Selective oxidation (preferential oxidation of a single alloy component) can be an important oxidation mode in the case of alloys such as Si-Fe, Al-Fe, and so on, when heat-treating in atmospheres of low oxygen potential. It was the purpose of this work to identify the oxide films formed on iron containing 31/4 pct Si at low oxygen potentials, and to make some observations on the H2O/H2 ratios required to form them. EXPERIMENTAL METHOD HYDROGEN of varying water content offers a very convenient method of establishing a wide range of oxidizing power, or oxygen potential. The method chosen to provide a desired H2O/H2 ratio was to nearly saturate hydrogen at room temperature by bubbling the gas through water at room temperature, and then to wring out the excess water by passing the wet gas through a long glass spiral immersed in a refrigerated liquid at a desired dew point. After oxidation, the samples were examined by electron diffraction in order to identify any film which might be present. PREPARATION AND TREATMENT OF SAMPLES The samples were prepared from a Si-Fe alloy made in the laboratory using electrolytic iron and 96 pct ferro-silico11, vacuum-induction melted, hot-rolled then cold-rolled to 0.015-in. thickness. After the cold-rolling the samples were annealed at 1000°C. Transmission Laue X-ray patterns showed very little evidence of preferred orientation, but it is likely that a weak texture could have escaped notice. The chemical analysis was as follows: 3.34 Si, 0.01 Al, 0.001 0, 0.006 C, 0.002 N. Before each sample was oxidized, it was polished through 4/0 emery paper, cleaned and dried using benzene, carbon tetrachloride, acetone, absolute alcohol, and ether. The method of oxidizing the samples was as follows: Samples about 1/2 by 1 by 0.015 in. were held in the upper, cool part of a vertical vacuum furnace until the desired temperature was established in the furnace, Fig. 1. The sample was then lowered into the uniform hot zone where it was heated quickly to the desired temperature, and subjected to hydrogen of controlled moisture content (dew point) as mentioned previously. Temperatures from 400" to 1000°C were used, and dew points from room temperature to —78°C were explored. In general, the runs lasted about 6 hr, but a few runs were of different duration, as will be indicated later. After the predetermined period of time had elapsed, the specimens were withdrawn by the hollow stainless steel-quartz holder to a cool zone at the top of the furnace. EXPERIMENTAL RESULTS The results are summarized in Table I. Most of the electron-diffraction patterns were obtained by glancing-angle reflection, but in a few cases it was possible to strip the oxide films from the surface by a total immersion in a 3 pct bromine-methanol solution. Some of the thinner stripped films yielded quite satisfactory transmission patterns. However, both diffraction techniques yielded the same results; the patterns while most frequently showing a (low) tridymite, also showed a (low) cristobalite in some cases. A few patterns showed evidence of both phases. Because of the known nonequilibrium behavior of silica, it is not surprising that both forms of silica could coexist on one sample. It was noted that at fairly low dew points such as —40°C, there was a tendency for diffuse diffraction rings, suggesting a very small crystallite size. Also some subsequent experiments to be reported later show that thin silica films can be amorphous.

Jan 1, 1959

By Eugene F. Broome, Hugh A. Walls

Self-diffusion coefficients were measured using the modified shear cell technique over a temperature range from 31" to 401°C. These data agree within experimental error with those of Petit and Nachtrieb, which were determined from 30°to 99°C. LIQUID self-diffusion behavior in gallium has been studied previously by Petit and Nachtrieb&apos; using their shear cell technique.&apos; Data were obtained in that investigation over temperatures ranging from 30.6 to 98.7"C, and these comprise the only published data for liquid gallium. In the work reported here, diffusion data were obtained from 30.8 to 400-9.Cusing a shear cell technique different from that of Petit and Nachtrieb. This modified shear cell method and the mathematical analysis for diffusion in a finite capillary geometry have been previously described.3 PROCEDURES AND ANALYSIS The segments of the modified shear cell were fabricated from types 304 and 316 stainless steel. No corrosion problems with gallium were encountered until attempts were made to obtain data at 500°C. The diffusion capillary diameter was 1.59 mm and capillary lengths for the four sets of cell segments used are given in Table I. Gallium with a purity of 99.999 wt pct was obtained from Var-Lac-Oid Chemical Co. The gallium-72 isotope used to measure the self-diffusion coefficients was produced from this inert gallium by irradiation in The University of Texas Reactor Facility, and was checked for radiochemical purity. Following a period of isothermal diffusion controlled to within 0.0l°C, the contents of each capillary section were emptied into a counting planchet, weighed to assure that gallium had not been lost during handling, and the radioactivity determined by windowless gas-flow proportional counting. Great care was taken to obtain a reproducible counting geometry for the samples. Diffusion coefficients were obtained from the solu-tion3 to the diffusion equation for the modified shear cell problem, viz.: in which B2= C2(t)Li + L2)- CSL1-COL2 P* (C0-Cs)(L1+ L2) and L, and L2 are the capillary segment lengths. The step-function initial concentration distribution was expressed as C(x,O) = C, for -L1 = x < 0 and C(x,O) = Co for 0 < x 5 L?. Also, C2(0 = ^- fcix,t)dx Computation of the diffusion coefficients was done numerically as described in our earlier paper.3 Because of the short half-life of gallium-72 (14.1 hr) and the relatively long counting times taken to give a precise value of the diffusion coefficient, it was necessary to account for the radioactive decay both during the actual count and between counts for different samples (before and after diffusion). Thus, the average count rate Cz(t) for a second sample counted from times t3 to t4 can be made consistent with the average rate Co determined for a first sample counted from times t1 to t2 by the relationship: N(e-»i-e-M») , , C2(f) " &-«,)(*-«.-«-»«) [21 in which N is the total number of counts taken and is the decay constant. RESULTS AND DISCUSSION The self-diffusion coefficients determined in this investigation are listed in Table 11. Values of the parameters used to calculate the coefficients are given in the table, as are values of the random counting error &apos; for the concentration ratio pz and the corresponding expected random variation AD in the diffusion coefficient. The quantity is calculable from: &apos;Cg — C2(t)} , „ ,2 .-„¦, M co-csl(ACs)J W in which AC is the error in the individual count rate. The mean values of the diffusion coefficients within each temperature group are also given in Table 11. Such temperature groupings of data are reasonable because of the small variations between the temperature~.~

