By R. M. Brick

THE etched microstructures of cold-worked alpha brasses, after reduc-tions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonomously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {111}, in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson5 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into sym-metry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By G. Sachs

According to Tammann,' the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes Ïn properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by Ewing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931

By J. F. Olk, E. D. Spaulding, R. E. Thurmond, G. A. Komadina, R. W. Hernlund, J. A. Journeay

THE Pima pit is a 1700x1400-St oval, the long T axis parallel to the strike of the orebody. The north side of the pit is carried as a final pit slope that coincides with the footwall of the orebody. The south side and east and west ends of the pit are working slopes continually being stripped back toward the final slopes. An inclined roadway extending from the natural ground surface on a 5 pct grade down to the north- east corner provides access to the pit. This road enters the pit 130 ft below the natural surface and continues as a pit ramp on a 5 pct grade to the 3150-ft bench (roughly the base of the alluvial cover). At this point the ramp system is steepened to a 12 pct grade and continues to the pit bottom. The 5 pct grade is maintained in the alluvial section to facilitate scraper haulage out of the pit. In addition to this main access ramp, temporary working ramps in the alluvial areas allow shorter routes to dumps. These are left on top of working benches and do not change the overall working slopes. Below the base of the alluvium, haulage is by truck down to the skip loading point or up from the bottom to the skip loading point.

Jan 4, 1958

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Y. C. Liu, G. A. Alers

Using X-ray pole-figure information and the single-crystal elastic constants, the angular variation of an elastic modulus in a polycrystal can be calculated and compared to measured clalues. This procedure has been used in the past to provide supporting ecidence for a particular choice of ideal orientations in the description o the X-ray pole figure. Since it is well-known that the absolute value oj an elastic modlus oj a poly crystal cannot be acczrralely calculated from the single-crystal elastic constants, there exists a serious question about the reliability oj this modulus method in the study of textures. This paper deriz-es sez3eral simple fornzulae for the ntzgular lariatiion of Young's modulus in the plane o a rolled sheet sing the same ssuinptions which lead to the lack oj detinztion of the absolute c'alre OJ the elastic ,nodulus. The vesults show that, although the absolute isallre oj Young's modulus depends strongly on the assumptions made, the shape of the modulus vs angle curve is not very sensitive to the assumptions and thus can be used reliably in texture studies. Exatzples oj' using this criteriotz are illustrated in the text. NeARLY all poly crystalline materials have some preferred orientation in the arrangement of their grains and hence exhibit anisotropy in their properties. This preferred orientation is usually measured and studied by X-rays which yield detailed information on the statistical distribution of grain orientations in the form of pole figures. The usefulness of these pole figures in theories of texture formation and in predictions of properties has come to depend almost entirely on the characterization of the pole figure by one or more ideal orientations. Unfortunately, this characterization is not unique and different authors often present different ideal orientations to characterize a given pole figure. In order to distinguish between these different choices of ideal orientations, it is necessary to go beyond X-rays and consider other physical properties which reflect the texture' simply because any choice of ideal orientations must predict correctly the observed anisotropy in all physical properties. The most common example of this procedure has made use of the angular variation of Young's modulus with respect to the rolling direction in the plane of a rolled sheet.3 4 Here the anisotropy can be measured easily and it can also be calculated from the single-crystal elastic constants and the chosen ideal orientation. Unfortunately the methods used to calculate this anisotropy were chosen for their simplicity rather than for their mathematical rigor so that there exists a serious question as to the validity of conclusions reached by this modulus method. It is well-known5 that the absolute value of the Young's modulus of a polycrystalline aggregate cannot be calculated very accurately because different mathematical averages over the grains yield different results. It is one purpose of this paper to examine the effect of different averaging procedures on the calculated anisotropy of Young's modulus in the rolling plane of rolled sheets in order to see if this property can be used reliably in texture studies. This particular modulus and type of material were chosen because the modulus is easily measured and rolled sheet is technologically important. The results show that, although different averages yield different absolute values for Young's modulus, the shape of the modulus vs angle curve is not very sensitive to the averaging procedure and thus can be used as a criterion to check the various ideal orientations used to characterize the X-ray pole figure. Examples of this checking procedure are given in the final section. Another purpose of this paper is to examine the possibility of using the anisotropy of Young's modulus as an indicator of texture without reference to pole figures or ideal orientations. Such a use would require that different textures yield quite different shapes for the modulus vs angle curve so that the distinction between textures would be quite clear. The experimental results presented in the final section indicate that there is easily enough variation in shapes to allow modulus measurements to be useful texture indicators, par-

