By Reed W. Hyde

Some information has been published on the sulphur dioxide concentration of gases from D wight-Lloyd machines sintering lead ores but most of this relates to the customary practice in which the charge is relatively high in lead and is sintered in two passes Over the machine. It is thought, therefore, that the following observations on sintering in one pass a low-lead, low-sulphur charge may be of interest. The data were obtained in sintering lead sulphide notation concentrates mixed with minus 20.mesh oxide ore, the mixture carrying 16,8 per cent Pb and 5.3 per cent S. No returns were used because of the limited amount of sulphur available as fuel, but the mixture pelletized readily. to make a satisfactorily permeable bed on the sintering machine. As there was a possibility that the SO z might be utilized, a series of runs was made to determine the concentration ofSO2 in the gases at different points along the wind box, and the effect on this concentration of changes in the wind-box vacuum. Several runs each were made with vacuums (as measured in inches of water at the wind box) of (1 2 to 1 in., ('1 4 to 3% in. and (3) 6 to 5% in. The averages of the determinations from each series are platted On the graph (Fig, 1). The vertical scale shows the percentage by volume of SOz (as determined by the Reich method), and the horizontal scale shows the time e~pressed as percentage of the total sintering time. Sintering was considered to be complete when no SOz could be detected in the gases. In all cases the depth of bed was 4 1/2 in. and the weight of dry charge per square foot of hearth area was 45.2 lb. Other data are given in the table. The volume of gases corresponding to the several points along the wind box at which SO2 determinations were made could not be measured, but has been calculated from the SO2 Content and sulphur elimination on the assumption that the volume is uniform throughout the sintering period. This is not strictly true, as with a given vacuum the volume usually will drop slightly toward the middle of the period and increase toward the end. However, this made is a reasonable approximation. several interesting features are brought out by these data. In general, the published data on SO 2 concentration in sintering under ordinary conditions show a high SO2 concentration in the early stages followed by a rapid decrease in concentration and with relatively little SOz in the gases from the last half or third of the operation. In other words, the greater part of the sulphur elimination is obtained in the first third or half of the period. In these runs, the 6-in. vacuum, which approximates the usual operating condition, gives a curve that follows this customary pattern. Maximum SO2 concentration is obtained 234 min. after

Jan 1, 1944

By L. J. Dijkstra, R. J. Sladek

IN earlier work the effect of manganese on the general behavior of nitrogen in iron was the subject of a careful examination by Fast.' Part of the investigation was made, in collaboration with one of the present authors (L.J.D.), by using the internal friction method. This technique, which has been described elsewhere,' showed some significant changes in the properties of Fe-N alloys by the addition of a small amount of manganese namely: 1—Under standard conditions the maximum of the nitrogen peak in pure iron appears around 20 °C and the half width is about 27 °C. By addition of 0.5 atomic pct Mn a general broadening of the internal friction peak occurs. The half width is increased by about 9°C. Moreover, a shift of the maximum of about 5°C toward a higher temperature takes place, Fig. 2. 2—The precipitation of nitrogen from the supersaturated solution, measured, e.g., at 200 °C, was inhibited by the addition of the amount of manganese given in effect 1. The broadening of the nitrogen peak was confirmed in more recent work3 on samples which were prepared from Westinghouse Puron iron. The effect of manganese on the rate of precipitation, however, was much less striking than in the earlier work' based on Philips high purity iron. Theory To explain the first change in properties just referred to, effect 1, the following two assumptions were made:' First, every manganese atom in sub-stitutional solid solution creates around it six interstices located between an iron and a manganese atom, as is evident from Fig. 1. These interstices, conveniently called Fe-Mn interstices, have for nitrogen a free energy level which is AG* lower than the normal Fe-Fe interstices between two iron atoms. For such low concentrations of manganese as 0.5 atomic pct, the possibility that two manganese atoms will be nearest neighbors can be disregarded. Second, it is assumed that in addition to the normal relaxation time TFe at least one new relaxation time, Mn, Fe, enters in the phenomena which is associated with the elementary diffusion jumps between a Fe-Mn interstice and an adjacent Fe-Fe interstice. Fig. 1 gives schematically the free energy for a nitrogen atom as a function of its position along the line ABC. A tentative analysis of the nitrogen peak in a 0.5 pct Fe-Mn alloy based on these assumptions has been made in Fig. 2. The dotted curve with a maximum at 22°C is caused by jumps between Fe-Fe interstices, the dotted curve with maximum at 32°C by jumps between an Fe-Mn and an Fe-Fe interstice. The two effects added together give the dash-dot internal friction curve for the alloy. In the following these two components will be referred to as the normal peak at 22°C and the abnormal one. (The small secondary peak at

