Search Documents

Jan 1, 1892

[A AALSETH Earl P (M 51) Consult Geol Engr 2019 Eldorado Dr, Billings, Mont ABADIE Henry G (M 43) Asst to. Supt of Oper Long Beach Oil Dev Co 925 Harbor Plaza, Long Beach 2, Calif. ABBET Waldo (A 56) Asst Diet Oper Supt Sun Oil Co P 0 Box 66, Stowelt, Tex ABBOTT Clifton T (A 60) Apartado 677, Maracaibo, Venezuela ABBOTT Fred E Jr (M 59) Abqaiq Diet Mgr Arabian American Oil Co Dhahran, Saudi Arabia ABBOTT J L (M 56) Partner Pritchard & Abbott 1010 Ft Worth Natl Bk Bldg, Fort Worth 2, Tex ABBOTT Richard H (J 51) Partner Abbott & Howard 422 W Hermosa, San Antonio 12, Tex ABBOTT William G (M 50) Div Mgr Rice Engrg &. Operating Inc Box 1142, Hobbs, N. M. ABDERHALDEN Ronald R (J 59) Prod Engr Continental Oil Co Box 100, Carml, 111]

Jan 1, 1961

By W. S. Hyler, W. L. Bruckart

The powder metallurgy and arc-cast types of wrought molybdenum stock were studied in rotating beam fatigue. Endurance ratios of unnotched specimens after 5x10 cycles were found to be 0.74 and 0.81, respectively. Fatigue notch factors (K,) of 1.36 and 2.05, respectively, were obtained on V-notched specimens having a theoretical stress-concentration factor Kt = 3.1. MOLYBDENUM and its alloys are rapidly gaining importance as engineering materials of construction for high temperature applications. AS a wrought material, molybdenum and its alloys are outstanding above 1800°F. It is necessary, however, with molybdenum to provide elevated temperature oxidation protection. This is currently being studied by a number of investigators. Thus far, there have been no published data on the fatigue behavior of molybdenum either at room temperature or at elevated temperature. The knowledge of fatigue behavior, particularly notched fatigue behavior, becomes increasingly important as the engineering importance of a material increases, especially from the design standpoint. The work described here was directed toward determination of the notched and unnotched rotating beam fatigue characteristics of molybdenum at room temperature. Also, it was desired to learn whether any difference exists between wrought molybdenum of the powder metallurgy and the are-cast types. Fabrication History of Bar Stock For this work, bar stock was procured from Climax Molybdenum Co. (are-cast type) and from Westing-house Electric Corp. (powder metallurgy type). The processing histories of these materials are listed in Table I. The first lot of are-cast molybdenum was deoxidized by aluminum additions. The second lot was deoxidized by carbon." Both lots of the powder Microstructure A microscopic examination of these materials, as received, revealed the powder metallurgy molybdenum to be free of inclusions and to be finely fibered. On the other hand, the are-cast C molybdenum possessed numerous carbide inclusions, and the arc-cast A appeared to have coarse grained fibers. These are shown in Fig. 1. Owing to the large apparent difference in fineness of fiber between the are-cast A and the powder product and are-cast C, a check was made of the recrystallized grain sizes to determine whether these differences persisted. A series of recrystallization anneals revealed mixed grain sizes in both the are-cast A and the powder product. Variations in grain diameter of as much as 50 times were found after full recrystallization at 1200°C for 30 min. There was no distinction between the two. Arc-cast C was not checked. Room Temperature Mechanical Properties Prior to subjecting the materials to fatigue tests, room temperature mechanical properties were determined. These data, together with the tensil: strength of the notched bars, data,togetherare listed in Table tensil: There were no significant differences in the tensile strengths of the two types of molybdenum. However, the powder metallurgy material was generally more ductile and yielded at a somewhat lower stress than the arc-cast material. Tensile strengths of the notched specimens indicated a slightly greater notch strengthening effect in the are-cast C than in the powder product, lot 2. Room Temperature Fatigue Properties Sample Preparation: Specimens were prepared for use in R. R. Moore rotating beam fatigue machines. These specimens had a continuous radius test section with a minimum diameter of 0.260 in. The specimens were prepared by grinding to shape and polishing to produce a smooth unworked surface. Polishing consisted of rotating a disk in the continuous radius section on which were attached, successively, emery belts of 240, 400, and 600 grit. The specimens were slowly rotated during the operation. The belt speed was high, and rotation was such that polishing scratches were longitudinal. Unnotched Fatigue Properties: Unnotched fatigue data were obtained from a number of specimens of each of the four lots of molybdenum. The results of the tests are presented in Fig. 2. From this figure,

Jan 1, 1956

By Keith R. Bock, Norman Parlee, Albert M. Barloga

Coils of pure iron and iron-carbon alloy wire (0.05 to 0.80 pct C) and sufficient sulfur to saturate the solid phase were equilibrated in evacuated or argon filled tubes. After rapid cooling, and removal of the outside nonmetallic layer, the wires were analyzed for carbon and sulfur and the data used to construct an Fe-S binary and isotherms of the Fe-C-S ternary in the range 1149° to 1427°C. THE solid solubility of sulfur in steel is of interest in connection with such phenomena as hot shortness, burning, and so forth. "Burning," the more or less permanent damage that some steels suffer when heated for forging or rolling, has been shown to be related closely to the behavior of sulfur and less closely to carbon and oxygen.' Attempts to interpret burning phenomena in steels fail because of lack of data on the Fe-C-S and the more complex systems in this family. Rosenqvist and Dunicz 2 and Turkdogan, Ignatowicz, and pearson3 have largely elucidated the Fe-S diagram in the region of interest but no information on the Fe-C-S diagram in this region appears to be available in the literature. This paper deals with the elucidation of the Fe-C-S diagram in these interesting ranges. The method employed is different from those used by previous workers2'3 on the Fe-S system. EXPERIMENTAL METHOD Pure iron wires (Ferrovac E) or iron carbon alloy wires of 1 mm in diam were cleaned with acid and acetone, coiled, and placed in silica tubes (7 mm OD and 5 mm ID) previously closed at one end. Enough sulfur was added to assure saturation of the solid iron phase. The filled tubes were either simply evacuated and sealed, or filled with argon at a reduced pressure and sealed. The argon was required at the higher temperatures to prevent collapse of the tubes. The filled and sealed tubes were placed in the middle uniform temperature zone of a Globar tube furnace and equilibrated at temperatures ranging from 2100°F (1149°C) to 2720°F (1493°C). After equilibration the tubes were removed from the furnace and quenched in air or water, the form of quenching being found to have no effect on the results. The tubes were broken open and the coils were placed in a 1 : 1 HC1 solution to remove the sulfide-rich layer. The coils were then cut into small pieces and analyzed for sulfur and carbon. In the early stages of the investigation different equilibration times ranging up to 17 hr were tried and the cores of the wires were analyzed to test for saturation. One hour appeared to be sufficient to reach maximum sulfur content at 1454°C and 2 hr sufficient at 1149°C. The practice adopted was to use at least 3 hr at the higher temperatures and at least 5 hr at the lower temperatures. The iron-carbon alloy wires used were made by carburizing pure iron wire with carbon monoxide gas in a one inch diameter ceramic tube at about 1204°C. Differing carbon contents were obtained by allowing fairly large coils to react with the gas for varying lengths of time at a flow rate of 800 cc per min. The reacting times ranged from 15 min to 4 hr depending upon the amount of carbon desired. The furnaces used were controlled by means of Leeds and Northrup Speedomax Type H instruments with D.A.T. Control attachment. Thermocouples were calibrated against the melting points of gold and copper. The temperatures recorded appear to be accurate within i2.7OC. Starting with run No. 85 and continuing with the

