By F. Keller

SOME PHRASEMAKER has aptly said that nature made aluminum light but research made it strong. Research has been a vital element in the past progress of the aluminum industry and its future growth likewise depends upon the application of the results of research. The role of aluminum products in World War II is well known and this metal will certainly be increasingly important in the postwar world. Some of the principal developments in the war years were in the field of high-strength aluminum alloys. New and stronger alloys were developed which enabled designers to get increased speed and performance in our fighter planes and bombers. The aircraft industry will continue to use these new materials for peacetime passenger and cargo airplanes. High-strength alloys will also find structural applications in trucks, buses, trains, ships, and bridges.

Jan 1, 1946

By AIME AIME

IT IS impossible in this short sketch to give a detailed description of each part of the plant at Bethlehem, therefore, only such facts will be touched on as are necessary to give a general idea of the works. The extent of the plant, and the fact that the units making up the various departments are located in different parts of the works, make it impracticable to mention the departments in any regular order with regard to their location. They are, therefore, mentioned approximately in the order of their relation to each other with reference to their functions in the making of the various products.

Jan 1, 1924

By E. B. BESSELIEVRE

THE great work of Gorgas in stamping out yellow fever in Panama during the construction of the Canal was one of the chief factors contributing to the ultimate accomplishment of the task, two previous attempts having failed largely through the demoralization of workers by epidemics of contagious diseases. Mining camps, rapidly constructed during the boom days of the rushes to new fields, have been frequent sufferers from typhoid when, as so often used to be the case, little or no attention was given to bacterial examination of the water supply or to the method used for disposing of the sewage.

Jan 1, 1930

By J. P. Hammond, C. J. Sparks, C. J. McHargue

IN a study of the effects of solid solution alloying on the deformation texture of titanium, an alloy containing 3.8 pct A1 was found to develop a (0001) [1010] texture instead of the texture characteristic of pure titanium.ls2 A short investigation has been made of the change in texture with aluminum content. Alloys containing 0.27, 0.47, 1.05, and 1.43 pct A1 were prepared by vacuum arc melting, using iodide titanium as the base material. Homogenized ingots were reduced 90 pct in thickness by cold rolling. Pole figures were obtained using the usual film techniques. Fig. 1 shows that the change from the tilted to the nontilted (0001) position is gradual. The dashed contour lines in Fig. 1 indicate the extent to which data was collected. The addition of 0.27 pct A1 resulted in a decrease in the transverse spread of basal poles. With increasing aluminum content, the amount of the tilt becomes less and the region of highest intensity takes the shape of a ring about the center of the pole figure. For aluminum contents greater than 1 pct, the (0001) [1010] texture is definitely present—the sharpness increasing as the amount of solute is increased.* It is interesting to note that Williams and Eppel-sheimer9 eported for commercial grade titanium a high intensity region 20" toward the rolling direction from the rolling plane normal in addition to. one 30" toward the transverse direction. Their basal pole figure was similar to Fig. 1, row inree. The observation that the texture changes gradually with solute concentration is similar to the results of similar studies on copper." At the present time these effects are not clearly understood. Acknowledgments This work was sponsored by the Aeronautical Research Laboratory (WCRRL), Wright Air Development Center, under Contract NO. AF' 33(038)-19574. The authors are grateful for the aid received and permission to publish these results.