Jan 1, 1954

By W. D. Von Gonten, R. L. Whiting

Regression analysis was used to correlate the physical properties of 478 sandstone and 90 carbonate core samples. Porosity, permeability, electrical formation resistivity factor, capillary pressure and the sonic velocity of the shear and compressional waves were measured. Prediction equations for porosity, permeability and electrical formation resistivity factor were found which should be useful in understanding the relationships between the physical properties of porous media in formation evaluation. INTRODUCTION The physical properties of porous media are important to the petroleum engineer and geologist. To evaluate fully the potential and behavior of a subsurface formation such as a petroleum reservoir, certain physical properties of the porous medium must be known. The problem of accurately determining physical properties of subsurface formations has not been solved because many determinations must be made by indirect measurements and because of the difficulties caused by complex pore structure and presence of clays in most naturally occurring porous media. Due to the difficulty in measuring some of the physical properties of porous media, it would be advantageous to be able to predict a certain physical property of a rock from other physical properties of the rock which could be measured more easily and more accurately. Since most potential reservoir rocks are heterogeneous, relationships between the physical properties are very complex and thus far no satisfactory correlations based on theory or laboratory models have been developed. It appears that empirical relationships obtained by measuring the physical properties of a large number of samples of naturally occurring porous media and applying regression analysis to develop equations for one physical property in terms of other rock properties is the best approach. REVIEW LITERATURE The three physical properties used as dependent variables for correlating purposes were porosity, permeability and formation factor. Since formation factor is more difficult to determine, a brief review of the literature is provided on this property. The first work on determining formation factors was published by Archie1 in 1942. He defined this property of a porous medium as F - Ro/Rw......(1) where Ro is the resistivity of the porous medium when completely saturated with a brine of resistivity Rw. Archie found the best correlation between formation factor and porosity was the following equation, where is the porosity fraction and m is the constant characteristic of the rock. The value of m was 1.3 for unconsolidated sand packs, and ranged from 1.8 to 2.0 for consolidated sandstones. In 1950 Patnode and Wyllie2 and De Witte3 observed that the formation factor as determined by Eq. 1 was valid only when the porous medium contained no conductive solids such as clay or shale. When conductive solids are present the formation factor is also dependent on the resistivity of the saturating fluid. Therefore, in samples containing conductive solids the formation factor decreased as the resistivity of the saturating fluid increased. Because of this. the measured formation factor was called the apparent formation factor and was designated Fa. Patnode and Wyllie proposed the following equation,

