By Donald McLaughlin

INCREASING variety of interests among mining geologists is becoming more and more marked, as the frontier of their science and of its applications continues to expand. Each of the traditional lines of inquiry provides its crop of new and better defined problems, and answers to them are being found in far more precise terms than in the past as older uncertainties .are swept away with the sharper techniques and the even sharper ideas of modern geology. A glance over the assemblage of projects and publications in 1939 reveals conspicuous activity in many different parts of the front, such as the attack on the controversial question of the acid or alkaline character of ore-forming solutions, the place of mineral districts in the larger structural framework of continents, and the place of ore shoots in the local patterns of districts. Instructive comparisons are being made which cut across lines of older correlations or which reinforce them by pointing out heretofore ne-

Jan 1, 1940

By L. M. Howe, J. Gordon Parr, E. Saarema

THE decreasing solid solubility limit at the titanium-rich end of the Ti-Cu constitutional diagram,' Fig. 1, suggests the possibility that titanium-rich alloys may be age-hardenable. However, results obtained by Holden et al. reproduced in Fig. 2 show that after quenching from 790°C the age-hardening of an alloy containing 1.7 pet Cu is very slight, while a 0.8 pet alloy decreases in hardness, during heat treatment at 400°C. It was believed possible that powder samples of alloys might show different results from the lump samples used by Holden et al., since small particles are often more sensitive to diffusion processes than larger samples. Consequently, a 1.9 pet (by weight) Cu alloy was made by the technique of levitation melting," checked for homogeneity, and filings of 48-65 Tyler screen size were cut from it for aging experiments. The filings were helium-quenched (by a technique described previously)' from 790°C, sealed in vacuo in silica tubes and aged at temperatures of 400°, 450°, and 500°C. Microscopic and X-ray examinations failed to reveal any structural changes during the aging process. This is not too surprising since early stages of precipitation do not usually manifest themselves in ways that are readily detectable by metallographic methods, and the extent of precipitation on overaging a 1.9 pet alloy is very small. However, hardness readings (taken on a Bergs-man micro hardness tester, using a 25 g load applied to a diamond indenter) do show a hardness peak at each aging temperature, Fig. 3. About a dozen readings were taken on each heat treated sample; the highest reading and the lowest reading were ignored and an average taken of the remaining values. In

Jan 1, 1957

By R. S. Shoemaker, D. L. Harris

Past investigations into the possibility of concentrating the low-grade iron ores of the Gogebic Range in Wisconsin have been hampered by the complex association of the constituent minerals. In part the problem arises from the fact that the iron occurs essentially as two minerals, hematite and goethite, having nearly the same chemical composition but exhibiting different physical properties. Individual grains of these minerals are usually so small that the ore must be ground to a size finer than 325 mesh if substantial liberation of the minerals is to be secured. Appraisal of beneficiation tests on this iron ore requires, therefore, some method of determining quantitatively the contents of constituent minerals in the various products of the beneficiation. Because of the chemical similarity of the two iron minerals, chemical analyses do not provide a means of differentiation. Although the minerals are different physically, they are both opaque and friable, and as the ore must be ground to a very fine size for liberation to be secured, quantitative microscopic methods of analysis are extremely difficult at best. In an effort to overcome these analytical problems, a quantitative X-ray diffraction analysis method has been developed at the University of Wisconsin for the research program on iron ore beneficiation.

Jan 5, 1955

Mr. Tays (communication to the Secretary): Mr. Wynne's criticism of my paper* brings forward a few points which are really important, and might properly have been considered in the original paper. By calling attention to them he has rendered me a service. It is quite true, as Mr. Wynne says, that, in the tests reported by me, the Bryan mill was always working at a relative disadvantage, and my comparison of the work of this mill with that of the stamp-battery should be interpreted, therefore, so much the more favorably to the mill. Of course, wire screens can be used to advantage on the Bryan mill, if they are not of smaller size than 30-mesh; but

