By L. L. Oriard

INTRODUCTION In order to make effective plans for the control of blasting effects, it is necessary to understand a few basic principles relating to the behavior of explosives. For the purposes of discussing this behavior, it is convenient to divide blasting effects into two zones. The first zone is the non-elastic zone in close proximity to the explosive charge where rupturing of the rock occurs. For this zone, our discussion will be oriented towards the factors which affect the rock breakage, and the means of controlling the limits of this breakage. The second zone is that zone more remote from the charge location where elastic vibrations are transmitted through the surrounding medium. In this zone, we are interested in the factors affecting vibration intensity, and the means of controlling the intensity so that no damage is done to structures, utilities, or excavated slopes. It has been easier to gather data in the elastic zone, because the stress levels are lower and time durations are longer. The instrumentation for obtaining data in this zone can be less rugged and less sophisticated. Consequently, more information of ad empirical nature has been gathered. In the non-elastic zone, there has been more dependence on theory, fewer measurements, and more questioning of the validity of the measurements. In spite of these questions, there has been an encouraging advancement in knowledge in recent years, both theoretical and empirical, of the effects that take place close to the source of an explosion. When discussing the problems encountered in rock excavation, we can simplify the terminology by referring to the physical phenomena encountered in the non-elastic zone as a problem in "over-break". The phenomena in the elastic zone could be called "vibration effects". Although there is some interdependence between the two, it is possible to control the rock breakage to neat surfaces and still have very high vibration levels. Similarly, it is possible to control the vibrations to moderate levels and still have a great deal of overbreak. THE ROCK BREAKAGE ZONE First, let us discuss the effects in that zone close to the blast source that we might call the non-elastic zone. This is the zone of cratering, breakage, rupturing, and fracturing. These effects will vary with the site conditions, and a meaningful, specific analysis could

Jan 1, 1972

By H. M. Howe

(New York: Meeting, October, 1913.) 1. INTRODUCTION.-This paper gives the results of our micro-graphic determinations of the position of Ae3 in a series of 14 hypo-eutectoid steels of varying carbon content, one of them very rich in phosphorus, and of SEe for one hyper-eutectoid steel. We have pro-ceeded chiefly by noting the temperature -at which the reabsorption of the pro-eutectoid element is found to be complete after a 30-min. holding, but in part also by noting the temperature at which its precipitation begins. Observations on these same steels by Messrs. Burgess, Crowe, and Rawdon, of the United States Bureau of Standards, are given in a paper' issued simultaneously with this, while in a third paper s one of us compares these data with those of earlier observers. These three papers are treated as one whole by numbering their sections, tables, and illustrations continuously, and by setting the folding plates of micrographs at the end of the last paper. THE COMPOSITION OF THE STEELS EXPERIMENTED ON is given in Table I. Notation. and Definitions.-Following Osmond's development of Tschernoff's notation; in which " Ac3 " is the upper limit of the hypo-eutectoid part of the transformation range as observed in heating up, and " Ar3 " is that same limit as observed in cooling down, and following the usual custom of calling the upper limit of the hyper-eutectoid part of that range "SE," we may go farther and call this latter limit " SEc " when observed in heating up .and " SEr " when observed in cooling down.

Jan 6, 1913

By D. A. Belforti, M. P. Lepie

Spectroscopically pure copper was melted on sapphire plaques in a zydrogen atmosphere. The surface tension of the liquid metal was determined using the sessile drop technique. Measurements were made by direct observation with the aid of a specially const,mcted telescope. The value obtained, 1268 dynes per cm, is compared to that found in the literature. THERE is at this time considerable interest in the use of ceramics for vacuum tubes. The crystalline material is superior to the more conventional glass in mechanical strength, chemical inertness, dielectric properties, ability to withstand high temperatures, and so forth. However, ceramics are much more difficult to seal hermetically with metals than are the glasses. For this reason an investigation was undertaken to determine the wetting and adhesion of metals to ceramics. The sessile drop technique offers a convenient means at elevated temperatures for measuring liquid surface tension, wetting angle, density, spread- ing coefficient, and work of adhesion. Thus, from the contour of a drop of liquid at rest on a solid surface one can obtain a quantitative evaluation of the degree to which the two substances will bond. To this end a special apparatus was constructed so that various molten metals could be observed. Standardization of the apparatus was done initially by measuring the surface tension of copper since this is well documented in the metallurgy literature. Although there are many methods available for the measurement of surface energy,'+ the sessile drop technique has been used most extensively for molten metals and ceramics.5"' Fig. 1 illustrates the dimensions to be measured. From these values, the surface tension of the liquid can be obtained using the Bashforth and bdams' equation and tables.