Jan 1, 1970

NEW YORK LOCAL SECTION Executive Committee Louis D. HUNTOON, Chairman ARTHUR S. DWIGHT, Vice-Chairman THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. E. MALTBY SHIPP, Treasurer GEORGE F. KUNZ W. DE L. BENEDICT Meeting, Jan. 16, .1914 A meeting of the New York Local Section of the American Institute of Mining Engineers was held at the Engineering Societies Building, 29 West 39th Street, New York City, Jan 16 1914 the Chairman, -L. D. Huntoon, presiding. Forty members weld present. In the absence of the Secretary, C. A. Bohn was appointed Secretary pro teen. N. H. Darton, Geologist of the U. S. Geological Survey, delivered an address on. The Occurrence of Gas in Coal, illustrated by lantern slides of charts, curves, and tables showing various features of gas occurrences. J. W. Richards, J. T. Beard, W. L. Saunders, L. D. Huntoon, and Mr. Darton participated in the discussion which followed the address. THOMAS T. READ; Secretary.

Jan 3, 1914

By Bailey, Lewis Newton

Bailey, Lewis Newton, Master Engineer, Senior Oracle, 4th Regiment, U. S. Engineers, Headquarters Company, died of pneumonia, at Camp Merritt, N. J., on April 30, 1918. Baird, Louis, Lieut., Royal Field Artillery, British Army, died on the battlefield in 1915. Ballamy, John H., Capt., 103d Engineers, killed in action near Fismes, Aug. 9, 1918. Burt, Andrew, died in active service, 1916. Cobeldick, William Morley, Royal Engineers, died from gas poisoning on October 7, 1915. Dougall, Ralph, 4th University Co., Princess Patricia Regiment, killed in action early in the war. Evans, Alfred Winter, Lieut.-Col., New Zealand Rifle Brigade, D. S. 0., D. C. M. killed in action on October 12, 1917. Gorman, Thomas C., Lieut., Canadian Engineers, killed in France, Mar. 18, 1918. Hague, William, 1st Lieut., Engineer Officers&apos; Reserve Corps, died in active service, Jan. 1,, 1918. Hall, William T., Capt., Royal Flying Corps, killed in action, May 19, 1917.

Jan 11, 1918

By D. H. Polonis, M. B. Kasen

AN unusual thermal etching phenomenon has been observed on the surface of a Cu-Si alloy. The observations were made during studies of vacancy condensation pit formation which were reported in previous papers.1,2 Figs. 1 and 2 are photomicrographs of the surface of a Cu-4.8 pct Si alloy after heating in vacuo (3 x X mm Hg) to 525°C and subsequently holding at that temperature for 16 hr in an impure (air-contaminated) argon atmosphere. Under these conditions preferential removal of silicon from the matrix by oxidation results in a surface which is entirely a phase overlying an a plus y structure. The light areas of Fig. 1 are regions in which very little thermal etching has occurred, while the majority of the surface has experienced severe etching. Similar regions in Fig. 2 are seen as plateaus above contours produced by net transfer of material from the specimen surface. Twin boundaries are also visible in Fig. 2. The difference in matrix mi-crostructure between Figs. l and 2 reflects the par- ticular orientation of low-index planes with respect to the surface of observation. Thermal etching contours of this type have been studied in detail by Hondros and Moore Both of the photomicrographs show that one or more dark spots are located approximately at the center of every protected area; where two spots are in close proximity, the protected areas have merged. The microstructures indicate that the anomalous resistance to thermal etching is related to the presence of these spots. Williams and Hayfield have shown that local regions of unusually high oxidation resistance can be caused by a surface monolayer of atoms with a work function higher than that of the base material. The result is an inhibition of the rate of electron removal from the base material and a decrease in the oxidation rate. The source of the protected layer may be either surface diffusion from contaminants on the specimen surface or pipe diffusion of solute atoms followed by migration across the surface. In the latter case the driving force is a difference in chemical potential resulting in a Gibbs adsorption phenomenon. In the present case, chemical polishing of the specimen surface precluded contaminants of a strictly surface nature. Consequently, diffusion of impurity atoms from within the lattice appears to be the most tenable explanation of the observed phenomena. The authors propose that the structures of Figs. 1 and 2 reflect the diffusion of impurity atoms along extended dislocations within the individual a phase grains prior to surface oxidation. The central spots within the protected regions are seen as sites of dislocation emergence which have become locally decorated with oxide in the manner discussed in Ref. 1. Williams and Hayfield observed protected regions adjacent to the grain boundaries of iron-contaminated copper which they attributed to the segregation of iron to the grain boundaries coupled with high dif-fusivity along the complex dislocation array at such boundaries. No evidence of such grain boundary protection was observed in the Cu-Si alloy; this

