By Maynard O. Serbousek, James R. McVey

IS there a quick way of assessing the conditions of a newly exposed roof in a coal mine? This has always been a nagging question. The problem is that unless effective controls are established as soon as possible, it becomes extremely difficult to extract coal safely and economically from conventional underground milling operations. Until recently, little has been done to provide a means of measuring the structural behavior of a coal mine roof while the face advances during actual production. (In fact, most measurements have always been made after the fact or during a roof pull-down where the roof is actually caused to fail with no support.)

Jan 9, 1976

By A. H. Geisler, R. F. Mehl, S. Barrett

The studies of the mechanism of pre= cipitation and of the resulting property changes in aluminum-silver alloysl-3 have presented some new concepts of the aging reactioxl—concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.l,4 These platelets grow in lateral dimensions and in thickness with aging time until they arc thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstatten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuoils precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 Expermental Procedure The alloys were made using 99.97 per cent A1 or distilled magnesium, with

Jan 1, 1943

By R. F. Mehl, A. H. Geisler, S. Barrett

The studies of the mechanism of pre= cipitation and of the resulting property changes in aluminum-silver alloysl-3 have presented some new concepts of the aging reactioxl—concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.l,4 These platelets grow in lateral dimensions and in thickness with aging time until they arc thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstatten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuoils precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 Expermental Procedure The alloys were made using 99.97 per cent A1 or distilled magnesium, with

Jan 1, 1943

By R. P. McLaughlin

In most branches of the mining industry it is a well-recognized fact that care must be taken to protect the mineral deposit from undue physical injury. It is comparatively easy to grasp this idea when the mineral is a solid and the lives of workmen depend directly upon the care with which it is removed from its natural position, but when the product is a liquid drawn up from pools several thousand feet beneath the surface of the ground through openings only a few inches in diameter, it requires some imagination to picture underground conditions and the changes which must often occur. The development of the petroleum deposits of California has been attended by numerous accidents, the results of which are readily noticed at the top of the wells and in the profit and loss accounts of the operators. Determination of the cause of these accidents has been the subject of considerable study, which naturally has fallen upon men familiar with technical methods. The greatest damage to the oil deposits of California has resulted from water finding its way into the oil-bearing sands, and it is the purpose of this paper to set forth briefly this phase of the oil industry. Much of the material here presented has previously appeared in publications issued by the California State Mining Bureau, which, under the direction of State Mineralogist Fletcher McN. Hamilton, has investigated the subject and taken steps toward improvement of conditions. The writer, having been in charge of this branch of the Bureau work, has gained considerable knowledge of existing conditions. Generally speaking, the oil-bearing formations of California are soft, unconsolidated sand beds, separated by clay strata, which are also soft. Some of the sand beds carry water instead of oil. All of the beds are more or less separated, probably being of lenticular shape. Very few of the beds in the oil fields lie flat or undisturbed over any great area. Folding and tilting are common, and faulting also occurs in some of the fields. The accumulation of oil is not confined to any single structural feature, such as the anticline, but occurs in many other structural features. Water-bearing strata occur in practically every oil field in the State. Complete data are not at hand for a comparison of the damage

Jan 1, 1916

By Lloyd R. Jackson

IN the past 15 years there has been a great deal of interest in the fundamentals of plastic flow and rupture in metals and a number of papers have presented substantial advances toward a fundamental insight into the mechanism of these two processes. This paper is an appraisal of the present position with respect to the following: I. The relative importance of shear and hydrostatic stresses in controlling the plastic flow of metals. 2. The relative importance of shear and hydrostatic stresses in determining the amount of flow before rupture in metals. 3. The use of generalid strains in determining the effect of plastic flow on the work-hardening of metals. FUNDAMENTALS INVOLVED IN PLASTIC FLOW In attempting to devise a quantitative description of plastic flow in metals, it has been customary to assume that metals are homogeneous and isotropic. The fact that neither of these assumptions is correct complicates the experimental appraisal of relations developed. Never- the less, as will be shown, metals are close enough to being isotropic and homogeneous so that considerable insight into the mechanism of plastic flow can be obtained. The assumptions of .isotropy and homogeneity allow both the elastic and plastic behavior of metals to be described in terms of 12 variables-six being stress variables, and six being strain variables. ) From this viewpoint, it should be possible to represent the stress-strain relations in the plastic range for metals by a surface in 12 dimensions. One boundary of this surface would be the surface of transition from elastic to plastic behavior; the other would be the surface of rupture. These two surfaces would be joined by the surface of plastic flow. The shape of this composite surface would depend on the test temperature and speed of straining. This paper is concerned only with results obtained at constant temperature and constant speed of straining. While such a representation is conceivable, the demonstration of such a surface would present almost insurmountable obstacles. The most fruitful simplification of this concept has been the recognition that the behavior of metals in the plastic region is primarily a result of shear stresses and strains. Based on this viewpoint, it is possible to utilize stress and strain invariants that are independent of hydrostatic components to define an effective stress and strain. In effect, this amounts to reducing the task of representing stresses and strains in 12 dimensions to one of representation in two dimensions. The two invariants (one for stresses . and one for strains) that have received most attention are the following: [ ]