Jan 1, 1963

By Irwin Roman

NUMEROUS results and formulas have been published for analyzing seismic records, but most of them apply only to large-scale phenomena such as are encountered in studying earthquakes. In a few cases,1 formulas have been published for some of the simpler structures. In the present paper, an attempt will be made to analyze several types of struc-tures without using methods more advanced than those of a first course in calculus. In, tracing a disturbance through a medium, it is almost always possible to base the analysis on Fermat's Principle of Extreme Time, which states that waves of displacement travel between points in such a manner as to make the time of travel an extremum with respect to all neighboring paths. In the simpler cases, comprising most of those used in optics or geophysical prospecting, this time is a minimum and the principle is often referred to as the Principle of Least Time. Within a homogeneous medium, having a uniform speed of transmission of the disturbance in all directions and throughout the medium, the paths are straight and are refracted at the interfaces in accordance with the Snell law of refraction, which states that the ratio of the sine of the angle, made by the ray with the normal to the interface, to the speed of trans-mission is the same on both sides of the interface. Thus, in any medium composed of homogeneous sections, this same ratio has a constant value at all points. In particular, if all interfaces are horizontal, it is apparent that the angles of incidence are the angles made by the ray with the vertical direction. Furthermore, the incident ray, the refracted ray and the normal to the interface are all in the same plane at each refraction;

Jan 1, 1933

By Paul Giesecke

SINCE most modem metallurgical plants are operated continuously and on a large scale, successful operation at maximum efficiency demands that an accurate knowledge of the performance at each stage of the process be available at all times. Quantitative analyses provide the most practical process guides, and it is essential to have analytical procedures that combine accuracy and speed. In continuous plant operations, large losses may occur if the time interval between the development of trouble at any stage and its recognition and correction is great. Many metallurgical plants are using rapid colorimetric and spectrochemical methods of analyses for control purposes. So-called "color coppers" may be cited as an example of the colorimetric methods, in contrast with the routine use of the ultraviolet spectrograph for the analysis of steels.42 By means of this more refined spectrochemical procedure, a complete quantitative analysis of the molten metal is obtained every few minutes. During the past two years the Physics Division and the Ore Dressing Laboratory of the American Cyanamid Company's Stamford Research Laboratories have collaborated in a study of the use of spectrochemical methods for the analysis of various metallurgical products. New methods have been developed, which have proved of practical value in plant operation. The following pages give a general review of the principles of spectrochemical methods and also the details of several specific analyses. PRINCIPLES OF SPECTROCHEMICAL ANALYSIS In general, it can be said that a visible light spectrochemical analysis can be performed for any ion or molecule that is naturally colored, or that can be made to react with another to produce a colored salt or complex. Whereas transmission measurements in the ultraviolet and infrared portions of the spectrum are most useful for the analysis of organic molecules, visible light measurements are of particular value for metal salts. Such elements as copper, manganese, cobalt, nickel, iron, molybdenum, vanadium, chromium, phosphorus, mercury, zinc, lead, and a great many others, can now be determined with a high degree of sensitivity, accuracy and dispatch. From the simplest of qualitative determinations, color analyses have been improved to such an extent that, at the present time, through the use of recording spectrophotometers, hundreds of accurate quantitative analyses can be performed by a single analyst during an 8-hr. day after the standardization curves have been established for the ions to be determined.

Jan 1, 1944

By M. L. Fuller

MOST commercial alloys undergo changes in phase composition after casting. This is a natural result of the fact that the alloys are not in a state of phase equilibrium as cast and phase changes will therefore take place, with more or less rapidity, in an attempt to attain equilibrium. The practical aspect of aging in zinc-alloy die castings concerns the changes in physical properties and in dimensions that may accompany aging phase changes. Harmful alterations have been reduced to a minimum and zinc-alloy die castings are being produced today that are so stable with respect to dimensions and physical properties that they are entirely suitable for most practical purposes1. In the first paper2 of this series, and in this paper, aging phase changes of zinc alloy die castings have been investigated and the possible influence of these changes on dimensional changes of the castings has been evalu-ated and compared with the dimensional changes actually experienced. The change of dimensions has been selected for practical comparison in these papers because the effect of phase changes on the dimensions of a casting is directly calculable; from X-ray crystal-analysis data of the phase structure. The die-casting alloys considered contain, in addition to zinc, 4 per cent of aluminum, about 0:03 per cent magnesium, and from 0 to 3 per cent of copper. It was shown in the former paper that the eutectoidal decomposition of the beta aluminum-zinc phase, while intrinsically capable of causing a considerable shrinkage, can have very little effect on the observed shrinkage of die castings because it takes place within a few days of aging, whereas the observed shrinkage continues for five weeks. It was therefore concluded that the other existing phase change,

