By Zhengen Zhou, Dachun Liu, Baoqiang Xu, Bin Yang, Yong Deng, Heng Xiong, Jia Yang

The thermogravimetric method was selected for investigating the evaporation of Sb2S3 in the pressure range of 50–300 Pa and in the temperature range of 823–1123 K, the gas phase diffusion was the rate-determining step for Sb2S3. The volatilization rate was related to the temperature and pressure, that the logarithm of volatilization rate yielded a line with the reciprocal of temperature and pressure. The volatilization rate for Sb 2S3 was between 0–0.023 g/C1 cm−2/C1 s. The apparent activation energy was between 65.8 and 60.6 kJ/mol.

Mar 1, 2018

By Du Sichen, S. Seetharaman, Wei Liu

"The viscosities of two-phase mixtures are of great importance in the modelling of the fluid flow in metallurgical processes. For example, in steel making and refining, the intimate mixing of metal droplets in the slag phase requires a consideration of the effective viscosities for the mixture. The present work was aimed at an understanding the phenomena underlying the viscous flow in a two-phase mixture with widely differing viscosities.Emulsions of silicone oils of known viscosities (345mPa.S and 1010mPa.S at 293K) with small amounts of water evenly distributed in the same were prepared by subjecting the mixture to uniform stirring using a magnetic stirrer. The viscosities of these emulsions were measured at constant temperature by rotating cylinder method using Brookfield Digital Rheometer. The uniformity of the preparation of the emulsions was confirmed by the reproducibility of the results. Th7 measured viscosities were generally found to be independent of the torque under the experimental conditions so that the two-phase mixture could be considered as a Newtonian liquid. The variation of viscosities with temperature and the effect of addition of a surface-active substance were also studied in this work.The measured viscosities were found to be· higher than those of both pure water and silicone oil. The experimental viscosities were found to increase with increasing concentration of water. The influence of surface tension on the viscosities was examined by adding surfaceactive agent to the mixtures. The result is discussed and compared with theoretical models developed by Einstein, Taylor and Oldroyd."

Jan 1, 2000

By Mim Li, Huimin Lu, Lisha Yang

"CuInS2 thin films solar cells have drawn much attention for their low-cost, stability and high conversion efficiency. The electrodeposition of Cu-In precursor films, as the first step in making CuinS2 solar cells electrochemically in the air-and water-stable ionic liquid based on choline chloride/urea eutectic mixture has been investigated at constant potential. Compared with aqueous electrolytes, the large electrochemical window as well as the high thermal stability of this ionic liquid allow the direct electrodeposition of Cu-In precursor films. Then the precursor films were sulfuretted in a tube furnace at different sulfurization temperatures to optimize the films properties. The films obtained were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS).IntroductionCuInS2 is one of the most prospective absorber materials for low cost thin film solar cells, with a high conversion efficiency that exceeds 32% in terms of theory and nearly 13% in laboratory level [1-2]. In addition to its long-term stability, CuinS2 has a band gap energy Eg ranging from 1.3 to 1.55 eV and an optimal optical absorption coefficient reaching 105cm-1 [3-4]. CuinS2 thin films have been prepared by several methods such as spray pyrolysis [5-6], r.f.sputtering [7], vacuum evaporation [8-9] and electrodeposition. Comparing with vacuum methods, electrodeposition has lots of advantages such as less energy consumption, preparation big area thin film, stable system and enabling cheaper films.The electrodeposition of most technologically important metals has been shown to be possible from a wide range of ionic liquids. These ionic liquids are currently applied in a wide variety area. It is reported that the cell efficiency of chalcopyrite absorber layer (CIS, CISeS, and CIGS) via an electrodeposition route in laboratory condition has reached 11.3% [10]. Copper and indium alloy film is regarded as important precursor for the production of compound semiconductors with sulfur. The electrodeposition of the alloy film from room temperature ionic liquid (RTIL) has not been widely investigated. Only few alloy films, such as ZnTe, CdTe, GaAs and AlSb have been electrodeposited."

Jan 1, 2011

By William Petruk

A mineralogical and image analysis study was conducted on samples of U tailings from pilot-plant runs on Midwest ore in Northern Saskatchewan. The tailings had been subjected to simulated weathering for the equivalent of 10 years in a tailings facility (lysimeter). The pH varied from 7.0 at the beginning of the test to 5.9 at the end. The results show that during the simulated weathering sane of the gersdorffite, uraninite, galena and pyrite had oxidized, with gersdorffite being the most reactive and pyrite the least. Reaction was evident at the top of the lysilleter , but was most intense at the seepage discharge. sane of the released ions precipitated as Ni, Pb, and U arsenates, sulfarsenates, sulfates and oxides on particles of all minerals. Green crystals of Ni sulfate and white crystals of ca sulfate had precipitated at the surface of the lysilleter. Clay minerals and chlorite had washed from the top of the lysirneter towards the seepage discharge.

