By Carl F. Floe, John Chipman

THE system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or C02 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modem metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100° to 1500°C., and pressures from about 20 mm. of mercury to somewhat above atmospheric. REVIEW OF PREVIOUS WORK The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as 02, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: [2M -}-G2 = 2MGK =G) IYf X[I]] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: [MG = Ki Pa,[2]] Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: [6Cu + S02 = Cu2S + 2Cu20[3] K Cu2S X (Cu20)2(Cu)e(Psm)[4]] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: [K1 =or Vdo,= K2/PBO [5] PsO]

Jan 1, 1941

By Roy C. Kirkman

Dear Editor: It is with great pleasure that I read Mr. Howard M. Wells article in the December 1978 issue of MINING ENGINEERING entitled: "Optimization of Mining Engineering Design in Mineral Valuation." Mr. Wells very adequately presents the case and point that there are a great number of variables which must be analyzed during an economic evaluation of an FUND RESOURCE, such as copper or uranium. I wish to take this opportunity to suggest that, given today's economic climate, decision making takes place under conditions of uncertainty and that this uncertainty justifies our need to examine each one of the parameters entered into the evaluation model. It is my contention that the influence of the tonnages and grades as well as their distributions, have the most profound effect upon the results of an evaluation. Everyone concerned with the evaluation of FUND RESOURCES realizes that as metal prices decline or stagnate with sharply rising direct operating costs, cutoff grades (Gc) must increase according to the equation below which Mr. Wells uses: Gc = Total Operating Cost/(Market Price X 20 X Recovery) However, historically, we have seen cutoffs move dramatically lower in both the copper and uranium industries for the past decade. Henceforth, this established the metals industry most important argument for processing greater tonnages of lower grade materials from disseminated deposits (refer to paper by Kirkman, Roy C.). These disseminated deposits, created by either concentration processes (uranium) or dispersion processes (copper, gold, molybdenum), have log-normal grade distributions (Fig 1). Gross profits are rising, but unit profits are falling. The industry has created longevity through economy of scale, i.e., mining vast tonnages of low grade. In order to develop the great tonnages necessary to prove economic viability, we must examine alternatives at the low-end of the tonnage grade relationship. Notice from [Fig. 2] that as we move further to the right away from line A-B drawn tangential to the average grade curve at 45°, total profits will increase (given fixed annual production capacity) and unit profits decrease. The theoretical optimum operating point is where: [ ] At this point my observation is that slight shifts in production capacity bring about greater changes in profitability due to greater grade changes. Therefore, the best financial risk evaluation is obtained by totally revising the mining engineers methods and fixing the financial parameters such as discount and interest rates. A 10% shift in either of these two parameters will not cause near the same variance in economic viability as will a change on the GRADE-TONNAGE curve [(Fig. 2)].

Jan 1, 1980

By Clarence Zener

THE internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites,4,5 localized weak regions introduced by cold-working,6,7 grain boundaries and possibly twinning planes.8.9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, 3-s in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff.10 EXPERIMENTAL METHOD The experimental method used has previously been described in Institute papers.5,6.9 The measure of internal friction adopted here, I/Q, is (p) X the logarithmic decrement, a measure used by some writers, and is also (I/2p) X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the fundamental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. EXPERIMENTAL RESULTS The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°°C. As shown in Fig. i, the internal friction increased by only a factor of 2 from room temperature to 300°°C., then by a factor of 100 during the next :too' interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction ~ e-HI/RT [I]

Jan 1, 1942

By Clarence Zener

The internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites, localized weak regions introduced by cold-working,6'7 grain boundaries and possibly twinning planes.8'9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, 3.i in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff. Experimental Method The experimental method used has previously been described in institute papers.5'6'9 The measure of internal friction adopted here, I/Q, is X the logarithmic decre- ment, a measure used by some writers, and is also X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the fundamental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. Experimental Results The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°C. As shown in Fig. I, the internal friction increased by only a factor of 2 from room temperature to 300°C., then by a factor of 100 during the next Ioo° interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction e-H/RT [I]

