By O. P. Arora, M. Metzger, G. R. Ramagopal

Single-phase aluminum containing 0.0001 to 0.06 pct Cu was studied in strong acid, mainly through observations of hydrogen evolution. The strong influence of copper was exerted almost entirely through the imposition after a certain delay time of an auto-catalytic localized-corrosiott reaction. Additions of cupric ion to the acid produced lower accelerations. The significance of the quantity and distribution of copper was discussed, and the implications for intergranular corrosion and neutral chloride pitting were indicated. AN investigation of intergranular corrosion in single-phase high purity aluminum exposed to hydrochloric acid indicated the copper content of the metal to have an influence on corrosion at lower levels than previously suspected.&apos; The work reported here was a closer examination of the action of copper but dealt with general corrosion to gain the advantage of having a continuous measure of corrosion through the volume of hydrogen evolved, the reduction of hydrogen ion to hydrogen gas being the principal or only cathode reaction in strong hydrochloric acid. Previous work on the hydrochloric acid corrosion of aluminum was sometimes insufficiently structure-conscious and the need for care in evaluating it arises from the low solubility of the iron impurity,&apos; and of some alloying elements, and the known or possible presence in many of the compositions studied of second phases leading to greatly increased corrosion rates.3 These increases are attributed to the presence of low hydrogen-overvoltage cathodes provided by the second phase.3&apos;4 For the present single-phase work, a few studies which used high-purity base material and small copper additions5-&apos; provide the essential information most unambiguously. The corrosion rate was shown to be increased markedly by the introduction into the acid of small quantities of the ions of copper (and of certain other metals) which cement on the aluminum and provide cathodes of low overvoltage.5 When there was sufficient copper in the aluminum, the same result was produced during the course of corrosion leading to a rate which increased with time as the reaction was stimulated by one of its products (autocatalytic reaction). In 2N (7pct) HC1, an accelerating rate was observed at 0.1 pct Cu but not at 0.01 pct.5,7 The present work dealt with corrosion rate and morphology and their correlation with the quantity and distribution of copper catalyst for copper contents from 0.0001 to 0.06 pct. PROCEDURE A lot of high-purity aluminum containing 0.0021 pct Cu, 0.001 pct Fe and 0.003 pct Si (Alloy A) was alloyed with copper to yield aluminum containing 0.014 pct Cu (B) and 0.06 pct Cu (C). Later it was found necessary to include the lower copper Alloy K which contained 0.0001 pct Cu, 0.0004 pct Fe and 0.0004 pct Si. The upper limit for any other element can be confidently estimated as 0.0005 pct. No element other than copper appears to be present in quantities sufficient to have an effect on general corrosion as great as the observed effect of the copper in A, B, and C. The only other heavy metal detected by spectrographic examination was silver (< 0.0001 pct). The acid was made up from a selected lot of 37 1/2 pct CP hydrochloric acid containing 0.1 ppm heavy metals (mainly Pb), 0.05 ppm Fe, and < 0.008 ppm As and from water distilled from 1 megohm-cm demineralized water and believed to have contained negligible quantities of heavy metals influencing corrosion. Acid strength was adjusted to within 0.05 pct HCl of the stated value by using precision specific gravity measurements. Test blanks 10 by 41 mm were sheared from 1.65-mm cold-rolled sheet. Edges were finished by filing. The blanks were annealed in air at 645°C for 24 hr in alundum boats and rapidly water quenched. The anneal is thought to have produced a substantially homogeneous solid solution—for iron, copper, or silicon, for example, the annealing temperature was 200°C or more above the solvus-and the quench is considered to have preserved the high-temperature structure except for the condensation of lattice vacancies into dislocation loops.&apos; The 0.06 pct Cu alloy did not appear unstable in respect to slow precipitation reactions at room temperature since two pairs of tests failed to show significant differences between specimens heat treated 3 1/2 years earlier and specimens heat treated 1 or 2 days before.

Jan 1, 1962

By G. M. Gay, R. L. Perrine

This paper describes a method of numerical computation for three-dimensional, unstable, miscible displacement behavior useful for heterogeneous systems, as well as for more ideal conditions. In the method, flow equations are first linearized by a perturbation approach. The basic flow process is separated and a solution for its behavior readily obtained. The remaining problem of deviations from the basic flow caused by non-ideal conditions is then subjected to numerical analysis. Results obtained from use of the method are also presented. Although conditions assumed in the test cal-culations were severe, results show the type of dispersing flow expected and appear quite satisfactory. The method has eliminated or reduced in importance problems of oscillating values near steep fronts, excessive computer smoothing, etc. A unique advantage of the method is that the source of variations from ideal behavior can be observed. ,The one serious drawback results from the algebraic complexity of the perturbation approach, and the need for second-order terms to be retained in calculations of interest. Fewer array points are available and more computer time is required than would be desired. However, these difficulties are also experienced with other approaches to the solution of three-dimensional dispIacement problems. INTRODUCTION Prediction of behavior of the miscible displacement process within a porous medium for any system of engineering importance is plagued by a number of difficulties. With typical fluid properties the displacing fluid has the lower viscosity, and there is a natural tendency toward flow instability. The problem of predicting instability is compounded by the fact that every real system is heterogeneous. Permeability will vary from point to point — not entirely systematically, and yet not in a random fashion leading to a readily defined average. Furthermore, permeability is unlikely to be isotropic. These permeability properties, which are characteristic of any real porous medium, accentuate the effects of flow instability. Another factor to be considered is that flow dispersion accompanies the displacement process in a porous medium. Mechanistically, dispersion is due to the fact that flow between any two points in the medium follows multiple tortuous paths, each characterized by slightly different flow properties. The fact that the coefficient characterizing dispersive properties of the real medium JS a tensor with variable elements complicates matters. Further difficulties arise because the parabolic influence, while not negligible, is small. Thus, there is a tendency toward steep and uneven displacement fronts along which dispersion smoothing must be represented accurately. Yet frequently used numerical analysis schemes may tend toward either instability, oscillation or excessive smoothing, none of which gives the desired accurate picture of flow behavior. Thus, while many experimental and analytical studies of the process have been made, predictions of actual performance are still subject to considerable uncertainty and possible improvement. This paper reports on part of a study which attempts to develop improved methods for solution of the flow equations describing the miscible displacement process. Of necessity, the calculations were performed on a large digital computer. A three-dimensional system is represented, and the coefficients defining dispersion and permeability can be varied in a manner representative of a real system. Because the differential equations are nonlinear, a first step is to linearize them using a perturbation approach. Objective of this approach has been to separate the basic flow which would occur in an ideal system and for which predictions are readily made. Then the numerical analysis, which is necessarily complex, is directed toward solution of the perturbation equations. These equations state how the basic flow is modified