Jan 1, 1935

By G. L. Oldright, Henry de Rycker, S. F. Ravitz

The upper limit of richness of concentrates that can be smelted by means of the blast furnace without added diluents is fixed by the operation of sintering. A sinter feed with normal gangue constituents, containing more than about 50 per cent of lead, tends to fuse; as a result, air does not come sufficiently into contact with the sulphides at roasting temperatures, and sulphur elimination is poor. Since most lead concentrates now contain 55 to 80 per cent lead, it is necessary to add diluents to lower the grade of such sinter feed to about 50 per cent or less. This not only entails the expense of providing barren diluents when adequate diluents containing precious metals are not available but also appreciably lowers the capacity of the blast furnace to produce lead and increases slag losses. Attempts to desulphurize rich lead concentrates by methods other than sintering have not proved successful. Flash roasting, for example, converts much of the lead sulphide to lead sulphate rather than to oxide. However, this suggested the possibility that deliberate flash roasting of the concentrates to sulphate, followed by sinter roasting of the resulting product, might prove promising, particularly inasmuch as the elimination of sulphur from lead sulphate requires heat alone and not contact with atmospheric oxygen. The sintering of lead sulphate products has additional interest because important amounts of such products are now treated by lead smelters. Considerable quantities of lead sulphate are present in rich lead flue dusts and other by-products; lead-chamber sulphuric acid plants and other

Jan 1, 1944

By Frederick Laist

Introduction IN a leaching process, having obtained the copper in solution, the choice of the precipitation method is influenced y the following factors: 1. Availability of precipitant. 2. Adaptability to the leaching process. 3. Final product desired. 4. Regeneration of leaching solutions. 5. Fouling of solutions. There are three general classes of precipitation methods: 1. The use of iron, scrap or sponge. 2. Electrolytic deposition. 3. The use of some gas or reagent y which the copper is obtained, usually in the form of an intermediate precipitate which requires further treatment. For example, the precipitation of the copper as Cu2Cl2 from chloride solutions, with SO2 gas. The use of iron is adapted to almost any process. It has the great advantage of extreme simplicity, and the recovery of the copper and any values present in a highly concentrated, easily treatable form. The disadvantages are the cost in isolated places, the uncertainty of the scrap-iron market, and the fouling of the leaching solutions. The latter is a serious factor, When a reagent such as salt is used in them, which makes necessary their re-use. Where applicable, electrolytic deposition is very attractive. The copper is obtained in a form directly marketable, there is a regeneration of acid amid no fouling of solutions. Unfortunately, chloride solutions do not lend themselves to electrolysis. An entirely satisfactory anode material has not yet been discovered, although magnetite, apart from being rather brittle, seems to answer the requirements fairly Well.

Jan 7, 1914

By R. E. Ogilvie, J. I. Goldstein, R. E. Hanneman

The interdiffusion coefficients for the Fe-Ni system were determined as a function of composition in both the a and y phases at 1 atm pressure. The inter diffusion coefficients were also determined in the y phase at 40 kbar pressure. The concentration gradients were measured with an electron probe, and the diffusion coefficients were calculated by the Matano analysis. At 1 atm, Ey increases with nickel content up to 65 at. pct Ni. The relationship of Dy with temperature and nickel concentration, up to 50 at. pct Ni, is given by the equation DY-l atm = exp(.0519 CN~ +1.15) MANY of the transformations that occur in the solid state are diffusion-controlled, especially those involving precipitate growth in most metallurgical systems. Multicomponent diffusion is usually expressed in terms of a chemical or an inter diffusion The activation energy Q at 1 atm decreases from pure iron to 60 to 70 at. pct Ni and decreases from pztre nickel to 60 to 70 at. pct Ni. The Kirkendall marker movement indicates that DFe is greater than DNi zcp to about 60 at. pct Ni. Above 60 at. pct Ni, however, DNi becomes peater than DFe The inter diffusion coefficients were also compared with those calculated from self-diffusion data. A comparison between calculated and measured coefficients shows only rough agreement. The effect of 40 kbar pressure is to decrease DyPl atm by an order of magnitude. The activation volumes for high-pressure diffusion are in favorable agreement with theoretical models developed for self-diffusion. coefficient which determines the rate at which material is transferred from the matrix phase to the precipitate and hence determines the growth rate of the precipitate. Since the numerical values of the diffusion coefficients differ widely as a function of the metallic system, temperature, and pressure, the diffusion coefficients must be determined for each particular environmental condition. Of long-standing interest is the growth of the classic Widmanstatten pattern in metallic (Fe-Ni) meteorites. The growth rate of the pattern is controlled by the diffusion coefficients in the Fe-Ni system. Since these coefficients are essential to calculating the growth rate of the pattern, we found it necessary to determine the diffusion coefficients

