By W. L. Phillips

Single crystals of aluminum, brass, and copper oriented for (100) and (110) slip were extended at 25°, 400°, and 600°C in simple shear. Aluminum specimens oriented for nonoctahedral slip began to shear at a higher critical resolved shear stress than specimens oriented for octahedral slip. Parabolic stress-strain curves were obtained from zero strain. The initial rate of parabolic hardening was lower for specimens sheared on the (100) plane in a close-packed direction <110>, than for specimens sheared in a nonclose-packed direction <100>. metallographic evidence, however, showed that all slip traces could be explained in terms of (111) <100> slip. All attempts to cause nonoctahedral slip in copper and 70-30 a-brass single crystals were unsuccessful. Instead of shearing, the crystals bent, allowing {111} type planes to come into action. NONOCTAHEDRAL slip in aluminum has been reported under three different conditions: first, as the main mode of slip in tension experiments at elevated temperatures;&apos;-&apos; second, as the main mode of slip in direct shear experiments at room temperat~re; and third, as a minor mode of deformation, i.e., as cross-slip, in tension, shear, and bicrystal experiments at room and elevated temperatures."-l2 However, as far as the author knows, nonoctahedral slip has not been reported in either copper or 70-30 a-brass. The present study was undertaken to determine whether nonoctahedral slip could be obtained in aluminum, brass, or copper at room or elevated temperatures when the shear stress was approximately constant over the cross-section, a maximum at the center, or a maximum at the surface. EXPERIMENTAL PROCEDURE A detailed description of the crystal preparation and shearing apparatus has been given previo~sly. Cylindrical crystals 1/2 in. in diam and 8 in. long were grown from the melt in a temperature-gradient furnace. The aluminum contained 0.001 pct Zn, 0.001 pct S, and 0.001 pct Fe; the 70-30 brass contained 0.015 pct Pb, 0.001 pct Fe, 0.01 pct Ni, 0.02 pct Sn, and 0.005 pct Se; the copper was certified OFHC of 99.98 pct purity. All samples were electropolished prior to testing. The shear apparatus was a modified Bausch type. The strain sensitivity was 4 x lob4 Load was applied by clamping the rods attached to the shear plates in an Instron tensile machine. The rate of loading was 0.02 in. per min. In all cases a 1/8-in. gage length was used. For the tests performed at 400° and 600°C the shear plates, collars, and rods were made of stainless steel. These elevated-temperature tests were performed in an argon atmosphere. A) Aluminum at Room Temperature. Values of a and ß for the various slip planes and slip directions investigated are shown in Table I where a is the complement of the angle between the specimen axis and the slip direction, and ß is the angle between the specimen axis and the normal to the shear plane. The shear stress is a function of a (assuming ß - 0);10 when a is less than 27 deg, the shear stress on the slip plane for which the specimen is oriented has a maximum at the center of the crystal; at a = 27 deg the shear stress is constant across the slip plane; for a greater than 27 deg the shear stress is a minimum at the center. Fig. 1 shows the stress-strain curves for specimens cut from crystals 1, 2, and 5, which were sheared on the (010) plane in the [loll direction at room temperature. These three crystals have shear-stress distributions corresponding to the three dif-

Jan 1, 1962

By N. K. Chen, R. Maddin

Columbium single crystals were deformed in tension and compression. Reorientation by X-rays and stereographic projections of slip traces indicate that plane of slip may be considered as (110). The plastic behavior is shown to be quite similar to the deformation of molybdenum single crystals. STUDIES on the crystallography of the deformation process in body-centered cubic metals have been renewed recently with investigations of iron single crystals1-" and molybdenum single crystals.4 It is now apparent that too many exceptions to the rationalization based upon the ratio of absolute testing temperature to absolute melting point by Andrade5 exist to permit more serious discussion of this type of analysis. The considerations of resolved shear stress utilizing only planes of the type {ll0}, {112), and {123)³,6 permit analysis of the deformation only on the basis of those three types of planes. The suggestions made by Elam7 and by Greninger8 in which the slip process is envisioned as a composite slip on two nonparallel {110) planes can be illustrated schematically in Fig. 1. It may be seen that an unresolved trace on any plane containing a <111> direction may be accomplished by varying the number of atoms participating in the composite process. By further varying the number of atoms in each plane but keeping the ratio of participating atoms constant, jogs could be obtained in the traces and hence wavy slip lines could be produced. Vogel and Brick&apos; studied the behavior of a iron single crystals in which they suggest that the plane of glide is "non-crystallographic" and may be predicted from the intersection between the great circle joining the slip direction and specimen axis with the great circle whose zone axis is the slip direction. In a more recent investigation on iron single crystals, Steijn and Brick" suggest that the slip mechanism may be considered as made up of a type of composite slip occurring on {110} and {112} planes. Evidence for a possible composite nature of the slip process has been presented for the case of molybdenum in the form of analysis of asterism and specimen axis rotation." Definite proof of a composite slip process must, however, await good electron microscopic resolution of the individual traces making up the unresolved optical trace used in determining the acting slip plane. The present investigation was undertaken to study the behavior of columbium single crystals not only in tension but also in compression since the specimen axis migration should indicate the plane or planes of glide in the same manner that the specimen axis migration in tension indicates the direction of glide. The orientations of eleven crystals investigated are shown in Fig. 2. Specific orientations are missing (those in the vicinity of [Ill] and [001] and consequently the effect of orientation on the crystallography of deformation could not be considered. Experimental Procedure The 1/8 in. rods (7 in. long) were subjected to an axial tension in vacuo while at temperatures in the vicinity of 2000°C for 2 to 4 hr. This treatment resulted in large cylindrical grains (about ½ in. long) occupying the entire cross section. A number of these rods were used for the tension studies by observing the behavior of the individual grains. For the compression studies, single crystals approximately % in. long by 1/8 in. in diameter were cut from the rods; the ends were ground parallel. All specimens were polished electrolytically in a solution of 15 cc HF(48 pct) and 85 cc H2SO4 (concentrated) using a platinum cathode, a current density of 0.04 amp per sq cm and a temperature between 25" and 60°C.10 Orientations were obtained using a Laue back-reflection method (3 cm film to specimen distance) with a ½ mm collimator 9 cm long. For the compression specimens, a reference mark was scratched on one of the compression sur-

