By J. B. Newkirk

IN 1939 Bitter and Kaufmann1 suggested that iron, precipitating from a copper-rich, Cu-Fe solid solution, appears initially as coherent particles of r-Fe which transform to the body-centered-cubic form of iron when the alloy is cold worked. Since then there has been considerable discussion, supported only by indirect evidence, regarding the validity of the concept. For example, Reekie, Hutchison, and Hether-ington2 interpreted the changes in electrical resistance accompanying the aging of Cu-Fe specimens in terms of a coherent 7-Fe precipitate which transformed to the incoherent a-phase during long aging or cold working. Greninger- ound that Cu-Fe alloys which had been water quenched from 1050" and then held at 650°C for 3 hr changed from weakly to strongly ferromagnetic as the aged wire was subsequently cold worked. He also found diffraction lines corresponding to body-centered-cubic iron in Debye-Scherrer patterns given by aged and worked specimens but lines corresponding to only one face-centered-cubic phase in specimens which had been aged but not worked. Knoppwost,' and later Cech and Turnbull,5 found that aged Cu-Fe specimens showed a slight increase in ferromagnet-ism after they had be? cooled in liquid nitrogen. Very recently Denney6 followed the kinetics of the precipitation reaction as indicated by the saturation magnetization, hardness, and diffuse X-ray effects. The experimental results reported by all of the authors mentioned above are readily explained in terms of the Bitter and Kaufmann concept. However, most of the evidence is indirect when used to define the structural changes involved. It was the aim of the present investigation to determine the mechanism of precipitation of iron from a Cu-Fe solid solution in the light of available published information and with additional new and more direct experimental data. Experimental Method At 1060°C copper will contain up to 3 atomic pct Fe in equilibrium solid solution.7 The solvus slopes rapidly toward lower iron concentration, so that at 600°C only about 0.5 pct Fe remains in solution at equilibrium. Below the eutectoid temperature (850°C), the iron-rich phase in equilibrium with the copper-rich solid solution consists of body-centered-cubic a-Fe. Above 850 °C the equilibrium iron-rich phase is face-centered-cubic r-Fe. The alloy to be studied was made by melting electrolytic iron and OFHC copper by induction under vacuum in an Alundum-lined crucible. The metal was held molten for about 5 min, after which time the power was turned off and the crucible was tipped about 70" to promote directional solidification. The resulting ingot, containing 2.5 wt pct Fe by analysis, was clean, large grained, and free of gross segregation. Slices % in. thick were cut from the ingot, rolled to 1/8 in. in thickness, homogenized in hydrogen at 1060°C for 24 hr and, finally, quenched in cold water. Specimens for all subsequent tests were made from these slices. Squares measuring about 1 cm on a side were cut from the slices to make specimens for studying hardness and microstructure. Wires (0.020 in.) for the Debye-Scherrer survey were drawn from 1/8 in. sq rods which had been cut from the homogenized slices. Large crystals for observing diffuse X-ray diffraction effects were prepared by mechanically