Jan 1, 1967

By S. Floreen

Seven iron alloys ranging from 5 to 12 pct Ni and 5 to 14 pct Cr were studied. All alloys transformed to bcc massive martensites. Tempering increased the strengths , probably because of relief of residual stresses generated by the martensite transformation. The major strengthening mechanism appeared to be solid-solution hardening by nickel and chromium. Studies of the work-hardening behaviw, of the effects of prior austenite grain size, and of the effects of changing strain rate and test temperature gaue results very similar to iron or low-alloy steels. Increasing nickel contents markedly improved the toughness at subzero temperatures. Studies of the flow properties did not, however, indicate the reason for the beneficial effect of nickel on toughness. The marine atmosphere corrosion resistance of the alloys was improved primarily by chromium additions, but increasing nickel contents were also beneficial at low levels of chromium. J\ number of maraging and PH stainless steels are strengthened by precipitation hardening in a low-carbon Fe-Ni-Cr martensite matrix. To some extent the resultant properties of these steels must depend upon the properties of this matrix. The present study therefore was conducted to evaluate the transformation characteristics and mechanical properties of a series of Fe-Ni-Cr martensitic ternary alloys. A limited evaluation of the corrosion resistance of the alloys in marine atmosphere was also made. ALLOY PREPARATION Seven 100-lb air induction melts were prepared using electrolytic iron, nickel, and chromium metal additions. The initial Fe-Ni charge also contained 0.05 wt pct graphite to produce a carbon boil during melt down. After melting of the base charge, the heats were refined with 0.1 wt pct additions of manganese, silicon, aluminum and titanium and poured into cast-iron molds. The ingots were homogenized at 1250°C and uni-directionally hot-rolled to 2-in. plate. They were then homogenized another hour at 1250°C, and unidirection-ally hot-rolled to %-in. plate at a finishing temperature of approximately 1050°C. The compositions of the heats are given in Table I. Two additional heats were prepared as 40-lb vacuum-induction melts using electrolytic iron, nickel, and chromium metals, and commercially pure molybdenum chips. A carbon boil, and 0.1 wt pct additions of aluminum and titanium were again employed, but manganese and silicon were not added. The heats were converted to %-in. plate using the procedure described above. The compositions of these heats are included in Table I.

Jan 1, 1967

By P. Wynblatt, J. E. Dorn

The effect of strain rate, temperature, and interstitial impurity concentration on the flow stress was investigated in a poly crystalline Fe-2 pct Mn alloy. The temperature dependence of the flow stress was found to be independent of the interstitial impurity concentration, removal of interstitials merely decreasing the atherma1 stress level. Below 160%, the large temperature dependence of the flow stress was interpreted in terms of the Dorn-Rajnak theory of the Peierls mechanism of plastic deformation. Above 160"K, some other thermally activated intrinsic meckanisln seems to be operating. The strong temperature dependence of the flow stress of bcc iron at low temperatures has been studied by numerous investigators and interpreted in terms of several different thermally activated dislocation mechanisms. The following mechanisms have been proposed: a) interaction of dislocations with interstitial impurity atoms1 or with solute atoms in general; b) interaction of dislocations with clusters of impurity atoms;3 c) resistance to the motion of dislocations due to jogs on screw dislocations;* d) resistance to the motion of dislocations due to the Snoeck effect;&apos; and e) interaction of dislocations with the intrinsic resistance of the bcc lattice or Peierls "hills". In previous work: it was found that the plastic behavior of polycrystalline iron containing 2 wt pct Mn (and 100 ppm C + N) is in good agreement with predictions based on the Peierls mechanismlo from 77" to 160°K whereas from 160" to about 370°K another as yet unidentified thermally activated mechanism is operative. The purpose of the present investigation was to determine the effect of interstitial impurities on the temperature dependence of the flow stress, by purifying the previously investigated alloy with respect to interstitial impurities. The investigation revealed that removal of the interstitial impurities to a level that eliminated Cottrell locking and the Portevin-LeChatelier effect (i.e., serrations in the stress-strain curve due to dynamic strain aging) affects neither the strong temperature dependence of the flow stress at low temperatures nor the general characteristics of the higher-temperature behavior. Such purification, however, lowered the athermal yield stress. I) EXPERIMENTAL PROCEDURE AND RESULTS The material used in this investigation consisted of an Fe-2 wt pct Mn alloy having the following additional elements present: 0.004 pct C, 0.006 pct N, 0.05 pct 0, 0.004 pct S, 0.003 pct P, and 0.001 pct Si. This was the same material as that studied in the previous investigation and will henceforth be referred to as the "impure material". The as received -jr by 2 in. hot-rolled bars were cold-rolled to 0.08-in. thickness, recrys-tallized under argon for 30 min at 80O0C, and further cold-rolled to 0.053-in. thickness. Flat tensile specimens 3 in. wide having a 1.625-in.-long gage section were machined from the sheet and then purified. The first stage of purification consisted of holding the specimens at 850°C for 24 hr in a stream of hydrogen saturated with water vapor at room temperature. Material prepared in this fashion will subsequently be referred to as "wet hydrogen purified material". It has been estimated that this type of treatment reduces the carbon content of iron to less than 5 ppm.&apos; The second stage of purification consisted of holding the specimens in a closed system through which hydrogen was circulated past the heated specimens as well as a zirconium hydride getter. The specimens were held at 850°C and the getter at 800°C. The process was continued for 212 hr. The starting material for this process was wet hydrogen purified material. Material prepared in this manner will be referred to as "ZrHz purified material". The technique used was substantially the same as that described by Stein et al.&apos; who have shown that the carbon level at the end of the process is reduced to about 5 parts per billion. The mean grain size of the three materials was found to be -60 C( for the impure material and -160p for the wet hydrogen and ZrHz purified materials. All tensile testing was carried out on an Instron Testing Machine either in controlled-temperature baths or at fixed-point baths such as boiling liquid nitrogen, and so forth. When fixed points were used the temperature was kept constant to better than *1°C whereas in all other tests the temperature variation was less than *2°C. Test of Purity. It was not possible to determine the purity achieved at each stage of the purification because the resulting level of interstitial impurities was near or below the limit of sensitivity of standard analytical techniques. It was possible, however, to obtain a qualitative measure of the extent of purification from the appearance of the stress-strain curves for the three materials. Fig. 1 shows the stress-strain curves for the three different materials tested at 300°K. It can be seen that the effect of wet hydrogen

Jan 1, 1967

By John W. Burd

A system is described for the simultaneous deposition of epitaxial layers on as many as eight substrates. A high degree of uniformity of both physical and electrical characteristics is achieved in the films. Variation of film thicknesses is consistently less than ±10pct within a wafer and from wafer to wafer within a run with the variation typically on the order of 55 pct. Composition variation of GaAs1-x PX layers within a wafer and from wafer to wafer within a run is consistently less than 51 pct. Electrical evaluation of the films by several techniques indicates excellent doping uniformity within a wafer and from wafer to wafer within a run. Mobilities for lightly doped GaAs films at 300°K are consistently >6000 cm2 v-1 sec-1 and mobilities > 7000 cm2 v- 1 sec-1 are regularly attainable. Techniques for the preparation of material with carrier concentrations from 1 x 1015cm-3 to 1 x 1019 cm-3 n-type and 5 x 1016 to 5 x 1018 cm-3 p-type are discussed. METHODS for the preparation of 111-V compounds by vapor phase reactions have been extensively reported in the literature.1-6 Almost all of the apparatus described for these various methods are suitable for processing one or at the most a very limited number of wafers simultaneously. With the recent rapid advances in the use of vapor grown GaAs for microwave oscillators and GaAs1-xPx as visible light emitters the requirements for these materials are steadily increasing. In order to satisfy these requirements it is necessary to move from a laboratory scale apparatus to one which is capable of processing a large number of wafers simultaneously. Desirable features would be a high degree of uniformity among the wafers and good reproducibility from run to run. The apparatus to be described fulfills these requirements very well. DISCUSSION The various methods reported in the literature can be classified under three headings: 1) closed tube, 2) open tube, and 3) the close-spaced method. Of these three the open-tube method is the most amenable for scale-up to a manufacturing process. It is the most versatile and the various operating conditions can be more precisely controlled than with the other two methods. A number of chemical reactions may be used to achieve vapor-phase growth of 111-V compounds. Sev-era1 of the more generally used reactions are shown in Fig. 1. All of these reactions have the following points in common: 1) generation of a volatile group III(Ga) species by the reaction of the transport agent (halide or HC1) with either Ga or GaAs, 2) introduction of the Group V(As and/or PI component, 3) a method of adding dopant, if desired, and 4) a region in which deposition from the vapor will occur and form as a single crystal epitaxial film on the substrates. The laboratory scale reactors permit the hot re-actant gases to flow into the relatively cooler deposition zone and pass successively over the several substrates which are arrayed along the long axis of the tube parallel to the gas flow. With this arrangement the composition of the reactant stream is continually changing as solid material is deposited on each successive substrate. As a result of this changing gas composition the reaction driving force also changes from substrate to substrate and the degree of uniformity of layer thickness, doping level, and so forth, is poor. This effect can be partially overcome by imposing a controlled temperature gradient along the deposition region to compensate for change in gas composition. However, even when this is done variations in layer thickness on the order of 30 to 40 pct are common and as high as 50 pct are frequently experienced between adjacent wafers in the tube. To expand this arrangement to a large number of wafers would only increase the nonuniformity from the first to last wafer in the line. From the above discussion the two undesirable features of changing gas composition and temperature gradient become evident. A reactor system which eliminates or minimizes these undesirable features is one in which the apparatus is mounted vertically as shown schematically in Fig. 2. The vertical mounting permits the disposition of a number of substrates on a suitable support so that all wafers are at the same vertical height in the furnace and hence at essentially the same temperature. By using only a single row of wafers the reactant gas mixture passes over only one substrate in its path through the reactor. Thus the two undesirable features of changing gas composition and temperature gradient are minimized. An additional design feature which further minimizes temperature variations is rotation of the substrate holder. Rotation serves to integrate any radial temperature gradient existing around the resistance heated furnace. A photograph of a reactor assembly at the completion of a run is shown in Fig. 3. MATERIAL PREPARATION Apparatus. Although any of the several chemical systems shown in Fig. 1 are adaptable for use in this apparatus the one generally used is System 2, the hydride synthesis system. This system has been de-

