By K. A. Elbarawy

Processing of Egyptian barite ore with a composition of 85.5% BaSO4; 2.75%SiO2;1.56%Fe2O3 and 5.1% Al2O3 was performed with the aim to prepare pure barium salts. The process took place through pelletization-solid state reduction and leaching steps. Each of these steps was optimized. Pure barium sulphate (99% < 0.82µm) and carbonate (99%<0.75µm )were the final products. This article deals with the reduction process that occur whn coal was added to the ore during pelletization in the ratio of 5:1 stoichiometry. Optimum reduction of pellets of 8-12mm in diameter was achieved after 60 minutes at 1050oC and under a rate of 5 lmin-1 of nitrogen atmosphere, where 87.79% of the ore was reduced. The kinetic studies showed that the reduction process could be modeled according to the core mechanism of diffusion control in which the effective diffusivity is based on the surface area of unreacted ore. The activation energy calculated was 92.7 kJmol-1.

Jan 1, 2006

By Liu Wei-feng

In this paper, the practice of separating precious metals from base metals in gold-antimony alloy by selective chlorination leaching under controlling potential in China has been introduced in detail. The precious metals and the base metals can be separated completely when the complex gold-antimony alloy is treated by this process. The impurity metals were removed effectively since the leaching efficiencies of copper, nickel and antimony are over 99%, with direct recovery of gold being 99.83% that is about 20% higher than that of the original process and silver, antimony, copper and nickel are also recovered effectively. The gold grade of the resulting crude gold powder can reach to 94%.The new process has been applied in the treatment of gold-antimony alloy for two years, and many former procedures have been cancelled, such as electrolysis, Anode slime leaching by nitric acid, smelting in crucible and blowing in muffle. The new process is more shorten, lower cost and friendly to the circumstance comparing to the original process.

Jan 1, 2008

By Manuela Castaneda, Henry A. Colorado

This paper is about the use and stabilization of iron oxide based powders with arsenic contents coming from the purification of water. Cement paste samples with 0.0, 2.5, 10 and 20wt% of waste were fabricated by mixing mechanically all components. There are two main positive impacts of using this waste, first, this waste is produced in large amounts worldwide, and therefore the stabilization has a significant impact for the environment. Second, the waste can be used as an admixture and filler for cement, and therefore reduce the amount of cement in the concrete, which has a major impact in the CO2 footprint since cement industry produces a lot of this gas. Compressive strength and density tests were tested after 28 days. Microstructure was analyzed with scanning electron microscopy and x-ray diffraction. Results show that compressive strengths greater than 20 MPa were obtained and the samples had calcite, portlandite and ettringite phases.

Mar 1, 2018

By K. Murayama, M. Kawakami, T. Takenaka, S. Yokoyama

"Cokes play an important role of spacer in blast furnace. However, they degenerate during Boudouard reaction. Blast furnace cokes are reacted with pure C02 at I 072 to 1673 K. Reaction rate was obtained by the weight change of spherical specimen. The specimen after reaction was examined by microscopic observation. The reaction rate increased with temperature and was expressed by two Arrhenius type lines. The activation energy was 126 KJ/mol at higher temperature than 13 73 K and 202 KJ/mol at lower temperature range. At the higher temperature range, the reaction proceeded from the surface leaving unreacted core, whereas homogeneously whole inside at lower temperature. The porosity increased from the center to surface at higher temperature, whereas it was almost constant at lower temperature.IntroductionThe cokes have the function of fuel, reductant and spacer to keep gas and liquid flow in the blast furnace. Thus, the reaction mechanism of coke with several gas and the strength after the reaction should be important factor to control the blast furnace operation. The reaction mechanism of coke with C02 has been studied extensively. The rate equations were derived by Gadsby[ I], Ergun[2] and Turkdogan and Vinters[3]. They were compared and discussed by Kobayashi and Omori [ 4]. Effect of crystallization degree on the reaction rate was examined by Kashiwaya and Ishii[5]. Catalytic enhancement effect of ash componets have been clarified by Kashiwaya et. al. [6]. Although degradation of coke in blast furnace has been examined recently[7], however, the degradation of coke after the reaction with C02 has not been well clarified yet. In the present work, the metallurgical coke specimen was heated in N2 and C02 and the reaction mechanism and degradation behavior after the reaction was investigated."