Jan 1, 1902

By J. M. Dahl, R. J. Warrick, O. K. Riegger, H. Van Vlack

A liquid which is rich in oxygen (and silicon) develops at steel rolling temperatures in resulfurized and plain-carbon steels. This liquid fluxes solid manganese sulfide. The composition of the liquid and the resulting microstructures vary with the manganese/silicon/oxygen ratios in the steel. The observations and conclusions zuhich are presented are used 1) to suggest a mechanism for MnS deformation in resulfurized steels, and 2) to rationulize hot-shortness anomalies between plain-carbon and resulfurized steels. 1 HIS is a summary of the dependence of sulfide inclusion microstructures upon steel composition, and an interpretation of the behavior of sulfide inclusions at steel-rolling temperatures. Sulfide inclusions are known to have several metallurgical effects upon steel. Their effects upon hot-shortness are best appreciated. Although hot-shortness is well known, it is questionable whether its mechanism is fully understood because there are several anomalies in our interpretation. For example, why should not high sulfur contents produce extensive hot-shortness in free-machining steels ? A second metallurgical consequence of sulfide inclusions appears because sulfide inclusions improve machinability. Furthermore, globular inclu- sions are to be desired over elongated inclusions. To date, we know that lower silicon contents (< 0.010 pct) favor the globular sulfides, but we do not know why this interrelationship between silicon content and inclusion shape exists. Finally, the evidence is strong that the surface quality of a hot-rolled steel is particularly sensitive to the sulfur content. SUMMARY OF PREVIOUS WORK The role of sulfur in hot-shortness was first suggested during the past century. It is uncertain who was the first to conclude that sulfur was less deleterious in the presence of manganese, and that manganese altered the sulfide phase from a liquid FeS to a solid MnS at steel-rolling temperatures. However, Urban and chipman&apos; emphasized that liquid FeS may accumulate as an interdendritic film during solidification. More recently, Keh and Van lack&apos; showed that the intergranular liquid does not completely surround the metal grains at all rolling temperatures. Rather, a small finite dihedral angle exists when geometric equilibration is attained at

Jan 1, 1962

By J. L. Bruce, N. B. Braly, F. A. Linforth, Wm. B. Daly, Paul A. Gow, C. L. Berrien, R. H. Sales, P. F. Beaudin, John Gillie, G. W. Roddewig

Butte mining district is situated in Silver Bow County, in the southwestern part of Montana. Butte originated as a placer mining camp, gold having been discovered in 1864, on Silver Bow Creek, near the southerly end of what is now Main Street. The Butte placer gold was heavily alloyed with silver, and only commanded $13 an ounce. Placer mining was vigorously prosecuted along Silver Bow Creek and its tributary gulches for about 5 years, at the end of which time, in 1870, the Butte camp was practically deserted. In the meantime, the quartz veins prominently traceable over the hillsides were located, the first location, July 12, 1864, being made by the Missoula Mining Co. and called the Missoula Lode Claim, and later relocated by G. 0. Humphreys. Reasoning from the presence of the gold placers, free milling gold and silver ores were eagerly looked for by the early prospectors. Claims covering the great Rainbow and other silver lodes were located in the 60&apos;s. The presence of valuable silver ores in these veins caused the staking of many claims, believed to be valuable only for silver, but which later, at depth, proved to be enormous copper producers.