Jan 1, 1958

By S. L. Couling, D. J-P. Adenis

i2) twinning in poly crystalline magnesium does not usually occur homogeneously but is concentrated in localized regions or bands inclined at about 45 deg to the stress axis. These bands of twinning are in many ways similar to the Luders bands seen in mild steel alzd Al-Mg alloys. Within a hand the percentage of the volume twinned may approach 100 with no twinning outside the band. Bands are not produced in specimens of grain size a3 x 10-= in. or in samples deformed at temperatures 300°F. Annealing of heavily twinned regions leads to re crystallization textures markedly different from those found in the starting material. The exact preferred orientation appears to depend on the starting grain size, the amount of compres-sive strain and the manner in which it is introduced. MAGNESIUM, with its hexagonal crystal structure, deforms plastically at room temperature by a variety of deformation mechanisms, one of the most important of which is (1012) twinning. In single crystals such twinning occurs on compression parallel to the basal plane or tension perpendicular to it. In wrought polycrystalline magnesium, such as rolled sheet, the preferred orientation is such that almost all the grains have their basal planes nearly parallel to the sheet surface. Therefore, if sheet material is deformed by cold rolling or by tension in the plane of the sheet, deformation of the grains by (1012) twinning is not favored. On the other hand, twins form readily on compression parallel to the plane of the sheet as in a compression test, on the compression side of a bent sample, or at the outer rim of a drawn cup. The first part of this paper deals with the morphology of (1012) twinning in polycrystalline magnesium. Some aspects of this subject were covered by Barrett and ~aller.' Of direct bearing on the work to be reported here are the comments of Jetter' in discussion to Ref. 1. He shows that Mg + 1.5 pct Mn alloy sheet when bent about a transverse axis develops a pattern of transverse bands on the surface of compression. A longitudinal section through the sheet shows that the bands are wedge-shaped and inclined to the rolling direction. The bands were identified as "outcrops of regions in which deformation is localized as the result of the reorientation brought about by (1012) twinning". The second part of the paper treats the recrys-tallization texture of the specimens twinned by compression. Magnesium deformed and then annealed generally recrystallizes with no change in orientation.1'3'4 This statement is true provided that the amount of (1012) twinning occurring during deformation is small. In an isolated observation, Anse15 has shown that, when deformation produces much (1072) twinning, annealing causes new maxima to appear in the pole figure. The second part of the paper elaborates on this point. I) MATERIALS AND PROCEDURES All of the experimental work to be reported was done using the commercial sheet and plate alloy AZ31B (nominal composition: 3 pct Al, 1 pct Zn, 0.4 pct Mn, balance magnesium). This alloy is available commercially in two tempers, -0 (fully annealed) and -H24 (partially annealed), and specimens of both tempers were used in various experiments. The average grain. diameter (AGD) for -0 temper 0.125-in. sheet is about 0.5 x 10- in.; where material of larger grain size was desired, anneals at elevated temperature were used to grow the grains. compression tests were made on a screw-driven "hard" machine. The specimens were clamped in a

Jan 1, 1964

By Ralph Arnold

WITHIN the past three weeks the price of crude oil in the Mid-Continent field has been cut 50 .per cent. Similar action has been taken, or probably, shortly will be taken, in most of the other fields of this country. This cut is very drastic. Is it justified? Some of the causes advanced for the cut are: that it is in line with the industrial downward readjustment now taking place throughout the country, and that there is an over-production of oil, which can best be slowed down by lowering the price of crude. In part, these two reasons are logically advanced, but such underlying causes as the great production- in Mexico have not been prominently brought forward nor the fact that it would be advantageous at this time to fill up the empty storage of many of the consuming companies at a low 'price. In order to properly comprehend the situation let us compare for a moment the production- of oil in the United' States and that in Mexico. Oil in the United States occurs in numerous often widely separated pools, varying in individual area, but each usually relatively extensive, compared to the area or gathering ground from which it is ultimately derived: It occurs in mod-erately porous reservoir rocks under such conditions of pressure, mobility and availability as to preclude its withdrawal except over a period of years-varying from 1 to at least 40 (average, say 15 years, depending on-the pool). One well will usually drain a limited area-2 to 10 acres-so that rate of withdrawal of oil under each owner's property is determined by the owner. - The important point to remember is that no matter how intensive the development, the oil reserves of -the United States cannot be materially exhausted' for at least 20 years, and the total available supply, not including shale oil, will probably require 50 to 75 years, or longer, for its withdrawal, the yearly rate of production decreasing slowly from this time on.

