By F. F. Schmidt, H. R. Ogden, E. S. Bartlett

ThE solubility of carbon in tantalum has been reported to be very low at temperatures below 1500 C,1'2 increasing to at least 0.02 wt pctl at the eutectic temperature of 2800°C. The solubility limits at low temperatures were based on metallo-

Jan 1, 1963

By William E. Ford, Edward Salisbury Dana

WheweUite. Calcium oxalste CaCz04.Hz0. In small colorless monoclinic crystals. Optically +. j3 = 1.555. From haxony, with coal; also from Bohemia, and Akace. Oxammite. Ammonium oxelate, (N&)rC20r.2HzO. From the guano of the Gudape Isbnds, Peru.

Jan 1, 1922

[1-Iron and Steel JOHN A. MATHEWS, Chairman RALPH H. SWEETSEH. Vice-chairman WILLIAM CAMPBELL. Vice-chairrmn MAX ROESLER, Secretary Iron Ore R C. ALLEN W. 0. HOTCHKISS MAX ROESLER ERNEST F. BURCHARD THOMAS T. READ DWIGHT E. WOODBRIDGE M. M. DUNCAN WILLIAM KELLY CARL ZAPFFE]

Jan 1, 1928

Established as a Division March 24, 1922 John R McMillan, '56, Chairman Claude R Hocott, '55, Past Chairman Thomas C Frick, '56, Vice-Chairman D W Akins, '57, Vice-Chairman Joe B Alford, Executive Secretary 800 Fidelity Union Building Dallas 1, Texas T A Pollard, Treasurer

Jan 1, 1954

Established as a Division March 24, 1922 R B Gilmore, '57, Chairman G L Yates, '56, Vice-Chairman Phil J Lehnhard, '56, Vice-Chairman John R McMillan, Past Chairman T A Pollard, Treasurer Joe B Alford, Executive Secretary 800 Fidelity Union Building Dallas 1, Texas

Jan 1, 1955

By Geo. H. Eldridge

This sketch of the Florence oil-field, presented to the Institute by permission of the Director of the U. S. Geological Survey, is accompanied with a map, Fig. 1, the topography of which has been taken from a field-manuscript of the Survey. The scale of the map and

Jan 1, 1892

By O. B. Hopkins

As prefatory to the body of this paper, a few general statements will be made (1) in regard to the history and importance of the asbestos, (2) as to the principal sources of the raw material, and (3) as to the types and modes of the occurrence of asbestos.

Jan 1, 1915

By Kichizo Niwa

A LTHOUGH studies on the roasting of ferrous A sulfide have been carried out by several investigators, some disagreements still remain among those results. Schwab and Philinis1 have measured the rate of oxidation by a precise thermobalance and have concluded that the rate is controlled by diffu-

Jan 1, 1958

By C. G. Rhodes

A technique for producing etch pits in uranium monocarbide has been developed. The pits, which are assumed to be associated with dislocations, appear individually and as arrays delineating sub-boundaries, as seen in Fig. 1. The samples used were single crystals prepared by the technique described by Nadler.* Uranium

Jan 1, 1963

[Officers and Committees of the Society of Petroleum Engineers 1 Officers and Staff of the AIME 2 . Officers of AIME Sections Predominantly Petroleum in Membership 3 AIME Local Sections and SPE Regional Organization Maps 5 Alphabetical List of Members 7 Geographical List of Members 102 Advertisers' Index 133]

Jan 1, 1961

University of Alabama University, Alabama Mining and Metallurgical Society STEPHEN STILLWELL, President VINCENT ZENOBILE, Secretary GEORGE '1 BATOR, Faculty' Sponsor RAY L. FARABEE, Counselor University of Arizona Tucson, Arizona Miners' Society RICHARD BRITTAIN, President FRED W. SHERMAN, JR., Secretary J. B. CUNNINGHAM, Faculty Sponsor E. P. GARDNER, Counselor

Jan 1, 1943

The production of Rumania for 1937 amounted to 54.142.600 bbl., which is a decrease of 10.319.636 bbl., or 15.9 per cent over that of 1936. In all. 1.300.000 ft. were drilled during the year— an increase of 220.000 ft. over 1936.

Jan 1, 1938

By D. A. Hinckfuss

The large and compact but simple Bougainville Copper Limited flotation circuit has been in operation for 3-1/2 years. Discussion of problem areas encountered since start-up and remedies that have been implemented or proposed, form the main basis of this paper. Full current operational data is also provided.