Jan 1, 1962

By V. Patarini, M. Salkind

BECAUSE of its high strength and stiffness coupled with low density, continuous boron filament is showing great promise as a potential reinforcement for both metals and nonmetals. Of primary consideration for structural applications is the fatigue behavior of boron fiber composites. Composite fatigue behavior is dependent upon three factors: 1) fiber fatigue behavior, 2) matrix fatigue behavior, and 3) the effect of the interface and fiber ends. The purpose of this note is to describe the behavior of boron filament in rotating beam fatigue. The filament, described by Talley' and Galasso, Salkind, Kuehl, and Patarini,' was made by the hydrogen reduction of boron trichloride on a hot tungsten filament. Testing was performed using a commercial rotating beam wire fatigue tester* described by Votta.~ One end of the test sample is held in a chuck in a synchronous motor. The sample is bent around in a "U" shape, and the other end inserted into a carbide bushing. The maximum strain occurs at the bottom of the "U" where the radius of curvature is a minimum. The strain is adjusted by adjusting the length of the specimen and the location of the bushing. Samples were rotated at 3600 rpm and an automatic shutoff device used to determine the number of cycles to failure. The measurements were accurate to the nearest 360 cycles. The fatigue behavior is summarized in Fig. 1 for fifty-one samples of 4.8 x 10"3 in. diam fibers and ten samples of 3.2 X 10"3 in. diam fiber. The two sample groups represent two different filament production runs and two different nominal size groups. Both groups exhibited nominal tensile strengths of 400,000 psi. No significant difference in the fatigue behavior of the two sample groups is apparent. The scatter in the data is not unexpected for a brittle filament which exhibits a tensile strength distribution with a standard deviation of 10 to 15 pct. Because the test procedure provides a known outer fiber strain in the sample, the maximum stress was calculated assuming a Young's modulus of 58 x 10' psi. This value was selected as being representative of several nominal fiber sizes.2 All of the samples which failed exhibited sudden, catastrophic fracture, and no permanent deformation. One sample was stopped after 1.66 x lo8 cycles at *200,000 psi. The fiber exhibited no apparent damage or deformation. It is apparent that the fatigue resistance of boron filament is quite good. It can therefore be speculated that the fatigue behavior of boron fiber composites would be controlled by the "weaker links", namely matrix fatigue resistance and interface behavior. In fact, preliminary investigations have revealed that this is true for boron-reinforced aluminum? It should be noted that the data presented herein may not necessarily reflect the tensile fatigue behavior of boron filament. It is well-known that boron filament has a radial residual stress pattern with the outer surface in ~om~ression.~ Because of this fact, tensile failure is normally nucleated in the interior of the filament.5 Since the data presented herein is for a rotating beam test in which only the outer surface of the fiber is stressed to the maximum value, it would be incorrect to assume that the failure mechanism and fatigue behavior would be the same if the fiber were tested in tensile fatigue. The fact that many of the data are well above the nominal 400,000 psi tensile strength would tend to support this argument. The authors would like to express their appreciation to the United Aircraft Research Laboratories for supporting this investigation and for permission to publish the results. A portion of this effort was supported by the Air Force Materials Laboratory under contract AF33(615)-2125.

Jan 1, 1968

By Dwight H. Seely, Louis R. Records

A process for low-temperature dehydration of natural gas utilizing Joule-Thomson effect in expansion through a throttling orifice has been tested in a full-scale field installation. The results of these tests are presented in the form of performance curves from which the process may be easily evaluated. The effect of separation temperature on condensate recovery from the process is also shown. INTRODUCTION The transportation of natural gas from producing well to the consumer has always encountered the problem of hydrate prevention. This problem has become increasingly important in the past ten years due to the rapid increase in produced gas volumes, production pressures, transportation pressures and distance from producing wells to consumer. Natural gas, as normally produced from gas or gas-condensate wells, is saturated with water vapor at well-head conditions of temuerature and pressure. The solution of the hydrate problem require; but one basic process — dehydration of the gas to a water content which will result in a water dew-point below the minimum temperature to be encountered from the producing well to the point of consumption. Much of the recent development of gas and gas-condensate reserves in the Gulf Coast Area has been in locations which are accessible only by water. High well-head pressures, pipeline construction and maintenance costs and the desirability of final central gas-condensate separation facilities have stimulated the development of dehydration equipment which can be installed at each well and which will permit hydrate-free transportation of both gas and condensate in the same line to central facilities. There are four types of natural gas dehydration processes now used: 1. Adsorptive processes. 2. Absorptive processes. 3. Chemical reaction processes. 4. Refrigeration processes. The first three of these processes are indirect in that they require use of adsorbents, absorbents or reactive chemicals. These materials require regeneration and part of the total gas stream is consumed in the regenerative process. Indirect processes have a wide range of flexibility as defined by allowable operating pressure and temperature, but most are not easily adapted to automatic operation. The refrigeration process described in this paper was designed for installation at the producing well-head. It requires no regenerative cycle and with normal well-head temperatures no external source of heat. The flexibility of this process is limited only by the pressure drop which may be allowed between well-head and transportation line. THEORY There are three basic physical concepts involved in the low temperature dehydration process. These are: 1. Formation of hydrocarbon hydrates. 2. Joule-Thompson effect resulting from the expansion of gaseous mixtures through a throttling orifice. 3. The equilibrium composition characteristics of water vapor and gaseous hydrocarbon mixture.. The chemical composition and physical structure of hydrate; have been described by several investigators.3,4,5,10 Specific conditions of temperature, pressure and composition as well as the requirements for turbulence and presence of free water necessary for hydrate formation have been described by Katz.6 Natural gas hydrates, as they are found in plugged gas pipe lines, have the appearance of packed snow. The mass of these hydrates has low continuous porosity and permeability. Joule-Thomson effect. or the reduction in temperature which occurs when natural gas is throttled throusll a restrictive orifice, is the basic phenomenon which permits efficient use of refrigeration for the purpose of dehydrating natural gas. Joule-Thomson coefficients for gafeous mixture; of methane with ethane and with butane have been reported by Buder.-I~olzer, Sage and Lacey.2 Brown1 predicted temperature drops for pressure drops from enthalpy-entropy calculations. Aside from this work there were no fundamental data found which would be applicable to natural gas mixtures of varying spe-

