By L. Evrard, S. Brouwer, E. Bosly, E. Boydens

"A partial desulfurization roasting process has been tested on a typical copper-zinc sulfide concentrate in a Nichols Herreshoff monohearth pilot furnace whereby the su!fµr is partially removed and iron is to a certain degree preferentially oxidized. The phase changes that occur in the particles during selective roasting at 650°C and 800°C over a range of residence times were investigated by the use of chemical analysis, optical microscopy, X-ray diffraction and electron microprobe analyses. The purpose of this work was to get an insight into the mineral assemblages formed by controlled oxidation roasting and to evaluate if this non traditional approach could be afterwards used to recover zinc, copper and iron by a physical separation method. IntroductionThere has been considerable interest over the years in improving extraction and processing procedures for recovering non ferrous metals especially from polymetallic ores containing copper, lead, zinc and iron sulfides with very fine intergrown phases. Complex sulfide ores, which represent considerable reserves and resources in copper, lead and zinc, as well as precious metals and sulfur, are difficult to treat by conventional physical processes, leading to impure concentrates at low metal recovery. Some methods that can be used to treat such ores were described by G. Barbery (1). Various metallurgical routes generally combining pyro- and hydrometallurgical methods have been explored to develop new processes to recover the metals from zinc-bearing sulfidic ores and concentrates (2, 3, 4). The feasibility of partitioning complex sulfide minerals to simpler phases in order to improve selective extraction of mineral constituents has also been investigated (5)."

Jan 1, 1999

By William Petruk, J. H. Gilles Laflamme, Jean Robitaille, Louis J. Cabri

"A quantitative mineralogical study using ore microscopy, electron microscopy, proton-microprobe, image analysis, and material balances was done on samples from the circuit of a concentrator in Quebec, with particular emphasis on the Cu concentrate. The ore contains many different minerals, of which the principal ones, in decreasing order of abundance, are pyrite, sphalerite, chalcopyrite, bornite, galena, tennantite, and pyrrhotite. Minor to trace amounts of covellite, chalcocite, stannoidite, mawsonite, colusite, wittichenite, miharaite, hessite, petzite, electrum, and an unidentified Cu-Pb-Bi-sulfide also occur.Liberation of pyrite is very high in all size fractions for all samples (ranging from 80-91 %). Liberation of chalcopyrite, bomite, sphalerite, and tennantite is relatively high, on average, in the head .sample and Cu concentrate (55-78% and 66-88%, respectively). Most of the chalcopyrite in the flotation tails is not liberated, whereas about one half of the tennantite and sphalerite are liberated in both the flotation and :final tails. Recoveries calculated for the Cu concentrate (on the basis of assays, mineralogy, and image analysis) are chalcopyrite 72. 5%, bornite 73. 7%, sphalerite 41.0%, tennantite 70.9 %, and galena (together with some trace minerals) 34.2%. It was also calculated that the Cu concentrate contains 10.0 % of the pyrrhotite and i.4 % of the pyrite.Materials balance calculations were done on the five major sulfide minerals to determine the mineralogical distribution of 13 major, minor, and trace elements (as determined by protonmicroprobe analyses). It was determined that tennantite is the principal carrier of Bi (67%), As (90%), and Te (86%) in the Cu concentrate. Therefore, removal oftennantite, which is mostly liberated in the Cu concentrate would significantly reduce these three contaminant elements, but at a loss of9% of the Cu, 2.0% of the Zn, and 0.7% of the Ag. The precious metals (Au, Ag) occur as discrete minerals (electrum, petzite, hessite). Some of the Ag also occurs in solid solution in bornite (23.1% of Ag in Cu concentrate), tennantite, and sphalerite. Four of the major sulfides (chalcopyrite, bomite, sphalerite, tennantite) in the ore also contain measurable concentrations of the following trace elements: Se, Cd, In, Sn, and Sb, occurring mostly as solid solutions. Some of these elements are also concentrated (up to about 18%) in minor and trace minerals such as colusite, stannoidite, and mawsonite."