Jan 1, 1954

By R. E. Reed-Hill, W. H. Hartt, W. A. Slippy

An unusual form of double kinking has been observed at the ends of {1121} twins in deformed zirconium. These kinks lie partly outside of the twin and partly inside. While they are undoubtedly closely associated with accommodating the twinning shear into the matrix, they are apparently closely related to other important aspects of twin growth. A mechanism is proposed for {1121} twin growth involving interactions between 1/3 (1120) dislocations in the bend planes and twinning dislocations. It is also shown that boundaries without long range strain fields develop at the tapered ends of the twins. The {1121} twins can, therefore, grow without forming high-energy noncoherent twin boundaries containing large numbers of closely spaced twinning dislocations. NUMEROUS investigators have indicated that slip is often closely associated with deformation twinning. An example is twin accommodation kinking,1-3 where dislocations form bend planes and permit accommodation of a twinning shear within the parent crystal. Another is the incorporation of slip dislocations into twins, as proposed by Sleeswyk and verbraak4 and Ishii and Kiho5 for iron and ß-tin, respectively, and observed in hcp metals by Price.6 In addition, it has been shown that shear discontinuities exist at the points of twin intersections in zinc,7 magnesium,8 titanium,9 ß-tin,10 and bismuth," where the continuity conditions for twin intersections, originally proposed by cahn,12 are not satisfied. A similar situation occurs for zig-zag (1121) twins in zirconium13 and ?-phase silver-aluminum alloys,14 where the twinning shears of the two component twins are not parallel. In all these latter cases additional deformation by slip is believed to accommodate the twinning shear discontinuity. The present paper is concerned with a newly observed aspect of the slip and twinning interrelation, in which two kinks, one inside the twin and the other external to the twin, are formed. These kinks, observed in conjunction with (1121) twinning in zirconium, form to accommodate the twinning shear. A model has been constructed explaining the growth and accommodation of (1121) twins in terms of these kinks. This mechanism may be significant since it is concerned with an important twin mode, which occurs not only in zirconium but also in titanium and hafnium. The practical significance of (1121) twinning has been adequately demonstrated. At 77° K the high ductility of zirconium containing a large number of grains unfavorably oriented for slip is primarily due to (1121) twinning.&apos;5 Also, (1121) twins nucleated at 77°K may grow during further deformation at room temperature. This growth can greatly increase the transverse ductility15 as well as produce large mechanical hysteresis effects.= EXPERIMENTAL PROCEDURE Arc-melted, sponge zirconium plate previously described17 was prestrained 0.65 pct at 77° K by cold-rolling to introduce {1121} twins into the structure. Tensile specimens were cut with axes normal to the plate rolling direction. These specimens were pulled in tension to near the point of failure in an Instron machine at room temperature at a cross-head speed of 2 x10-2 in. per min. This additional deformation caused growth of the twins nucleated by prestrain. Deformed specimens were then prepared for metallo-graphic examination. This included an anodizing treatment18 that made the surfaces sensitive to polarized light, permitting small lattice rotations to be revealed. EXPERIMENTAL RESULTS Nature of the Twin-Kink Band Structure. Fig. 1 is a photomicrograph of a typical specimen after prestrain at 77° K. The structure is characterized primarily by long, narrow, parallel sided (1121) twins which norma1ly traverse the entire grain. Fig. 2 shows several (1121) twins after additional straining at room temperature. These lie near the center of the polarized light photomicrograph and are inclined upward to the right. It is evident that this latter deformation has resulted in appreciable twin growth. The dark regions extending from the ends of these twins are accommodation kinks. The difference in reflected light intensity indicates the

Jan 1, 1969

By Gordon W. Hodgson, Edward Tipman

INT&apos;RODUCTION An appreciable number of the oil fields in Western Canada are accumulations of heavy black oils in more or less unconsolidated sandstones. When the crude oils are produced by conventional means, they are frequently contaminated with both sand and oilfield water. The water is usually present as emulsified water, and the sand and other solid materials are suspended in the emulsions. The presence of the solid material in the crude oils is troublesome and, in general, little is known about the behavior of suspended solid particles in emulsions. The Stokes equation describes the behavior of suspended particles in homogeneous fluids in terms of particle size, density differential, and fluid viscosity. In the case of an emulsion, particle size and density differential introduce no difficulties, but considerable doubt centers around the viscosity term. It has been reported1 that the viscosity of an emulsion is related to the viscosity of the continuous phase by an expression of the type: n = a, (1 + a C) where n is the viscosity of the emulsion, n,, is the viscosity of the continuous phase, a is a constant, C&apos; is the volume concentration of the disperse phase. The value of 17, the coefficient of the concentration term, has been determined for various systems, and has been found to vary from a value of 1 to 4.75. The value of 2.5 has been found to be applicable to a large number of systems, and this is the value that is widely used in the equation which then becomes the Einstein equation for the viscosity of emuls~ons. It is of considerable significance that neither the particle size nor the viscosity of the disperse phase enters the expression; the expression for the viscosity of the enlulsion is based solely upon the viscosity of the continuous phase and the concentration of the disperse phase. For crude oil emulsions the Simha equation and the data presented by Fukushima and lchimurai show a non-linear dependence of the viscosity ratio on the water concentration. While it is undoubtedly reasonable to use these data for predicting the viscosity of a specific emulsion, and while it is equally reasonable to expect the calculated viscosity to predict the settling rate of a solid spherical particle in the emulsion by means of Stokes equation, there seems to be no direct evidence that this calculation is indeed sound for describing the settling rates of solid particles in emulsions of water in crude oils. PROCEDURE A direct approach to the problem was thus indicated. Laboratory equipment was designed and built for the direct determination of the rate-of-fall characteristics of solid particles in emulsions of water in oil. Although the apparatus incorporated the basic design of conventional falling-ball viscometers, the study was concerned directly with the rate-of-fall characteristics of particles in emulsions, rather than with the viscosity of the emulsions as such. The crude oil used in this study was a very heavy black crude oil—the McMurray oil obtained from oil-soaked sands outcropping on the Athabasca River in northeastern Alberta. It was produced from the sands by strip mining followed by hot-water separation of the oil in the separation plant of the Alberta Government at Bitumount&apos;. The primary plant product was a wet crude oil containing about 5 per cent solids and 35 per cent water. The final plant product was only slightly different from the native oil, having lost only about 4 per cent of its bulk as light ends during dehydration distillations. In the present investigation two kerosene dilutions of the McMurray oil were used in addition to the dry plant product. The McMurray oil contained 1.92 per cent solids. Analysis of the solids by X-ray diffraction showed the presence of kaolinite, pyrite, and illite as major constituents. with lesser amounts of quartz. Particle size of the pyrite and quartz was less than 10

