By Glenn C. Waterman

Richard Strong (Oliver Iron Mining Div., U. S. Steel Corp.)—Mr. Waterman states (p. 59, Trans., January 1954): "Core-sludge combining factors have been calculaied for any combination of core-sludge recovery on the basis of several logical assumptions: 1—The sludge sample loses reliability geometrically as sludge recovery drops. 2—The sludge sample should not be used if the percentage of sludge return is less than the percentage of core recovered. 3—A core sample should receive a weighting at least equal to the percentage of core recovery." Assumptions 1 and 2 seem justified at Chuquicamata and most geologists would agree to the validity of assumption 3. However, contrary to the statement quoted above, the core sample does not in general receive a weighting at least equal to the percentage of core recovery when the Chuquicamata methgd is used. Furthermore, the basic Chuquicamata method is identical to the Longyear or relative volume core-sludge assay combining method. Finally, the Chuquicamata method does not, in its present form, reflect true geometric loss in sludge sample reliability according to the relationship L = AR (N-1) The basic equations representing the two steps of the Chuquicamata method can be combined algebraically as follows (using the symbology of the original article except as noted): Vol A + B Assay 2 = ASA = Assay 1 Vol A VolB Core Assay [I] Vol A CA.F + ASA (100 —F) Combined grade =[21 100 Pct where F and (100 — F) are the core and adjusted sludge assay factors from Fig. 3. Substituting Eqs. 1 and 2 and collecting terms Combined grade = Vol B Vol A + B CAF (100—-F) + Assay 1 (100-F) Vol A Vol A 100 pct Eq. 3 is a unified and general statement of the Chuquicamata method. The true core factor includes not only the factor F from Fig. 3 but also the quantity VolB ------------- (100 — F), which is implicit in the value of Vol A the adjusted sludge assay. This quantity is real and positive for all values of F and core recovery less than 100. Therefore the true core factor is always less than F except when F is equal to 100. If sludge recovery is 100 pct, Eq. 3 can be further simplified as follows: Let F = percentage of core recovered. Let Vol A = Vdh (100 Pct — Pct CR) where Vdh is the total volume of the sampled interval and let Vol B = (Vdh — Vc.) Pct CR where V, is the core volume in the sampled interval at 100 pct core recovery. Then combined grade = Vo V. CA Pct CR- + Assay 1, 100 Pct — Pct CR Vdh Vdh [4] 100 Pct Eq. 4 shows that when sludge recovery is 100 pct the laboratory sludge assay receives significant weight in the Chuquicamata method, even at 100 pct core recovery. The maximum weight assigned to the laboratory sludge assay depends on drillhole size, as follows: Eq. 4, with suitable changes in symbology, is identical to Royce's formula 8,' which is a statement of the Longyear or relative volume method of combining core and sludge assays. If Mr. Waterman's assumption 3 is of paramount concern to the geologist, the Royce method (for core recoveries of 60 pct and above) or a method employing the percentage of core recovered as a core weighting factor are the only recognized methods known to the writer which achieve the desired result. A modification of the latter method embodying Mr. Waterman's assumptions 1 and 2 would result from applying the factors from Fig. 3 directly to the laboratory core and sludge assays.

Jan 1, 1956

DEVELOPMENT of a chemical process for the extraction of pure metals from mill concentrates or metal scrap has progressed beyond the pilot plant stage and may prove an important adjunct to present smelting and refining methods if initial commercial operations prove economically successful. Developed by the Chemical Construction Corp., the new process involves the treatment of oxide and sulphide ore concentrates by chemical methods, instead of the usual smelting and refining techniques. Several of the many applications are now scheduled for commercial use. Refiners using the new process will prepare ore concentrates by standard flotation methods, introduce the concentrate as a slurry into an autoclave along with water and an acid or ammonia. From the resulting leach solution, recovery of individual metals is made by use of suitable reducing agents. By varying conditions during treatment, different metals in the ore are produced separately as pure powders, which may be pressed into forms ready to market, or in the case of copper, extruded as rods or pipe. The reagents are generally recovered. By manipulating the variables during reduction, selective separation of nickel, and/or cobalt, and/or copper can be made simultaneously. The separation is a continuous operation. Low metal prices are not immediately in view because of the tremendous demand at this time. However, reduced metallurgical treatment costs will allow economical mining of orebodies with lower metal content, permitting increased production to meet demand. Although the practical horizon for use of the new process appears to be limitless, one factor may enter into its employment. Just how low grade a concentrate can be economically used is unknown. In addition, for present practical considerations, only metal below zinc in the electromotive series may be processed. Each commercial application requires specific technique adaptation and pilot-plant data for engineering design. A nickel-cobalt-copper process has been researched and piloted in collaboration with Sherritt Gordon Mines, Ltd., for the firm's Lynn Lake properties. In addition, processes were tailored for cobalt concentrates of Howe Sound Mining Co., and National Lead Co., in view of the urgent need for this specific metal. Major General William N. Porter, president of Chemical Construction, says of the new process, "piloting experience has shown that production cost, from ore concentrates to pure metals should be considerably below current costs." Other savings may be realized by cutting transportation and personnel costs, and by reducing the time lag between mining and pure metal from months to a matter of hours. First commercial use of the process will start sometime this summer. Chemico is slated to finish building a $2.5 million cobalt refinery for Howe Sound Mining near Salt Lake City. The plant is expected to raise world cobalt production by 40 pct. The plant will process 35 tons of 20 pct cobalt concentrates from Howe Sound's Blackbird mine near Cobalt, Idaho, daily. Yearly production is expected to reach 2000 tons of pure metal, about one half of U. S. consumption in 1950. Steps in the Howe Sound application of the process are: 1. Acid oxidation leach. 2. Filtration (residues thrown away are insoluble compounds-gangue, iron, arsenic). 3. Cementation (for Cu removal because Cu content is too low for recovery). 4. Reduction from ammoniacal solution. 5. Separation of Co and Ni as mixed metals (95 pct Co and 5 pct Ni). 6. Recovery of ammonium sulphate. Under construction at the Fredericktown, Mo., mine of National Lead is a $5 million refinery sched- [ ]

