By Earl W. Palmer, Cyril Stanley Smith

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors' conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935

By Cyril Stanley Smith, Earl W. Palmer

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors' conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935

By W. R. Barclay

IN MY general contact with industry I have become more and more impressed with the need for the closest possible co-operation between engineers and metallurgists, and particularly with the need for appreciation of the work that each group is doing to assist the other. Also, I am convinced that from time to time it. is vitally important to a true perspective of human progress in all its branches, and certainly a salutary corrective of undue optimism and pessimism to endeavor to carry the mind hack over certain periods in the advance of technical knowledge, and form some kind of broad estimate of what has been accomplished in the application of science to industry in the fields with which we, as individuals or groups, may for the time being be concerned. We cannot without some appreciable mental effort realize what our forerunners have dine For us. If the young engineer or metallurgist entering industry today could be suddenly transported to a quarter of a century ago, and be compelled to work with the materials then available and within the limitations of knowledge then attained, he would, on his return to present-day life, have a much greater appreciation of what has been accomplished before lie arrived on the scene, and, what is even more important, a far more acute sense of its inherent value to his profession. I propose here merely to indulge in a general summary of the subject of improved engineering metals and alloys rather than in details, and to deal exclusively with developments within my own experience.

Jan 1, 1938

By AIME AIME

THE John Fritz Medal Board of Award, at its annual meeting on Jan. 21, 1921, awarded its gold medal and diploma to Sir Robert Hadfield for the invention of manganese steel. On June 1, announcement was made that the Board of Award had awarded its gold medal and diploma to Charles Prosper Eughe Schneider for "achievement in metallurgy of iron and steel; for development of ordnance, especially the 75-mm. gun, and for notable patriotic contribution ' to the winning of the war." The award to Sir Robert Hadfield is for the year 1921; the award to Mr. Schneider is for 1922. The latter was made at this time in order that the medal might be presented by the group of American engineers now visiting England and France.*

Jan 1, 1921

INTRODUCTION Conditions for formation of porphyry copper deposits appear to have been propitious in the Appalachian orogen from the end of Precambrian into Middle Ordovician, and again from Middle Devonian into Mississippian. In the Appalachians we can now record the evolution of a porphyry copper province within a developing orogen, one that reached metamorphic and structural maturity by the end of Devonian. Fig. 15, after Irwin and Coleman (1972), locates that portion of the Appalachian orogen included in this study, and Fig. 16 illustrates general geology of the area. Deposits mentioned in Table 3 and in the text are shown in Fig. 16. Data presented summarize personal observations by the author, published descriptions of specific areas noted in the bibliography, and abstracts from Provincial assessment files. Sources of previously published data are acknowledged. Few comprehensive descriptions of individual porphyry copper deposits in this area exist, so much of the data presented is new to the literature. Porphyry mineralization has, for this chapter, been restricted to porphyry copper de- posits, although porphyry molybdenum de- posits (Clark, 1972) are also shown in Fig. 16 (Hollister, et al., 1974). Copper- molybdenum and tungsten-molybdenum skarns are also omitted to simplify discu sion, though each is known in the area studied. Gaspe Copper is included, however; min- eralization in this deposit is present in the intrusion as well as in the skarn adjacent (Bell and Scott, 1954). Porphyry deposits listed in Table 3 are included because of some important feature, although other deposits have been reported (e.g., Kirkham and Soregaroli, 1975 ) . Clearly, no table now compiled could be complete. The pace of exploration insures that new occurrences will probably be found. Summaries of features exhibited by intrusions shown in Table 3 should remain valid, however, since they appear representative and are based on an adequate number of deposits in the area studied. Paleozoic porphyry copper prospects (shown in Fig. 16) are more common, apparently, in the northeastern part of the orogen, rarely having been found south of Catheart or west of the Logan Line. Occurrences of molybdenum and other associated lithophile elements are, however, known to the south and west as well as further north. Killeen and Newman (1965), King (1970),

Jan 1, 1978

By H. D. Newell

THERE has been much research and commercial development in recent years in the use of chromium and nickel in steels of various types, including those intended for high-temperature service. By "high-tem-perature steels" are meant those specifically designed for service at ele-vated temperatures in steam plants, oil refineries and other industries where high-temperature operations are conducted. This paper is devoted to some preliminary data on the effect of silicon on certain of the most popular chromium-molybdenum steels now being used in quantity by the refining industry and includes a short statement on the influence of copper in steels intended for high-temperature service.