Jan 1, 1967

By B. Russell, J. R. Tuffley

The stability regions of the normal sulfate and the various basic sulfates of lead in 02-SO2 and PhS-SO2 gas atmospheres were calculated from available thermodynamic data over the temperature range 600o to 1200oC. Roasting experiments were carried out on samples of synthetic lead sulfide at various temperatures and for various roasting times. Compounds in the oxidized surface layers were identified by X-my techniques. The order in which the various reactions occurred was determined by considering the experimental results in conjunction with the thermodynamic calculations. The results of these investigations were applied to the sintering of lead sulfide concentrates, and the extent to which each of the various reactions occurred in a sinter bed was determined. PRODUCTS which may be formed during the roasting of PbS are PbS04, PbSO4. PbO, PbSO4 . 2PbO, PbSO4 . 4PbO, PbO, and Pb.1, 2 The formation of some sulfates has been studied by a number of investigators3-' whose experiments have mostly been confined to the temperature range between 500" and 850°C. Culver, Gray, and spooner3 were able to isolate the reactions which formed PbSO4 and PbSO4. PbO by carefully controlling the compositions of the roasting gases. The kinetics of these reactions were studied within the temperature range 673" to 807°C. Gardner4 and Merrick5 also studied the kinetics of oxidation of PbS. Gardner disregarded the existence of basic sulfates and, as a result, misinterpreted some of his experimental data. Merrick recognized that most of the products of oxidation were mixtures of basic sulfates, but was unable to identify the individual components. Hoschek6 oxidized PbS in air at temperatures up to 800°C. The products were analyzed after roasting had proceeded for some minutes, but no attempt was made to follow the reactions in the initial stages. Consequently, no roasting mechanism was derived. He also showed that PbSO4 and PbSO4 - 4PbO decomposed slowly in air at temperatures in the region of 800°C. The stability regions of sulfates in the temperature range 500" to 850°C have been only partially determined, while practically no information is available for higher temperatures. In the lead sintering process, PbS concentrates are roasted at temperatures within the range 1000o to 1200°C. In order to investigate sulfate formation, it is necessary to determine the effects of temperature and gas composition upon the various oxidation reactions and upon the regions of stability of the various lead sulfates. Kellogg and Basu2 introduced an equilibrium diagram similar to those in Figs. 1 to 3 which provides a convenient medium for represent-

Jan 1, 1964

By Lyman Taylor, Alexander R. Troiano

STUDIES of the transformation of austenite at constant subcritical temperatures have been numerous since the work of Davenport and Bain.1 Considerable information has been obtained on low-alloy steels and on high-carbon alloys containing undissolved carbide or graphite at the austenitizing temperature. Little is known of the isothermal transformation of austenite containing in solution large amounts of both carbon and a single alloying element. In this investigation four steels containing one per cent carbon and with chromium in the range 3 to 9 per cent have been examined with the view to establishing the fundamental character of the isothermal reactions when all carbon and chromium are initially in solution in austenite. EXPERIMENTAL PROCEDURE Alloys The chemical compositions of the steels investigated are given in Table I. The 4 per cent Cr alloy is a commercial steel. The other steels were made by the Carpenter Steel Co. as 50-lb., induction-furnace heats and rolled to 5/8-in. round bars. Bars were softened at 650° to 700°C. before the specimens were cut. [ ] Metallographic Method Most of the lines on the transformation diagrams presented here have been placed on the basis of the microscopic examination of partially reacted specimens. Thees specimens were approximately ½ by ¼ by 1/8 in. in size. Specimens of the 9 per cent Cr steel were held 10 to 12 hr. at 1200° to I225°C. before quenching to the various subcritical temperatures. The other steels were held for 2 to 2 ½ hr. at 1200°C. before quenching. These treatments, carried out in an atmosphere of purified nitrogen, produced an austenite grain size larger than A.S.T.M. No. I, some grains being 1 to 2 mm. in diameter. There were a few undissolved carbide particles in some specimens of the 9 per cent Cr steel. It is believed, however, that any errors in the results due to incomplete solution of carbon and chromium in austenite are negligible; that is, austenite compositions may be considered as being those listed in Table I. X-ray Methods Constituents were identified and martensite axial ratios determined from Debye