Jan 1, 1952

By W. R. Wilcox

The camphor-anthracene system was chosen as a transparent low-melting analog of the zirconium carbide -graphite system. Camphor and zirconium car -bide both grow nonfaceted, while casting of mixtures yields platelets of both anthracene and graphite. Zone melting of thin layers of organic was observed under the microscope. Irregular lamellar structures were produced at high values of the ratio of the temperature gradient G to the zoning rate V. The anthracene invariably led the camphor, indicating lower kinetic undercooling for the anthracene. The lamellar spacing was an order of magnitude greater than typical spacings for metal eutectic systems. Exact behavior depended on orientation of the anthracene. Oriented dendritic structures were produced at low values of G/V. Transient and oscillatory behavior were also observed—much of it unexpected. A.RC-CAST refractory carbide-graphite mixtures are promising thermal-shock resistant materials. Oriented structures of these materials would be superior to arc-cast materials for many applications. Mollard and Flemings1 and Cline2 have shown that aligned structures can be obtained for a wide range of Pb-Sn alloys. However, these metals both solidify in a nonfaceted manner while graphite yields platelets or flakes. In addition only small diameter samples of Pb-Sn alloys were produced because it was necessary to avoid free convection and to have high temperature gradients. The purpose of the present work was twofold: 1) To observe the solidification of a transparent low-melting analog of carbide-graphite systems and 2) to see if larger diameter samples can be produced. EXPERIMENTAL PROCEDURE When zirconium carbide-graphite mixtures are cast, the resulting structure naturally depends on composition. Carbide-rich mixtures yield metal-like nonfaceted carbide dendrites in a eutectic matrix. Graphite-rich alloys have graphite platelets in a eutectic matrix. Empirically it was found that camphor-anthracene mixtures produce similar structures with camphor being nonfaceted and anthracene forming plates. The organic eutectic melted at 116°C and was composed of 78 wt pet camphor.3 The camphor used was U.S.P. grade from Fisher Scientific Company; the anthracene was 98+ pet fro Aldrich Chemical Co. The impurity content is judged to be on the order of 1 pet. Mixtures ranging from 50 to 88 wt pet camphor were employed for the experiments. All but one of the experiments were performed on the microscope-stage zone melting apparatus described in detail elsewhere.4 The organic mixtures were contained in horizontal cells made of microscope slides or cover glasses. In most of the cells the organic was present as a very thin layer, thus giving almost two-dimensional growth behavior. The cells were moved slowly under a heated wire, which caused a molten zone to move through the solid at rates ranging from 0.01 to 5.4 cm per hr. The temperature gradient was estimated before moving the zone by measuring the distance between the line where all solid was melted (freezing point) and that where solid first began to melt (eutectic temperature). The temperature gradient was found to be 465°C per cm in the thinnest cells used, which were made by pressing together two microscope cover slips in the organic melt and then rapidly withdrawing them. RESULTS The experimental results are described in four parts: simultaneous growth, dendritic growth, irregular growth, and transients and erratic phenomena. Steady state data are summarized in Fig. 1. Except where noted all comments are for the cells containing a thin layer of organic. A) Simultaneous Growth. Simultaneous and roughly parallel growth of anthracene and camphor was obtained over the full range of compositions investi-

Jan 1, 1970

By J. D. Forrester, Erich Sarapuu, T. C. Cheasley

Electrocarbonization of coal will produce cheap fuel for electric power plants. The complete electrification of industry and domestic power consumption of gas generated as fuel in situ is a worthwhile goal for the coal industry. Production of synthetic oils, gasoline, and coal chemicals from coal gas will create additional new markets for the coal industry. RANKING high in the nation's wealth of natural resources, readily available liquid and gaseous hydrocarbons are nevertheless falling steadily in supply, while industrial requirements for hydrocarbon compounds are greater today than during the peak period of World War 11. Theoretically, several processes will increase the future supply of liquid and gaseous fuels, but the practical application of these methods depends on two controlling factors: 1—that enough carbon-bearing material be available to warrant industrial exploitation, and 2—that the given process be physically, chemically, and economically applicable. With regard to the first factor, the Western Hemisphere is fortunately well supplied, see Table I. Table I not only shows the extensive occurrence of many fuel sources, but also the wide discrepancy among quantities of fuel substances in various materials. Great quantities of potentially available fuel have not been recovered. Many coal seams and other hydrocarbon-bearing deposits are so situated that production is uneconomical by present-day mining or oilwell pumping methods, and even in many exploitable deposits where the most efficient production methods are used a large proportion of material is never recovered. Industrial production of hydrocarbon liquids and gases must be better balanced, and processes must be developed which will convert coals, oil sand, and oil shales into fabricated commodities. Among the techniques employed by scientists and engineers to secure fuel masses not economically available at present are several processes of underground gasification. These are all concerned with converting raw materials into gaseous products by thermal treatment of source substances while they are still in the ground and therefore require that a subsurface heat (fire) zone be induced to affect pervasively the buried raw fuel deposit. This is possible only where sufficiently high temperature exists and where the fuel material is satisfactorily opened or channelized. Also, to compete successfully with common mining or oilfield practices, a given method must be controllable and must not involve greater operational expense than regular methods. Preferably, it should be less expensive. Since the close of World War 11, England has continued field studies of underground gasification methods. Experiments have also been conducted in Sweden, Estonia, France, Belgium, Italy, and Germany. The U. S. Government has sponsored field studies at Gorgas, Ala., and because gasification in situ is vitally important to establishment of the nation's fuel resources, the mining engineering department at the Missouri School of Mines has been actively interested in developing the process of underground electrocarbonization. Research was conceived by Erich Sarapuu, and preliminary experiments in treating bituminous coal were begun at the school in September 1947. The work consisted of laboratory experimentation until June 1948, at which time, through a cooperative agreement with the Sinclair Coal Co. of Missouri, pilot plant studies were instituted at the Tiger mine of the Hume-Sinclair Coal Co. near Hume, Mo., to test the encouraging laboratory findings. This comprehensive field program was pursued continuously until the beginning of 1952."'" The broad term underground electrocarbonization describes a unique gasification process that releases by electricity the desired economic constituents from a raw carbon-bearing material, converting the substance of such deposits into deliverable form and greatly reducing the cost-of-mining factor. Underground electrocarbonization is not subject to the major limitations of many other underground gasifi-

Jan 1, 1955

By W. J. Helfrich, C. L. Sollenberger

Many present direct reduction processes utilize iron ore concentrates for the production of sponge iron and the sponge iron is usually preferred as an agglomerate. Pelletizing a high grade iron oxide concentrate prior to reduction is a simple approach to the high capacity production of a uniform and agglomerated sponge iron product. The present paper describes the effect of different atmospheres and physical characteristics on the reduction of pelletized iron oxide concentrates. The kinetics of iron oxide reduction have been I studied by numerous investigators1-4 and a rate equation for the hydrogen reduction of hematite and magnetite has been proposed. Mc Kewan' obtained kinetic data for the reduction of hematite spheres sintered at 13'70°C (2498'F'). The kinetics of magnetite reduction was studied by Quets. He compacted the oxide at a pressure of 1 ton per sq cm and sintered the specimens to densities of 95 to 96 pct of theoretical. These studies demonstrated that the reduction of iron oxide is a topochemical process and that the rate of reduction is proportional to the receding surface area of remaining iron oxide. Thus, the measurement of the kinetics of iron oxide reduction depends upon the development of a measurable and well defined interface between metal and reacting oxide. It is evident that the reduction rate will be constant only when the rate of formation of the reaction product layer is constant. It was recognized by Joseph' and Edstrom' that the physical character of the oxide will determine the configuration of the interface between oxide and metal. The reduction of oxides which exhibit few pores or no interconnected pores should proceed by topochemical processes. However, if a massive or dense crystalline ore cracks during the reduction of the oxide, thus allowing the reduction to Proceed away from a well defined oxide/metal interface, then the observed reduction rate will vary or change during reduction. From a process standpoint, it would be difficult to apply absolute reduction rates determined for crystalline or nonporous iron oxide to the direct reduction of a porous pellet of iron ore concentrate. Most present direct reduction processes are attempts to utilize iron ore concentraates in the production of sponge iron. The sponge iron is usually preferred in an agglomerated form for subsequent melting practices. Pelletizing a high grade iron oxide concentrate prior to reduction is a simple approach to the high capacity production of a uniform and agglomerated sponge iron product. One process for preparing such a product has already been de-scribed. This paper describes the effect of different atmospheres and physical characteristics on the reduction of pelletized iron oxide concentrates. ORE CONCENTRATES STUDIED A magnetite concentrate from Reserve Mining Co. and a hematite concentrate from U.S. Steel Corp. were used in preparing pellets for these experiments. A head analysis of these concentrates is given in Table I. To compare the reduction rates of pelletized concentrates, it was necessary that each pellet contain equal amounts of oxygen which could be removed by reduction, regardless of the oxidation state, i.e., Fez% or Fe304. Also, because of the difficulty in preparing spherical pellets of uniform size, weight, density, and porosity for experimental purposes, pellets of a cylindrical shape were formed in a press.