Jan 1, 1989

By Jukka S. Sulanto

Outokumpu has applied its well -known copper Fl ash Smelling Process also for smelting su1phide lead . concentrates. The lead in the Flash Smelting Furnace slag is recovered by reducing the oxygen potential of the slag in an electric furnace by injecting reductant into the slag bath. A series of tests have been carried out in a 1000 KVA electric furnace? adjacent to a pilot Flash Smelting Furnace. The furnace has been fed continuously with molten Flash Furnace Slag. The feed rate has varied from 0.5 to 3.1 MTPH (0.55 - 3..4 STPH) depending on the feed rate and the quality of concentrate to the Flash Smelting Furnace. The inlet slag contained 15 to 40% of lead and the cleaned slag 1. 5 to 3. 0%. The lead recovery from sol id raw material was tested in the same continuous process by feeding lead calcine into the furnace. Feed rate was 0.7 to 0.95 MTPH (0.8 - 1.05 STPH) and the calcine contained 33 to 34% of Pb. Several reduction agents and procedures were tested. The process proved to be suitable for continuous recovery of lead from solid oxide raw materials.

Jan 1, 1990

By M. Sakamoto, S. Karaswa, Y. Yoneoka, Y. Ohmizo

"The Annaka Refinery has been processing leach residue by Waelz process for 17 years. Recently, the quantity of the leach residue has increased due to a decline in the quality ~f zinc concentrate. Meanwhile, negative factors (e.g. deterioration of water balance due to improved electrolytic power consumption rate) have increased· in the processing of the leach residue.We have implemented various measures in responses to this situation, while striving to increase ·processing capacity and achieve stable operation. AS we have largely completed our assessment of the efficacy of these measures, we report on our recent process improvements.IntroductionWe have been treating leach residue by the Waelz kiln process since 1981. At that time, treatment of only 50,000 tons of leach residue per year was anticipated. However, subsequent process improvements have revised this figure up to 75,000 to 80,000 tons per year.However, today's increased Fe zinc concentrate grade has resulted in increased amounts of leach residue. In addition, improvements have reduced electrolytic power consumption rate of zinc electrolysis, limiting the amount of water that can be used in ·the zinc refining processes and for deaning leach residue. Consequently, we encounter an increasing number of problems and factors adversely affecting leach residue treatment, including increases in water-soluble Zn (WsZn) and. S (S04) in leach residue.To solve these problems, we have taken several measures to ensure long-term continuous operation and treatment of this increased · amount of leach residue. This paper discusses these measures."

Jan 1, 2000

By Guohua Bai, Lin Zhang, Shan He, Xuling Chen, Min Gan, Xiaohui Fan, Yanbin Tang

"For reducing the dust content in flue gas during copper smelting in the Ausmelt, technologies and mechanism of strengthening the pelletizing of copper concentrate were studied. The results show that adding bentonite, organic binder or composite binder can effectively enhance the strength of green pellet and reduce the rate of shedding powder in drying process, and composite binder works best. When adding 1 % of composite binder, the drop strength of green pellet increased from 1.9 times/P to 4.5 times/P, the rate of damage dropping from 2 m reduced from 50.12% to 13.08% and the rate of shedding powder reduced from 60.28% to 25.13% at drying temperature of 400111. In addition, the mechanism of binder absorbed in the surface of mineral was investigated by infrared spectroscopy. The results showed that composite binder absorbed in the surface of copper concentrate was in the form of chemisorptions, which made hydrophilic enhanced, while bentonite absorbed in the surface of copper concentrate was physisorption.IntroductionWith the technologies of copper smelting developing, the equipment of copper smelting steps into a large-scale and efficient level in recent years. As Ausmelt smelting is characterized by being efficient, environmentally-friendly and energy-saving, it is generally recognized by the enterprises of copper smelting [l]. The process of Ausmelt smelting starts with materials mixing, and then pelletizing. From this point onwards, pelletized balls are charged to the top of the furnace, undergoing drying and smelting reaction[2]. Since copper concentrate is fine-grained, directly adding into smelting furnace can make it blown out of the furnace together with the airflow upwards, rendering flue gas high in flue dust, which can cause the loss of concentrate greatly, and make smelting environment poor as well. The concentrate transported into the furnace and smelted after disc balling is conducive to improve the capacity of melting furnace during copper concentrate smelting, reduce the powder shedding rate and improve enterprise benefits."