Jan 1, 1970

By G. Ansel, J. P. Doan

THE important literature concerning zirconium in magnesium-base alloys is predominantly contained in patent references. Sauerwald, Eisenreich, and Holub1-4 discovered the profound grain-refining influence of small amounts of zirconium on cast magnesium and the attendant increases in strength, and ductility. They extended their work to reveal that limited amounts of certain other elements, including zinc, could be added for further improvement in strength and hardness. British. Patent 5111376 relates to the parent discoveries of Sauerwald, Eisen¬reich, and Holub. All of these references deal primarily with casting characteristics and properties in the cast state. Minor mention is made of desirable tensile strength, ductility, and toughness of wrought Mg-Zr alloys* modified by one or more additional elements. No extensive reference in the literature" has been found to the particular characteristics of wrought Mg-Zn-Zr alloys, with which the present paper is concerned. - The work to be discussed represents essentially an extrusion study of the Mg-Zn-Zr alloys and indicates that this system is highly interesting in the wrought state both academically and commercially. Accordingly, an important aim of this paper is to describe the hot-workability, tension and compression properties, metal¬lography, and toughness of these alloys. Compositional variations are limited to the ranges o to 7 per cent Zn and o to I per cent Zr. EXPERIMENTAL PROCEDURE Alloying and Casting Alloying ingredients were cell mag¬nesium, commercial zinc (intermediate grade), and a chloride salt containing approximately 50 per cent ZrCl2 and 50 per cent alkali chlorides. This salt is produced by Titanium Alloy Manu¬facturing Company. Melting, alloying, and pouring procedure essentially followed the crucible process as described by Nelson.6 The magnesium was melted using Dow No. 310 flux, and the temperature raised to 1350° to 1400°F for the alloying operations. After alloying of the zinc, the zirconium containing salt was added in small portions with vigorous stirring. This is an adaptation of the method described in British Patent 533264.7 The alloying efficiency of zir¬conium was approximately 30 per cent. During the alloying of zirconium, fluorspar was added in amount required as a flux¬inspissating agent. Next the melt was refined with Dow No. 310 flux and held quietly for 15 min. Finally billets were cast in a book-type permanent mold

Jan 1, 1946

By L. H. Robinson

Triaxial compression tests have been performed to determine the strength characteristics of limestone, sand-stone and shale rocks subjected to controlled stress conditions. This control tuns exercised by varying the liquid pressures within and around a plastic-encased rock specimen. The pressure in the pores of the rock was varied throughout the range from atmospheric to 15,000 psig; the external pressure was changed over the same range with various positive pressure differences between is and the intertnal pressure. The data show that the rock strength increased and the mode of failure changed as the pressuire. surrounding the rock became greater than the pressure in the pores of the rock. These observations and the resu1ts of microbit drilling experiments indicate that the increased rock strength under pressure may bc an important effect in reducing drilling rare, but that other factors are probably of even greater importance. INTRODUCTION A large part of the research conductcd to reducc thc cost of drilling is directed toward improving present drilling technology and dcveloping new drilling methods. In spite of the fact that drilling is essentiaIly the act of making rocks fail, many details of the mechanism of failure are not known. It seems probable, therefore, that continuing studies of the fundamentals of rock failure can lay a foundation for future improvements in drilling technology. One of the factors which affects rock failure is the stress applied to the rock. This effect has been known for many years.&apos;.&apos;.; As an example, stress studics have been published by engineers&apos; concerned with the strength characteristics of concrete in large dams. More recently, a number of investigators4-12 have explored the effects of stress on the strength of geologic formations and the geologic implications of their findings. During the last few years some research&apos;" on rock strengths has also been conductcd in an attempt to gain additional insight into the factors which affeet rock drillability. In detcrmining the strength characteristics of rocks under different stress conditions, investigators have conventionally used triaxial compression equipment. wherein a jacketed rock cylinder is uniformly loaded from all directions and then compressed longitudinally. The results of this work have demonstrated that the mode of failure (brittle or malleable) is dependent upon the loading pressure, and that the strength of the rock increases as the loading pressure increases. These results clearly manifest that the stress, which is determined by the loading pressure, affects rock strength, and this implies that rocks under stress should be stronger and hence harder to drill. During the drilling of a porous rock the stress conditions are determined not only by the pressure surrounding the portion of the rock undergoing failure (confining pressure) but also by the pressure of the interstitial fluids within the rock (pore pressure). The importancc of both these pressures on the drilling rate of rocks has already been demonstrated by a number of investigators. Murray and Cunningham" found in microbit drilling expcriments that at constant pore pressures the drilling ratc decreased as the hydrostatic pressure surrounding an unjacketed, impermeable rock increased. Later Eckel" found that for jacketed Iimestone specimens the differcnce between hydrostatic (wellbore) pressure and formation (pore) pressure had an important effect on drilling rate. These observations of the effect of pressure on drilling rate emphasize that for drilling studies triaxial compression tests should be conducted under conditions of confining and pore pressure which simulate conditions underground. In the past, triaxial tests have been made under conditions which do not reproduce those underground. In particular, most of the tests on porous materials have keen made at varying confining pressures but with atmospheric pore pressures. In only one group of tests&apos; was any data on the effect of pore pressurc reported, and these few data were on materials not representiltive of those encountered in drilling earth formations. The research described herein was initiated to deter-mine the importance of both internal pore pressure and confining pressure on failure characteristics of limestone. sandstone and shales. Triaxial loading equipment was used to obtain strength data at pressures up to 15,000 psig. An additional objective of this research was to apply these results to drilling rate studies by comparing them with the previously published drilling data of Murray and Cunningham" and of Eckel12. The work reported here is but one step in determining and evaluating the fundamental mechanisms which control drilling rate. Additional research is needed to clarify other aspects of the drilling process. The better