Jan 1, 1961

By C. E. Silverblatt, D. A. Dahlstrom

Previous bench-scale studies demonstrated that a substantial moisture reduction can be obtained by the application of steam to coal filter-cakes, particularly to those containing a limited amount of minus 200-mesh material. Consequently, U.S. Steel's Applied Research Laboratory conducted a study to determine the feasibility of steam filtration of 1/4 in. by 0 coal on a continuous pilot-scale installation in which an Eimco extractor is used. The test results showed that the moisture content of this coal could be reduced to 5.5% at a steam loading of about 175 lb of steam per ton of dry cake. In terms of steam consumption, this loading is calculated to be 1-1/2 lb of steam per lb of water removed. In some tests, only 1 lb of steam per lb of water removed was required. These levels of steam consumption are significantly less than the actual heat requirements of conventional thermal dryers. The satisfactory moisture reductions were obtained at filtration rates of 125 to 186 lb of dry solids per sq ft per hour. However, the proper design of commercial filters should improve the potential rates that can be attained. These results indicate that steam filtration has considerable economic potential for drying 1/4 in. by 0 coals and also has additional advantages over the conventional thermal drying of coal. The results of the previous bench-scale studies and those published by Burton' demonstrated that a substantial moisture-content reduction can be effected by the application of slightly superheated steam to coal filter-cakes, particularly to those containing a limited amount of minus 200-mesh material. Consequently, US Steel's Applied Research Laboratory conducted a study to determine the feasibility of steam filtration of 1/4 in. by 0 coal on a continuous basis. In the continuous process, the dewatering operation on the filter is conducted in stages. In the first, the bulk of the water in the feed slurry is removed by conventional mechanical dewatering on a portion of the filter before the steam is applied. In the second stage, steam is applied to the cake. The steam condenses and releases its latent heat, thereby reducing the viscosity of the remaining cake water; this reduced viscosity then facilitates further drainage and produces a cake of lower moisture content. Because of the availability of feed coal on a continuous basis and since steam was readily available from a low-pressure boiler, the Applied Research Laboratory selected for the test site a coal-preparation plant that cleans Pittsburgh Seam coal. A slurry of table and flotation coal in percentages as they occur normally was used as feed stock. Typical analyses of this slurry are shown in Table I. DESCRIPTION OF FILTER AND EXPERIMENTAL PROCEDURES An Eimco Extractor was selected for the evaluation of steam filtration in a continuous process. This unit was chosen because of its availability and its design features that permit relatively simple hood construction, instrumentation, and operation. A photograph of the Extractor is shown in Fig. 1. In the filter a cloth medium is used that travels horizontally and continuously with a grooved, rubber drainage belt. The total effective filter area was 12.5 sq ft. As the feed slurry flows by gravity from the feed box onto the medium,

Jan 1, 1964

By D. W. Loughridge

INTRODUCTION Raising capital in the 1990s is a timely subject. However, many of us thought why should raising capital in the 1990s prove to be unlike it was in the 19805, the 1970s, the 1%0s, or earlier? There are a lot of creative people in banking and in corporate treasury departments. New tools and techniques are continuing to emerge, many of which are discussed in other papers in this book. While we have new financing tools at our disposal, the underlying issue has not changed. Projects and investments must be judged on their own merits. If they cannot be justified by conventional financial analysis, they should not be built. If they can be justified, it is likely that the financing will be available. The challenges faced in raising capital in this decade will persist to the next. The issues of the 1980s -- currency fluctuation, disruptive merger and acquisition activity, commodity price volatility, political risk, and debt crisis -- will all persist in an increasingly international business environment. I will focus on the financing we have just completed for the Escondida Copper Project in Chile. The Escondida financing is structured along the classic project financing model developed in the late 1970s, but it deals with issues of the 1980s and the 1990s. The financing was intriguing, not just because of the technical issues involved, but also the challenge of reaching an agreement in a large and diverse group. Escondida had the one essential feature that made its financing possible. It was commercially very attractive. It would produce at low cost a commodity (copper concentrates) that direct consumers felt would be in tight supply. The project had the direct support not only of its sponsors, but also its customers, and, very importantly, its host government. The non- recourse financing of Escondida would not have been possible without the support of these parties, and without the robust economics that made this effort worthwhile. The issue was more complicated. Operations in all parts of the world entail some political exposure. This project is in Chile, where there was a constitutional requirement that a plebescite be held when the project would be in its early stages. This plebescite would determine the fate of a 15 year old military dictatorship. The project is copper, a commodity generally deemed to be in surplus. Copper has a history of price volatility (whose price has varied from $.58 to $1.53 per pound over the past two years). It is politically sensitive, not only in Chile, but in the United States, Canada and other developed countries. The project is international, with all the problems of dealing with a variety of currencies, a variety of cultures, and a variety of laws and commercial practices. The project is also large and capital intensive, with a total cost of U.S. $1.1 billion. ESCONDIDA PROJECT Escondida, the largest known copper ore body in the world, was discovered in March of 1981, by Utah International in a joint venture with Getty Oil Company. In 1984, both Utah and Getty were involved in ownership changes, Utah being acquired by BHP. A later restructuring of the ownership of Escondida resulted in BHP, as manager, carrying a 60% interest, Rio Tinto-Zinc Corporation (RTZ) 30%, and a consortium of Japanese companies led by Mitsubishi Corporation with 10%. The Japanese consortium is incorporated as JECO (Japan Escondida Corporation). This ownership structure, which spread ownership around the world, was the first tangible step toward managing both the commercial and political risk associated with the project.