Jan 1, 2000

By Husamuddin Ahmadzai

A survey of regulations and state of the art control technologies is presented relating to the smelting of primary aluminium, copper and recycling of residues. Some costs associated with the alternatives and trends for the coming decade in this. sector are identified.

Jan 1, 1992

By E. Oshima

In May 1991, a New Mitsubishi Continuous Copper Smelter Line started operation at Naoshima. Recently, it has been continuing steady operation and one and a half year campaign life has been achieved. In 1996, new records of on line time, the amount of copper concentrate treated and copper anode production were achieved. 1t proves the superiority of the process with respect to pollution control, energy efficiency, flexibility and easiness of the operation and over all economy including off gas handling cost. Furthermore, .plans are underway to prolong the campaign life for two years and to improve the process efficiency. This paper describes recent operation, improvements, and a future capability study.

Jan 1, 1998

By P. Henry

A novel electrochemical cell has been developed for the recovery of MnO2 from residue of pyrolusite ore leading loaded with Fe, Al Ni, Co and Si impurities, This new process can be considered as an alternative to the traditional methods : S02, H2O2 or bioleaching. It has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. Electrochemical characterization and kinetic studies have shown that MnO2 is effectively leached by electrogenerated ferrous ions at high current density from a pulp containing less than 5 g8 Fe. The chemical reactions are : Cathode (inox) : 2F23+ + 2e ? 2 Fe2+ Bulk: MnO2 + 2 fe2+ 4H+ ? Mn2+ + 2 Fe3+ + 2 H2O Anode (Pb-Ag) : H2O ? ½ O2 + 2H+ + 2e Global: MnO2 +2H+ Fe2+ = Mn2+ + H2O + 1/2 O2 The catholyte (MnO2 pulp) circulates upward in the expanded mesh cathode separated from the sulfuric acid solution anolyte by a separator which shows high mechanical resistance, low porosity, low potential drop, and reasonable cost. Laboratory and mini-pilot tests have led to the construction of an OT crating pilot plant (100 kg/hr) able to leach more than 95% of Mn, Ni, Co at 1000-1200 A/m2, 50°C with high faradic yield (> 95 %) and low power consumption (3.2 kWh/kg kWh/kg &4D). New applications like the treatment of spent Zn-Mn batteries, polluted soils, spent catalysts and oxide ore (cobalt, nickel) with electrogenerated redox species are now investigated at a laboratory and mini-pilot scale.

Jan 1, 2000

By Saskia Duyvesteyn

Small ion-exchange resin particles provide faster mass transport than conventional-sized beads. Unfortunately, high pressures are needed to pump solutions through columns containing small resin particles. It is preferable to disperse fine resins in the solution being treated. Screens have been used to separate the resin from the solution, but screens do not retain fines created by attrition of the resin particles. We have developed a separation process based on flotation, which relies on the surface characteristics of the resin, instead of size. The resin is conditioned with a surfactant before dispersing it in the solution to be treated; this increases the hydrophobicity of the resin sufficiently for froth flotation, without introducing surfactant directly into the solution. The surfactant adsorbed on the resin surface does not appear to impair the kinetics of metal ion removal. A flowsheet for an effluent treatment process is proposed; other applications are clearly possible.

Jan 1, 1998

By J. W. Holzenthaler

Teams continue to play a major role at the Phelps Dodge Mining Company El Paso Operations, especially during the present time of low copper prices. The El Paso Operations&apos; teams have taken the initiative during this copper market downturn and have helped reduce operating costs significantly. Because of this, Phelps Dodge El Paso Operations has continued to grow within the team process by creating a total, non- exempt salaried workforce. In the last year alone, the El Paso Operations have implemented three major initiatives to accommodate the team process. The first was the creation of "guiding principles", a policies and procedures handbook. Second was the "zero and beyond" safety initiative. Third was team compensation. In addition, the Copper Products Company has now adopted a work-team environment, following the lead of the refinery.