Jan 1, 1958

By H. Rush Spedden, Arvid Thunaes

R. R. Knobler and F. E. Albertson—Following the testwork done by Thunaes and Spedden, a Sullivan deck plant was built for the Colquiri mill. This plant started to operate in April 1945 and continues in successful operation. Since May 1950 the Colquiri mill has operated with a completely revamped flowsheet at a rate of 1000 tons per day. The old Sullivan deck section was retained with this new flowsheet. The "slime plant" in Colquiri consists of one 12-cell Denver No. 18-Sp. Sub-A flotation machine, one 16-ft and one 12-ft hydroseparator, six five-deck Sullivan-frames and six shaking tables for cleaning up the Sullivan deck concentrates, as well as 12 Deister plus three Plat-O tables on which the fine sands, which are not treated on the S-decks, are concentrated. Only —325-mesh fines are treated on the Sullivan decks. The combined hydroseparator overflows are fed to the S-decks. From 1946 to 1949, i.e. with the "old" flowsheet and an average mill feed of 800 tons per day an average of 45 tons per day was treated on four Sullivan rougher frames. The two additional frames were used as cleaners. At times, up to 90 and 120 tons of slimes were treated successfully on this Sullivan deck installation. The average operating data for the S-deck section in Colquiri for the year 1949 were as follows: The tests reported in this paper indicated a tin recovery of 42 pct. The actual plant results for 1949 show a 54 pct tin recovery from the Sullivan decks. The total average quantity of tin produced from the S-deck section in 1949 was 15 tons of tin per month. This corresponds to 3 pct of the total mill recovery. The difference between the 6 pct overall recovery-increase expected after the tests in 1943 and the actual plant results given for 1949 is explained as follows. According to the tests, a total of 170 tons was expected to be routed to the Sullivan decks, but because of certain changes in the flowsheet and mill amplifications,

Jan 1, 1951

By H. Rush Spedden, Arvid Thunaes

R. R. Knobler and F. E. Albertson—Following the testwork done by Thunaes and Spedden, a Sullivan deck plant was built for the Colquiri mill. This plant started to operate in April 1945 and continues in successful operation. Since May 1950 the Colquiri mill has operated with a completely revamped flowsheet at a rate of 1000 tons per day. The old Sullivan deck section was retained with this new flowsheet. The "slime plant" in Colquiri consists of one 12-cell Denver No. 18-Sp. Sub-A flotation machine, one 16-ft and one 12-ft hydroseparator, six five-deck Sullivan-frames and six shaking tables for cleaning up the Sullivan deck concentrates, as well as 12 Deister plus three Plat-O tables on which the fine sands, which are not treated on the S-decks, are concentrated. Only —325-mesh fines are treated on the Sullivan decks. The combined hydroseparator overflows are fed to the S-decks. From 1946 to 1949, i.e. with the "old" flowsheet and an average mill feed of 800 tons per day an average of 45 tons per day was treated on four Sullivan rougher frames. The two additional frames were used as cleaners. At times, up to 90 and 120 tons of slimes were treated successfully on this Sullivan deck installation. The average operating data for the S-deck section in Colquiri for the year 1949 were as follows: The tests reported in this paper indicated a tin recovery of 42 pct. The actual plant results for 1949 show a 54 pct tin recovery from the Sullivan decks. The total average quantity of tin produced from the S-deck section in 1949 was 15 tons of tin per month. This corresponds to 3 pct of the total mill recovery. The difference between the 6 pct overall recovery-increase expected after the tests in 1943 and the actual plant results given for 1949 is explained as follows. According to the tests, a total of 170 tons was expected to be routed to the Sullivan decks, but because of certain changes in the flowsheet and mill amplifications,

Jan 1, 1951

By O. P. Dolph

SPANIARDS were probably the first to mine the rich surface ore in the veins cutting the rhyolite capping that outcrops on the hills of La Mazata, oil the Allyones side of the Magdalena valley in Jalisco, Mexico, although the name comes from a word of Indian origin meaning "deer". The camp is about 12 km. west of Magdalena, a town on the Southern Pacific Railroad, and about 17 km. north of Etzatlán, on the Mexican National Railroad, at an elevation of 4500 ft. The climate is subtropical with no extremes of heat or cold, the rainy season beginning in June and ending in October.