Jan 1, 1943

By Clarence Zener

The internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites, localized weak regions introduced by cold-working,6'7 grain boundaries and possibly twinning planes.8'9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, 3.i in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff. Experimental Method The experimental method used has previously been described in institute papers.5'6'9 The measure of internal friction adopted here, I/Q, is X the logarithmic decre- ment, a measure used by some writers, and is also X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the fundamental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. Experimental Results The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°C. As shown in Fig. I, the internal friction increased by only a factor of 2 from room temperature to 300°C., then by a factor of 100 during the next Ioo° interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction e-H/RT [I]

Jan 1, 1943

By Donald E. Crowell

In the fall of 1969, ASARCO and Newmont Mining Co. began the design of the 700tpd concentrator at their Black Cloud shaft located near Leadville, Colo. The concentractor would treat by flotation a Pb-Zn-Ag ore containing minor gold values. Flowsheet design was based on laboratory test work performed at the Minerals Research Testing Laboratory of ASARCO. Since the concentrator is located at an elevation of 11,000 ft, cold weather was a major factor in design considerations. The original capacity was designed as 700 tpd but for various reasons an ultimate capacity of 1,000 tpd was desired. This necessitated special consideration in the design of several areas, particularly the grinding circuit. The grinding circuit chosen was a single 9 X 12 ball mill operating in closed circuit with one 20-in. cyclone. The ball mill will operate at low speed and as an overflow type originally. The mill can be speeded up and converted to grate type for handling the larger tonnage when required. Thickeners and filters were oversized and space was left for additional flotation cells in order to handle the increased tonnage in these areas. Pumps were sized so that they could handle the increased tonnage by increasing their speed. Construction began in May 1970; the Black Cloud concentrator went on-stream in April 1791.

Jan 1, 1974

By Eric Jette

The nickel-chromium alloys form the base f for many industrial heating alloys, so that this system is of considerable practical importance. The literature on these alloys, however, contains much conflicting evi-dence, not only regarding the solubility limits of the terminal solid solu-tions at different temperatures but even regarding, the number of phases existing in the system. Part of the difficulty undoubtedly arises from the fact that chromium of sufficiently high purity has been available only during the last few years. A second and possibly even more impor-tant difficulty arises from the ease with which chromium reacts with silicon and carbon compounds and the atmosphere to form silicides, carbides, nitrides and oxides. Pilling and kihlgren1 in 1929 reviewed the existing scanty information. They did not consider the diagram by which they summarized the various bits of information to be entirely satisfactory. Matsunaga2 investigated the system by thermal analysis, microscopic examination and other means. Electrolytic nickel of 99.9 per cent purity and thermit chromium containing 0.30 per cent al, 0.40 per cent fe, 0.25 per cent si and 0.04 per cent c were used. A tammann furnace with hydrogen flowing through it was used for melting. Sekito and matsunaga3 reported an x-ray, investigation presumably on these same

Jan 1, 1934

By Keith E. Robinson, Brian Stimpson

INTRODUCTION In inclined sedimentary strata slope failure may occur by sliding along bedding and along a discontinuity or weak zone, as illustrated in Fig. 1. This mode of failure may be called 'bi-linear', as the failure surface is comprised of two linear or approximately linear segments. This type of failure has been suggested for the famous Frank Slide, Alberta, Canada (Cruder and Krahn, 1973) in which an estimated 90 M 5 tons (8.97 x 10 MN) of rock separated from Turtle Mountain and buried the town of Frank. Also, with the increasing depth of open pits and the construction of highways through inclined sedimentary strata this mode of failure is of major concern to the rock slope stability engineer. A computer program for calculating factors of safety for this slope failure mode is provided and includes the ability to vary shear strengths of potential slide surfaces, ground water elevations and wedge geometry. LIMITING EQUILIBRIUM MODEL The simple limiting equilibrium model used in the analysis is shown in Fig. 2. It is assumed that jointing is orthogonal to bed- ding and that the interface between the upper and lower wedges there- fore corresponds to a joint plane or planes. No shear strength is attributed to the interface so that the resultant force, P, from the upper wedge acts normally across the interface. The normal loads