Jan 1, 1957

By AIME AIME

AN unusually interesting meeting devoted to the discussion of the ways and means of improving coal mining practice, through the larger use of machinery underground, was held in the Auditorium of the Engineering Societies Building on March 11. The meeting was organized by the Materials Handling Division of the A. S. M. E. and held under the auspices of the Metropolitan Section of that Society and the National Coal Association. The New York Section of the A. I. M. E., which had been invited to participate, found itself unable to do so formally because of a conflicting date for its March meeting but informally did its part to aasure the success of the meeting. As a result of the discussion at and preceding the meeting, the National Coal Association, through Walter Barnum, chairman of its research committee, has asked the A. S. M. E. and A. I. M. E. to join the Association in a study of the present problems of the bituminous coal industry. Messrs. Harry L. Gandy, Calvin W. Rice and H. Foster Bain have been selected to act as a committee which shall develop plans for a joint program.

Jan 1, 1926

By T. A. Rickard

The notion prevails that writing is a knack, that the skilful use of the pen is a gift of nature. This is an error. Dogberry may be responsible for it; he said: "To be a well-informed man is the gift of fortune, but to write and read comes by nature". Because Dogberry said it, we may be sure that Shakespeare thought otherwise. Ability of any sort may be partly innate, but my own observation and experience lead me to conclude that most of the easy writers have become so by constant practice. As I recall the names of men successful with the pen, I remember that most of them have written a great deal and have taken particular pains to improve their style. The suggestion that proficiency in the difficult art is a happy accident provokes a sardonic smile. The larger part of the great writing in our literature is the result of persistent effort. An easy fluency has been the undoing of many; their flamboyant and fantastic scribbling has proved as perishable as froth. This criticism applies to technical writing also; in order that a technical description or discussion may hold the interest of the reader, at least long enough to cause him to read it to the end, the writing must be done carefully and systematically; otherwise it will fail in its purpose of conveying information. Clearness is absolutely essential. "It is not enough to use language that may be understood; it is necessary to use language that must be understood."* The purpose of writing, at least of that which is meant to be read by others, is not only to express ideas but to communicate them. Lack of perspicuity may prove as %ad as

Jan 1, 1931

By J. K. Buehler

With the rapid acceleration of the cost of shovel dippers and major standard shovel clipper rebuild components, maintenance management at Kennecott Copper Corp.&apos;s Bingham Canyon mine initiated a dipper maintenance and rebuild program. The program focused on extending the service life of the shovel dipper, reducing field labor in maintaining dippers, and lowering shovel dipper rebuild costs. While comprehensive evaluation of the program is still underway, preliminary benefits of the program indicate: •Reduced field ,gelding for shovel dipper field maintenance, •Fewer dipper rebuild units entering the shop, and •Reduced dipper rebuild costs per unit.