Jan 1, 1938

By Ovid W. Eshbach

ENGINEERING education has been powerfully affected by the impact of war, just how powerfully can be better understood after considering the postwar problems regarding students, staff, and plant. In time of war no one will question the necessity of expediency of military training. With the cessation of hostilities, expediency gives way to the evolutionary process of strengthening engineering education as need is exemplified by experience. During the war, except for the Navy V-12 program, engineering education was at its lowest ebb of the century. Freshman enrollments were largely limited to those graduating from high school at the age of seventeen; and the upperclass, to those disqualified for active service. In most schools the experienced staff was either in service or government and industrial research. Many may never return to their former occupations. The most immediate problem is that of maintaining and building a staff to meet the enrollment of returning veterans. It is estimated that out of the eleven

Jan 1, 1945

By H. M. Roche

MAGNETITE mining and milling in the Eastern States was sharply curtailed in 1938, production showing a decrease of 36 per cent from 1936 and 57 per cent from 1937. Six mines, one in Pennsylvania, two in New York, and three in New Jersey were in operation, either part or full time, during the year. In recent years ten Eastern magnetite mines have been more or less active but since the World War the market for Eastern ores- has been spotty. The scrapping of Eastern merchant pig iron furnaces, imports of cheaply mined duty-free foreign ore, and high freight cost have been contributing factors.

Jan 1, 1939

By G. K. Manning, A. R. Elsea, A. B. Westerman

A considerable number of high-tem-perature alloys, that is, alloys which have load-carrying ability at elevated temperatures, have been developed on an empirical basis. In order to determine why these alloys possess this particular ability, a project was started at Battelle Memorial Institute on the fundamental factors promoting high-temperature strength of alloys. .4t the time of inception of this study, the cobalt-base alloy, Vitallium, was widely used because of its good high-temperature properties. One phase of this study was to include an investigation of the structures observed in vitalliurn after various heat treatments. Howcver, before investigating the structural features of Vitallium, it appeared logical to examine the phase diagrams of the related binary systems in order to develop information as to which phases might be present in Vitallium. A preliminary survey of the pertinent alloy systems was made, with particular emphasis on the cobalt-chro-mium system, which is the base for the Vitallium series of alloys. The early work of Lewkonja and Guertler2 indicated that cobalt and chro-mium are completely miscible in the liquid state, and, within a narrow temperature range, in the solid state; that the liquidus shows a minimum; and that the alloys containing 45 to 85 pct chromium undergo a transformation at [zoo to 12 50 c More recently, Wever and Haschimoto,3 Wever andLange,4and Matsunaga5 carried Out experimental work which led to the diagrams shown in Fig I and 2. Both diagrams are based on thermal analysis, metallogra~hic, magnetic, and dilatation data; in addition, X ray diffraction results were used by Wever and Haschimoto, and electrical resistance measurements by Mat-SUnaRa. It is apparent from a comparison of the two diagrams that there was a difference of opinion as to the locations of the boundaries of the various phases, and as to the existence of a phase containing approximately 47 pct chromium. With these excep-tions noted, it might be pointed out that the two diagrams are similar, and that, in general, any particular reaction which is shown on both diagrams occurs at a lower temperature on the Matsunaga diagram than on that of Wever-Haschimoto-Lange. Thus, in view of the gaps in the data arid the questionable features in the published diagrams, it appeared desirable to start the fundamental study of Vitalhum by deter-mining the diagram for the cobalt-chro-mi~m system- Experimental Work For the convenience Of the reader, the diagram as determined by the present investigation is presented in Fig 3. The liquidus and solidus data for the low-chromium alloys were taken from the work of Wever and Haschimoto,3 while the melting point for pure chromium is the

Jan 1, 1949

By F. Keller, J. D. Edwards

The anodic treatment of aluminum presents problems of scientific as well as of commercial interest.l-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non-adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By F. Keller, J. D. Edwards

The anodic treatment of aluminum presents problems of scientific as well as of commercial interest.l-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non-adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By Robert I. Jaffee, Bruce W. Gonser, Eugene M. Smith

