By Carle R. Hayward

This work was first undertaken in the metallurgical laboratory of the Massachusetts Institute of Technology in 1907 by L. A. Dickinson, E. Phelps, and V. S. Rood, under the author's direction. They attempted to determine the diagram for the system Cu2S-MiS, but several inexplicable results were obtained. The following year, P. H. Mayer with Mr. Dickinson carried on some experiments with nickel sulphide and found that the molten material slowly lost sulphur until it reached a composition corresponding to the compound Ni3S2, established by Bornemann.l At this point the composition remained stable. The freezing points of the mixtures gradually fell off with the loss of sulphur. Since the above facts seemed to explain the erratic results obtained in the first experiments, Mr. Mayer with F. Jaeger attempted in 1910 to establish a correct equilibrium diagram for the Cu2S-Ni3S2 series. They prepared pure Cu2S and Ni3S2 and determined the cooling curves for various mixtures. The fusions were made in a platinum resistance furnace and the temperatures were measured with a platinum-iridium thermocouple connected with a Sullivan galvanometer. The curve was established for mixtures containing more than 40 per cent. Cu2S, but they were unable to determine certainly the direction of the curve beyond that point. Nothing further was attempted with this series until the present year, when the work was carried to a successful conclusion with the assistance of A. Butts, Jr., and E. H. Weil. The results of this work are given in the following pages. Preparation of Cu2S.—A piece of cathode' copper from the Buffalo plant of the Calumet & Hecla Co. was cut into shavings by a shaper and converted into sulphide by heating in boiling sulphur. A porcelain casserole was used for the purpose, the heat being furnished by a Bunsen burner. It was found that after boiling in the sulphur for an hour the copper shavings were completely converted into sulphide. The liquid sulphur was then poured off, leaving the solid sulphide in the casserole in

Jan 1, 1915

By Richard Borg

The partial molal free energy of Cd in each of the four intermediate phases, Cd3 Cu, Cd8 Cu5, Cd3Cu4, and CdCu2 is determined using the Knudsen vapor pressure technique. Measurements are made also within the two-phase regions, and thus the variation in FCd is now known across the entire phase diagram. The absolute values are all less the 2.0 kcal and increase regularly with increasing Cd concentration. The small absolute value of the free energy precludes the possibility of obtaining highly accurate values; nevertheless, the results are compatible with those previously reported for the liquid phase. Additional results are reported concerning the lattice parameters of the 6, E, and b phases. THE elements Cu and Cd combine to form four intermediate phases which are designated* and E and which include respectively the following inter metallic compounds: CdCu2, Cd3Cu4, Cd3 Cu5, and Cd3 Cu. The extent of each phase with respect to temperature and composition is shown in Fig. 1 which is the equilibrium diagram drawn according to Hansen.1 All four phases are brittle, and most probably are true intermetallic compounds. Only the crystal structure of the 6 phase has been thoroughly investigated.2,3 The structure is cubic and isotypic with y brass. The structure of Cd3 Cu has not been previously reported, It is hexagonal with a = 8.11 and c = 8.76 0.02Å and the structure is presently being determined.* The compounds Cd3 Cu4 and CdCu, have been each previously the subject of a single investigation. Cd3Cu, is presumed to be cubic4 with the space group Fd3m, whereas CdCu2 is hexagonal2 with the C14-type structure. Cu2 Cd is found by X-ray analysis to be hexagonat with lattice parameters a = 5.00A and c = 16.17Å. The material appears to be pure Cu2Cd as all reflections could be indexed on the basis of the single hexagonal structure. These values disagree with those of Kripyakevich and coworkers5 who report a = 4.96Å and c = 7.98Å. Their investi-