Jan 1, 1976

By G. R. St. Pierre, L. M. Adelsberg, R. Speiser

OXIDE platelets have been observed'-3 in oxidized tantalum adjacent to the metal-oxide interface, Fig. 1. The origin and identity of the platelets are important with respect to the proposal of an acceptable mechanism of tantalum oxidation. At reaction temperatures below 750°C, it has been established that the platelets

Jan 1, 1967

By Walter Crafts, C. M. Offenhauer

IN the course of study of the heat-treatment of low-alloy steels, the behavior of alloy carbides at subcritical temperatures was found to vary from that indicated by published investigations. In order to establish the ranges of formation of carbides in low-chromium steels, a series of steels containing up to 0.60 per cent carbon and 7.5 per cent chromium has been investigated with respect to the type of carbide formed after quenching and tempering at subcritical temperatures. The types of carbide formed as products of austenite transformation to pearlitic and pseudomartensitic structures have also been determined. There have been numerous investigations of the carbides in chromium steels and diagrams of the iron-chromium-carbon system.1 Westgren, Phragmén and Negresco2 identified the following carbides in chromium steels: [Cementite Fe3C (containing up to about 15 per cent Cr) Trigonal carbide Cr7C3 (containing up to about 55 per cent Fe) Cubic carbide Cr4C (or Cr23C3) (containing up to about 25 per cent Fe) Orthorhombic carbide . Cr3C2 (containing only a few per cent Fe)] The most complete information on the iron-chromium-carbon system was supplied by Tofaute, Sponheuer and Bennek3 and by Tofaute, Küttner and Büttinghaus.4 By means of dilatometric and microscopic studies, sections of the diagram were established. This diagram showed the presence of the special carbide Cr7Ca in steels containing about 2.5 per cent to 12 per cent chromium in low-carbon steels and from about 5 to 20 per cent chromium in r per cent carbon alloys from A1 to room temperature. The present investigation has shown that a carbide inversion from Fe3C to Cr7Ca occurs in chromium steels containing more than about 1 per cent chromium after hardening and tempering at subcritical temperatures above about 500°C. The type of carbide observed to be more stable in quenched and tempered specimens was also found to be produced by direct austenite transformation in corresponding ranges of temperature and composition. EXPERIMENTAL PROCEDURE The steels used in these experiments were made in magnesia-lined crucibles in high-frequency furnaces and were poured into 2-in. ingots. The ingots were forged into 1-in. round bars, and all heat-treatments were conducted on specimens of this section .size. Sections of the bar stock 8 in. long were hardened in air, oil or water depending on the composition, after heating to a temperature sufficiently high to dissolve the carbides. The low-carbon and low-chromium steels were not entirely martensitic after quenching, and contained some ferrite and pseudomartensite. No pearlite was observed in the microstructures after auenchine. The quenched bars were cut into

Jan 1, 1942

By Frederick C. Langenberg

IT has been shown1 that copper can be removed from iron-base alloys by solvent extraction with molten lead and sodium sulfide slags. In these processes copper removal is favored by a positive deviation of copper in iron from ideal behavior. Chou' determined the distribution of copper between liquid silver and iron and obtained a value for the activity coefficient of copper in iron at 1600°C, y°, of 9.12. Chipman" calculated the activity coefficient from the Fe-Cu phase diagram to be 12 at 1600°C. More recent work by Koros and Chipman" yields a value at 1600°C for y V equal to 8.0. In this latter work, the distribution of copper between silver and iron was measured at 1600°C, while the activity of copper in the silver phase was determined from calculations based on the Ag-Cu phase diagram. The present work presents another value of based on calculations from the Cu-Pb phase diagram, on the heat of mixing data for the Cu-Pb system, and on an experimental study of the distribution of copper between iron and lead at 1600°C. These experiments were part of a larger research on the removal of copper from iron-base alloys conducted at The Pennsylvania State University. Experimental Procedure—The distribution of copper between pure iron and lead at 1600°C was made in the furnace assembly shown in Fig. 1. The melts were made in high purity alumina crucibles under an atmosphere of prepurified argon. Temperatures were read with an optical pyrometer sighted into a %-in. hole drilled in the inductor. Extensive calibration of the optical readings with immersion readings had been carried out previously. The initial charges consisted of 100 g of electrolytic iron and varying weights of copper. The melts were brought rapidly to 1600°C and 75 g of lead added. The temperature was quickly readjusted to 1600°C, and the melts were held for 10 min at this temperature. A sample was then drawn from the iron layer in a fused silica tube. This sample was analyzed to determine the copper content of the iron layer at equilibrium, while the copper content of the lead layer was determined from a material balance. The validity of the material balance was confirmed by a chemical analysis of the entire lead layer for one heat in which the crucible was removed and quenched after the iron sample was taken. The calculated copper content of the lead-rich phase was 1.18 pct; while the entire lead layer analyzed 1.20 pct Cu. The distribution results are shown in Fig. 2. The distribution constant, N,.'r'"/N, is equal to 3.95. Discussion—From the Cu-Pb phase diagram' it can be seen that lead-rich liquid Pb-Cu solutions

