Search Documents

By Brian F. Dyson

The surface tensions at 1550°C of some Fe-S alloys (in the range 0.008 to 0.052 wt pct S), Fe-Sn alloys (0.31 to 48.4 wt pct Sn), Fe-P alloys (0.038 to 2.38 wt pct P), Fe-Cu alloys (2.15 to 22.8 wt pct Cu), and Fe-1 pct C-S alloys (0.005 to 0.076 wt pct S) along with the surface tension of the base iron have been measured by the sessile-drop method. A mean value of 1754 dynes per cm was found for the surface tension of the base iron. Sulfur was found to be highly surface-active, the surface-tension results being in quantitative agreement with existing data. Tin and copper were found to be less surface-active than sulfur while phosphoms was completely nonsurface-active. The surface tensions of Fe-1 pct C-S alloys were found to be lower than those of the Fe-S alloys containing the same sulfur content. This was shown to be a mmzifestation of the increase in the thermodynamic activity of suZfur by carbon. It is only in recent years that attempts have been made to measure the surface tension of liquid iron of known high purity.1-3 Earlier measurements4-7 were made on liquid iron containing variable amounts of what are now known to be surface -active solutes. The exact value of the surface tension of liquid iron is still, however, open to some doubt. Halden and Kingery' reported a value of 1720k 34 dynes per cm at 1570°C, Kozakevitch and Urbain8 gave 1790k 25 dynes per cm at 1550°C, while Van-Tszin-Tan et al. obtained a value of 1865k 37 dynes per cm at 1550°C. The first systematic investigation into the effect of controlled solute additions on the surface tension of iron was made by Halden and Kingery.' They showed that sulfur and oxygen were highly surface-active, whereas nitrogen was only slightly active, and carbon inactive. A subsequent investigation by Kingery indicated that two other group-6B elements, selenium and tellurium, were also surface-active. This highly surface-active nature of sulfur and oxygen has recently been substantiated by Kozakevitch and Urbainla and Van-Tszin-Tan et al. l1 Kozakevitch and Urbainl2 have also conducted an experimental survey of the effects of a number of metals on the surface tension of liquid iron. Their surface-active nature was, in all cases, less than that of the group 6B elements. The present investigation was undertaken to study in more detail the surface tensions of dilute Fe-S alloys and to measure the surface tensions of binary alloys of iron containing phosphorus, copper, and tin. The effect of sulfur additions on the surface tension of Fe-1 pct C alloys was also determined. EXPERIMENTAL PROCEDURE The sessile-drop method was employed in the present investigation. An apparatus was built similar in principle to that described by Humenik and Kingery.lS It consisted of a horizontal silica tube, which could be evacuated to pressures less than 10-5 torr, with its central portion surrounded by a water jacket within which was a high-frequency coil. This generated heat in a tantalum susceptor placed inside the silica tube, which in turn radiated heat to the specimen mounted on a recrystallized alumina plaque. Temperatures were measured by an optical pyrometer and photographs of the molten drop were taken on a fixed-focus plate camera giving a magnification of X2. Surface-tension values were determined from the resultant drop using the method described by Baes and Kellogg.l4 The high vapor pressure of molten iron made it necessary to conduct all the experiments under a 1/4 atm of argon (greater than 99.995 pct purity). The analysis of the base iron used in the investigation is given in Table I. Each sample was approximately 3 g in weight and had a hemispherical base to ensure a uniform advancing contact angle on melting. The iron alloys were prepared individually in the sessile-drop apparatus by drilling a hole in the top of each sample and adding the required amount of solute, the drops being analyzed after the experiment. This method of preparation had the advantage of ensuring a consistent minimal contamination by oxygen due to refractory attack and also allowed surface tension to be measured at the same time. Every precaution was taken to ensure that the specimen was not contaminated by grease when it was introduced into the apparatus, the samples being cleaned in acid, dried in alcohol, and rinsed in petroleum ether. All handling was done with tweezers. Once the specimen had been placed inside the susceptor, the furnace was evacuated and the Sample leveled. The furnace was then degassed at approximately 1000"C before the argon was introduced. In every case the surface tension was determined at 1550" C.

Jan 1, 1963

By M. J. Marcinkowski, K. S. Raghavan, A. S. Sastri

A detailed transmission electron microscopy investigation was carried out in connection with a manganese Hadfield Steel. At small plastic strains, numerous individual intrinsic stacking faults are observed. With increased plastic deformation, the stacking faults thicken into twin lamellae which in turn subdivide the original austenite matrix into smaller domains. The twin boundaries act as strong barriers to subsequent dislocation motion and is in a sense equivalent to grain refinement. It is this "grain refinement" which is believed to be the cause of the very high work hardening rates in the Hadfield Steels. In many cases, especially where an hcp phase is the stable one at low temperatures, the stacking fault energy in fcc metals and alloys decreases with decreasing temperature.' Since stacking faults of the intrinsic type are precursors of both twins as well as the hexagonal close packed structure, both of these entities should become more frequent as the temperature of a fcc crystal is lowered. In the case of the twin, there is no chemical driving force for its formation and it is generally necessary to provide the required driving force by an applied stress, i.e., strain energy. In the case of the hcp structure the transformation from the fcc modification can occur spontaneously (marten-sitically) since a decrease in chemical energy does in fact occur; however, an applied stress will provide an even greater driving force toward complete transformation. Since the transformation products mentioned above occur in an inhomogeneous manner throughout the crystal and since these can act as potential barriers to further plastic deformation2 marked strengthening effects can be anticipated. Also because metal and alloy strenghening is in general proportional to the shear modulus, these effects should be greatest in steels of the austenitic type (y), i.e., the fcc types. Perhaps the two most important steels in this category are the austenitic stainless steels and the Hadfield manganese steels. Both may be quenched from elevated temperatures so as to retain the austenitic states characteristic of those temperatures. The effect of subsequent deformation at lower tem- peratures has a profound effect on the stress-strain curves of these alloys. In particular Fig. 1 shows the compressive stress-strain curves obtained with an 18-8 stainless steel which was quenched from 1850°C after annealing for 1 hr so as to produce all y. As the temperature is lowered, the work hardening rate increases markedly. Although some hcp or c mar-tensite can be generated by plastic deformation as the temperature is lowered,~ it is believed to be a transition phase4 and most of the martensite produced is of the bcc or a variety.3 It is this stress induced martensite which gives rise to the very low initial work hardening at 77°K as can be seen in the stress-strain curve in Fig. 1. Similar low initial work hardening rates have been observed in the stress induced Ni-Ti martensites.5 Fig. 2 shows that an even more rapid rate of work hardening occurs in the Hadfield steels treated in the same way as that described for the 18-8 stainless steels a; the temperature is lowered. It is this ability to work harden to such high stress levels that makes the Hadfield steels particularly suitable for armor plate and heavy construction equipment. However, unlike the case of Fig. 1, no initial low rate of work hardening is observed in any of the curves in Fig. 2. Thus the stress induced formation of any low energy martensite phase in any significant quantity must be ruled out. This observation is in accord with the X-ray findings of Otte.~ On the other hand, small quantities of the E phase have been observed by other investigators using transmission electron microscopy (TEM) above Even more significant was the fact that large numbers of deformation twins were observed in the deformed Hadfield steels,678 which were postulated to be one of the reasons for the high work hardening ability of this class of steels.8 It is the purpose in what follows to discuss a series of experimental observations pertaining to the stress induced transformation in a Hadfield steel and to formulate a dislocation mechanism which adequately accounts for the observed results. EXPERIMENTAL PROCEDURE The stainless steel used to obtain the curves shown in Fig. 1 was of the AISI Type 303 containing approximately 18.0 pct Cr and 8 pct Ni. On the other hand, the Hadfield manganese steel used to obtain the curves shown in Fig. 2 contained between 1.00 to 1.25 pct and 11.5 to 13.5 pct Mn. In all cases the samples were in the form of compression cylinders 0.220 in. in diam and 0.370 in. long. Prior to testing the samples were annealed for a hr at 1050°C and rapidly quenched into a brine solution. This treatment was sufficient to preserve the y phase for subsequent testing at lower temperatures. All samples were compressed in an Instron testing machine using a cross head speed of 0.02 in.