Jan 1, 1946

By W. A. Anderson

Recrystallization of cold-worked metals has long been known to proceed by a process of nucleation and growth.' When a cold-worked metal is heated to a temperature at which recrystallization will ensue, nuclei of new grains, essentially strain-free, appear and grow. As the process proceeds, nuclei continue to appear and to grow, until the cold-worked matrix has been entirely consumed and recrystallization has been completed (Fig. I). Conducted isothermally, a measurement of the fraction of the matrix recrystallized plotted against time, yields an isothermal recrystallization curve, showing the time course of the recrystallization process (Fig. 2).2 Evidently, then, the rate of recrystallization is determined by the rate at which nuclei form and the rate at which they grow. The rate of nucleation N is the number of nuclei that form in unit time in unit volume of the unrecrystallized matrix, and the rate of growth G is the increase in radius of the recrystallized grain per unit time. In recent years attempts have been made to determine N and G as these vary with the well-recognized variables affecting recrystallization: time, temperature, degree of deformation, etc.1 Such studies yield information that is more fundamental than that conveyed by the conventional recrystallization diagram,' since the rate of recrvstallization is thus analyzed into its two component rates3 Methods are now available by which N and G can be measured, and analytical expressions have been developed for the interrelationships among N, G, the isothermal recrystallization curve, and the final grain size, which greatly facilitate analysis.2-4 The application of these methods has been demonstrated recently for the recrystallization of silicon ferrite.2 Data on N and G in dependence upon the recognized recrystallization variables are, however, very fragmentary;" values of N and G have been determined for some metals, but the effect of temperature, which would yield the fundamentally important activation energies, has been too little studied. Thus far there has been no detailed study of the recrystallization of any one metal in terms of X and G ovcr appreciable ranges of the variables time, temperature, degree of deformation, and original grain size. It is the purpose of the present paper to provide such a study, employing aluminum.

Jan 1, 1945

By A. H. Tousley

The cement industry is on the horns of an economic dilemma. Within the last ten years, its over- capacity in the United States has varied from 139- 127% of demand (Fig. 1). The most direct effect of this is seen in cement prices, which reached a peak in 1960, retreated steadily through 1966 and only recently climbed back to the 1960 level again. With prices in a slump and production costs estimated to be up almost 30%, there has been a steady drain on cement profits. Since 1960, labor costs have increased 86% while fuel costs have risen 18%. Meanwhile, customer service costs have also soared owing to the competition for cement customers and the wider variety of available cement products. This search for sales advantage has in turn led to a higher Blaine number, which means more grinding and hence bigger mills, more power, and, once again, higher costs. New plants as well as expansions and revisions to existing plants are also costing more owing to higher

Jan 1, 1971

By M. G. Corson

Until recently, the characteristics of cast copper have seldom been studied and such study as has been made has been inadequate. The prevailing idea seems to be that since pure copper is infrequently used in the cast stlate, there is no reason for trying to establish precise data regarding the properties of the metal in that condition. On the other hand, wrought copper either in the shape of sheets or wire rarely fails in service, except as a result of the action of reducing gases at the annealing temperatures, so there is little incentive to study the properties of the cast shapes —cakes, bars, ingots and billets—for the sake of tracing the causes of failures of the wrought metal to the cast stock. However, about a decade ago, wirebars of American origin often cracked badly while being hot-rolled in mills in Germany. This Icd to four investigations: by E. Seidl and E. Schieboldll by P. Siebe12 by 0. Bauer and G. Sachs,3 and by G. Welter.4 These authors came to the conclusion that failures in hot-rolling were due essentially to the presence of a wide zone of columnar crystals between t'he thin layer of fine crystal5 near the surfaces of the bars and the large but more nearly equiaxed grains of the central core. This macrostructural defect was explained in turn by the probable upward deviation in the temperature of the metal while it was being poured into the molds of the castling machine. More recently, cast shapes of copper were investigated by X. 1'. Allenh and by C. Blazey. Allen examined vertically cast wirebars and hori-zontally cast wedge cakes of electrolytic tough-pitch copper, but only for the distribution of densities; i.e., porosity. Blazey was interested mainly in the mechanism of the variations in electrical conductivity due to cold-work and anneal, but gave introductively an account of the composi-tion and average densities of the tough-pitch horizontally cast Wirebars used. As far as the present writer can tell, no investigation mas under-taken for the sake of presenting a picture of the distribution of mechanical characteristics in the wirebars of copper, or otherwise.

