATUS The apparatus shown in Fig. 1 consists of a pin-hole collimator, (a), projecting through a rotatable circular film in a holder, (b), which records X-ray reflections in the back-reflection region. The specimen, (c), is mounted on the end of a shaft, (d), which is provided with an adjustment, (e), so that the specimen surface can be placed accurately on

Jan 1, 1962