Jan 1, 1970

By E. C. W. Perryman

The recovery and recrystallization characteristics of superpurity aluminum have been investigated using electrical resistivity, X-ray line breadth, and hardness measurements for the former and the micrographic method for the latter. The three different properties recover at different rates and have different activation energies. The recrystallization results agree well with Avrami&apos;s theory and furthermore indicate that the perfect subgrains formed during recovery are not the nuclei for re-crystallization. WHEN a metal is plastically deformed, its physical and mechanical properties generally undergo considerable changes and by subsequent annealing these changes are partly or wholly annihilated. Thus, a recovery process can be discussed, taking this term in its general sense. In practice, however, there is reason to discriminate between two apparently different processes, one most easily followed at low temperatures, in which the properties return to an almost constant value between that of the cold worked and fully annealed material, and a second process in which the properties return to their original values before cold working and which is accompanied by the formation and growth of new grains having an orientation different from that of the matrix. In this paper the word recovery will be taken to mean the changes in some property as a function of annealing time which occur either without the appearance of new grains or under conditions such that the new re-crystallized grains are very small (= 2 microns), are very few in number, and substantially do not affect the property being measured. This definition is rather abitrary, for it will depend upon the sensitivity of the technique used for the observation of new recrystallized grains, which in the present work was about 1 to 2 microns. However, it is helpful to use the term recovery in this sense and to reserve the term recrystallization for the processes of nucle-ation and growth of new grains in the cold worked matrix. Although considerable work has been done on recovery and recrystallization, most workers have based their study on the measurement of one or perhaps two parameters. Since very small amounts of impurities have such a profound effect on the recrystallization characteristics of a pure metal, it becomes extremely difficult to correlate one piece of work with another. With this in mind, the present work on recovery and recrystallization was done on the same material. Experimental Procedure Material Used and Fabrication: The composition of the superpurity aluminum used throughout this investigation was 0.002 pct Cu, 0.003 pct Fe, 0.003 pct Si, and <0.001 pct Mg. The ingot was hot rolled to 0.250 in., annealed, and cold rolled to 0.034 in. A large number of reductions and intermediate anneals were carried out so as to produce material with a minimum of preferred orientation and maximum homogeneity. For the recovery part of the investigation, the final cold reduction was 20 and 80 pct and for the recrystallization part, 20 pct. After each pass in the cold rolling process, the material was quenched in cold water in order to keep the rolling temperature as near room temperature as possible. Annealing Procedure: For the recrystallization work, specimens 1x1 in. were cut from the 0.034 in. cold rolled sheet and a hole was drilled in each through which a wire was threaded to support it in the salt bath. The temperature of the salt bath was controlled to +2°C and the time taken for a specimen to reach temperature was approximately 5 sec. These 1 in. squares were then divided into three groups, one of which was given 5 min at 318°C and another 2 hr at 244°C. These treatments were such that recovery was almost complete and a well defined subgrain structure produced. Separate specimens of each group were annealed for different times at 301°, 318°, 355°, and 373°C, i.e., three specimens for each annealing time. The delay between finish of cold working and start of annealing was about 1 hr. For the recovery work, strips 0.062 in. thick were cut from the cold worked sheet, annealed, and then given the last cold rolling operation. This was done for each annealing temperature. By this means it was possible to minimize the delay between cold working and annealing. In general, all measurements were carried out within 1 hr of the last cold rolling operation. Annealing at low temperatures was done in an oil bath the temperature of which was maintained constant to +1°C. Electrical Resistivity Measurements: Strips 20x0.5x0.05 in. were machined and the electrical resistance measured using a Kelvin double bridge. Measurements were made in an oil bath maintained at 20rt0.1°C. The same specimen was used for the complete isothermal annealing curve.