Jan 1, 1962

By J. Chipman, J. C. Fulton

Reduction of silicon from blast-furnace-type slags by carbon-saturated iron is a very slow reaction even under conditions of rapid stirring. Equilibrium under atmospheric pressure of carbon monoxide was approached from both sides, and the silica-silicon relation was established at temperatures of 1425º to 1700°C for slags containing up to 20 pct Al2O3. Silicon carbide is formed by reaction of graphite with high silica slags and the conditions for its formation were determined. Activities of SiO2 and of CaO in their binary solutions at 1600°C were determined. The effects on the activity of SiO2 were established for additions of 10 to 20 pct AI2O3 and of 10 pct MgO. STUDIES of chemical reactions between blast-*>-5 furnace slags and metal have been focussed on the transfer of sulphur from metal to slag. The important role which silica reduction plays in this process' has led to a study of the transfer of silicon from slag to metal and the equilibrium represented by the equation SiO2 (in slag) + 2C (graphite) = Si + 2CO (g). [I.] The authors2 have published an account of the experimental method employed in attacking this problem and of three series of experimental results at 1600°C. This paper contains data on some additional compositions and extends the observations to cover the temperature range 1425° to 1700°C. The data are used to determine the activity of silica in the slags. As in the earlier experiments, the atmosphere was carbon monoxide which flowed through the furnace at 150 ml per min. In certain heats designated in the tables and figures, the gas was bubbled through the melt using a graphite tube. The latter increased in porosity during a run and in some cases bubbling ceased as indicated by cessation of surging. Some results were discarded for this reason. Experimental Results The new data are shown in Tables I through V and both old and new data are plotted in Figs. 1

Jan 1, 1955

By A. Weiss, W. A. Coster

The search for ore is characterized by a great variety of uncertainties, each of which can be resolved by obtaining information at a cost. Three exploration stages may be distinguished in which information can be obtained, based on inherently different cost structure: 1) the reconnaissance or scanning stage, 2) the examination or screening stage and 3) the project stage. This exploration sequence would roughly coincide with replies to questions as to: where, how, why and how much. As complete information in each stage is too costly to acquire, we must assess the probability that adequate information will be furnished by a limited amount of effort and attempt to maximize the expected value of ore to be found for a given exploration expenditure. Several problems are discussed relative to the mathematical formulation and possible computer procedures for determining the optimum allocation of a total exploration effort. Based on the available literature possible solutions to this problem are indicated. When scanning through published literature on mineral exploration, it seems at first that there is little room for substantial and systematic improvements in the efficiency with which the problem of discovery of new ore deposits is presently being handled by large organizations active in exploration. It appears equally difficult to offer something relevantly new which could generate a break-through in exploration thinking and cause a marked improvement in the ratio of successful undertakings to the total exploration projects started. On the other hand, a number of experts in recent years have urged that the problems in prospecting be analyzed in a more skillful and sophisticated manner than in the past. Their thesis is based mainly on the premise that the cost of finding mineral deposits will increase with increasing technical difficulties. In present large-scale exploration ventures, especially in those regions where outcrops and immediately visible geologic evidence are scarce, older methods of prospecting are increasingly being replaced by more indirect and systematic geophysical and geochemical methods with more emphasis on correct statistical design of exploration patterns. It is perhaps the oil industry which has made the greatest strides in developing statistically, well justified patterns in its search for oil; possibly because oil seepages, as indicators of the presence of oil, left off at an earlier point in time than did outcrops as indicators of base metals. Among the pioneers in the field of statistics and operations research, as applied to mineral exploration, the excellent works of Allais, Slichter, Koop-man, Mickey, de Guhnin, Krumbein, Griffith, Sichel, Krige, de Wijs, and Matheron may be mentioned. It should, however, be pointed out that three subjects of basic importance to the allocation of exploration efforts have so far received only scant attention in published literature, even by the aforementioned authors. In the first place, a more precise definition of the object of the search, i.e., a minimum-size orebody, seems to be outstanding. Secondly, a decision model is not a widely-discussed subject. Thirdly, no concentrated attempt so far seems to have been made to establish probabilities of the occurrence of economic deposits on a regional scale and to arrive at a slightly more accurate knowledge of the probability laws governing the deposition of ore. It is not the purpose of this paper to create new order in the complexity of uncertainties in which our decision processes in exploration necessarily have to be conducted. Rather, we intend to highlight some of the outstanding, hitherto unmapped territory, where diligent compilation and a utilization of present and historic data may statistically improve our chances of success. We hope that the contribution of this paper will lie in bringing allocation problems into better focus and in increasing the mineral industry's realization of the magnitude of the factors involved. THE MINIMUM-SIZE OREBODY The concept of target specifications for what constitute a minimum-size orebody in exploration is a rather variable one and depends to some extent on