Jan 1, 1964

By Rodolfo V. de la Cruz

The accurate assessment of the in situ deformability of rock masses is very important in the de and construction of underground openings for mining and geotechnical engineering applications. This paper presents a method and device for determining the in situ deformability of rock masses by relating the borehole jack load to the diametral displacements at a number of orientations around the borehole wall. The method called mu1tiple measurement method include the steps in which: a) diametral displacement sensors are installed at different orientations around the borehole to measure the changes in length of various diameters of the borehole; b) a uniaxial load is applied on two opposed octants of the borehole wall, and; c) using elastic theory and assuming a reasonable value for the Poisson&apos;s Ratio of the rock mass, the in situ deformability of the surrounding rock materials is determined from the measured diametral displacements and applied unidirectional load. The multiple measurement method has a significant advantage over existing methods since it provides several independent data in a single test from which to calculate the in situ deformability of the rock mass. The multiple data provide a check and counter check on the reliability and accuracy of the various measurements. The multiple data would also provide a means of quantifying the degree of fissuring on the borehole wall. Information on the degree of fissuring is very important in numerical modeling of rock masses.

Jan 1, 1984

By Joseph J. Yancik

From previous work, it was learned that relative strengths of blasting agents can be reasonably predicted from heats of detonation modified by their (D/D*)2 ratio.(1) Bulk Strength = Q x d x (D/D*)2 x K (1) In this equation Q is the ideal heat released during detonation, d is density, D represents actual detonation velocity while D* is ideal velocity. An energy transfer coefficient, K, was used to account for differences among rock strata in response to explosive loading. This equation gave reasonable, field supported strength values for oxygen balanced blasting agents. For aluminized nitrocarbonitrates and slurries which have high Q&apos;s the rating system predicted better strengths than were shown in the field. This discrepancy was felt to be related primarily to problems in calculating Q and D*. Theoretical calculations cannot take into account varying energy contributions from particulated aluminums whose reactivities vary substantially with physical properties. One approach to circumventing this problem would be to use a characteristic Q that is dependent on mass reactivity of ingredients as components in explosive formulations. Since the underwater testing method is capable of measuring a functional, relative energy release, it was chosen for study.

Jan 1, 1971

By F. Clerf

Blast-furnace practice in France is determined more or less by the character of the ores used. Some French ores are siliceous and others are calcareous, therefore by proper burdening a self-fluxing mix can be used. This is not always done, as, for instance, at the Caen furnaces of the Société Métallurgique de Normandie, where the Soumont ore of Normandy is used, which is a carbonate. This ore is crushed and calcined at the mines, yielding a product that is porous and well sized for blast-furnace consumption. The lines of the Caen furnaces are given in Fig. 1. Originally these furnaces had 16 tuyeres; six are plucked and these tuyeres are set in the lower part of the bosh. Operating data on these furnaces are given in Table 1. Table 1.—Operating Data, Caen Furnaces Kg. Lb. Blast-furnace burden per ton of iron: Soumont ore....................................... 200&2100 (44004650) Limestone...................................... 900-1000 (2000-2200) Basic Bessemer slag (bearing phosphorus).............. 100 (220) Scale.............................................. 35 (77) Manganese ores.................................... Coke.............................................. 1100-1200 (2420-2640) Coke analysis: Ash, per cent............. 9.5 H2O, per cent............. 4.0-10.0 Flue dust (approx.), kg. per metric ton.... 200 (440 lb.) Blast volume, cu. m. per hr.............. 83,000 (49,000 cu. ft. per min.) Preesure, lb............................ 12 Blast heat, deg. C....................... 650 (1200" F.) Top temperature, deg. C................ 250 (445O F.) Top-gas analysis, per cent............... CO2 9.3 CO 30.3 O2 0.3 H2 3.0 Production per 24 hr. about 510 tons. MINETTE ORES The most important ore deposits in France are in the west of Lorraine. They are called the "minette" ores and are of two classes-—siliceous and