Jan 1, 1938

By M. G. Corson

Until recently, the characteristics of cast copper have seldom been studied and such study as has been made has been inadequate. The prevailing idea seems to be that since pure copper is infrequently used in the cast stlate, there is no reason for trying to establish precise data regarding the properties of the metal in that condition. On the other hand, wrought copper either in the shape of sheets or wire rarely fails in service, except as a result of the action of reducing gases at the annealing temperatures, so there is little incentive to study the properties of the cast shapes —cakes, bars, ingots and billets—for the sake of tracing the causes of failures of the wrought metal to the cast stock. However, about a decade ago, wirebars of American origin often cracked badly while being hot-rolled in mills in Germany. This Icd to four investigations: by E. Seidl and E. Schieboldll by P. Siebe12 by 0. Bauer and G. Sachs,3 and by G. Welter.4 These authors came to the conclusion that failures in hot-rolling were due essentially to the presence of a wide zone of columnar crystals between t'he thin layer of fine crystal5 near the surfaces of the bars and the large but more nearly equiaxed grains of the central core. This macrostructural defect was explained in turn by the probable upward deviation in the temperature of the metal while it was being poured into the molds of the castling machine. More recently, cast shapes of copper were investigated by X. 1'. Allenh and by C. Blazey. Allen examined vertically cast wirebars and hori-zontally cast wedge cakes of electrolytic tough-pitch copper, but only for the distribution of densities; i.e., porosity. Blazey was interested mainly in the mechanism of the variations in electrical conductivity due to cold-work and anneal, but gave introductively an account of the composi-tion and average densities of the tough-pitch horizontally cast Wirebars used. As far as the present writer can tell, no investigation mas under-taken for the sake of presenting a picture of the distribution of mechanical characteristics in the wirebars of copper, or otherwise.

Jan 1, 1938

By C. R. Ramachandra, C. C. Patel

Flotation of chalcopyrite from a low grade ore was studied by using different xanthates and dixanthogens as collectors and by conditioning the flotation pulp with oxidizing gaseous systems. The improvement in the recovery of chalcopyrite with the oxidizing systems was mainly due to the auto-activation of chalcopyrite, leading to the enhanced adsorption of xanthates and dixanthogens even when the latter were formed by oxidation of the xanthates. With air or oxygen as oxidizing system, the amount of ethyl xanthate required at pH 8.5 was much less than normally employed in the industry, the recovery being 97-99% of chalcopyrite with a concentrate of 24% copper. With isopropyl and isoamyl xanthates, the recovery was improved but the grade was lowered. By conditioning the pulp with air-CO2 or oxygen-CO2 mixture, the recovery was lowered with ethyl xanthate only, mainly due to the depressant action of bicarbonate formed. Flotation with dixanthogens gave cleaner concentrates of chalcopyrite. because iron pyrite did not float with these collectors. Of the dixanthogens tried, diisopropyl dixanthogen gave the highest recovery, 99% chalcopyrite with a concentrate containing 28.5 to 30% copper, when the pulp at pH 8.5 was condi-tioned with air. Isopropyl dixanthogen was found to be the best collector of all the xanthates and dixanthogens studied. It was found that the adsorbed ethyl, isopropyl and isoamyl xanthates at chalcopyrite surface, activated by cupric sulfate, and at iron pyrite surface were oxidized to the corresponding dixanthogens to different degrees in presence of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture.' The dixanthogen formed at chalcopyrite surface was, however, firmly adsorbed while that at iron pyrite surface was easily desorbed. Since dixanthogens formed have greater hydrophobicity than the corresponding xanthates, as revealed by contact angles,1,2 the former were expected to improve the flotation results. It was, therefore, thought desirable to find out the effect of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture on the selective flotation of chalcopyrite when individual xanthates were used as collectors. The effect of direct use of dixanthogens as collectors on the selective flotation of chalcopyrite was also investigated. For these studies, low grade chalcopyrite ore, received from the Indian Copper Corp., Ltd. (I.C.C.), Ghatsila, Bihar, was employed. At the milling plant of the I.C.C., chalcopyrite is floated at a pH of 8.5, employing ethyl xanthate as collector. EXPERIMENTAL Materials Employed: XANTHATES - Ethyl, isopropyl and isoamyl xanthates of potassium were prepared in a pure state by the methods described earlier.4 A 0.03% aqueous solution of a xanthate was freshly prepared in air-free distilled water for flotation studies. DIXANTHOGENS - Diethyl, diisopropyl and diisoamyl dixanthogens were prepared by the oxidation of xanthates by iodine and purified by extraction with petroleum ether. A 0.03% alcoholic solution of dixanthogen was used as a collector. FROTHER - A 0.2% solution of pine oil in ethyl alcohol was employed. SODIUM CARBONATE - A 0.4 N solution was used. ORE - The composition of the -100 +200-mesh size (Tyler standard) powdered ore, as determined by standard methods of analysis, was: copper 1.57%, iron 10.29%, sulfur 3.15% and acid insolubles 66.10%. Iron present as chalcopyrite (CuFeS2) was 1.38%, while that present as iron pyrite (FeS,) was 1.37%. Both chalcopyrite and iron pyrite were found to be liberated from the gangue minerals and from each other, as observed under a microscope. Flotation of Chalcopyrite with Xanthates in Presence of Different Gaseous Systems: Fifteen grams of -100 + 200-mesh size ore were shaken well with 100 ml of distilled water. The pH of the pulp was adjusted to 8.5 by the addition of sodium carbonate solution. Then 0.1 ml of xanthate solution (0.005 lb xanthate per ton of the ore) was mixed with the pulp, and the latter together with washings transferred to a