Jan 1, 1999

By Chunyang Guan, Jilai Xue, Jun Zhu, Qiaochu Liu

"Al-Sc Alloys have showed many advanced properties for a wide range of industrial application, which is usually produced using thermal reduction process. This work is aimed to develop an electrochemical process to make Al-Sc alloy using industrial Hall aluminum reduction cells. The experiments have been carried out in a lab cell where NaF/AlF3-Al2O3-LiF as electrolyte, Sc2O3 as raw material, and liquid aluminum as cathode were used at operating temperature of 950 °C. The resulting Al contained 0.2 - 0.5 wt.% Sc that is the common range in its content for advanced applications. However, a small fraction of Sc was found from thermal reduction at Al melts interface. SEM-EDS and ICP-AES analysis showed a uniformed distribution of Sc at varying locations of the Al-Sc alloy sample. In addition, a higher Sc content in Al-Sc alloy can be obtained with introducing ultrasound through the cathode than that without it.IntroductionIn recent years, scandium has been investigated as an alloying element for aluminum alloys. With addition of a small amount of Sc, Al alloys can improve the strength, weld ability, resistance to re-crystallization and corrosion resistance [1-3]. Due to their advanced properties and potential applications, the demand for Al-Sc alloys will increase in the future. However, the difficulties in reduction technologies and the high costs in production process may limit their expansion in application areas.The current major method of producing Al-Sc alloys is to mix Sc into Al by melting Al-Sc master alloy. This alloying process has several technical problems, such as easy segregating and heavy burning loss, etc. The price of Sc metal or starting material is also high, so the mixing process is an expensive alloying method. Molten salt electrolysis is alternative method to prepare RE metal and RE alloys [4, 5]. It also can reduce the segregation of alloying elements. Sc2O3 is an ideal material as raw material with low price and decomposition voltage. Some work has proved that Al-Sc alloys can be obtained by electrolysis Sc2O3 directly in cryolite [6-8], or CaCl2 molten salt [9]."

Jan 1, 2012

By S. R. Reddy, R. G. Reddy

"The Margules equation is used for interpreting excess Gibbs energy of several ternary systems. In the present study activity coefficient of a dilute solute, 2, in a binary solvent 1-3 was derived. The derived expression is used to interpret logarithmic activity coefficient of oxygen and sulfur in several metallic systems. Self interaction parameter of the solute is derived from the partial function of solute using constant compositional path. An expression for logarithmic activity coefficient and self - interaction parameter of solute is also derived using Maclaurin infinite series. The derived equation is based on Maclaurin infinite series used successfully to deduce thermodynamics of self interaction of oxygen as a interstitial atom in two metallic systems. The predicted thermodynamic parameters values using Maclaurin infinite series and Margules equations, are in excellent agreement with the experimental data and also our predictions are far more accurate than the predictions made by other models.1 IntroductionIn most of the pyrometallurgical high temperatures processes, interactions of solutes such as oxygen, nitrogen and sulfur, with the solvent atoms are most important during refining processes. There are numerous theories are developed [1-25] to interpret the thermodynamics of solutes in multicomponent alloy systems. Which are mainly developed using statistical or Quasichemical equations.Wagner [4] developed one energy parameter ideal solvent model based on activity coefficient of solutes compositional dependency. He used one energy interaction term which is not able to account for interaction energy parameters for the same solute concentration at different solvent compositions and also it is ineffective model to predict for strong interacting systems."

Jan 1, 1996

By R. G. Reddy

The Margules .equation is used for interpreting excess Gibbs energy of several ternary systems. In the present study activity coefficient of 'a dilute solute, 2, in a binary solvent 1-3 was derived. The derived expression is used to interpret logarithmic activity coefficient of oxygen and sulfur in several metallic systems. Self interaction parameter of the solute is derived from the partial function of solute using constant compositional path. An expression for logarithmic activity coefficient and self - interaction parameter of solute is also derived using Maclaurin infinite series. The derived equation is based on Maclaurin infinite series used successfully to deduce thermodynamics of self interaction of oxygen as a interstitial atom in two metallic systems. The predicted thermodynamic parameters values using Maclaurin infinite series and Margules. equations, are in excellent agreement with the experimental data and also our predictions are far more accurate than the predictions made by other models.

Jan 1, 1996

By Agnes Y. Lee

he U.S. Bureau of Mines developed a method to treat lead-contaminated soil and ebonite battery casing wastes to produce a nonhazardous material. The cleanup procedure involves wet screening to separate a minus 18-mesh soil fraction; removal of metal1ic lead, rocks, wood, etc. ; carbonation to change lead sulfate to acid-soluble lead carbonate; size reduction; acid leaching; and rinsing. The casing wastes undergo size reduction and washing to remove the lead sulfate sludge before carbonation. Similarly, the minus 18-mesh soil is carbonated, then acid leached and rinsed. In leaching, fluosilicic acid (H SiF,) and hydrogen peroxide (H20,) are used to dissolve lead compounds. An electrowinning method is employed to strip lead from the lead-rich leachate. The acid content in the leachate is replenished with fresh H,SiF, acid prior to recycling. Treated casing wastes and soils pass the Toxicity Characteristic Leaching Procedure (TCLP) test and can be reclassified as nonhazardous materia1s. Based on this process, a conceptual pilot plant has been designed which will be demonstrated on wastes from two Superfund sites.