Jan 1, 1963

NAME "Utah" is derived from the name of the Indian tribe, variously spelled "Yuta," "Ute," "Youta." "Uta." "Eutaw," and finally "Utah." It means "in the tops of the mountains," or "on the heights." The state emblem is the "Beehive," typical of industry. State nickname is "Beehive State." AREA Utah is the tenth state in area. It contains 84.990 square miles, of which 2.806 miles are water. When admitted as a territory in 1850. Utah included all the area from the east line of California to the summit of the Rocky Mountains between the 37th and 42nd parallels, which embraced practically all of the present state of Nevada, all of western Colorado, part of Idaho and part of Wyoming, in addition to the present area of Utah.

Jan 1, 1925

By H. I. Smith

THE technical and safety press have devoted much space in support of or in opposition to the use of booster and auxiliary fans in coal mines. The Mine Safety Board of the U. S. Bureau of Mines has given the matter consideration, and the Mine Ventilation Committee of the A. I. M. E. is now seeking a discussion of the merits and demerits of such fans to guide it in formulating recommendations. In this paper, I will set up some principles on which I believe most engineers will agree and from which we may work toward a decision, though as to what that decision shall be there may be a difference in opinion. Before stating the points on which I believe. there is accord, I will distinguish between booster and auxiliary fans.

Jan 1, 1927

By Henry F. Hebley

This paper brings within the compass of one comparatively brief article a general description of the situation concerning the nation's water resources. It touches upon the phenomenal growth in the demand for water supply and emphasizes the problems facing the coal industry both with regard to acid mine water drainage discharged from active and abandoned mines and the suspended solids discharged to the stream system from wet coal preparation plants.

Jan 4, 1953

Jan 1, 1890

By Wm. Reuben Webster

BRASS is an alloy of copper and zinc. The brasses (using this term to denote all useful proportions of the two constituents) are the most valuable and widely employed of all [ ] nonferrous alloys, because of their high resistance to ordinary corrosive agencies and the very wide range of properties that may be imparted to them by variations in the proportions of the constituents and by variations in mechanical treatment and heat-treatment. Fig. I shows the normal physical properties, as determined by standard tensile tests, of the series when in the annealed condition. Fig. 2 shows the effect of varying amounts of cold-working on an almost pure brass containing 70 per cent copper and 30 per cent zinc. Fig. 3 shows the effect of annealing at various temperatures on the same alloy. This effect is somewhat modi [ ] fled by the degree of cold-working to which a brass has been subjected, as shown by Fig. 4. A fourth test, which is empirical, has been found useful because of its simplicity -the hot hammer test. Samples Y2 in. in diameter and ¾ in. long are placed in a suitable furnace. These are withdrawn one at a time at successively higher tempera¬tures and are subjected to the blow of a drop hammer weighing 50 lb. with a drop of 4 ft. The percentages of' reduction in length of the cylinders are plotted against temperatures and give a comparative measure of plasticity at different temperatures. The results of this test on several

Jan 1, 1942

By Oliver C., Ralston

THE following data were obtained during Tan exhaustive research into the possibilities of concentrating United Verde massive sulfide copper-zinc-iron ores by flotation. The composition of these ores approximates the following mineralogical analysis: 3 to 15 per cent chalcopyrite; 3 to 11 per cent marmatite (ferruginous sphalerite) ; 47 to 69 per cent pyrite; and 10 per cent quartz. The remainder is usually schist gangue. The sulfide minerals are finely dis-seminated; chalcopvrite and marmatite begin to be liberated on grinding at about 100 mesh, but complete liberation from gangue (pyrite in this case is considered a gangue mineral) is