Jan 1, 1990

By David W. Wisecarver, James F. Reynolds

INTRODUCTION The Department of Energy is cooperating with Snowmass Coal Company near Carbondale, Colorado to introduce the longwall mining method in moderate to steeply pitching coal seams in the United States. This venture is part of a coal mining research program directed toward development, trial, and analysis of mining technique8 to improve production and recovery in the more difficult mining conditions such as thick, multiple, and steeply pitchly seams found in the Western U.S. The project at Snowmass is the first attempt in the United States to operate a longwall in a steep coal seam. Plans are to mine three adjacent, successively downslope panels in the eight foot thick seam which varies in pitch from 27 to 33 degrees. During this work, researchers and mine engineers are expected to obtain answers to many engineering questions relative to panel design and development, selection of face equipment and beet operating techniques and procedures. They are also committed to obtaining hard data on costs, recovery, production, safety, and behavior of underground mine structure as the three panels are mined. This information is essential to future mine engineering and profitable mining of pitching Western coal reserves. Development of the first trial panel was begun in 1979 and completed in June 1981. The longwall mining equipment was then installed in the starting room and retreat mining begun on August 11, 1981. Project duration is expected to be about five years during which over tm million tons of coal will be produced. TRAINING The longwall mining method is new to Snowmass. For years the mine produced coal by room and pillar methods using conventional techniques to mine upslope rooms and Alpine F6A miners to cut entries and rooms on strike. Miners were experienced in room and - pillar mining from other mines. News of the longwall demonstration was received enthusiastically by Snowmass miners. Employee interest in the project was 100%. However, there was minimal longwall experience on site. In fact, most of the work force had not even seen a longwall. Mine and company management were well aware of the immediate need to develop trained longwall face mining crews and maintenance people qualified to work on longwall equipment and also expertise in longwall planning, equipment selection, power distribution design, ventilation requirements and panel development. The first approach to answer this huge deficiency in longwall mining experience was obviously training. Hence a training program directed toward those mining specifics most urgent to the beginning mining phases was initiated in mid-1980. Classroom lectures and hands on training, using instructors from equipment suppliers and available company longwall expertise, was conducted in longwall subjects to include face mining procedures, panel development, operation of equipment, equipment assembly and maintenance, electrical circuitry and controls, ventilation, move of longwall equipment, and safety procedures. At the same time, responsible engineers and foremen were sent on a tour of European pitching longwalls to see first hand how other mines working under similar seam conditions conducted their operations. Development techniques, types of equipment, methods for transport of men and materials, and ground control techniques were discussed with engineers, foremen and officials at each mine. This look at European longwall mining operations gave Snowmass good insight into the unique problems associated with longwall mining on 30' pitch. Mining considerations such as face conveyor/ support system slippage downslope, panel development, maintenance, safety considerations, manpower requirements, and haulage methods were covered with European experts

Jan 1, 1982

By Norman Weiss, H. W. Kaanta

CUSTOM ores reach across the New Mexican mesa to American Smelting & Refining Co.'s new lead-zinc mill at Deming. The influx of ores justified increasing mill capacity from 12,000 tons per month to 20,000 tons per month with the installation of a second milling section. Deming mill has met a complex material handling problem with the successful instrumentation of modern machinery and knowledge. A tight, compact plant does a big job with the aid of the latest ore moving equipment. Location and Layout The mill is located three miles northwest of Deming in the tumbleweed covered valley of the Mimbres River, 30 miles north of the Mexican border. Deming has a population of 4000 and is about halfway between Lordsburg and Las Cruces and 54 miles southeast of Silver City. The AT&SF and the SP railroads and U.S. Highways 70, 80, and 260, cut across the mesa to the town. Asarco mill station is east of the AT&SF single track, and north of Deming. The nearly level terrain is covered with fine sand supporting only yucca and tumbleweed. Compacted gravel at depth affords excellent foundation bearing. The climate is semi-arid, but the district is underlain by water-bearing strata. Tailing disposal space is plentiful. The Deming site appeared favorable because of easy rail and highway access, central location in a mining district, excellent climate, plentiful water supply, space for all present and future requirements, and proximity to a town. The milling plant is a 250-ft square. The rail spur forms the west side; sampling plant, fine-ore conveyor and bins are on the east; track hopper, primary conveyor, and crushing plant lie on the south; and the mill building completes the north side of the square. Construction The mill site was chosen and the land purchased in 1,946 and 1947. Design began in 1948, and Stearns-Roger Mfg. Co. of Denver started construction in June 1949 completing work in April 1950. Construction is steel and concrete throughout, with main concrete floors supported on cellular steel beams. The building is covered by galvanized corrugated iron, attached to the frame by welded Nelson studs, and made dust tight at the joints with roofing paper and asphalt sealing compound. Crushing and Sampling Custom ores, delivered to the mill by railroad cars or trucks, are weighed on arrival. A Robbins car shaker dumps the ore into a 100-ton capacity steel hopper. Adjacent is a 40-ton truck hopper. Three 36-in. Pioneer apron feeders supply ore from the receiving hoppers to a 36-in. conveyor which runs to the crushing plant. A tramp-iron detector protects the primary crusher except when handling magnetite containing ores. A 2 ½ -in. spaced grizzly precedes the primary Traylor 24x36 in. jaw crusher set at 4 in. A Symons 4-ft cone crusher in closed circuit with 48x78 in. Robbins Gyrex screen completes crushing to 5/8 in. The discharges of both crushers drop upon a common conveyor, which, after gaining sufficient elevation, transfers ore to a return conveyor. This return conveyor passes under a suspended magnet and over a magnetic head pulley to the Gyrex screen. Screen undersize is conveyed by a 20-in. belt to the sampling plant. Crushing rate varies from 60 to 90 tons per hour. Ores containing magnetite and pyrrhotite nullify the magnetic detector and overload the magnets

Jan 1, 1952

By H. K. Najarian

This paper describes recent development work on the Wheaton-Najarian Vacuum Condenser for Zinc at Josephtown Zinc Smelter, wherein, to dissipate the heat of condensation, the "airlift" action of gases bubbling through the molten zinc in the condenser is utilized to circulate the zinc through an outside "cooling well" and cooling it continuously. AN earlier paper1 gave an account of initial development of the Wheaton-Najarian Vacuum Zinc Condenser at the Josephtown Zinc Smelter of the author's company. This paper is a progress report of further development work over the years directed toward improving the efficiency and increasing the capacity of the condenser. In this type of zinc condenser, zinc vapor with accompanying noncondensable gases from electro-thermic zinc smelting furnaces is passed upwardly through a mass of molten zinc confined in a refractory-lined U-tube. The zinc vapor condenses in the molten zinc and the noncondensable gases are drawn out of the condenser by suction applied over the surface of the molten zinc. The heat of condensation of zinc, amounting roughly to 1000 Btu per lb of zinc condensed, is absorbed by the molten zinc and, in turn, is dissipated continuously to keep the temperature of molten zinc in a range to permit effective condensation. At the time of publication of our first paper, we had at Josephtown Smelter five units of 69-in.-bore metal furnaces and one larger metal furnace having 96-in. bore. Each 69-in. metal furnace had a condenser with 22-ft overall length. The 96-in.-bore furnace had a condenser with overall length of 31 ft. Condensers were of circular cross section, with corrugated steel outer shell and carborundum lining. Diameter of these condensers was 32 in. inside the refractory lining. Molten metal in the con- denser was kept cool by spraying cold water on the outside of the condenser shell. Under good operating conditions, 22-ft condensers produced some 12 tons of metal per day; and the 31-ft condenser, about 22 tons. When the furnaces produced zinc vapor at higher rates, invariably the condenser temperature would rise to levels where excessive blue powder would form and accumulation of accretions in the condenser would be accelerated. We found that, with the system of cooling in use, we had to provide heat-exchange surface of some 150 sq ft to condense 1000 lb of metal per hr with reasonable efficiency. The wall of the condensers was made up of 5/8-in.-thick corrugated-steel shell having next to it several layers of mica and inner refractory lining of special carborundum shapes to fit the corrugation in the steel shell, and having a minimum thickness of about 2 in. Relatively low rate of heat transfer through the thick condenser wall and slow internal circulation of the molten zinc limited the rate of heat exchange between hot metal within the condenser and the cold water flowing over the outer steel shell. The thickness of the condenser wall was about minimum that we considered suitable for continuous operation. As we learned to operate the electrothermic furnaces with higher power input, producing zinc vapor at higher rates, it became apparent that we needed condensers having larger heat-exchange surfaces. Our 96-in.-bore furnace had 6 single-phase power circuits with transformers rated at 500 kva each and normally good for power input of 3000 kw.