By P. R. Sperry

Aluminum alloy 3S was examined to determine the relationship between the applicable phase diagram and the microstructures produced under conditions tending toward non-equilibrium as well as equilibrium. The only phases present in the alloy were aluminum, (Mn,Fe)A16, aAI(Mn,Fe)Si, and silicon. It was found that the alloy behaved essentially as though it belonged to the Al-Mn-Si system. The effects of various solidification rates and of various homogenization treatments were studied. Particular attention was given to a nonuniform precipitate distribution which reflected the solute distribution in the cast aluminum solid solution. Some possible explanations for the solute distribution based on characteristics of the Al-Mn-Si or AI-Mn systems were discussed. ALUMINUM alloy 3s (aluminum plus 1.25 pct Mn) is one of the oldest and the most widely used of the wrought aluminum alloys. In spite of this fact, there are some aspects of the metallography of 3s which have not been revealed or which have not been brought to the attention of the metallurgist working with the alloy. The purpose of this investigation was to demonstrate in general how some of the fundamentals of equilibrium phase diagrams may be applied to the study of an alloy and to show specifically the origin of certain metal-lographic features of aluminum alloy 3s. It is hoped that this information can serve as a basis for solving specific problems relating microstructure to such things as mechanical properties, recrystallization, grain growth, and surface finish. Literature Survey Considering that alloy 3s contains only one alloying addition, manganese, it seems reasonable that it would have characteristics pertaining to the A1-Mn system. However, those characteristics might well be altered by the impurities in the commercial alloy, especially iron and silicon. Therefore, not only the simple binary but also more complex systems had to be reviewed. One characteristic of the A1-Mn system worthy of mention is its sluggishness, which leads to conflicting solubility data1,'2 and makes it relatively easy to supersaturate the solid solution and shift the eutectic composition during rapid solidification.3'4 Another characteristic is the strong influence which small amounts of impurities, especially iron, exert in lowering the solid solubility of manganese. Undissolved manganese is ordinarily present in an intermetallic phase, MnAl,, having an orthorhombic crystal structure. A metastable precipitating phase designated as "G" has been reported but small amounts of iron and silicon suppress this phase entirely." Raynor has established that MnA1, can dissolve a considerable amount of iron by a substitution of iron for manganese atoms up to 50 atomic pct.'" Consequently, in the Al-Mn-Fe liquidus diagram, the eutectic valley separating the primary aluminum and (Mn,Fe)Al, fields is fairly close to a constant Mn + Fe content." This is an important consideration in regulating the composition of 3s and also other aluminum alloys with high manganese additions."

Jan 1, 1956

By W. F. Carew, H. D. Kessler, F. A. Crossley

AS part of a program on phase relationships and transformation processes of titanium alloy systems, the titanium-rich corner of the Ti-Mo-V system has been investigated. This region was surveyed primarily to supply information toward the development of a creep resistant, weldable alloy, with a minimum alloy content, for use in the 425° to 550 °C range. Specifically, the investigation was directed toward the development of a stable ß alloy with less total alloying additions than is found in the Ti-30 pet Mo alloy. A secondary objective was the development of a creep resistant, weldable a-ß alloy for application around 300°C. Molybdenum was selected as primary additive to titanium on the basis of an investigation1 which showed that the Ti-30 pet Mo alloy had promising elevated temperature tensile properties. Furthermore, aging studies1 showed no tendency for this