Jan 1, 1999

By Hideki Minoura

"Two novel electrochemical techniques for the preparation of highly crystallized CdS film have been presented. One is cathodization of a conductive substrate in an acidic chemical bath containing cadmium salt and thioacetamide, where electroreduction of proton at small current densities induces a growth of highly crystallized CdS thin films, whose growth is not disturbed by the reactions in the solution phase. The other technique is electoreduction of aqueous Cd2+— SCN complex. An advantage of this technique lies in no formation of solid particles in the bulk, of the bath.IntroductionIn recent years much attention has been paid to materials preparation by solution processing because of its advantages in lowering the cost as well as the stress to the environment, as compared to the conventional gas phase techniques which unavoidably require high temperature and/or vacuum. We have been trying to explore novel techniques for preparing functionalized compound semiconductors by aqueous solution process. Semiconductors which we have been mainly focusing on are CdS and ZnO, which are important semiconductors finding applications in various devices. In the present paper, some of the techniques that we have recently established for the preparation of highly crystallized CdS will be presented.Methods of the CdS film processing in solution phase (wet process), which have been reported so far can be divided into two major groups; one is chemical bath deposition (CBD) in alkaline solution containing Cd2+ and thiourea 1)4) and the other is electrodeposition (ED) in acidic solution containing Cd2+ and thiosulfate ions - 5)-8) or organic solutions containing dissolved sulfur 9)-11)."

Jan 1, 2000

By Kazuyuki Kakegawa

The sintering characteristics and the change in the compositional distribution in the PbTiO3 PbZrO3-Pb(Mgl/3Nb2/3)O3 system during the sintering process by spark plasma sintering (SPS) method were examined. They were compared with those by a normal sintering method. The densification by the normal sintering was slow even at high temperatures, When SPS method was employed, much lower temperature and shorter period resulted in sintered bodies having almost the theoretical density. As expected in normal sintering, the compositional distribution decreased as the sintered density increased. On the contrary, the change in the compositional distribution by SPS was much smaller than that in the normal sintering. This sintering characteristic of SPS suggested a possibility of fabrication of sintered material having a desired compositional distribution.-

Jan 1, 2003

By Jesús Contreras

Since the commencement of its activities in Huelva in 1970, Atlantic Copper has maintained a course of action that has been more demanding than the successive environmental legislations current at different times. As its primary objective it has sought compatibility between the protection of the environment and both its industrial activity and the social and economic development of the area in which its Metallurgical Complex is located. For this reason, since the seventies it has maintained a continuous programme of investments which have allowed it to attain its present environmental situation. As a consequence of the Environmental Policy of Atlantic Copper, in April 1998 it obtained certification for its Integrated System of Environmental Management (SIGMA) according to international standard IS0-14001, and under European Community Regulation 1836/93 (replaced by the 76112001) for the Eco-Management and Eco-Audit System (EMAS). The SIGMA formalises the environmental management practices of Atlantic Copper and engages it to have available a system that can be fully audited. Atlantic Copper was the first European Company in the non-ferrous metallurgical sector to obtain both the UNE-EN-ISO 14001 certification and the EMAS registration. The present paper reviews the actions by Atlantic Copper in environmental matters that have allowed it to achieve its present position. It also describes the coming stages of improvement planned and the modifications to be carried out in the near future, in particular the criteria for the selection of technologies on the basis of the concept of BAT (Best Available Techniques) introduced by the European Union, and always guided by the final objective of converting Atlantic Copper into a reference within the sector, comparable to the best designed and operated installations in the world.

Jan 1, 2003

By Shinroku Matsuzaki

Data the measurement sensor installed with spatial distribution on the blast furnace were successively accumulated online from the process computer to the database system over a long period. This is a new system that accurately considers the relation with the installation position of each sensor, and picture computerization of the measurement data was developed. The overall operation state of a blast furnace, which skilled operators can see in their mind?s eye, was objectively visualized as pictorial information.