Jan 1, 1956

By P. Chiotti, G. R. Kilp

Thermal, metallographic, vapor pressure, and X-ray data were obtained to establish the phase diagram for the zinc-zzrconiz~m system. Five compounds corresponding to the stoi-chiometric formulas ZrZn, ZrZn,, ZrZn,, ZrZn,, and ZrZn14 were observed. All these compounds, with the exception of ZrZn2, which melts congruently at 1180°C under constrained zinc-vapor conditions, undergo pexitectic reactians. The temperature at which the zinc vapor pressure is I atm for a series of alloys was determined from vapor-pressure measurements. The data obtained are summarized in the construction of a I-atm-pressure phase diagram and a phase diagram corresponding to a pressure of less than 10 atm. THE purpose of this investigation was to establish the phase diagram for the zinc-zirconium system. Thermal, metallographic, vapor pressure, and X-ray data were employed in determining the phase regions. Partial investigations of this system have been conducted by Gebhardt1 and Carlson and Borders.&apos; Carlson and Borders studied the high-zirconium region and established the existence of a eutectic at 69 wt pct Zr with a melting point of 1015°C. The terminal phases of the eutectic horizontal were shown to be an intermetallic compound ZrZn and a solid solution of ß zirconium containing 21 wt pct Zn. The ß solid solution decomposes into ZrZn and a zirconium at 750°C. The eutectoid composition is given as 15 wt pct Zn, and the solubility of zinc in a zirconium at temperatures below 750°C is indicated to be negligible. Gebhardt studied the zinc-rich region and observed a lowering of the melting point of zinc from 419.5" to 416°C and temperature horizontals at 545" and970°C. Some preliminary observations by Chiotti, Ratliff, and Kilp were reported by Hayes.2 pietrokowsky3 has reported the compound ZrZn2 to have a cubic MgCu2 structure with ao = 7.396A. MATERIALS AND EXPERIMENTAL PROCEDURES The metals employed in the preparation of alloys were Bunker Hill slab zinc or Baker analyzed reagent granulated zinc, both 99.99 pct pure and hafnium-free iodide-process crystal bar zirconium obtained from the Westinghouse Electric Corp. The zirconium contained 200 ppm Fe, 200 ppm Si, 100 ppm C, and minor amounts of other impurities. The zirconium was milled or machined into thin chips or shavings. These were cleaned with a nitric-hydrofluoric acid solution, rinsed with water, and acetone, and dried just prior to their use in alloy preparation. The granulated zinc was similarly cleaned using dilute nitric or hydrochloric acid. Weighed quantities of these materials, 20 to 30 g total, were mixed and pressed at 20,000 to 70,000 psi to give relatively dense compacts. During the early part of this investigation the pressed compacts were placed in MgO-15 wt pct MgF, crucibles which were then sealed inside of quartz ampules. The compacts were given various prolonged heat treatments prior to their use for thermal analyses, or vapor-pressure measurements. Because of expansion of the compacts and the relatively high zinc vapor pressure it was difficult to heat to the melting temperatures of the alloys without failure of the quartz ampules. Homogenization at temperatures below the melting temperature gave brittle, porous alloys unsuitable for metallographic examination. It was also difficult to prevent condensation and segregation of zinc on the colder parts of the quartz ampules during heating and cooling operations. These problems were eliminated to a great extent by the use of tantalum crucibles. Tantalum proved to be a satisfactory container with little or no reaction between the alloys and the tantalum. Small tantalum thermocouple wells were successfully welded in the bottom of these crucibles. Pressed compacts were sealed inside the tantalum crucibles by welding on preformed caps under an argon atmosphere. Heat treating and differential thermal analysis were combined into a single operation. The experimental sample assembly is shown in Fig. 1. This assembly was enclosed inside a stainless-steel tube heating chamber which could be evacuated and filled with an inert gas. The thermocouple leads were brought out of the heating chamber between two rubber gaskets used to provide a vacuum seal for the water-cooled head. Most of the compounds in this system undergo peritectic decomposition. After heating above the temperature of a particular peritectic horizontal the sample was cooled to just below the peritectic temperature and held at temperature for several hours. The sample was then reheated through the peritectic temperature and the size of the thermal arrest, if still present, compared with the one previously obtained. If the thermal arrest was not characteristic for the alloy composition being investigated its magnitude diminished and repeated cycling and annealing eventually eliminated it. The peritectic thermal arrests characteristic of a particular composition were established in this manner.

Jan 1, 1960

By P. A. Laxen, H. R. Spedden

WHEN a mineral particle is fractured, bonds between the atoms are broken. The unsatisfied forces that appear at the newly formed surface are considered to be responsible for the adsorption of ions at the mineral surface. A knowledge of the mechanism and extent of ion sorption from solution onto a mineral surface is of interest in the development of the theory of flotation.&apos;*&apos; Study of the adsorption of sodium from an aqueous solution oftheon quartz offers a simple approach to this complicated problem. The availability of a radioisotope as a tracer element meant that accurate data could be obtained."." Three main factors which appeared likely to affect the adsorption of sodium are: l—concentration of sodium in the solution, 2—concentration of onotherof cations in the solution, and 3—anions present in the solution. Hydrogen and hydroxyl ions are always present in an aqueous solution. By controlling the pH, the concentration of these two ions was kept constant. The variation in thesethe amount of sodium adsorbed with variation in sodium concentration was then determined under conditions standardized in regard to hydrogen ion. The effect of concentration of hydrogen ions and of other cations was also measured. A few experiments were made to get a preliminary idea on the effect of anions. The active isotope of sodium was available as sodium nitrate. Standard sodium nitrate solutions were used throughout these experiments except when the effects of other anions were studied. It was found that sodium adsorption increased with sodium-ion concentration, but less rapidly than in proportion to it. Increasing hydrogen-ion concentration, or conversely decreasing hydroxyl-ion, brings about a comparatively slight decrease in sodium-ion adsorption. Increasing the concentration of cations other than hydrogen or sodium decreases somewhat the adsorption of sodium ion. It would appear as if the kind of anion is a secondary factor in guiding the amount of sodium ion that is adsorbed. Materials and Methods Quartz The quartz was prepared as in previous work in the Robert H. Richards Mineral Engineering Laboratory&apos; except for the refinement of using de-ionized distilled water for the final washing of the sized quartz, prior to drying." To minimize the laborious preparation of quartz, experiments were made to determine .whether the sodium-covered quartz could be washed free of sodium and re-used. The experiments were successful as indicated by lack of Na" activity on the repurified material and by its characteristic sodium adsorption. Table I gives the spectrographic analyses of the quartz used. The quartz ranged from 16 to 40 microns in size, averaging about 23 microns (microscope measurement), and had a surface of 1850 sq cm per g (lot I), 2210 (lot 11) and 2000 (lot 111) as determined by the Bloecher method." Radioactive Sodium Method of Beta Counting for Adsorbed Sodium: Na22, the radioisotope of sodium, possesses convenient properties.&apos; It has a half-life of 3 years, thus requiring no allowance for decay during an experiment. On decay it emits a 0.575 mev ß+ radiation and a 1.30 mev r radiation. The decay scheme is illustrated in the following equation: ß+ NaR-------&apos;8&apos;77NeZ2 3 years The /3 radiation is sufficiently strong to penetrate an end-window type of Geiger-Mueller counting tube. This, in turn, makes it possible to use external counting, a great advantage in technique. Furthermore, it permits the assaying of solids arranged in infinite thickness, while assaying evaporated liquors on standardized planchets. The equipment used was standard and similar to that employed by Chang.R The original active material was 1 ml of solution containing 1 millicurie of Na" as nitrate. This active solution was diluted to 1000 ml. Five milliliters of this diluted active solution was found to give a quartz sample a sufficiently high activity for accurate evaluation of the sodium partition in the adsorption measurements. Also, 1 ml of final solution gave a sufficiently high count for precision on the liquor analyses. The sodium concentration of the diluted active solution was 1.2 mg per liter, so that 6 mg of sodium for 60 ml of test solution and 12 g of quartz was the minimum amount used. The active solution was stored in a Saftepak bottle. Procedure for Adsorption Tests: The method consisted of agitating 12 g of quartz with 60 ml of solution of known sodium concentration for enough time to establish equilibrium between the solution and the quartz surface. The quartz was separated as completely as possible from the solution by filtering and centrifuging. The activity on the quartz and in the equilibrium solution was measured and the partition of the sodium was calculated from the resulting data. The detailed procedure for the adsorption test is set forth in a thesis by Laxen." In brief, it included the following steps: 1—Ascertainment of linearity between concentration of Na" and activity measured. 2—Evaluation of factor to translate activity on solid of infinite thickness in terms of activity on an evaporated active film of minute thickness, on the various shelves of the counter shield. 3—Taking precautions to avoid evaporation of water during centrifuging