Jan 1, 1979

By J. E. Andersen, J. Halpern, C. S. Samis

In the presence of oxygen, galena is oxidized in an aqueous medium containing sodium hydroxide, in accordance with the following reaction: PbS + 2O2 + 3OH ? HPbO2 + SO4 = + H2O A novel method was devised for following this reaction which takes place in an autoclave under oxygen pressure, by measuring the concentration of HPbO2- in the solution with a cathode ray polarograph employing stationary platinum electrodes. Using this procedure a study was made of the kinetics of the reaction, in which the effect of a number of variables, including temperature, oxygen pressure, NaOH concentration, and agitation, on the rate, were determined. The results of this study are described and discussed, in terms of possible mechanisms for the reaction. IT is known that sulphide minerals can be oxidized in aqueous media in the presence of oxygen under pressure. Reactions of this type can be classified in two categories depending upon whether the products of oxidation are insoluble or soluble in the aqueous medium. An example of the first type of reaction is the oxidation of pyrite in alkaline solutions, giving rise to an insoluble iron oxide. The kinetics of this reaction have been investigated and its mechanism established.&apos; It has been applied in the oxidation of iron sulphides present in refractory gold ores to improve the subsequent recovery of gold by cyanida-tion.&apos; The second type of reaction finds application where it is desired to recover the metal by leaching during oxidation. In this case a medium is selected in which the oxidized mineral is soluble. For example, nickel, copper, and cobalt sulphide ores can be treated by oxidation in the presence of a solution of ammonia dissolving the nickel, copper, and cobalt as the metal ammine sulphate salts.:&apos; A similar treatment has also been reported to apply to zinc sulphide ores.&apos; It is known that lead sulphate is soluble in solutions of sodium hydroxide or ammonium acetate. It should therefore be possible to dissolve the lead from galena ores by aqueous oxidation with oxygen under pressure using either of these solutions. The applicability of the ammonium acetate treatment has been investigated and confirmed in a recent study.&apos; The present paper describes the results of a similar study in which the kinetics of the oxidation of galena in sodium hydroxide solutions have been investigated. The object of this investigation was pri- marily to obtain information of a fundamental nature relating to the kinetics and mechanism of this reaction. The use of pulps of comminuted ore in a study of this type is undesirable because of the difficulty in controlling and measuring the surface area. The measurements were therefore made using galena crystals of measured surface area and in this way absolute reaction rates were obtained. The reaction was found to proceed as follows: PbS + 2O2 + 3OH ? HPbO2 + SO4 + H2O [I] The products are sodium plumbite and sodium sulphate salts which dissolve in the aqueous solution. The reaction studies were carried out in an autoclave in which a desired pressure of oxygen was maintained. The reaction was followed by measuring the concentration of lead in the solution with a cathode ray polarograph. The results obtained in this investigation are presented and discussed in the present paper. Experimental Materials: The crystals of galena were obtained from Violamac Mines, Sandon, B. C. The following impurities were indicated by spectrographic analysis carried out by the Provincial Assay Office, Victoria, B. C.: Sn, 0.02 to 0.2 pct; Sb, 0.07 to 0.7; Zn, 0.01 to 0.1; Si, Fe, Mg, As, less than 0.05 pct; Ag, 126 oz per ton, the latter determined by standard fire-assaying procedure. After cutting a specimen measuring approximately 5x7x12 mm, the crystal surfaces were ground parallel to the 100 axes using No. 2 emery, washed with water, and the dimensions were measured with a micrometer. Oxygen gas was of commercial grade and supplied in cylinders by Canadian Liquid Air. Solutions were made up with chemicals of chemically pure grade and distilled water. Equipment: Autoclave: The autoclave used in these studies was constructed of stainless steel and

Jan 1, 1954

By L. L. Handy

The development of a theory for miscible liquid displacement requires evaluation of the variables which affect growth of the mixing zone between solvent and displaced oil. Factors which appear to be important are individual fluid viscosities, viscosity ratios, flood rate, fluid densities, flow characteristics of the porous medium and molecular diffusion coefficients of the fluid components. The primary purpose of this paper is to evaluate diffusion effects. Theoretical treatments to date have been limited to floods for which the viscosity ratio is one. Two principal theories have been proposed. Von Rosenberg adapted for porous media a theory derived for capillary tubes by G. Taylor.&apos; ,&apos; In this theory molecular diffusion perpendicular to the direction of flow is a primary factor in sharpening the flood front. Slow floods give sharper fronts for a given distance traveled than fast floods. An alternative theory considers miscible liquid displacement as a statistical problem.3,4,5 Diffusion is not an important factor in this theory, but it leads to the same general type of equation as von Rosenberg&apos;s. Both theories predict S-shaped concentration profiles with the same dependence on distance traveled. The statistical or "dispersion" theory predicts rate independence, however. To supplement rate studies a direct measurement of a diffusion effect would be helpful in evaluating which of the two proposed mechanisms best describes miscible liquid displacement for one-to-one viscosity ratio systems. No quantitative theory has been proposed for floods in which a low-viscosity fluid displaces a high-viscosity fluid. It might be anticipated, however, that the extensive fingering observed in floods with adverse viscosity ratios would increase opportunities for an exchange of components between displaced and displacing liquids by a diffusional process. Even if molecular diffusion were not an important mixing mechanism for one-to-one viscosity ratio systems, it could be significant in systems with adverse viscosity ratios. METHOD FOR EVALUATING DIFFUSIONAL MIXING In solvent flooding the displacing liquid can become mixed with the displaced liquid by a number of processes; in general, either mechanical or diffusional in character. To evaluate the contribution of diffusion, a method was sought that would distinguish diffusional mixing from mechanical mixing. Suppose two soluble tracers are added to the displacing liquid and that one tracer has a diffusion coefficient much greater than the other. Then, if diffusion is important during miscible liquid displacement and if diffusional transport is primarily transverse to the direction of flow, substances with high diffusion coefficients will have sharper concentration profiles than those with comparatively low molecular diffusion coefficients. In order to have material balance the profiles for the two tracers must intersect. For one-to-one viscosity ratios the intersection would occur at the 50 per cent concentration point. It is generally assumed that diffusion in the direction of flow is negligible. This assumption appears reasonable because flow velocities are ordinarily orders of magnitude greater than diffusional velocities. If this is not a valid assumption, however, the shapes of the fronts will be further degraded by longitudinal diffusion. The effects of rate and molecular diffusion coefficients are the opposite for longitudinal diffusion to those for lateral diffusion. Higher rates or lower diffusion coefficients would tend to give sharper fronts. The double tracer method offers several unique advantages in evaluating effect of molecular diffusion. First, the method gives a direct measure of the effect of diffusion on mixing zone size. Second, the effect of a difference in diffusion coefficients is determined from a single experiment. Comparison of several experiments at different rates is not required. Third, the method is applicable for any viscosity ratio. Fourth, the method is unaffected by density differences between the two fluids which might result in rate dependent gravity effects. EXPERIMENTAL PROCEDURE Suitable tracers are substances whose diffusion coefficients differ as widely as possible, but whose adsorptions on rock surfaces is negligible. The two tracers selected were methanol and sucrose in water solutions. The approximate diffusion coefficients for methanol and sucrose, as given in the International Critical Tables, are 1.3 X 10-5 and 0.3 X 10-5 m2/sec, respectively. Concentrations in the water solutions were 200 gm/liter of solution for both methanol and sucrose. These high