Jan 1, 1993

By C. H. Tsau

The intermetallic compounds of Ni-25Al-xFe, x is 20-40 at.%, were prepared by arc melting and drop casting into ingots, and were rapidly solidified into ribbons by melt spinning. The microstructure evolution of these alloys with varied Fe content were examined by the x-ray diffraction, optical microscope, scanning electron microscopy and transmission electron microscopy. The results reveal that two phases, {y'} and {B} phases, are existing in the alloys with low Fe content, and the microstructure changes from the mixture of y' and {B} phases to a single 0' phase when the Fe-content reaches to 40 at.%. Also, the formation of y' phase will be suppressed by rapidly solidified process. For annealing both of the melt-spun and the cast specimens, a disorder 0 phase was revealed in both of the ribbon and the cast ingot of Ni-Al-Fe alloys with higher Fe content. In addition, increasing the increment of iron which substituting nickel in this alloys results in increasing the lattice parameter of both {y'} and{B} phases.

Jan 1, 1992

By Youqi Fan

Complicated copper oxalate precursor powder was prepared using ammonium oxalate as precipitating agent in the Cu(II)-C2O42--NH3-NH4+-H2O system. The composition and morphology of the powder are characterized by chemical analysis, X-ray Diffraction (XRD), scanning electron microscope (SEM), infrared spectroscopy (IR). The effects of temperature, copper ion concentration, pH value are investigated. It?s indicated by the experimental results that precursor of copper oxalate is prepared below a critical pH value, whereas the precursor turns to be a complicated copper salt combined with NH3 while over the pH value. Probable chemical formula CuC2O4?x(NH3)?yH2O can be assumed which x and y are relation to experimental conditions. Technological parameters, such as temperature, initial copper concentration and solution pH value, have significant effects on particle size, morphology and dispersion of precursor powder. By controlling certain technological conditions, various morphologies of precursor, pie shape, spindle shape and rod shape can be synthesized.

Jan 1, 2009

By Duan Xin-hui, Wang Xin, Peng Jin-hui, C. Srinivasakannan, Zhang Li-bo

The work attempts to optimize the process of preparation of modified semi-coke from semi-coke using phosphoric acid (H3P04) as the activating agent using the response surface methodology (RSM). The influences of three major dependent variables, the impregnation ratio, activation time, and activation temperature were assessed on the independent variables yield and the iodine number. The empirical relationship between the dependent and the independent variables were established using the quadratic response surface models, which were utilized to optimize the process parameters. The significance of each of the parameters and interaction among the parameters on the independent variable was assessed based on analysis of variance (ANOVA). The process variables were varied within the range of impregnation ratio (IR) from 1.5 to 4, activation time from 30 to 90 min and activation temperature from 550 'C to 650 'C. The optimized process conditions were estimated to be an IR of 2.29, activation time of 32 min, and an activation temperature of 605°C respectively using the process optimization tool. The BET surface area of modified semi-coke of the optimized sample was estimated to be 915m2/g, with the pore volume of0.71cm3/g, with an average pore diameter of 3.09 nm, with micropore volume fraction being 52.36%. The scanning electron microscope (SEM) images were utilized to visualize the surface pore structure.

Jan 1, 2013

By I. Gaballah

Jarosite contains up to 15 % of heavy metal compounds 'HMC'. The current waste disposal methods will not be allowed in the near future due to new environmental regulations and pollution risks. For these reasons, thermal treatments of raw or decomposed jarosite, in controlled atmospheres, were investigated. The aim of these treatments is to decontaminate the jarosite and/ or to recover the HMC for recycling. According to physico-chemical characteristics of the samples, the thermal treatments in controlled atmospheres N2, CO+N2 and C12+air lead to the extraction rate that vary from 93 to 98 %. Heavy metal compounds were separated by cooling the gaseous phase. The treatments' residue was almost free from HMC. Between 700 "C and 800 "C, the chlorinating treatment was successful of eliminating more than 97 % of HMC contained in four different samples.