Jan 1, 1963

By Paul Bechtner

THE name bentonite formerly was applied solely to a peculiar clay occurring in Wyoming and South Dakota, which was distinguished from other clays by its unctuous feel when wet and the property of swelling in water. In the last decade scientific studies of clay have recognized that bentonite is composed mainly of the clay mineral montmorillonite and the name bentonite has been extended to cover the entire family of clays that have montmorillonite as their chief constituent. Montmorillonite has the chemical formula of A1203-4Si0-xH2O, With Fe203 and MgO replacing part of the A1203. The montmorillonite crystal is an Si-Al-Si clay mineral, being formed of two silicon-oxygen sheets with an aluminum-oxygen sheet sandwiched between them. In contrast, kaolinite-the chief clay mineral of most clays other than bentonite-is Si-Al, one silica and one alumina sheet. The unit crystal of montmorillonite is much thinner than that of kaolinite, with greater surface area. These differences in crystal structure patterns are leading factors in the dissimilar properties and commercial uses of bentonite compared with other clays. Mineralogically, bentonites are 85 to 90 pct montmorillonite with fragments of feldspar, gypsum, calcium carbonate, quartz and traces of other minerals. They vary in color; the widely used Wyoming type is creamy white when dry and a light shade of tan when wet; the low-swelling bentonites of the southern United States and elsewhere are found in many shades of gray, blue, yellow, red, and brown. Pure white bentonites are rarer and generally of the medium or low-swelling type, though there are a few exceptions to that general rule. PROPERTIES Bentonites may be divided into two general classes: (1) those that adsorb large quantities of water, "swelling" greatly in the process, and that remain in suspension in thin water dispersions; (2) those that adsorb only slightly more water than ordinary plastic clays or fuller's earths, do not swell noticeably, and settle rapidly in thin water dispersions. Another distinction is that some varieties of the No. 2 type

Jan 1, 1949

By J. R. Long, C. E. Armantrout, A. H. Roberson, T. R. Graham

The preparation and fabrication of copper-manganese-zinc alloys and the evaluation of their engineering properties have for some time been an integral part of a research program of the Federal Bureau of Mines. In this project, the use of electrolytic manganese, along with high purity copper and zinc, has permitted the preparation of alloys which contain a minimum of impurities which are capable of producing detectable effects in the properties studied. The initial work on the physical properties of wrought alpha solid solution alloys and a general outline of the alpha solid solution area for alloys containing up to 40 pct manganese have been presented in previous reports. 1,2,3,4,5 The evidence accumulated in these investigations clearly showed that additions of manganese to the copper-zinc alloys improve the strength properties of the brasses without seriously reducing their characteristic ductility and that considerable quantities of manganese could be added to the copper-zinc alloys without exceeding the mutual solubilities of manganese and zinc in copper. In continuation of these studies, additional data have been obtained in a more extensive investigation of the phase relationships of the copper-manganese-zinc ternary system. The present report delineates the solid phase boundaries of the ternary system from the copper-zinc binary to the manganese-zinc binary for alloys containing up to 50 pct zinc. Summary The alloys used in this investigation were conditioned by working schedules designed to homogenize the structures prior to heat treatments required for the equilibrium phase sludy. The treated alloys were examined by metallographic methods including hardness and X ray data for confirmation. The composite data of the investigation are summarily presented in a series of isothermal sections of the ternary system at 1100, 1200, 1300, 1200, and 1500°F. The salient features of the system as outlined by these data are: (1) the continuous alpha solid solution which extends across the diagram to the gamma-manganese phase of the manganese-zinc system at temperatures of 1200°F and higher, (2) the beta phase of the copper-zinc system similarly forms a continuous solid solution with its counterpart the beta field of the manganese-zinc binary, (3) at 1100°F (593°C) these alpha and beta fields are greatly restricted by complications arising from the allotropic transitions of manganese and the decreasing solubility of manganese in the alpha solid solution. The alpha + beta fields intersect the alpha + alpha manganese field to produce the beta + alpha manganese field and two adjacent three phase fields consisting of alpha + beta + alpha manganese and gamma + beta + alpha manganese. Typical microstructures representative of the various phase areas at each temperature are also presented. Review of Previous Work The copper-manganese-zinc alloys have periodically been the subject of numerous investigatioris of both prac-