Jan 1, 1957

By Harry Udin

IN 1948, the writer and his associates determined the surface tension of solid copper by balancing the force of surface tension in a very fine wire against an external load.' At that time we, in common with other early workers, assumed that grain boundary energy in a pure metal is very small in comparison to the energy of an external surface. Accordingly, we neglected the internal surface energy of the coarse-grained specimens. Since that time, experimental evidence has accumulated showing that grain boundary energy, far from being small, is generally about one-third of the energy of an external surface.2-4 This is sufficient to introduce a significant error into our determination. The differential equation governing equilibrium is: wdl - yds, + y*ds2 [I] rather than wdl = yds as originally written. w is the balancing force in dynes, 1 the length of the specimen, sl the external and s2, the internal surface area, y the copper/ copper vapor surface tension, and y* the grain boundary tension. Fortunately, we had made for another purpose a careful study of the size and shape of the grains, and found that the boundaries, with rare exceptions, traversed the specimens and were perpendicular to the wire axis. For this case, eq 1 leads to w = rry -(n) r2y* [2] where r is the wire radius and (n is the number of grains per unit length. A count of some twenty 5-mil wires indicated that - n became 80 & 10 after a short anneal near the melting point, and remained nearly constant for as long as 96 hr at temperature. An assumption of y* = 1/3y leads to a defining eauation for r: [31 The term in the brackets may be considered a correction factor applied to eq 11 of ref. 1. Upon applying this factor, the surface tension of solid copper at its melting point is found to be 1650 & 100 dynes per cm, rather than 1370 as previously reported.' The new temperature coefficient is —0.55 dynes per cm per "C. Grain boundary energy is more significant than surface energy to the physical metallurgist. It is evident from eq 2 that a series of experiments with wires of different grain size can lead to an evaluation of y*. The details of such an experiment are being worked out now. References 1 H. Udin, A. J. Shaler, and J. Wulff: The Surface Tension of Solid Copper. Trans. AIME, 185, 186-190; Journal of Metals (Feb. 1949) TP 25303. 2 G. L. C. Bailey and H. C. Watkins: Surface Energies in the System Solid Copper-Molten Lead. Proceedings Physical Society. (London) (1950) 36B, 350. 3 L. H. VanVlack: Inter granular Energy of Iron and Some Iron Alloys. Ph.D. Dissertation, Univ. of Chicago, Sept. 1950. 4 . P. Greenough: Grain Boundary Energies in Silver. R.A.E. Report, No. Met. 52. (May 1950) Fan-borough, Hants, England.

Jan 1, 1952

By W. J. Reagan

All of the material described in the following paper is within the following specifications: carbon, 0.50 to 0.85 per cent; phosphorus and sulfur, 0.04 per cent max.; manganese, 0.60 to 0.85 per cent; silicon, 0.20 to 0.30 per cent. Steels with much lower carbon contents can be handled in exactly the same manner. One of the first things necessary to basic open-hearth slag control is uniformity of charge, particularly as to the silicon content and the percentage of lime charged. Our past work has shown that the silicon content of the charge is more important than the carbon content in determining the carbon at which a heat will melt. We have found that by keeping the silicon content of the charge about 0.60 to 0.65 per cent, and with a lime charge of about 7 per cent (limestone equivalent), our heats melt sufficiently high in carbon to allow a moderate feed of ore and the slag will be of low iron oxide content. In making a heat of 0.75 carbon steel we endeavor to have the heat melt at about 1.20 per cent carbon. The iron oxide content of the finishing slag depends upon the final phosphorus desired; for a given ratio of lime-silica in the slag, the lower the phosphorus desired in the final steel, the higher the iron oxide content of the finishing slag must be. By reducing the lime charge to a minimum, the heats melt faster, and by keeping the silicon content at the desired figure the heats melt with a high SiO2 slag, which has been shown in previous work to give a low iron oxide slag. In most of our work, using a 180,000-lb. charge and with basic pig containing about 1.20 per cent silicon, we use a lime charge of 8500 lb. of limestone and 2000 lb. of burnt lime. The pig charge is about 48 per cent of cold pig, and the charge contains a large percentage of works scrap. This causes a heat to melt with about 1.20 to 1.30 per cent carbon, for a heat that will finish about 0.75 per cent carbon. This gives a heat that will need a feed of about 2000 lb. of ore, and also a slag with an FeO content of about 4 to 5 per cent at melting. The additional FeO obtained from the ore addition will bring the FeO in the slag at tapping to about 6 to 7 per cent. It is necessary to carry quite a fluid slag to prevent pickup of FeO, as a too heavy slag causes FeO to build up in it, giving a finishing slag with a greater FeO than is desired. By adjusting the lime charge of a basic open-hearth heat, a very sensitive adjustment of the slag may be obtained. The figures in Table 1