Jan 1, 1953

By P. A. Laxen, H. R. Spedden

WHEN a mineral particle is fractured, bonds between the atoms are broken. The unsatisfied forces that appear at the newly formed surface are considered to be responsible for the adsorption of ions at the mineral surface. A knowledge of the mechanism and extent of ion sorption from solution onto a mineral surface is of interest in the development of the theory of flotation.&apos;*&apos; Study of the adsorption of sodium from an aqueous solution oftheon quartz offers a simple approach to this complicated problem. The availability of a radioisotope as a tracer element meant that accurate data could be obtained."." Three main factors which appeared likely to affect the adsorption of sodium are: l—concentration of sodium in the solution, 2—concentration of onotherof cations in the solution, and 3—anions present in the solution. Hydrogen and hydroxyl ions are always present in an aqueous solution. By controlling the pH, the concentration of these two ions was kept constant. The variation in thesethe amount of sodium adsorbed with variation in sodium concentration was then determined under conditions standardized in regard to hydrogen ion. The effect of concentration of hydrogen ions and of other cations was also measured. A few experiments were made to get a preliminary idea on the effect of anions. The active isotope of sodium was available as sodium nitrate. Standard sodium nitrate solutions were used throughout these experiments except when the effects of other anions were studied. It was found that sodium adsorption increased with sodium-ion concentration, but less rapidly than in proportion to it. Increasing hydrogen-ion concentration, or conversely decreasing hydroxyl-ion, brings about a comparatively slight decrease in sodium-ion adsorption. Increasing the concentration of cations other than hydrogen or sodium decreases somewhat the adsorption of sodium ion. It would appear as if the kind of anion is a secondary factor in guiding the amount of sodium ion that is adsorbed. Materials and Methods Quartz The quartz was prepared as in previous work in the Robert H. Richards Mineral Engineering Laboratory&apos; except for the refinement of using de-ionized distilled water for the final washing of the sized quartz, prior to drying." To minimize the laborious preparation of quartz, experiments were made to determine .whether the sodium-covered quartz could be washed free of sodium and re-used. The experiments were successful as indicated by lack of Na" activity on the repurified material and by its characteristic sodium adsorption. Table I gives the spectrographic analyses of the quartz used. The quartz ranged from 16 to 40 microns in size, averaging about 23 microns (microscope measurement), and had a surface of 1850 sq cm per g (lot I), 2210 (lot 11) and 2000 (lot 111) as determined by the Bloecher method." Radioactive Sodium Method of Beta Counting for Adsorbed Sodium: Na22, the radioisotope of sodium, possesses convenient properties.&apos; It has a half-life of 3 years, thus requiring no allowance for decay during an experiment. On decay it emits a 0.575 mev ß+ radiation and a 1.30 mev r radiation. The decay scheme is illustrated in the following equation: ß+ NaR-------&apos;8&apos;77NeZ2 3 years The /3 radiation is sufficiently strong to penetrate an end-window type of Geiger-Mueller counting tube. This, in turn, makes it possible to use external counting, a great advantage in technique. Furthermore, it permits the assaying of solids arranged in infinite thickness, while assaying evaporated liquors on standardized planchets. The equipment used was standard and similar to that employed by Chang.R The original active material was 1 ml of solution containing 1 millicurie of Na" as nitrate. This active solution was diluted to 1000 ml. Five milliliters of this diluted active solution was found to give a quartz sample a sufficiently high activity for accurate evaluation of the sodium partition in the adsorption measurements. Also, 1 ml of final solution gave a sufficiently high count for precision on the liquor analyses. The sodium concentration of the diluted active solution was 1.2 mg per liter, so that 6 mg of sodium for 60 ml of test solution and 12 g of quartz was the minimum amount used. The active solution was stored in a Saftepak bottle. Procedure for Adsorption Tests: The method consisted of agitating 12 g of quartz with 60 ml of solution of known sodium concentration for enough time to establish equilibrium between the solution and the quartz surface. The quartz was separated as completely as possible from the solution by filtering and centrifuging. The activity on the quartz and in the equilibrium solution was measured and the partition of the sodium was calculated from the resulting data. The detailed procedure for the adsorption test is set forth in a thesis by Laxen." In brief, it included the following steps: 1—Ascertainment of linearity between concentration of Na" and activity measured. 2—Evaluation of factor to translate activity on solid of infinite thickness in terms of activity on an evaporated active film of minute thickness, on the various shelves of the counter shield. 3—Taking precautions to avoid evaporation of water during centrifuging