Jan 1, 1951

By Dwight H. Seely, Louis R. Records

A process for low-temperature dehydration of natural gas utilizing Joule-Thomson effect in expansion through a throttling orifice has been tested in a full-scale field installation. The results of these tests are presented in the form of performance curves from which the process may be easily evaluated. The effect of separation temperature on condensate recovery from the process is also shown. INTRODUCTION The transportation of natural gas from producing well to the consumer has always encountered the problem of hydrate prevention. This problem has become increasingly important in the past ten years due to the rapid increase in produced gas volumes, production pressures, transportation pressures and distance from producing wells to consumer. Natural gas, as normally produced from gas or gas-condensate wells, is saturated with water vapor at well-head conditions of temuerature and pressure. The solution of the hydrate problem require; but one basic process — dehydration of the gas to a water content which will result in a water dew-point below the minimum temperature to be encountered from the producing well to the point of consumption. Much of the recent development of gas and gas-condensate reserves in the Gulf Coast Area has been in locations which are accessible only by water. High well-head pressures, pipeline construction and maintenance costs and the desirability of final central gas-condensate separation facilities have stimulated the development of dehydration equipment which can be installed at each well and which will permit hydrate-free transportation of both gas and condensate in the same line to central facilities. There are four types of natural gas dehydration processes now used: 1. Adsorptive processes. 2. Absorptive processes. 3. Chemical reaction processes. 4. Refrigeration processes. The first three of these processes are indirect in that they require use of adsorbents, absorbents or reactive chemicals. These materials require regeneration and part of the total gas stream is consumed in the regenerative process. Indirect processes have a wide range of flexibility as defined by allowable operating pressure and temperature, but most are not easily adapted to automatic operation. The refrigeration process described in this paper was designed for installation at the producing well-head. It requires no regenerative cycle and with normal well-head temperatures no external source of heat. The flexibility of this process is limited only by the pressure drop which may be allowed between well-head and transportation line. THEORY There are three basic physical concepts involved in the low temperature dehydration process. These are: 1. Formation of hydrocarbon hydrates. 2. Joule-Thompson effect resulting from the expansion of gaseous mixtures through a throttling orifice. 3. The equilibrium composition characteristics of water vapor and gaseous hydrocarbon mixture.. The chemical composition and physical structure of hydrate; have been described by several investigators.3,4,5,10 Specific conditions of temperature, pressure and composition as well as the requirements for turbulence and presence of free water necessary for hydrate formation have been described by Katz.6 Natural gas hydrates, as they are found in plugged gas pipe lines, have the appearance of packed snow. The mass of these hydrates has low continuous porosity and permeability. Joule-Thomson effect. or the reduction in temperature which occurs when natural gas is throttled throusll a restrictive orifice, is the basic phenomenon which permits efficient use of refrigeration for the purpose of dehydrating natural gas. Joule-Thomson coefficients for gafeous mixture; of methane with ethane and with butane have been reported by Buder.-I~olzer, Sage and Lacey.2 Brown1 predicted temperature drops for pressure drops from enthalpy-entropy calculations. Aside from this work there were no fundamental data found which would be applicable to natural gas mixtures of varying spe-

Jan 1, 1951

By E. I. Salkovitz, F. W. von Batchelder

DURING the last few years several papers1-' have been published in which internal friction measurements have been used to determine the quantity of carbon or nitrogen dissolved in a iron. This method is based on the fact that, in pure Fe-N and Fe-C alloys, nitrogen and carbon cause peaks in the internal friction vs. temperature curve; at a frequency of 1 cycle per sec (cps) these peaks appear at $-200 and +360C, respectively, and if internal friction is expressed as Q-1, which is equal to times the logarithmic decrement, this figure will, by coincidence, give the weight percentage of nitrogen or carbon in solid solution.' In most of the studies published, very pure iron (Puron) was used. In one case the influence of manganese on the behavior of nitrogen in a iron was mentioned.4 It would be of great value, especially for the study of aging and related phenomena, if this method could be applied to commercial mild steel with norrnal percentages of manganese, phosphorus, sulphur, etc. As a rule, in such steels carbon and nitrogen are present together, and the amounts of these elements in solid solution should preferably be determined separately. The fact that their internal friction peaks appear at different temperatures (+36° and + 20°C in pure iron) seems promising for such a selective determination. It is necessary, however, that the peaks are narrow enough not to interfere with one another, and further, that there is no effect from carbon on the behavior of nitrogen in stress induced diffusion, and vice versa. According to Fast,' however, in the presence of manganese the nitrogen peak gets wider and appears at a higher temperature nearer the carbon peak, and thus the prospects for selective determination are reduced. (The carbon peak was not affected by the presence of manganese.) But even if fully quantitative de- terminations of the two elements are not attained, some relative figures on the sum of them and an indication of which one is the predominant one, would be of value. Some results from experiments along these lines will be reported here. An internal friction measuring device was assembled mainly following a description by KG." The measurements were also carried out as reported in that paper. Table I gives the chemical compositions of the four different materials used in this investigation. All materials were drawn to wires with diameter about 0.8 mm, and the analyses refer to these final shapes. Determination of Nitrogen Peak Wires from steels A, B, and C were decarburized in wet hydrogen (about 30 pct H2O) at 700°C until no carbon or nitrogen could be found by chemical analysis. No peak was then found in the internal friction. The wires were further annealed at 580°C for 16 hr in hydrogen bubbled through a solution of 6.8 pct NH3 in distilled water. Chemical analyses gave 0.04 pct N in A and C, and 0.06 pct in B. After annealing at 580°C for 15 min in a lead bath and water quenching, the internal friction was immediately measured. The resulting curves are shown in Fig. 1. At these high values of the internal friction the accuracy is comparatively poor; at Q-1 - 0.030 it is estimated to be 0.002. In order to make possible a calculation of the activation energy for diffusion of nitrogen, measurements were made at two different frequencies. Steel A shows rather broad peaks, and their temperatures can hardly be expected to be very accurate. Steels B and especially C are better in this respect. The finding of Fast' that manganese broadens the nitrogen peak is con-