By M. R. Tek

A new method for correlating the data on multiphase flow through vertical pipe is presented. The correlation is based on a "two-phase f factor" concept which was developed and successfully applied to horizontal multiphase flow by Bertuzzi, Tek and Poettmann. Field data previously published on several flowing and gas-lift wells have been used as the basis for the developed correlation. The application of the method to actual two-phase flow problems indicate that this method is capable of predicting the pressure distribution in vertical multiphase flow strings well within the accuracy range usually desired for common engineering and design calculations. A new working chart developed for calculation of two-phase pressure gradients and a graphical step-by-step procedure for the computation of pressure distribution are presented along with an example problem. INTRODUCTION Multiphase flow through vertical pipe is encountered in many engineering installations. In petroleum, chemical process, nuclear engineering and many other industries, problems associated with simultaneous flow of two or more phases through vertical pipe have been of interest for a long time. This interest has increased considerably during recent years due to applications to new processes in petroleum production and refining and to problems of steam generation and heat removal from nuclear reactors. One prominent example of vertical two-phase flow is provided by the gas-lift process where oil, water and gas flow simultaneously. If the pressure profile in a gas-lift well can be predicted within reasonable accuracy, it would be possible to get good estimates of the power required to lift the oil, the optimum depth, the pressure and the rate at which to inject gas. Furthermore, the effect of production rate and tubing sizes on these quantities can be evaluated before any design decision is made on the installation and operation of the flow string. The majority of experimental work available in the literature deals with two-component systems where individual phase flow rates in and out of the pipe remain constant. The general problem of prediction of pressure drops in multiphase flow systems is very complicated. The co-existence of numerous flow patterns of widely different geometry and mechanism, conditions of surface instability and the nature of force fields acting upon the system are among the major difficulties commonly encountered. The classical approach of fluid dynamics which would be based upon the formulation and solution of Navier-Stokes equations has been found by many investigators completely devoid of any hope of success-—not only because of inherent nonlinearities but also because of insurmountable analytical difficulties standirng in the way of setting up the boundary conditions. The presence and effect of interfacial forces on mu1tiphase flow systems further complicate the theoretical approach. For these reasons, many investigators choose to adopt semi-empirical if not purely empirical approaches in order to obtain solutions of engineering utility. A prominent practical solution has been given by Poettmann and Carpenter&apos; in the form of an empirical correlation. In their paper, total flowing densities of fluids and solubility effects of gas in oil have been taken into account for the correlation of field data covering a wide range of operating conditions for oil wells. They treated the gas. oil and water as a single phase of combined propcrties and correlated the multiphase friction factor as a function of the product (pvd), i.e., density X velocity X diameter of the flow string. However, because the product (pvd) is dimensional while the frictior factor is dimensionless, the generality of their result&apos;s is somewhat restricted. It seems that the omission 01 viscosity effect may be one of the reasons for the scatter of data as shown in their correlation chart. The concepts of the "two-phase f factor" and the "two-phase Reynolds&apos; number function" were recently developed and successfully applied to correlate horizontal multphase flow by Bertuzzi, Tek and Poettmann.&apos; Recently, two new methods of correlation by Tek and Chan&apos; have been presented on simultaneous flow of liquid and gas through vertical pipe. These two methods of correlation and the working equations in field units necessary for their application are included in this paper. The extension of the conccpt of two-phasc Reynolds&apos; number function successfully developed for horizontal flow into vertical multiphase flow systems, development and evaluation of working charts permitting calculation of two-phase pressure gradients and

By H. A. Hoffman

Competition from an all-flotation plant, with demonstrated economies and efficiencies, plus a change in smelting contract and introduction of improved cyclones lead to conversion from gravity-flotation. Detailed descriptions are given of equipment installed and procedures used at St. Joseph Lead&apos;s Federal mill. Future plans include further quality control by instrumentation in all aspects of the mill operation. Also planned are improvements in materials handling systems. Competitive conditions will continue to dictate improvements and changes in the mill flowsheet. The advent of all-flotation mills in the Lead Belt was introduced by the Indian Creek mill in late 1953. This modern and efficient plant then became a pattern for the other mills in this area to re-evaluate their circuits in an effort to develop flowsheets that would improve operating conditions and metallurgy. The Indian Creek mill demonstrated that all-flotation would require considerably less operating and maintenance labor than the combination of tabling and flotation that was common in the Lead Belt at that time. Two significant changes occurred in recent years to allow all-flotation to be seriously considered in other Lead Belt mills. One was a change in the smelting contract which did not require gravity concentrate. Another was the development of cyclones which provided classification of the flotation feed in a very small space. Since the Federal mill was the largest concentrating plant in the Lead Belt it was felt that the greatest savings could be made by investigating the all-flotation possibilities at this mill. Interest was stimulated by the milling and ore dressing Depts. to determine if this mill would be converted without undue cost, provided the metallurgy could be improved. Accordingly, laboratory tests were initiated to learn what metallurgical benefit could be derived. Numerous tests were run which indicated that grinding to all-flotation would improve the tailing by as much as 0.02 pct Pb. This was quite significant when multiplied by the tonnage of ore treated. Projecting the added cost of power for extra grinding and flotation, and the additional flotation reagents required, plus additional new equipment that would have to be purchased, it would still add up to a considerable saving. The all-flotation mill would reduce man power by some 30 pct, and make a metallurgical improvement. Operating costs could be reduced bv 2$ per ton. The metallurgical improvement would amount to 4$ per ton, for a total of 6$ per ton of ore milled. An estimate of the cost of the conversion was set at $250,000. With the savings as estimated this could be paid off in about two years. On paper it therefore seemed attractive enough to justify a mill test. MILL TESTING One section of the Federal mill was made available for use as a separate test circuit. Cyclones and density controllers were borrowed from the Viburnum and Indian Creek mills. Denver flotation cells were obtained from the Desloge mill that was then shut down. Two 10-cell groups of Fagergren flotation machines, consisting of eight roughers and two cleaners in each bank, were segregated from the remainder of the plant. The 9x12-ft rod mill was continued as a primary grinding mill. The two 6%x12-ft mills on this section were converted from rods to balls, and the speed increased to 22.0 rpm. Cyclones were installed to close the circuit of these ball mills. The ground pulp from each of the ball mills was fed separately to its own bank of flotation cells so that two completely separated test circuits could be run in parallel. This test circuit operated on a three-shift basis from Dec. 22, 1959 to Mar. 21, 1960. The first few weeks were occupied in developing conditions for proper metallurgy and trouble-free operations. Results were rather erratic but as the ore dressing laboratory and the mill operators became more familiar with conditions they were able to obtain expected results, which could be duplicated day after day. The last five weeks of testing indicated the best results and are tabulated in Table I. During the first two weeks a Denver unit cell was used on No. 1 flotation circuit. Even though it recovered almost one half of