There has been little investigation of the gold-germanium binary alloys. Haughtonl does not mention any work on the system. In a review article commemorating the fiftieth anniversary of the discovery of germanium, E. Einecke2 mentioned a gold-germanium eutectic at 24 atomic per cent Ge (10.4 weight per cent) melting at 359°C., but did not give the source of his information. From measurements of electrical conductivity, J. 0. Linde3 estimated that at least 0.6 weight per cent germanium is soluble in gold. The recent availability of germanium in this country in commercial quantities has led to interest in its properties and its alloys. This study is part of a program of investigation on germanium alloys; work on ternary alloys involving germanium and gold will be reported later. In this investigation, the composition and melting point of the Au-Ge eutectic reported by Einecke has been found to be substantially correct. Eutectic composition has been placed at I2.0 per cent germanium, however. An alloy of 10.4 per cent Ge, Einecke's value, was found to have a few gold dendrites in it. The cutectic temperature has been determined as 356.0 6 ± 0.5°C., slightly less than the temperature of 359°C. reported by Einecke. The liquidus curves and the solid solubility of ger- manium in gold have been determined, and are shown in Fig. I. Materials and Alloying The germanium used in this investigation was prepared by the Eagle-Picher Lead Co. from pure germanium oxide, by reduction in clay crucibles with sodium cyanide. The regulus is quite pure, assaying over 99.9 per cent Ge. High-purity gold obtained from Handy and Harmon was used. Alloying was carried out in graphite crucibles in an atmosphere of purified hydrogen. The temperature was brought up to 1050" to iioo°C., and the metal was allowed to freeze in the crucible. Prepared in this way, the gold dendrites in hypoeutectic alloys were somewhat segregated at the bottom and sides of the ingot, and on the hyper-eutectic side the lighter primary germanium tended to gather at the top. Most of the alloys were made from virgin metal. Low-germanium heats were made by alloying pure gold with the eutectic. Melting losses were consistently a few milligrams or less, and the composition could safely be taken from the intended analysis. The 30 per cent and 50 per cent germanium heats for thermal analysis were made in part from remelted higher germanium heats, and they may be OR composition as much as one per cent. Because of the high cost of materials, the weight of heats for thermal analysis were 15 to 20 grams and heats for metallo-graphic, X-ray, and hardness specimens were 2 to 4 grams.

Jan 1, 1945

By C. E. Sims

The carbon-oxygen reaction without doubt is the basic reaction in steelmaking. It is important on several counts: In the first place, carbon is the element that distinguishes steel from iron. It is the principal element controlling properties, and its control is of prime concern. Although the principal objective of the carbon-oxygen reaction is to oxidize excess carbon, the accompanying boil should not be underrated. The mechanical agitation, stirring, and mixing resulting from the boil are so useful in the distribution of heat and in promoting uniformity of composition in the bath that, were it not a natural accompaniment of the carbon-oxygen reaction, it is probable that something would have to be invented to replace it. The open-hearth operation, for example, with the bath heated from above by radiation, would be impracticable without the carbon boil. The electric-arc furnace is somewhat less dependent on it, but every melter knows how much easier it is to gain temperature with minimum damage to refractories during the boil than with a dead bath The motor action of the induced current of the induction furnace makes the carbon boil unnecessary but even there a severe oxidation has been found useful in giving greater freedom from porosity in certain steels. The quantitative aspects of the carbon-oxygen reaction have been given considerable attention by a large number of investigators, and the principles of physical chemistry have played an important part in these studies. Physical chemistry is the science of the mechanics and mathematics of chemical reactions. It is possible to study the mechanisms of reactions in a qualitative manner writhout reference to mathematics and thus obtain valuable concepts as to the manner in which the wheels go around. When it is desired to express quantitative relations in these reactions, however, resort to mathematics is not only convenient but necessary. Mathematics may also be regarded as the shorthand language of physical chemistry. A basic relation whose description requires numerous words may be expressed very simply by a mathematical formula or equation. A good example of this is the equilibrium constant for a chemical reaction. Expressed verbally, it is: When a chemical reaction has reached a condition of equilibrium, the Product of the concentration of the reacting substances on one side of the equation, divided by the product of the concentration of the reacting substances on the other side, gives a quotient that is a constant at constant temperature For the carbon-oxygen reaction C + O ^ CO this is expressed simply as % C X % O -%co where K (from the German Konstant) is the equilibrium constant for the reaction. Although mathematics is such a necessary and useful tool, it is also a potential pitfall. Mathematics in itself is an abstract science, which is not inhibited by consideration of mechanisms or materials.