Jan 1, 1925

By A. J. Mortlock

Cobalt and nickel have been diffused at tracer concentrations in gold at several temperatures in the range from approximately 700° to 950°C. The diffusion penetration profiles were determined by a serial sectioning technique in which the gold is first anodized and then the anodic layer is dissolved in acid. In this ulay sections as thin as 250A could be removed reproduci-bly. In all cases, the region close to the specimen surface was characterized by irregular behavior in the sense that the logarithm of concentration was not linear in the square of the penetration distance. In sotne cases, there zuas an indication of the operation of very slow dijfusion in this region, while in others the apparent diffusion coejj&apos;icient was negative. Possible reasons for this anomalous behavior are briefly discussed. In recent years it has been found that the region close to the surface of a metal can sometimes exhibit anomalously slow diffusion characteristics relative to the interior of the metal. One of the best examples of this fact is the work of Styris and omizuka,&apos; who showed that the apparent diffusion coefficient for zinc in the region withi: about 1 p of the free surface of copper was about ,,,, that at deeper penetrations. This result is particularly interesting, because it is free from the possibly complicating effects of low solubility of the diffusing tracer in the solvent metal. In the case of diffusion under conditions of low solubilitjr, interpretaticn of the results in terms of lattice diffusion is difficult because of the enhanced short-circuiting produced by segregation to dislocations.2&apos;3 Measurements by Duhl et 1. suggest that cobalt diffusing in gold may also show a near-surface effect of this type. Once again the solubility is high, so that this result could be of great interest. However, the technique used for analyzing the diffusion penetration zones by Duhl, viz. the counting of residual gamma activity in the specimen following sectioning, appears to have indicated a near-surface effect in a parallel experiment on the self-diffusion of gold reported at the same time. The latter result is known to be spurious, since Kidson5 has demonstrated that self-diffusion in gold does not show this effect. Duhl et 01. also reported some measurements on the diffusion of nickel in gold, but failed to give any data for the near-surface region. As the solubility of nickel in gold is high, such data would also be of special interest. We, therefore, decided to conduct another set of experiments on the diffusion of nickel and cobalt in gold, using a sectioning technique that allows the individual sections to be assayed for solute content and thus gives direct determinations of penetration profiles. Also, by sectioning with an anodizing/stripping tech- nique, very thin layers can be removed and the region close to the surface studied in detail. MATERIALS The gold specimens were supplied as single crystal disks $ in. in diam by a in. high by Monocrystals Co. of Cleveland, Ohio. The gold itself was of spectro-scopic purity, i.e., better than 99.99 pct pure. METHOD Specimen Preparation. One flat end face of each gold crystal was spark planed with a Servomet spark erosion machine set for minimum spark energy. Following this treatment the crystals were preannealed for 2 to 4 days at temperatures of either 400" or 700°C. The three crystals preannealed at 700°C showed signs of recrystallization. The spark-planed end face of each crystal was then coated with the appropriate amount of 63i or 60 radioactive tracer. This deposit was laid down in a simple plating bath containing the as-supplied solution of the radioactive isotope as well as sufficient ammonium oxalate to saturate the solution. Some ammonium oxalate remained undissolved on the floor of the bath for this purpose. During plating further additions of ammonium oxalate were sometimes required to allow the plating to continue satisfactorily, perhaps due to passivation of the undissolved oxalate already present. The thickness of the deposited layer was determined by comparison of the apparent surface activity of the plated specimen with that of a similar specimen having a weighable deposit of the isotope on its end face. Correction for self-absorption of the radiation was made in this calculation. Annealing. The deposited crystals were annealed in a hydrogen atmosphere in sealed silica tubes. During this heat treatment they were supported, active face down, on optically flat silica plates. The temperature was measured with calibrated Pt vs Pt-10 pct Rh thermocouples, and the tabulated values can be taken to be correct to Z°C. All the crystals showed evidence of recrystallization following these heat treatments, suggesting that initially they may not have been good single crystals or had suffered strain during delivery. Concentration Profile Analysis. After annealing, the crystals were sectioned by the anodizing-stripping technique.6 The anodizing involved suspension of the specimen with its cylindrical axis horiz6ntal by a gold wire in a 200-ml beaker containing 1 M Hg304. A cathode in the form of a strip of gold sheet, 2 in. wide and positioned to be in contact with the curved side of the beaker, completely encircled the specimen. An anodizing current of 30 ma, corresponding to a current density of 5 ma per sq cm on the surface of the specimen, was passed for times ranging from 5 to 150 min depending on the thickness of gold to be removed; the solution was stirred continuously during this process. Following this treatment, the specimen

Jan 1, 1969

By R. G. Ward, A. E. El-Mehairy

A technique was developed to calculate the density of liquid metals from the profile of a weighed levitated drop obtained by emitted light photography and calibration. The density of liquid copper was determined over the temperature range 1370" to 2100°K and expressed with the equation: The molar volumes and thermal coefficients of expansion are calculated. Copper, upon melting, was found to expand 3.34 pct. A knowledge of the density of liquid metals is essential as it is a parameter appearing in most theories of the liquid state. The liquid density is also necessary for the calculation of the commercially important contraction occurring on solidification. Unfortunately good density values are rarely available and the present work was undertaken to establish a new method of density determination free from the limitations of the existing methods. For liquid metals with high melting points, the variation and the limited number of density values reported in the literature have been caused primarily by difficulties in technique, a matter which has been adequately discussed by Urbain.&apos; In all the methods used for measuring the density of the high-melting liquid metals there are sources of error, and corrections have to be made. For example, in the method of balanced columns, the formation of gas bubbles in one or both arms was a great source of error. In the pyknometer3 and immersed-sinker methods, corrections of certain volumes for thermal expansion to the operating temperature exceed 4 pct. In the maximum-bubble method5 a correction for the thermal expansion of the bubble-tube is used (about 1.6 pct); a second correction takes into account the change in the volume of liquid displaced by the bubble-tube (about 3.5 pct). Another method used is based on the shape of a drop of liquid, at rest on an inert refractory plaque, obtained photographically or radiographi-cally. The volume is calculated from the shape, which is sensitive to the surface tension and supporting material, by some intricate empirical relation. The drop contour changes with 90 deg rotation of the support.7 The application of all methods is limited by reaction between liquid metal and the apparatus. The successful stabilization of a mass of liquid metal during levitation melting8 afforded a technique for measuring the density of liquid metals out of contact with solid materials. The technique was developed by using copper as the density of liquid copper has already been studied extensively, thus allowing comparison with the new method. It consists of calculating the volume from the dimensioned profile of the levitated drop obtained by emitted-light photography and careful calibration. The molten egg-shaped drop spins around the magnetic axis of the coil (lined vertically) at a speed which seems to increase with increasing temperature. The method does not involve corrections and the experimental setup allows the use of vacuum or special atmospheres. The maximum operating temperature is limited by excessive evaporation of metal from the droplet. EXPERIMENTAL Levitating System. A stabilizing ring was used in conjunction with a 3-turn levitating coil energized by a 450-kc per sec, 10-kw Toccotron with a high current-low voltage output stabilized to f 1 pet.&apos; APyrex glass tube with a Pyrex Optical flat window inserted through the coil and ring allowed the use of special atmospheres during levitation melting, as shown in Fig. 1. Optical System. Fig. 1 shows the optical arrangement used to photograph the profiles of the drop, parallel and perpendicular to the vertical spinning axis, simultaneously on the same frame of a high-speed 35-mm film. The optical system was adjusted to avoid any distortion of the profiles and to ensure that both profiles are in focus. The length of path from object to objective was about 30 cm, and a magnification factor close to 1 was obtained with the single-lens reflex-camera system. Temperature Measurement and Control. In operation, the specimen temperature was constant to 5 C for a fixed power input to the levitating coil and fixed rate of gas flow through the tube. The temperature was measured by an automatic two-color pyrometer (Coloratio) checked at the melting