Jan 1, 1962

By P. Somasundaran, D. W. Fuerstenau

The length of the collector is found to influence the flotation of the mineral even at incipient conditions, which are below the concentration at which interaction at the solid-liquid interface begins to take place to form hemi-micelles. To study this dependence, concentration for incipient flotation of quartz was determined as a function of pH with collectors of various chain lengths. The observed effect of chain length on flotation is ascribed to that of collector adsorbed on the bubble surface. In previous studies, it was shown that at low concentrations the alkyl collector ions adsorb at the solid-liquid interface as individuals.&apos;&apos;2 At higher concentrations, the collector ions adsorbed at the solid-liquid interface associate with each other to form two-dimensional aggregates called hemi-micelles. Above the hemi-micelle concentration, the length of the hydrocarbon chain is extremely important since the hydrocarbons are in effect removed from water during the association, making the energetic conditions more favorable for adsorption at the interface. Because of this enhanced adsorption, one observes a very rapid increase in flotation associated with the hemi-micelle formation at the solid-liquid interface. However, a dependence of flotation on the chain length at concentrations below that required for hemi-micelle association was also observed,&apos; and this cannot be explained by the above mechanism which postulated hydrocarbon chain interactions only at the solid-liquid interface. This prompted an investigation into other possible reactions of the hydrocarbon chains and an examination of the conditions at the bubble surface involved in the flotation system and how these observations might explain the reactions at the solid-gas interface which cause the particle-bubble attachment required for flotation. To obtain more information on chain length effects, flotation, under incipient conditions, was tested by vacuum flotation techniques. The collector-concen-tration-pH relationships for flotation of quartz with alkyl ammonium acetate collectors was delineated by observing the pH at which quartz particles begin to float to the liquid surface. By investigating flotation as a function of pH, it was also possible to study the effect of neutral molecules on incipient flotation conditions, since the aminium ions hydrolyze to amine molecules at higher pH values. EXPERIMENTAL WORK Brazilian quartz specimens were crushed and sized, and the 270 x 400 mesh fraction was used for flotation studies. The samples were leached with concentrated hydrochloric acid until no coloration of the acid occurred. The leached material was washed free of chloride ions and stored in distilled water. The vacuum flotation technique developed by Schuhmann and prakash3 was used to determine the critical pH-concentration curves. This method, which can be used to delineate conditions for incipient flotation, is fairly simple and rapid. About 0.5 gm of 270 x 400 mesh quartz was placed in a 100 ml graduated cylinder which was then filled to the 100 ml mark with the collector solution made from high-purity alkyl ammonium acetate salts. The water used for the test was conductivity water saturated with air that had been passed through a cleansing train consisting of Drierite, Ascarite, a water wash bottle, and a trap. After the pH was adjusted, the cylinder was then conditioned for thirty minutes. In the tests where an acid pH was desired, sufficient acid was added before the collector solution to avoid any effect due to slow desorption of collector from the quartz surface. After conditioning, vacuum was applied to the system and the flotation or nonflotation of the quartz was noted. The pH at which the quartz particles began to float to the liquid-gas interface was taken as the critical PH. Critical pH curves were thus determined for different concentrations of the various collectors. Hallimond tube flotation data were taken from the authors&apos; previous publication1 for correlation with that from the vacuum flotation. RESULTS AND DISCUSSION The results of vacuum flotation studies for determining critical pH-concentration curves, i.e., curves which delineate conditions for incipient flotation, are shown in Fig. I. In generaI, all the curves exhibit an upper and lower pH limit between which flotation will

Jan 1, 1969

By S. C. Hollister

An evaluation of the function of the engineer, so that means whereby education can best serve his needs can be adopted.