Jan 1, 1999

By Jorge Alberto Soares Tenório

Household zinc based batteries contain some heavy metals such as zinc, manganese and mercury. There is a large effort from manufacturers in order to eliminate the last one. As a municipal waste, the disposal of batteries has become an increasing worry. The aim of the present work was to characterize dry batteries scraps, and establish a flowsheet for their processing. This was done using unit operations of mineral processing and parameters and yields of each stage have been defined. Such procedures have been chosen due to their low cost. The operations were hammer mill grinding, size separation, magnetic separation and specific weight separation in water. The characterization step was done through chemical analysis and x-ray difiactometry. After size classification, it was verified that 76.6% of the total amount of zinc was over 1.70mm. This fiaction was constituted basically of zinc and some coarse pieces from the steel body, paper and plastics. This fraction was submitted to magnetic separation followed by specific weight separation in water. A visual examination showed that during the grinding process, graphite was concentrated in the finer fractions. Manganese concentration in the fractions over 6,35mm was less than 2%. This means that there was low contamination by the paste in this fraction. It was due to the entrapment of the paste by steel scraps (from the body) and zinc (from the cup) during grinding.

Jan 1, 1999

By Ramana G. Reddy

Thermodynamic modeling and experimental study on impurity capacities and their distribution between mattes or metal and slags in smelting, converting and refining of non-ferrous metals was discussed. A brief review on the recent developments in copper smelting and converting is presented. The analysis showed that, copper smelting capacity increased by a factor of 10 since 60's, smelting rate increased by a factor of more than 5 and process fuel equivalent decreased by a factor of 2. A thermodynamic model for prediction of impurities capacities in slags and their distribution in mattes and slags was developed. The impurities capacities (i.e. sulfur and arsenic) of slags were calculated a priori with no adjustable parameters using the Reddy-Blander model. The capacities predictions were made in a wide range of matte and slag compositions, PSo, and temperatures in conditions pertaining to copper and lead industrial slags. The calculated results for sulfide and arsenate capacities are in good agreement with the available experimental and industrial copper and lead industrial slags data. The sulfide and arsenate capacities in copper slags (fayalite, ferrite and olivine) and lead slags are reviewed. The application of RB model predicted ratios of O2 and S2 partial pressures in industrial copper smelting processes are discussed. Application of this model for the prediction of Sb, Bi and other impurity capacities and their distribution ratios in mattes or metal and slags, in industrial smelting and refining processes is discussed.

Jan 1, 2003

By P. N. Anyalebechi

"The as-cast microstructure of two commercial-size ingots of aluminum alloy 3004 produced by the electromagnetic casting process was quantitatively characterized. This involved the quantitative determination of through-thickness and across-width variations in dendrite cell size, grain size, macrosegregation of alloying elements, interparticle spacing, and the types, volume fractions, and sizes of the constituent or second phase particles. More than ninety-five percent of the constituent phases in the ingots consisted of the A16(Mn,Fe) phase; the desirable a-Al 12(Fe,Mn)3Si phase was not detected in any of the ingots by Guinier X-ray diffraction analyses or electron probe X-ray microanalyses. A significant microstructural heterogeneity through the thickness and across the width of both ingots was observed. For example, macrosegregation, and the sizes of the constituent phase particles, dendrite cells, and grains increased concomitantly from edge to mid-width and from surface to center of the ingots. There was a -20% depletion (negative macrosegregation) of Mg and a +54-87% enrichment (positive macrosegregation) of Ti in the center of the ingots. With the exception of grain size, there was no significant microstructural difference between the two ingots examined. The causes and practical implications of the observed microstructural heterogeneity in the ingots are discussed.IntroductionThe first step in the fabrication of majority of wrought products of aluminum and its alloys is the casting of large ingots or billets of simple shapes (round or rectangular). The sizes of the ingots vary from 10 mm to 450 mm diameter or 25 mm to 780 mm thick. The quality of the finished products is established at the ingot casting stage. This is because the microstructural characteristics, such as secondary dendrite cell size or arm spacing, amount of alloying elements retained in solid solution, macrosegregation, and the characteristics of second phases, produced during casting cannot be reversed by subsequent processing. Up until twenty-five years ago, the effect of as-cast microstructure of large ingots on the structure and behavior of thin sheets (0.34 mm thick) during drawing and ironing processes was incorrectly assumed to be minimal or nonexistent. This was based on the erroneous notion that the thermal treatments and large reduction (>99.94%) and strain that the ingot undergoes during production of the sheets completely destroys the original ingot structure and its inherent heterogeneity. However, the effects of ingot structure can, a priori, be deduced from the observed effects of constituent phase particle size, type and volume fraction on recrystallization, development of texture during annealing and deformation, and earing. In fact, careful examination of the behavior of products produced from different size ingots or castings have shown that the original microstructure of the ingot has a direct impact on the properties and performance of the end products."