Jan 1, 1953

By Benny J. Nelson

AS a part of the fundamental research program of Aluminum Research Laboratories, some data were obtained on the ternary system Mg-Al-Mn. As very little information on the magnesium corner of this diagram has heretofore been published, it seems desirable to make available the values found for the liquidus and solidus surfaces of this system. Procedure The settling procedure was used for the determination of the liquidus compositions. Metallo-graphic examination of quenched samples, and stress-rupture upon incipient melting, were used for the solidus determinations. The settling procedure has been described in a previous paper.&apos; Briefly, this method involved saturating the alloy with manganese at a temperature substantially above that at which the sohbility was to be determined, then cooling the melt to the latter temperature, and holding it at that temperature for a substantial period of time. Samples for analysis .were carefully ladled from the upper portion of the melt at hourly intervals during the holding period. After the ladling of each sample, the melt was stirred to redistribute some of the manganese that had already settled, because it appeared that when the latter particles of manganese again settled, they aided in carrying down more of the manganese and thus hastened the attainment of equilibrium. The melts were prepared and held in a No. 8 Tercod crucible holding approximately 4 lb of metal. The manganese was added either in the form of a prealloyed ingot (Dow M) containing about 1.5 pct Mn or by the use of a flux (Dow 250) containing manganese chloride. In calculating the flux additions, it was assumed that the manganese introduced would be equal to 22 pct of the total weight of the flux. Temperatures were measured with an iron-constantan thermocouple enclosed in a seamless steel tube, the lower end of which was welded shut. This protection tube also served as a stirring rod. The samples ladled from the upper portions of the melts at the various intervals were analyzed for aluminum, manganese, and iron. When making the alloys which were to be used for the determination of the solidus, 2½ in. diam tilt mold ingots were cast, scalped to 2.0 in. in diam, and extruded into ? in. diam wire. The principal impurities in the melts for this investigation were iron and silicon; their total not exceeding 0.03 pct. Portions of the wire, approximately 2 in. in length, were enclosed in stainless steel capsules for protection from the atmosphere. Bundles of these capsules, with a dummy capsule containing an iron-constantan thermocouple, were heated inside a large steel block (acting as a heat reservoir) in a closed circulating-air type electric furnace. At ap- propriate times, the capsules were removed and quenched in water. The wires were examined metallographically to determine the temperature of initial melting. Short times at temperature were used at the beginning for wire specimens of all alloys to obtain quickly the approximate temperatures at which melting could be first observed. When approximate solidus temperatures had thus been determined, equilibrium heating was attempted. This equilibrium heating consisted of an 8 or 16 hr period at a temperature, about 50 °F below the lowest temperature at which melting occurred when short heating cycles were used, followed by further heating for 1 hr periods at consecutive 10" higher temperatures. The theory for the method of stress-rupture at incipient melting has been well covereda and its limitations are recognized. Thus, if the interfacial tensions are such that the first minute quantity of liquid is "bunched up" at the grain boundary junctions instead of spreading out along the grain boundaries,³ temperatures higher than the solidus are required before melting will be manifested by rupture of the specimen. This point will be elaborated later. Specimens of the wires with a reduced section (approximately 1/16 in. diam) were suspended vertically in a tubular furnace. The setup used is shown in Fig. 1. The clamp holding the specimen was made from alumel thermocouple wire and the thermocouple was thus completed across the specimen by attaching a chrome1 wire to its lower end. Temperatures were read from a Speedomax recorder used in conjunction with a calibrated thermocouple. The small weight attached to the specimen and a vibrator attached to the furnace tube, to aid in distributing the molten constituent along the grain boundaries, were used to bring about rupture at a temperature closely approximating the solidus. The specimens were heated at a rate of about 5°C per min. The rupture of the specimens was indicated both by sound and by the action of the recorder. An argon atmosphere containing a small amount of SO² was used for protection of the specimen. The assembly was taken out of the furnace immediately following rupture and the specimen removed. Some of the broken specimens were examined metallographically and will be referred to later. Results and Discussion Fig. 2 shows a set of typical time-composition curves for liquid samples of the Mg-Al-Mn alloys used for the settling tests. The data as presented

Jan 1, 1952

By Jerome J. English, Gordon W. Powell

An experimental investigation and mathematical analysis of the thermal-dilation behavior of the titanium alloy Ti-7Al-3Cb have shown that the linear dimensional changes associated with the polymorphic transformation need not be isotropic. The absolute magnitude of the linear dimensional change, which may be either positiue or negative, associated with the cr-p transformation is dependent upon the relutzve volumes of different orientations of the transformation product. It is hypothesized that the dilation irregulati-ties that have been observed during the polymorphic transformation of pure, coarse-grained titanium and other titanium-base alloys can be explained in the same manner. When titanium is heated above about 165O°F, the hcp a structure transforms to bcc 0. Thermal-dilatioh measurements have shown that the transformation is accompanied by a decrease in length of 0.16 pct.&apos; Such dilation behavior would be expected because the volume of the hcp unit cell is about 0.3 to 0.4 pct greater than that of the bcc unit cell. A recent investigation2 of the thermal-dilation behavior of an experimental a-p* titanium alloy, Ti- 7A1-3Cb, containing 0.06 wt pct 0 showed that its dilation behavior during the polymorphic transformation differed substantially from that reported for unalloyed titanium. The first time the alloy was cycled through the transformation, the dilation curve closely duplicated that of unalloyed titanium. However, upon repeated cycling through the transformation temperature range, both the magnitude and the sign of the dimensional change associated with the transformation were observed to vary with each cycle. This investigation was undertaken to obtain additional data on the dimensional changes associated with the polymorphic transformation in the Ti-7A1-3Cb alloy and to determine the cause of the dimensional irregularities. After testing, the specimens were examined metallo-graphically. In addition, Laue back-reflection patterns were obtained from selected sections taken perpendicular to the specimen axes to determine the a orientations present in these sections. White radiation from a tungsten target and a 0.1-mm-diam collimator were used to produce the diffraction patterns. RESULTS Dilation Curves. Three types of thermal-dilation curves were obtained when the a-8 titanium alloy was heated and cooled through the transformation temperature range. These three types of curves are illustrated in Fig. 1. The type I curve represents what is considered normal behavior, because the dilation change is what would be expected on the basis of the volumes of the unit cells of a and p. The Type I1 curve is the inverse of Type I. Normal behavior is characterized by an expansion on cooling through the transformation, whereas a contraction takes place in the Type 11 curve. With Type ni behavior, no clearly distinguishable length change occurs during the transformation. No other anomalies that might be indicative of other phase transformations were observed in the dilation curves at lower temperatures. Apparently, the cooling rate was low enough for equilibrium to be reached during the 0 to a transformation. Table I lists the types of dilation curves observed during the polymorphic transformation as a function of the direction of measurement and cycle number. The A1 value was determined by extrapolating the low-temperature (a + 5 pct p) and high-temperature (100 pct p) segments of the dilation curves to a common temperature and measuring the difference in the or-dinates at that temperature, see Fig. 1. The transformation occurs over a temperature range in this alloy, so the magnitude of A1 is not an absolute value but depends on the choice of temperature. A mean temperature, T,, within the transformation temperature range was selected for the measurement. T, on cooling occurred about 100°C lower than T, on heating. The first time each of the three dilation specimens was heated to above the temperature, that is, Cycle 2, normal Type I behavior was observed. In Cycle 3, two deviations from normal behavior occurred. First, during cooling of the longitudinal specimen, a substantially larger expansion, +0.21 pct, was measured as 0 transformed to a compared with +0.03 pct in Cycle 2. Second, the thickness specimen was observed to undergo a contraction instead of the anticipated expansion on cooling. Continued cycling of the three specimens from room temperature to 2500°F produced additional changes in the dilation behavior. These changes did not seem to be related to the fabrication direction of the alloy because the values of a1 for the longitudinal, transverse, and thickness specimens varied unpredictably in magnitude and sign. Furthermore, both the longitudinal and transverse specimens showed all three types of dilation curves at least once during the six cycles that they received. Fig. 2 is a sketch of the transverse specimen after