Jan 1, 1983

By S. R. B. Cooke, R. O. Huch, C. S. Chang

IN the flotation of iron ores laurylamine derivatives have been used for considerable time.1, 2' To effect satisfactory separation of the gangue, pre-dominantly silica, from the iron oxide minerals, the addition of specific depressants for the iron oxides has been found necessary. Starches and starch products have been used for this purpose.V here is, however, very little published information on the effects of these materials and other variables on this process. In some cases it has been found that prior acid scrubbing and desliming are essential," and depending upon the efficiency of the subsequent washing step, there will be accompanying changes in pH. It was the object of this investigation to test and observe the effects of the above factor as well as to examine and compare the action of various starches and starch products. Ore Preparation The ore used in this experiment was a wash-ore tailing obtained from the western Mesabi range. Microscopic examination and x-ray analysis of the ore showed it to consist of hematite, goethite, and quartz. Physical properties of the iron minerals ranged from hard and crystalline to earthy and ocherous. The quartz grains were discolored either because of iron-oxide inclusions or because of a sur-face coating of iron oxide. The ore assayed 27.52

Jan 1, 1954

By J. L. Stokes, L. J. Demer

It has recently been shown' that epitaxial films of silicon carbide deposited on silicon single crystals possess desirable properties for semiconductor applications. There is one apparent disadvantage to such a system, however; since epitaxial deposition is a high-temperature process, it can result in plastic deformation of the silicon substrate. The accompanying Berg-Barrett X-ray diffraction photographs reveal plastic deformation in two silicon semiconductor crystals which occurred when the crystals were coated with an epitaxial layer of silicon carbide at 1150°C. Due to differences in thermal expansion between the silicon substrate and the epitaxial silicon carbide, the silicon was subjected to stresses while still in the plastic temperature range. Both crystals shown were 0.7 in. in diam and 0.0055 in. thick. The crystals were sliced from a larger crystal so that their polar axes were parallel to the [ill] direction. After cutting, the crystals were polished with diamond paste, and etched in HC1 vapor to remove surface damage re- sulting from the cutting and polishing operations. This provided clean, damage-free surfaces on which to deposit the silicon carbide. Figs. l(a) and l(b) are reflection and transmission photographs, respectively, of the same crystal. A smaller portion of the crystal is shown in the transmission geometry, because a vertical slit was

Jan 1, 1965

By E. Alan Haley

Accurate and economic control of line and grade on long tunnels, large structures, excavations and waterways has been a problem to surveyors and engineers for decades. The conventional method of surveying, incorporating a level, transit and a number of surveying technicians, has proven to be a very expensive and time-consuming operation. Now, however, engineers have adapted the laser to help ease the problems of surveying, at the same time increasing the efficiency of such operations. The laser, which projects a continuous, narrow red beam of brilliant light, provides a constant alignment reference that does not interfere with personnel or equipment. A complete laser alignment system, specifically designed for and suited to a variety of mining and tunneling operations, has been developed by the Perkin-Elmer Corp. The engineering significance of this development can be fully realized when it is noted that, aside from potentially tremendous economic advantages in terms of labor savings, the laser beam provides a system of alignment that is at least ten times more accurate than presently used optical systems. The new laser system provides accuracies within 10 microinches per foot (1 x 10-5in.) when used with an accessory centering detector. In one of its first field trials, the laser was used for alignment of a two-mile tunnel which showed a total deviation of less than 5/8 in.

Jan 4, 1968

By Cyril Smith

SOMEWHAT over ten years ago the author described studies1,2 on the constitution of the copper-silicon system. The copper-rich portion of this diagram is shown in Fig. 1. The experimental points freely dotted about the diagram seemed to justify an otherwise unconvincing diagram and for several years the curious reverse bend in the alpha-phase bound-ary was accepted as substantially correct, even by later investigators3,4 of the system who introduced changes in the high-silicon phases. The binary diagram has been used as a base for several ternary systems" without any suggested changes. Voce10 suspected the existence of another phase from his study of the cast alloys in the copper-manganese¬silicon system, but evidently hesitated to extrapolate this to the binary diagram, particularly in view of the too ingenious explanation that was advanced" to account for the pools of constituent clearly visible in castings; namely, that they were secondary alpha of twinned orientation deposited from beta. Von Schwarz,12 in 1932, called attention to the fact that this micro-constituent in copper-silicon alloy castings was anisotropic under polar-ized light and asserted that a new phase, not cubic, should be placed in the diagram adjacent to alpha. Sautner,13 on the basis of investigations with the polarizing microscope and with X-rays, introduced this phase into the diagram at about 6 per cent Si. The relevant part of his dia-gram is shown in Fig. 2. Sautner called the new phase beta, renaming the old beta phase zeta. To avoid confusion, in redrawing Fig. 2 the phases have been renamed in accordance with the terminology adopted in the present paper, in which the new phase is called kappa and the other phases retain the designation given them by Arrhenius and Westgren.4