Jan 2, 1950

By C. Law McCabe, R. G. Hudson

The Knudsen cell has been employed to determine the free energy of formation of Mn7Cs in the temperature range 800" to 950°C. A value of 66,440 cal was found for hH°o for a-manganese. Measurements of the pressure of manganese over a mixed carbide, (Fe,Mn),C, points to a power relationship between aun7cs and N.4,. RECENTLY Kuo and Perssonl have reported that the carbide of manganese which is in equilibrium with graphite at temperatures up to 1100° C is Mn7Ca. There are no published data on the thermo-dynamic properties of this compound. In order to determine the stability of Mn7Ca, it appeared that, by obtaining the pressure of manganese above 8-manganese and also above Mn,C, in equilibrium with graphite, the free energy of formation of Mn7Ca from 8-manganese and graphite could be obtained. In addition, the vapor pressure of manganese, reported by Kelley From data of Bauer and Brunner,&apos; is subject to some uncertainty and further determinations of the vapor pressure of manganese seemed warranted. In this investigation of the pressure of manganese vapor above pure manganese and also above the carbide of manganese in equilibrium with graphite the apparatus used is the Knudsen orifice cell. The same apparatus, experimental procedure, and method of calculating the pressure was used in this investigation as in one previously reported.~ Care was taken to insure that the cells were at constant weight before using them in a run. The manganese charged in the cell was CP grade powder, carbon free, obtained from the Fisher Scientific Co. A spectroscopic analysis of the manganese after appreciable amounts of it had vaporized from the Knudsen cell showed that no element was present in sufficient quantities to contribute to a weighable weight loss or to decrease the vapor pressure of manganese to any appreciable extent. The spectro-graphic analysis was 0.002 pct Cu, 0.05 pct Fe, 0.002 pct Pb, and 0.002 pct Ni. 8-manganesea is the allo-tropic form of manganese which was present in the cell at temperatures used in this investigation. The manganese carbide, Mn,Ca, was made in the following way: In a closed graphite cell manganese powder was added to graphite powder, which was made from graphite rods for spectrographic use. The manganese powder was the same as that described previously; 5 pct excess graphite was added over that required for the formation of Mn7C,. The mixture was heated in a closed graphite cell for approximately 20 hr at 1350°K under vacuum. X-ray analysis revealed that there was no manganese present after this treatment, but that the lines due to Mn,C, were present. In order to prove that there was no volatile carbide of manganese which was effusing out of the cell, the following experiment was performed: A graphite effusion cell containing graphite power, in excess of that to form Mn,C, of a desired amount, was brought to constant weight on heating at 1228°K. The required amount of manganese was accurately weighed and then added to the graphite effusion cell. The cell was placed in a vacuum at 1228°K for one week, which was the time calculated for the manganese to have effused completely, assuming instantaneous formation of Mn,C8. The cell was then weighed again. This experiment was carried out on two different occasions and both times the weight loss of the cell came within 1 pct of the weight of manganese originally charged minus the weight of manganese left in the cell, as determined by chemical analysis. These data are summarized in Table I. This agreement is considered to be within experimental error and is taken as proof that no carbide of manganese is volatile in this temperature range. It was established, by X-ray analysis, that Mn,C, formed before appreciable amounts of manganese vaporized from the metal powder which was charged. The identification of the carbide of manganese which was present in the Knudsen cell in equilibrium with graphite and manganese vapor was carried out by Kehsin Kuo at the University of Uppsala. He established that the authors&apos; sample, which was submitted to him for analysis, contained the phase

Jan 1, 1958

By J. B. Wagstaff

The raceway in front of the tuyere of the blast furnace has been studied quantitatively and a correlation obtained for the penetrastudiedtion of the blast. Some evidence is presented for the height and width of the raceway which suggests that all the raceways of a ffurnace overlap. The size of the coke in this zone has been measfurnaceoverlap.ured photographically during normal operation and results are given for the various areas. IN an earlier paper,&apos; it was shown that a raceway exists opposite each tuyere of a blast furnace. This raceway is formed by the jet effect of the air emerging from the tuyere and consists essentially of a turbulence in which coke particles are recir-culated at high speed. Its presence was deduced originally from observations on movies taken with a high-speed camera through the tuyeres of various furnaces and was confirmed by experiments made on a model. In the model described,&apos; this raceway was shown as operating in a vertical plane only, although there was a suggestion in the motion-picture film exhibited at that time that the raceway was three dimensional, unless artificially restricted. There was also some doubt then about the factors influencing its size. This paper describes the next steps in the investigation. Since the size of the raceway is obviously of importance in the operation of the furnace, it seemed worth while to study the subject more carefully. It is probably in this region that about half the coke in the furnace is consumed, so that the movement of the stock column may well be controlled by raceway behavior. Furthermore, there is some evidence to suggest that the coke is packed densely in the center of the furnace to form the "dead man" and more loosely above the raceway. It is therefore probable that the bulk of the gases passing up the stack flow from the top surface of this raceway. Clearly then, a knowledge of this critical zone is of interest to the blast furnace operator, and the first half of this report is devoted to a quantitative discussion of the subject. A further topic of interest among operators is the degree of breakdown of coke in the furnace, with which is inseparably linked the importance of a strong coke. Indeed, the whole question of the optimum size and type of coke may be as dependent on the condition of the coke in the bottom of the blast furnace as at the top. Attempts have been made from time to time to obtain samples of coke from the tuyeres and other furnace openings but they all suffer from the fact that the coke is filled to a varying degree with metal and slag and is probably broken up by the very act of taking the sample. It has proved difficult to make any reliable studies of coke size by these methods. However, it did seem possible to use the highspeed movies mentioned earlier1 to estimate the size of the coke. These movies provide an accurate record of individual coke particles so that, in theory at least, it should be possible to measure the size of the particles one by one and to obtain, for the first time, information on the coke being blown around the raceway under actual operating conditions while the furnace is performing normally. Such a study has been made and is discussed in the second half of this paper. The results obtained enabled the blast furnace data to be correlated with the model results given in the first half. Raceway Size In order to make a quantitative study of the size of the raceway it was necessary to devise some apparatus of laboratory scale, which could be handled quickly and easily. This focused attention on models, which in turn means that the laws of similarity governing this particular process must be ascertained. Method of Procedure: Since the work was to be carried out on a smaller scale than the blast furnace, the linear dimensions of the model became unimportant provided that the scale was known; it is only important to insure that the container does not affect the raceway being observed. The studies therefore were carried out in a glass-sided box, 11 in. high x 7 in. wide x 3 in. deep, using air jets ranging

Jan 1, 1954

By A. M. Strauss

This contribution illustrates the application of the theory of period doubling to the description of the formation of microcracks in rocks. The fundamental mathematics is described and a method of prediction is proposed. The invariance (universal constants) of a generic microfracturing (damage) process is described. Finally, the method is presented as a deterministic method of predicting the failure of an engineering material while keeping track of the amount of damage that has occured at any point.