Jan 1, 1937

By James Malcolmson

(New York Meeting, February, 1913.) THE Tigre Mining Co. of Mexico, owned by the Lucky Tiger Combination Gold Mining Co. of Kansas City, decided early in 1910 to enlarge its mill, which consisted of a concentrator milling 3,000 tons of ore per month. The enlarged plant was designed to crush and concentrate 6,000 of ore and to cyanide 7,500 tons per mouth. The extra tonnage cyanided was to be obtained from tailings which were stored below the old mill. Power was supplied to the old mill from four boilers; a 150-h-p.. Corliss engine and two Weber 60-h-p. gas-engines using producer-gas made from charcoal. The total horse-power required, including 60 h-p. used for machine-drills in the mine, was approximately 275. Cord-wood cost $4.32 per cord, 8 by 4 by 3 ft., and charcoal $15 per ton. The fuel supply in the surrounding country was approaching exhaustion; more than 150 mules and 50 men were engaged in cutting and transporting this fuel, and the unsettled political, conditions in Sonora were such that it would be practically impossible to keep an organization of this kind together. The price of fuel was steadily rising and at times it became almost impossible to get sufficient fuel to operate.

Jan 4, 1913

By T. J. Woodside

A. E. LEE*—One question of the flue leading to the tube coolers. What gas velocity is maintained to prevent settling of the finely divided fume ? T. J. WOODSIDE (author's reply)— 30 fps. Of course some fume settles out, but is immediately carried away by the screw conveyors. H. R. BIANCO —How effective are the soot blowers ? Do you have to use any hand lancing? T. J. WOODSIDE Only one point, which is right at the top of the economizer and which the soot blowers do not reach, we occasionally hand lance. But everywhere else the soot blowers have been very effective and no hand lancing has been done. L. V. DAVIDSON*—Do you have considerable variation in the lead content of the fume collected if the lead is higher, and is there greater tendency for the fume to stick on the boiler tubes ? T. J. WOODSIDE—There is very little variation in the lead content. From 5 to 7 pct is the widest range variation we have had and we have noticed no difference in the behavior of the fume. C. R. KUZELL—Mr. Woodside has been quite generous with data pertaining to metal and fuel economics. I think he stated that the coal consumption of the furnace was 21/10 21/10 for a pound of zinc recovered. I take it that that is the gross coal input to the furnace. I wonder what the net fuel consumption in terms of coal might be after crediting the fuel equivalent of the waste heat steam recovered? T. J. WOODSIDE—The fuel value of the waste heat steam is approximately 42 pct of the heat input to the furnace. A very large part of the heat, of course, goes out in jacket water—44 pct. A. D. TERRELL*—I would like to know how much lead is in the deleaded material. T. J. WOODSIDE—It is a little less than 2 pct now.