Jan 1, 1948

By C. E. Sims

The carbon-oxygen reaction without doubt is the basic reaction in steelmaking. It is important on several counts: In the first place, carbon is the element that distinguishes steel from iron. It is the principal element controlling properties, and its control is of prime concern. Although the principal objective of the carbon-oxygen reaction is to oxidize excess carbon, the accompanying boil should not be underrated. The mechanical agitation, stirring, and mixing resulting from the boil are so useful in the distribution of heat and in promoting uniformity of composition in the bath that, were it not a natural accompaniment of the carbon-oxygen reaction, it is probable that something would have to be invented to replace it. The open-hearth operation, for example, with the bath heated from above by radiation, would be impracticable without the carbon boil. The electric-arc furnace is somewhat less dependent on it, but every melter knows how much easier it is to gain temperature with minimum damage to refractories during the boil than with a dead bath The motor action of the induced current of the induction furnace makes the carbon boil unnecessary but even there a severe oxidation has been found useful in giving greater freedom from porosity in certain steels. The quantitative aspects of the carbon-oxygen reaction have been given considerable attention by a large number of investigators, and the principles of physical chemistry have played an important part in these studies. Physical chemistry is the science of the mechanics and mathematics of chemical reactions. It is possible to study the mechanisms of reactions in a qualitative manner writhout reference to mathematics and thus obtain valuable concepts as to the manner in which the wheels go around. When it is desired to express quantitative relations in these reactions, however, resort to mathematics is not only convenient but necessary. Mathematics may also be regarded as the shorthand language of physical chemistry. A basic relation whose description requires numerous words may be expressed very simply by a mathematical formula or equation. A good example of this is the equilibrium constant for a chemical reaction. Expressed verbally, it is: When a chemical reaction has reached a condition of equilibrium, the Product of the concentration of the reacting substances on one side of the equation, divided by the product of the concentration of the reacting substances on the other side, gives a quotient that is a constant at constant temperature For the carbon-oxygen reaction C + O ^ CO this is expressed simply as % C X % O -%co where K (from the German Konstant) is the equilibrium constant for the reaction. Although mathematics is such a necessary and useful tool, it is also a potential pitfall. Mathematics in itself is an abstract science, which is not inhibited by consideration of mechanisms or materials.

Jan 1, 1948

By Jack A. Kanz, Samuel R. Shortes, E. C. Wurst

Zinc diffusion into GaAs from the vapor phase through reactively sputtered SiO, films Izas been inrestigated for various zinc pressures at 1000"C. Diffusions were carried out in evacuated quartz ampules with elemental zinc and with various Zn-Ga alloys. Sputtered films have proved effective in lowering surface concentrations and preventing surface deterioration during diffusion. Approxin.ate complenzentary error-function impurity distributions were found when surface concentrations were reduced to approximately 3 -—4 x 10" atoms cm'3 or less with dilute zinc sources or by diffusion through SiO, films. Zinc difhsions in GaAs tlzrough SiO, films produced more planar diffusion fronts than were observed with uncoated zuafers under identical conditions. A) Surface Deterioration During Diffusion. Device technolorn-- in compound semiconductors has been hampered by several difficult problems not normally encountered with silicon and germanium. 111-V and 11-VI compound semiconductors generally have volatile constituents at temperatures used for diffusion. To achieve specific junction depths in reasonable lengths of time, or to obtain particular impurity distributions and doping levels, it is often necessary to use temperatures which cause surface deterioration and erosion of the wafer. The resultant surfaces are generally unsuitable for devices. The type and extent of surface damage depends to varying degrees on the particular environment of diffusion and on the particular impurity in question. The most common type of deterioration results from simple dissociation of the gallium and the arsenic during diffusin.' The deterioration process is significantly enhanced by thermal gradients in the diffusion zone, usually resulting in vapor transport and condensation at the cooler portion of the system. The resulting damage sometimes appears as a general haziness over the surface or an array of pyramidal etch pits characteristic of the particular orientation. Occasionally, erosion of the surface occurs uniformly over the wafer so that surface loss is not readily apparent. Workers in GaAs usually resort to the sealed-ampule type of diffusion system3"5 rather than the more conventional open system used for silicon and germanium. Another type of deterioration results from direct interaction of the impurity with the surface. The form of deterioration may vary from surface alloying, as in the case of zinc, to direct chemical attack and vapor transport of the reaction products, as in the case of sulfur. Surface alloying with zinc occurs at higher temperatures and source vapor pressures.4 The process is largely controlled by the amount of free gallium on the surface of the wafer in equilibrium with the arsenic lost to the system. The group-VI elements, sulfur, selenium, and tellurium, are commonly used donor impurities for gallium arsenide. These elements are characterized by high vapor pressures and high chemical