Jan 1, 1937

By Gerald Edmunds

THE liquidus line on the phase diagram for temperature versus composition of a binary alloy system, representing the boundary between the homogeneous melt and the heterogeneous melt plus solid, besides showing the minimum casting temperature, is useful in determining eutectic compositions and the presence of phase changes such as peritectic transformations and intermetallic compound formation. The liquidus often is determined by the cooling curves of thermal analysis, but supercooling frequently occurs, so that the temperature values are low. An alternative method, the one employed here, consists of determining the com- position of samples of the melts from heterogeneous alloys that are at equilibrium. With meticulous attention to fundamentals, this method is capable of yielding values limited in precision only by the temperature control and measurement and analyses. APPARATUS By starting, on the one hand, with a supersaturated solution and allowing the excess solute to precipitate, and on the other hand with an undersaturated solution and allowing more of the solute to be dissolved, both processes being carried out at the same temperature, equilibrium may be said to have been approached from both directions; that is, from above and from below. If the analyses show the solutions to contain the same fraction of solute when equilibrium has been approached from above and from below, one is assured that equilibrium has been reached in both determinations. In order to carry out such determinations, it is necessary to have equipment for obtaining and maintaining the proper temperatures; for holding the melt, measuring its temperature, and stirring, sampling and analyzing it. The present work required temperatures from 420° to 900°C. The equipment consisted of: A furnace, which was a vertical alundum tube, 1 ¾ in. diameter inside and 18 in. long, wound with Nichrome resistance wire, surrounded by a 3-in. i.d. alundum tube wound for 5 in. of length near each end, for compensation of end losses. This muffle was contained in an iron shell with Transite end plates, the intervening space being packed with Sil-O-Cel. The outside dimensions of the furnace were 12 in. in diameter by 18 ½ in. in height. Heating current was supplied by three independent variable-voltage transformers (Variac), one connected to each end compensator winding and manually controlled, and one connected to the main winding through a series resistance of 5 ohms. This resistance was short-circuited for

Jan 1, 1944

By G. Bruggeman, K. G. Kreider

Grain boundary dij]usion coefficienls were measured in tungsten between 1400° and 2200° C and can be expressed by the equation sq cm per sec This activation energy confirms some eavlier estimates made .from tungsten sintering experiments. Grain boundary diffusion was found to occur in sub-bozrndavies having -misorientations of less than 10 deg. The actiuation energy for this subboundavy diffusion is equal to that for dijjusion in incoherent grain boundaries with in the limits of error. This is shown to be consistent with the dislocation model of Low-angle boundaries wheve diffusion occlcvs along- the dislocation &apos;YPipes" comprising -tile boundary. RECENT investigations of the sintering of tungsten powders all report activation energies which are considerably less than the activation energy for tungsten volume diffusion. Kothari&apos; reports a value of 100 * 5 kcal per mole, Hayden and Brophy&apos; obtained 90 kcal per mole, and Vasilos and smith3 found 110.7 kcal per mole from their sintering studies. Since most determinations of the activation energy for volume diffu-sion4-&apos; fall between 120 and 160 kcal per mole (the true value seems most likely to be nearer 150 kcal per mole), the conclusion is drawn that the mass transport leading to densification during sintering is accomplished by grain boundary diffusion. This interpretation is consistent with various diffusion models of the sintering process. 10-12 Vasilos and Smith calculate diffusion coefficients from their data which fit the equation D * 1.36 x 10* exp(-llO,700/HD However, no direct measurements of tungsten grain boundary diffusion have been made. Furthermore, considerable disagreement exists between the directly measured values of tungsten volume diffusion.&apos;-&apos; In order to corroborate the inferred results of the sintering experiments concerning grain boundary diffusion and to provide accurate diffusion data essential to the analysis of the kinetics of creep, oxidation, precipitation, and so forth, the present work was undertaken to measure self-diffusion in single-crystal and polycrystalline tungsten between 1400" and 2200°C. It is within this temperature range that tungsten sintering is done, the re crystallization of tungsten occurs, and the widest application of tungsten as a high-temperature material will probably be made. EXPERIMENTAL PROCEDURE Radioactive WlE5 was produced by irradiating tungstic acid in a neutron flux of 1.2 x 1012 neutrons per sq cm per sec for 36 hr. A 2-week waiting period was allowed for the decay of w"~ also produced by the irradiation. (w"~ has a half-life of 24 hr.) The half-life of the remaining isotope was determined to be 75 days confirming the presence of w lE5 and the absence of any undesired radionuclide. Specimens 4 in. in diam and $ in. thick were cut from polycrystalline swaged tungsten rods (recrystal-lized) and from Linde single-crystal rods. Chemical analyses of these materials appear in Table I. Actually upon closer examination, the single-crystal specimens were found to consist of several subgrains separated primarily by tilt boundaries in which the misor-ientation ranged from 3 to 10 deg. Thus, it was possible to measure boundary diffusion coefficients in these low-angle subboundaries as well as in the incoherent boundaries of the polycrystalline specimens. The two faces of each specimen were ground flat and parallel within 0.0001 in. The radioactive tungstic acid was dissolved in concentrated ammonium hydroxide, placed on the ground flat of the specimen, and evaporated to dryness. The oxide was then reduced in hydrogen at 1000°C resulting in a layer of wlE5 approximately 1 p thick. The diffusion anneals were performed in vacuum in a tantalum resistance furnace. Time at temperature ranged from 10 hr at 1400°C to 2 hr at 2200°C. The penetration profile was determined by measuring the residual activity after successive removal of surface layers by grinding on metallographic polishing paper. Extreme care was exercised to insure that sections were always taken normal to the diffusion direction; this was verified repeatedly by checking that front and back surfaces of the specimen remained parallel. The activity was measured with an end-window Geiger-Mueller counter. The sides and edges of the specimen were well-shielded to eliminate possible effects due to surface diffusion. The weight of the