Jan 1, 1950

By G. J. W. Kor, F. D. Richardson

The sulfide capacities a1 1500°C of slags in the systern CaO + CaF, +Al2O3 have been measured by bringing samples into equilibrium with gas mixtures made from CO + CO2 + SO, + N2. The capacities are negligzble both JOY CaF, and CaF, + Al2O3 melts but when lime is present even at 20 wt pct capacilies as high as 30 x lom3 can be obtained. The results have yielded information concerning the liquidus at 1500°C and fluoride-oxide melts in general. The slags used in electroslag refining contain substantial amounts of calcium fluoride. Robinson and Grainger' report that good results can be obtained by using slags of the approximate composition 70 wt pct CaF2 + 30 pct Al2O3. It has also been reported2 that a mixture of 50 pct CaF2 + 30 pct A12O3 + 20 pct CaO makes a good slag for general use. In view of the fact that very low sulfur contents are claimed for ingots produced by the electroslag process. studies have been made of the sulfide capacities [c, = wt pct S (PO2/Ps2)1/2 at 1500°C. of slags consisting of pure calcium fluoride, and of its mixtures with lime and/or alumina. These studies have also provided information on the phase diagrams. The slags were brought into equilibrium with gas mixtures prepared from NZ + CO + CO2 + SO2. Because CaFz is volatile and also easily hydrolyzed. measurements were made of its loss in weight in various flowing gas mixtures. EXPERIMENTAL Procedure. The apparatus and procedure were the same as described previously. Both platinum and iridium crucibles were used (height and inner diameter about 1 cm), but those made from iridium were stronger and able to withstand a greater number of experiments. In each experiment two crucibles were set in an alumina support and 1 g of slag mixture was divided between them. The materials from each crucible were analyzed separately after being brought to equilibrium with the gas, and then quenched in the water-cooled end of the reaction tube. Materials. Alumina and lime were prepared as de-scribed previously.4 Calcium fluoride was obtained by igniting Analar calcium fluoride in a platinum boat at about 800°C in a stream of pure dry nitrogen: the product was cooled in a desiccator. The slags were produced from mixtures of the powdered constituents, these being melted together in the course of each equilibrium experiment. The sulfur analyses and the X-ray diffraction meas- urements on the solidified slags were made as described previously.4 From the latter it appears that the CaF2 contained less than 0.5 mol pct CaO. RESULTS Values of (ps2/po2) for the Gas Mixtures. The re-sults have been represented in terms of (ps, /Po,)"? for the various gas mixtures used. The va1;es of this function at 1500°C are listed in Table I: they were calculated from the data cited previously for calculations at 1350°C 4 Weight Losses with CaF, and CaF, + CaO. The re-sults of the weight loss measurements* at 1500°C for

Jan 1, 1970

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

Binary alloys of titanium with silver, lead, tin, nickel, copper, beryllium, boron, silicon, chromium, molybdenum, manganese, vanadium, iron, and cobalt were studied. One-half-pound ingots of the alloys were prepared in an arc furnace, employing a water-cooled copper crucible, an argon atmosphere, and a water-cooled tungsten electrode. The half-pound ingots were fabricated by forging at 1700°F in air to 1/4-in. slab, followed by hot rolling at 1450°F to 0.060-in. sheet. Tensile properties, minimum bend radii, hardnesses, response to heat treatment and aging treatment, and phase relationships were determined for these alloys. EARLY in 1947, as one phase of the evaluation of materials for Air Force Project RAND, Battelle successfully arc melted Bureau of Mines titanium and obtained a few basic properties of unalloyed titanium and several titanium-base alloys. The low density, excellent resistance to corrosion, and high tensile properties of these materials stimulated a great deal of interest among metallurgists and designers seeking better materials of construction. As a result of this early work, Battelle, under contract with the Air Materiel Command, Wright-Patterson Air Force Base, has continued extensive studies of titanium alloys. The result of the first year's work is described in three papers. The present one deals with binary alloys, the second with ternary alloys, and the third paper with quaternary alloys. Melting Method The arc furnace for melting titanium and other refractory metals was developed at Battelle Institute under Air Force Project RAND. During the present work, considerable improvement has been made in the design and operation of this furnace for making small ingots of titanium and titanium alloys. The improved furnace design is illustrated by fig. 1, which shows a cross-sectional view with the dimensions of various parts and their relationship to one another. The essential features of the furnace are the inert argon atmosphere, the water-cooled copper crucible, and the water-cooled tungsten elec- trode. The melting crucible is formed by spinning 0.064-in. annealed copper sheet. A groove for an O-ring seal is spun into the flange of the crucible. A fiber gasket between the crucible flange and the water-cooled brass cover provides electrical insulation. The brass cover is fitted with a sight glass, an opening for the water-cooled electrode, and a tube through which the material is charged. Direct current is used for melting, with the positive electrical terminal connected to the water jacket and the negative terminal to the electrode. A typical heat is made in the new furnace as follows: Approximately, 0.20 lb of titanium under 2 mesh per in. and the alloy addition, if any is to be used, are placed in the bottom of the crucible. The cover is clamped on the crucible so that the O-rings make a tight seal. The remainder of the charge is placed in a glass bottle, and this is connected by a rubber hose to the charging tube of the furnace. The crucible and the charge are evacuated with a mechanical pump to a pressure below 50 mm of mercury, or less if desired, and held at this reduced pressure for 5 min. Hot water is circulated through the jacket during the evacuation period to assist in outgassing the crucible. Following the evacuation, tank argon of 99.92+ pct purity is flushed through the crucible for 5 min and then adjusted to give a positive pressure of 1 to 2 psi. During subsequent operation, an argon pressure regulator introduces only enough argon to compensate for the small leakage which occurs through a mercury trap. Re-evacuation and reflushing the melting chamber with argon produced a negligible reduction in contamination. Two 550-amp generators, connected in parallel, constitute the power source. Normally, about 800 amp are used for melting alloys which are not extremely refractory. The generators are set for 90 v open circuit and 200 amp. The arc is struck and the electrode is withdrawn to produce an arc of 23 to 26 v. This voltage is maintained while the electrode tip is moved slowly around a circle 1 in. smaller than the diameter of the ingot. The current