Jan 1, 1963

Aamot, Olav Crone, (M&apos;29) Chem. Engr., Elektro¬kcmisk, Raadhusgt. 32, Oslo. Norway. . Aase. Glenn D., (J&apos;40) Jr. Met., American Smelt. & Refin. Co., Selby, Calif. Abadie, Henry G., (J&apos;43) Petr. Engrg., Avenal, Calif. Abadilla, Quirico A., (M&apos;38) Min. Engr., Dir., Bureau of Mines, Manila, P. I. Abbott, Agatin Townsend, (J&apos;40) Jr. Engr., Phelps Dodge Corp., Morenci Branch. Morenci. Ariz. Abbott, Clarence E., (M&apos;04) Civ. Engr. V.P., Tennessee Coal Iron & R.R. Co., 1542. Brown Mars Bldg. Birmingham. Ala. Abel, Raymond L.. (M&apos;23) Chem. Engr., Com¬manding Officer, Pittsburgh Chem. Warfare urement Dist., American Bank Bldg.. Pittsburgh. Pa. Abel, Walter D., (M&apos;32) Min. Engr., Supvr. Engr.. R.F.C., Los Angeles, Calif. Abele, Louis T., (M&apos;31) 423 3rd Ave., Decatur. Ga. Abell, Leo M.: (M&apos;31) Mill Supt. & Met.. Em¬ peror Gold Min. Co., Ltd., Vatukoula. Fiji Islands. Abernathy, G. E., (M&apos;38) Geol., Kansas State Geol. Survey, Pittsburg, Fan. Abernathy, Jack H., (M&apos;40) Cons. Petr. Engr., First National Bldg.. Oklahoma City, Okla.

Jan 1, 1943

By H. S. Kalish, F. J. Dunkerley

INTRODUCTION AND PREVIOUS WORK THE determination of the low temperature tensile properties of tin and tin-lead alloys was initiated as part of an extensive research program on the phasial equilibria of tin binary systems below 13.2°C and the property changes associated therewith. A survey of the literature revealed that, although some room temperature tensile data were available for tin and a few tin-lead alloys, there existed no survey report of the low temperature tensile properties of these alloys. Accordingly, the tensile data for tin and a series of pure tin alloys containing from 0.01 to 50 pct lead were measured at eleven temperatures from -196 to +20°C and are presented here in survey form. In addition to the importance of these tensile data as a preliminary to certain fundamental research, this information promises also to be of commercial importance because of the &apos;extensive use now being made of tin-lead solders in refrigeration and gas liquefaction equipment. Occasional failures of the solders in low temperature service have been attributed by some metallurgists to low temperature mbrittlement, while others hold that failure results from the transformation of the tin-rich phase of the solder from the solid white (beta) to the powdered gray (alpha) form. From the data previously available in the literature, neither of these explanations can be completely corroborated. Cohen and van Lieshout1 have established the beta to alpha tin transformation at 13.2°C and have shown that strain accelerates the transformation. Further, they showed that although I pct lead retarded the transformation, it was not eliminated. It will be pertinent, then, to note whether the beta to alpha transformation of the tin-rich phase will occur in a short-time tensile test. Polanyi and Schmid2 studied the tensile . properties of tin single crystals at -185°C and report that tin is brittle at-this temperature. In 1946, Kostenets3 reported that pure tin was brittle at -196 and -253°C, while lead remained ductile at both these temperatures. He also studied the tensile properties of tin-lead alloys containing from 10 to 75 pct lead at -253, -196 and +17°C. The ultimate tensile strength increased more than two times in going from room temperature to -196°C and about three times that value on further cooling to -253°C. All the alloys were brittle at -6°C except those containing more than 75 pct lead. Even at -253°C, the 75 pct lead alloy retained 36 pct elonga¬tion in a 30 mm-ga. length. Creep is also an important phenomenon