Jan 1, 1967

By H. R. Page, A. E. Jr Lee

From the inception of zinc retorting on a commercial scale in the United States in 1890,&apos; the retort employed has undergone wide variations in its composition and manufacture, facilitating in part equally remarkable improvements in furnace capacities. The early day hand made clay retort was charged with carbonates or silicates or with coarse dead roasted concentrates mixed with a large proportion of charge fuel resulting in a relatively low zinc burden and fired 24 hr in direct coal fired furnaces. Its modern counterpart is fabricated in hydraulic presses from clay mixtures containing sizeable amounts of either silicon carbide or silica flour, charged with sintered flotation concentrates to more than three times the early day zinc burden and fired 24 to 48 hr in gas fired furnaces. This paper does not attempt to describe in detail the early day clay retort practice as it is well outlined in treatises by Ingalls,2 Lodin,3 Liehig,4 Hofman5 and others. A brief review of clay retort practice is presented together with a description of the major developments since 1912. Clay Retorts The Belgian type retort, both in the circular and elliptical forms, has been used almost exclusively. Typical dimensions of press made clay retorts around 1910 are shown in Table 1. Variations in these dimensions were used at different plants according to local conditions to a maximum inside diameter of 9 in. and inside length of 54 in. However, the effective heat penetration in a 24 hr firing cycle and the tendency of the retort to bend limited the retort size. Use of the elliptical vessel was an attempt to present a stronger cross-section resisting the tendency to bend and to increase the burden without increasing the depth of heat penetration. One exception to the 48-54 in. length was the 60 in. retort used as early as 1905 at Palmerton by means of supporting the last 12 in. at the butt end with a specially designed furnace back-wall. This backwall construction with the 60 in. retort had been developed and used at Bethlehem by G. G. Con-vers and A. B. DeSaulles. An attempt was made at Blende, Colo. to use even larger retorts of the Rhenish type based on European practice and requiring much higher furnace temperatures. Satisfactory plastic clays capable of withstanding these temperatures were not available, and the plant never operated successfully. PREPARATION OF BATCH Composition of the clay retort by weight was 40 to 50 pct raw clay and the balance "grog." Generally speaking the mix consisted of 7 parts plastic clay to 9 parts grog by volume. Principal source of the clay used was the Cheltenham vein—sometimes referred to as "St. Louis city clay." A typical analysis was A12O3-31.0 pct, SiO2-50.0 pct, Fe2O3-2.5 pct, MgO-0.3 pct, CaO-1.5 pct and loss on ignition 14.0 pct. At the smelter the clay was weathered whenever possible and then crushed to 0.08 in. or finer. Grog consisted of calcined adobies, cleaned retort scrap and cleaned refuse fire brick such as old furnace brick, blast furnace linings, and others. Saggers from ceramic plants and calcined flint clay were later used. The grog materials were ground to 0.12 m. or finer. Occasionally coke dust up to 10 pct of the mix was substituted for a part of the grog following European practice.² Particle size of the grog has a major influence on the retort properties—the larger the grain, the better can the retort withstand thermal shocks, resist bending at furnace temperatures and resist corrosion from slag; the smaller the grain, the lower the loss of zinc vapor through the retort walls. Grog forms the skeleton of the retort, and the clay shrinks around its grains to act as a binder. In the drying process, the grog has a stabilizing effect on the drying rate, decreasing shrinkage and giving up previously absorbed water to the surrounding clay to minimize the danger of cracking or checking.² Grog and clay were mixed through a horizontal pug mill with 10 to 20 pct water added, depending on whether the retort was to be formed by hand or mechanically, more water being required for the hand process. The batch or "mud" extruded from the pug mill was cut in convenient lengths for handling, stacked in piles or in special rooms, covered with wet burlap and allowed to "rot" or age from 1 to 8 weeks to increase plasticity. HAND MOLDING If the retort was to be molded by hand, the mud was repugged after the rotting period and given to the molders. Their molds consisted of 3 sheet iron or wood cylinders, each one third the retort length and defining the outer shape of the retort. Beginning with the bottom section, mud was placed in the form and tamped with a rammer

Jan 1, 1950

By W. A. Backofen, R. L. Fleischer

Single crystal, bicrystal, and polycrystal tensile tests of aluminum at 4.2°K, 77°K, and 300°K have been used to examine the role of grain boundaries in the deformation process. Results indicate that a grain boundary may affect the extent and slope of easy glide. The stage II hardening rate, on the other hand, is independent of the presence or absence of grain boundaries. This conclusion allows the size of the region of multiple slip caused by an incompatible grain boundary to be determined. For the size of bicyystal sample used in this study, multiple slip occurs in about half of the cross section. PREVIOUS studies of the stress-strain characteristics of bicrystals of face-centered-cubic metals have been limited to aluminuml-5 at room temperature. Recent results, however, indicate that the stress-strain curves of single crystals of such metals may be separated into at least three stages6 in which different deformation processes are occurring7 provided testing is done at sufficiently low temperatures.&apos; Since for aluminum a well-defined stage II develops only below room temperature, previous studies have not been able to relate effects of grain boundaries to all of the three stages of deformation. It is therefore to be expected that low-temperature deformation of aluminum single crystals and bicrystals should clarify the effects of grain boundaries on the different processes of deformation. EXPERIMENTAL PROCEDURE Single crystals and bicrystals were grown from the melt by the standard techniqueg with aluminum reported by Alcoa to be 99.993 pct pure. Ridges in the boat were used to guide the grain boundary during growth, assuring that the boundary would bisect the sample.10 The rate of furnace motion during growth was 1.0 cm per hr. During growth zone purification resulted, as evidenced by the ability of the first material to freeze to recrystallize at room temperature following severe deformation. Samples were approximately 4.4 X 6.6 mm in cross section and 103.5 mm in length between grips. Samples were annealed at 635" i 5°C for 40 hr and furnace cooled over a 7-hr period. They were then electropolished in a solution of 5 parts methanol to 1 part perchloric acid at a current density of 15 amp per sq dm for about 30 min at temperatures below 0°C. Tensile testing was performed at 295" (room temperature), 77" (sample in liquid nitrogen), and 4.2"K (sample in liquid helium) on the hard-type machine indicated schematically in Fig. 1. The machine con- sists basically of a tube surrounding a rod; one end of the sample is attached to each member, and the rod is pulled up the tube to extend the sample. The rod is rigidly mounted and is moved vertically by a system described by asinski." The pulling force is measured continuously by an electrical strain gage load cell, and the relative displacement of the tube and rod is also recorded continuously by a soft cantilever beam with electrical strain gages. Maximum stress and strain sensitivities were ±2g per sq mm and * 3-10-5. In all tests the strain rate was approximately 5.10-5 per sec. The thin wires in the tensile apparatus introduce softness, which may be corrected for, however, by measuring load vs displacement with the sample replaced by an elastic member. For loads greater than 15 kg the spring constant is 1.875.106 g per cm. The flexible wires also served to reduce substantially the large shearing forces which may arise in the case of grips having horizontal rigidity.&apos;&apos; As in any gripping system, however, bending moments will arise in the course of deformation by single slip. Engineering stress, s = (load)/(original cross-sectional area), and strain, E = (increase in length)/ (original length), are used for stress-strain curves unless otherwise indicated. Tables list resolved shear stress, T=mo and shear strain ? = dm, where m is the usual Schmid resolved shear stress factor for the primary slip system at the start of deformation. The first group of samples to be described forms an isoaxial set, all of the crystals making up the single crystals or bicrystals having the same tensile axis, the orientation of which is indicated by the cross in Fig. 2. For this orientation the primary slip plane and slip direction make angles of 45 deg with the tensile axis and the Schmid factor m has its maximum possible value of 0.5. Rotations about the tensile axis are indexed by means of an angle 0 between the small-area surface of the samples and the projection of the primary slip direction onto the cross section, as defined in Fig. 3. In single crystals, values of 0 were 0 and 90 deg, while in bicrystals 0 values were (0 deg, 180 deg), (90 deg, 270 deg), and (0 deg, 90 deg) as indicated in Fig. 4.