Jan 1, 2011

By S. W. Marcuson

Smelting of nickel-copper sulfide ores at Vale Inco’s Sudbury operations commenced in 1888 and the first converting plant went into operation in 1892. As the demand for nickel grew, the smelting operations expanded and by the 1960’s the Copper Cliff Smelter featured the longest converter aisle in the world with space for nineteen Peirce-Smith converters. During this long period, different converting techniques and vessels were employed. The evolution of converting is reviewed with special emphasis on the modifications made to the Peirce-Smith vessel to accommodate the metallurgical and process needs of the changing times.

Jan 1, 2009

By N. J. Themelis

In the last two decades, the Outokumpu flash smelting process has become the dominant new technology for copper smelting and has? also been applied to the smelting of other metal sulfides. The application of oxygen enrichment and improvements in concentrate burner and furnace design have resulted in ever increasing smelting rates per unit volume of the reaction shaft. This paper examines the. rate phenomena taking place in the reaction shaft of the Outokumpu furnace and compares information obtained from a mathematical model of heat and mass transfer rates to results obtained in pi1ot tests conducted at Pori, Finland, and to actual performance of a number of flash smelters around the world. 2?

Jan 1, 1985

By Alexander V. Derevyanko, Victor P. Popov, Alexander I. Raitchenko

"If an electric current flows along some electroconductive suspension in columnar form the solid particles are 'experienced thermal, mechanical, and electromagnetic influences.The objects were suspension Sn (liquid) - Ni-Cr-Mo-W alloy (solid particles). This is refractory alloy on the Ni base. The direct constant current (with density -106 A/m2 ) flowed through the named suspension during 180+300 sec. At the beginning of experiments samples were ones containing particles suspended uniformly in volume. Although density of solid particles was ~9x103 kg/m3 , i. e. higher than density of liquid Sn (-6.8x103 kg/m3 ), after end of this processing, the non-uniform distribution of particles in volume of samples was observed: concentration of Ni-alloy particles in lower part was smaller than their concentration in upper part of samples, and simultaneously their concentration is increased near outer surface. There was probably the natural convection of Benard-Rayleigh type which had carried, so lid particles upwards, and, in same time, there was the action of spatial Lorentz-forces directed to center forcing the radial movement.The knowledge of named phenomena can be useful for elaboration of technology of gradient dispersed materials and development of some materials science fields.IntroductionThe liquid metal with the electric current or under the alternating magnetic field is experienced compression. This action causes the pressure within metal and the change of the surface of the metal column (see, for example, [1-4]). One of results of such an electromagnetic compression is extraction of the foreign solid particles from a cylindrical liquid sample to surface in the radial directions. However, more complicated paths of the inclusions are observed under some conditions of electric treatment."

Jan 1, 1999

By R. T. Jr. Faria, H. Vargas, R. Toledo, S. Cosin, V. P. Souza

"With the purpose of decrease environmental impact, caused by industrial residues (just discarded in the environment) and clay extraction in the ceramic industry, sanitary ware wastes were incorporated into clay. In contrast, it is important to evaluate not only the technological essays but also gases emissions in the ceramic firing process. The pollutant gases emitted in ceramic with residues can be in much larger concentrations than that in a pure clay ceramic firing or, on the other hand, can decrease the pollutant gas concentrations. With the aid of thermal analyses and photo acoustical techniques it was observed that sanitary ware waste can reduce the C02 emission. The gas emissions were shown as in function of firing temperature from 300 DC to 1100 DC. In order to analyze phase transformations during the firing process, clay samples and wastes were both analyzed by x-rays fluorescent chemical analysis and x-rays diffraction.IntroductionResearch works on the structural and physical changes that wastes, mainly industrially produced, cause to the final ceramic product has been rapidly expanding in these last two decades. See, for instance references in [1]. In spite of these examples of a continuous effort to incorporate wastes into clay ceramic motivated by technical and economical advantages, environmental issues are still a matter of concern. However, the gas emission due to the clay firing process and its related atmospheric pollution may be enhanced as a consequence of an incorporated waste [2]. It is known that the firing of clay ceramics in conventional furnaces using fuels such as wood, charcoal, heavy oil and natural gas generates appreciable amounts of gaseous components, mainly carbon dioxide (CO2), carbon monoxide (CO) and methane (CH4). Additionally to the atmospheric pollution, these gas sets could be harmful to the human health and can corrode equipments [3,4]."