Jan 1, 1953

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2'3 and

Jan 1, 1969

By J. M. Dumore

If in a vertical, downward miscible displacement, the transition zone between the displacing and displaced fluids is neglected, a criterion for stable displacement can be obtained by considering a small hypothetical protrusion of one of the fluids into the other. This criterion leads to the definition of the well-known critical rate, uc = kg p/p. The consideration is further extended by taking into account the transition zone that develops as a result of diffusion and mixing. A generalization of the previous criterion leads to the definition of another characteristic rate, the stable rate, which in actual miscible drives will be less than the critical rate. In such drives, the entire transition zone is stable at rates less than the stable rate. At rates between the stable and critical rates, the displacement is only partly stable, i.e. part of the transition zone adjacent to the displaced fluid is in an unstable position. From that part of the transition zone viscous lingers will develop. At rates greater than the critical rate the entire displacement is unstable and viscous lingers will develop more strongly. Results of laboratory experiments are in agreement with the expected behavior based on the theoretically deduced stability of the displacement. INTRODUCTION The simplest form of miscible drive in an oil-bearing formation is the injection of a fluid that is completely miscible* with the oil under reservoir conditions. In general, such a fluid, a solvent for example, is less dense and less viscous than the oil present in the formation. If it is injected into a horizontal homogeneous layer, gravitational forces will lead to the formation of a gravity tongue of solvent in the upper part of the layer and the adverse solvent-oil viscosity ratio will cause viscous fingers to develop. If, however, the solvent is injected up-structure into ,a dipping layer, gravity has a favorable effect, because it tends to keep the less dense solvent up-structure. Tongue formation and viscous fingering are consequently reduced and it is even possible that they will be suppressed completely. Viscous fingering and gravity tonguing are the consequences of the instability of the displacement. A stable displacement cannot result in growing viscous fingers and/or growing gravity tongues. Since large amounts of oil can be bypassed if there is viscous fingering and/or gravity tonguing, the stability of a miscible drive is very important with respect to the recovery efficiency of the drive. The stability is of particular importance in miscible-slug drives, as it determines how quickly the miscible slug between the displaced and displacing fluids will be distorted and broken up, after which the drive is no longer completely miscible. Stability is thus a most important factor in determining the success of a miscible drive, and it is considered that the aspects of stability considered in this paper will make a useful contribution to existing theories. Consideration is given only to vertical downward displacements, in which no gravity tongues can develop and which are therefore simpler than downward displacements in sloping layers. THEORY CRITERION FOR STABLE DISPLACEMENT Let us consider a vertical column of a homogeneous permeable medium saturated with oil. A solvent less dense and less viscous than the oil is injected at the top of the column at a constant rate; in the column the velocities of oil and solvent are assumed to be uniform. Diffusion and mixing of oil and solvent will at first be neglected, i.e. we assume that solvent and oil are divided by a sharp interface. An additional assumption is that the interface is horizontal. Continuity of pressures exists at the interface, because no capillary forces are present between the two miscible fluids. Consequently, at the interface (Z = I)):** Ps = Po - P-where Ps is the pressure at the solvent side and

Jan 1, 1965

By J. P. Hammond, C. J. McHargue, S. E. Adair

Cold-rolled sheet textures have been determined for binary solid solutions of aluminum, columbium, tantalum, and zirconium in titanium. An alloy containing 3.8 pct Al had a (0002) [10101 texture, whereas alloys with the other elements had rotated (0002) [10101 textures similar to that of iodide titanium. THERE have been relatively few studies of the effect of alloying on deformation textures. A second element may be present in the base metal in solid solution and/or as a second phase. The literature offers no satisfactory explanation for the effects of solid solution alloying on textures noted thus far. For example, there is no satisfactory explanation of the difference in the textures of copper and a brass. The most complete study of the effects of solid solution alloying on deformation textures has been that of Brick, Martin, and Angier.¹ These investigators reported that the copper texture was retained by alloys of copper with up to 30 pct Ni, less than 5 pct Zn, less than 2 pct A1 or Co up to the limit of solubility. Copper containing more than 5 pct Zn, more than 2 pct Al, or the maximum soluble concentration of tin, silicon, or manganese showed the deformation texture of a brass. Bakarian² reported that additions of 0.20 pct Ca to 99.98 pct Mg or 2.0 pct Mn plus 0.15 pct Ca to magnesium resulted in entirely different textures than for the pure magnesium. The texture obtained for high-purity magnesium sheet showed the basal plane to be concentrated parallel to the rolling plane. The texture obtained for the alloy containing 0.20 pct Ca had the basal planes concentrated in elliptical areas whose centers were tilted 15" from the center of the pole figure toward the rolling direction. This split basal orientation was even more pronounced in the alloy containing 2.0 pct Mn and 0.15 pct Ca. Fuller and Edmunds" studied the rolled sheet textures in a zinc alloy containing 1 pct Cu and 0.01 pct Mn. The basal pole figure of this alloy contained a region of strong concentration not found in the pole figure for pure zinc.' In the above cases, results were discussed in terms of possible changes in slip and/or twinning systems and critical shear stresses. However, there were no experimental data to relate these speculations with the observed textures. It has been suggested that the deformation textures of titanium, zirconium, and beryllium could be directly ascribed to their low c/a ratios. The complex deformation mechanisms of titanium" also have been suggested to be characteristic of hexagonal close-packed metals with low c/a ratios. The purpose of this investigation was to study the cold-rolled sheet textures in binary titanium-base a alloys in which the c/a ratios were greater than, less than, and about the same as the c/a for iodide titanium. The annealed textures of these alloys will be reported in a subsequent article. Materials and Methods The chemical analyses of the metals used in this investigation are given in Table I. The alloys were prepared as 15 g buttons on a water-cooled copper block in a vacuum arc-furnace. The furnace was evacuated to pressures of the order of 10.' mm Hg, flushed with 99.98 pct pure argon, and melting was carried out in 0.2 atm pressure argon. Each button was remelted until radiographs and chemical analyses indicated complete solution of the solute elements. All buttons were forged and homogenized 72 hr at 500°C. The buttons to be rolled were ground and etched to sizes and shapes suitable for the rolling