Jan 1, 1951

By Joseph R. Stephens

Deformation substructures of' polycrystalline tungsten, W-2, 9, and 24 pct Re, and W-3 pct Ta were studied by tra?zsrnission electron microscopy. The stress-strain curve for unalloyed tungsten showed gradual yielding followed by work-hardening. Electron nzicrographs indicated a gradual increase in dislocation density with increase in strain up to 5.0 pct. Dislocations, although frequently jogged, were straight over moderate distances and were in a randorn array. Stress-strain curves for alloy specimens of W-2 and 9 pct Re and W-3 pct Ta exhibited a drop in stress at yielding followed by only slight work-hardening. Electron micrographs of these specimens after strains of 0.05, 0.1, and 0.5 pct revealed no change in dislocation substructure from the unstrained specimens. After 2.0 pct strain, the three alloys exhibited dense networks. W-3 pct Ta was characterized by straight, frequently jogged dislocations comparable with the dislocation structure in unalloyed tungsten after a similar amount of strain. In contrast, W-2 pct Re exhibited dislocations that contained widely spaced jogs, while W-9 pct Re had developed a cell structure after the relatively srnall strain of 2.0 pct. The W-24 pct Re alloy contained a few dislocations after 0.1 pct strain, while after 0.5 pct strain twins were evident. Dislocation slip bands apparently preceded the twins. The stress-strain curve for the alloy indicated that twinning commenced after approximately 0.25 pet strain. These results indicate that the primary effect of low rhenium concentrations (2 and 9 pct) in tungsten is to increase dislocation multiplication after macroyielding by reducing the Peierls-Nabarro force (lattice resistance to dislocation motion). The dislocation bands that precede twins in W-24 pct Re may be caused by localized internal stresses resulting fro a metastable structure, for example, clustering of rhenium atoms. The effect of high rhenium additions (22 a 65 pet* Rproperties of tungsten. Klopp, Witzke, and Raffo5 reported bend transition temperatures as low as -100°F (200°K) for dilute electron-beam-melted W-Re alloys tested in the worked condition. Recrystalliza-tion increased the bend transition temperature, but alloys with 2 to 4 pct Re were still markedly superior to unalloyed tungsten. Fractographic examinations of tungsten and W- 3 pct Re and W- 5 pct Re alloys by Gilbert 6 revealed that these low rhenium alloys showed a greater tendency toward cleavage failure than did tungsten. Garfinkle 7 showed that rhenium additions, up to 9 pct, to (100) oriented tungsten single crystals increased the proportional limit stress and decreased the flow stress and the rate of work-hardening. In addition, while deformation in unalloyed (100) oriented crystals apparently involved both (110)100) and (112) slip, crystals with rhenium contents of 5 andpct or more deformed primarily by (112) slip. The mechanism by which high and low rhenium additions affect the mechanical properties of tungsten is still not well-established. The present investigation was undertaken to determine by transmission electron microscopy the effects of low rhenium additions, 2 and 9 pct, and a high rhenium addition, 24 pct, on dislocation substructure in the early stages of deformation of polycrystalline electron-beam-melted tungsten. Unalloyed tungsten and a W- 3 pct Ta alloy were included for comparison. EXPERIMENTAL PROCEDURES Materials. Triple electron-beam-melted tungsten, W-2, 9, and 24 pct Re, and W- pet Ta were used for this investigation. Chemical analyses of the cast ingots are given in Table I. A description of the starting metal powders and melting and fabrication pro-cedures for unalloyed tungsten and the W-Re alloys is reported.5 The W-3 pet Ta alloy was processed in a similar manner. Compression specimens measuring 0.300 in. (7.6 mm) in length by 0.130 in. (3.3 mm) in diam were machined from swaged rods. All alloy specimens were annealed in a vacuum of 8 x 10- 6 Torr (10'2iVper sq m) for 1 hr at 3600°F (2255°K). The recrystallized grain size ranged from 0.06 to 0.08 mm diam for the alloy specimens. Unalloyed tungsten was annealed at 2400° F (1589°K) for 1 hr to produce a recrystallized grain diameter of approximately 0.12 mm. Specimens were electropolished in a 2 pet NaOH solution to a diameter of 0.125 in. (3.18 mm) to remove surface notches resulting from grinding and to improve reproducibility of t data. The ends o the compression specimens were ground flat, parallel to each other, and perpendicular to the longitudinal axes with 4/0 emery paper. Compression Tests. The compressive stress-strain apparatus used for compression tests is described in detail by Stearns and Gotsky.9 Room-temperature compression tests were conducted at a crosshead speed of 0.01 in. per min (0.25 mm per min).