Jan 1, 1968

By R. L. Slobod, B. H. Caudle

In the past, the main emphasis in attacking the problem of the recovery of oil has been on the determination of fluid flow characteristics and residual oil saturation in the part of the reservoir which is contacted by a displacing phase. It is recognized that the determination of the fraction of the reservoir contacted in secondary recovery operations is also of great importance in predicting the ultimate recovery to be expected. A method is described in which radiographic techniques are used to determine these areal sweepout factors for any type of well spacing. Data showing the relationship of viscosity ratio and relative permeability to areal sweepout efficiency are presented for the five spot and the direct line drive well spacing patterns. Further applications of the method to studies of the displacement efficiency in the area contacted are mentioned. INTRODUCTION The problem of increasing oil recovery from typical reservoirs is generally attacked by trying to devise some means for reducing the residual oil in that part of the reservoir which is contacted. The fraction of the reservoir contacted in the displacement process. however, is also of major importance but has been given less consideration in the past. one reason for this neglect is the meager information available on the portion of the reservoir contacted and the magnitude of changes in this factor as operating conditions are varied. Until recently, the only means available for determining this quantity has involved the use of the electrolytic or poten-tiometric modelsl in which one is limited to working with a mobility ratio of unity. while means for calculating the volume of a reservoir contacted do exist. the calculations are very tedious for systems with mobility ratio different from unity. Recently several such determinations have been reported,213 and an experimental method involving a step-wise use of potentiometric models has been described.&apos; A new method which has been developed for studying the areal distribution of phases in a porous medium is discussed below. This tool can be&apos; used to determine the effect of operating variables such as viscosity, relative permeability, presence of gas, mobility ratio, rate and stratification on the fraction of the reservoir contacted by the displacing medium. This development based on the use of X-rays gives a pictorial representation of the location of the phases. Further, the amount of each phase at each point of interest can be determined quantitatively. X-RAY METHOD FOR AREAL STUDIES In this method the location of various phases distributed Over a test area are observed simultaneously by obtaining a photographic record of the transmission of X-rays through the test plate. This procedure is an adaptation of the radiographic techniques which have 10% been used in the medical and industrial fields. Just as the medical profession uses a chest plate to show spatial interrelationships, the location of an X-ray absorbing fluid and a nonabsorbing fluid in a porous medium can be determined by obtaining a photographic record of transmitted X-rays. Moreover, as changes occur in such a System, these changes can be observed by taking successive photographs. Previously, X-ray methods have been used in fluid flow studies to determine quantitatively the saturation at a given point in the system. The intensity of the transmitted X-rays was measured by an ionization chamber, so that a point by point survey of saturation could be made. In comparison with this earlier quantitative procedure, the photographic procedure which simultaneously observes the saturation at many

Jan 1, 1952

By G. F. Sager, B. J. Nelson

Magnesium alloy forgings offer higher and more uniform mechanical properties than heat treated magnesium alloy castings and are used principally for light weight parts that may be stressed in fatigue or subject to impact loads, or where space limitations do not permit the use of the necessarily bulkier magnesium alloy castings. Compositions and Properties of Magnesium Forging Alloys The nominal compositions and properties of the principal commercial magnesium forging alloys are given in Table 1. The two that are most commonly used are AMC58S and AM65S. The former has the highest strength and is, therefore, employed for heavy duty applications. However, the forging of this alloy and of AMC57S ordinarily requires the use of slow speed hydraulic presses. The forging alloy AM65S combines good, although somewhat lower, mechanical properties with excellent forging characteristics. This alloy can be forged on hammers, upsetters, rolls, and mechanical presses, as well as on hydraulic presses. These characteristics make it particularly useful for many applications. Manganese Segregation in AM65S The alloy AM65S contains 5 pct tin, 3 1/2 pct aluminum, and a small amount of manganese, the manganese being added to insure satisfactory resistance to corrosion. Some manganese segregation was occasionally encountered in this alloy. In many applications, such segregation is of no particular consequence, but when forgings are acid dipped prior to the application of various chemical coatings, the segregated particles of manganese constituent may stand in relief. The resultant surface roughening may impair appearance and is undesirable in forgings employed in the textile industry, where very smooth surfaces are essential to avoid the catching and breaking of fine threads. An effort was therefore made to determine the cause of manganese segregation in this alloy and find a method for its elimination. Radiographic examination of a series of cast ingot sections and extruded samples of the AM65S type having manganese contents ranging from zero to about 0.7 pct revealed no appreciable manganese segregation when the manganese was less than about 0.4 pct. A small amount was observed with a manganese content of 0.46 pct and considerable with manganese contents of 0.6 pct or higher. Attempts to eliminate the manganese segregation by variations in the melting and casting conditions were unsuccessful and it soon became apparent that the trouble was attributable to the fact that the manganese contents that caused segregation were in excess of the amounts that would remain in solution at temperatures encountered in the melting and/or casting operations prior to the complete solidification of the ingots. A knowledge of the amounts of manganese that would be soluble in molten alloys of the AM65S type at various temperatures was obviously desirable. The liquid solubilities of manganese in binary Mg-Mn alloys and in Mg-Al-Mn and Mg-Zn-Mn alloys have been determined by Tiner and others,* but no data on the solubility of manganese in molten magnesium alloys containing tin and aluminum are given in the literature. For this reason, an investigation to determine the solubility of manganese in a magnesium alloy containing 5 pct tin and 3.5 pct aluminum (AM65S type) was undertaken.