Jan 1, 1945

By Gerald Edmunds, M. L. Fuller

The development of "fiber" or preferred orientations, during the plastic deformation of metals, and the relation of such structures to the anisotropic characteristics of worked metals has become a subject of common knowledge among metallurgists. Very little has been published, however, relative to variations existent throughout the cross-sections of rolled strips,1 and the influence that such variations may have. This paper presents such a study on a rolled zinc alloy.2 The significance of small differences in surface structure is shown in relation to bending properties. Experience with zinc and its alloys has shown that the outer radius of the bend, which is subject to tensile deformation, is the common region of failure. In considering relations of structural characteristics to bending properties it will suffice, therefore, to consider the ease and possible extent of tensile deformation resulting from various orientations. It is necessary in this connection to assume that on the average the individual crystals of a polycrystalline material act substantially as if their movements were unobstructed by the surrounding grains. This assumption is not strictly valid, but the error involved is unlikely to affect seriously the qualitative conclusions derived from its use. The mechanism of the plastic deformation of zinc crystals has been described by Mark, Polanyi and Schmid3 and by Mathewson and Phillips14 and is regarded as being accomplished by block movements or * Investigator, Rolling Mill Section, Research Division, New Jersey Zinc Co. f Investigator, X-ray Laboratory, Research Division, New .Jersey Zinc Co. 1 Variations of structure throughout the cross-section of wire have been reported in the literature. 2 This alloy contained, in addition to zinc, 1.0 per cent copper and 0.01 per cent magnesium. Its crystal form is hexagonal close packed, the sarne as that of pure zinc. 3 H. Mark, M. Polanyi and E. Schmid: Vorgange bei der Dehrlung von Zink-kristallen. Zlsch. f. Phys. (1922) 12, 58. 4 C, H. Mathewson and A. J. Phillips: Plastic Deformation of Coarse-grained Zinc. Proc. Inst. Met. Div., A. I. M. E. (1927) 143. C. H. Mathewson: Twinning in Metals. Proc. Inst. Met. Div., A. I. M. E. (1928) 7. The results of a further study of plastic deformation of zinc as related to twin-

Jan 1, 1932

By A. B. Hildebrandt

P. B. Baxendell is to be complimented for an exccllent piece of work. To our knowledge there has been no previous publication of field data on the flow of oil and gas through the annulus of a well. It is certainly gratifying to see this work on annular flow confirm the previous published correlation procedure on tubing flow. It extends considerably the range under which reliable gas-lift calculations can be made. Baxendell discussed this work with us about a year ago and was kind enough to send a large scale plot of his correlation. We had been designing gas-lift installations on flow through the annulus, assuming that the original correlation of the f factor based on tubing flow' was valid as long as we stayed within the same mass velocity range on which the correlation was based. Doing this work necessitated the use of an equivalent diameter for the annular flow. The equivalent diameter is defined as area' of stream cross section wetted perimeter and for the case of an annulus is D, — D,. Substituting this in the basic equation correlating energy loss along with the area to flow required to convert the velocity, to volumetric flow rate, D (Baxendell's Eq. 7) becomes dell's expression, D,). Similarly, the D in 1.4737 X 10 (M&/D) becomes (D, + D;) for annular flow. On receipt of Baxendell's data, we. of course, recalculated it to put it into the form we were using, and to see how well it agreed with the correlation based on tubing flow. Fig. 1 shows the results, which were certainly gratifying. For low values of (D, - D,) pv, the data coincide with the data on flow through tubing, whereas at high values the data on flow through the annuli appear to be leveling off to a constant value. For very high rates of flow where the turbulence is very high, one might expect the value f to level out and become constant. A bulletin published in 1914 by the U. of Wisconsin presented results of a large number of laboratory teats in air lifting water through short lengths of 1.25-in. tubing. It was possible to correlate a random sampling of