Jan 1, 1961

By J. J. Pye, J. B. Drew

Mzasurements of the surface diffusion coefficients of metals have been made. Diffusion profiles for the Ag-Ag system were obtained by means of a radioactive point source and a precision auto-radiographic technique. The activation energy for silver self diffusion (=8.1 kcal per mole) is lower than that previously reported (-10 kcal per mole) on poly crystalline wire by Nickerson and Parker. The bresent data indicate an effect due to parasitic volume diffusion at temperatures above 500°C. RELATIVELY few measurements have been made of the surface self-diffusion coefficients of metals. Nickerson and arker&apos; measured the diffusion of silver over the surface of poly crystalline wires and estimated that the activation energy was 10.3 kcal per mole. Winegard and chalmers2 carried out measurements on both polycrystalline and single crystal surfaces but did not report a value of the activation energy. They found, however, that at temperatures between 250" and 400°C the diffusion coefficients were on the order of lo-&apos; sq cm per sec and that there was an acceleration of the migration of silver on the polycrystalline sample when a change of surface shape occurred. Winegard and Chalmers used an autoradiographic technique, hereafter designated ARG, and Nickerson and Parker used a surface scanning geiger counter in order to determine the diffusion profiles. More recently, Hackerman and simpson3 measured the surface self-diffusion coefficient of copper at a single temperature (750°C), and the value of the diffusivity (- 10-5 sq cm per sec) is in agreement with that given by jostein from his thermal grooving measurements. This paper reports the results of an investigation of the surface self-diffusion coefficients of silver over a large temperature range and describes the adaptation of autoradiographic (ARG) techniques for the determination of diffusion profiles obtained from a radioactive point source. EXPERIMENTAL PROCEDURE The experimental procedure is a modification of the method employed by Hackerman and simpson3 in their measurements on copper. A brief description of their technique is as follows: A radioactive needle which sinters to the surface during the diffusion an- neal serves as the source of diffusing atoms. After the diffusion run the needle is removed and the surface is scanned with a shielded counting arrangement. The diffusion profiles reported in this paper were obtained by a modification of the above procedure which employs a precision ARG technique. Previous investigations in this laboratory and elsewhere51B have shown that under carefully controlled developing conditions and by the use of calibration sources a linear relation exists between the concentration of the isotope and the photographic density for values below unity. The use of ARG under these conditions has advantages over the counter scanning method in that cumbersome shielding and requirements for great mechanical precision of the scanner are eliminated. Also the ARG gives a complete picture of the surface which is advantageous in studies of anisotropic diffusion. A recording microdensitometer having a 0.1 p wide slit was employed. At low temperatures the disturbing effects of subsurface radiations are negligible. The diffusion anneals are carried out in the cell shown in Fig. 1. The needle is formed by grinding down a 1.0 mm rod of high-purity silver until a tip of 0.2 mm radius or smaller is formed. This tip is plated withA"&apos; which becomes the source of the diffusing atoms that are detected by ARG. The needle carrier and the crystal holder, Fig. 1 are constructed of quartz and ports are provided in the holder pedestal which allow free vapor circulation ((2.0 oz) and the carrier apron fits snugly over the crystal holder cap, insuring that the needle does not move and scratch the surface. Temperatures are provided by a stabilized tubular furnace which can be quickly positioned around the cell, thus bringing the crystal up to temperature in a time that is short compared to the diffusing times. The diffusion anneals range from 2 hr for the high-temperature samples to about 25 hr for those at the lowest temperature. The possibility of vapor transport of the radioactive metal as a contributing factor in the diffusion profile was investigated in two ways. One method was to suspend the needle directly over a dummy sample, raise the temperature, for periods of time equal to the diffusion times, and then take an auto-radiograph of the surface. Negligible radioactivity appeared. In the second method a thin slot in the crystal face on one side of the source provided a "cong path" for surface diffusion. If evaporation was the primary source of surface atoms the region of radioactivity around the source would be symmetrical. This was not the case. The profile dipped abruptly at the edge of the slot but on the other side of the source the usual diffusion profile appeared.

Jan 1, 1963

By Mehl, Robert F.