Jan 1, 1921

By R. Shuttleworth, R. Smith

A Knudsen effusion tnethod I~as been used lo measure the vapor pressure of pure iron in the temperature range 1000° to 1500°C. Neutron-irradiated , natural iron was used and the Mn'~proclzdced by the (n, p) reaction removed by evaporation at high temperature. The results can be represented by the equation: where pM - 1.088 x 107 atm and T, = 20,890°K. A value of 100.2 kcal per g- atom was obtained for AH;. THE vapor pressure of pure iron in the temperature range 1000" to 1500°C has been measured. Radioactive iron and a Knudsen cell technique were used and the Mn' produced by an (n, p) reaction removed by evaporation at high temperature. From the variation of vapor pressure with temperature values of the enthalpy and entropy of solid iron have been found. Previous workers2 used a Lang-muir method and measurements were made over a smaller temperature range than that in this work. EXPERIMENTAL The apparatus used was similar to that of Pyle and Shuttleworth, and McLellan and Shuttle worth. However, because of the higher temperatures the Knudsen cell was machined from tungsten bar and the flanged furnace tube was beryllia. Heating was by passing a high current (70 amp at 7 v for 1500°K) through a strip of tantalum foil laid across the top of the cell and through a turn of molybdenum wire around the furnace tube. This method of heating ensured that the top of the cell was slightly hotter than the base and prevented condensation and re-evaporation from the orifice. The temperature was measured by means of a pt/Pt 13 pct Rh thermocouple spot-welded to the base of the crucible. To ensure accurate temperature measurement the iron was in the form of a thin disc (0.75 cm diam by 0.075 cm) which lay on the base of the cell. The high-purity iron was irradiated in the Harwell pile for a week at a neutron flux of 1.2 X 10" neutrons per sq cm per sec. The isotopes fe'~ and Fe" are produced by (n! y) reactions but only Fe", half-life 45.1 days, is a emitter; Mn which is also a y emitter, half-life 300 days, is produced simultaneously by an (n,p) reaction.' Immediately after irradiation of natural iron the ratio of ~e" to Mn y activity was 100:l. However, manganese is very much more volatile than iron and almost all the y activity of the condensate is due to Mn'~. Thus it was essential to eliminate all the manganeses before any measurement of the vapor pressure of iron was made and this was done by preliminary heating for 20 hr at 1400°C. For each determination the iron was dissolved from the target with acid and the y activity compared to a known weight of iron. By means of a y-ray spectrometer the y-activity measurements were made at the 1.09-mev peak of the 17e5' spectrum where the background was of the order of 3 cpm. Despite the low specific activity of ~e" a mass of 10- " g of iron could be determined corresponding to a vapor pressure of about l0-'' atm. RESULTS The vapor pressures were calculated from the equation: Where m is the mass of iron effusing in a time t through an orifice of area a2, r is the radius of the target, Z is the distance from the orifice to the

Jan 1, 1965

By Donald Ofte, L. J. Wittenberg

The absolute viscosity coefficients and activation energies for viscous flow of bismuth, lead, and zinc are reported. The viscosities were measured in an oscillating cup viscosimeter from nearly 1000°C to within 1 deg of the melting point of zinc; 2 deg of the melting point of lead; and in the supercooled condition of bismuth, 9 deg below the melting point. Two methods of relating the change in the viscosity coeflicient with temperature were compared. From the plot of the logarithm of viscosity (77) as a function of reciprocal absolute temperature (1/T), the equations of the lines which fit the data are: AS a part of the Reactor Fuels and Materials Research program at Mound Laboratory, precise measurements of the physical properties of liquid metals are of interest because the desirability for a low vapor pressure liquid coolant in high-temperature nuclear power plants has focused attention on the properties of the liquid metals.' Also, a clearer understanding of the liquid metal state can be achieved when better measurements are available. For these reasons, the viscosity values of certain liquid metals have been determined. The viscosities of the liquid metals, bismuth, lead, and zinc are measured in an oscillating cup viscosi-meter. In this apparatus the liquid is sealed in a right-circular cylindrical cup which is attached to a torsion fiber so that the system forms a torsion pendulum. The damping effect of the molten metal upon the normal oscillations of the torsion pendulum is a function of the viscosity of the liquid. This method is advantageous because of the small amount of sample required (8 to 10 cc), the ease of remote operation of the apparatus in a vacuum system, and the containment of the liquid metal in a hermetically sealed, nonreactive, tantalum crucible. With the liquid metal sealed in the crucible, loss of liquid by vaporization and chemical reactions with atmospheric gases are prevented. Additionally, an absolute viscosity determination is obtained which avoids the sources of possible error in a relative measurement. The difficulties in a relative method include the repetitious cup calibrations, and the uncertainty inherent in the practice of calibration of the apparatus at room temperature and extrapolation to the high temperatures necessary for the investigation of most liquid metals. The oscillating cup viscosimeter was first described by Meyer in 1891.2 The first complete mathematical treatment offering an absolute measurement of viscosity with this type of apparatus was proposed by Andrade and chiong3 in 1936 for an oscillating sphere filled with a liquid. This solution was modified to include a right circular cylinder by Hopkins and Toye4 in 1950, and R. Roscoe5 in 1958. Roscoe's treatment for the calculation of the viscosity of a liquid at a particular temperature from the logarithmic decrement and period of oscillation of the torsion pendulum was used in this investigation. A detailed description of the method of calculating the viscosity from these measurements has been reported earlier.' This calculation has been programmed for the IBM 704 and IBM 1620 computers for expedition of the otherwise laborious calculations. APPARATUS The cutaway view of the apparatus in Fig. 1 shows the suspension system within the high vacuum enclosure. The low residual gas pressure. maintained between 1 x 10-4 and 5 X 10-6 mm Hg during a determination, avoided both air drag on the pendulum and