Jan 1, 1969

By J. L. Huitt, D. K. Lowe

This laboratory flow study covers propping agent transporl in horizontal fractures as influenced by the characteristics of the propping particles, fluid and fracture. Correlations are presented for the transport of particles, deposition and fingering through dunes. For particles moving individually, the article velocity in some cases may be low compared to the hulk average fluid velocity; in other cases, the particle velocity may exceed the bulk average fluid velocity. At high propping agent concentration or low fluid velocity, the likelihood of particle deposition and dune formation increases. Fingering and channeling accompany dune formation. Dune formation can be limited to the outer region of tile fracture by adjustment of pump rate, fluid viscosity and particle concentration. A method is presented by which pump rate and fluid vircosity may he selected to control dune formation for given propping agent concentrations. INTRODUCTION The area and flow capacity of a fracture predominantly control the stimulation derived from hydraulic fracturing. Generation of fracture area exposes the rock matrix to a flow channel; the flow capacity of the fracture controls the flow through the channel to the wellbore under a given pressure gradient. This paper pertains to an important factor that affects the flow capacity of a fracture: the transport of the propping particles in the fracturing during the hydraulic fracturing treatment. With a better understanding of particle transport, fracturing treatments may be designed to obtain more effective distribution of the propping agent. RELATED STUDIES In recent years, the approach to obtaining high fracture flow capacity has been partial monolayer propping. Three papers1-3 have dealt with various facets of this concept. However, in some papers dealing specifically with particle transport, the results generally indicate that packing the propping particles within a fracture is inevitable. In early work&apos; with a sand slurry flowing in a pie-shaped flow cell, qualitative results showed that particle deposition in a fracture during transport should be expected. In other studies"" correlations based on slurry flow in vertical linear flow cells showed particle deposition was primarily a function of fluid velocity. In a recent paper the rate of sand advance (movement of dunes) in a horizontal linear flow cell was discussed. Subsequently, a method was given for designing fracturing treatments, based on the extent of sand advance during a treatment. In this work, particles whose diameter was small relative to the fracture width (i.e., dl W< 0.2) were primarily considered. The particle transport approaches that of sand transport in a stream bed. The industry trend, however, has been to use larger size propping agents. That is, particles with diameters approaching fracture widths predicted by Perkins and Kern.&apos;&apos; This trend has led to generally better fracturing treatments with particle relative sizes in the range 0.2 <d/W < 1.0. In all of the particle transport studies previously cited, the fluid characteristics were discussed. However, little or no attention was given to the parzicle characteristics. In this study the particles. as well as the fluid and fracture, are considered. VARIABLES AFFECTING PARTICLE TRANSPORT In the exploratory work to set LIP a program for this study, it was noted that particles within a batch moved at different velocities in a horizontal linear flow cell. In some cases the particles moved independently. In others there was particle interference. Also, particle deposition and fluid fingering occurred in some cases (Fig. 1). As a result of observing the easily distinguishab&apos;le types of particle movement, the particle variables as well as the fluid variables were included. In addition, the fracture width was included because the fluid velocity profile surely must affect the movement of the larger particles differently than that of smaller particles. Particle variables were density, diameter (based on a sphere of equal volumetric displacement), long and short dimensions, drag coefficient and velocity. Fluid variables were density, viscosity, yield shear strength and velocity. Fracture variables were the width and the angle between the plane of flow and a horizontal plane. Two factors which may prove to be important were omitted because of the complexity resulting from the parameters cited above. These are the fracture-surface roughness and gross irregularities that cause changes in the direction of flow. EXPERIMENTAL EQUIPMENT AND PROCEDURE A linear parallel-plate flow cell (Fig. 2) was used in the study. Lucite plates 1 in. thick formed the test section and permitted a viewing section 11 ft long and 10 in. wide. Spacing between the plates was adjusted with shims to give fracture widths 1/36 to 1/2 in. The model could be tilted to an angle of 45" with the horizonltal plane. Fluid flow was maintained with a Moyno positive displacement pump. Single particles were placed in the flow stream with a particle injector. A .4 - in. diameter plunger moving at a constant rate in a