Jan 1, 1939

By W. D. Robertson, H. Conrad

Incremental loading creep tests were conducted on magnesium single crystals in tension and direct shear at 78" to 364°K. The creep curves were transient in character and exhibited waves or periodic behavior, especially at small strain rates. A sigmoidal curve was frequently observed following the first occurrence of creep. Repeating of segments of a master curve was observed at all temperatures indicating that identical conditions for flow existed after various stress and strain histories. A logarithmic time law with a independent of temperature whs observed at 78°and 203°K, while a parabolic (power) time law was approximated at 298" and 364°K. The departure from logarithmic creep was attributed. to recovery, which was observed at 298" and 364°K. The temperature independence of a represents a serious objection to the theory of low-temperature creep based on the intersection of dislocations. IN a previous paper1 it was found that the initial creep rate of magnesium single crystals, y, following the addition of a stress increment in the range of 78° to 364°K, was given by the expression ? = C exp - {?H/kT} exp {B(T- h ?)} [1] where B and C are constants, AH is an activation energy of 10,300 cal per mole, T is the applied stress, ? is the total strain at the time of the stress increment, and h is the strain-hardening coefficient. The present paper is concerned with certain other features of creep behavior observed during this investigation; namely, the form of the creep curves, time laws for creep, recovery, and microscopic and X-ray observations of the structural manifestations of the creep flow. To the authors' knowledge the temperature range of the present investigation (0.08 Tm to 0.40 Tm) has not been covered previ-

Jan 1, 1959

By S. H. Gelles

Samples of poly crystalline zinc of 99.999+ pct purity were observed metallographically after having been exposed to hydrostatic pressures of up to 27 kbars. The deforrnation produced by this treatment was analyzed using X-ray and metallogaphic techniques. Basal-plane slip occurred universally in all grains exumined at the lowest pressure used (8 kbars). At pressures of >23 kbars, {1012} twin nucleation and growth were noted as well as slip. Formation of bend planes, complex kink bands, and recrystallization at the gain boundaries were also observed in this pressure range. These observations are discussed in reference to the expected deformation behavior of zinc under high hydrostatic pressure. It has been shown over the past few years1'3 that anisotropic, poly crystalline metals can be made to deform plastically by the application of a hydrostatic pressure. The effect is greater 1) the larger the anisotropy of linear compressibility and 2) the smaller the stress level needed to produce plastic deformation. Zinc having both very anisotropic linear compressibilities and a very low critical resolved shear stress (CRSS) for basal-plane slip has been shown to exhibit large amounts of plastic deformation when subjected to a hydrostatic pressure.2,3 At pressures up to 15 kbars, grain boundary migration and slip on one set of glide planes have been reported.' After exposing samples to 20 kbars pressure, grain boundary migration, single slip, multiple slip, and twinning have been noted.' The identification of the deformation modes operative under these conditions has not been reported. It was the purpose of this research to identify the deformation modes induced in poly crystal line zinc by the action of a hydrostatic stress and to study the strain accommodation at grain boundaries. Hydrostatic pressure could affect the operational modes of deformation by altering the Peierls-Nabarro stress. This may be roughly approximated by the relationship4