Jan 1, 2006

By Thomas E. P. Wechsler

The limiting factor for most pyro-metallurgical processes in secondary cop- per melting is the time required to heat and melt the product. American Combustion&apos;s proprietary PYRETRON variable £uel/air/oxygen combustion system improves the throughput of existing scrap melting and heating furnaces for copper and copper alloy production by increasing the rate of heat transfer from the flame to the product. The increased productivity and energy savings obtained from this technology can result in sizable reductions in operating costs for smelting operations.

Jan 1, 1991

By Richard D. Hagni

Microscopic examination of selected, representative, unweathered samples of Birmingham, Alabama, Silurian, sedimentary iron ores has fully revealed the nature of the phosphorous-bearing mineral grains. The grains are composed of carbonate-fluorapatite (collophane), range in size from 1 um to 2.25 mm, and exhibit varied types of intergrowth with hematite. Modal analyses conducted under cathodolumi-nescence have provided quantitative data on the a3undance of each of 15 types of phosphorous-bearing mineral grains and made it possible to assess the potential phosphorous liberation from four types of iron ore. The results indicate that 27% of the total phosphorous contained in the iron ores in the western part of the Birmingham district can be expected to be liberated by fine grinding; 60% for ores in the eastern part of the district.

Jan 1, 1982

By R. C. Chaturvedi, S. B. Padwal

"Padwal and Chaturvedi have developed the model based on M-K theory, considering Hosford's yield criterion and critical thickness strain criterion"" to predict the sheet metal forming limits under simple (constant) strain ratio paths. This analysis has been extended in this paper to predict the sheet metal forming limits under complex strain paths. The effects of exponent ""a"" in Hosford's yield criterion and strain paths on the forming limits under complex strain paths are studied using this analysis. The predictions of the present analysis are compared, both for simple and complex strain paths, with experimental results of Ishigaki for A.K. steel and also with the predictions of Rao and Chaturvedi's model. The quantitative analysis of the error in predicting the forming limits has also been carried out using a method suggested by the authors earlier.1. INTRODUCTIONThe constant strain ratio condition has been assumed in the theories developed for prediction of forming limit diagrams (FLO). In actual forming operation, this condition is seldom satisfied. Even in the case of simple single stage press formed components, the strain path becomes curved and non-linear. In the case of pressings with complex shapes, or multiple stages of forming, the changes in strain path are more pronounced and even abrupt.Experimental study of the forming limits, under two stage strain paths, by Ishigaki [1], has shown that the forming limits are path dependent. It has been observed that the forming limits lower than that under simple strain paths, may be obtained under certain strain paths (when the first stage strain path is either equibiaxial tension or uniaxial tension, followed by the second stage strain path as plane strain). Rasmussen's work [2J, on the theoretical study of forming limits under curvilinear strains paths, has shown that a large drop in formability can result from very small changes in strain path. Thus if a deformation process gives rise to failures due to plastic instability, the failure is not necessarily due to insufficient formability of the material. In such cases, FLOs based on constant strain ratio path should not be used directly in predicting the success or failure of the forming operation. Thus the knowledge of forming limits under complex strain paths is of great importance to the interpretation of press-shop problems."

Jan 1, 1994

By Yuanbo Zhang, Daoyuan Zhang, Youlian Zhou, Guanghui Li, Tao Jiang

"Modified humic acid (MHA) has been developed by Central South University (CSU) and authorized in China. It has been reported that MHA is an effective binder for oxidized pellets prepared from specularite concentrates. In this research, effects of MHA binder on roasting behaviors of the specularite pellets are studied. MHA is an organic binder, containing much carbon, hydrogen, oxygen, etc. During the roasting, MHA can provide some heat because of combustion of hydrocarbon, which is beneficial for the recrystallization of Fe2O3 in the specularite pellets at high temperature. Simultaneously, part of hematite particles within the pellets are firstly reduced to magnetite, then, magnetite is oxidized into secondary hematite, which obviously improves the roasting performance of specularite pellets.IntroductionOxidized pellets have been widely used in steel production as a kind of high quality burden for blast furnace ironmaking [1]. In recent years, production of oxidized pellets is developing very fast. Therefore, the supply of high quality magnetite concentrates, which is the most suitable for pellet production, becomes scarce. It is imperative to pursue new alternative materials for oxidized pellet production [2]. Specularite concentrates have attracted widespread attention due to the advantages of high total Fe grade and low impurity content. However, due to the poor ballability and firing performance, specularite has not yet been widely applied into pellet production [3, 4]."