Jan 1, 1950

"Located on the Big Hole River, three miles from Divide, Montana, and 21.75 miles from Butte.Built in 1899.DAM: Rock-filled wooden crib, 512 ft. long and 57.5 feet high.SPILLWAY: Equipped with flash-boards 189 ft. long, 8 ft. 10 inches high.PENSTOCKS: Two 8 ft. diameter of steel, each branching and supplying two wheels.WHEELS: Four double horizontal, double discharge turbines, made by The James Leffel & Co., 1,000 h-p., 180 r. p. m., direct connected to generators, operating at 60 ft. head. GENERATORS: Four G. E., revolving field, 750 k-w., 180 r. p. m., 800 volt, 3 phase, 60 cycle alternators.EXCITERS: Two water-wheel driven exciters.TRANSFORMERS: 12 250-k-w. G. E. air blast, primary 15,000 volts, Secondary 800 volts.OPERATION: The plant operates essentially as a peak load plant. Except in flood period, there is insufficient water to operate at full load continually. In December its average output is about 500 k-w."

Jan 1, 1913

By C. J. Guntner, R. P. Reed

A commercial 18Cr-8Ni iron alloy (AISI 304L) was examined in tension at 300°, 76°, 20°, and 4°K. Continuous stress-strain recordings were made, X-ray analyses at periodic stress (strain) intervals were obtained, and the magnetic measurements were taken. From this data the percentage of martensitic products [bcc(a) and hcp (E)] was computed as a function of stress (strain). It was found thatup to 15 pct E phase forms at low temperntures. The amount of E formed increases to a maximum at about 5 pct strain, then decreases. This decrease indicates the additional transformation of E to a&apos;. The total amount of E and a&apos; was suppressed at constant stress (strain) at 4°K as compared to 76°K. It is proposed that the suppression of E and a&apos; is associated with the decreased mobility of extended dislocations at very low temperatures. The yield strength decreased as the temperature was depressed below room temperature and then increased rapidly near 4°K. SOME ferrous alloys which are austenitic (fcc ?) at room temperature appear to be unique in that two martensitic products (hcp e and bcc a&apos;) may form on cooling to lower temperatures or on application of mechanical stress. The most common room-temperature austenitic ferrous alloys are 18Cr, 8Ni stainless steels. Most aspects of the spontaneous transformations have been previously described for these steels.&apos; Several previous papers have described special aspects of the stress-induced transformations at low temperatures for the stainless steels, such as the existence of the hcp phase (c) after straining at 76oK,2-7 the morphology after straining using electron microscopy,7 and the decrease in E at higher strains at 76oK.4 However, for a complete representation, one must know the stress-strain characteristics and the dependence of both martensitic products on applied stress and temperature. It is the intention of this paper to provide that documentation. To accomplish this, continuous stress vs strain recordings were made at four temperatures: 300°, 76", 20°, and 4°K for annealed AISI 304L (a commercial 18Cr-8Ni alloy). At periodic stress intervals at each temperature the integrated X-ray line intensity of a selected peak for each phase (y, E, and a&apos;) was measured. In addition, photomicrographs of the strained surfaces were taken and magnetic measurements were made. The magnetic readings can be directly converted into percent a&apos;.&apos;,e With these measurements the percentage of each phase may be plotted as a function of stress (or strain) and test temperature. It was found that up to 15 pct E phase forms upon stressing the AISI 304L alloy at low temperatures. The E percentage increases abruptly after the alloy yields, but then decreases gradually at higher stresses. The rapid increase in e at 76°K is associated with an "easy-glide" portion of the stress-strain curve. The total amount of a&apos; + .G is suppressed below 76°K at a constant stress or strain. The yield strength decreases down to 76°K but increases rapidly below 20°K. EXPERIMENTAL PROCEDURE Tensile test specimens were cut parallel to the rolling direction from 0.1-in.-thick sheet. Continuous stress vs strain recordings were obtained at each test temperature (300°, 76o, 20°, and 4°K) using equipment and methods described elsewhere.&apos; The specimens which were used in the X-ray analysis were stressed to successive increments of strain at each temperature, analyzed at room temperature, then restressed at the test temperature. This procedure was repeated until approximately ten X-ray analyses had been performed with approximately 1.0 pct strain increments. The specimens had a reduced section 1 in. long, 1.2 in. wide, and 0.1 in. thick. They were electro polished prior to testing and after each strain increment. Table I lists the chemical composition, grain size, and hardness for the alloy which was used. This is the same alloy for which extensive mechanical-property tests3 and morphological studies of the spontaneous transformations&apos; have previously been made. For the low-temperature tests (76o and 4°K) below the Ms temperature the specimens were initially cooled to the test temperature, held for 1/2 hr, then warmed and X-rayed at room temperature. The results are listed in Table 11. From earlier work8 it was known that additional transformation on the second cycle would be considerably less (-0.1 pct