Jan 1, 1967

By David R. Maneval, H. B. Charmbury

At the turn of the century, iron and coal were the keys to industrial prosperity. At that time, Pennsylvania was the leading mineral producer in the Country, producing 200,000,000 tons of coal in a typical post-World War I year. Close to 90% of the Nation&apos;s energy was generated by coal. Today, coal accounts for but 22% of the energy generated, leading to a drastic reduction in Pennsylvania coal output. In contrast with the post-World War I days, 1964 figures showed a drop in production to 93,846,480 net tons. This huge decrease has created a serious economic problem in a state so much dependent on the coal industry. Along with the reduction in coal production, employment has dropped considerably through these years (the number of miners alone has gone from 280,011 to 43,149), thus causing a heavy burden of supporting the unemployed on the taxpayers. As far back as 1939, coal operators and economists saw the problems on the horizon and the need for improvement. Realizing that research was a way to improve and stabilize the industry they demanded legislative action. The Legislature reciprocated with a small grant to The Pennsylvania State University with the provision that each State research dollar be backed with one from the industry. This initial grant laid the foundation for the further growth in coal research.

Jan 3, 1966

By R. F. Yap, N. Arbiter, C. C. Harris

A fully-instrumented driving mechanism has been constructed to study the power, aerating and solid suspension characteristics of several laboratory flotation machines. Machines operating over normal flotation speed ranges give substantially constant power numbers in liquid systems indicating that they operate close to fully baffled turbulent flow conditions. Owing to lack of geometrical scaling, power numbers for different sizes of cells of the same make are different. Even larger differences occur between cells of different manufacturers. For a given impeller, varying the tank size did not significantly affect the power consumption. Tank geometry and baffling has a slight effect on power consumption with shrouded impellers. For a given impeller speed, suspension height decreases while power increases with increasing mass of solids in suspension. While power consumption is hardly affected by particle size and clearance between the impeller and tank bottom, the suspension height significantly increases as clearance increases and as particle size decreases. Aeration was found to affect not only power but also the suspension characteristics of the machine. For closely sized particles, drastic sedimentation occurred when a critical value of the air flow number was exceeded. The critical air flow number decreased with increasing particle size. This effect was less marked with a wide particle size range. The self-aerating capacity of flotation machines increases with cell size at a given speed for the same impeller-shroud system, but decreases in the presence of frother and solids. Equations have been established for correlating all of the studied variables. Data taken from the literature were also correlated with these equations. The modern mechanical flotation machine has, over a period of 60 years, displaced other designs to become the dominant type. Once the correct chemical environmental conditions have been established, the major requirement, selective mineral-air adherence, is essentially a function of two operating variables — impeller speed and air rate. The special nature of this dependence is such that in the same apparatus, but under different operating conditions, adherence can be either prevented or destroyed. Another aspect of this observation is that flotation machines though differing in detail to a considerable extent can produce similar metallurgical results. It must be concluded that having determined the correct reagent levels, establishing the correct operating conditions are at least as important as machine design. Since about 1960, after 30 years of fairly stable circumstances, manufacturers have been developing new types of machines whose major feature is emphasis on pulp flow characteristics by virtue of new im-peller-stator designs. As far as can be ascertained, these new designs necessitate radical departures from accepted impeller speed-air rate values. Performance data are still awaited. Flotation machine development has been empirical, as is selection of operating conditions. The purpose of the work at Columbia University has been to elucidate the fundamentals of the subject so that the purely mechanical aspects of the flotation process can be understood in hydrodynamic terms.1-6 Hopefully, this might lead to intelligent selection of a particular machine and its operating conditions for a specific ore based on a minimum of testing, or even to new types of flotation machines. The present investigation is the most comprehensive to date.7,8 Earlier work, which was largely exploratory, has been repeated and extended and employes the most accurate measuring techniques available. Additionally, sufficient hydrodynamic data were obtained under flotation conditions to delineate the relevant operating ranges. Attention has been given to scaling in that several geometrically scaled tanks and impellers have been constructed and tested; it has been pointed out elsewhere that undistorted geometrical scaling rarely pertains in flotation machine design.5 This paper is divided into sections dealing with relevant combinations of the three phases: liquid, air and solid. Summaries of the literature have been given in previous publications2-4 and will not be repeated here. Recently, several reviews of mixing have appeared, which can be usefully referenced.9-11 It is of interest to note that flotation is not included