Jan 1, 1935

By Irving B. Cadoff, Stojan M. Zalar

AgInTe2, CuInTe2, and all Proportions of CuxAg1-xInTe, forMed homogeneous single phase alloys after direct solidification from the nielt. X-ray analysis indicated a zinc-blel~de strzccture typical of the chalcopyrite compounds, and the electrical resistivity and Sccbeck coefficient values were in the semiconducting range. AuInTe, and AuxA4g,-, InTe, formed by what appeared to be a peritectic reaction (the thermal analysis curves showing more than one arrest) and were conseyue~ztly polyphase. Substitution of copper into AgIrzTe, resulted in a continuous transition in the room tenzperature Seebeck coefficient from the negative AgIzTe, to the positive CuInTe,. A zero coefficient was obtained at about Cuo.55 Ago.45 InTe, . The temperatzire variation was similar to that observed for the stoichiometric compounds, that zs, tendency towards "p" concEuction at elevated temperatures. The thernzoelectric figure of merit for the compo~uzds, as determined by the Putley -Harmnn method were in the range 10- to 10-7 "K-l; the thermal conductivities in the order of 0.15 cal per sec-cm-oK. INCREASED interest in semiconducting intermetallic substances is expanding much of recent research from simple binary compounds into polyatomic systems and solid solutions. Ternary compounds A' represent a covalent extension of the binary semiconductors Within the a tin isoelec-tronic series, Ag-Cd-In-Sn-Sb-Te-I, divalent cadmium atoms in CdTe are being substituted for by monovalent silver and trivalent indium atoms to form the compound AgInTe, . By cross-substitution with elements of other isoelectronic series, a great number of ternary compounds A 'B"'c? is possible. In all of them, however, a necessary though not sufficient condition for the covalent, semiconducting bond—that there be four sharing orbital electrons per atom—must be fulfilled. In AgInTe,, each silver or indium atom is tetrahedrally surrounded by four tellurium atoms, while each tellurium atom is co-valently bound to two silver and two indium atoms. Synthetic chalcopyrites A'B"'c~ were first recognized as potential semiconduct&rs by Goodman and Douglas.' Austin, Goodman, and Pengelly discuss preparation difficulties and some electronic measurements on AgInS, , AgInSe, CuInSe, , AgInTe, , and CuInTe,. Chalcopyrites A B c2v are mentioned in papers attempting to classify and predict semiconducting behavior of intermetallic compounds; on the basis of saturated tetrahedral sp3 bonds,3 by specific selection criteria,' and by crystallographic considerations."

Jan 1, 1962

By J. A. Kitchener, J. P. Anfruns

Measurements have been made of the rate of capture of single particles of strongly hydrophobic, surface-methylated, quartz, of sizes ranging from 12 to 40 µm diam., by single rising bubbles of diam. 0.5 to 1.1mm. The results agree closely with the theoretically calculated hydrodynamic collision rates, indicating that, in this system, every collision results in capture and retention of a particle.

Jan 1, 1976

Jan 11, 1951

By J. B. Goddard

Crystallization of ammonium paratungstate (APT) is frequently the last effective purification step in producing high-purity tungsten. However, crystallizer mother liquors are often several times higher in tungsten than predicted by the solubility of APT. The formation of heteropoly anions, particularly those containing phosphorus and silicon, is largely responsible. Solubility of tungsten in APT mother liquor can be linearly correlated with the concentration of these and other impurities. The problem can be overcome by direct treatment of the crystallizer feed solution with aluminum sulfate. By appropriate treatment, the aluminum hydroxide flocculates and is easily filtered, resulting in a purified low-aluminum crystallizer feed from which high APT yields can be attained.