Jan 1, 1954

By Gerald Sherman

MINING asbestos ore by caving at Thetford Mines, Quebec, has been described in the Transactions of the Canadian Institute of Mining and Metallurgy in papers presented by the staffs of The Asbestos Corp. Ltd., in 1934, and Johnson's Co. Ltd., in 1941. The production by caving prior to 1949, in round figures, has been 14,500,000 tons of ore by The Asbestos Corp. and 5,500,000 by Johnson's Co. They are the only caving operations in asbestos at the present time. The Jeffrey mine of the Canadian Johns-Manville Co. at Asbestos, 40 miles southwest of Thetford, is well along in preparations for caving, and The Bell Asbestos Mines Ltd. at Thetford Mines, will follow their examples later. GERALD SHERMAN, Member AIME, is Consulting Engineer, Johnson's Co. and Canadian Johns-Manville Co., New York, N. Y. AIME San Francisco Meeting, Feb. 1949, and New York Meeting, Feb. 1950. TP 2828 A. Discussion (2 copies) may be sent to Transactions AIME before May 31, 1950. Manuscript received Nov. 2, 1949. Nearly all of the asbestos produced by the western hemisphere is mined in those districts of Canada. Since it has been the subject of a number of technical papers, this contribution is offered as a review of progress. Some introductory information seems appropriate, for few members of the American Institute of Mining and Metallurgical Engineers are familiar with the mineral, or how asbestos deposits differ from others in caving characteristics. Asbestos is found in peridotite, a basic intrusive rock irregularly altered to serpentine and erratically fractured, well enough to cave in bulk, but leaving many blocks of solid ore of all sizes scattered through the deposit. Chrysotile is the variety of asbestos produced in Canada. Its fibers are the most valuable commercially, having a good proportion of long fibers, strong, silky, flexible, and suitable for spinning. The fibers occur in all lengths, from the microscopic to 3 in., or more, the shorter are more abundant. Their values depend on length combined with other qualities noted above. They occur as veinlets filling fissures in the peridotite, with crystals compactly arranged in parallel across the cracks. They are sometimes lightly frozen to the walls but the partings are distinct, often marked by particles of magnetite adhering to the fiber ends. Sometimes they break away from the rock in slabs an inch or more in thickness. In wide fissures the fibers are not always continuous, the "broken fibers" being separated by lines of parting with occasional scattered grains of magnetite, which is an injurious mineral to be elirninated when possible. In addition to the chrysotile ''Cross fiber," some "slip fiber" is found in fault fractures in limited quantities of less valuable character. With the exception of the Asbestos Corp, ore, in which the content is said to be more uniform, asbestos is eccentrically distributed through the peridotite. It is the general impression that the higher grades are more often found in hard rock. There are rich pockets and leaner areas which range down through various grades to minor barren sections. Wholesale mining is necessary to make sure of recovering all the high grade for there are no reliable indications of its existence. Ore selection only appears in constructing assay-grade limits for caving. The mill yield of the Thetford ore body in 1934 was 6 to 10 pct of the ore milled, made up of all classes, with occasional runs up to 15 pct or so. Quotations for Canadian asbestos* are as follows: Per Ton No. 1 Crude (% in. and longer) $896 @ $960 No. 2 Crude (Y8 to % in.) 350 @ 545 Spinning (less than % in.) 204 @ 378 Other classes, price diminishing with length. Shorts or "refuse" 24 @ 46 • From Eng. and Min. Jnl., Nov. 1948. Asbestos of even superior quality for electric insulation is found in Arizona limestone. It is white, containing very little combined iron, but occurs only in small quantities.

Jan 1, 1951

By C. S. Matthews, P. Hazebroek, F. Brons

A method has been developed for calculating the average pressure in a bounded reservoir. The reservoir is first divided into the individual drainage volumes of each well, by using the criterion that at steady state each individual drainage volume is proportional to a well's production rate. The average pressure in each drainage volume is then calculated by a method developed in the report. By volumetrically averaging these individual drainage volume pressures, the average pressure in the entire reservoir is obtained. To calculate the average pressure in each drainage volume, a correction is applied to the ordinary extrapolated pressure, i.e., the pressure obtained by extrapolating to infinite time the linear portion of the graph of closed-in pressure versus log[?t/(t + ?t)], where At is the closed-in time and t the production time. The correction, which is a function of the production time, is presented in graphical form for different shapes of the drainage area (horizontal cross section of the drainage volume). INTRODUCTION It is important to be able to find the volumetric average pressure in a reservoir so that the size of the reservoir may be determined from material balance calculations. It is also desirable to be able to find the approximate distribution of pressure within a reservoir for detection of fluid movement. 'The purpose of this paper is to present a method for calculating both the average reservoir pressure and the approximate distribution of pressure within a bounded reservoir — that is, a reservoir with no water drive. In reservoirs where the pressure builds up rapidly after wells are shut in, the determination of average pressure generally poses little problem, for one often need only average the final buildup pressures. It is when pressure buildup is slow that difficulties arise. For practical and economical reasons, the time allowable for closing in wells is limited. If at the maximum allowable closed-in time the pressure has not reached a con- stant value (and this is more often the case than is generally realized), calculation of average pressure presents difficulties. One method which has been used in the past for obtaining an "average" pressure involves the extrapolation to infinite closed-in time of curves of pressure as a function of closed-in time. Contour maps of these extrapolated pressures are used in arriving at an average pressure. In some cases wells are shut in for arbitrary Lengths of time, and contours of these arbitrary shut-in pressures are used for calculation. All these methods are somewhat arbitrary and suffer from lack of fundamental theoretical basis. For example, no precise meaning can be given either to the extrapolated or to the arbitrary shut-in pressure. Furthermore, there seems to be no reason why either set of pressures should be contourable. It was because of the vagueness of these old methods and their lack of a sound theoretical basis that, the present method for determining average reservoir pressure was developed. SYMBOLS A = drainage area of a well, cm' A, = drainage area of well j, cm2 A , = total drainage area of all wells in a reservoir, cm2 c = coefficient of compressibility of fluid at reservoir temperature, atm-1 f = hydrocarbin-filled porosity, fraction h = net thickness of formation, cm k = permeability of formation, darcy p = pressure at a well, atm p0 = initial reservoir pressure, atm p* = pressure obtained by straight-line extrapolation of linear portion of plot of p versus log [At/(t+ At)] p = volumetric average pressure inside drainage volume of a well q = volume flow rate at a well, cc/sec a: prevailing reservoir conditions q, = total volumetric flow rate from a reservoir, cc/sec at prevailing reservoir conditions rw = radius of well bore, cm T = kt/fµcA t = corrected time of production of a well, seconds, defined by