Jan 1, 1963

By Walter Crafts

KEYNOTE of the technical sessions of the Iron and Steel Division at the Annual Meeting was struck by Leo F. Reinartz in his Howe Memorial Lecture on "The Development of Research and Quality Control in a Modern Steel Mill." In describing recent developments in steel-producing practices at the American Rolling Mill Co. the co-ordination of practical observation and directed research with operations was stressed and was shown to have resulted in economical production of steels of uniformly high quality. Empirical methods based on inaccurate and incomplete experience resulted in the production of commercial products of variable quality and were recognized as inadequate; a research program was therefore initiated that has been justified by its fruits. To name a few outstanding achievements such as Armco iron, steel for electrical sheets, wide continuous strip of superior surface and quality, and non-aging steel is not sufficient to summarize the results of this increasing effort toward better steel products. In addition to the development of new products the faithful observation of operating procedures, the co-ordination of the resulting information, and the standardization of processes have made the steel of today much more uniform and thus more economical and useful to the nation.

Jan 1, 1943

By A. W. Hahn

USE of gold leaf goes back to biblical and even to prehistoric times. Both gold and silver, as well as other metals, were employed in illustrating or illuminating manuscripts. The medieval monks also used bronze powders. Metals were subdivided as finely as possible by mechanical methods, or by granulation and then were pounded into finely divided flakes. Substances such as honey have also been employed, since early times to keep the flakes of metal apart during grinding. Stearic acid is a more modern agent used in flaking aluminum and other metals. Finely divided "blue powder" is a by-product in retorting zinc ores, and contains from 78 to 90 per cent of zinc metal. This has been used as a precipitant for precious metals in the cyanide process and for chemical reduction processes. The making of zinc dust by atomizing is a step well known in electrolytic zinc plants. The Thermit process of Goldschmidt also requires the use of finely divided aluminum.

Jan 1, 1937

By Alfred R. Powell

LATE in 1944 a group of petroleum and coal technologists was organized in Wash¬ington under the sponsorship of the Petroleum Administration for War and the U. S. Bureau of Mines. This group, known as the Technical Oil Mission, was placed under the authority of the Technical Industrial Intelligence Committee of the Joint Chiefs of Staff, which was then promoting the organization of other missions to be sent to Germany to obtain technical information regarding various industries in that country. The objective of the Technical Oil Mission was to obtain technical data on German production of synthetic oil from coal and all other commercial practices and research projects connected with the oil industry. The primary purpose was to obtain such data as were immediately essential to assist the war against Germany and Japan, with secondary emphasis on technical information that would assist American industry after the end of the war. Since oil-production facilities in Ger¬many and the occupied countries con¬trolled by Germany were the top targets for strategic bombing, the Technical Oil Mission was the first group under the Technical Industrial Intelligence Com¬mittee to enter Germany. A few members of the group flew to London in February 1945 and the majority of the remainder followed in March. In London they were joined by an equal number of British investigators and the combined, mission was then sent into Germany under the authority of the Combined Intelligence Objectives Subcommittee (CIOS). A sum¬mary of the more important information gained by this combined British and American mission is presented below. GERMAN OIL PRODUCTION The oil available to Germany, both natural and synthetic, and including pro¬duction from occupied countries, reached a peak in late 1943 and early 1944. Pro¬duction at this time was at the rate of 1,200,000 metric tons per month, equiva¬lent to i00,000,000 bbl. per year, or about 7 per cent of the wartime production in the United States. Of this production, 50 per cent was crude oil from Romania and Hungary, 12 per cent was crude oil from Germany itself, including Austria, 9 per cent com¬prised coal-carbonization products, that is, tar and light oil, and only the remaining 29 per cent was synthetic liquid fuel made from coal or tar. Synthetic liquid fuel made in Germany was equivalent therefore to less than 2 per cent of war¬time production of crude oil in the United States. The success of the strategic bombing campaign against German oil-production facilities is demonstrated by the fact that by September 1944 the Ploesti fields of Romania and much of the syn¬thetic oil production had been eliminated, so that the amount of oil available to the German war machine was only 25 per cent of the peak quantity mentioned above. By early 1945, when the combined British and American oil mission was entering