Jan 1, 1985

By C. H. Cheng, C. E. Birchenall

The fundamental problem in the thermodynamics of solid solutions is the determinatiorl or calculation of the activities of the components as a function of temperature and composition. Since the theory of metals is not suficiently developed to allow a priori calculation of these quantities, they must be obtained from experiment. C. Wagner1 has reviewed the literature of this subject for the period before 1940. Although several important and extensive studies have been made in the meantime, the number of systems to which any sort of quantitative information can be assigned is vanish-ingly small. These data have become of great potential importance in studies of the structure of solid solutions2 and intermetallic compounds, the nature of the diffusion process,3,4 and perhaps even the mechanism of mechanical deformation.5 For these reasons, it. seems very worthwhile to extend the experimental data in this field. Although there is little use in duplicating Wagner's review, attention should be directed to the most recently reported investigations. A brief enumeration of the methods of measurement previously employed also should be valuable. The most direct method is the determination of the partial pressure of the components in the vapor phase in equilibrium with the solution. Both equilibrium and kinetic methods have been tried in metal systems, but almost exclusively on liquid phases. Only in the ease of carbon in iron alloys and in the copper-zinc system have extensive measure- ments been made which include solid phases. When one of the components is an element, such as nitrogen or carbon, which forms compounds which are very volatile and stable at normal temperatures and pressures (CH4, Co2, CO NH3), it is frequently possible to equilibrate mixtures containing these (such as CH4-H2, CO2-CO, NH3-H2) independently with the elernents (C, X) and with the metal (Fe, Ni, etc.). Such measurernents have been made for carbon in iron, iron-silicon, and iron-manganese alloys by Smith6 and in iron and iron-nickel alloys by Toensing.7 Differences between carbon activity values at the same temperature and carbon content when carboil is introduced from CH4-H2 rnixtures or CO-CO. mixtures indicate that the effects of hydrogen and oxygen in the system are not negligible, and one can only hope that the true value lies somewhere between these sets of results, probably nearer the CH4-H2 data since hydrogen is less soluble in iron than oxygen. This is essentially an equilibrium method, although flowing gas is employed. A kirletic method has been employed which consists of sweeping an inert gas (generally hydrogen) over the alloy at a series of rates, condensing the metal vapor out,, and analyzing it. The metal content can be extrapolated to zero flow rate (equilibrium). Wejnarth's8 work on Cd-Mg and Zn-Mg is a good example of this frequently used method. A variant of this consists of equilibrating a known volume of inert gas with the alloy, sweeping it out quickly, and analyzing for metal. In common with the above method, it has the disadvantage that the "inert" gas is generally somewhat soluble in the alloy. Moreover, the former continuously displaces the system from equilihrium and may give low values if solid diffusion is involved. The dew point method applied by Hargreaves9 to the alpha and beta brasses and by Schneider and Stolll0 to A1-Zn avoids the introduction of another component to the system, but is useful only in systems in which one component is much more volatile than the other. The alloy sealed in one end of an evacuated silica tube is heated to the desired temperature. The temperature of the other end is lowered until droplets of the volatile component condense. When the temperature is raised slightly, the droplets will evaporate. By careful adjustment of temperature, the range between evaporation and condensation can be narrowed appreciably. An independent determination of the vapor pressure of the . pure volatile component is necessary to give the partial pressure over the alloy. This is the method employed here to determine the vapor pressures of zinc and cadmium over their silver alloys up to 34 pct in cadmium and 76 pct in zinc. The former involves only the a solid solution, but the latter covers the a, ß, y, and e fields. In recent determinations, Herbenar, Siebert, and Duffenbarkl1 used the

Jan 1, 1950

SINCE it seems to me that guns are of greater importance in the art of casting than any of the other things that are made by it, and that they require more foresight and care because they need many perfections, I wish now to repeat certain useful and necessary precautions in corroboration, for though I have already spoken to you of them in some detail, the power has not been granted me to pass with one breath completely through a subject with many parts. Therefore it will not be wearisome to you to hear the same thing told again, because it will not be without amplification of some pertinent points. For this reason I have prepared the present discourse, which I have called admonitions. The first of these concerns the making of the pattern upon which the

Jan 1, 1942

By Ralph K. Foster

During five underground mine fires which occurred in Arizona during 1980 and 1981, sealing the fire area became necessary. To minimize leakage into the fire area, ventilation control measures were instituted to balance pressure across the bulkheads. Problems en- countered in sealing the fire areas and measures taken to improve these conditions are discussed. The routing of the ventilation and ventilation control to en- sure the workers' safety were also important considerations in reopening the mines. The use of continuous CO monitors is discussed. One important consideration was the condition of the fire, and chromatographic analysis was used to establish this. Graphs comparing the Trickett ratio, carbon monoxide, carbon dioxide, and oxygen concentrations are given. The Trickett ratio was useful but needed to be augmented by the comparison of CO, C02, and 02. Problems with getting good samples from sealed areas and recommended procedures that were developed during these fires are discussed.