Jan 1, 1948

By C. F. Austin

lined-cavity shaped charge is an explosive mass with a cavity at one end and the detonator at the opposite end. The cavity is lined with a dense material, such as metal, glass, or a ceramic. Such an explosive device can be a useful drilling tool. Lined-cavity shaped charges are constructed to do just one thing — create a high-velocity jet of liner particles that can bore a hole in a target. The liner must be smooth and symmetrical, and high-velocity, high-brisance explosive must be used rather than ordinary commercial dynamites. Since the depth of target penetration is related to jet length, a standoff distance should be provided to hold the charge a short distance from the target. This allows the jet to lengthen prior to target impact. The best results are obtained when the jet is perpendicular to the target surface. Charges can be positioned for firing by taping them to a stake or simply laying them on a flat surface at the proper distance and angle with respect to the target. EFFECTS ON THE TARGET When a jet strikes a rock target, the jet and target particles at the jet-target interface move outward radially with respect to the jet axis to create a tremendous compressive load on the target material immediately below the target surface. The result is a shallow crater formed by spalling at the point of target entry. After cratering ceases, the steadily deepening hole continues to form as a result of the jet&apos;s imparting radial motion to the target particles at the jet-target interface. These radially moving particles collide with one another and with the hole walls, the net motion of the spent jet particles and target particles being back out of the hole in an axial direction (the backblast). The backblast keeps the penetration free of debris during penetration, al- though loose surface rock often falls into the hole after penetration ceases. The sudden stress relief after penetration ceases sometimes results in minor hole-wall rebound, which can partially fill the hole. The hole bottom will taper as the jet velocity decreases, until the jet velocity is too low to maintain the backblast. At this point the remaining jet and the following slug material are simply packed into the hole bottom. HAZARDS INHERENT IN USE Air blast from the highly brisant explosives used in shaped charges can damage nearby structures

Jan 1, 1961

By J. Hall Carpenter, James E. Lawver

Shortly after the passage of the Taconite Amendment in Minnesota, several mining companies announced their intention to build new magnetite taconite plants and another announced its intention to augment present facilities. It is clear that Minnesota will enjoy an expanding magnetite taconite industry, but despite the fact that the reserves are large, eventually they will have to be supplemented by oxidized deposits. Furthermore, not all producers have magnetite taconite reserves. Due to the extensive oxidation of most of the western part of the Mesabi Range, there are no large blocks of unaltered magnetite taconite that lend themselves to open pit operations. Unless a commercial process can be developed to concentrate the oxidized, or so- called "nonmagnetic", taconite and semi-taconite, the existing mines operating in the western part of the range will be forced to shut down when the direct shipping, wash and gravity ores are depleted, or are no longer salable, because of their poor quality compared to high-grade pellets. KNOWN PROCESSES COSTLY The enormous reserves of the oxidized iron- bearing formation have offered a tantalizing challenge to metallurgists for many years. In fact, several processes for concentrating certain types of oxidized ore have been successful at both laboratory and pilot plant level, but to date no process for concentrating semitaconite or oxidized taconite has reached commercial fruition. Magnetic roasting, followed by low-intensity magnetic separation1, has shown considerable promise because the high iron recovery makes the ratio of concentration of many of the oxidized ores more favorable than that of magnetite taconite. However, the capital and operating costs are high and, in many cases, a high- grade concentrate cannot be made without resorting to flotation of the magnetic concentrate. Hence, most research groups are investigating alternate methods of concentration with the hopes of reducing the cost.