Jan 1, 1946

By Clair Upthegrove, E. S. Rowland

The widespread interest in the alloys of beryllium with copper is due principally to the fact that certain compositions show very favorable precipitation-hardening characteristics and are, in fact, the stronges nonferrous alloys known at the present time. Investigations have been conducted by Masing and Dahl and others on the physical characteristics of ternary beryllium alloys, in an attempt to produce precipitation hardening effects with a smaller amount of beryllium than that required in the binary copper-beryllium alloys (2.0 to 2.5 per cent Be). The results of these investigations show that ternary alloys of beryllium with Cu-Sn, Cu-A1 and Cu-Zn, among others, exhibit promising improrcmc~nts in physical properties after precipitation-hardening treatment and, while the increases in properties obtained are not as high as those reahzed from the binary copper-beryllium alloys, excellent properties arc obtaincd with beryllium contents averagirlg about one-half the amount reqnired in the binary alloys. This paper presents the results of an investigation of the equilibriun relations of certain alloys containing copper, tin and beryllium. The alpha-phase boundary of the ternary system is given for alloys containing from 0 to 1 per cent beryllium. The equilibrium conditions beyond the alpha-phase boundary are presented for alloys containing up to 32 per cent tin and 1 per cent beryllium. The data were collected by means of quenching experiments, microscopic examination and thermal analysis The results of some powder-method X-ray determiniations on the alloys, conducted by Mr. William Mikulas and Prof. Lars Thomassen at the University of Michigan, are used as evidence in this paper. The con

Jan 1, 1935

By E. S. Rowland, Clair Upthegrove

The widespread interest in the alloys of beryllium with copper is due principally to the fact that certain compositions show very favorable precipitation-hardening characteristics and are, in fact, the stronges nonferrous alloys known at the present time. Investigations have been conducted by Masing and Dahl and others on the physical characteristics of ternary beryllium alloys, in an attempt to produce precipitation hardening effects with a smaller amount of beryllium than that required in the binary copper-beryllium alloys (2.0 to 2.5 per cent Be). The results of these investigations show that ternary alloys of beryllium with Cu-Sn, Cu-A1 and Cu-Zn, among others, exhibit promising improrcmc~nts in physical properties after precipitation-hardening treatment and, while the increases in properties obtained are not as high as those reahzed from the binary copper-beryllium alloys, excellent properties arc obtaincd with beryllium contents averagirlg about one-half the amount reqnired in the binary alloys. This paper presents the results of an investigation of the equilibriun relations of certain alloys containing copper, tin and beryllium. The alpha-phase boundary of the ternary system is given for alloys containing from 0 to 1 per cent beryllium. The equilibrium conditions beyond the alpha-phase boundary are presented for alloys containing up to 32 per cent tin and 1 per cent beryllium. The data were collected by means of quenching experiments, microscopic examination and thermal analysis The results of some powder-method X-ray determiniations on the alloys, conducted by Mr. William Mikulas and Prof. Lars Thomassen at the University of Michigan, are used as evidence in this paper. The con

Jan 1, 1935

By C. H. Mathewson, H. M. Day

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By H. M. Day, C. H. Mathewson

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By J. R. Low, M. B. Reynolds, L. O. Sullivan