Jan 1, 1950

By Marston G. Fleming

CRITICAL pH has been defined by Wark1 as that pH value below which a mineral will float and above which it will not float in solutions containing a given concentration of collector but free from other depressants or activators. - The relationship between mineral, collector concentration, and pH is expressed in the form of a critical pH curve determined by the captive bubble method and is generally regarded as being fundamental to the system involved. The mechanism of alkali depression is currently in dispute, two general theories having received authoritative support. The view expressed in Taggart's chemical theory of flotation2 is that in the presence of a critical concentration of hydroxyl ions, all the metal ions available at the surface of the mineral are present as anions of the form [M (OH)x]-y. The formation of the necessary metal xanthate is thus precluded and, furthermore, any metal xanthate coating previously formed, at a lower pH, will be dissolved. Gaudin3,4 and the Melbourne school under Ware hold that alkali depression is caused by the preferential adsorption of hydroxyl ions by the mineral surfaces. This paper describes an investigation of the mechanism of alkali depression in each of the three systems: cerussite-aqueous carbonate-xanthate, cerussite-xanthate, and galena-xanthate. Alkali Depression of Cerussite by Control of Carbonate Ion Concentration Wark and Cox6 have shown that in the presence of Na2CO3 a higher concentration of xanthate is required to effect bubble contact with a cerussite surface than in carbonate-free solutions. To examine this depression of cerussite by sodium carbonate, a series of captive bubble tests was carried out on cerussite specimens in solutions containing 100 mg per liter of potassium ethyl xanthate and varying concentrations of sodium carbonate. The pH was adjusted by the addition of dilute hydrochloric acid. For purposes of comparison a standard critical pH curve was determined for cerussite with potassium ethyl xanthate in solutions containing no added carbonate. In the latter case pH adjustment was made with sodium hydroxide. The experimental method employed in both series was broadly similar to that described by Wark and Cox;7-9 a number of refinements suggested by Sutherland10 were adopted, and the procedure was further developed and modified to suit the particular requirements of the investigation. The relationship between pH and the concentration of potassium ethyl xanthate necessary to induce bubble contact at cerussite surfaces is shown in Fig. 1. The relationship between pH and the concentra- [ ] tion of sodium carbonate necessary to prevent bubble contact at cerussite surfaces in the presence of 100 mg per liter of potassium ethyl xanthate is shown in Fig. 2. Comparison of the. two curves shows that at a collector concentration of 100 mg

Jan 1, 1952

By A. E. Wells, H. O. Hofman, R. P. Reynolds

A Discussion of the Paper of H. O. Hofman, R. P. Reynolds and A. E. Wells, read by title at the London Meeting, July, 1906 ; presented at the New York Meeting, April, 1907, and printed in Bi-Monthly Bulletin, No. 13, January, 1907, pp. 37 to 52. GEORGE A. PACKARD, Boston, Mass. (communication to the Secretary*) :-The very interesting results obtained by Prof. Hofman and his assistants came to my attention when I had temporarily assumed charge of the metallurgical department of the Missouri School of Mines, and had found it, pending the completion of a new building, lacking a furnace in which to roast ore preparatory to the customary lead blast-furnace run. An attempt at lime-roasting had been already determined upon, but the use of a charge which would make a slag of definite composition was a new idea. The results following were obtained by Messrs. Aubrey Fellows, J. C. Long, E. R. Wash, and Dr. T. C. Tseung, under my supervision. It is regretted that the data are not more complete; but the work was done simply incidentally to securing the desired ore for the blast-furnace, with no idea of obtaining any results of especial interest. It is submitted because of the metallic lead obtained, no notice of which has been seen elsewhere. The ore was an aggregate of several lots of concentrates, apparently from Missouri ores. The analysis follows, with that of the limestone and sandstone used, as far as made:. Ore, SiO2, 3.04; Fe, 0.77; CaO, 2.53; Pb, 68.74; Zn, 5.77; S, 13.9 per cent.; limestone, SiO2, 1.0 ; CaO, 54.35 per cent.; sandstone, SiO2, 99.8 per cent. The converter was made in the shops from a sheet of No. 14 iron riveted in the shape of a truncated cone, 20 in. in diameter at the top, 15 in. at the bottom and 22 in. high. A grate of No. 8 iron, 17 in. in diameter, with 130 s-in. holes placed at about 1.25-in. centers, was held in place by the shape of the