Jan 1, 1964

By Frank Foote, E. R. Jette

Precision lattice-constant measurements have been widely used in the study of cubic solid solutions but as yet have been rarely applied to noncubic solid solutions. (See, however, references I and 2.) With the high precision at present attainable in the measurement of lattice constants, the X-ray method should be readily applicable to noncubic solid solutions. In the work reported here, hexagonal close-packed magnesium was used as the solvent and either lead, bismuth or gold as the solute. In the magnesium-lead and magnesium-bismuth systems the a and c lattice constants were determined as a function of composition, densities were calculated from these lattice-constant data, these theoretical densities were compared with those directly measured and the solid solubility limit was determined on quenched specimens over a considerable range of temperature. In the magnesium-gold system, the solid solubility is very small but we have obtained an indirect check on the solubility limit previously reported. Materials and Preparation oF the Alloys The magnesium used was obtained from the Aluminum Company of America and was 99.987 per cent pure. Impurities as reported On the label were: Fe, Al, 0'004 per cent; Si, 0.009 per cent; Zn, trace; Cu, Pb, nil. The bismuth was Merck's analytical grade, minimum purity 99.95 per cent. Maximum impurities as listed on the label were: Fe, 0.008 per cent; Pb, 0.010 per cent; Ag, 0.010 per cent; Cu, 0.005 per cent; Sn, 0.003 per cent; Sb, 0.00; As, 0.000; S, 0.01 per cent. The gold was purified by double precipitation with sulphur dioxide. The lattice constants of these three metals have been previously reported.3 The lead used was test lead, silver free and with a maximum of 0.10 per cent heavy metal impurities. The lattice constant 01 this lead has been measured and found to be 4.94057 ± 0.00016 at 25°C. The alloys were prepared by melting together weighed amounts of the constituent metals in magnesia-lined alundum crucibles under an atmosphere of hydrogen purified by passing over magnesium heated to 500°C. The magnesia lining prevented contamination 01 the alloys with aluminum. Vacuum melting could not be used because of the volatility of magnesium. A high-frequency induction furnace was used for the melting operation and the stirring action of the current resulted in thorough mixing of the constituents. The melts were allowed to freeze in the crucible, the ingots obtained weighed about 10 grams. An extremely thin white film formed on the surface of the melts, sometimes covering only a part of the exposed surface. The ingots were filed clean, placed in small iror crucibles with close-fitting lids and indi. vidually sealed into Pyrex glass tubes Before sealing off, the tubes were alter