By F. J. Schuh

The drilling industry long has been plagued by failures in the bottom few joints of surface and intermediate casing strings. This paper presents an analysis of the various possible causes of failure and concludes that failures are caused by short-lived, high-energy torque impulses delivered from the drill string through the bit while drilling out the cementing plugs, cement and floating equipment. The magnitude of these torque impulses is shown to be a function of the rotational momentum of the drill string, and a method is derived to calculate the magnitude of these impulses. The available methods of strengthening the bottom joints are reviewed. It is concluded that, while present methods are ineffective, a combination of improved procedures for strengthening and minor restrictions on drillout practices will prevent failures. Introduction In most cases, failure in the bottom few joints of casing strings is not discovered until electric logs record that the bottom one, two or three joints have parted from the casing string and slipped down the hole. However, in some cases the parted section of casing uncovers a high-pressure or lost circulation zone, or shifts laterally restricting the passage of drilling equipment. In these instances extensive remedial work is required to realign the parted pieces and seal the exposed formations. Several methods used to strengthen the bottom joints of casing strings include locking set screws in the couplings, putting wedges in special collars, welding straps across the couplings, welding the couplings and, most recently, using epoxy resin-based, thread-locking compounds. Since none of these techniques has eliminated the problem, this study was initiated to find the cause of failures and to evaluate the available methods of prevention. Mechanics of Casing Failures An analysis of the various possible causes of failure indicates that the casing is unscrewed rather than broken and that therefore failure must occur before the shoe is drilled. Since there is no general agreement as to the causes of casing failure, some possible mechanisms were ATLANTIC RICHFIELD CO. DALLAS, TEX. considered in this analysis. Failure of the bottom joints of casing can occur by only one of three types of stress: tension, torsion or bending. The possible mechanisms of failure were evaluated by determining the forces required to cause casing failure by each of the stresses; and, where applicable, the possibility of failure by fatigue was considered. For casing to part under tension requires a downward load of more than the tensile strength of the casing. The lightest API weight H-40 grade casing requires a bit load on the bottom of the casing of 27,000 to 34,000 Ib per inch of bit diameter (Table 1). Since maximum drill collar weights seldom exceed 10,000 Ib per inch of bit diameter, it is apparent that casing strings cannot be parted by the downward load of the drill string. The second mechanism considered was failure by bending. This mechanism requires that the lowermost casing joints be free to be deflected laterally until the bending stress exceeds the strength of the pipe. To fail, the casing (at a height L above the shoe) requires a force and deflection&apos; at the shoe of To deflect the casing shoe with the drill string obviously requires a dog-leg at the casing shoe. This dog-leg must have a rate of change equal to or greater than the change in curvature of the deflected casing, which is given by

Jan 1, 1969

By J. W. Freeman, E. E. Reynolds, A. E. White

Fram a study of 63 systematic alloy modifications it was found that molybdenum, tungsten, and columbium, added individually or simultaneously, and increases in chromium cause major improvements in 1200°F rupture strengths of Cr-Ni-Co-Fe base alloys. Rupture strengths were a function of the effect of composition modifications on both the inherent creep resistance and the amount of deformation the alloy would tolerate before fracture. THIS paper describes the results of an investigation of a series of alloys with systematic variations of the chemical composition of the following basic alloy: C, 0.15: Mn, 1.7; Si, 0.5; Cr, 20.0; NI, 20.0: Co, 20.0: Mo, 3.0; W, 2.0; Cb, 1.0; N, 0.12; Fe, 32.0 pct. The 62 modifications of this alloy were produced under conditions which minimized all factors influencing properties at high temperatures except composition. Melting, fabrication, and heat treatment were carefully maintained constant. Stress-rupture properties at 1200°F were used as the primary criteria of evaluation of the alloy. The objective of the study was to obtain data for determining the fundamental role of the influence of alloying elements on properties of heat-resistant alloys at high temperatures. In addition the results should be useful in determining optimum chemical compositions, the sensitivity of properties to variations in composition, and the degree to which alloy content could be reduced while retaining worthwhile properties. It is difficult or impossible to develop correlations between properties at high temperatures and systematic variations in chemical composition from published data for wrought heat-resistant alloys developed for gas turbines.&apos; &apos; The main reason for this is the extreme dependence of the properties on conditions of treatment of the alloys." In most cases variation in final treatments between alloys so influences the properties that the influence of chemical composition is obscured. In addition it is recognized Table I. Basic Alloy and Some Modifications Used Basic AllOy, Variations in Element Pct Composition, Pct C 0.15 0.08. 0.40. 0.60 Mn 1.1 0.03,0.25.0.50,1.0,2.5 S1 0.50 1.2, 1.6 Cr 20.0 10, 30 Ni 20.0 0, 10,30 Co 20.0 0. 10, 30 MO 3.0 0. 1.2.3, 5, 7 W 2.0 0, 1, 5, 1 Cb 1.0 0.2,4,6 N 0.12 0.004, 0.08, 0.18 Fe 32.0 that variations exist between heats of the same alloy which are related to melting practice and that there is a strong possibility that conditions of hot working influence response to final treatments. The development of heat-resistant alloys has been based on the gradual accumulation of data roughly related to composition from extensive testing programs. There is every reason to believe that in most cases the optimum compositions have been achieved by this procedure in the alloys commercially available. There are, however, very little data showing the influence of systematic variations of composition free from the influence of other factors, particularly for alloys of the type investigated. Several investigators of cast alloys have demonstrated compositional effects, notably Grant,1-6 Epremian,t Guy,8 and Harder and Gow.9 Sykes10 eviewed the work on the wrought alloy Rex 78 and the systematic variations of carbon, copper, molybdenum, and cobalt leading to the development of the stronger Rex 337A alloy. From the papers by Wilson11 and Henry12 it is possible to deduce the beneficial effect of substituting cobalt for iron in 0.45 pct C-20 pct Cr-20 pct Ni-4 pct Mo-4 pct W- 4 pct Cb alloys. Wilson mentioned but did not present the extensive compositional studies involved in developing these alloys. Binder" showed optimum properties for 3, 2, and I pct, respectively, for molybdenum, tungsten, and columbium in 20 pct Cr-20 pct Ni-20 pct Co-30 pct Fe alloys for limited systematic variations of these

Jan 1, 1953

1. What Is a Rock Burst? . . . . 569 Jack Spalding . . 569 A. F. Robertson . 569 W. R. Crane . 569 G. S. Rice......569 P. J. Shenon........... 569 L. C. Graton........... 569 2. What Are the Causes of Rock Bursts? 573 Jack Spalding..........573 A. B. Yates and P. J. Shenon 574, 578, 592, 596 A. F. Robertson . . . . . 575, 595 W. R. Crane. ... 579 G. S. Rice.........582 Oscar Weiss .........582 P. B. Bucky..........582 P. H. Bird.....588, 592, 593, 595 M. K. Hubbert.........593 G. Wheeler.......... .593 B. F. Tillson........593, 595 T. T. Read............594 3. How Can Rock Bursts Be Prevented?. 597 Jack Spalding..........597 A. B. Yates and P. J. Shenon ... 598 A. F. Robertson.......599 W. R. Crane....... .602 G. S. Rice............602 Page 4. How Can Rock Bursts Be Predicted?. 602 Jack Spalding.........602 A. F. Robertson.......602, 603 A. B. Yates and P. J. Shenon ... 602 W. R. Crane......602 G. S. Rice......602 B. F. Tillson...........603 5. How Can Rock Bursts Be Controlled? 603 Jack Spalding..........603 A. F. Robertson.......603 W. R. Crane...........604 A. B. Yates and P. J. Shenon 604 Oscar Weiss........605 G. S. Rice......- 604, 609 R.D.Hoffman..609, 610 R. D. Hall..........609 R. H. Cromwell . . 609 P. J. Shenon...........609 P. B. Bucky......609, 611 B. F. Tillson.........609, 611 A. B. Yates...610, 611 P. H. Bird.......610 6. General Discussion........ 611 Jack Spalding.......... 611 R. D. Parker....... . 616 C. Baring Horwood........ 618 P. B. Bucky........... 619 Foreword This symposium brings together points of view, experiences and ideas on rock bursts from a goodly portion of the globe. Some conceptions, particularly those regarding the necessity of depth, have been fairly well shattered, as we find that they are present in the water tunnels of New York, on the surface at marble quarries in Vermont, and in the coal mines of the United States, as well as in the deep mines of the South African and Kolar gold fields, and in the nickel, copper and gold mines of Canada. Their occurrence under such a variety of conditions is, therefore, a challenge, which, if successfully met and overcome,