The effect of neutron bombardment upon the stability of type 347 austenitic stainless steel has been investigated by a magnetic technique. The relation of the ferrite content of a stainless steel to its magnetic properties is given, and an apparatus suitable for the measurement of the ferromagnetic saturation induction of small specimens is described. Results of measurements on irradiated specimens are tabulated. Exposure to a neutron flux was found to cause a slight increase in the ferrite content of type 347 stainless steel, the change increasing with increasing length of exposure and with increasing initial ferrite content. The similarity of the effect of irradiation to the effect of annealing is pointed out. Possible effect of irradiation upon density of austenitic stainless steel is discussed. COMMERCIAL austenitic stainless steels are alloys of iron, chromium, and nickel, plus small quantities of other elements. Although these alloys are normally used in the austenitic condition, this state is thermodynamically metastable at ordinary temperatures and transformation to a more stable state takes place under favorable conditions. In the austenitic state, these stainless steels have the face-centered-cubic crystal structure characteristic of y iron, but the stable state at room temperature is a mixture of austenite and body-centered-cubic ferrite. The transformation from the pure austenitic condition may be brought about by cold working the alloy at a temperature below that at which the aus- tenite becomes thermodynamically unstable (about 400°C), the completeness of transformation increasing with increasing severity of cold work and decreasing temperature. The behavior of the austenitic stainless steels under ordinary conditions of use is rather well known. However, use of these alloys in a nuclear reactor introduces a new variable: the effect of neutron bombardment upon the transformation from the austenitic to the ferritic state. It was with this in mind that a study of the radiation stability of austenitic type 347 stainless steel was undertaken. Magnetic Technique for Ferrite Determination Commercial austenitic stainless steels such as type 347 undergo little transformation under normal conditions of fabrication and use. In view of this fact, it seemed likely that neutron irradiation would change the ferrite content of the alloy but little. The method chosen for measurement of the effect of neutron irradiation was thus limited to one which would be quite sensitive to small changes in the ferrite content of the alloy. Of the properties of the stainless steel which can be measured, the magnetic characteristics are most sensitive to the quantity of ferrite present.

Jan 1, 1956

By Sam Tour

OF the new alloys achieving commercial prominence during the year, an aluminum-silicon magnesium casting alloy, which is similar in many respects to the 4 per cent copper alloy, developed about 1921, which has attained such a wide field of service, may be mentioned. The new alloy, like the old, is a heat-treatable type and develops about the same physical properties. The alloy casts easily and is relatively insensitive to high pouring temperatures. Its ability to produce substantially leak- proof castings is noteworthy. A second casting alloy development is the new Aluminum Co. of America No. 132, "Lo-Ex" piston alloy, a result of nearly eight years of research. The alloy contains about 14 per cent silicon and varying amounts of nickel, copper, and magnesium. It exhibits a low coefficient of expansion and thus permits small piston clearances. Its lower specific gravity is a further advantage.

Jan 1, 1932

By R. J. Wasilewski

Axial expansion has been determined by X-ray diffraction up to 600° to 760°C in a titanium and four high-oxygen alloys. Expansion data cannot be fitted to the usual quadratic expression and anomalies observed are believed indicative of the changes in the bonding configuration of the valence electrons. Furthermore, there is significant disagreement between data obtained on poly crystalline and single crystal powder specimens. The major disagreement occurs within the temperature range (-470°C) where both mechanical and electrical properties also show markedly anomalous behavior. X. HIS work forms part of an investigation of physical properties of pure titanium and its osolid solutiono alloys with oxygen and nitrogen. In view of the anomalies observed in both the electrical resistivity' and the susceptibility behavior it was decided accurately to determine the thermal expansion behavior of the pure and alloyed a titanium. PREVIOUS WORK The axial expansion coefficients reported for pure titanium are listed below. As can be seen, there is a marked discrepancy between the axial expansion and the experimentally determined coefficients on poly crystal line material. Thus, if we take the most recently reported axial expansivities3,4 we obtain perature interval of 25o to 700°C. The experimental value reported for polycrystalline metal is, however, of the order of 9.7 x 10o6 per OC. EXPERIMENTAL I) Pure Titanium. High purity titanium powder of -325 mesh was used throughout most of this work. The only significant impurities present were the interstitials, oxygen and nitrogen, which analyzed respectively 650 and 80 ppm. The purity of the ma-