Jan 1, 1964

Jan 1, 1941

By C. S. Smith, K. K. Ikeuye

In an earlier paper1 one of the authors called attention to the significance of the relative free energies of grain boundaries and interphase boundaries in alloys in determining the shape and distribution of micro-constituents. The ratio of the interphase and inter-crystalline boundary energies (that is, —?12, where ?12 is the energy of the interface between a crystal of phase 1 and a crystal of phase 2, and ?11 is the energy of the boundary between two crystals of phase 1) will be denoted by F. It is this ratio that determines, by the simple triangle of forces relation, the dihedral angle, ?, of phase 2 where it adjoins a boundary between two grains of phase 1. On a metallographic sample various angles are actually obtained because of the random orientation of the plane of observation, but the statistically most frequent angle is the true one. These basic principles were discussed in detail in the earlier paper. The experiments described below show the effect of both composition and temperature on ? and T for some alloys containing a liquid phase, and provide data on the rate of approach to the equilibrium angles in both solid and liquid phases. All the alloys were melted in a graphite crucible and cast into ingots 3/4 by 11/8 in. cross-section. Some of the aluminum alloys consisted of two immiscible liquids from which uniform castings could not be obtained. The amount of liquid phase varied locally to a considerable extent and the analyses were meaningless. Nevertheless, the composition of the liquid would not differ from that in an alloy of the intended gross composition, and the synthetic composition of the alloys was therefore used in considering the surface energy results. The ingots were given initial deformation by cold-rolling to 50 pct reduction, annealed, and given a second 50 pct reduction prior to cutting into small samples for heat treatment at the times and temperatures subsequently reported. The resulting micro-samples were carefully prepared metallographically and examined at magnifications of 650, 1280, or 2500. The objectives used were 21X, 0.40 NA (dry); 41X, 0.65 NA (dry); and 80X, 1.40 NA (oil emulsion). The appropriate angles were measured by rotation of the stage of a Bausch and Lomb metallograph to align the appropriate boundaries successively with a cross-hair in a micrometer eyepiece. About 250 angles were measured on each phase. Though the angles were read to 1°, the accuracy is probably not above 3°, because of uncertainty in setting the cross-hair tangent to the sometimes curved boundary. The corners of very small particles, particularly in early stages of adjustment after cold-rolling, were difficult to measure and the results were slightly dependent on the magnification used (compare Fig 1-C and 1-D). With particles of larger size and more nearly equilibrium shape, magnification made no difference (vide Fig 1-F and 1-G). The measured angles were grouped in 10° intervals (5° if ? was less than 20°) and plotted in bar

Jan 1, 1950

By H. E. Wheeler

THE work described was carried out during 1917 and 1918 at the testing laboratory of Watertown Arsenal at the instigation of the Nitrate Division and later with the concurrence of the Cannon Section of, the Ordnance Department, U. S. A. The experiments follow three principal lines of work: First, the effect of nitrogen under pressure on steel containers of various compositions at a red heat; second, the effect of decomposing ammonia on various alloy steels, iron, and non-ferrous alloys; third, a new theory of the erosion of guns in respect to the effect of nitrogen in steel. PART I In the Haber process for the manufacture of ammonia from its elements, it is necessary to have nitrogen and hydrogen of 1500 lb. per sq. in. (105.5 kg. per sq. cm.) at a temperature of 500 to 600° C. The steel containers for these gases gave trouble by failing without apparent cause. When the General Chemical Co. began to develop its method for the production of ammonia, it experienced the same difficulty and, knowing that the Haber process had solved the difficulty by the use of alloy steels, it made several small steel bottles of different compositions and kept them filled with these gases at this pressure and temperature until they failed. The time of service varied from a few days, for the plain steel casting, to two years for a chrome-vanadium forging. Four of these steel bottles were sent to this laboratory for investigation; they were a plain carbon-steel forging, a nickel-steel forging, a chrome-vanadium steel forging, and a chrome-steel forging. The time of service was as follows: plain carbon steel, 4 mo.; nickel steel, 6 mo.; chrome-vanadium steel, over 2 yr.; chrome steel, 4 mo. When these containers were cut open and the cross-section surface polished, they showed an inside zone with a different luster from the rest of the metal. Upon etching, this zone was almost unaffected while the rest of the steel etched normally.

Jan 4, 1920

"In the spring of 1927, six members of the American Institute of Mining and Metallurgical Engineers met for dinner at the Chemists&apos; Club in New York to discuss the possibility of setting up a committee within the Institute to further the current interest in the science of steelmaking. Attention to this subject had been crystallized by a symposium held by the Faraday Society in 1925. After a prolonged discussion, ranging from thermodynamics to slag conditioning, it was decided to approach the Institute with the request that a standing committee on "The Physical Chemistry of Steel Making" be set up. This committee proposed to promote scientific and practical papers on the subject, and was designed to cooperate with the Open Hearth Committee of the Institute in bringing scientific developments to the attention of open-hearth operators throughout the country. . . . "As the life of the [Physical Chemistry of Steelmaking] Committee lengthened and general interest in the technical phases of steelmaking grew, it .became evident that there was a distinct need for a book that might serve the open-hearth interests to better advantage than standard texts whose scope is necessarily wide and whose detailed exposition of the open-hearth process is, therefore, somewhat limited. With this thought in mind, the Committee, after some years of consideration and debate, embarked on the venture of writing a manuscript on &apos;Basic Open Hearth Steelmaking&apos;." The foregoing paragraphs, taken from the introduction by C. H. Herty, Jr. to the first edition, well describe the circum- stances which led to the publication of “Basic Open Hearth Steelmaking” in the spring of 1944. The book consisted of nine- teen chapters contributed by twenty-three authors and edited by the staff of Alloys of Iron Research and T. S. Washburn, H; M. Larsen, and J. S. Marsh with Frank T. Sisco as consulting editor. The Engineering Foundation and the Open Hearth Steel Committee of the Iron and Steel Division, AIME, made financial grants; steel companies and other organizations supported the publication by contributing time and expenses of staff members in their capacity as authors or editors. The volume was sponsored by the Seeley W. Mudd Memorial Fund and appeared under the