Jan 1, 1965

By C. F. Frey, P. J. Ahern, J. F. Wallace

THE high affinity of molten titanium for oxygen and nitrogen has resulted in considerable difficulty in developing a satisfactory melting procedure. It has been found necessary to perform melting operations either in a vacuum or inert atmos-phere, and failure to obtain a satisfactory crucible material has necessitated the use of special melting techniques. These techniques have included cold-mold arc-melting utilizing both consumable and nonconsumable electrodes, skull-melting, drip-melting, and levitation melting.' It has been recognized generally that the melting of both titanium sponge and titanium scrap would be expedited by the use of induction-melting procedures but the lack of a crucible capable of containing molten titanium without objectionable contamination thus far has prevented the use of induction-melting procedures. An extensive investigation: which included the common refractory materials was not successful in developing a satisfactory crucible for induction-melting. Some success in induction-melting has been attained with the use of a graphite crucible material, but in all instances sufficient carbon contamination was encountered to cause an appreciable reduction in the optimum mechanical properties of the titanium or titanium alloys. These investigations"" report an increase in the carbon content from approximately 0.3 to 1.0 pct. A serious reduction in the tensile and forming properties has been observed as a result of this carbon contamination. The development of a satisfactory induction-melting procedure for titanium without undue contamination undoubtedly would have considerable economic significance. Such a process would be particularly useful in melting the large quantities of low-cost scrap now available that can only be reprocessed at considerable expense and difficulty by the more elaborate techniques referred to previously. In addition, the process could provide a satisfactory method of melting and alloying of bri-quetted sponge for forging ingots.

Jan 1, 1959

By R. C. Thompson

THE lead-zinc mill of Phelps Dodge Corporation, Copper Queen Branch, Mines Division, Bisbee, Arizona, is about 3 miles from the main hoisting shafts of the Junction and Campbell mines at Lowell. All the ore treated in the mill is obtained from these two mines. The mill was designed for an all-flotation treatment of 450 tons of lead-zinc ore per day, and has been operated at that capacity since the start of milling operations on Nov. 17, 1945. An expansion program is underway whereby the mill capacity will be doubled, but this article describes only the original program and presents results of the 45o-ton operation. GENERAL DESCRIPTION The milling plant consists of an ore-receiving bin and three steel-constructed buildings housing, respectively, the primary crushing equipment, the secondary crushing equipment, and the ore-storage bins, grinding, flotation, and filtering equipment. The mill site is the one that was used for a previous copper-concentrating plant, which was operated over a period of years and then dismantled. There remained from this operation some milling equipment, a reservoir for mill-water supply, railroad tracks, tailings-disposal ponds, and a steel-constructed building, all of which were incorporated in the design of the present lead-zinc mill. The location plan of the plant layout is shown in Fig I. The flowsheet of the mill is based on the conventional scheme for lead-zinc treatment, however, several innovations were made necessary in order to utilize the existing building. Placing of equipment also was governed by the design of the building; thus making the mill unique in many respects. The following brief description of the mill building as adapted to the flowsheet points out the compactness of the installation and some of its unusual features. The first floor (Fig 2) houses the grinding equipment, with connecting conveyors for ore feeding, also an air compressor, two vacuum pumps, bins for lead and zinc concentrate storage with individual conveying systems for loading the two kinds of concentrates. Filtering of concentrates is done on the second floor, the concentrates discharging directly into the concentrate-storage bins. On this floor are the lead and zinc filters, two diaphragm pumps, sample-filtering equipment, sample-preparation room and a change room for the mill employees. The flotation machines are on the third floor, at elevations allowing a gravity flow of the lead and zinc concentrates to the thickeners. The annex to the building contains a freight elevator and provides space for all reagent mixing and feeding, also storage of reagents and grinding balls. All the water used for milling purposes is pumped from the Junction mine and