Jan 1, 1935

By W. J. Reagan

All of the material described in the following paper is within the following specifications: carbon, 0.50 to 0.85 per cent; phosphorus and sulfur, 0.04 per cent max.; manganese, 0.60 to 0.85 per cent; silicon, 0.20 to 0.30 per cent. Steels with much lower carbon contents can be handled in exactly the same manner. One of the first things necessary to basic open-hearth slag control is uniformity of charge, particularly as to the silicon content and the percentage of lime charged. Our past work has shown that the silicon content of the charge is more important than the carbon content in determining the carbon at which a heat will melt. We have found that by keeping the silicon content of the charge about 0.60 to 0.65 per cent, and with a lime charge of about 7 per cent (limestone equivalent), our heats melt sufficiently high in carbon to allow a moderate feed of ore and the slag will be of low iron oxide content. In making a heat of 0.75 carbon steel we endeavor to have the heat melt at about 1.20 per cent carbon. The iron oxide content of the finishing slag depends upon the final phosphorus desired; for a given ratio of lime-silica in the slag, the lower the phosphorus desired in the final steel, the higher the iron oxide content of the finishing slag must be. By reducing the lime charge to a minimum, the heats melt faster, and by keeping the silicon content at the desired figure the heats melt with a high SiO2 slag, which has been shown in previous work to give a low iron oxide slag. In most of our work, using a 180,000-lb. charge and with basic pig containing about 1.20 per cent silicon, we use a lime charge of 8500 lb. of limestone and 2000 lb. of burnt lime. The pig charge is about 48 per cent of cold pig, and the charge contains a large percentage of works scrap. This causes a heat to melt with about 1.20 to 1.30 per cent carbon, for a heat that will finish about 0.75 per cent carbon. This gives a heat that will need a feed of about 2000 lb. of ore, and also a slag with an FeO content of about 4 to 5 per cent at melting. The additional FeO obtained from the ore addition will bring the FeO in the slag at tapping to about 6 to 7 per cent. It is necessary to carry quite a fluid slag to prevent pickup of FeO, as a too heavy slag causes FeO to build up in it, giving a finishing slag with a greater FeO than is desired. By adjusting the lime charge of a basic open-hearth heat, a very sensitive adjustment of the slag may be obtained. The figures in Table 1

Jan 1, 1935

By M. C. Fuerstenau, D. W. Fuerstenau

Long-Chained aliphatic amine salts have been used for the separation of sylvite (KC1) from halite (NaC1) by flotation. It is puzzling how these two minerals, which are so similar chemically and crystallographically, can be separated by this method. Gaudin as postulated that the difference in floatability of halite and sylvite with salts of primary amines depends on ionic size: In the case of amine flotation, the cation would attach itself to the chloride. I have a speculation there, which I cannot prove, that the ammonium group, that is the –NH3 group in the amine, floats potassium chloride because the dimensions of this group as it has been measured in other compounds is almost identically the dimensions of the potassium ion, quite different from the sodium ion, and so it fits where potassium had been, in place of it and not attached to it.

Mar 1, 1956

By Warren Weaver

SOME of the advantages of the inductive method of electrical prospecting were emphasized in a paper by Dr. Max Mason.1 Since this emphasis was misunderstood by some to indicate a too exclusive interest in inductive methods, we are especially happy to help correct this impression by reporting on some of our work on surface potential methods. EARTH CURRENTS AND SURFACE POTENTIALS When two electrodes, A and B, are placed on the surface of the ground a distance d apart, and a 100-volt battery is connected across the elec- FIG. 1.-LINES OF CURRENT FLOW AND SURFACE POTENTIAL IN MILLIVOLTS IN THE CASE OF A HOMOGENEOUS EARTH. trodes, current flows from the positive electrode A to the negative electrode B. The current does not pass directly from A to B along the straight line joining these two points. In fact, a negligible amount of the

Jan 1, 1928

By Francis H. Brownell

During the 1920's lead consumption in the United States reached the highest average total ever known. For the ten-year period 1921-'30, it was slightly over 600,000 tons per year, or say 50,000 tons per month, and the price averaged 6.81 per lb. But the I930's witnessed a severe drop in the consumption of lead is in other business activities. The average U.S. consumption for the ten-year period 1930-'40 was slightly less than 380,000 tons per year, or under 32,000 per month, with the average price dropping to 1.191c. per lb. The outlook in early 1939 was for a continuation of this average consumption and price a demand of 35,000 to 40,000 tons per month, and a price level of 4 1/2 to 5c. in the United States.