Jan 1, 1982

By B. L. Sackett

LEAD smelting has been an important industry in Utah for many years. The first lead smelting was done, over 60 years ago, at the Rollins mine in Beaver County, by burning heaps consisting of alternate layers of wood and high-grade carbonate ore. The lead thus obtained was. molded into bullets. With the development of. the mines, the problem of cheaper handling of the ore became important. The only outlet for this ore was Swansea or the Atlantic Coast but to ship to either cost $150 per ton or more for treatment and handling. From 1864 to 1871, experimenting was done with blast, Scotch hearth, and reverberatory furnaces, with the blast furnace surviving as, the standard plant. The first crude furnaces were circular or hexagonal in shape, and were made of adobe and stone, which quickly burned out. They were small, about 2 1/2 ft. in diameter, and smelted from 3 to 10 tons. in 24 hr. The metal had to be tapped from the bottom of the crucible, necessitating a shut down of the furnace during this process. This pro¬cedure caused salamanders to form around the tap hole when the furnace was started again, which frequently resulted in freezing. The campaign lasted until a tap of bullion was made. The first successful plant of the crude stone type was operated in 1870. From 1870 to 1872, there was a smelter building craze in the state. During that period, about 20 furnaces were built, chiefly near the mines, and their operation was limited and sporadic. The work was then placed in the hands of trained metallurgists, who standardized on the rectangular form of furnace. In 1871, Daggett, at the Winnamuck mine in Bingham, installed water-jackets around the smelting zone of the furnaces. These furnaces were circular; the diameter at the tuyere line was 3 ft. 6 in. and at the charge floor 5 ft. 3 in. The height from tuyere line to charge floor was 14 ft., height of tuyere line above top of crucible was 3 ft. 8 in. Fur-

Jan 8, 1925

By O. W. Ellis

THE writer has dealt with the effect of various methods of melting copper upon the gas content of the metal.1 The copper referred to in his in his earlier paper was melted in the foundry both in the oil furnace and the electric furnace. As the metal, did not measure up to conductivity FIG. L -INGOT OF OVERPOLEP COPPER. standard, the term "casting copper" was applied to the material in the title of the paper. It was thought that some information in regard to the gases in a sample of overpoled copper might also be of interest, and through the courtesy of C. R. Stevens, superintendent of the copper mill of the Westinghouse Elec. & Mfg. Co., such a sample was obtained. The metal was chill-cast in the form of an ingot about 7 in. long, 2 ½ in. deep (from the base to the raised surface of the ingot) and from 1 3/8 to 1 7/8 in. wide. A photograph of part of the ingot is shown in Fig. 1. The effect of overpoling on the surface of the metal is here quite clearly shown.

Jan 1, 1929

By Walter Harvey Weed

The Republic of Mexico is traversed by many mountain ranges, and presents a great diversity of climates, soils and geographical features, yet its grander geographic provinces are few and peculiarly well defined. The Gulf plain, the Cen tral plateau, the Sierra Madre, and the lowland or Tierra Cali ente of the western coast are the main features of the geogra phy of the Republic, and in the northern half these provinces are particularly well defined. The Sierra Madre separates the Republic into eastern and western parts, and from the City of Mexico north to the Texas line presents an almost impassable barrier to east and west travel. On the north, the first wagon road pass from east to west is at El Paso del Norte, the site of the Texan city of El Paso. Southward for many hundreds of miles the Sierra Madre, traversed by well-worn trails, over which all travel from the west coast to the interior must pass, is a stupendous barrier to social and commercial intercourse. The Sierra Madre is commonly described as a range or con geries of mountain ranges. In fact, it is, in Chihuahua at least, a great plateau, fringed by mountains on the east, trenched by deep canons in its center, and bordered by a wild and rugged complex of mountains carved out of the plateau on the west. Professional duties took me across this region from Parral westward to the Gulf of California via Guadalupe y Calvo. As it includes some of the great ore-deposits of Mexico, and its geological features have never, so far as I am aware, been described, I have prepared a diagrammatic section made from my observations on a horseback trip across the Sierra, and added such notes as seem to be of general interest.

Jan 1, 1902