Jan 1, 2013

By Charles H. Bucknam

A gold sampling optimization study was carried out in support of open pit gold mining operations for the Newmont Gold Company Bootstrap-Capstone deposits in Northeastern Nevada. Six bulk samples were tested using fire refining techniques at field particle size, to determine coarse particle heterogeneity of the ores, and by gravity .concentration methods at 10 mesh particle size, to observe any particulate gold liberation. An overall sampling model is presented for the deposit based on the pooled test information, to reconcile the results of coarse particle heterogeneity testing and the fine particle 'liberation testing. The sampling model is used to recommend procedures to control the variability of gold grade estimation due to the fundamental error (nugget effect) during sampling, sample preparation and assaying of the ores and other fundamental variances. The technique of simplified quantitative risk analysis (SQRA) is used to provide an economic justification for implementation of. recommended improvements to field sampling practices.

Jan 1, 1999

By Mariana M. Arantes, F. R. Valenzuela-Díaz, Olgun Guven, Vijay K. Rangari, Julyana Santana, Esperidiana Moura

Nowadays, the development of polymeric materials reinforced with residues of vegetal fibers is becoming popular for application in different segments, from the automotive to the civil construction and furniture industry. Vegetal fiber residues may be used as reinforcement of the recycled polymer materials, for instance, to produce foams to packaging or to thermal and acoustic isolation for green building application. This work is focused on the development and characterization of recycled-HDPE/EVA foam reinforced with fiber residues from babassu coconut epicarp. Firstly, composites based on recycled-HDPE/EVA blend reinforced with babassu coconut fiber were obtained by melting extrusion process. The composites were then extruded in a special single screw for foaming. The foam samples were submitted to mechanical tests, density measurement, DSC, TG, and FE-SEM analysis.

Mar 1, 2018

By Zhen Zhang, Jiang Diao, Xuan Liu, Tao Zhang, Bing Xie, Hong-Yi Li

Extracting vanadium from vanadium containing hot metal by LD process has been proven an effective solution for the utilization of vanadium-titanium magnetite ore, but the systematic analyses of vanadium extraction rate and mechanism by basic slag are seldom reported. In this study, mathematical model of vanadium transfer from metal to slag was formulated and the rates of vanadium extraction of hot metal with basic slag were investigated. The results indicated that the apparent vanadium extraction rate constant, kp, were in the range of 1.33~9.07×10-4g/(cm3·s). And the rate constant was increased with the increase of final slag basicity, reaction temperature and stirring gas flow. The apparent of mass transfer parameter decreases significantly from 0.13 cm3/ s to 0 cm3/ s in 20min, and the data changed as negative due to the decrease of slag oxidation and recovery of vanadium from slag to metal.

Jan 1, 2015

By Selim Coskun

In this study, tungsten matrix composites reinforced with 2 wt% TiC particles were mechanically alloyed (MA?d) for 3h, 6h, 12h and 24h. 1 wt% Ni is used as sintering aid which is added before and after mechanical alloying. Microstructural and phase characterizations of composite powders and sintered samples were carried out via SEM and XRD analyses. Furthermore, density and hardness measurements of as-consolidated and sintered samples were carried out. Additionally, DSC experiments were conducted to investigate the sintering behavior of the MA?d powders.

Jan 1, 2009

By V. Jiricny

The novel spouted-bed electrode (SBE) is a cathode system where copper is deposited at a high current density in a moving bed of copper particles. Preliminary results on the deposition of copper from acidic sulfate electrolytes using this novel cathode system were described during Copper '95 conference. Despite a high current density, the electrical energy consumption was equal to or lower than that in the conventional electrowinning. The present paper describes more investigations on SBE. The SBE consists of copper particles with approximately 1 mm diameter onto which copper is deposited from acidic sulfate electrolyte whose composition is similar to conventional electrowinning. Three types of anodes were used in conjunction with the spouted-bed cathode, namely, DSA anode for oxygen evolution, and two novel anodes. One anode is less expensive than DSA; however it showed much promise in energy consumption. At a superficial current density of 2200 A/m2, the energy consumption was around 1.0 kWh/kg copper. The research activities described in this paper were supported by BHP Copper.