Jan 1, 1959

By H. C. Rogers, B. W. Roberts

Vanadium foils and wires, either cold-worked or recrystallized, show a ductile-brittle-ductile fracture sequence with temperature. At about 150°C the hydrogenated vanadium wires are found to be ductile. At room temperature the wires show brittle fracture, and at liquid nitrogen temperature the wires are again ductile, although to a lesser extent than found at 150°C. Hydrogenated cold-rolled vanadium foils have been found to fracture in unusually straight lines along the [100] texture directions. The hydrogen content required to show this [loo] texture fracture is limited to a few atomic percent in range. Hydrogen content above this range causes fracture to occur in random directions. PRELIMINARY experiments with hydrogenated vanadium foils indicated that the embrittling effect of the hydrogen on the vanadium, which was severe at room temperature, was reduced at both lower and higher temperatures. In order to investigate more quantitatively the ductility changes with temperature, vanadium wires were tested in tension at three temperatures. The reduction of area was measured and the fractures examined. Specimen Preparation—The material used was kindly supplied by A. U. Seyboltl in the form of M-in. rod. The nominal analysis was: 99.2 pct V assay, 0.2 pct C, 0.01 pct Si, 0.01 pct Fe, 0.015 pct Ca, 0.02 pct O,, 0.01 pct N2, and 0.003 pct H,. The specimens were 0.035-in. diam wires. These were prepared by cold-swaging the supplied rod to the final diameter without intermediate anneal. They were finished with long-bearing dies. The surface was then given a light polishing with 0 emery paper and degreased in trichlorethylene. An X-ray check indicated that the cold-swaged wire had a fairly strong [110] fiber texture. The wires were then recrystallized in vacuum in continuously pumped quartz tubes at two temperatures to give two different grain sizes. One group of wires was given 45 min at 800°C; another, 60 min at 1000°C. The microstructures in Fig. 1 show the wires after they have been electropolished and elec-troetched in 10 pct HCI. After the 800°C anneal, the vanadium grains had a diameter of 1 to 2p and there appeared to be a tendency to elongation in the longitudinal direction. However, the latter may be an etching effect. After the 1000°C anneal, the grains appeared to be equi-axed, but there was a very large spread in grain size, probably due to some impurity segregation in the wire, Fig. 1, right. The grain diameters varied between the limits of 1 to 150p. The small particles shown particularly clearly in Fig. 1, left, are also visible on the polished surface of all samples before etching and are undoubtedly carbides and nitrides of vanadium. An X-ray check indicated these annealed wires had a strong [110} recrystallization fiber texture. The hydrogenation was carried out in an iron retort with dry hydrogen flowing through it, the retort and contents being heated in a tube furnace with a hydrogen atmosphere. The hydrogenation temperature was approximately 500°C. The hydro-genation times chosen were approximately those which would be just enough to cause the vanadium to be brittle at room temperature and thus allow the greatest chance for ductility to occur at the other two temperatures. Part of the fine grained specimens were hydrogenated for 21/2 min at 490°C. Part of the coarse grained specimens were hydro-genated for 11/2 min at 515°C.

Jan 1, 1957

By John R. Keith

Lead and zinc contents of elm, maple, and oak trees and of soils in which the trees grew were determined in samples from the Upper Mississippi Valley mining district, and from an area outside but contiguous to the district. The lead and zinc analyses of plant materials served to differentiate the mineralized and nonminer-alized areas. Stems contained about two times as much lead and about two to five times as much zinc as did leaves taken from the same stems. Lead and zinc analyses of all soil horizons could be used to differentiate between the two areas. Soils at most sample sites in the mineralized district seemed to be more reliable than plants for geochemical prospecting and are a more practical sampling medium. Soil samples from areas with thick loess cover, however, failed to indicate the presence of mineralized bodies whereas tree samples from the same sites contained anomalous amounts of lead and zinc. It is suggested that in areas of thick loess cover, plant samples could be used in prospecting for lead and zinc. The important part that plants play in the cycling of elements through the soil horizons is well-known. The concentration of elements in the upper soil horizons by the action of plants has been called the Goldschmidt enrichment principle.' The fact that plant species vary greatly in their ability to concentrate particular elements in their tissues is also well-known.' Agricultural literature has dealt extensively with relationships of the major nutritive elements in soils and plants3 The extent, however, to which plant actions cycle the minor nutritive and the nonmetabolic elements in the soil has not been adequately investigated. Lead is non-nutritive and toxic to plants, whereas zinc is a micronutrient in low, but toxic in high, concentrations.4 This report presents the results of a biogeochemical study concerned with the amounts of lead and zinc in some plants and soils that occurred both within and adjacent to the Upper Mississippi Valley lead-zinc district. Field work for this study was done in the summers of 1961 and 1962. SAMPLE TARGETS AND CHEMICAL ANALYSES Geologic and physiographic descriptions of' the district have been made by Heyl 5 and several other authors in a series of U.S. Geological Survey (USGS) reports and quadrangle maps.6-I Sedimentary rocks, mostly dolomite, limestone, shale, and sandstone, of Cambrian, Ordovician, and Silurian age predominate in the area. Mineral deposits are of the vein and cavity-fill type; the principal ore minerals are galena and sphalerite. Vegetation of the area was characterized by Curtis1 6 as southern hardwood forest interspersed with patches of oak savanna and prairie. Plant genera typical of the eastern United States Temperate Zone, including ash, cherry, dogwood, elm, hackberry, hickory, maple, oak, and other woody and herbaceous genera, are present. The natural vegetation has been greatly modified by agricultural, logging, and mining operations. The species of the original flora are present, but not in their former relative abundance. Soils of this district belong, for the most part, to the Brunizem and Gray-Brown Podzolic great soil groups. The Brunizems are the soils developed under prairie vegetation.'' The Gray-Brown Podzolics are the soils developed under deciduous forests,18 They are derived from both bedrock and from loess parent materials, and

Jan 1, 1970

By J. E. 214-000-000-010 Warren, M. R. J. Wyllie, T. Meidav, L. Scharon, R. Uhley, A. J. deWitte