Jan 1, 1964

By H. S. Choi, I. Iwasaki

The effect of temperature as a parameter in ore flotation has not been systematically studied, although for some ores it has been known for many years that selectivity and grade of concentrates can be improved by conditioning or flotation at moderately or substantially elevated temperatures. In 1934 Coghill and Clemmer&apos; stated that "elevated temperature seems to make hard water more tolerable" in soap flotation, and a cursory examination of the literature indicates that some earlier investigators were aware of beneficial results obtained by floating above room or mill-water temperatures. Tartaron,2 Mitchell et aL.,3 and particularly Hamilton et al.&apos; have shown that high pulp temperatures give high recovery and selectivity in soap flotation of fluorite from a variety of gangue minerals. As a result of the work of these and of other investigators, high-temperature flotation has been successfully applied to industrial flotation of fluorite. Falconer" stated: "The use of high temperature conditioning (above 35°C and preferably above 60°C) in connection with the soap flotation of nonsulphide ores, as covered in B. Kalinowski&apos;s French Patent No. 847,-215, Dec. 7, 1938, is claimed to provide more intense activation, better separation of values from gangue, and reduction in quantity of reagents." The various investigations quoted above clearly demonstrate the improvements to be realized by increasing the temperature at which fluorite is floated, and it is surprising that little or no information has been published on systematic investigation of the same method as applied to other ores. The present article describes comparative results obtained at room temperature and at elevated temperatures by otherwise conventional flotation of iron ores, by single-mineral flotation in the Hallimond tube, and by contact-angle measurements. It is not the purpose of this article to evaluate the commercial feasibility of high-temperature flotation of iron ores, although preliminary calculations show that the cost should not be excessive and that the gains to be realized may well outweigh the extra cost of heating the pulp. LABORATORY FLOTATION TESTS Experimental: All flotation tests reported in this article that use a laboratory Fagergren cell were made on ore A (either containing the primary slimes or deslimed at 20µ as specified) following the preparatory procedures described elsewhere- or this particular ore. Ore A contained hematite, goethite (limonite), quartz, chert, and minor quantities of magnetite. Confirmatory tests made on other ores show that the same general principles apply to ores of similar mineralogy and structure. Conditioning was performed by adding the collector, as a soap, to the vigorously stirred and heated pulp. Conditioning time was 5 min, the pulp contained 60 pct solids, and the equivalent of 0.5 Ib of fatty acid was added per ton of original (unde-slimed) ore. The pH of the pulps ranged from 6.8 to 7.1 (25°C measurement) during conditioning. The pH was adjusted in the flotation cell by addition of either NaOH or H2SO4, the values reported being those of the pulp cooled to 25°C. During conditioning and flotation the pulp temperatures were controlled within l° to 2° by immersion of Variac-controlled Calrod elements in the conditioning beaker and in the cell, and by the use of water, heated to the appropriate temperature, for transferring pulp, adjusting pulp volume, and washing. Selectivity indexes have been calculated on the same basis as those reported in the article by Cooke, Iwasaki, and Choi." Results: Table I gives the results obtained by floating deslimed ore A with pure oleic acid at 25" and 50°C, and Fig. 1 shows the selectivity indexes plotted against pH of flotation. Inspection of Table I

Jan 1, 1961

By F. E. Bash

Previous to the war, this country depended on Europe for its supply of a number of alloys of great importance in the manufacture of electrical apparatus and equipment. When this source was cut off shortly after the beginning of hostilities and the small stocks in the United States were exhausted, either inferior substitutes had to be used or the manufacture of the apparatus suspended. Since electrical equipment was of primary importance in the prosecution of the war, the substitutes had to be used until the composition and processes of manufacture of the alloys could be determined. Included among these alloys was one generally known as manganin, which is composed chiefly of copper and manganese and which, beside having a low-temperature coefficient of resistance, has a low thermal electromotive force against copper. These qualities make it valuable for the manufacture of electrical instruments and machines in which it is used in the shape of wire, rod, and strip. As a result of these circumstances, an investigation was started to determine how manganin could be made on a commercial basis so that a product of uniform quality and the necessary electrical characteristics could be produced. The object was to procure an alloy with temperature coefficient of resistance not greater than 1 X 1X per " C. and a thermal e.m.f. against copper no greater than that of the imported material. It is characteristic of manganin that the temperature-resistance curve is not a straight line but has a peak, which varies in position with different samples; it is most desirable, however, to have it at a temperature of 25&apos; C. if possible. The coefficients of manganin from all records available ranged from a large negative to a large positive value. The composition as reported by different authorities is given in Table I. Prof. Matthew A. Hunter, of Rensselaer Polytechnic Institute, made up a number of small melts of manganin in a graphite crucible and the one that he reported as having the best cocfficient gave the following analysis: Copper, 83.6 per cent.; nickel 2.5 per cent.; manganese, 13.6 per cent.; iron, 0.3 per cent. An analysis of a sample of German manganin gave the following: Copper, 82.6 per cent.; nickel, 3.8 pcr cent.; manganese, 12.8 per cent.; iron 0.7 per cent.