By A. W. Hull

The new valves described in this article are the latest product of the Research Laboratories of the General Electric Co. Some of them are still in the laboratory stage, others have already found important applications. Some of the larger ones, which have graduated from the laboratory, are waiting for their apprenticeship in industry, there to refine their frailties and complete their preparation as electrical servants. The career that awaits them, though dimly foreseen, appears fascinating. And as surely as history repeats itself, scenes still more romantic, now beyond the horizon, will unfold as we approach them. This is the romance of science. Counting Electrons Let the smallest tube lead the march of review. It is a special Pliotron, designed to measure currents smaller than any yet detected. It goes by the unromantic name of Pliotron FP-54. Fig. 1 shows this miniature tube—miniature in performance rather than size, for it is the size of an ordinary radio receiving tube. Its appearance has nothing distinctive, except the quartz beads above and below the plate, which support the grid. They minimize insulation leakage. In principle, the FP-54 is like any grid-controlled high-vacuum electron tube; but in structure and operating characteristics it is entirely special. An extra "space-charge" grid, maintained at 3 volts positive with respect to the filament, holds back the small but pernicious current of positive ions emitted by the filament; the normal plate voltage is 6 volts, grid bias 3 volts, thoriated-tungsten filament temperature 1700" K., plate current 40 microamperes. These conditions are essential to the avoidance of grid-currents, which may consist not only of insulation leakage and positive ions from the hot filament and from residual gases, but of high-speed electrons from the filament, photo emission from the grid due to the light of the filament, and electron emission caused by X-rays generated by the impact of electrons on the plate.

Jan 1, 1932

By W. A. Backofen, N. E. Paton

DEFORMATION twinning contributes to the plasticity of titanium and has been reported on {10i2}, {1121},{11221}, {1123}, and {1124} planes.' Twinning on {1011} has also been reported in commercially pure titanium as a result of quenching from 1000', but no reports of such twins occurring as a result of deformation alone are known to the authors. In this study single crystals grown from iodide titanium were compressed parallel to the c axis over the temperature range 25 to 800°C. From it has come evidence that (10il) deformation twins are the most common type between 400" and 800°C. Crystals about 6 mm high with a rectangular cross section measuring about 3 by 4 mm were used in the tests. Chemical analyses showed them to contain 220 to 250 ppm 0 arid 10 to 15 ppm N. The long axes of the crystals were made parallel to the c axis while the sides were parallel to (i100) and (1120), as shown in Fig. 1. The crystals were compressed between polished alumina platens with no lubrication, in a vacuum of 2 x lom5 torr. Between 25' and 300°C the predominant twinning mode was (11221, which is to be expected for this stress state. There was an abrupt change at 400°C, however, and from that temperature up to 800°C twinning took place almost entirely on (10i1 ). Twin planes were determined by the two-surface rnethd. Measurement of the crystal orientation within several (10i1) twins by means of polarized-light4 and transmission electron microscopy showed that the lattice reorientations were the same as those previously reported for the (10i l ) twinning in magnesium.' This reorientation is consistent with The calculated (10il ) twinning shear for titanium is 0.10, while that measured from surface offsets on a (1150) face, which is parallel to the shear direction, was about 0.15. Slip within the twins, or in the matrix adjacent to the twins, probably accounts for the larger measurement. Slip in both locations was judged to have occurred from observations on foils in the electron microscope.

Jan 1, 1970

By Elliott J. Roberts

In spite of the fact that the percentage of true colloids in an ore grind is very small,' these pulps exhibit many of the properties of true colloidal suspensions. A quartz particle, appreciably finer than 10 microns in diameter, has a settling rate so low that at a dilution of 5:l or over, the capacity of a settling tank to settle such particles would be uneconomical if the individual particle rate prevailed. However, by grouping the finer particles into aggregates or flocs, the settling rate can be increased to an economical value. The colloidal chemistry of pulp thickening is thus chiefly concerned with particles having diameters of between 1 and 10 microns, although particles as coarse as 40 microns in diameter are more or less involved. These particles must be associated in such a manner that they settle at an economical rate and give a clear, supernatant liquid or overflow. The treatment of the subject may be divided into three phases, cach phase having a more or less different colloidal aspect. The first phase is the problem of getting the pulp or suspension into the proper condition of flocculence; the second is the behavior of the flocculent pulp in its initial and intermediate stages of settling; the third is the behavior of the flocs in the find period of settling or thickening stage. Let us look first into the methods and mechanism of obtaining the flocs and then consider their behavior and properties. Flocculation Colloids are merely ordinary substances reduced to a very small particle size, the upper limit being placed by definition at 1 micron (0.001 mm.) diameter by the soil chemists and at from 0.2 to 0.1 micron by various other colloid chemists. The lower limit is reached only when the particles approach molecular dimensions. The term L'colloid" should not necessarily imply lack of crystallinity. Particles as small as 0.01 to 0.02 micron give perfect X-ray patterns, while with 0.005 micron particles the bands on the powder photograph are merely broaderled and diffused.2