IT has been shown by numerous studies that the orientations of new metal crystals are determined by the orientations of the crystals in the original matrix, whether these new crystals are formed by recrystalliza-tion, by precipitation from solid solutions, or by transitions in the solid state. The orientations of crystals formed by recrystallization of cold-worked worked metals that bear preferred orientations are occasionally simply related to the initial preferred orientation; often, however, the relation-ship is not simple, but complicated and obscure in origin.1 The orientations of crystals formed by precipitation from solid solu-tions have been shown by many studies in this and other countries to be determined by the orientation of the crystals of the solid solution stable at the higher temperatures, though here again complicated cases have been found and no general theory is available .2 Related to this latter class

Jan 1, 1934

By Francis H. Brownell

During the 1920&apos;s lead consumption in the United States reached the highest average total ever known. For the ten-year period 1921-&apos;30, it was slightly over 600,000 tons per year, or say 50,000 tons per month, and the price averaged 6.81 per lb. But the I930&apos;s witnessed a severe drop in the consumption of lead is in other business activities. The average U.S. consumption for the ten-year period 1930-&apos;40 was slightly less than 380,000 tons per year, or under 32,000 per month, with the average price dropping to 1.191c. per lb. The outlook in early 1939 was for a continuation of this average consumption and price a demand of 35,000 to 40,000 tons per month, and a price level of 4 1/2 to 5c. in the United States.

Jan 1, 1941

By Grafton M. Thrasher

For the proper discussion of this subject it is necessary to incorporate in this paper the substance of part of an article published by me in Metallurgical and Chemical Engineering for January, 1915. Several years ago, while I was chief chemist for a malleable-iron company, it occurred to me that the mere regulation of silicon was not sufficient to produce the desired degree of chill. But only after repeatedly encountering this fact in both open-hearth and air-furnace, as well as cupola metal, was I led to regard variation in the total carbon as the principal cause of disturbance; and I resolved to determine the total carbon as well as the silicon in every heat, and by a carefully prepared test piece to gauge the approximate degree of chill. The test piece selected was a round plug, 2 in. in diameter and 12 in. long, cast on end

Jan 1, 1916

To Install Waste Heat Boiler at White Pine White Pine Copper Co.&apos;s smelter 18 miles southwest of Ontonagon, Mich., will have a six story high boiler utilizing what otherwise would be waste heat from a copper reverberatory furnace. Designed and under construction by the Babcock & Wilcox Co., the boiler will supply steam to a turbo-generator furnishing power for the projected development. The boiler will be in line with and following the reverberatory furnace. Using waste heat from the furnace in place of fuel for steam generation, about 50 pct of heat in the fuel originally supplied to the furnace will be recovered by the waste heat boiler. Exploration conducted over the past 15 years at White Pine, wholly owned subsidiary of Copper Range Co., has disclosed reserves of 309 million tons averaging 21.3 lb of copper per ton. Ore mineral is chiefly chalcocite (Cu2s).

Jan 5, 1953

By W. Rostoker, S. A. Spachner

STUDIES of precipitation phenomena by use of X-ray diffraction effects have shown that atoms of the precipitating phase initially form lattices of limited periodicity in two or three dimensions.1, 2 Such diffraction effects are usually plotted in reciprocal space to facilitate identification. Atomic chains, or gratings possessing unlimited periodicity in only one dimension, cause uniform intensity planes in reciprocal space. Platelets, or gratings possessing unlimited periodicity in two dimensions, cause uniform intensity rods in reciprocal space. Such studies have been accomplished by use of white radiation (Laue technique) or characteristic or monochromatic radiation used with rotating single crystal or Weissenberg cameras. Each one of these techniques have associated drawbacks. If the Lque or rotating single-crystal technique is used, the results which are obtained may be ambiguous.3 Diffraction photograms made with a WeisSenberg camera do provide a direct but distorted representation of the variation of diffracted

Jan 1, 1960

By Gligorije Stankovic

This paper describes the fluo-solids roaster and acid plants at the new 40,000-TPY Trepca electrolytic zinc plant. The electrolytic zinc plant units were constructed to the design of Singmaster and Breyer, New York and began operation in mid-1967. The fluo-solids roaster plant, constructed according to the design of Dorr-Oliver, Paris, includes concentrate handling and storage facilities; two independent concentrate roasting circuits, each with a 110 to 155 TPD fluo-solids roaster; waste heat boilers; cyclones; electrostatic precipitators; calcine coolers; and calcine conveyors. The acid plant uses the "Petersen system" contact process. The plant has one acid circuit with a capacity of 230 tons of monohydrate per day. Gases for the acid plant are obtained from roasting zinc concentrates. When the roaster plant is operating at maximum capacity, excess SO2 is used in two other Petersen System circuits in the near vicinity.

Jan 1, 1970

By Oscar Aguilar, Jin-ichi Nakamura, Kazuo Nakamura

Michiquillay deposit is porphyry copper type with over 500 million tons of 0.70% Cu ore. In order to reflect the true nature of the orebody as to shape and value distribution and to compensate for insufficient data in the outer perimeter and lower portion, "Triangular Interpolation Method" is used in the computation, wherein block grades are determined by "Plane Regression". The results thus obtained are compared with the data from additional investigation and are found to match well with each other. Aside of total Cu, assays of Fe, S, MoS2 and geological data such as alterations, rock types, faults, mineralogical compositions are also stored in the computer. By this system, their distribution and relation to alteration become clear and classification of ore into types affecting recovery become possible. The outputs of this system make clear the characteristics of the orebody and furnish valuable geological data on the orebody.

Jan 1, 1976

By Paul Billingsley

THE term Boulder batholith was first applied in 1897 by W. H. Weed&apos;2 to the extensive mass of granite in western Montana within whose borders occur the ore, deposits of Butte. In a general, way this was known to extend from Helena on the north to the Highland Mountains near Butte on the south, and to be relatively narrow in its east-west diameter. Its intrusive relations to the surrounding sedimentary , rocks, and its probable Tertiary age, were described by Weed, but in many ways his statements, based upon incomplete data, have required revision. Most notable of the errors of this description of the batholith were the failure,3 since corrected, to recognize the intrusive contact of the granite with the capping of andesite, and the complete absence of any reference to the many extensions of the granite beyond the somewhat narrow limits of its largest exposure.

Jan 1, 1915

By J. J. De Witte, J. G. Cazort

The Paranam plant in Surinam (formerly Dutch Guiana) was built during 1939-40 to supply crushed and dried bauxite for the growing U.S. aluminum industry, supplementing production from the Suriname Aluminum Co.&apos;s Moengo works, which began operation in 1922. A subsidiary of Aluminum Company of America, Suralco&apos;s total annual production from these two plants averages 2.55 million dry metric tons of various grades of bauxite. Starting in 1941 with bauxite from mines on the west side of the Suriname River, annual production at the Paranam plant has varied from a low of approximately 450,000 tons to more than 1 million tons in 1949. High production rates during World War II and the late 1940&apos;s rapidly depleted these reserves, and in 1950 plans were made to mine the known deposits on the east bank of the river, about five miles downstream from the original Paranam plant.

Jan 11, 1960