Jan 1, 1967

By Laurence Hicks

CONSIDERATION of the past work on the subject of the diffusion of chromium into iron suggested that additional information might be given by the use of X-ray spectroscopy in following the concentration changes through the diffusion zone. Grübe and Fleischbein1 packed rods of electrolytic iron in a mixture of alumina and chromium. These specimens were heated in an atmos-phere of purified hydrogen for varying lengths of time. After treatment the specimens were examined metallographically and showed the usual structure, consisting of a border of radially oriented columnar grains ending in a sharp boundary line. Reference is made to the fact that etching with certain reagents will attack only the material inside the border of columnar growth and also to the fact that polishing seems to develop a ridge at the position of the boundary between the etched and unetched areas. By chemical analysis of thin layers turned off on a precision lathe, the authors were able to obtain depth-concentration curves. These curves, reproduced in Fig. 1, show that 'in most cases a pronounced change of slope occurs, corresponding to the position of the boundary of the columnar grains. In a later paper Grübe extends his work to other systems which show the same characteristics.2 He concludes that the reason for the break in the curve is that a hindrance of diffusion occurs at the place where the regularly oriented grains of the diffusion zone meet the random grains of the interior portion, on the assumption that the diffusion velocity in one direction in a grain may be greater than in another direction, and that the grains in the diffusion zone orient themselves so as to give the maximum diffusion rate. Kelley3 points out that Grübe has failed to note that the boundary line does not consistently cross all grains and

Jan 1, 1933

By M. Friedman

Applications of rock mechanics to the design of engineering structures in rock involve the assumption that the stresses are due entirely to the present applied loads. For instance, it is assumed that the vertical normal stress in undisturbed rock free of topographic effects is equal to the weight per unit area of the overburden. In fact, vertical dilatational strains associated with stresses of more than 100 times the present overburden pressure have been measured by strain-relief methods on outcrops. 1,2 The notion of residual strain (stress) or latent stress3 seems unassailable; and indeed this has long been recognized by metallurgists. It is difficult, however, to assess the residual component of the in-situ state of elastic strain with conventional strain relief methods employed in mines or down boreholes. That is, in principle, the in-situ state results from the superposition of present applied loads (natural or man- induced) and potentially recoverable elastic strains (stresses) that exist in a given volume of material even though there are no external forces across the boundaries of the body (Voight,4 and Fig, 1). Accordingly, only in unloaded blocks can the true residual strains be measured by strain relief methods. Using X-rays, the elastic strains locked within the quartz grains or crystals of a rock can be measured. These strains are known to persist even when the rock is reduced to small chips but to vanish when the rock is disaggregated and the grains are powdered. Although we have just begun to investigate the mechanisms by which the strains are stored (see Preliminary Results), we believe that "pressure solution'' at grain boundaries, secondary cementation under load, permanent ("plastic") deformation, and temperature changes are possible processes. In any event, in our study of naturally deformed rocks, it is significant that we are work-

Jan 1, 1972

By Laurence C. Hicks

Consideration of the past work on the subject of the diffusion of chromium into iron suggested that additional information might be given by the use of X-ray spectroscopy in following the concentration changes through the diffusion zone. Grube and Fleischbeinl packed rods of electrolytic iron in a mixture of alumina and chromium. These specimens were heated in an atmosphere of purified hydrogen for varying lengths of time. After treatment the specimens were examined metallographically and showed the usual structure, consisting of a border of radially oriented columnar grains ending in a sharp boundary line. Reference is made to the fact that etching with certain reagents will attack only the material inside the border of columnar growth and also to the fact that polishing seems to develop a ridge at the position of the boundary between the etched and unetched areas. By chemical analysis of thin layers turned off on a precision lathe, the authors were able to obtain depth-concentration curves. These curves, reproduced in Fig. 1, show that in most cases a pronounced change of slope occurs, corresponding to the position of the boundary of the columnar grains. In a laler paper Grube extends his work to other systems which show the same characteristics.~ He concludes that the reason for the break in the curve is that a hindrance of diffusion occurs at the place where the regularly oriented grains of the diffusion zone meet the random grains of the interior portion, on the assumption that the diffusion velocity in one direction in a grain may be greater than in another direction, and that the grains in the diffusion zone orient themselves so as to give the maximum diffusion rate. Kel1ey" points out that Grube has failed to note that the boundary line does not consistently cross all grains and