By considering the stoichiometry of the underground combustion process, an equrztion was derived relating the point velocity of the combustion front as a function of the air flux, fuel content, efficiency' of oxygen uitilization, hydrogen:carbon ratio, and ratio of carbon dioxide In carbon monoxide produced. In addition, an equation for cnlcrllating the amount of injected air necessary 10 produce the oil from I Cu. ft of reservoir space was derived. This equation has a direct bearing on evaluating compression costs for the process. Values calculated from these equations are in good agreement with experimentnlly obscrvcd values obtained from laborator) tube runs reported in the literature. The equations are also u\eful for atlcrlyzinf: experinlental data for inconsistencie.r.. I NTRODUCTION The injection of energy in the form of heat into an oil-bearing formation as a means of increasing the recovery of oil has been the subject of much discussion and experimentation as far back as 1920. The ideas have ranged from the injection of steam to the direct use of electricity as a means of getting thermal energy into a formation. However, most laboratory and field studies have been confined to the process whereby a portion of the crude in the reservoir is burned to generate the necessary heat to increase the mobility of the oil by reducing its viscosity. A recent paper by W. L. Martin, et al.', described the results of a number of laboratory experiments in which the combustion process was studied in a sandpack. Studies such as this indicate that with the temperatures involved, the oil is partially coked in this process and it is this coke which provides the fuel for combustion. The combustion of this residual coke can be analyzed theoretically by applying simple stoich-iometric principles to the combustion process. It is the purpose of this paper to compare the results reported in these experiments with those obtained from theoretical considerations. The variables studied by Martin, et al, among others, include combustion front velocity, air flux, oxygen utilization, fuel concentration, ratio of carbon dioxide and carbon monoxide in combustion gases, and the hydrogen:carbon ratio of the residual fuel. All these variables come into consideration when the stoichiometry of the combustion process is studied. The experimental conditions and results are tabulated in Tables 3 and 4 of Ref. 1. For purposes of comparison with calculated results, it was necessary to change the units of a number of the variables. UNDERGROUND COMBUSTION STOICHIOMETRY The combustion or oxidation of the carbonaceous residue or "coke" on the sand can be described in terms of the equation: where n is atomic ratio of hydrogen to carbon, m is ratio of moles of CO2 to CO produced, and CH. is taken as the unit molecular weight, realizing that actually the coke has a large range of high molecular weights. Assuming that all the fuel laid down in the sand is burned, the ratio of moles of oxygen consumed to moles of coke can be written as follows. Moles 0MolesMolescoke In terms of moles O2 per pound of coke, where 12 + n is the molecular weight in pounds per mole. If the 0, consumed is measured in standard cubic feet (60°F and 1 atm) and the coke in pounds per cubic foot of formation, 2, then:

By F. R. Brotzen, A. R. Troiano, E. L. Harmon

Precipitation processes leading to drastic property changes are a frequent occurrence in titanium alloys containing large amounts of the retained high temperature P phase. In order to establish the kinetics and nature of these precipitation processes, a series of Ti-V alloys was studied. Time-temperature-transformation diqgrams were obtained for 12.5 and 15 pct V-Ti alloys. These diagrams consisted of two intersecting C-shaped curves: one in the high temperature region for the euilibrium transformation P +u+P, and another at lower temperatures depicting the formation of the meta-stable transition phase, o. Presence of the transition phase retarded the precipitation of the equilibrium a phase. Deformation of retained P resulted in the formation of the o phase. Reversion and retrogression phenomena of the transition phase were observed. A negative temperature coefficient of resistance was found in quenched alloys containing from 15 to 20 pct V. CERTAIN titanium-base alloys can be heat treated to produce appreciable changes in properties. For example, remarkably high hardness values may be obtained by aging or isothermal quenching treatments. Most of the information available to date on the hardening of titanium-base alloys has been systematized recently in an article by L. D. Jaffe.' It was pointed out by that author that the hardening was the result of the decomposition of the retained j3 phase to the equilibrium constituents, a and p, and that this decomposition had many of the characteristics of an age-hardening reaction. Recent work by Frost et al.' 3 has contributed much to the fundamental understanding of the hardening mechanism in titanium-base systems. These authors established the presence of a transition phase in the transformation from j3 to a + j3, which they designated o. The transition phase, in their opinion, was at least partially responsible for the hardening and embrittling effects which accompanied low temperature aging. The present investigation of the mechanism and kinetics of the hardening reaction was carried out for the Ti-V system. Ti-V alloys were ideally suited for a study of the decomposition of j3, since age hardening was known to occur readily in this system." Moreover, no intermetallic compounds occur in this system, Fig. 1, thus simplifying the interpretation of the results. Material and Procedure Alloys containing 12.5 and 15 pct V were prepared by Battelle Memorial Institute from iodide titanium furnished by Watertown Arsenal and vanadium of 99.8 pct purity. Ingots of 8 Ib each were prepared by arc melting in an inert atmosphere with a tungsten electrode and water-cooled copper crucible. Each of the ingots was melted once, forged at 1600°, and rolled at 1400°F. Following this, the ingots were remelted, forged, and then rolled to % in. sq bars, which were subsequently grit blasted, pickled, and wire brushed. Another set of alloys containing nominally 17.5 and 20 pct V was produced by the Research Div., New York University. These alloys were arc melted in an inert atmosphere in lots of 20 g each. Heat-Treating Procedure: Whenever feasible, specimens were heat treated in high vacuum resistance furnaces at pressures below 5x10." mm of Hg. Aging and isothermal quenching treatments were generally carried out in salt baths. Specimens were not attacked by the salt, provided the tempera-

Jan 1, 1956

By F. von Gemmingen, E. J. Fasiska, L. Zwell

EARLIER studies of the dependence of creep on structure1 and of the dependence of creep rupture on creep behavior2 did not include detailed discussion of the phases present in the specimens under examination. It is of interest to determine the nature and amounts of such phases present since it is well known that these are dependent on composition, heat treatment and creep conditions.3 This investigation has therefore been undertaken to identify these constituents and to determine their relative amounts. This report presents the results of this investigation and describes an improved "extraction replica" technique developed in the course of the work. The composition of the Type 316 austenitic stainless steels studied in this investigation is given in Table I. The specimens were solution treated at 2000°F for 1/2 hr and water quenched. Those specimens subjected to prestrain at room temperature Methods for extracting precipitate particles from materials for electron and X-ray diffraction analysis have been described by Fisher,4 Smith and Nutting: and Booker and coworkers.6'7 Electrolytic extraction methods have been described by Andrews and Hughes.8 The first two methods have been used at this Laboratory, but have not proved satisfactory for many problems requiring X-ray diffraction analysis. It has been difficult to remove the replicas or to avoid tearing them during removal. These difficulties are overcome by backing the replica with a water-soluble plastic such as Dupont 51-05 Elvanol (polyvinyl alcohol). The backing increases the thickness of the replica so that it can be mechanically stripped from unloosened particles without folding or tearing. This procedure eliminates the stripping of wet replicas, which usually have a low tear strength. By stripping replicas after drying, it is possible to extract partially loosened particles which otherwise would remain imbedded in the metal. The modified method is as follows: after the specimen is polished, it is etched for 60 min in modified glyceregia consisting of 30 ml glycerol, 7 ml nitric acid, and 4 ml of hydrochloric acid. The sample is then washed, air dried, and coated with a 20 pct Baker and Adamson 1611 collodion (85 pct amyl acetate by volume) film. After the collodion film is dry (about 15 min), the sample is again etched in the modified glyceregia for 50 min, washed with isopropyl alcohol (to prevent dissolving the collodion) and air dried. A very thick coat of polyvinyl alcohol (about 50 pct solution "Elvanol Dupont 51-05" in water) is poured over the sample and is permitted to dry for about 24 hr. The composite film containing the precipitates is then stripped from the specimen and floated, polyvinyl alcohol side down, in water (at about 50°C) until the polyvinyl alcohol dissolves. This usually takes about 15 min. Should any of the polyvinyl alcohol remain on the replica, it does not give a crystalline diffraction pattern and therefore does not hinder identification of the precipitates. The extraction replica, floating in water, is picked up on a glass fiber and mounted in the Debye-Scherrer camera for X-ray diffraction analysis. Concentration of the etchant, and also etching time, had to be increased for several of the samples. Fig. 1 shows two extraction replicas taken from different areas of spec. M74-37; X-ray analysis showed a strong diffraction pattern of M23C6 and a medium one of u phase. A