Jan 1, 1941

By Hallan Marsh

THE subject of this paper is apt to bring to mind wells ranging from 6000 to over 8000 ft. in depth. However, it is uncommon to pump wells at depths greater than about 5000 ft. Fig. 1 shows the number of wells being pumped at various depths by one company in Southern California. FIG. 1.-NUMBER OF WELLS BEING PUMPED BY ONE COMPANY FROM VARIOUS DEPTHS IN SOUTHERN CALIFORNIA. A few companies have a very few wells pumping at depths greater than this. This paper will deal with wells between 3000 and 5500 ft. in depth. Most California oils at these depths are between 25° and 35 gravity. The subject is so broad that it will be necessary to omit many interesting phases, and to treat others very briefly. Power, power transmission equipment, power efficiency, counterbalancing, sucker rods, pumps and volumetric efficiency will be discussed.

Jan 1, 1928

By W. C. Hagel

In 1952, Hauffe and pfeiffer1,2 reported that parabolic rates of nickel oxidation are decreased by factors of two and four at 1100° and 1000°C, respectively, when Li2O vapor is present. Hauffe 's3 explanation was that monovalent lithium enters the crystal lattice of p-type NiO to decrease cation-vacancy concentration and, hence, diffusion of Ni2+ ions across the growing oxide. After first succeeding in adding lithium directly to molten nickel, the purpose of this investigation was to determine whether alloyed lithium is a more effective oxidation inhibitor than the external vapor. Seven 650-g heats were prepared by melting carbonyl nickel inductively under 1 atm of argon. Various amounts of lithium were added by dropping small chunks into the melt. Only about 10-pct recovery was achieved with the remainder lost by spattering and volatilization. Nominal and actual

Jan 1, 1965

SEC. 1. The membership of the Institute shall comprise seven classes, namely: 1. Members; 2. Honorary Members; 3. Senior Members; 4. Associates; 5. Junior Members; 6. Rocky Mountain Members; 7. Junior Foreign Affiliates. All shall be equally entitled to the privileges of membership, excepting that no member of any class whose residence shall be outside of the United States of America, except those residing in Mexico and Canada, shall be entitled to vote. SEC. 2. Members: A person to be eligible for election or transfer into the class of Member must be at least 27 years of age and must have had at least six years' employment in the practice of engineering, mining, geology, metallurgy, or chemistry, during at least three years of which he must have held positions of responsibility in one or more of these fields. This shall not apply to Rocky Mountain Members.

Jan 1, 1946

By Paul Weir

Bleaching clays have been used extensively in the oil-refining industries for a number of years. Their use in water purification is relatively recent and less extensive. They are frequently classified as (1) those naturally active and (2) those active after artificial activation with acid. Fuller's earths fall within the general group of bleaching clays and gradually the commercial term "fuller's earth" has been applied to natural clays originating, for the most part, in the southeastern section of the United States. Bentonitic clays are usually classed as activable and are prevalent in the southwestern section of the United States.l Bleaching clays vary considerably in chemical and physical properties throughout the country, or even in different parts of one deposit (Table 1). The fuller's earth type of clay is characterized by a lack of plasticity, relatively adsorbent, foliated structure, and does not swell to form a