Jan 1, 1970

By Theodore B. Comstock

The existing topographical features of the United States present many points of interest to the student of dynamical geology, but there is, perhaps, no subject which offers a more promising field for investigation than the relations between the geological structure and the mineralogical characteristics of the principal mining districts. There are seven prominent culminating points in the relief of North America, each one of which can be used as a type of the physical features of all the others. Again, if we divide these seven elevated districts into two sets, we shall discover a still more striking parallelism between the individual members of each group. But the most remarkable revelation is the fact that each one of these points is more or less closely the centre of an area of economically important mineral resources. It is interesting to note in this connection that six of these mineral tracts lie mainly within the borders of the United States, three of them being almost wholly in our territory. For

Jan 1, 1883

By J. F. Emig

The Burns Harbor Plant was designed to produce and process large ingots into plate, hot rolled sheet, cold rolled sheet and tin plate. Rimmed ingots, in particular, are poured 96" to 106" high and weigh up to 85,000 lbs. During the latter part of 1970, a quality problem was encountered involving white line "sliver" defects on the surface of cold rolled, low carbon, rimmed steel sheet. Sheets containing these defects are not desirable for exposed automotive items because of the possibility of opening during forming or becoming more apparent after forming. Metallographic work located and identified two basic types of inclusions within the white line defects: (1) complex oxides consisting largely of iron and manganese oxides and (2) scale-type iron oxide. The presence of these oxides strongly suggested that the-white line defects were resulting from an unsound, unclean rim zone.