Jan 9, 1965

By C. S. Smith, E. W. Palmer

For several years an investigation has been in progress in the research laboratory of The American Brass Co. to determine the thermal and electrical conductivities of most copper alloys of commercial importance and several of scientific interest. This paper contains such data on the binary alloys of copper with silicon, aluminum, manganese and nickel, and on a large number of ternary or more complex alloys. Some interesting general relationships between the thermal and electrical conductivities for all copper alloys at all temperatures are pointed out. The data for the copper-zinc, copper-phosphorus and copper-tin binary systems have already been published1,2 † except for the electrical conductivity at 200" C., which is given in the appendix of this paper. Literature on Thermal Conductivity of Copper Alloys The papers referred to above contained a summary of the figures available in 1929 for the thermal conductivity of copper alloys. There is given in Table 1 herewith a selection of the data that have appeared since that time. The measurements of Hanson and Rogers3 are particularly interesting since they cover a series of alloys in the alpha solid solution range and show the effect of heat-treatment. Their alloys were tested as annealed castings, and are not therefore directly comparable to the worked alloys measured in the present investigation, although the difference is small. Bailey&apos;s determinations4 were carried out on the alloys used by Lees6 in 1906, and extend his results to higher temperatures. It is most unfortunate that the alloys were not analyzed, for the approximate compositions given are hardly sufficient identification of the material. It is equally to be regretted that neither Hanson and Rogers nor Bailey give data for the electrical conductivities of their samples. Sager6, using the heat-wave method of King, determined the thermal conductivity of copper, nickel and four alloys of the two metals. His results are included in Table 1.

Jan 1, 1935

By C. S. Smith, E. W. Palmer

For several years an investigation has been in progress in the research laboratory of The American Brass Co. to determine the thermal and electrical conductivities of most copper alloys of commercial importance and several of scientific interest. This paper contains such data on the binary alloys of copper with silicon, aluminum, manganese and nickel, and on a large number of ternary or more complex alloys. Some interesting general relationships between the thermal and electrical conductivities for all copper alloys at all temperatures are pointed out. The data for the copper-zinc, copper-phosphorus and copper-tin binary systems have already been published1,2 † except for the electrical conductivity at 200" C., which is given in the appendix of this paper. Literature on Thermal Conductivity of Copper Alloys The papers referred to above contained a summary of the figures available in 1929 for the thermal conductivity of copper alloys. There is given in Table 1 herewith a selection of the data that have appeared since that time. The measurements of Hanson and Rogers3 are particularly interesting since they cover a series of alloys in the alpha solid solution range and show the effect of heat-treatment. Their alloys were tested as annealed castings, and are not therefore directly comparable to the worked alloys measured in the present investigation, although the difference is small. Bailey&apos;s determinations4 were carried out on the alloys used by Lees6 in 1906, and extend his results to higher temperatures. It is most unfortunate that the alloys were not analyzed, for the approximate compositions given are hardly sufficient identification of the material. It is equally to be regretted that neither Hanson and Rogers nor Bailey give data for the electrical conductivities of their samples. Sager6, using the heat-wave method of King, determined the thermal conductivity of copper, nickel and four alloys of the two metals. His results are included in Table 1.

Jan 1, 1935

By Robert D. Pehlke, Arden L. Bement

A mass transfer coefficient for the removal of hydrogen from liquid aluminum by inert flush degassing has been determined experimentally at 700°C. A mathematical model has been derived, assuming transport control, which adequately describes the experimental data. The removal of hydrogen is shown to increase with decreasing bubble size, and with increasing flow of flushing gas. The presence of hydrogen in liquid metals in amounts which exceed the solid solubility at one atmosphere hydrogen pressure is highly undesirable, causing unsound ingots or castings, or resulting in difficulties during further fabrication. The removal of hydrogen from liquid metals can be accomplished by several methods, the principal two being vacuum treating and inert flush degassing. The design of a process involving either of these techniques is based on the mass transfer coefficient for hydrogen between the liquid metal and a hydrogen-dilute gas phase. In an effort to extend our knowledge in this area, an investigation of the rate of removal of hydrogen from liquid metals by inert gas flushing was undertaken. In view of the difficulties encountered with gas porosity in the casting of aluminum and aluminum alloys, and because of certain experimental advantages, liquid aluminum was selected for the study. PREVIOUS INVESTIGATIONS The removal of gases from liquid metals, particularly steel, has received considerable attention in recent years, The first definitive work of a theoretical nature was presented by Geller1 who considered the case where equilibrium exists between purging gases and metal bath during flushing, and also deviations from this ideal case. Hulme2 has surveyed a number of experimental studies and discussed some of the practical limitations of removing dissolved gases from molten metals. More recently a number of studies have been reported on degassing of steel melts by flushing with an inert gas.3&apos;4 Considerable work has also been reported on aqueous and organic liquid-gas systems, and an excellent summary prepared by Hovis.5 The treatment of liquid aluminum by a flushing gas to remove dissolved hydrogen has been known for several decades.6 A number of gases have been used for this purpose, including nitrogen, argon, and chlorine, or mixtures of these gases. Tikkanen and Erkko7 have studied the relative density changes of aluminum castings poured from melts degassed with chlorine, nitrogen, and mixtures of the two gases. Their

Jan 1, 1962

By Peretti, E. A.