Jan 1, 2012

By J. E. Dutrizac

Fracture-exposed surfaces of sphalerite samples having five different solid solution iron contents ranging from 0.0 wt% to 14.8 wt% Fe were leached for 15 to 120 s at 100°C in 0.3 M Fe(S04)1.5 -0.3 M H2S04 media. The reacted samples were examined using X-ray photoelectron spectroscopy (XPS) which provides chemical state information on the first few nanometers of the solid surface. Surface compositions show that the leaching rate increases with increasing solid solution iron content of the sphalerite. Detailed evaluation of high resolution S2p spectra show that the leaching progresses via the formation of polysulphide species. Disulphide species were not detected in any of the experiments. Examination of the Zn2p and Fe2p spectra indicate little change in the chemical states of these elements over the duration of the experiments. Longer leaching times resulted in the generation of elemental sulphur. The ratios of elemental sulphur to dissolved ferrous ions and zinc suggest that less than 5% of the sulphide is oxidized to sulphate. Morphological studies showed that the elemental sulphur commonly formed at a few isolated sites, such as the grain boundaries. Furthermore, euhedral sulphur crystals were often identified. These observations suggest that at least part of the elemental sulphur forms via dissolved sulphide species which are oxidized in solution by ferric sulphate.

Jan 1, 2003

By Yang Jian-guang, Deng Zi-xiang, Zhang Xu-liang, Li Jun-yuan

"Hyperaccumulator biomass harvested after heavy-metal phytoremediation must be considered as hazardous waste that should be contained or treated appropriately before disposal or reuse. As a potential method to detoxify the biomass and to convert this material to a suitable bio-energy resource, the hydrothermal upgrading process was applied to remove heavy metals and upgrading crude bio-oil from Pteris vittata stems and leaves harvest. Parameters such as material granularity, temperature, Liquid/Solid (L/S, ml/g), pressure, duration and catalysts were examined for their effect on the removal efficiency of heavy metals and upgrading efficiency of crude bio-oil. Maximum heavy metal removal efficiency of>99% and crude bio-oil upgrading efficiency of 83% were attained with an 200 mesh (75 µm) granularity, LIS 40:1and23 MPa at 380°C in the presence ofO.l mol L-1 K2C03 for 30 min. GC-MS analysis results show that the resulting bio-oil mainly consists of benzene 11 %, ketone 42%, alcohols 14%, alkene 15% and ester 11 %, etc., and the relative molecular weight distribution lies in 94-282, carbon number distribution lies in 6-18, calorific value is 32MJkg-1.IntroductionPhytoremediation of soil or water with hyperaccumulator has been extensively explored in recent years [1-4]. Living plants can clean up soils or waterways. This approach exploits the ability of various plant species to thrive in high metal environments where large amounts of toxic elements are accumulated, such as heavy metals, and is particularly appropriate when slow remediation of relatively low metal concentrations is acceptable. Advantages compared with existing remediation methods include the minimal site destruction and destabilization, low environmental impact, and favourable aesthetics; advantages compared with biosorption include continuous in situ regeneration of the biomass, and the ability of living plant cells to supplement passive sorption of metals with metabolic mechanisms of metal uptake and detoxification [5-8]."

Jan 1, 2014

By E. Maziar Sauber

In order to prepare a more desirable feedstock for a rare earth elements separation refinery, cerium, a penalty element in the refinery feedstock, should be removed from the mixed rare earth elements oxide or carbonate feedstock. In this study, cerium (III) to cerium (IV) oxidation by calcium hypochlorite and subsequent precipitation was used to remove cerium from a mixed rare earth elements chloride solution. A factorial design of experiments was used to determine the effect of process variables such as temperature, pH, and oxidizer addition on the oxidation of cerium (III) using synthetic solutions. Under certain test conditions, all of the cerium was successfully removed from the chloride solution, and some REE accompanied cerium and reported to the precipitate. This proposed technology can allow for low cost removal of cerium from mixed rare earth elements chlorides.