Jan 1, 1935

By Allen H. Rogers

It has always seemed to me that there is a certain similarity between the work of the mining engineer and that of the doctor of medicine — each has very often to be governed in his actions by conditions which he cannot see. It is not necessary to detail the unseen conditions with which the mining engineer or geologist has to deal—the further extension of ore-bodies, the existence of new ones, the throw of a fault, the probable change in grade' or character of the ore with advance of the workings, are a few of the conditions which the mining engineer has to determine as well as he can from the deductions he is able to make from what he can observe. Just so the physician is often confronted with conditions that he can not observe. Probably less than half of human ills make a manifestation at the surface of the body from which definite and certain conclusions can be drawn. The diagnostician must observe various things and, from these observations in combination, conclude what his course should he to bring about the cure of the trouble. Both professions would be assisted immensely by any agency that would permit them to look below the surface, something that would make more certain the diagnosis which each is called upon to make. The physician has had such an agency since 1895, when Röntgen discovered the X-ray; which, by making possible shadowgraphs of the osseous portion of the human body, advanced immensely the diagnosis of bone lesions Later, with improvement in the technique and more understanding in the interpretation of what the photographic plate shows, other portions of the human anatomy could be examined and at the present time there is hardly an instance of internal disorder to which the aid of the X-ray is not called. Some organs are made opaque by administering mineral substances; in other cases, conclusions are drawn from barely perceptible shadows on the photographic plate. Generally the surgeon's knife is directcd with exactitude to the seat of the trouble and so not only is the difficulty revealed but the necessity for an exploratory operation is averted. What the X-ray is to medicine and surgery, geophysical prospecting methods are to the mineral industry. They give the mining engineer and geologist information regarding subsurface conditions which otherwise

Jan 1, 1929

By H. L. Luo, W. Klement

By rapidly quenching Ag-Pt alloys from the melt, a continuous series of solid solutions has been obtained. At equilibrium''2 these fcc elements form a peritectic system, Fig. 1. Weighed amounts of silver and platinum powder (325 mesh, purity greater than 99.9 pct) were mixed for 24 to 120 hr, pressed into compacts, sintered at 1000°C in a hydrogen atmosphere for at least 16 hr, and then furnace-cooled. Because of the difficulty in achieving homogeneity in alloys containing more than about 40 at. pct Pt, the sintered compacts were induction-melted under hydrogen in alumina crucibles and then cold-rolled into wires. Small amounts ("30 mg) of alloys cut from various sections of the sintered compacts or rolled wires were heated to at least 50' ~ above the liquidus in an alumina insert held within an induction-heated graphite crucible; then the molten alloy was ejected by a blast of helium onto a lightly polished copper strip held on the inner periphery of a rotating wheel. The flakes thus obtained were typically 1 sq mm in area or often slightly larger for the silver-rich alloys. X-ray diffraction patterns were obtained with nickel-filtered copper K radiation in a 114.6-mm-diam Debye-Scherrer camera with rotated specimens. Lattice parameters and associated uncertainties were estimated from extrapolations against the Nelson-Riley function. High-angle lines were always resolved and spacings were computed relative to r(CuKa!,) = 1.540508 The details of these techniques have been discussed previously.s'6 Lattice parameters of the solid solutions are plotted in Fig. 2, together with the data of Schneider and Esch,' Johansson and Linde,' and Novikova and pudnitskii. Each of the present lattice spacings represents two or more independent determinations. The alloys were homogeneous within 2 at. pct of nominal composition as estimated from the uncertainties in the lattice spacings. Many of the mechanisms involved in the achievement of metastable solid solutions by rapidly quenching from the melt have been previously discussed. There is some evidence" that such solid solubility cannot be obtained when the liquid alloys are cooled