Jan 1, 1946

By W. L. Dennen, W. W. Wirth

Research looking toward the reduction of the cost of roof support by substitution of longer-life materials for wooden timber is fully justified by the fact that roof support is an important element of all production costs. Permanent or semipermanent roof support will reduce the expense of timber-maintenance crews during steady operations, but even more markedly during idle periods. The management, therefore, is faced with the important problem of timber renewals, which in times of regular operation are frequently obscured by more urgent problems of production. Increased use of timber in the Anthracite Region of Pennsylvania is caused mainly by increased percentage of coal obtained from robbing areas, which requires more timber for safety than development work, and maintenance of long haulageways through crushed ground despite the fact that less coal is transported over them. The timber reserve in the immediate vicinity of the mines has been depleted to such an extent that it is necessary to secure 70 per cent of the timber requirements from distant sources. Originally, mine timbering in this region was done by largely utilizing round props or legs with round collars. The whole cross section of the tree from which timber was cut was utilized by forming the joints between the legs and the collars with saw and adze, using plank or round saplings for lagging behind the legs and over the collars to prevent material falling between them. The Mine Inspectors&apos; report of 1898 records an important digression from the use of round timber, when two tunnels at the Babylon colliery, near Pittston, Pa., were timbered with 12 by 12-in. square timber sets with mud sills, through quicksand for distances of 425 and 160 ft., respectively. The timbers were lagged with 3-in. plank to control sand. An early step toward the permanent type of roof support was the installation of "brick pillars or perfect arched brick rooms" instead of

Jan 1, 1940

By A. T. Chatas

A description of the geometrical characteristics of spherical reservoir systems, a discussion of unsteady-state flow of such systems and examples of engineering applications are presented as backgmund material. The fundamental differential equation, a description of average spherical permeability and the introduction of the Laplace transformation serve as theoretical foundations. Engineering concepts are investigated to indicate particular solutions of interest, which are analytically obtained with the aid of the Laplace transform. These are numerically evaluated by computer, and presented in tabular form. INTRODUCTION A tractable mathematical analysis of unsteady fluid flow through porous media generally requires incorporation of a geometrical symmetry. The simplest forms include the linear, cylindrical (radial) and spherical. Most analytical endeavors have concentrated on cylindrical symmetry because it occurs more often in petroleum reservoirs. Nevertheless, some reservoir systems do exist that are better approximated by spherical geometry. Review of technical literature revealed but a single reference to unsteady spherical flow in petroleum reservoirs.l The motive and purpose of the present work was to remove this gap in technical information, and to provide the practicing engineer with some useful analytical tools. The mathematical details associated with the particular solutions of interest involved use of the Laplace transformation. Hurst and van Everdingen previously demonstrated the efficacy of this operational technique, and in many respects the present treatment was patterned after their earlier work.2 PRELIMINARY CONSIDERATIONS GEOMETRICAL CHARACTERISTICS Geometrically, a spherical reservoir system is defined at any instant of time by two concentric hemispheres whose physical properties of interest vary only with the radial distance. Every physical property is thus restricted to be a space function of only one variable: the distance along a radius vector emanating from the center. Such a system is composed of an outer region and an inner region, separated by a defined internal boundary. The inner region simply extends inward from this boundary, whereas the outer region extends outward from it to an external boundary. The position of the internal boundary is presumed fixed, so that the size of the inner region remains constant. On the other hand, the position of the external boundary at any given instant of time is determined by the distance into the system that a sensible pressure reaction has occurred, Thus, the external boundary may change position with time. It initially emerges from the inner region and advances outward to its ultimate position. When this ultimate position coincides with a geometric limit, the reservoir system is said to be limited. When it coincides with points subject to pressure gradients furthest removed from the internal boundary, yet short of a geometric limit, the system is said to be unlimited. In this investigation two different boundary conditions are imposed at the ultimate boundaries of limited systems. The first requires that no fluid flow occur across this boundary; the second that the pressure remain fixed at this boundary.3-5 UNSTEADY-STATE FLOW In a strict sense virtually all flow phenomena associated with a reservoir system are unsteady-state. The transient behavior of these phenomena requires accounting, however, only when time must be introduced as an explicit variable. Otherwise, steady-state mechanics may be used. Analytically, steady-state conditions prevail in a reservoir system only over that portion of its history when this relation is satisfied:

Jan 1, 1967

By Ronald K. Linde

Metastable Ag-Cu solid solutions at two compositions beyond the maximum limits of solubility obtainable by quenching from the solid state were obtained by rapid quenching from the liquid state. The process of transformation of the metastable solid solutions into the equilibrium phases was studied by means of X-ray diffraction intensity measurements and electrical-resistance measurements; metallographic examination was also performed. Results are compared with those for an alloy quenched from the solid state at a composition which exists as a solid solution at elevated temperatures. Activation energies for the trans-formation were computed to be 33,600 * 2500 and 33,100 * 2000 cal per g mole for the 60.1 and 75.0 at. pct Ag;Cu compositions, respectively THE kinetics of precipitation in supersaturated solid solutions obtained by quenching from high temperature has been thoroughly studied in many alloys, and detailed investigations of the early stages of nucleation and subsequent growth of the equilibrium phases have been carried out. All of these studies have been made on alloys quenched from the solid state, however, and it is the purpose of this paper to present some of the results on the kinetics of transformation of metastable solid solutions in Ag-Cu binary alloys whose compositions lie outside of the solid-state limits of solubility. Limits of solubility in the solid state can be increased by rapid quenching from the liquid state. This was first demonstrated by Falkenhagen and Hofmann, who obtained appreciable increases in solubility limits of the elements of the first transition series in aluminum by rapid cooling of liquid alloys through contact with a copper mold maintained at liquid nitrogen temperature.&apos; The same basic idea of cooling a liquid alloy by conduction onto a substrate rather than by convection of a gas or liquid (conventional quenching) has been recently revived and extended to very high rates of cooling by Duwez and his collaborators. The new technique was first applied to Ag-Cu alloys because the existence of a eutectic in this system is not predicted by the Hume-Rothery rules of alloy phase formation. Rapid quenching from the liquid state resulted in metastable solid solutions at all concentrations. The kinetics of decomposition of these metastable solid solutions containing 60.1 at. pct Ag;Cu (eutectic composition) and 75.0 at. pct Ag;Cu is the subject of the present paper. EXPERIMENTAL TECHNIQUES Alloys were made in 10- to 20-g heats using silver of purity 99.99 pet and copper of purity >99.999 pct. Components were weighed accurately to 0.1 mg and melted by induction heating in an alumina crucible under an atmosphere of hydrogen. Weight losses amounted to less than 0.02 ~ct in all cases. Rapid cooling from the liquid state was achieved in an apparatus of the type described by Pietrokowsky. 3 In this technique a freely falling drop of molten alloy is caught between a stationary anvil and a fast moving piston, both anvil and piston being lined with copper. The resulting foils were approximately circular (about 2 cm in diam) and from about 50 to 150 u in thickness, depending on the pressure driving the piston. Metallographic samples were prepared for polishing by edge-mounting foils in Quickmount. The mostef-fective etching procedure was found to be: 10 parts NH4OH (concentrated), 1 part H2O2 (30 pct), 5 parts H2O, swab for 5 to 10 sec. The transformation of the metastable alloys to equilibrium was followed by X-ray diffraction and electrical-resistivity measurements. The peak intensity and the integrated intensity of suitable Bragg reflections of the metastable and stable solid solutions were studied with a Norelco dif-fractometer, using nickel-filtered copper KO radiation. The peaks were step-scanned at intervals of 0.05 deg. Using either a Kelvin bridge or a null circuit with a Leeds and Northrup K-2 potentiometer, the changes in electrical resistance due to phase transformation were measured for specimens cut into strips about 20 mm long and 4 mm wide. All resistivity measurements were carried out at liquid-nitrogen temperature. The isothermal heat treatment was accomplished by sealing the samples in argon-filled aluminum containers with stainless-steel O-rings. Containers were then suspended in wax baths with temperatures in the