Since its development about forty years ago by J. V. N. Dorr (Cyanidation and Concentration of Gold and Silver Ores, McGraw Hill Book Co., 1936, 1-5), and others, continuous countercurrent decantation has not only become one of the standard methods for extracting gold and silver from their ores, but has also found wide application in other metallurgical and chemical industries. In 1917 L. B. Eames published an excellent paper (Countercurrent Decantation, Trans AIME, 1917, 57, 143- 158), in which he determined the effects of grade of ore, ratio of solution precipitated to ore treated, variations in the density of the thickener spigot discharge and variations in the value of the barren solution upon the gold assay of the solutions discharged from the thickeners in the system. Eames showed that, other things being equal, the dissolved gold lost in the tailing varies directly as the value of the ore and as the value of the barren solution. The tailing loss de- creases rapidly as the ratio of solution precipitated to ore treated is increased to about three or four to one. Beyond this point the improvement is negligible.

Jan 1, 1949

By W. B. Triplett, H. I. Aaronson, G. M. Andes

THE morphology and mechanism of the proeutectoid a and the eutectoid reactions have been recently investigated in some detail in an iodide-base Ti—7.22 pct Cr alloy.&apos; These studies have now been extended to an iodide-base Ti—10.8 pct Cr alloy in order to evaluate the effects of composition on the proeutectoid and eutectoid transformations in titanium-chromium alloys. The alloy used in this investigation had the following composition: 10.8 Cr, 0.0327 0, 0.011 N, 0.0063 H, and 0.011 pct C. Specimens of this alloy were heat treated in evacuated and internally get-tered Vycor capsules. The specimens were solu-