Jan 1, 1934

By G. C. Gould

The nature of freckle segregation is determined by chemical analyses, microradiograplzy, and electron microprobe. In addition, the influence of chemistry variation on freckle formation is studied in laboratory experiments. It is demonstrated that controlled laboratory solidification can produce freckle segregation. "FRECKLE" segregation is a discontinuous, rod-like segregation observed in vacuum consumable -electrode ingots. Figs. 1 and 2 show this segregation as pencil-like, dark etching areas of segregation found in longitudinally and transversely sectioned consumable-electrode ingots. In most cases the segregation is perpendicular with respect to gravity and parallel to the longitudinal axis of the ingot. The segregation is most often encountered at or around midradius in large vacuum consumable-electrode ingots. The austenitic alloys, A-286* and 718, † have shown particular susceptibility to this mode of segregation. The origin of these rodlike pockets of segregation is not well-understood. It has been suggested that the segregation is a result of a portion of the electrode dropping off and passing through the arc un-melted. On the other hand, smeltzer1 has demonstrated the freckle segregation in A-286 to be comprised of low-melting constituents relative to the matrix melting point. The discontinuous nature of the segregation is the most perplexing facet of the freckle-segregation problem. It was to gain some insight into this part of the problem that this work was undertaken. I) PROCEDURE At the outset of the work identification of the phases present and the elements concentrated in the freckle areas was undertaken. The electron micro-probe was used to determine general enrichment as well as -specific phase chemistry. Microradiography using cobalt and chromium radiation was also used on the freckle areas again to determine the elements involved in the segregation. X-ray diffraction patterns were made from portions of these same foil specimens. Optical microscopy and Knoop hardness measurements were also used

Jan 1, 1965

By J. L. Rodda, M. L. Fuller

In connection with an investigation in this laboratory on the high-zinc side of the copper-zinc system, it was observed that well developed segregate structures of the Widmansttten type were formed when a secondary phase precipitated from the solid solution of copper in zinc. This paper presents an analysis of the crystallographic relationship between the segregate and the solid solution matrix. The data to be presented are an interesting addition to the literature on segregate structures in that the plane of segregation is one of the less densely populated planes. In agreement with the generalization of C. H. Mathewson and D. W. Smith' the plane of segregation in the matrix contains the direction of closest atomic packing of the lattice. Furthermore, the matrix and the segregate are both hexagonal close-packed, which has not been reported hitherto in the 1iternture.l The increasing commercial importance of zinc alloys containing copper makes this fundamental study of value to the metallography of zinc alloys. Zinoeich Copper-zinc Alloys Copper enters into solid solution with zinc to at least 1.8 per cent at 400" C., according to W. M. Peirce.3 The solubility is less at lower temperatures. Thus a solid solution of copper in zinc, saturated at an elevated temperature, will precipitate the excess copper in a separate phase at a lower temperature, conditions of concentration, time, and temperature being suitable. The nature of these two phases has been established by the X-ray method of crystal analysis. Westgren and Phmgmén4 and also Owen and Preston5 have shown that the solid solution eta (7) is of the substitu-tional type with copper atoms replacing zinc atoms on the hexagonal

Jan 1, 1933

By C. F. Quest

THE steel industry has a definite need in its tonnage mills for a formula relating expected tensile strength to the analysis of the steel. The McWilliam-Barnes1 and other less comprehensive formulas are used for this purpose, but these formulas were designed for an analysis range that does not include the medium manganese and silicon-bearing steels. This type of steel is being produced to meet the demand for tensile strength slightly higher than that of ordinary structural steel but not high enough to justify expensive alloy steels. The purpose of this paper is to present a somewhat more compre-hensive formula based on data accumulated over a number of years by the Inland Steel Co., and to discuss the method followed in obtaining a formula to fit the data. The resultant formula admittedly is still weak in some respects, but for the expanded analysis range appears to be an improvement over the other formulas. It is hoped that with the collec-tion of more data and possible collaboration with other mills studying this problem it will be possible to work out a more nearly perfect formula. Several publications have been issued on this subject. In some, the equation type of relation was evolved while others made a combina-tion of tables and an equation. The latter include work by Campbell2,3 and Webster.4,5 Campbell classified the steels as acid and basic and applied a different formula to each. For basic steels, he used the equation: Tensile strength = 41500 + 770C + 1000P + yMn [1] y was a variable depending on the carbon and manganese content of the steel and was listed in tables, Webster investigated acid Bessemer steel and developed the equation Tensile strength = 38000 + 800C + xP + yMn [2]