Jan 1, 1955

By J. T. Norton, N. J. Grant, A. M. Gervais

An investigation of the creep deformation of coarse grained specimens of high purity aluminum in the temperature range 800' to 1150°F, permitted the formulation of a theory explaining the formation of kink bands. The X-ray Laue back-reflection technique was used in conjunction with metallographic studies to determine the crystallographic elements involved in kinking and to measure the rotations of the bands. THAT metals deform by the formation of kink bands was first shown by Orowan1 in 1942. He manually compressed cadmium single-crystal wires, the basal planes of which were parallel to the wire axis and to the direction of compression. He found that kink bands formed quite suddenly. Similar experiments were performed by Hess and Barrett2 on zinc with a hydraulic testing machine to permit slower more careful compression. They observed that kink bands formed progressively with increasing compression. Recently Washburn and Parker3 observed the formation of kink bands in zinc single-crystal specimens during tension creep experiments. Each of these authors observed the formation of kink bands but did not make a complete analyses of the crystallographic relationships. In addition to these studies on hexagonal metals, extensive investigations of kink bands formed during deformation of aluminum in tension at room temperature have been reported. Two types of deformation bands have been observed during the deformation of aluminum at room temperature. These are: 1—kink bands: these exhibit a sharp curvature of the lattice along certain surfaces, and 2—bands formed by secondary slip along certain regions. As has already been shown by Honeycombe,4 it is important to point out the difference characterizing the two types of deformation bands. In the first case. for moderate deformation, only one system of slip planes normally is active; in the second case, however, two slip systems are active in the deformation bands. The latter have a rumpled surface because of the action of the two slip systems. In the present work only the first type of band was studied and to avoid any confusion the term kink band will be used exclusively in the discussion which follows. Honeycombe' observed that very narrow kink bands (width, 0.01 mm) formed along the (110) planes during the deformation of high purity aluminum at room temperature. He observed narrower ones in commercially pure aluminum and found also that their width decreased with decreasing temperatures. Chen and Mathewson5 reported the formation of kink bands during tensile testing of single crystals of high purity aluminum at room temperature and pointed out that some rotation occurred about a [211] direction. The influence of the bending moment on the formation of kink bands was illustrated by the experiments of Rohm and Kochendorferl0 who used a Polanyi apparatus to obtain pure shear during tensile testing of high purity aluminum single crystals. Under such conditions only one slip system was active and no kink bands were observed; consequently, no noticeable asterism was detected after deformation. The influence of the bending moment will be discussed later. Calnan8 gave a detailed account of the work performed on kink bands obtained during deformation of aluminum at room temperature. Because no explanation of the process of kink band formation in creep was given in the previous investigations and because some of the above observations are vital to the following discussion the brief review of the literature has been given. It is proposed in the present work to provide an explanation of kink band formation during creep deformation at elevated temperatures. Results and Discussion Kink bands were observed to form during tensile creep testing of high purity (99.995 pct) aluminum specimens, having a very large grain size, in the temperature range 800" to 1150°F. These observations were made in grains which occupied the whole cross section of the specimen. The specimens were originally round (diameter, 0.187 in.; gage length, 1 in.) and had parallel flats milled to permit easier metallographic and X-ray observations. The final

Jan 1, 1954

By Gerald Sherman

MINING asbestos ore by caving at Thetford Mines, Quebec, has been described in the Transactions of the Canadian Institute of Mining and Metallurgy in papers presented by the staffs of The Asbestos Corp. Ltd., in 1934, and Johnson's Co. Ltd., in 1941. The production by caving prior to 1949, in round figures, has been 14,500,000 tons of ore by The Asbestos Corp. and 5,500,000 by Johnson's Co. They are the only caving operations in asbestos at the present time. The Jeffrey mine of the Canadian Johns-Manville Co. at Asbestos, 40 miles southwest of Thetford, is well along in preparations for caving, and The Bell Asbestos Mines Ltd. at Thetford Mines, will follow their examples later. GERALD SHERMAN, Member AIME, is Consulting Engineer, Johnson's Co. and Canadian Johns-Manville Co., New York, N. Y. AIME San Francisco Meeting, Feb. 1949, and New York Meeting, Feb. 1950. TP 2828 A. Discussion (2 copies) may be sent to Transactions AIME before May 31, 1950. Manuscript received Nov. 2, 1949. Nearly all of the asbestos produced by the western hemisphere is mined in those districts of Canada. Since it has been the subject of a number of technical papers, this contribution is offered as a review of progress. Some introductory information seems appropriate, for few members of the American Institute of Mining and Metallurgical Engineers are familiar with the mineral, or how asbestos deposits differ from others in caving characteristics. Asbestos is found in peridotite, a basic intrusive rock irregularly altered to serpentine and erratically fractured, well enough to cave in bulk, but leaving many blocks of solid ore of all sizes scattered through the deposit. Chrysotile is the variety of asbestos produced in Canada. Its fibers are the most valuable commercially, having a good proportion of long fibers, strong, silky, flexible, and suitable for spinning. The fibers occur in all lengths, from the microscopic to 3 in., or more, the shorter are more abundant. Their values depend on length combined with other qualities noted above. They occur as veinlets filling fissures in the peridotite, with crystals compactly arranged in parallel across the cracks. They are sometimes lightly frozen to the walls but the partings are distinct, often marked by particles of magnetite adhering to the fiber ends. Sometimes they break away from the rock in slabs an inch or more in thickness. In wide fissures the fibers are not always continuous, the "broken fibers" being separated by lines of parting with occasional scattered grains of magnetite, which is an injurious mineral to be elirninated when possible. In addition to the chrysotile ''Cross fiber," some "slip fiber" is found in fault fractures in limited quantities of less valuable character. With the exception of the Asbestos Corp, ore, in which the content is said to be more uniform, asbestos is eccentrically distributed through the peridotite. It is the general impression that the higher grades are more often found in hard rock. There are rich pockets and leaner areas which range down through various grades to minor barren sections. Wholesale mining is necessary to make sure of recovering all the high grade for there are no reliable indications of its existence. Ore selection only appears in constructing assay-grade limits for caving. The mill yield of the Thetford ore body in 1934 was 6 to 10 pct of the ore milled, made up of all classes, with occasional runs up to 15 pct or so. Quotations for Canadian asbestos* are as follows: Per Ton No. 1 Crude (% in. and longer) $896 @ $960 No. 2 Crude (Y8 to % in.) 350 @ 545 Spinning (less than % in.) 204 @ 378 Other classes, price diminishing with length. Shorts or "refuse" 24 @ 46 • From Eng. and Min. Jnl., Nov. 1948. Asbestos of even superior quality for electric insulation is found in Arizona limestone. It is white, containing very little combined iron, but occurs only in small quantities.

Jan 1, 1951

By R. J. Teitel

The Pb-U system has been investigated by X-ray, thermal, and microscopic analyses. Two pyrophoric intermetallic compounds were found; UPb3 and UPb. The crystallographic structure of UPb3 is reported. A phase diagram was drawn for the system showing three eutectic and one syntectic reaction. AS a result of the interest in uranium metallurgy, the Pb-U system has been investigated. Practically no quantitative data appears in the literature concerning this system. Chips were machined from bars of high-purity uranium obtained from Ames Laboratory and the lead was 99.9 pct high-purity grade from Bel-mont Smelting & Refining Co. The chips were pickled in a dilute solution of nitric acid, washed in water and then alcohol, and dried prior to use for alloy preparation. The lead was simply sheared from the pig with no chemical treatment. Lead and uranium were placed in graphite crucibles and loaded into an induction furnace. In order to insure good alloy formation, the lead was loaded above the uranium to wash the uranium chips into the melt. After the charge was held at the desired preparation temperature for 15 to 30 min, it was allowed to cool in the crucible. The entire melting operation was accomplished in an atmosphere of helium (double charcoal refined grade with no further treatment). The procedure was to outgas the furnace by first evacuating it to 10-% m Hg, admitting helium to 8 psi gage and sealing the furnace off. An optical pyrometer focused on the charge through a hole in the crucible cover was employed for thermal measurements. Usually a 50° to 70°C correction had to be added to the instrument value. The most suitable alloy preparation temperature range was found between 1220° and 1280°C. The reason for this is explained by the phase diagram, Fig. 7. Above this temperature range two liquids separate preventing alloy formation upon cooling at a reasonable rate. On the other hand, below this range the uranium was coated with a layer of both compounds and the rate of reaction was diminished by diffusion processes. The fastest reaction rate occurred in this narrow range of temperature because only UPb coats the uranium and it evidently does not protect the uranium as well as UPb,. Apparatus and Procedures The development of apparatus and techniques was determined by the peculiar properties of the alloys. All the alloys were pyrophoric, and, consequently, the alloys had to be protected from oxidation by handling them in a dry box or inert atmosphere furnaces. Other operations performed outside of this equipment had to be done as quickly as possible. Thermal analyses were conducted in a furnace and arrangement similar to that described by the author.' Graphite crucibles having a thermocouple well in the bottom were used to contain the prepared alloy, while a helium atmosphere protected the melt from oxidation. The furnace was outgassed by pumping a 10-3 mm Hg vacuum until the furnace had been heated to 400°C. Then helium was admitted and the furnace sealed under 8 psi gage pressure. Chromel-alumel thermocouples were used for thermal analysis and the accuracy of thermal measurements was judged to be k 5°C. At first, an attempt was made to use platinum-platinum-rhodium thermocouples, but evidently lead vapors attack it at high temperatures forming low melting alloys. These lead vapors had direct access to the thermocouple because the graphite crucible was porous. A differential temperature control was used to regulate thermal analyses. The thermal gradient across an alundum tube placed between the windings and the crucible was maintained constant by a controller.