Jan 1, 2012

By Lijun Lu, Honghui Fang

This article carried out the experimental study on using desulfurization ash in steel slag composite material. This was done by investigating the desulfurization ash content in formula one and formula two samples on the influence of setting time and strength of mortar. Through this study the following conclusions were reached for formula one: (1) a setting time of more than 10 hours is required, (2) a dosage of desulfurization ash of 1 ~ 2% is optimal, where flexural strength is reduced by 10% ~ 23% and compressive strength reduced by 5.7% ~ 16.4%. The conclusions of formula two were: (1) when the dosage of desulfurization ash is within 5%, the setting time is within 10 hours; (2) when the dosage of desulfurization ash is 1 ~ 2%, the flexural strength is increased by 5 ~ 7% and the compressive strength is reduced by 1 ~ 2%. The results show that the formula two is better.

Jan 1, 2015

By Batric Pesic

Silver dissolution with thiourea was studied by using the rotating disk technique. The major parameters studied were: thiourea concentration (0-0.5M), ferric sulfate concentration (0-0.5M), sulfuric acid concentration (0-0.5M), and the effect of many foreign ions (Mn, o.i, Co, Ca, Na, etc.). Temperature effect was studied in the range 5-35 .C. The activation energy was 5.4 Kcal/mole. The dissolution of silver was first order with respect to ferric sulfate, and the secord order with respect to thiourea. Among the additives, copper had a dramatically negative effect. The strong oxidants such as hydrogen peroxide and manganese dioxide were also detrimental for silver dissolution. Silver does not dissolve with thiourea in the absence of ferric ions. Sulfuric acid does not participate in the dissolution reaction either. Chemically, the most important parameter for silver dissolution is the ferric sulfate/thiourea ratio. Thus, in the solutions with excess of ferric sulfate, a solid silver-thiourea complex is formed, which precludes transfer of silver into solution. In the solutions with the excess of thiourea, the free thiourea reacts with formed solid silver-thiourea complex and silver goes into the solution. The solid silver-thiourea complex was characterized according to its chemical composition. The complex contains 6.54%C, 2.49\H, 14.77%N, 16.09%0, 21.62%8, and 37.13% Ag. This composition corresponds to a Ag2so4.3&apos;1U.2ff:i0 compound The soluble silver species are present in the solution as the dimers of AgTU+3 complexes.

Jan 1, 1989

By Qiu Dingfan

The Slurry Electrowinning Process (SEP) is a new hydrometallurgical method and clean technology, Sulfide ores can be treated by the SEP without S02 emission and the sulfur from the sulfides can be recovered in element form which is easy to stockpile and can be transported at low cost. In a special slurry electrowinning cell one can achieve at the same time the leaching of elements from the feed and the electrowinning of metals from the electrolyte, Because the anode reactions are utilized for leaching of some elements the consumption of the energy is decreased, SEP also has the advantage of separation some elements, It is especially suitable for treatment of complex concentrates containing Pb, Cu, Au, Ag and S, which could hardly be accepted by any smelter. In this work, the behavior of different metals in this process has been studied and it was found that the separation of metals in some minerals is possible through the SEP, Beijing General Research Institute of Mining and Metallurgy (BGRIMM) has studied the possibility of the SEP to treat bismuth concentrates containing S, Be and F in laboratory and pilot-test scale as well as in commercial plants, The commercial plant was set up in 1997, It has been in operation since that time, According to the results of laboratory experiments and pilot- plant test, a new plant to treat complex gold minerals was set up in 1998 and is in operation in 1999

Jan 1, 2003