Jan 1, 1947

By Chung Yu Wang, Guy C. Riddle

There are found in nature upward of II2 minerals containing antimony, but only a few of them, listed in Table I, can be considered as antimony ore-forming minerals. Stibnite (Sb2S3), antimony sulphide or glance, is the principal ore of antimony. The oxide ores—cervantite, kermesite, valentinite, sernarmontite—occur sparingly in nature. Dry methods are generally adopted for the extraction of the metal. Electrometal-lurgical methods have had much attention in America and Germany and have not yet found, on economic grounds, practical or extended application, except in a few places. During recent years, treatment of the poor grades of the ore, especially sulphide, by ore-dressing methods, has commanded some attention and been adopted at a few plants. The impure sulphide of antimony, resulting from the liquation process, is called lLneedle," "liquated" or "crude" anti- mony, and the refined metal itself is called antimony "regulus." The different processes for the treatment of antimony ores are shown in the diagram of Fig. I. Liquation of Crude Antimony The first step in the smelting of antimony is a simple one, the process of LLliquation," which produces crude or needle antimony. Ores containing $ 50 per cent Sb are used in the liquation process for the production of crude. The temperature required for liquation is between 550' and 600°C. Ores to be liquated are broken to about walnut size. If the pieces are larger than this, the low heat used will not penetrate' effectively, and if they are smaller the ore tends to pack too closely for adequate penetration. A packed charge also prevents the free escape of the fused sulphide. Intermittent Liquation in Crucibles The unique type of furnace that is in use in China for smelting is not highly efficient but is simple in construction and operation. The furnace is generally built

Jan 1, 1944

By G. R. Lehman

The Inspiration Consolidated Copper Co. had an orebody at Miami, Ariz., of close to 100,000,000 tons of low-grade copper ore, and the method of mining this ore most profitably was of great importance. The selection of a method was practically limited to a "top-slicing," a "shrinkage-stope" or a "caving" method. The "top-slicing" method would give a high extraction of the developed ore, at a high mining cost, and the "shrinkage-stope" or "caving" methods a lower extraction of the developed ore, at a lower mining cost. Ore-Drawing Tests To decide on the method to be used it was necessary to know about what extraction of the ore could be obtained by the "shrinkage-stope" or " caving " methods. As no definite information regarding the,question was available at the time, C. E. Mills, the general manager, thought that some information could be obtained by experimenting in drawing ore, covered with capping, from an experimental box. Some work had already been done along these lines by W. C. Browning for the Inspiration Copper Co. and by myself for the Live Oak Development Co. The idea was to represent as nearly as possible, in the experimental box, the conditions within an area of caved stopes of caved ore all ready for drawing. That is, the area was supposed to represent a semibroken mass with the capping above it in the same condition and ready to follow the ore downward as it was drawn out of the chutes under the ore. To represent the above condition, in the experimental box, crushed ore from the mine was placed in it to a given height, and red barren capping from the mine was placed on top of the ore. The Experimental Box The experimental box shown in Fig. 1 was made of wood and glass. The glass was used for the sides so that the drawing action of the outside row of chutes could be seen and noted, the latter being cut in the center by the glass sides. The length of the box was 30 in., width 20 in. and the

Jan 1, 1917

By E. P. Abrahamson II

The effect of transition element binary solid-solution additions upon the recrystallization temperature of vanadium has been investigated. Cr, Fe, Co, Ni, Mo, Ru, Rh, Os, and IY lower the recrystallization temperature, while Ti, Mn, Zr, Cb, Pd, Hf, Ta, W, Re, and Pt raise it. The majority of elements have their greatest effect in less than 0.15 at. pet. Both the rate of change of recrystallization temperature with atomic percent solute and the limit of initial linearity are found to Correlate with the free atom grozdnd state outer electron configuration of the sollte element. THE work of Abrahamson and Grant1 and Abraham-son and Blakeney2 has shown that the solute's elec- tron configuration appears to be a prime determinant of both brittle-to-ductile transition and recrystallization temperature in dilute binary alloys. It has also been shown by Abrahamson3 that the limit of linearity, i.e., the limit of initial linear change of recrystallization temperature with atomic percent solute, is also a function of the electron configuration of the solute in iron base alloys. Because of the systematic nature of the solute electron configuration correlation, it is to be expected that some systematic variation might be observed upon changing the solvent. Thus, this study of recrystallization in vanadium base alloys is the first of a series aimed at defining the role played by the electron configuration of solute in determining the recrystallization characteristics of dilute transitional alloys. PROCEDURE All alloys were made using 99.8 pct V containing 0.011 C, 0.024 N, 0.08 0, 0.006 H, 0.035 Ta, and