Jan 1, 1967

By W. V. Green

Creep of tantalum was measured at temperatures from 0.6 to 0.89 of the absolute melting temperature. The creep curves include first, second, and third stages. Steady-state creep rate depends on the fourth power of stress. The activation energy for creep throughout this temperature range is approximately 114 kcal per mole, measured by the aT technique. Subgrain formation occurs as a result of creep strain, and pile-up dislocation arrays are observed in etch-pit patterns. BECAUSE of its high melting point-which is exceeded only by those of rhenium and tungsten—and its high room-temperature ductility compared to most of the other high-melting-point metals, tantalum will undoubtedly be utilized in an increasing number of high-temperature applications. Alloying studies directed toward increased high-temperature strength must use data on tantalum itself as a base line in order to evaluate the effectiveness of the alloying additions. However, to date, no systematic study of creep of tantalum at temperatures above one-half of its melting point has been reported in the literature. Conway, Salyards, McCullough, and Flagella1 have measured linear creep rate of tantalum sheet as a function of stress, but at only one temperature, 2600°C. This paper describes a relatively thorough study of the high-temperature creep of tantalum. METHOD Material Tested. The commercially supplied, l/2-innch-diameter tantalum rod used for this work was electron-beam-melted, cold-forged, rolled, swaged, cleaned chemically, and vacuum-annealed for 1 hr at 1000°C, all by its manufacturer. The vendor&apos;s analysis included 60 to 170 ppm C, 3.4 to 4.2 ppm H, 60 to 80 ppm 0, 15 ppm N, and a hardness ranging from 66 to 81 Bhn and averaging 76 Bhn. Creep eimens Used. Two creep-tested specimens are shown in Fig. 1. The 1/4 in.-diameter gage section was 3/4 to 1 in. long, and terminated either at shoulders 5 mils high or at 20-mil-diameter tantalum wires spot-welded to the circumference of the gage section. Both kinds of shoulders served equally well as fiducial marks for optical strain measurements. The spot welding did not alter the creep behavior in any detectable way; the 5-mil- high sharp shoulders did not result in any detectable localized effect on the strain. Before testing, each tensile bar was first mechanically polished -id then electrochemically polished according to the method referred to by Forgeng2 as the "Thompson Ramo Woolridge" method, which was suitable for tantalum after small adjustments of technique were made. Two tensile bars tested at low stresses had 1/8-in.-diameter gage sections and utilized only the weight of the bottom grip for the applied load. Although these diameters were smaller than were desired for other reasons, applied loads were known with high precision in the tests in which they were used. Testing Procedure. Two different constant-load creep-testing machines were employed, one of which has been described by Smith, Olson, and Brown.3 In both, the tensile bar is held vertically on the axis of a cylindrical tungsten tube or screen heater by threaded tungsten grips. The tensile bars and associated grips are heated by radiation from the incandescent heaters, which are heated by their own electrical resistance. Both testing machines use pins to hold the bottom grips in place. The load is applied to a tensile bar through hanging weights, a constant force-multiplication lever, a pull rod sealed to the chamber lid, and a top grip threaded to the pull rod at one end and to the tensile bar at the other. In one machine, the vacuum seal is a bellows with a low spring constant; in the other, the seal involves a rotating "0 ring". With the latter, rotation is converted to translation with a crank shaft, so that elongation of the tensile bar is accommodated with no change of tensile load. The incandescent tensile bar is viewed by an external optical system through slots in the radiation shields and heater, and an enlarged image is projected on a ground-glass screen. Gage-length measurements are made on this image with cathetometers on traveling microscopes. With regard to creep-test results, the two machines were identical. Thorium oxide coatings were applied to the threaded ends of the tensile bars, to prevent diffusion welding of the tensile bars to the grips during testing. Specimen temperatures were measured with an L. & N. optical pyrometer which had been calibrated against a standard carbon arc, and were corrected fir window absorption by calculation from the measured spectral transmittance of the quartz observation windows. Longitudinal temperature gradients in the tensile-bar gage length and temperature drifts during testing were detectable but small, and were estimated to be 10°C or less. Accuracy of temperature measurement was confirmed by comparing the temperature measured on the surface of a special

Jan 1, 1965

By M. P. Tixier, F. Segesman

Explanations bused on theory and laboratory tests tire offered for certain unusual features of SP logs which may befog their interpretation, namely the "sawtooth" SP and the reduction or increase of SP with time. The sawtooth SP is frequently seen in SP recordings of thick, very permeable watcr. sands of the Louisiana Gulf Coast. Using SP data from a resistor network analog, this anomaly is explained on the basis of a thin shale streak within the sand. under which the invading filtrate accumulates by gravity segregcitiorr. The electromotive force then appearing across the shale streak gives rise to the anomalous SP. Reduction of the SP on successive logging runs Ira often been observed in very permeable sands when as indicated by the resistivity curves, the invasion depth has been reduced to practically zero. Laboratory results verify that this phenomenon may be due, to the presence of air electromotive force, across the mod rake when the fluids on either side differ in activity. Also, there is, in some cases; an increase of SP deflection on successive logging runs, because the emf initially present across the mud cake disappears as the somewhat saline water just behind the mud cake is progressively flushed out by the invading filtrate.. Field example and laboratory data are presented. I N T R ODUCT1ON Some unusual features are frequently observed on certain SP logs which make interpretation difficult. The purpose of this paper is to offer explanations of several cases of interest. All of these arc related to the conditions of invasion. The cases to be discussed are as follows. 1. The sawtooth SP anomaly which is frequently seen within the thick, highly permeable saltwater sands of the Louisiuana Gulf Coast 1. Reduction of the SP deflection from the usual sand line in very permeable sections when the depth of invasion is practically nil. As will be explained, such a reduction is attributable to a membrane electromotive force across the mud cake. 3. An increase of the SP with time just after the iormation is drilled as a result of progressive flushing of the invaded zone. FUNDAMENTALS OF SP PHENOMENA An explanation of SP phenomena must begin with the following basic ideas. 1. The SP log derives its character from ohmic potential differences in the hole produced by currents flowing through the mud.&apos; These currents are driven by electromotive forces which are primarily electrochemical in origin. Other possible types of SP-producing electromotive forces may be disregarded for the purposes of this paper. 2. The electrochemical emf&apos;s associated with permeable formations are now understood to consist of liquid-junction emf&apos;s and membrane emf&apos;s.&apos;,&apos; As schematically shown by thc battery symbols in Fig. 1, the liquid-junction emf, E,,,, exists at the contact between waters of different chemical activities, a,,,, (mud filtrate) and tr,,. (formation water); the shale membrane emf, lS.sn. exists across the adjacent shales whcn they separate waters of different activities. The emf&apos;s just cited are additivc in producing SP currents (arrowed circles of Fig. I). Thus, neglecting for the moment any possible membrane emf across thc mud cake, the total electrochemical emf, E,, will be given by their sum, where K,., -! K,q,, = 12 + 59, or 71 at 75 °F. In the log interpretations the SP of a thick sand (i.e.. the static SP) is generally related to the activities of the filtrate and formation water through Eq. 1. by setting the static SP equal to - E,.