Jan 1, 1941

By Frank Foote, E. R. Jette

Precision lattice-constant measurements have been widely used in the study of cubic solid solutions but as yet have been rarely applied to noncubic solid solutions. (See, however, references I and 2.) With the high precision at present attainable in the measurement of lattice constants, the X-ray method should be readily applicable to noncubic solid solutions. In the work reported here, hexagonal close-packed magnesium was used as the solvent and either lead, bismuth or gold as the solute. In the magnesium-lead and magnesium-bismuth systems the a and c lattice constants were determined as a function of composition, densities were calculated from these lattice-constant data, these theoretical densities were compared with those directly measured and the solid solubility limit was determined on quenched specimens over a considerable range of temperature. In the magnesium-gold system, the solid solubility is very small but we have obtained an indirect check on the solubility limit previously reported. Materials and Preparation oF the Alloys The magnesium used was obtained from the Aluminum Company of America and was 99.987 per cent pure. Impurities as reported On the label were: Fe, Al, 0'004 per cent; Si, 0.009 per cent; Zn, trace; Cu, Pb, nil. The bismuth was Merck's analytical grade, minimum purity 99.95 per cent. Maximum impurities as listed on the label were: Fe, 0.008 per cent; Pb, 0.010 per cent; Ag, 0.010 per cent; Cu, 0.005 per cent; Sn, 0.003 per cent; Sb, 0.00; As, 0.000; S, 0.01 per cent. The gold was purified by double precipitation with sulphur dioxide. The lattice constants of these three metals have been previously reported.3 The lead used was test lead, silver free and with a maximum of 0.10 per cent heavy metal impurities. The lattice constant 01 this lead has been measured and found to be 4.94057 ± 0.00016 at 25°C. The alloys were prepared by melting together weighed amounts of the constituent metals in magnesia-lined alundum crucibles under an atmosphere of hydrogen purified by passing over magnesium heated to 500°C. The magnesia lining prevented contamination 01 the alloys with aluminum. Vacuum melting could not be used because of the volatility of magnesium. A high-frequency induction furnace was used for the melting operation and the stirring action of the current resulted in thorough mixing of the constituents. The melts were allowed to freeze in the crucible, the ingots obtained weighed about 10 grams. An extremely thin white film formed on the surface of the melts, sometimes covering only a part of the exposed surface. The ingots were filed clean, placed in small iror crucibles with close-fitting lids and indi. vidually sealed into Pyrex glass tubes Before sealing off, the tubes were alter

Jan 1, 1941

By C. F. Floe, N. J. Grant, A. Joukainen

A CCORDING to Guertler,¹ Smith and Hamilton were the first to study the Cu-Ti alloy system, but because of the presence of large amounts of impurities their data are inconclusive. Hensel and Larsen² in 1930 and Kroll³ in 1931 determined the high copper end of the diagram. In 1939 Laves and Wallbaum,4 in a short summary of compound determinations in titanium binary alloys, mentioned the existence of a face-centered cubic compound, Ti2Cu, with 96 atoms per unit cell, and also a compound, TiCu3, which was said to have a deformed hexagonal close-packed structure in which ordering had been observed. The existence of a compound, TiCu, was also found but the crystal structure was not determined. Craighead, Simmons, and Eastwood determined the effect of copper on the allotropic transformation in titanium. The investigation was limited to alloys containing from 0 to 5 pct Cu, using titanium of fairly high impurity content. Experimental Procedure The methods used for determination of the diagram included metallographic examination and X-ray and thermal analyses. The system was first worked out using the higher purity "Process A" sponge titanium and oxygen-free copper. The high titanium region was next determined more accurately using iodide titanium and vacuum-melted, oxygen-free copper. Preparation of Alloys: The alloys were prepared by arc melting under prepurified helium atmos- pheres in water-cooled copper crucibles. The high purity iodide titanium alloys were prepared by melting three compositions along with a specimen of unalloyed titanium in a single charge. A multiple crucible was used which consisted of a copper plate with four cup-like depressions. The unalloyed titanium was melted first and acted as a getter for any oxygen and nitrogen in the melting chamber. Since these elements harden titanium, the hardness of the standard specimen was an index of the highest probable contamination of the alloy melts. The sponge titanium alloy melts weighed from 100 to 200 g each and the iodide titanium melts from 20 to 25 g. In order to insure greater homogeneity most of the alloys were melted, turned, and remelted twice. The larger buttons made from sponge titanium were sectioned or crushed before remelting. These alloys up to 30 pct Cu were further homogenized by forging at 925°C. They forged readily up to 20 pct Cu but numerous cracks were formed in the alloys containing from 20 to 30 pct. Above 30 pct Cu the sponge titanium alloys were homogenized by heating for 200 hr at 850°C under prepurified helium. Similarly, the iodide-grade titanium alloys containing up to 3 pct Cu were homogenized at 1000°C for 24 hr and all others at 880°C for 200 hr.

Jan 1, 1953