Jan 1, 1962

By G. V. Raymor, James T. Waber, I. Rex Harris

The lattice parameters of a series of fcc alloys of cerium and thorium were measured at 93 " and 298OK. Lattice parameters were also estimated for 171OK. Substantial deviations, y, from Vegard's law were observed. Although y was negative at the two higher temperatures, it was positive and large at the lowest temperature. A variety of models, which have been proposed in the past, were considered, and the calculated values of y were compared with the observed values. The best agreement was achieved with values computed with Friedel's equation. THE purpose of this investigation was to determine the effect of temperature on the lattice parameter and on deviations from Vegard's law of Ce-Th alloys. A large negative deviation from Vegard's law was first observed independently by Weiner, Freeth, and Raynor' and Van vucht2 in the room-temperature lattice parameters of Ce-Th alloys that form a continuous series of solid solutions. This observation was confirmed by Evans and Raynor. The allotropy of unalloyed cerium was reviewed recently by Gschneidner, Elliott, and McDonald. In two subsequent papers,5" these authors reported the influence of various alloying additions on the y= transformation, which occurs below room temperature. Although other rare earths tend to stabilize the double-hexagonal phase, thorium, plutonium, and scandium as solutes tend to stabilize the normal fcc phase. With addition of sufficient thorium as a solute, there is evidence that the formation of is suppressed and it becomes possible to pass continuously with decreasing temperature from the room-temperature phase to the fcc a phase. Thus there is a closed loop which is similar in many ways to the y loop well-known in ferrous alloys. A closed field also occurs in the pressure-temperature "equilibrium" diagram of unalloyed cerium. Because of interest in the effect of thorium additions and their influence on the a and phases, lattice-parameter measurements were made at low temperatures on the fcc phase for a series of alloys ranging from 10 to 90 at. pct Th. The results obtained at three temperatures are shown in Fig. 1. Evans and Raynors analyzed the deviations from Vegard's law in Ce-Th alloys in terms of changes in the occupancy of the 4f electron level in cerium,

Jan 1, 1964

Jan 1, 1969

By G. F. Jenkins

ASBESTOS is a general term embracing the fibrous varieties of a number of minerals. Of these, the hydrous magnesium silicate, chrysotile (H4Mg3Si209), a variety of serpentine, is the most abundant and useful to industry. All other types of asbestos belong to the amphibole group of minerals and are classified as: crocidolite, NaFe(SiO3), FeSiO3; anthophyllite, (MgFe)SiO3; amosite, also a ferromagnesium silicate but with iron content higher than that of anthophyllite; tremolite, CaMg3(SiO3)4; and, actinolite, Ca (MgFe)3(SiO3)4. PROPERTIES The commercial value of asbestos depends largely on the physical property that permits it to be readily separated into fine filaments of high tensile strength and flexibility, which, coupled with the fact that it has the quality of incombustibility of a mineral-in distinction to vegetable and animal fibers-makes it of unique usefulness for many purposes. To some extent, the value depends upon the length of the fiber, although extreme length is neither necessary nor desirable for most purposes. Chrysotile occurs as cross-fiber veins, in which the asbestos fibers are approximately' at right angles to the vein walls, with vein width- or fiber length-seldom exceeding 2 or 3 in.; also as slip-fiber, in which the fibers 'lie in the same plane as the vein or on slippage planes. A cleanly broken vein of cross-fiber has a pearly luster and may range from a deep green or brown color to light shades of yellowish green or cream. When of good quality, the fiber filaments forming the vein may be easily drawn away from their neighbors and exhibit a fine silkiness and pure white color. They may be twisted into a thread and when flexed between thumb and fingers are found to be strong and pliable. Chrysotile withstands comparatively high temperatures without breaking down completely or fusing but begins to lose water of crystalliza-

Jan 1, 1949

By K. J. McGrew, J. W. Murphy

Introduction Maximization of profit consistent with environmental protection is the principal goal of new applications development for any conventional or in situ mining technique. Efficient evaluation of all the parameters that contribute to mining costs and production hinges on proper design and evaluation of testing programs and data. The program discussed uses several field and laboratory procedures to estimate ore deposit characteristics and optimize lixiviant compositions. Ore characteristics and lixiviant compositions are then used in a long path leaching test (stream tube test). Stream tube test data are analyzed by mathematical models with computer assistance to predict such wellfield rate parameters as target metal production, lixiviant consumption, and restoration. When these predicted rates are combined with market values for target metals, capital expenditures, prices of lixiviant chemicals, and other economic variables (labor costs, power rates, and licensing fees), an assessment of the relative feasibility of various proposed mining plans is possible. The flowsheet in Fig. 1 illustrates this process. [ ] Field and Laboratory Procedures In general terms, the procedures followed in the evaluation of an in situ leaching application aim at accomplishing: •rapid leaching and maximum recovery of the target metal in a marketable form, •low consumption of lixiviant chemicals, •unquestionably satisfactory restoration of the mined aquifer, and •minimization of capital and operating costs for the above through development of an optimum mine plan. Keeping these goals in mind, the following minimum test program is generally recommended. Geology •Estimate of ore reserves and their variability. •Average disequilibrium value for uranium deposits. •Ore thickness, depth to ore, water level, degree of confinement, and consolidation. •Characterization of quality and quantity of other ore deposit constituents (e.g. sulfide minerals, ion exchange parameters). Hydrology •Single well pump and injectivity test. •Downhole vertical permeability test to compare flow rates of barren and mineralized formations. •Groundwater quality as it may affect licensing, hydro metallurgy, and restoration. Hydrometallurgy • Flask or autoclave tests for optimization of lixiviant parameters and determination of specific reaction rate constants. • Flask or autoclave tests for assessing amenability of lixiviant solutions with ore, consumption of lixiviant, stability of metal in solution contacting ore, and environmentally important species mobilized. • A long-path leach test for modeling the behavior of the lixiviant solution flowing through a long mineralized streamline (stream tube testing). •Metal recovery tests from lixiviant solutions (ion exchange, electrowinning, etc.). •Lixiviant regeneration tests. •Environmental restoration tests.