Jan 1, 1984

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

IN THE past year, Jaffee and Campbell&apos; and Finlay and Snyder2 reported on the mechanical properties of titanium-base alloys, some of which were in the same ranges of composition as are covered in this paper. In this paper, evidence confirming that given by Finlay and Snyder on the effects of carbon, oxygen, and nitrogen on titanium will be presented; and, in addition, new data will be given on the effects of these elements on the flow properties and phase transformation of titanium. Materials and Preparation of Alloys The preparation and general properties of iodide titanium have been adequately described elsewhere.&apos; , As-deposited iodide titanium rod, prepared at Battelle, of Vickers hardness less than 90 was employed as the base metal in the present work. This was the same material as that used by Finlay and Snyder.2 The probable analysis reported by them for standard quality metal holds here also: N 0.005 pct, 0 0.01 pct, C 0.03 pct, Fe <0.04 pct, A1 <0.05 pct, Si <0.03 pct, and Ti 99.85 pct. Carbon was added in the form of flake graphite supplied by the Joseph Dixon Crucible Co. Oxygen was added in the form of c.p. grade TiO, powder, produced by J. T. Baker Chemical Co. Nitrogen was added in Ti3N4 powder, supplied by the Remington Arms Co. Individual ingots weighed 7 or 8 g. Carbon, oxygen, or nitrogen was added by placing the corresponding powder in a capsule made from as-deposited iodide titanium rods and melting the capsule with the balance of the charge. The charge was are-melted with a tungsten electrode on a water-cooled copper hearth under a partial vacuum of very pure argon (99.92 pct minimum). Melting was practically contamination free. Vick-ers hardness increases of less than 10 points were normal for unalloyed iodide titanium control melts. Nitrogen analyses of are-melted iodide titanium showed a nitrogen content of 0.005 pct, about the same as is present in the as-deposited rod. No tungsten pickup was found in a melt of iodide titanium analyzed for tungsten. Weight losses in melting nitrogen-free alloys were very small and varied consistently from nil to 0.015 g (0 to 0.2 pct). This permitted the use of nominal composition for these alloys. Chemical analyses made for carbon, which can be analyzed conveniently by combustion methods, justified this procedure. Where nitrogen was added, considerable splattering took place. Here it was necessary to analyze for nitrogen by the Kjeldahl method. The ingots were hot rolled at 850°C to about 0.045 in. thick. After hot rolling, the strips were descaled by mechanical grinding, and then given a cold reduction of 5 to 10 pct to insure a uniform thickness throughout the length of the specimen. The edge strips and the tensile strips were annealed in a vacuum of 1x10-4 mm Hg pressure for 3 1/2 hr at 850°C and furnace cooled. Methods of Investigation Hardness Measurements: At least five Vickers hardness measurements were taken using a 10-kg load on each sample in the following conditions: (1) top and bottom of each ingot, (2) top and bottom surface of as-rolled and annealed sheet, and (3) on cross-section of annealed sheet and all quenched specimens. Tensile Tests: Tensile tests were conducted on Baldwin-Southwark testing machines having load ranges of 600 or 2000 lb. Tests were made on 1-in. gauge-length specimens, 3 1/4-in. overall length, 1/2 in. wide, 0.040 in. thick, with a reduced section 1 1/4 in. long and 0.250 in. wide. Two SR-4, A-7 strain gauges, one mounted on each side of the specimen, were used to measure the strain over a limited range to determine the modulus of elasticity. After the modulus of elasticity readings had been taken, load vs. strain readings were taken, using only one strain gauge, at increments of 0.0001 in. until the yield points were passed and then at 0.001-in. increments to the limit of the strain-gauge indicator (0.02 in.). Strain readings above 0.02 in. per in. were taken every 0.01 in., using dividers to measure the strain between the 1-in. gauge marks until the maximum load had been reached. Crosshead speed, when using the SR-4 gauges, was 0.005 in. per min, and, when using dividers, 0.01 in. per min. Flow Curves: Flow curves were determined using the true stress-true strain data obtained during the tension test. The usefulness of this type of information has been dealt with very adequately elsewhere by L. R. Jackson,&apos; J. H. Hollomon,6 and many others. Flow curves of true stress vs. true strain could be converted to the more conventional cold-work curve of 0.2 pct offset yield strength vs. percentage of cold reduction by means of the transformation, 1/1 = 1/1-R, where R is the fraction reduction in cold working. Thus, the true strains corresponding to percentage reduction can be calculated, and the 0.2 pct offset yield strengths scaled off the — 6 curve by taking the true stresses corresponding to the values of 6 + 0.002 strain. Heat Treatment: For the transformation studies, the alloys were heat treated in a horizontal-tube furnace using a dried 99.92 pct argon atmosphere, and quenched into water. Essentially no contamination was found after several hours of heat treatment at temperatures up to 1050°C. Metallography: Specimens were prepared in the

Jan 1, 1951

By F. Newton Parks

SOUND management organization is as essential to a mining operation as sound mining practices, exploration methods, concentration processes, or marketing methods. In fact, if a mining company is well organized, with the right people in the right management positions, it can be reasonably assured of the adequacy of its operating practices. Management problems in mining are unique, but certain principles of organization are universal. These principles should be used as ground rules in mining as they are in other industries.

Jan 5, 1958

By J. M. Mutmansky, T. K. Greer

This paper takes a look at the optimal velocity to be used in coal mine entries and determines a statistical relationship for optimal velocity that can be applied under current mining conditions. This relationship provides the optimal velocity for coal mine airways under variations in power cost, mining cost differential, airway friction factor, time value of money, airway lifespan, and quantity of air carried. This enables the ventilation engineer to make an easy, rapid determination of the optimal velocity for planning purposes.

Jan 1, 1985

Iron and steel lire subjects that will receive the attention clue them at the meeting in. St. Louis. Within the past 2 years the smelting of iron ore on a large scale has been started in the St. Louis area, and the blast furnaces are in full operation. Ore is being received. from the Lake Superior region, in large barges .brought clown the Mississippi River. Firebrick, for the lining of the furnaces, is made in the. St. Louis district to a greater extent than elsewhere in the country. At this meeting, there will probably be a discussion of the possibilities of the increase of manganese production in this country, and of improved methods of using it in steel manufacture.

Jan 10, 1917