Jul 1, 1907

By F. D. Rosi

IN the production of single crystals by the Bridg-man method of solidification from the melt in vacuum at a crucible lowering rate of 0.25 in. per hr, a cellular structure was frequently observed in copper and copper-base alloys at the terminal surface of the as-cast crystals (i.e., the surface representing the last portion of the crystal to solidify). The geometrical form of this structure varied from crystal to crystal, but, in general, could be classified as either hexagonal or quadrilateral. Fig. 1 shows examples of this cellular structure, which is similar to that reported by Buergerl and, more recently, by Pond and Kessler&apos; and Rutter and Chalmers. In the micrographs of Figs. lb and c, the cubic structure in the alloy crystals is obscured somewhat by excessive surface evaporation in the final stages of solidification. X-ray orientation studies indicate that the traces outlining the various geometrical forms correspond to octahedral planes, which are the planes of greatest reticular density in the face-centered cubic lattice. It would appear from this that the view first propounded by Bravais,4 that the surface energies and normal growth velocities of the different crystal planes are inversely proportional to their reticular densities, applies to this cellular structure, since those surviving are the planes of greatest atomic density. Thus, the observed variation in the geometrical form of this structure in crystals of different orientation is readily understandable from the distribution of the (111) planes in the standard {111}, (1101, and (1001 stereographic projections. Depending upon whether the crystal axis (i.e., the direction of crystallization) coincides with a <111>, <111>, or <100> direction, the cellular structure viewed from a surface perpendicular to the crystal axis will consist of a network of regular hexagons, skewed hexagons (with interfacial angles of 110" and 125"), or cubes, respectively. It follows, moreover, that off-orientations from these principal directions will yield modifications of these three basic geometric configurations. In this connection, it is interesting to note that the bounding planes of the hexagonal structure observed in tin by Rutter and Chalmers3 showed no preferred orientation.

Jan 1, 1954

By R. H. Tien

This paper presents an analytical solution of the problem of freezing of a semi-infinite slab with constant surface temperature; in this analysis accoz~nt is taken of the heat evolution during the solid-state transformations in the frozen skin. The regions where transformations occur are treated as plane isothermal heat sources; i.e., the rates of transformations are assumed to be infinite. In the model considered, three plane heat sources are assumed to be present in the frozen solid. The solution yields the temperature distribution in the solid, the rates of movement of the heat sources , and the rate of movement of the solidification front. It is shown that, although the sum of the heats of transformations in the solid is about 20 or 43 pct of the heat of fusion of iron or manganese, respectively, the effect of the heat evolution in solid-state transformations on the rate of solidification is insignzficant. IN several recent mathematical studies of solidification of liquid metals&apos;-3 no account was taken of the heat evolution accompanying the solid-state transformations. In the case of, for example, steel, there are several phase transformations 6 -y, y -a, and the magnetic transformation. Whether or not a significant error is introduced into the mathematical simulation of solidification processes by the omission of the heat effects associated with these phase transformations is not known. The purpose of the present study is to investigate the effect of these phase transformations on the temperature distribution and the rate of solidification based solely on the heat transfer point of view. That is, for the sake of simplicity, freezing of a pure metal with solid-state transformations will be considered. The mathematical model which represents the present problem includes four moving heat sources representing freezing and phase transformations, 6— y — a — ferromagnetic. The thermal properties such as conductivity and specific heat, and so forth, are different from one phase to the other. But they are considered to be uniform over any particular phase. The usual Fourier heat flow law is employed. The concept of conservation of energy is applied at every heat source in order to estimate their rate of movement. The temperature distribution in the solid and the positions where transformations occur are expressed analytically in terms of error function solutions and four coefficients which are determined from four nonlinear algebraic equations. These coefficients can be calculated either by trial and error or by any numerical method. MATHEMATICAL ANALYSIS Fig. 1 is a schematic diagram showing the zones of different phases 1, 2, 3, and 4 in the solidified portion of a semi-infinite pure liquid metal. The heat is subtracted from the system at x = 0 which is maintained