Jan 1, 1959

By A. C. Fraker, H. H. Stadelmaier

In the systems Mo-Fe-C, Mo-Co-C, and Mo-Ni-C the phase boumdaries of the cubic Ij carbides were determined at 1000°C and the variation of the lattice parameter with composition was measured. In the system Mo-Fe-C a single ternary carbide, Mo3Fe3C, was observed. In Mo-Co-C and Mo-Ni-C two new n phases of the type M12C were found: Mo6C06C and Mo6Ni6C. At 1000°C they coexist with the M6C phases MO3-4,CO3-2C and Mo3-4Ni3-2C, respectively. Mo3C03C and Mo4C02C are not separate phases but parts of a single M6C phase region, and the same is true of Mo3Ni3C and Mo4Ni2C. THE n carbide structure type has been known since it was determined by westgren&apos; in 1933, yet reliable information on phase compositions of this type is ap-parently scarce. The following selection of suggested formulas illustrates the extent of the confusion con-cerning compositions: W2-3Fe4-3C,1W6Fe6C,2 W2_4Fe4-2C,3 (W,Fe)6C,4 Tj.-W4Co2C and nz-W6Co6C,5 n1-W3Co3C and n2-w4Co2C,5 W3C03C and w6Co3C2,7 MO3Fe3C,8n2-M04Fe2C,9 (MO,Fe)6C,4 MO3CO3C,8 n2-MO4CO2C.9 Many of these compositions obviously overlap, some disagree in carbon content. The use of the designations 77, and n2 is not consistent. There is uncertainty whether two carbides M6C coexist or whether there is only one M6C with a wide range of substitution of one metal for the other. The existence of M12C seems questionable altogether if one ignores the results of a neutron diffraction study of W6Fe6C supporting that particular metal to carbon ratio.&apos;&apos; More reliable information is available for the iso-typic oxides studied by Nevitt,11 Nevitt, Downey, and orris," and Meussner and carpenter.l3 That n car-bides and oxides are structurally identical, particularly with respect to the location of the metalloid atom, has been demonstrated clearly by Stadelmaier and Meussner14 and also by Parthe, Jeitschko, and sadagopan.15 Therefore the present paper, which attempts to establish the phase boundaries of n defini-tively for three carbon systems, has implications for the whole family of filled Ti2Ni types. EXPERIMENTAL PROCEDURE The samples were prepared in two stages. Pellets weighing 3 g were compacted from powders of the elements and presintered in a closed tube of fused silica that had been evacuated to lO-4 mm Hg. This was fol- lowed by arc melting the sintered samples under argon. Remelting the button once was sufficient to produce homogeneous specimens. The metal powders had the following minimum purities in wt pct: molybdenum 99.5, iron 99.0, cobalt 99.7, nickel 99.9, graphite 99.94. Carbon determinations by the gas volumetric method were obtained from thirty-one of the one hundred samples in the annealed condition. They were limited to compositions that were critical to placing a boundary line in the isothermal sections. The carbon losses were comparatively low and averaged less than 1.5 at. pct. For annealing, the samples were sealed in tubes of fused silica evacuated to 10-4 mm Hg. The annealing schedule was 20 hr at 1250°C followed by 150 hr at 1000" ±10°C. For the water quench the silica glass tubes were broken mechanically to speed the quench. The specimens were examined in the as-cast and annealed condition by standard metallographic techniques. Some of the as-cast and all annealed samples were studied by X-ray diffraction using a 114.6-mm powder camera with filtered Co radiation. The lattice parameters of the n phases were determined by graphic extrapolation to 8 = 90 deg on a plot against sin2 8. It is estimated that the maximum error in the lattice parameters is ±0.002A.. The phase fields were determined by the disappearing phase method, relying on X-rays for phase identification and on microscopy to detect small amounts of a phase. RESULTS Pertinent information on the binary side diagrams has been summarized by Hansen and Anderko16 and Elliott17 and will not be discussed further. Photomicrographs documenting the equilibria at 1000°C have been selected to avoid redundancy due to the similarity of the three systems. Thus there will be only one picture showing an equilibrium with Mo2C, and so forth. Molybdenum-Iron-Carbon. An isothermal section of most of the Mo-Fe-C system at 1000°C is shown in Fig. 1. No attempt has been made to distinguish between a and y iron or to determine their phase boundaries. A conspicuous absence is the phase Fe2 1Mo2C6 with the Cr23C6 structure, supporting the suggestion by Krainer4 that it decomposes by annealing at high temperatures. The only ternary phase is found in a narrow range around Mo3Fe3C (MO43Fe43C14). A microstructure with a two-phase mixture of Mo + n is seen in Fig. 2. The variation of the lattice parameter of n with the estimated composition is shown in in Table IA. The phase diagram does not agree with the results of Kuo9 who reported n2-Mo4Fe2C. Our lattice parameter Varies from 11.095A at the iron-rich end to 11.140Å at the molybdenum-richoend of the phase field whereas Kuo9reported 11.26Å for Mo4Fe2C. We are in agreement with the older work

Jan 1, 1970

AlFred JamEs," London, Eug.:—I thank you, gentlemen, for Sour kind invitation to address you. It is a very great pleasure for me to be here at your annual meeting, and, although I have been a member since 1894, this is the first opportunity I have

Jan 1, 1909

By Cyril S. Taylor, Junius D. Edwards

Magnesium is the lightest metal used for structural purposes, for which reason perhaps more than usual interest is attached to measurements of its density. Although the density of solid magnesium has been det,ermined frequently, no measurements of the density of the liquid metal are available. Because of unusual experimental difficulties in measuring the density of the liquid, only a limited number of measurements of good precision were secured. The results, especially the value for the crystallization shrinkage, are of great interest in connection with the casting of the metal. A number of samples for these measurements were made available through the courtesy of the American Magnesium Corp. They were in the form of extruded bars 3/8 in- in diameter and several were of exceptional purity, as indicated by careful analyses. Table 1 gives the density values (at 20" C.) for magnesium of varying degrees of purity. The density was measured at room temperature by comparison of the weight in air, and when immersed in distilled water. The necessary buoyancy corrections were applied, so that the density could be expressed in absolute measure—grams per milliliter. The effect of the buoyancy of the immersed suspension and the surface-tension pull of the water upon the suspension were eliminated from the results by a preliminary weighing of the suspension immersed to the working depth. Great care was necessary to prevent the introduction of a significant error by the formation of gas bubbles upon the clean magnesium surfaces; these are sometimes very minute and easily escape observation. They may be detached by raising the specimen from the water and again immersing; this should be done just prior to completing the weighing. Their formation may be almost entirely prevented during a measurement by previously immersing the specimen in a solution of paraffin in petroleum ether. The thin film of paraffin remaining after the evaporation of the solvent prevents wetting of the magnesium surface by the water. In one such determination, the paraffin coating on a 22-gm. Specimen

Jan 1, 1923