Jan 1, 1963

By T. C. King

AT the new Graham-Central Mill of Eagle-Picher, near Galena, Ill., material is simultaneously dewatered and introduced into the ball-mill scoop boxes by the use of variable-speed, 24-in. spiral classifiers. This arrangement has proved satisfactory in that the moisture content of the wet feed is reduced, thus allowing maintenance of density within the mills, and a constant feed at any desired rate to the mills is provided. In this mill the primary feed is wet crushed to minus 1/2 in. and preconcentrated by jigs to produce a bulk lead-zinc-iron concentrate and a waste tailing. The jig concentrate is then dewatered by a conventional dewatering classifier and stored in bins ahead of the ball mills. Even though this material is well dewatered, the discharge at the bin bottom is sloppy because of the gradual drainage of the water from the surface of the particles. Conventional belt feeders with vertical cutoff gates are unsatisfactory because of the flushing characteristic of the wet sand. The new installation employs 24 in. x 10 ft, 9-in. Simplex double-pitch spiral classifiers for feeders from the bin bottoms to the ball mill scoop boxes (fig. 1). These units are arranged with straight tanks and are driven by 5 hp motors through a U. S. Vari-Drive to provide a 4 to 1 speed ratio. Each bin discharges through a chute into the rising side of the spiral. The flushing characteristic of the material from the bottom of the bin is utilized to maintain a steady feed. A small amount of water tapped into the bottom of the bin insures uniform feed to the classifier. Excess clear water drains over the weirs. Feed rate to the mills is controlled by the variable-speed drives. The feed delivered by the spiral at a given speed setting is relatively dry, uniform, and steady, and as such is easily controlled by the operator. The classifiers are set on a pitch of 5 in. per ft and have a sand-raking capacity of from 8 to 32 tons per hr. It is believed that the solution of this problem offers possibilities for the storage of deslimed rod-mill sands and other similar products of the industry.

Jan 1, 1951

By T. C. King

AT the new Graham-Central Mill of Eagle-Picher, near Galena, Ill., material is simultaneously dewatered and introduced into the ball-mill scoop boxes by the use of variable-speed, 24-in. spiral classifiers. This arrangement has proved satisfactory in that the moisture content of the wet feed is reduced, thus allowing maintenance of density within the mills, and a constant feed at any desired rate to the mills is provided. In this mill the primary feed is wet crushed to minus 1/2 in. and preconcentrated by jigs to produce a bulk lead-zinc-iron concentrate and a waste tailing. The jig concentrate is then dewatered by a conventional dewatering classifier and stored in bins ahead of the ball mills. Even though this material is well dewatered, the discharge at the bin bottom is sloppy because of the gradual drainage of the water from the surface of the particles. Conventional belt feeders with vertical cutoff gates are unsatisfactory because of the flushing characteristic of the wet sand. The new installation employs 24 in. x 10 ft, 9-in. Simplex double-pitch spiral classifiers for feeders from the bin bottoms to the ball mill scoop boxes (fig. 1). These units are arranged with straight tanks and are driven by 5 hp motors through a U. S. Vari-Drive to provide a 4 to 1 speed ratio. Each bin discharges through a chute into the rising side of the spiral. The flushing characteristic of the material from the bottom of the bin is utilized to maintain a steady feed. A small amount of water tapped into the bottom of the bin insures uniform feed to the classifier. Excess clear water drains over the weirs. Feed rate to the mills is controlled by the variable-speed drives. The feed delivered by the spiral at a given speed setting is relatively dry, uniform, and steady, and as such is easily controlled by the operator. The classifiers are set on a pitch of 5 in. per ft and have a sand-raking capacity of from 8 to 32 tons per hr. It is believed that the solution of this problem offers possibilities for the storage of deslimed rod-mill sands and other similar products of the industry.