Jan 1, 1968

By E. A. Gulbransen, W. S. Wysong, K. Andrew

The reaction of carbon in solid solution in a metal with the surface oxide fim on many metals may be inferred from thermo-dynamic calculations for high vacua and high temperature conditions. Holm has recently shown that oxide films may be removed from ferrous materials by heating in a vacuum at high temperatures and that carbon is the essential element in the reaction. considerable work has been described in the literature on the de-carburization reaction. Several general references may been 2,3,4 However, the nature of the mechanism involved in the decarburization is not well understood. Our interest in this reaction resulted from many attempts to degas and to reduce by pure and dry hydrogen the surface oxides on strips of various types Of chrome-nickel alloys. Some of the early experiments On the behavior Of &apos;3 pct chrome-iron in vacua of the order of 5 X lo&apos; mm and at a temperature Of 600°C have been reported.5 These experi-merits showed a &apos;low reaction with the residual Oxygen Or water vapor in the system and no reaction with hydrogen. This is in accord with thermodynamic data which would lead to the prediction that it is extremely difficult to maintain a hydrogen atmosphere at 600&apos; C pure enough to reduce Crz03 formed On the surface. The crystal structure of the superficial oxide film formed on 13 pct chrome- iron and Nichrome V has been investigated in the thin film range by Gulbransenr Phelps and Hickman,&apos; and shown to be "203. It Was surprising to us to note that when a specimen of Nichrome V containing approximately 80 pet nicke1 and 20 pet chromium was heated to 850°C in a high vacuum, the specimen lost weight. The rate Of weight loss was very temperature sensitive. A study of this reaction in vacua and in a hydrogen atmosphere is the subject of this communication. Type Reactions Let us consider the various reactions which may occur when a metal is heated in vacua, in a hydrogen atmosphere, or in an oxygen atmosphere. The number and kind of reactions will depend upon the chemical nature of the metal, its alloying constituents and the location of the alloying constituents. The metals used in this study are chrome-nickel alloys of the heater type, They consist essentially of chromium, nickel and iron, small amounts of carbon, silicon and manganese and traces of zirconium, calcium, aluminum and magnesium. The trace elements are added to improve the lifetime and other characteristics of the alloy when used as a heater. Seven of the more important reactions with which we are going to be concerned here are as follows: 1. Metal . (gas) F? metal + gas — degassing of the metal 2. zM(s) + y }i Oi(g) M MIOu(s) -oxidation

Jan 1, 1949

By C. W. Haworth, M. G. Hall

THE diffusion of copper in silver has been studied by Sawatzky and Jaumot1 and Cahoon and Youdelis.2 Sawatzky and Jaumot measured tracer diffusion in single crystal specimens but the 12.9 h half-life of CU64 limited the time of the diffusion anneal to about 50 hr, and in consequence the minimum temperature of the investigation was 716°C. Cahoon and Youdelis employed polycrystalline diffusion couples, and measured the interdiffusion coefficient over the range 0 to 2 at. pct Cu. These experiments were performed at temperatures down to 630°C and a discontinuity in the Arrhenius plot was observed at -700°C. The high D-values at lower temperatures were attributed to the effect of grain boundary diffusion. The present experiments were undertaken to investigate this anomaly and study the low temperature region of the diffusion of copper in silver. The method employed single crystal samples and a plated source of copper. Silver single crystals 2½ by 4 in. sq were grown from zone-refined silver bar (>99.99 pct Ag) by the Bridgeman technique, and $ in. thick slices were cut by spark machining. The specimens were electro-polished, and a 2 µm layer of copper was electroplated on to the planar surface at one end of each specimen using a potentiostatic voltage source. The following solution was used for plating: CuSO4 . 5H2O 125 gm H2SO4 (S.G. 1.8) 53 ml H2O 1000 ml The diffusion couples were sealed in capsules, in an argon atmosphere, and were annealed at either 701, 597, or 498°C. The temperature measurements were made to an accuracy of *l°C After the anneal, the penetration of copper into the silver was determined using an electron probe micro-analyzer. 100 sec scaler measurements of the intensity of Cu Ka! X-radiation were performed at 2 to 5 µm intervals along a line normal to the source, with a beam potential of 25 kv. Allowances were made for the background radiation, and the dead-time of the counting system in the normal way, and the intensity ratios were corrected to weight concentration by the method of Duncumb & de-Casa.3 For the analysis of the diffusion profiles, it was first observed that the copper layer did not completely dissolve in the host crystal for the specimens annealed at 498 and 591 whereas for the specimen annealed at 701°C, a single phase solid solution was formed. For the 498" and 597°C specimens, the concentration of copper in the silver at the interface was therefore constant throughout the anneal and the analysis for a