Jan 1, 1953

By G. S. Cole, G. F. Bolling

ThE exact type of fluid flow which occurs in a solidifying ingot is important in determining subsequent grain structure. This has been shown in studies of natural Convection" and of forced stirring or other disturbances of the melt."16 We shall explicitly argue that a complement to the existing natural flow in an ingot should be more effective than other types of flow in promoting the columnar-to-equiaxed transition. The ultimate effects of fluid flow upon structure is one of the topics of solidification that we have investigated in the alloy system Pb-Sb, under conditions simulating casting. In Fig. 1, the essential features of a bidirectional growth apparatus are shown; horizontal freezing from water-cooled faces within a low-thermal-conductivity lavite boat is a reasonable simulation of an ingot section. Details such as the furnace and thermocouples are omitted in order to show the location of four permanent. magnets, each with a pole separation of 21 in. providing a central field of about 1000 Gauss. When coupled with a dc current imposed through appropriate connections made at the cooled faces, a flow of fluid is produced as shown schematically. This technique described by Pfann and ~orsi" is ideal for our purpose since the flow indicated is the same as that we observe to occur naturally in this system. Components of 99.999 pct purity were used for study and all due precautions were taken in alloy preparation to avoid contaminants. Sections of the specimens were taken to ensure results representative of the interior as well as the surface of specimens. All proportions of equiaxed and columnar regions were measured by tracing the etched grain structures onto graph paper and simply counting squares. Four alloys were examined at superheats of 40" * 5°C and 100" * 9°C. Preliminary tests had shown that no appreciable enhancement of structure was obtained with magnetic field alone, so that this condition is not reported; it should nevertheless be noted that other configurations of magnetic field will reduce convection and thus enhance columnar growth.'8 For the tests reported the magnetic field was applied to a specimen by bringing the four preassembled magnets to a position 2 mm from an outer tube immediately after the ingot was poured. The dc current of 30 amps passed through the sample throughout the entire solidification cycle, resulting in a power dissipation of 9 w per sq cm of interface. This may be compared to the evolution of latent heat of approximately 18 w per sq cm. Table I contains the results of this experiment in terms of the total area ratio, equiaxed/columnar grains, as a function of the field interactions, solute concentrations, and superheats employed. The total structure of the ingot is seen to be most influenced when both the field and current are applied simultaneously; when current acts separately, little effect may be noted in spite of the heat supplied. In addition, the change in structure from the no field-no current case to the field-current condition is more pronounced at the higher superheat, and the higher the concentration of antimony. An example of the grain refinement, as well as the increased equiaxed zone, is shown in Fig. 2. It is now important to prove that there is indeed an increase in fluid flow due to the presence of the field-current interaction; this is done by temperature measurements in the liquid metal. Let us consider a bidirectional casting in which heat is applied to and removed from the system, in such a way that rate of solidification is zero.* When a sensitive thermocouple

Jan 1, 1967

By Nicholas J. Grant, Robert H. Kane, Bill C. Geissen

The platinum-rich section of the Ta-Pt Phase diagram was worked out by metallographic and X-ray techniques, using twenty alloys; solidus temperatures and solid solubilities were determined. Besides s phase, four intermediate stoi-chiometric phases were found: TaPt (high-temperatzrre phase, structure unknown); TaPt2 (ortho-rhomhic, new type); a TaPt3 (orthorhombic, TiCu3 type); ß TaPf3 (monoclinic, new type). TaPt2 and TaPt3 melt congmentlv; two eutectic, two beritec-tic, and one eutectoid reactions occur in the inuestigated range. THE Ta-Pt system was examined as part of a study of the phase diagrams and the intermediate phases of niobium and tantalum with Group VIII transition metals. Since the main scope of this work was the relation among the ordered close-packed phases occurring in the concentration range from AB to AB3 (A = Nb, Ta; B = Pd, Pt, and so forth), only the platinum-rich side of the diagram was worked out thoroughly, while spot checks were made to determine the approximate outline of the tantalum-rich portion. The system has not been thoroughly treated in the literature; Greenfield and Beck1 in their survey of refractory metal intermediate phases found a o phase between -18 and 37 at. pct Pt which coexists at higher platinum concentrations with an unidentified intermediate phase. Browning2 worked on the range between 55 and 100 at. pct Pt; however, this preliminary study did not cover temperatures >1500°C, and included no conclusive crystallo-graphic data. More recently, a study of the platinum-rich section of the Ta-Pt system has been carried out by Ray,3 while Hartley, Parsons, and steedly4 have studied the tantalum-rich section. The crystal structures of TaPt2, a TaPt3, ß TaPt3, and others have been reported in abstracted form by Giessen and Grant.5 EXPERIMENTAL METHODS The methods of alloy preparation and processing and of the metallographic and X-ray procedures follow very closely those described by Ritter, Giessen, and rant' for other refractory metal-noble metal systems, and will not be repeated except where significant differences exist. Starting materials were: tantalum rod of 99.95 pct purity, supplied by National Research Corp., and platinum sponge 99.9 pct, supplied by The International Nickel Co. An oxygen analysis of the tantalum rod showed 30 ppm O; other impurities were C, N, Si, Nb, Mo, none of these exceeding 50 ppm, and 100 ppm W. Homogeneous buttons were readily prepared as follows: ingots of 5 g were weighed and arc-melted under welding grade argon, followed by two remelts after inverting the button. Between 40 and 100 at. pct Pt, weight losses during the first melt rarely exceeded 0.1 pct, in which case the alloy was rejected, and were nil on subsequent remelts. Since the vapor pressure of platinum far exceeds that of tantalum, the small evaporation loss could be assumed to consist of platinum; therefore, a corresponding amount of platinum was added on the second melt. Since it was confirmed on pure tantalum samples that no weight gain through oxygen or impurity pickup occurs (see Ref. 71, it could be assumed that the uncertainty in the composition did not exceed ±0.1 at. pct for the range 40 to 100 at. pct Pt. For the four control melts from 0 to 40 at. pct Pt, an error of ±0.5 at. pct was calculated. Microscopic examination of the whole buttons after melting showed no inhomogeneity other than local coring. This was eliminated by a homogenization heat treatment. A total of twenty-three alloys were prepared. Heat treatments were carried out in a tantalum