Jan 1, 1951

By P. M. Kelly, E. P. Butler

Four Mn-CLL alloys, containing 60, 70, 80, and 90 pct Mn, respectively, have been examined in the quenched and the quenched and aged conditions using electron microscopy and electron, neutron, and X-ray diffraction. After certain heat treatments the alloys transform from fee to fct and in the tetraom1 condition show a domain structure parallel to {101} planes. Neutron diffraction indicates that the domains are antiferrornagnetically ordered. The domain boundary contrast has been examined using bright- and dark-field microscopy, and the contrast effects observed under favorable conditions have been used to deduce the c axis orientation in each domain. The domains are extremely mobile and can be nucleated at precipitate particles and screw dislocations. The domain mobility is responsible for the high damping capacity. In the aged material a Mn precipitates in the Kurdjumov-Sachs orientation and results of both electron microscopy and neutron diffraction indicate that the matrix separates into two components—one rich in manganese and the other rich in copper. ALLOYS of manganese and copper have the unusual combination of a high damping capacity and good mechanical properties and have been the subject of a number of investigations as part of a general interest in high damping capacity alloys for engineering purposes.&apos;,&apos; SO far, however, there has been no reported electron metallographic study of these alloys. The Mn-Cu system has an extensive range of solid solubility at high temperatures, and the equilibrium phases are expected to be y (fee) and a Mn. The high damping capacity is associated with a metastable tetragonal structure of variable c/a ratio, which forms from the high-temperature y phase. This latter phase becomes more difficult to retain as the manganese content increases, and alloys containing more than 82 wt pct Mn undergo a reversible martensitic fcc — fct transformation on quenching. The X-ray work of Basinski and christian3 showed that the Ms temperature for the transformation was below room temperature for alloys in the range 70 to 82 pct Mn and increased linearly with manganese content. When quenched from the y region, alloys in the range 50 to 82 pct Mn are cubic at room temperature, but become tetragonal if aged at temperatures between 400" and 600°C. The martensite transformation occurs on cooling from the aging temperature. Tetragonal alloys have a banded microstructure and the bands analyze to be traces of (110) planes. Similar microstructures have been observed in In-Tl4 and in other manganese-base systems, such as Mn-Au5 and Mn-Ni.6 The mobility of the bands in Mn-Cu alloys can be demonstrated by optical examination of a polished specimen surface subjected to a cyclic stress.7 The bands appear and disappear as the stress is varied, and X-ray measurements of the (200,020) and (002) peak intensities confirm that a reversible reorientation of the tetragonal structure occurs. Meneghetti and sidhu8 investigated the magnetic structure of Mn-Cu alloys and found antiferromagnetic ordering in furnace-cooled alloys of composition >69 at. pct Mn. Magnetic super lattice reflections occurred at the (110) and (201) positions and the proposed structure was fct with the spins along the c axis. A more complete investigation by Bacon et al.9 confirmed this structure. The magnetic ordering temperature Tn was found to increase linearly with manganese content in the same way as the Ms temperature, and at any composition, Tn > Ms. This relationship suggested that the magnetic ordering was responsible for the cubic — tetragonal transformation in the manganese-rich alloys. The purpose of this investigation was to study the mechanism of high damping and the structural changes that occur on aging. The main technique used was transmission electron microscopy, but X-ray and neutron diffraction experiments were also carried out. EXPERIMENTAL Materials and Heat Treatment. The four alloys, provided by the Admiralty Materials Laboratory. were of nominai composition 60, 70, 80, and 90 Mn and all had low impurity levels, <0.05 pct C, <0.2 pct Fe. This material was cold-rolled to 200-µ strip with intermediate annealing and then given a final heat treatment of 24 hr in the range 800° to 900°C followed by water quenching. An identical heat treatment was given a length of 3/4-in.-diam bar of the 70/30 alloy from which the neutron diffraction specimens were machined. It was suspected that the tetragonal structures would be metastable at room temperature, and so the alloys were not aged until required for experiments. After aging in a salt bath the alloys were water-quenched. Thin Foil Preparation. Initial thinning to 50 to 75 µ was possible in a solution consisting of: 50 ml nitric acid 25 ml acetic acid 25 ml water The surface deposit and grain boundary etching was removed by a final electropolish at around 20 V in an electrolyte consisting of:

Jan 1, 1969

By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,&apos; indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1&apos;, following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By Robert Mehl

THE importance of the Widmanstätten structure to structure theory in metallography has been recognized by many writers.1 It is a structure produced by the precipitation of a new phase from a solid solution upon cooling as a result of changing solid solubility, and displays a characteristic appearance indicating a crystallographic relationship between the new phase and the original solid solution (Fig. 1). First discovered in 1808 by Alois de Widmanstätten2, the structure has been traced by analogy through many alloy systems. Particularly is this true of the steels. Sorby&apos;s classic work3 on the microstructure of iron and steel was in essence an attempt to explain the origin of this characteristic structure in meteoric iron. He observed in a Bessemer steel and in a cast-steel ingot structures which we now recognize as typical Widmanstätten figures.4 Osmond5 observed structures in a steel ingot analogous to those found in meteorites. Arnold and McWilliams6 obtained (and recognized) a

Jan 1, 1930