By C. Cronquist

Since April, 1962, Shell Oil Co. has operated a peripheral line-drive waterflood of the 10.750-ft lower Tuscaloosa (Cretaceous) Denkman sand in the Little Creek field. Located in southwestern Mississippi in the lower Tuscaloosa trend, the field was discovered by Shell in Jan., 1958. Among the largest in the trend, the accumulation is controlled stratigraphically and occurs in an extensive series of alluvial-point bar deposits across a nose that dips gently to the south. The crude oil is 39" API gravity and was highly undersaturated at initial conditions. Early production behavior indicated a depletion drive with slight water influx; primary recovery wm estimated to be 25 million bbl, or 24.5 percent of stock-tank oil originally in place. A.s a result of a favorable mobility ratio and remarkably uniform rock properties, the volumetric sweep eficiency in the waterflood has exceeded 90 percent. Despite the high connate water saturation (56 percent), the displacement efficiency by water injection has been quite efficient, contrary to traditional concepts. Based on observed field flood-out performance, ultimate recovery is calculated to be 46 million bbl. As anticipated, the production rate began declining during 1964 due to a continu ing reducrion in the number of producing wells as flood fronts advanced across the field. Cumulative recovery as of Jan., 1968, was 44.8 million bbl; waterflood operations ~hould be complete by 1970. Introduction Most waterfloods described in reservoir engineering literature involve pattern operations, the most common of which is the five-spot pattern. Only occasiona&apos;lly are linear drives described, even though there probably are increasing numbers being put into operation. Increasing use of linear floods may reflect the accelerating trend towards early application of fluid-injection programs when linear drives are more efficient, as was the case at Little Creek. However. the Little Creek operation is unusual in several respects. It is one of a few successful waterfloods conducted in sands with connate water saturations approaching 60 percent, and it is among the deepest successful water-floods being operated anywhere. Development The Little Creek field was discovered in Jan., 1958, in the lower Tuscaloosa trend in southwestern Mississippi (Fig. 1). The discovery well, Shell-Lemann No. 1, was drilled on a seismic closure about 2 miles southeast of lower Tuscaloosa production at Sweetwater. The well was completed in the Denkman sand at 10,752 ft, and on initial potential it flowed 588 BOPD of 39" API crude on a %+-in. choke; psi was 730 and GOR was 442:l. Development proceeded rapidly on 40-acre spacing, and by the end of 1958 the field was producing approximately 9,100 B/D from 56 wells. Almost all this production came from the northern half of the field. The southern part was discovered in Nov., 1958, at a location almost 2 miles from previously established production. Subsequent drilling established an apparent conneotion about half a mile wide between the twd areas. Development of the field was practically complete by 1961 with the drilling of 155 producers and 35 dry holes. Some early wells were completed open hole but moslt are completed with casing cemented through the productive interval and perforated for production. Geology The lower Tuscaloosa structure in this area is a north-south nose with maximum dips of about 2" on the flanks. There is no discernible faulting at the producing horizon. Productive limits of the field are shown in Fig. 2, which is contoured on a marker just above the main productive zone. A common water level at 10,415 ft subsea was logged at both the northwest and southeast ends of the field. There is a gross oil column of nearly 100 ft (Fig. 2). Since there is less than 40 ft of closure, it is apparent that bhe accumubtion is controlled stratigraphically, being limited by a sand pinch-out across the creslt of the nose. The total produc-

Jan 1, 1969

By L. F. Porter, G. J. Dienes

The effect of netltron irracliation on mart ensite transformation in the iron-nickel system was studied by means of electrical resistance and magnetic induction measuremertts. Irradiation lowers the M8 temperature of the allay, causes changes in the electrical and magnetic properties of the high-temperature phase which indicate either an accelemtion of phase separation or a clustering of nickel, and enhances strain recovery on specimens partially transformed to martensite prior to irradiation. Possible mechanisms to account for the effects; are discussed. 1 HERE is a good deal of evidence to indicate that neutron irradiation is capable of affecting phase changes in metals and alloys. While the mechanism of the effect often is not well understood, such studies hold promise of improving our understanding not only of irradiation damage but also of the phase changes involved. To date systematic and detailed investigations have been made of the influence of nuclear radiation on order-disorder transformations in the copper-gold, nickel-manganese, and copper-zinc system, and on precipitation reactions in the copper-iron, nickel-beryllium, and copper-beryllium system.&apos; These solid-state reactions are diffusion controlled and the results can be explained largely on the basis of enhanced diffusion due to the presence of irradiation produced vacancies. Reversion of low-temperature eutectoid phases to the high-temperature phase has been observed in the fissionable uranium-molybdenum and uranium-niobium systems.2 Here it is necessary and logical to postulate a displacement spike mechanism to account for the effect. The only case of irradiation induced diffusionless transformation in metals is the allo-tropic transformation of p to a tin reported by Flee-man and Dienes. 3 They found that neutron irradiation markedly decreases the incubation time for transformation, but the mechanisnl is not well understood. Another diffusionless transformation which one might expect to be influenced by neutron irradiation is the martensite transformation. This transformation is known to be sensitive to strain, structural hardening, and the presence of imperfections.6,7 Since the transformation is diffusionless, one also

Jan 1, 1960

By F. H. Deily, Jean M. Quets, Milton E. Wadsworth, John R. 222-000-000-012 Lewis, D. S. Rowley, R. J. Howe

Samples of synthetic magnetite were reduced in hydrogen-water vapor atmospheres in the temperature range 450o to 900oC. The reaction was always surface controlled, indicating the final products of reaction are nonfirotective. Three separate cases have been identified from the kinetic results: Case I, reduction of magnetite to iron below 570°C; Case II, reduction of magnetite to iron above 570°C; and Case 111, reduction of magnetite to wustite above 570 oC. In Cases I and 111 the kinetics have been explained by the formation of oxygen anion vacancies in the magnetite surface followed by associated diffusional processes. In Case 11 the observed kinetics have been related to the concentration of iron cation vacancies in the wustite layer formed, followed by associated steady-state diffusional processes. The concentration of cation vacancies in the wustite is maintained constant by the magnetite-wustite equilibrium. THE reduction of the oxides of iron has been a subject of study and interest for many years. However, few attempts have been made to interpret the results in terms of the mechanism of reduction of an iron oxide by either hydrogen or carbon monoxide. Stalhane and Malmberg&apos; using CO, H2, and CO-Hz mixtures, developed the rate expression: where m = mass of oxide reduced, t = time, k = a constant, s = surface area, P = partial pressure of of CO or H,, and P, = partial pressure of the reducing gas at equilibrium. The rate of reaction per unit area was proportional to the difference between the partial pressure of the reducing gas and its pressure at equilibrium. Hansen, Bitsianes, and Joseph2 studied the reduction of pellets of hematite to magnetite with mixtures of CO-CO,. They concluded that below 450°C the reaction proceeded according to a model in which CO reacts with the hematite surface producing an oxygen ion vacancy. The rate controlling step was then assumed to be oxygen ion diffusion through vacancies resulting in the formation of magnetite. They derived an expression giving the rate of reduction proportional to the cO/CO, ratio. Recently McKewan3 published results for the reduction of magnetite spheres in atmospheres below 570°C. He explained his results by an equation of the form where K, is the equilibrium constant for wustite-iron equilibrium attributed to the formation of wustite as an intermediate in the reduction of magnetite. According to McKewan, Kp is an equilibrium constant for H, -HO adsorption in which oxygen is deposited on the surface from the H,Oand subsequently acts as a poison for reduction by hydrogen. Sample Preparation and Experiments. In this work the authors used the same apparatus and experimental procedure employed in the hydrogen reduction of magnetite. Sintered disk samples weighing approximately 1.5 g and measuring 1.2 cm in diameter and 0.25 cm in thickness were prepared by a method described previously.4 Partial pressures of hydrogen and water vapor were controlled by bubbling hydrogen through a series of flasks containing distilled and deionized water maintained at constant temperature in an oil bath. The total flow rate of the reacting gases—hydrogen and water vapor—was approximately 0.5 liter per min. The entire external system was maintained at a temperature above the oil bath to prevent condensation of water vapor. This was accomplished by wrapping electrical resistance elements over all surfaces. The glass column containing the weighing system-a McBain balance suspended from a gold chain-was enclosed in an aluminum tube heated by nichrome resistance wire enclosed in an insulating material. The temperature of the glass column was held constant by means of a series of thermocouples connected in parallel to a Leeds and Northrup temperature controller. This was necessary since variations in temperature resulted in expansion and contraction of the glass column and could be readily observed with the cathetometer. The spring extensions were measured through a window with a gaertner cathe-