Jan 1, 1957

By L. D. Jaffe, D. C. Buffum

EARLIER the authors and coworkers had pre sented data on isothermal temper embrittlement of an SAE 3140 steel?' In that work, however, attention was concentrated on embrittlement at 575°C and below. Preliminary measurements showed that embrittlement at 675 °C was much mote rapid than would be expected from the data at the lower temperatures: and indicated the need for further work above 575°C. The possibility of an upper nose in the time-temperature embrittlement diagram above 575°C was pointed out. Procedure The same heat of SAE 3140 steel was used as in the previous work, and experimental methods were the same. All blanks were austenitized 1 hr at 900°C and water, quenched. Groups were then tempered 1 hr at 675"C, water quenched, and given embrittling treatments for times of 5 min to 240 hr at 675" to 600 °C, as shown in Table I. Other groups, after the temper and quench, were embrittled 48 to 1440 hr at 550°C. Another series was tempered 240 hr at 675"C, quenched, and held for various times at 650" to 375°C (Table 11). For comparison, a series was tempered for these same times at 700°, 675", and 650°C (Table 111). The Ae, temperature for this heat of steel had been determined as approximately 690°C;1*a the treatments at 700°C were introduced to determine the effects of tempering in a range where a little austenite would fonn. A large number of other treatments, involving holding at two temperatures in succession after the temper, and occasionally slow cooling or heating, were also studied. These treatments are listed in the tables. Austenitizing was done in air; all subsequent treatments were in salt. Blanks were always water quenched after the last treatment. The heat-treated blanks were machined to standard V-notch Charpy specimens. A transition curve for each group was obtained by breaking the specimens at various temperatures on a 217 ft-lb impact machine having a striking velocity of 16.8 fps, and plotting the observed percentage of fibrous fracture vs the test temperature. From this plot, the transition temperature was taken as the lowest temperature at which the fracture appeared 100 pct fibrous; its accuracy is estimated as +5"C. Generally, hardness was measured on every bar. Since a decrease in hardness itself seems to decrease the transition temperature somewhat, a correctiona of —0.28"C per Bhn was applied to permit comparison of the transition temperatures on a uniform basis of 24 Rc. The transition temperature and hardness results are given in Tables I through VI. Where overlap of earlier work1.' occurred, data were combined.

Jan 1, 1958

By K. K. Rao, M. E. Nicholson

IN a recent paper on the solubility of carbon in Ni-Cu alloys,' Nicholson reported that the carbon solubility appeared to be limited by the electronic structure of the alloys and that the solubility was propor- tional to the density of states at the Fermi surface of the "3d" band. In order to determine whether or not this relationship is a general one, the study has been extended to other systems. One of these is the CO-Ni system. This system was chosen for study because 1) it is adjacent to Ni-Cu system in the periodic table, 2) the alloys of cobalt and nickel do not form stable carbides at 1000°C, and 3) the system exhibits no pronounced change (less than 1 pct) in lattice parameter from cobalt to nickel,' see Fig. 1. The alloys were prepared from -200-mesh 99.92 pct Ni furnished by the International Nickel Co. and spectroscopically pure -200-mesh cobalt sponge obtained from Johns on-Matthey and Co. The powders were weighed, mixed, and pressed using a pressure of 40,000 psi. The samples were sintered for 24 hr at 900° C in dry hydrogen and then cold rolled to a thickness of 0.010 in. (Samples containing more than 70 wt pct Co had to be annealed after cold reductions of about 20 pct to avoid cracking.) The alloys were carburized at 1000°C in an alun-durn boat containing Acheson AUC powdered graphite in an atmosphere of carbon monoxide cylinder gas which had been passed through Ascarite to remove carbon dioxide. After carburizing for either 12 or 24 hr the samples were moved to a cool zone of the furnace to cool. Cooling required about 5 min. The samples were filed to remove about 0.005 in. from the surface and then analyzed using a conventional combustion-gravimetric analytic method. The results of this investigation are shown in the lower portion of Fig. 1 and Tabulated in Table I. The nickel percentages for these alloys were determined from the weights of the powders from which the alloys were made. The solubility of carbon in pure cobalt at 1000°C (fcc) is 0.25 wt pct. This is somewhat less than the 0.33 wt pct measured by Boecker.3 From his data, it would appear Boecker's samples were supersaturated before the equilibrating treatment and that a 20-min treatment was not long enough to achieve equilibrium. Since in the present investigation the 12 and 24 treatments produced essentially equal carbon contents, our figure is presumed to represent more nearly the equilibrium value. The solubility of carbon in nickel of 0.19 wt pct agrees quite well with the value of 0.21 wt pct