Jan 1, 1942

By Paul Weir

Bleaching clays have been used extensively in the oil-refining industries for a number of years. Their use in water purification is relatively recent and less extensive. They are frequently classified as (1) those naturally active and (2) those active after artificial activation with acid. Fuller's earths fall within the general group of bleaching clays and gradually the commercial term "fuller's earth" has been applied to natural clays originating, for the most part, in the southeastern section of the United States. Bentonitic clays are usually classed as activable and are prevalent in the southwestern section of the United States.l Bleaching clays vary considerably in chemical and physical properties throughout the country, or even in different parts of one deposit (Table 1). The fuller's earth type of clay is characterized by a lack of plasticity, relatively adsorbent, foliated structure, and does not swell to form a

Jan 1, 1942

By James S. Browning

The Mineral Resources Institute and State Mine Experiment Station of the University of Alabama conducted Humphreys spiral tests on fine coal waste from nine preparation plants of Alabama strip mining operations to determine the feasibility of recovering low ash and sulfur fuel meeting steam coal specifications. The ash in the samples ranged from 9 - 5l%, and the total sulfur ranged from 0.4J- 2.39%. Continuous laboratory tests using a Humphreys spiral gave good recovery of the coal with excellent rejection of the ash and pyritic sulfur. Coal recoveries of 83.6 - 94.1% were achieved from the different samples. Ash content of the clean coal products fell within a range of 5 - 12.2%, with a total sulfur content of 0.62 and 1.10%. In quality, the products were comparable or superior to those now being shipped from the preparation plants.

Jan 1, 1980

By Clinton L. Miller

MINING operations have been carried on in the immediate area of the Elizabeth mine during periods of high copper prices since 1793, when copperas and vermillion were first won from the outcrop. Present operations started in 1942 as a war baby. Since then production has totaled 1.7 million tons of 1.8 pct Cu ore. Elizabeth mining operations are on a pyrrhotite- chalcopyrite orebody contained in a gently plunging amphibolite syncline. The oreshoot varies in width from 10 to 40 ft, and in the area under consideration is about 150 ft in vertical extent, and more than 1000 ft long. Surface pits or cuts have been worked in three areas along the outcrop, with one pit just completed and a second in full production. Present production is 24,000 tons per month, of which 6000 to 7000 tons is trucked from the open pit.

Jan 11, 1954

By J. L. Wyatt

THE strain sensitivity, K, a property of metals defined as the unit change in electrical resistance per unit strain, was measured for commercial purity titanium wire to determine its usefulness as a strain gage material. A Kelvin double bridge, accurate to 0.000001 ohm, was used to make measurements from 0 to 1 pct total strain. A positive value of 0.17 for K was found. This compares with 2.15 for constantan and 3.5 for cold-worked invar, two of the more common strain gage materials. The effect of temperature also was determined. It was found that a change in temperature of 30°F caused the same resistance change as 1 pct strain. It is therefore concluded that titanium would have utility as a strain gage only if the thermal fluctuations in the specimen could be controlled to a high degree and in applications of very large total strain.

Jan 1, 1953

By Garry M. Hughes

Sherritt's new, 3000 tpd, copper- zinc Fox mine is situated 30 miles southwest of Lynn Lake. The copper-zinc orebody is part of a large body of massive and semi-massive sulfides consisting chiefly of pyrite; with chalcopyrite, sphalerite (containing 7-9s Fe) and pyrrhotite in varying proportions which occur within a series of volcanic and sedimentary rocks. The average sulfide content is 67%. Higher zinc zones are masses of pyrite grains cemented by sphalerite with lower than average copper content. Zones higher in copper and lower in zinc are slightly more quartzose. Gold and silver are present in small amounts roughly proportional to the copper content. Surface diamond drilling indicated an orebody containing 12,269,000 tons grading 1.74% Cu and 2.35% Zn to the 2000 ft level. Underground drilling established the tonnage at 11,- 300,000 tons containing 1.96% Cu and 2.74% Zn.

Jan 4, 1972