Jan 1, 1962

By R. P. Agarwala, M. S. Anand

Using residual activity technique, the diffusion of palladium, silver, cadmium, indium, and tin in alunzinum has been studied in the temperature range of 400" to 630°C. The diffusivities (in units of square centimeters per second) have been expressed as: IMPURITY diffusion in aluminum,1-9 silverand lead5 for cases of low solid solubility of the impurity in the host metal has yielded frequency factors in the range of l0-6 to l0-9 sq cm per sec whereas the activation energy is practically half the self-diffusion activation energy value. From the observed values of frequency factor, activation energy, and entropy of activation, it has been suggested&apos; that these solutes are not diffusing by vacancy or interstitial mechanisms but by a mechanism which should be consistent with such low values of the diffusion parameters (Do and Q). However in spite of extensive work on these types of systems, the mechanism of diffusion is still not well understood. The present investigation on the diffusion of palladium, silver, cadmium, indium, and tin in aluminum has been carried out to throw further light on the diffusion mechanism in systems, where the solid solubility is very low (except for the case of silver). The results are discussed on the basis of solid solubility and the structural changes involved owing to the presence of the solutes in aluminum solid solution. An attempt has also been made to apply the existing theories of charge5-8 and size8 difference between the solute and the solvent. EXPERIMENTAL PROCEDURE Specimens (1/2 in. diam by 3/8 in. high) were machined out of pure aluminum (99.995 wt pct) rod obtained from Johnson Mattheys. They were sealed under vacuum in quartz tubes and annealed at 620° C for several hours; the grains thus developed were sufficiently large to eliminate the possibility of diffusion along the grain boundaries. The flat ends were prepared carefully after polishing as described previously,10 Radioactive nitrates of cadmium, indium, and tin and chloride of palladium containing, respectively, cd115, 1n114, sn113, and pd103 were dissolved in distilled water and mixed with 30 pct acetone. By means of a micropipet a drop of this solution was placed on a smoothly polished and lightly etched surface of the specimen. Due care was taken to see that the solution spread uniformly on the surface of specimen without trickling down its sides. Radioactive silver was elec-trodeposited using a AgCN-KCN bath. The amount of sample deposited in all the cases was not more than 0.1 µ thick. The samples were then sealed in quartz tubes in vacuum. The cadmium samples were sealed in a purified argon atmosphere to avoid evaporation. The samples were then diffusion-annealed. The temperature of annealing varied between 400° and 630°C and was controlled to ±5°C. On heating to -400°C,the deposits of cadmium, indium, and tin, which were of the order of 0.1 p in thickness, were converted to their respective oxides. The contribution of oxygen present in the lattice of aluminum due to these oxides has been calculated and found to be less than 10 ppm in all cases. Oxide method has already been used by other workers11&apos;12 in diffusion studies without any controversy on the issue. However, in some of these investigations, metallic deposition was also tried. The diffusivities calculated from these measurements were found to agree very well with the diffusivities obtained by using the oxide method. Thus it is assumed that the measured diffusivities represent true diffusion coefficients. Since palladous chloride decomposes at about 500°C, the deposited samples which were to be diffusion-annealed below 500°C were heated in vacuum for a very short time at 500°C to allow the decomposition of palladous chloride to palladium metal. Time taken in decomposition of nitrates to oxides and chloride to metal was negligibly small as compared to the period of the diffusion anneals. The residual activity technique13 was used to study the diffusion profiles where thin layers from the specimen surface were removed by grinding it parallel to a flat surface on a 600-grade carborundum paper. The specimen was washed, dried, and weighed, the differ -ence of the weight being the measure of the thickness of the layer removed. After each such abrasion and weighing, the total residual activity on the surface of the specimens was measured by counting 0.656, 0.94,

Jan 1, 1968

By A. E. Jenkins, L. A. Baker, N. A. Warner

The electromagnetic levitation technique has been successfully applied to rate studies of the de-carburization of liquid Fe-C alloys from 5.5 to zero pct C at 1660°C using gas mixtures containing 1 to 100 pct CO2 with CO or helium as diluents. The rate was shown to be independent of carbon concen -tration in the melt and only slightly affected by total pressure. The results were shown to be consistent with control either wholly or predominantly by gaseous diffusion. As well as avoiding side reactions with the crucible, levitation allowed precise calculation of reaction rates since the geometry of the system was accurately known. It also enabled interpretation using the established mass-transfer correlations for a gas flowing past a single sphere, The existence of gaseous-diffusion control and the extremely high rates of reaction reported for gas flowing past small spheres are of great practical significance in relation to current investigations into the use of spray-refining techniques in continzcous steelmaking. PREVIOUS work on the kinetics of carbon removal from liquid iron has generally involved the use of oxygen as the gaseous oxidant. Investigations have been made on commercial steelmaking furnaces and in addition laboratory-scale experiments have been attempted with a slag phase present. The general lack of agreement and the obvious difficulty in interpreting the results is at least partly due to the complexity of the systems used. This work has been reviewed by carter1 and more recently by Bods-worth2 and ward.3 The gas-liquid metal reactions have also been studied with slag-free melts by the conventional technique of blowing oxygen onto the melt contained in a crucible. The reaction between the oxidant and carbon could be followed by sampling either the melt or the gas phase. Side reactions with the crucible material have precluded direct interpretation of the results. Fujii, 5-7 using O-A mixtures, attempted to correct for the crucible reaction and reported that the reaction between carban and oxygen occurred at the melt surface and was controlled by gaseous diffusion for carbon contents greater than a critical value and by carbon-diffusion control in the metal for carbon contents less than the critical. The critical value was given as approximately 0.15 pct C. However, whereas this was the case for oxygen contents in the gas stream up to 10 pct, between 10 and 20 pct the rate was found to be approximately independent of oxygen content, and Fujii attempted to explain this observation by postulating the presence of an oxide "film".7 Turkdogan et a1.&apos; have studied iron fuming during decarburizing and suggested gaseous-diffusion control of the reaction above a critical carbon concentration, given as approximately 2 pct C. Filippov9-12 reports in a similar manner to Fujii but makes no mention of the crucible reaction with the carbon in the melt, even though this would be expected with the temperature, crucible material (MgO), and carbon contents used. Both CO2 and O2 were used as oxidant gases. In the present work the decarburization of liquid Fe-C alloys was studied using an adaptation of the electromagnetic levitation technique, and thus the complexities introduced by crucible side reactions were eliminated. In this technique a single sphere of the Fe-C alloy is freely suspended and heated by electromagnetic induction in a flowing stream containing the oxidant gas. The full range of carbon levels up to saturation was studied, the temperature of the melts in this instance being held constant at 1660°C. The oxidant was CO2 which was used either pure or in association with a diluent gas, the total gas pressure being maintained either at 1 atm or at a reduced pressure. Thus the reaction under study was:

Jan 1, 1964