Jan 1, 1962

By R. G. Davies

Isothermal annealing of quenched Fe3Al reveals that the superlattice forms by the nucleation and growth of ordered domains. The activation energy for isothermal ordering and initial domain growth is -29 keal per mole, which is thought to he the activation energy for vacancy migration. Domain growth, in the absence of excess vacancies, has an activation energy of -100 keal per mole. A maximum in the hardness is observed when the structure consists Of ordered domains, -35-4 in size, growing into a short-range ordered matrix and, also as a function of degree of order, S, with an infinite domain size at S = 0.4 to 0.5. It is proposed that both maxima are due to a transition from deformation by unit dislocations to deformation by superdislocntions. FE-AL alloys containing more than -23 at. pet Al, when quenched from above the critical temperature for the Fe3A1 type of order, always contain the maximum possible amount of FeAl (B2) type of order' (see Fig. 1). Thus when the Fe3A1 superlattice forms, in a 25 at, pet A1 alloy, it does so from an imperfect FeAl structure. The formation of the Fe3Al superlattice has been the subject of several recent X-ray,1, 2 electrical-resistivity,3"6 and dilatometric3 investigations. McQueen and Kuczynski3 concluded that the isotherma1 ordering of Fe3Al, after quenching from 800°C (T,, the critical temperature for order, is 55O°C), takes place by the nucleation and growth of ordered domains. However, Feder and Cahn4 found that the isothermal ordering was complex but more like a homogeneous nucleation process than a nucleation and growth process. Lawley and Cahn2 reported that the degree of order is a continuous function of temperature which is a characteristic of a homogeneous nucleation process. Thus, the evidence is conflicting as to the nature of the Fe3Al ordering reaction. Lipson7 was the first to suggest that ordered domains should exist in the Fe3A1 structure since, as

Jan 1, 1964

By M. A. Hunter

IN the present state of public affairs, the reviewer turns from his traditional role of recording the progress made in research during the year and views the whole situation in which he finds himself in direct relation to the immediate needs of the nation. The slow progress of research year by year fades into comparative insignificance. The sum total of that research in all the years which have past becomes of importance only in direct relation to the extent to which we have translated or can immediately translate it into in¬dustrial production. For in a wartime economy immediacy is of paramount importance. The outcome of the war is being determined by our ability to pro¬duce and fabricate the metals and alloys which we require for its prosecution. Aside from iron and steel which lie outside the limits of this review, the most important of the nonferrous metals now needed in wartime production are aluminum, magnesium, nickel, chromium, and manganese. Some remarks on their production and fabrication follow.

Jan 1, 1942

By Roy L. Zuber

Identification and analysis of mining hazards involves the correlation of accident, injury and illness information from all segments of the mining industry. It would not be feasible to process the volume of data involved without substantial reliance upon a computerized information system similar to that maintained by the Health and Safety Analysis Center. Numerous statistical programs are applied to the computerized accident-injury-illness data base to identify those mining tasks and associated activities which are responsible for most of the injuries and occupational illnesses. These programs are used to flag those mining tasks or conditions at specific mines or segments of the mining industry where either a significant increase in the injury/illness trend has been reported or where the number of injuries/illnesses related to specific mining tasks or conditions are high. Upon identification of those mining hazards which warrant further analysis, a computerized search of the coded accident data is performed to correlate the predominant categories by cause of injury or illness, source of injury, nature of injury, type of accident, etc. From this correlation, those factors most common to the conditions responsible for the hazard may be identified. Based upon analyses of this form, recommendations are made regarding the appropriate engineering, training, and/or operational improvements necessary to alleviate the hazard. In addition to mining hazard analysis, the computerized data base also has application in the area of optimum resource allocation. Computer programs have been developed to assist management in allocating resources based upon organizational requirements and historical accident - injury trends.