Jan 1, 1963

By Robert P. Burrows

Discussion of the paper of R. P. Burrows, presented `at the New York meeting, February, 1916, and printed in Bulletin No. 107, November, 1915, pp. 2237 to 2245. EDWIN M. CHANCE, Wilkes-Barre, Pa.-I have been very much interested in the comprehensive and able discussion of the important topic of mine lighting just given by Mr. Burrows, especially as I know by common report Mr. Burrows' ability and his close touch with the development of the electric mine lamp, and its use in mines in connection with a portable electric lamp. It is regrettable that Mr: Burrows was not able to acquaint himself more closely with the cost of mine illumination, the actual cost, as produced by a portable light as carried by miners, whether a flame safety lamp or an open light. Had he been able to acquaint himself more closely with these data, he perhaps would not have arrived at some of the conclusions which he has presented to us in his paper. For example, we find Mr. Burrows advises that the open torch is by far the cheapest source of illumination, as produced by a portable light. I am very sure that is not the fact. The cost of miners' oil varies from about 25.c. a gallon to 90b. a gallon. The various States have passed laws from time to time rendering it mandatory that the miner shall use, whether he is willing or not, a so-called better or higher grade of burning oil. These laws have entailed the use of an oil so expensive that the use of the oil torch has become practically impossible, and the acetylene or carbide miners' lamp has largely taken its place. I have evolved a few figures showing the relative efficiency and usefulness of the open oil torch and the acetylene miners' lamp. For example, the acetylene miners' lamp consumes or burns 4 liters of acetylene per hour, or 0.14 cu. ft.; the oxygen consumed is 10 liters, or 0.35 cu. ft. per hour; air consumed, 50 liters, or 1.76 cu. ft. per hour; black-damp produced, 40 liters, or 1.41 cu. ft. per hour; air rendered extinctive to the acetylene flame, 112 liters, or 3.95 cu. ft. per hour; carbide con- sumed, 13 g. per hour. The open oil torch, on the other hand, burns about 20 g. of oil per hour; the oxygen consumed is 48 liters, or 1.69 cu. ft. per. hour; air consumed, 240 liters, or 8.47 cu. ft. per hour; blackdamp produced, 191 liters, or 6.73 cu. ft. per hour; air rendered extinctive to oil flame is 1,413 liters, or 49.92 cu. ft. per hour.

Jan 5, 1916

By R. F. Stilwell

There are three things that all coal consumers look for when they burn coal: (1) suitability for their particular requirements and burning equipment, (2) uniformity of shipments, and (3) quality as expressed by heating value and other chemical and physical tests. Suitability, or proper application, is determined generally from previous buying experience. It is a function of (1) the reliability and integrity of the shipper and distributor, (2) of a certain coal field or seam and of (3) uniformity and quality. Quality is limited by the location and geology of the seam and mine, the mining and preparation methods and equipment and the knowledge and ability of the personnel. Uniformity of shipments is in many ways the most important factor in coal selection. Lack of uniformity in chemical quality, size consist and treatment cause most of the customer complaints that arise from faults of the coal shipper. Lack of uniformity destroys suitability and quality standards, causing a large customer turnover, and greatly increases sales expense and reduces the net return to the operator. Oil and gas fuels are more uniform in quality than solid fuels, and there will be more gas and oil competition for coal markets after this war than before, because the size of their market is a direct function of the dimensions of their pipe lines, which have been greatly increased during the war. Present mechanical coal-cleaning equipment based upon gravity concentration has gone a long way toward giving us a coal of uniform ash content. The chart in Fig. I, by Hebley,1 shows the greater uniformity of the ash content of washed coal as compared with that of raw coal. Wide variation in the nature and amount of ash in the coal feed to the washer leads to a coal of non-uniform ash content. Mechanica1 cleaning equipment does not understand such terms as ash-softening temperature, coking properties, size consist and sulphur content. Unless the feed to the washer is uniform, the washed coal probably will not be uniform. Table I shows the ash, sulphur and ash-softening temperature of two mines in the Pittsburgh bed, both raw and washed, loaded over the same tipple; also No. 3 and No. 4 Pocahontas seams, both raw and washed, loaded from the same preparation plant. It is obvious that they must be blended or loaded separately if a uniform product is to be obtained. Why Is Blending Necessary? It was natural for the operators of captive mines producing by-product coals to recognize the necessity for blending raw coals of different quality and coking characteristics. They have had many years of experience with blending high, low and medium volatile coals at their oven plants. They have found that careful blending gives a coke of more uniform quality and better structure. Coals that could not be

Jan 1, 1947