Jan 1, 1962

By O. E. Palasvirta

Close examination of most so-called n.eu processes in mineral dressing reveals that they were conceived and developed a long time ago. High-intensity magnetic separation is no exception. Although its application in iron ore beneficiation seems new, in Germany the process has been commercially successful for almost two decades. High-intensity separators have long been standard equipment in the glass sand industry; they have also been used in concentrating some of the more unusual para-magnetic minerals. The basic features of an induced-rotor, high-intensity magnetic separator were described by Desire Korda in Paris in 1905,' and many patents have since been issued for improvements on the original design. Fig. 1 shows the basic design of an induced-rotor separator. Several U. S. manufacturers have been supplying induced-rotor separators for many years, but these are all devices of relatively low capacity, not suitable for treating such low-cost commodities as iron ore. On the other hand, two German manufacturers are offering induced-rotor separators of high capacity, both proven in the field. The present investigation was prompted by the apparent success of the German installations and by the discovery of iron ores on this continent which may be amenable to high-intensity separation. The objective was to gain better insight into the underlying principles of separation in a high-intensity field and to use this knowledge in selecting or designing an optimum separator. THEORETICAL CONSIDERATIONS he well known low-intensity magnetic separators are. without exception, of the the magnet type with more or less similar field shapes. It is therefore permissible to speak of their comparative strengths in terms of field intensity alone. However, proper understanding of the high-intensity magnetic separation process requires somewhat deeper analysis of the relationship between the magnetic field and the attractive force. Contrary to a widely held belief, a magnetic field of parallel lines of flux exerts no attractive force on a magnetically susceptible particle, but merely aligns its poles parallel to the lines of flux. On the other hand, a non-uniform field attracts a magnetically susceptible particle in the direction of the converging lines of flux. Thus the force of magnetic attraction varies as the product of the field intensity and the field gradient: dH ds As the induced-rotor magnetic separator is primarily intended for separating feebly magnetic materials, it is important that maximum attraction be attained. For the designer, then, the relationship between the magnetic field and the attractive force has the following implications: 1) Insofar as possible, the separation gap must be saturated with flux. 2) The rotor surface must be shaped to insure maximum convergence of lines of flux toward the rotor. 3) The primary pole face (opposite the rotor, on the other side of the separation gap) must be shaped so that the lines of flux do not diverge from it at any location in the effective separation zone. The actual attractive force of the rotor, and its critical speed, can be calculated as shown by Runo-linna, provided that the true flux density, the field gradient, and the magnetic susceptibility of the mineral can be measured with sufficient accuracy. The irregular shape of the rotor surface makes flux measurements difficult, but it can be done if a suitable gaussmeter is available (see Fig. 2). Calculations by the author, and comparisons with the centrifugal force exerted by the rotor, indicate that the force pinning a hematite particle to the rotor is of the same order of magnitude as the force holding a

Jan 1, 1960

By P. G. Meikle, C. T. Holland

The effect of the condition of friction upon the ultimate unit compressive strength as determined between the compressed faces of precisely machined coal specimens and specially prepared testing platens has been examined. Reductions of 30 to 40% in the ultimate unit compressive strength of these model coal pillars have been verified when lubricants areused between the faces as compared to non-lubricated faces. Increase in unit compressive strength due to confinement at each of three levels of friction appears to follow generally the widely accepted "1/2 power law", i.e. S - C (L/T)1/2 where S is the unit ultimate strength, C is a constant dependent on the coal being tested and the coefficient of friction acting at the compression surfaces and L and T are the least width and thickness of the specimen, respectively. Results suggest that the surface condition of both the specimen and platens should be mentioned in detail in conjunction with compression testing, for although the term (L/T)1/2 is adequate for all practical purposes, the coefficient C is directly dependent on the condition of interfacial friction, all else remaining constant. One phase of the investigation of the confining effect of friction on the ultimate unit compressive strength of small coal specimens has recently been completed at the School of Mines of West Virginia University. The efficient control of ground is of fundamental importance to successful mining operations and the design of support pillars has always presented the mining engineer with a difficult and intriguing engineering problem. Since about the turn of the century, many investigators have performed extensive laboratory tests on small coal specimens in efforts to solve some of the perplexing problems of strata control and pillar action in coal mines. A detailed review of this work would serve no purpose here, but a brief mention of the more significant contributions is in order. Muller16 was perhaps the first to illustrate the effect of confining pressure on the strength of coal specimens in compression. His work has recently been more carefully expanded by the experiments of Murrell17 in Great Britain. Rice and Enzian l9 observed that as the size of cubical test specimens increased, the unit compressive strength decreased. These observations were later supplemented by Lawall and Holland, 13 by Greenwald4,5 et a1 at the U. S. Bureau of Mines, by Gaddy3 as well as by Steart,22 Millard15 et a1 and Evans2 et al. Gaddy3 seems to have been first to quantify this relationship with his equation: S = K/vd , where S - ultimate unit compressive strength (psi), K = a constant dependent on the coal, and D =edge dimension (in inches). Holland7 concluded that the strength of coal as affected by lateral dimensions and thickness could be expressed as where K = a coefficient dependent upon the coal, L = least width of pillar (in.) and T = thickness of pillar (in.). Data supplied by this formula have been compared to the estimated stresses in pillars that had been standing for long periods in coal mines and in the cases so far studied the results indicate that the formula predictions are sufficiently accurate for engineering purposes (Holland11 ). This equation therefore is believed to be the simplest and most accurate tool available at the present time for approximating the strength of a coal pillar (over a specified range of L/T) in situ. However, Holland7,9 has indicated that friction between the coal pillars and the top and bottom rock