Jan 1, 1985

By D. G. Russell

Two techniques have been developed with which the applicability of pressure build-up analyses can be extended to include pressure data which previously have been considered virtually unusable. One of the interpretation methods makes possible the analysis of pressure build-up performance during the wellbore fill-up or after production period which occurs soon after a well is closed in. The other technique is an extension of a method for analyzing pressure build-up performance during the late-time portion of the pressure build-up which occurs after boundary eflects first begin to alter the shape of a conventional pressure build-up curve. With both of these methods it is possible to obtain estitnates of the kh product, the skin factor and the reservoir pressure. In addition, with the late-time analysis technique it is possible to obtain an estimate of the contributory drainage volume of the well being tested. This means that in some cases a check on reservoir limit test and (or) material-balance calculations can now be obtained from pressure build-ups. Both methods are slightly more time-consuming than conventional pressure build-up analysis methods because trial-and-error plots of pressure data must be made. The late-time method for analysis of pressure build-ups is in principle applicable to the late-time portion of a two-rate flow test or a pressure drawdown test. The interpretation formulas and procedures for these types of tests are also outlined. In these cases, as with pressure build-ups, it is significant that an estimate of the contributory pore volume is also obtained. On the basis of limited experience with the new techniques, it appears that satisfactory estimates of the kh product, skin factor, reservoir pressure and, for late-time analysis, contributory drainage volume can be obtained. INTRODUCTION The analysis of bottom-hole pressure build-up behavior in closed-in wells has been a a subject of interest in petroleum engineering circles for many years. In fact, few other subjects have received as much attention as pressure buildup analysis methods have. The cause for this interest is essentially twofold in nature. First, the pressure behavior of a well can normally be measured with a reasonably high degree of accuracy so that good data for analysis can be obtained. Secondly, over a fairly wide range of operating conditions, valuable information as to the quality of the reservoir rock and completion efficiency of the well can be obtained at a nominal cost. In recent years, numerous papers have been prepared on the effects of various operating conditions and reservoir heterogeneities on pressure buildup behavior. Very little work has been done, however, on extension of pressure build-up analysis methods to those pressure data which are not amenable to analysis by the present methods. The theory upon which the analysis of shut-in bottom-hole pressure build-up data is based is derived from the solution of the radial flow equation for a slightly compressible fluid for constant-rate conditions. It requires that the well be closed in for a sufficient period of time to obtain a clearly defined linear portion on the plot of observed bottom-hole pressure vs log (t + ?t)/ ?t (where At is shut-in time, and t is producing time to the instant of shut-in). From the slope of the plot and other normally obtainable data, the formation permeability, the well damage or skin factor, and the reservoir pressure at infinite shut-in time (if the reservoir were infinite) can be estimated. The successful application of this procedure depends on being able to recognize the straight-line section on the basic pressure build-up plot. The presently used pressure build-up interpretation theory also assumes that a well is closed in at the sand face and that no production into the well occurs after shut-in. In practice, of course, the well is closed in at the surface, and inflow into the well continues until the well fills sufficiently to transmit the effect of closing-in to the formation. This adjustment period is commonly referred to as the "afterproduction" or "fill-up" portion of the pressure build-up. During the period that the well fill-up effect is most pronounced, the basic pressure build-up plot is nonlinear. At later shut-in times after the effects of a drainage boundary have been felt at the well, deviation from the straight-line behavior of the pressure build-up plot also results. In many cases either of these effects or a combination of both can make the straight-line portion on the pressure build-up plot difficult to recognize. Obviously, an extension of pressure build-up analysis methods to include the afterproduction period and the period in which boundary effects are being felt would be desirable and might render valuable pressure data which for years have been considered virtually unusable. The principal reference of note concerning pressure buildup analysis during the afterproduction period is a paper by Gladfelter, Tracy and Wilsey.1 In the approach of these authors it is necessary to measure the rate of influx into the well during the afterproduction period. This is done through sonic measurements or through measurement of tubing-head and casing-head pressures simultaneously with