Jan 1, 1972

By H. I. Aaronson, H. A. Domian, G. M. Pound

Zener&apos;s two-parameter theory of the y a reaction in Fe-X alloys is extended to encornpass austenite-stabilizing as well as fewite-stabilizing elements, and is then cottzbitzed with statistical thermodynamic theories of Fe-C alloys to permit development of a ther-modynamic description of the proeutectoid fewite reaction in Fe-C-X alloys. Equilibrium tielines are calculated for tile a + y rep&apos;on from experimental data and frort extrapolations of the y/y +a equilibrium surface. Sectzovs of the y/y + 0 surface are calculaled for the tzetastable sstuation LYL u-kich alloyrtg eleitzents do not partition betzseen azrstenite andfer-rite. The finding that the metastable y/a + y curves Lie close to their equilibriuwz counterparts when X = Si, .Vo, Co, Al, and Cu but well below them when X = A/ln or Ari pr-elides a thermodunamic explanation for the expcri1?7e?ztally obserted absence of partition during the proeutec toid ferrite reartlon in the fortner alloys and for the occurrence of partition at hzgher ternperatures in the latter alloys. Cotarison ofno- patitzoa free-energy changes and y/y i a curr,es in Fe-C-X alloys with the equilibrium 11al1es of these quantities in Fe-C alloys furnishes additional qualitative insight into the irqluence of allojling elements upon the kinetics of the proeutectoicl ferrite reaction. THE introduction of a substitutional alloying element, X, appreciably complicates calculation of the thermodynamics of the formation of proeutectoid ferrite from austenite. As noted in the preceding paper,&apos; the positional entropy of the interstitial species is the principal component of the free energy of an interstitial solid solution with which theory has so far been able to deal. One would expect, however, that other components of the free energy of this type of solid solution may be significantly altered by the addition of a substitutional alloying element. Even if the assumptions are made, by analogy to the case of Fe-C alloys,&apos; that changes in the positional entropy of carbon represent a significant part of the thermodynamic effects of an alloying element, and that the remaining effects can be taken into account by fitting the equations developed on this basis to experimental data on Fe-C-X phase diagrams or on the activities of carbon in alloyed austenite and ferrite, the experimental information available on either of these quantities is not yet sufficiently accurate or extensive, respectively, to make such an approach useful. An attempt made by Zener on the former basis to explain the effects of alloying elements on the thermodynamics of Fe-C alloys in terms of a temperature-independent "free-energy change" (actually enthalpy hane&apos;) required to transfer 1 mole of an alloying element from austenite to ferrite, in which the "free-energy change" was determined by fitting the theoretical relationships developed to Fe-C-X phase diagrams, thus proved inadequate in part because of deficiencies in the available ternary-phase-diagram data.= Other difficulties of a more fundamental nature, however, also indicated the desirability of a different approach to the problem.3y4y6 zener6 subsequently proposed that the free-energy change associated with y — a transformation in pure iron can be decomposed into magnetic and nonmagnetic components. Alloying elements were assumed to affect those components separately. One parameter was used to describe the quantitative effect exerted on each component. These parameters were evaluated from Ms (martensite-start) temperature data and from other experimental information usually either readily available or measurable with acceptable accuracy. Zener applied this treatment only to the calculation of Fe-X phase diagrams in which X is a ferrite-stabilizing element. In the present study, this treatment is extended to include austenite-stabilizing elements, and then combined with treatments previously considered for Fe-C alloys1 to permit calculation of the thermodynamic quantities of interest in the austenite - proeutectoid ferrite transformation in Fe-C-X alloys, where a number of representative, and commonly used alloying elements are chosen for X, including Si, Mn, Co, Mo, Al, Cr, and Cu. The results are used to explain important features of the partition of alloying elements between austenite and proeutectoid ferrite, as reported in a companion paper7 on the basis of electron-probe analysis, and to provide some additional understanding of the influence of alloying elements upon the kinetics of nucleation and growth of proeutectoid ferrite. Portions of this treatment6 have been clarified in the course of a review by Kaufman and Cohen.3 The consolidated summary of these developments with which this section is begun provides a basis for further clarification of the treatment, from which extension to include austenite- as well as ferrite-stabilizing elements is a natural consequence. The division of the free-energy change associated with the 7 - a transformation in pure iron, into two independent components is formally stated as:

Jan 1, 1967

By H. C. George

IN 1901, the United States produced 69 million barrels of crude oil, which was 41.4 per cent of the world production. By 1931, these figures were 850 million barrels and 62.1 per cent respectively, showing over this period of thirty years an increase in the world production of 718 per cent. Over this same period, the increase in the demand for technically trained men in the industry was much greater than the increase in crude-oil production. This was because much of the increase in production was secured by the application of geology and physics to the finding of new oil fields and by .the development of engineering methods and equipment incident to drilling and producing from much greater .depths.

Jan 1, 1934

By Ralph H. Sweetser

MUCH progress in -blast-furnace construction and in the manufacture of firebrick for furnace linings has been made since the publication of Bulletin 130 of the U. S. Bureau of Mines on "Blast-Furnace Breakouts, Explosions and Slips, and Methods of Prevention," by F. H. Willcox in 1917. At the time of publishing this report comparatively little information was available to blast-furnace men as to the fundamental facts relating to the character of blast-furnace refractories. Some of the accepted theories of only a few years ago have been completely reversed. The mortality of blast-furnace linings used to be so great that nearly every furnace plant had one or more complete linings in the brick shed ready for use in case of a lining suddenly "going out"; it was generally accepted that a furnace could not "keep her lines" more than two or three years at best, and often a hot spot in the shell would develop, or a breakout occur in the hearth or bosh within a year or two after blowing in on a new lining. In some respects these frequent relinings were not so detrimental as to he a complete loss because they afforded opportunities to take advantage of advances in blast-furnace practice. At present the cost of relining has greatly increased, but the life of a lining has also increased. Anything less than five years on a lining is now considered a short blast.

Jan 1, 1932

On the following pages are abstracts of papers published by the Institute during the year 1936 as TECHNICAL PUBLICATIONS and CONTRIBUTIONS, papers in bound volumes appearing for the first time, and papers in MINING AND METALLURGY For abstracts of papers that appeared in bound volumes in 1936 but that were published as TECHNICAL PUBLICATIONS in 1935, see the YEAR BOOK dated January 1936.

Jan 1, 1937