Jan 1, 1965

By N. S. Bornstein, M. A. DeCrescente

ThE nickel and cobalt base superalloys employed in gas turbine engines under some conditions' oxidize at an accelerated rate when exposed at elevated temperatures to atmospheres containing minor quantities of sea salt. It is generally agreed by investigators in the field that the major steps comprising this phenomena of accelerated oxidation, also called hot corrosion or more commonly, sulfidation, are a) a slag composed primarily of Na2S04 is formed on turbine components, b) the protective oxide scale is rendered ineffectual, c) the slag reacts with. the substrate to form metal sulfides, and d) the substrate is rapidly oxidized. Sodium sulfate, a minor constituent of sea salt, is formed within the gas turbine engine from the reactions between NaC1, the major constituent of sea salt, and the oxides of sulfur.' Depending upon concentration, engine compression ratio, and temperature, the Na2S04 will be present in the gaseous or condensed state. It has been determined that in order for sulfi-dation to occur the Na2S04 must be present in the condensed state.' Although a number of sulfidation mechanisms have been postulated, there is no consistent explanation of oxide scale breakdown and subsequent catastrophic oxidation. Some investigators believe that after oxide scale breakdown, the Na2SO4 reacts with the substrate to form lower-valent sulfur compounds. The accelerated rate of oxidation is due to oxidation of a nickel-sulfide phase." Other investigators believe that sulfur from the fused salt reacts with chromium in the alloy to form chromium-rich sulfides; thereby depleting the alloy of an element which imparts oxidation resistance.3,4 This publication will demonstrate that the accelerated rate of oxidation associated with sul-fidation is due to interactions between Na20, a con-stituent of NazSO.,, ancl the substrate. The aim of this study was to separate and determine the effect of compounds of sulfur and sodium on the oxidation kinetics of various nickel-base superalloys, in order to elucidate the sulfidation mechanism. The work reported herein is sponsored in part by the Naval Ship and Development Center-Investigation of EXPERIMENTAL PROCEDURE The nickel base alloys B-1900, U-700, and Waspaloy were chosen for this study. The nominal compositions are presented in Table I. The specimens, approximately 1 in. by 1 in. by 0.060 in. received in the "as cast" condition were polished with 600 grit emery, washed, and rinsed with acetone immediately prior to oxidation experiments. Sulfida-tion attack was duplicated in the laboratory by apply-ing a saturated aqueous solution of Na2S04 onto the al loy substrate and subsequently exposing the specimens in oxygen at elevated temperature. The method of Na2S04 application is described elsewhere in detail.6 In another set of experiments the affected substrate microstructure associated with sulfidation was reproduced free of the normal oxide scale, by reacting and diffusing elemental sulfur into the alloy. The experimental procedure is also described elsewhere in detail. All oxidation studies were performed using an Ainsworth thermobalance type RV-AU-1, which is readable to 0.01 mg and is reproducible to ±0.03 mg. The specimens, introduced into a heated furnace, were exposed in the temperature range 800" to 1000°C

Jan 1, 1970

By Dean Goodermote, Carla S. Stone

I Introduction Coal fuels China. Roughly 70 percent of all commercial energy demand is supplied by domestic coal production and with the recent Chinese opening to the West, the Chinese Coal Industry may figure prominently in the export market as well. Because of the importance of China's coal industry to the future of China and the Pacific Rim energy balance, this paper reviews the industry and offers some cautious projections for its outlook. II Energy's Position in the Current Political and Economic Climate Traditionally, Chinese society has been dominated by the policies of its most important government leaders. Deng Xiaoping, Vice Chairman of the Communist Party is the current leader of China. Deng and his proteges are pragmatists. Although China's government structure is based on Marxist/Leninist tradition, Deng and his followers are promoting experiments with market economics and expanded relationships with Western Countries, which have encouraged foreign investment in China. Energy companies represent just one type of industry that is interested in helping the Chinese to develop their abundant natural resources. Although China's leadership is committed to a program of economic modernization, that program currently is experiencing what the Chinese government terms "readjustment". Readjustment cuts back in imports due to deficient foreign exchange and deemphasizes heavy industry, while it encourages agricultural and consumer goods output and, most imporant, energy production. Increased Chinese coal and oil production is essential both to fuel industry and, equally important, to provide foreign exchange. If sufficient energy production is not forthcoming, then economic growth will be severely retarded. China's 1979 per capita GNP of $260 is only slightly better than the weighted average achieved by low income countries of $230. (1) Delays in growth could lead to social unrest, threatening the position of the current leadership. Since there is no institutionalized mechanism for leadership succession and policy continuation, it is reasonable to assume that leadership changes could result in energy policy changes. III Energy Consumption Energy production is important to China's future economic health as highlighted by the World Bank. If China's economy grows rapidly, 5 percent to 6 percent during this decade, the Bank noted, a significant energy shortfall could occur as early as 1985. This state of affairs contrasts sharply with China's current position as a net hydrocarbon exporter. (2) To assure a healthy economic future, China's leadership is attempting to reduce its rate of increase in energy demand through conservation as well as to boost energy output. A massive conservation promotion program has been underway since 1979 and there is much room for improvement. China's industrial sector is only about half as energy efficient as is U.S. industry. (3) During the last two decades, each percent of increase in GNP has been accompanied by a 1.8 percent of increase in energy consumption. (4) This compares rather poorly with the United States where a less than one-to-one relationship exists. IV Energy Supply The short term prospects for oil production are uncertain. Production increases were rapid in the 1960's and early 1970's, averaging 20 percent annually, but most of this increase came from one field, Daquing. Now that Daquing's production has peaked and the offshore potential has yet to be developed, petroleum production has maintained a plateau of 2.1 million b/d, at least temporarily, of which approximately 15 percent is exported. (5) Output

Jan 1, 1982

By T. R. Ingraham

The thermal decomposition of cupric sulfate and of cupric oxysulfate has been examined by deter-mining the equilibrium gas pressure generated over each pure compound. The equilibrium data have been used to calculate the thermodynamic properties of both compounds, and the results have been combined with previously published data to establish a predominance-volume diagram for the Cu-S-O system over the normal range of roasting temperature and gas composition used in the treatment of copper minerals. Copper oxysulfate recrystal-lizes at 1100°K with an apparently irreversible en-dothermic heat requirement of 2.9 * 0.3 kcal per mole. WHEN mixed sulfide minerals containing copper are roasted, either of two procedures may be followed, depending on the nature of the other metals. In the first procedure, the roasting is controlled to produce a maximum amount of water-soluble copper sulfate which may be removed selectively from the water-insoluble compounds of the other metals. In the second, control is directed toward the production of water-soluble sulfates of the other metals and an insoluble salt of copper. Effective control of either of these processes would be enhanced by knowledge of the thermal stability of cupric sulfate and of cupric oxysulfate. In this paper, established data for the thermal stability of cuprous and cupric sulfide and of cuprous and cupric oxide will be combined with new data for the therma1 stability of cupric sulfate and cupric oxysulfate, to designate the volumes of stability of the significant compounds in the Cu-S-O system in the temperature range 750° to 950°K. EXPERIMENTAL Materials, Apparatus, and Procedure. The copper source material used in all experiments was Fisher Certified Reagent Grade "anhydrous" cupric sulfate, for which the following analysis was supplied by the manufacturer: chloride, 0.002 pct; alkalies and earths, 0.2 pct; insoluble, 0.002 pct; iron, 0.020 pct. Cupric oxysulfate was prepared from the normal sulfate by two procedures. In the first, equimolar quantities of cupric oxide (prepared by decomposition of the sulfate) and cupric sulfate were ground together and heated under vacuum in a sealed silica vessel at 800°C. This procedure was subject to failure because of explosion of the silica vessels due to the pressure of the final traces of water released from the sulfate on the initiation of its decomposition. The second procedure involved roasting the cupric sulfate, with frequent rabbling, in a muffle furnace at 725°C for a period of 48 hr. This produced an excellent product, which was confirmed as copper oxysulfate by X-ray and chemical analyses. The experimental technique used was that of measuring the total pressure exerted by the sulfur trioxide, sulfur dioxide, and oxygen produced by the following reactions: 2 CuS04 = cuo • CuSO4 + SO3 [1] cuo . CuSO4 = 2 cuo + SO3 [2] SO3= SO2 + 1/2 O2 [3] The apparatus used in the experiments has been described previously.1-3 Its main feature of a U-tube mercury manometer in which the mercury is protected from corrosion by enclosure in a flexible Pyrex bellows. Before beginning a run, the interior of the apparatus, including the bellows-manometer and all connecting tubing, was thoroughly washed with hydrochloric acid and distilled water to remove any

Jan 1, 1965