Jan 1, 1965

By W. C. Winegard, J. E. Gruzleski

The stages in the development of cells in the Sn-Cd eutectic have been studied by unidirectionally solidifying specimens under known conditions of growth rate, temperature gradient, and impurity concentration. By means of a quenching technique, the shape of the solid-liquid interface during solidification could be observed. Cells are shown to develop from defects or depressions which exist on the solid-liquid interface of even a pure eutectic. Th,e container wall, grain boundaries , and fault lines in the micro structure play an important role in cell development. A two-phase eutectic dendrite found at high impurity concentrations is described. L HE cellular or colony structure formed during eutectic solidification caused much confusion among early workers in their attempts to classify eutectic structure, and a major advance in our understanding of eutectic solidification was made when the colony structure was identified with a cellular interface caused by the presence of impurity elements.1'2 To date, however, no detailed investigation of the stages in cell development in eutectics has appeared, and little work has been done on the cell morphology. The present paper presents the results of such an investigation. EXPERIMENTAL The Sn-Cd eutectic was used in this investigation with lead as the impurity element to promote cell formation. Materials of 99.999 pct purity were zone-refined to an approximate purity of 99.9999 pct. Alloys as close as possible to the eutectic composition, 67.75 wt pct Sn, were prepared using zone-refined tin and cadmium. The alloys were then zone-melted to the exact eutectic composition, as described by Yue and Clark,3 using a total of twenty to twenty-five passes on each eutectic bar. Only those portions of the bars which contained no primary phases were used in subsequent experiments. Master ternary alloys were prepared by melting together the required amounts of lead and the Sn-Cd eutectic in a sealed Pyrex tube under argon, and these alloys were then diluted with pure Sn-Cd eutectic as required. Unidirectional solidification was conducted vertically upward using the two-element resistance furnace shown schematically in Fig. 1. With this apparatus, it was possible to obtain a range of growth rates and temperature gradients so that the cell structure could be studied under different growth conditions. Growth rates in the range of 0.4 to 9.1 cm per hr and temperature gradients from 2.25° to 1475°C per cm were used. To ensure steady-state solidification, power to the furnace was stabilized, and the entire apparatus was enclosed in a large box in which the temperature was controlled to within ± 0.2°C. The apparatus was arranged so that the specimen could be quenched in situ during solidification by pouring a large quantity of water down the central vycor tube. Excellent delineation of the solid-liquid interface at the time of the quench was obtained because of the structural changes accompanying the rapid solidification of the remaining liquid. The quenching rate was always extremely rapid as no evidence of a transition in the lamellar spacing at the interface was ever observed. The alloys to be solidified were contained in degassed, high-purity graphite tubes, 1 cm OD and 0.6 cm ID. The specimens were about 18 cm in length. After the alloy had been cast into the tubes, three 0.8-mm holes were drilled in the tube to the center of the specimen. One hole was placed 1 cm from the bottom of the ingot, and the other holes were placed at 8 and 9 cm, respectively, from the base of the ingot. Thirty-four-gage chromel-alumel thermocouples were sealed in the holes. The lower thermocouple was used to position the solid-liquid interface at the start of each experiment,

Jan 1, 1969

By B. M. Larsen, T. E. Brower, J. W. Bain

A mass of circumstantial evidence is presented to indicate that the main source of alloy losses in open-hearth tapping is oxidation by air, with the steel apparently reacting with an amount of oxygen equivalent to about 30 times its own volume of air. The effect is erratic from heat to heat, depending largely on turbulence and distance of free fall of the stream of liquid metal. THIS paper reports another phase in a general study of oxidation in the open-hearth, various aspects of which have already been discussed in previous papers.1,2,3 It is based on experiments conducted on commercial, basic open-hearth furnaces at various times when opportunity offered, beginning about 1938, in an attempt to determine the mechanism and measure the amount of air oxidation during the flow of the tapping stream through the air into a ladle. This effect is closely connected, not only with alloy losses and control of chemical analysis, but possibly with various questions regarding inclusion content and steel quality and with a true picture of the deoxidation of steel in general. Thus it is believed that discussion of a large part of the results to date may be of assistance to others who are studying problems related to deoxidation or to steel cleanliness and quality. The literature reveals that strangely little attention has been devoted specifically to the effect of pouring steel through open air. Bardenheuer and Henke4 in 1939, in a paper devoted largely to overall losses of manganese in the basic open-hearth, reported that for a number of heats tapped into a tilted ladle held just beneath the runner so that the maximum distance of drop of the stream through the air was held to less than about 30 in., there was in most cases almost no loss of manganese from furnace to ladle. Hultgren,5 in 1945, showed that in high-carbon basic electric steel deoxidized in the furnace and containing no large inclusions as it left the furnace, large silicate inclusions, often rich in manganese oxide, were present in samples dipped from the pool in the ladle; also that the rise in content of large inclusions (above 0.01 mm dim) was greater when the metal stream was made to spray or flow in a turbulent manner. Our interest in this phase of oxidation in the open-hearth was first aroused by a study of alloy efficiencies on ladle additions. The frequency curves of manganese efficiency (net recovery of metal added in ladle) given in fig. 1 are of interest in this connection. Lowest, and also most variable (47 to 95 pct), recovery was in low-carbon heats having no coal additions to the ladle, progressing upward to a maximum average and least variable (82 to 97 pct) recovery in high-carbon heats killed with aluminum and silicon. Both coal additions and higher carbon contents in the tap stream, as well as additions of silicon and aluminum, help to lower the amount of manganese loss. But the most interesting point is the amount of manganese oxidized in many heats tapped at 0.50 to 1.06 pct carbon. It has been shown in a previous paper3 that the amount of oxygen in the tap stream in such heats is very small, usually below 0.01 pct, too small to oxidize any appreciable amount of manganese. Also, the fact that manganese should be oxidized at all in a metal solution containing such more stable oxide-forming elements as aluminum and silicon is an indication of some rather intense oxidizing effect such as could be caused by reaction with the air during ladle filling. Oxygen Balances from Tap Stream to Teeming Stream: Data in the form of alloy efficiencies, such as those shown in fig. 1, are not a proper measure of such a general oxidation effect. Having available

Jan 1, 1951