Jan 1, 1970

By A. Lawley, H. W. Schadler

TWINNING has long been recognized as a possible mode of deformation in crystalline solids and has been studied in a wide variety of crystals.&apos; Recently, deformation markings which have the topographical characteristics of twins have been seen in tungsten" and the body-centered cubic alloys of tungsten and molybdenum with rhenium.3-7 These markings have been identified as twins because: 1) they are visible after polishing and etching;2,3 2) their formation is accompanied by an audible click and a drop in load;4 and 3) the habit plane is {112}, the plane which has been identified as the twinning plane for several body-centered cubic metals.&apos; However, there has been no published evidence for the specific determination of the twinning direction in rhenium alloys of tungsten and molybdenum, because usually the deformation twins were not broad enough to be detected with a conventional X-ray beam. Consequently, [111] is inferred as the twinning direction since the latter must lie in a plane of symmetry perpendicular to the twinning plane (112). As Sims and Jaffee3 and Lawley and Maddin4 have shown, the addition of rhenium to molybdenum and tungsten increases the ductility of the alloy over that of the pure metal, but twinning is much more profuse in these alloys than in the pure elements, particularly at Mo-35 pct Re*and W-30 pct Re. Since twinning is often associated with brittle fracture in iron8 and the silicon-irons,9 direct experimental proof that the deformation markings in tungsten and molybdenum alloys of rhenium are twins seemed to be needed. Using the Laue back-reflection technique, the deformation markings in a Mo-35 pct Re alloy are shown to be deformation twins. The twins have a (112) habit plane and the twinning direction is <111>. The Mo-35 pct Re specimen used was taken from a 0.060-in. zone-refined single crystal deformed 6 pct in tension at 78°K. The Laue back-reflection technique, with a film to specimen distance of 2 cm, and white radiation from a copper target were used.

Jan 1, 1962

By W. W. Stephens, W. J. Kroll, H. P. Holmes

THE only two methods for producing commercial quantities of malleable zirconium, up to now, have been using magnesium reduction of the anhydrous chloride under a neutral gas, and using purification of raw zirconium by the iodide dissociation method on a hot filament. The purity of the metal obtained by the latter process is about the same as that resulting from the chloride reduction, with the exception of the oxygen content, which may be about 0.05 pct lower in the iodide metal. Even traces of oxygen have a strong hardening effect on zirconium. Since, in the iodide process, the impurities, Si, Al, Fe, Ni, and Mg in the raw zirconium used, are carried over, it would appear uneconomical to use this method of refining solely to eliminate the traces of oxygen, unless very soft metal is desired. One important step to improve the iodide method, namely, dissociating pure iodide made from carbide and recycling the iodine, which would change this refining process into a method for extracting zirconium from the ore, has not yet been made. The Bureau of Mines, by using the chloride reduction, wanted to produce quantities of a reasonably pure and malleable metal at low cost for large-scale industrial use. This aim has been achieved, and a pilot plant permitting production of 600 lb of malleable zirconium per week will be described (fig. 1). Briefly, the Bureau of Mines process consists of reducing purified gaseous anhydrous zirconium chloride with fused magnesium under a noble-gas atmosphere. The reaction product, magnesium chloride, and any excess magnesium metal present are removed from the sponge zirconium in the next step by fusion and evaporation in a good vacuum at about 925°C. In this process, care is taken to keep air out of contact with the hot metal, which otherwise would contaminate the product with oxygen and nitrogen. Both these impurities embrittle zirconium even when present in an amount as low as 0.1 pct. A number of previous reports1-3 describe the method and the various improvements that finally led to a workable process. The major steps made were the production of large quantities of carbide, which is the raw material for producing the chloride, its chlorination with reasonable efficiencies, and the elimination of iron trichloride contained in the raw chloride, as well as that of the zirconium oxide which is always present in this product. The physical nature of the anhydrous chloride, which sublimes at 331°C at atmospheric pressure and melts at 420°C under a pressure of 25 atm, made it necessary to provide a special safety device on the purification and reduction vessels in the form of a lead-alloy seal, permitting escape of excess gases if pressure tended to build up. The main difficulties encountered in the reduction and in the following step, salt separation in a vacuum at elevated temperature, were caused by the material from which the reaction pot was constructed—iron. This metal reacts with zirconium at about 940°C with formation of a eutectic. The last step, salt separation by evaporation of the magnesium and magnesium chloride in a vacuum, is quite unconventional and has not been used before on such a scale. It is only due to the improved construction of high-vacuum pumps, especially oil-diffusion pumps, that such a method could be used. The various steps of the Bureau of Mines process, as described in the general outline above, may be summarized as follows: (1) production of the carbide, (2) chlorination of the carbide, (3) purification of the raw chloride, (4) reduction of the pure chloride with fused magnesium, (5) separation of excess magnesium and magnesium chloride in vacuum at elevated temperature, and (6) melting of the sponge obtained. Production of Carbide The arc furnace, described in a previous report,&apos; was improved both to reduce the graphite consumption caused by the burning of the bottom plates and to concentrate the heat in order to obtain better power efficiency. This was achieved by providing the bottom with graphite plates entirely embedded in refractory bricks, the contact with the current being made with three water-cooled copper plugs. Figs. 2 and 3 show the arrangement. The crucible, made

Jan 1, 1951