Jan 1, 1967

By Alan Arias

On grinding in pure water, zirconium, tantalum, iron, and stainless-steel powders were extensively comminuted and simultaneously oxidized with hydrogen release, whereas nickel, copper, and silver powders did not react with water and their particle sizes increased. On grinding nickel, copper, and silver in water pressurized with oxygen, nickel and copper became extensively comminuted and were oxidized, whereas silver did not react with oxygen and its particle size increased. From these results and other considerations , it is hypothesized that for extensive comminution of ductile metals and alloys to occur on grinding they must react with the grinding media. UlTRAFINE metal and alloy powders are finding an ever-growing number of applications in metallurgy and in other fields.' Of particular interest are ultrafine metal and alloy powders suitable for dispersion strengthening.2'9 Various research programs on dispersion strengthening are being carried out and in some of these programs the ball-milling method is being used to produce dispersion-strengthened materials. This method usually involves the simultaneous grinding of metal or alloy and a dispersoid followed by consolidation of the resulting powder mixture. To obtain the ultrafine powders required for dispersion strengthening,' grinding is carried out in many liquids, including aqueous and nonaqueous media, with or without grinding aids.4'5 Nonaqueous liquids usually contain water as an impurity and some grinding aids may contain water of hydration.5 The water present may affect the grinding process. The writer has shown5 that. on ball milling chromium in water, the chromium is oxidized and hydrogen is released. It was surmised that the same reaction may occur on ball milling other metals and alloys in waterbearing liquids. Therefore, the investigation of ball milling in water was extended to metals and alloys other than chromium. In the course of the investigation, however, it became apparent that the data-to-gether with the results from a few additional experi-ments—could be used to postulate a comminution mechanism for ductile metals and alloys. A well-known comminution theory is that of smekal.7 According to this theory, comminution is possible because of the weakening effects of surface cracks and other imperfections in materials. This theory imposes a lower limit of about 1 µm for the ground particles. The beneficial effects of liquids and additives on the rate of grinding are well known.8 Mechanisms by which liquids and additives may aid in grinding were reviewed by Rose and Sullivan.' One aspect of these effects is based on Rehbinder's theory of crack propagation in materials under stress.9 According to Reh-binder's theory, liquids or additives may promote the spread of cracks in stressed materials by lowering the surface tension at the crack tip. Rose and Sullivan surmise that the same mechanism may be operative during grinding, thereby facilitating comminution of the particles. In addition, Rose and Sullivan reviewed how additives may act as dispersants as a result of their being adsorbed on the surface of the particles being ground. This concept has been suggested by Quatinetz, Schafer, and smea15 to explain from their experiments the major role of additives that enabled them to grind metal down to 0.1 µm. Discussions of other comminution theories and additional sources of material on the subject will be found in Ref. 10. None of these previous suggestions and theories, however, can account for all phenomena encountered during ball milling of metals to submicron size in this and in a previous investigation by the author.6 The objectives of this investigation were to determine the behavior of metal powders during ball milling either in pure water or in oxygenated water and to gain an insight into the grinding mechanism. Zirconium, tantalum, iron, nickel, copper, and silver powders were ball-milled in pure water. These metals were selected because their oxides cover a wide range of free energies of formation. For comparison purposes, an alloy-type 430 stainless steel-was also ball-milled in pure water. The pressure of the hydrogen released during ball milling was monitored in order to determine the oxygen that combined with the metal or alloy. In order to obtain more information on the nature of the grinding process, nickel, copper, and silver powders were also ball-milled in oxygenated water (water pressurized with oxygen). The oxygen that reacted with the powders was determined from the pressure decrease in the mills. The powders resulting from ball milling in pure water and in oxygenated water were subjected to surface area, optical microscopy, and X-ray diffraction analyses. With these data, the oxygen calculated to be combined with the metals during ball milling, and comparison of the free energies of formation of the oxides of the milled powders with that of water, a comminution mechanism was postulated. MATERIALS, EQUIPMENT, AND PROCEDURES The materials used in this investigation were powdered metals, deaerated distilled water, high-purity helium, and commercial grade (99.5 pct purity) oxygen. The powdered metals used were zirconium, tantalum, iron, nickel, copper, and silver. A 16 pct Cr, ferritic stainless steel, type 430, was also used. The purities (or nominal compositions) and the surface areas of these metals and the alloy are given in Table I.

Jan 1, 1970