Jan 1, 1983

By T. Federighi, S. Ceresara, C. Panseri

The results of an exploratory investigation by means of resistivity measurements at -195ºC, on the aging characteristics of a set of Al-Mg alloys with a maximum content of 7 pct Mg, are reported. Whereas for dilute alloys (Mg < 1.5 pct) only a decrease in resistivity is observed at about 100°C (due to the elimination of quenched-in vacancies), for more concentrated alloys such a decrease is preceded by an increase in resistivity in the range between -60ºand +40°C. Following some previous suggestions, this increase is considered as good evidence for clustering of solute atoms @reprecipi-tation process). From the analysis of the results it appears that, although the process is substantially similar to that observed in other Al-rich alloys, it is characterized by a strong interaction between vacancies and zones. THE process of formation of Guinier-Preston zones, i.e., preprecipitation,1&apos;2 which occurs during the aging at about room temperature in many supersaturated aluminum-rich alloys, has been extensively investigated in the past few years by several workers.2,3 owever, a very interesting question arises when the case of Al-Mg alloys is considered: although it is very easy to supersaturate Al-Mg alloys, just in the same way as for many other aluminum alloys showing preprecipitation, only very little experimental evidence was available until a short time ago in the literature supporting the existence of "natural" aging in supersaturated Al-Mg alloys (see, for example, Refs. 4 to 6). On the other hand, as is well known, the X-ray method is not useful in this case because the X-ray scattering factors of magnesium and aluminum atoms are about the same. Recently, however, Cordier and Detert7 have stressed that during the aging at about room temperature of a supersaturated Al-Mg 10 pct alloy it is possible to detect an increase in resistivity; since, as is well known, such an increase is observed also in most alloys showing preprecipitation, the above authors have interpreted their results as evidence for the formation of magnesium-rich clusters (or Guinier-Preston zones) during the aging. In the course of or ientative investigations on preprecipitation in several aluminum-rich alloys, we also could detect a similar phenomenon in more dilute Al-Mg alloys, see Instituto Sperimentale Metalli Leggeri, Annual Report, 1959, and also Ref. 8. Since the details of our observations, although of a preliminary nature, differ from those of Cordier and Detert and allow one to draw a more advanced picture of the preprecipitation process in Al-Mg alloys, we have thought it useful to report our results in this paper and to comment on them briefly.

Jan 1, 1963

By F. H. Spedding

From thermal, metallographic, X-ray, dilatometric, and electrical resistance data a Phase diagram is proposed for the La-C system. TWO compounds are formed, body-centered-cubic Laz C, having a large range of solid solubility, and body -centered-tetrago-nal Lac2 . The former melts incongruently at 1415°C, and at 25OC it has an electrical resistivity about two and one-half times that of bure lanthanum. The latter melts congruently at 2356°C and at room temperature has an electrical resistivity about equal to that of bure lanthanum. The addition of carbon to La lowers the melting Point of La about 115&apos; C, raises the higher (B-Y) transfomzation about 10" C and appears to have no effect on the lower ( a-0) transformation. The addition of carbon appears to lower the oxygen content in the metal and improve the machinability; however, the tendency to oxidize is increased. Two eutectics are formed in the system. The first occurs at 2.2 pct C and melts at 806" C, while the second occurs between Lac2 and C with a melting point of2271"C. PETTERSSON,~ in 1895, was the first to prepare lanthanum dicarbide by heating the oxide with carbon in an electric furnace. He showed that this yellow, crystalline but brittle carbide had a formula corresponding to LaCz and that it reacted with water with the evolution of hydrogen and hydrocarbons and the formation of the hydrated oxide. Von Stackelberg&apos;s investigation of the crystal structure of the MCz carbides showed that the lanthanum dicarbide is of the tetragonal calcium dicarbide-type structure. He found the lattice parameters were a = 3.92 and c = 6.56.* Bredig,&apos; using X-ray methods, showed that the room-temperature form of lanthanum dicarbide is stable up to 1750 °C and that above this temperature it transformsoto a face-centered-cubic structure, a = 6.0 ± O.lA, probably of the pyrite, FeSzstruc- typ? The reported discovery of two new cerium carbides, suggested that a corresponding face-centered-cubic lanthanum monocarbide and a body-centered-cubic lanthanum sesquicarbide might exist. This paper describes work on the lanthanum-carbon system which is part of a study of the rare earth metals and their alloys now in progress in this laboratory. EXPERIMENTAL PROCEDURE Source of Materials—The lanthanum metal was prepared at the Ames Laboratory by metal1o;hermic reduction of the fluoride with calcium metal. The results of spectrographic and chemical analysis indicated the presence of 0.01 pct Y, Al, Cu, Fe, and Si; 0.02 pct Ca and Mg; 230 ppm C; and 115 ppm N. The carbon used was of two types: 1) "National Special Graphite Spectroscopic Electrodes," and

Jan 1, 1960