Jan 1, 1999

By Donghai Li, Cheng Pan, Xuewei Lv, Mei Liu, Enguang Guo

"Phosphorite is the main raw material for the production of phosphorus in chemical industry. More attentions have been drawn to the phosphorite concentrate beneficiated from low-grade phosphorite due to the decrease of high-grade phosphorite. For another, the agglomeration process is necessary for the phosphorite concentrate after beneficiation process. The mineralogy and sintering process of the phosphorite from Leshan, China were studied in this work. The result shows that the main phases in the phosphorite are fluorapatite (Ca3(P04)3F), hydroxylapatite (Cas(P04)3(0H)), quartz (Si02) and dolomite (CaMg(C03)2). The yield of the sinter increases with increasing the carbon dosage to 7%, and then decreases when it continuously increases. Similar regularities were found for the strength and the content of P20s of the sinter. The best strength of the sinter as well as its P205 content were discovered when the carbon dosage is 7%. Fluorapatite ((Ca5(P04)3)F) is the main phase in the sinter while fuggerite (Ca2MgSiz01) is the main binder phase.IntroductionPhosphorus is an important foundation industrial raw material of national defense industry, food industry and chemical industry, where it is used to produce red phosphorus, phosphonium hydroxide, phosphorus pentasulfide and phosphoric anhydride[l-2]."

Jan 1, 2013

By Yang Jian-guang, Deng Zi-xiang, Zhang Xu-liang, Li Jun-yuan

"Hyperaccumulator biomass harvested after heavy-metal phytoremediation must be considered as hazardous waste that should be contained or treated appropriately before disposal or reuse. As a potential method to detoxify the biomass and to convert this material to a suitable bio-energy resource, the hydrothermal upgrading process was applied to remove heavy metals and upgrading crude bio-oil from Pteris vittata stems and leaves harvest. Parameters such as material granularity, temperature, Liquid/Solid (L/S, ml/g), pressure, duration and catalysts were examined for their effect on the removal efficiency of heavy metals and upgrading efficiency of crude bio-oil. Maximum heavy metal removal efficiency of>99% and crude bio-oil upgrading efficiency of 83% were attained with an 200 mesh (75 µm) granularity, LIS 40:1and23 MPa at 380°C in the presence ofO.l mol L-1 K2C03 for 30 min. GC-MS analysis results show that the resulting bio-oil mainly consists of benzene 11 %, ketone 42%, alcohols 14%, alkene 15% and ester 11 %, etc., and the relative molecular weight distribution lies in 94-282, carbon number distribution lies in 6-18, calorific value is 32MJkg-1.IntroductionPhytoremediation of soil or water with hyperaccumulator has been extensively explored in recent years [1-4]. Living plants can clean up soils or waterways. This approach exploits the ability of various plant species to thrive in high metal environments where large amounts of toxic elements are accumulated, such as heavy metals, and is particularly appropriate when slow remediation of relatively low metal concentrations is acceptable. Advantages compared with existing remediation methods include the minimal site destruction and destabilization, low environmental impact, and favourable aesthetics; advantages compared with biosorption include continuous in situ regeneration of the biomass, and the ability of living plant cells to supplement passive sorption of metals with metabolic mechanisms of metal uptake and detoxification [5-8]."

Jan 1, 2014

By Yuanyuan Zhang, Patrick J. Masset

"The reduction of FexO in slag is one of the fundamental reactions in iron and steelmaking technology, including the blast furnace process (BF). Experiments on the reduction reaction of iron oxide using CaO-SiO2-Al2O3-FexO-C mixtures were carried out using thermogravimetric analysis (TGA) under reducing conditions at temperatures up to 1100°C. The composition of the primary slag was chosen so that the FexO concentration varied between 0 and 75 wt % and the CaO/SiO2 ratio being kept constant to 0.90. From the TGA curves recorded isothermally at different temperatures the kinetic parameters of the iron oxide reduction were determined.IntroductionIn blast furnace the iron ores and coke are charged in layers from the top. The reduction of iron oxide by coke is one of the fundamental reactions in the blast furnace process. Although a great amount of work has been done on the topic of reduction of composites [1, 2, 3], gasification of carbon [4, 5] and reduction of iron oxides by CO [4, 5, 6], the mechanism of reduction in iron oxide - carbon powder mixtures is not fully understood. Fruehan [1] and Rao [2] studied the reaction rate of the reduction of iron oxide by different types of carbon and concluded that the reaction mechanism is controlled by the oxidation of carbon at temperatures up to 1200°C. Rao [2] studied the reaction of hematite with graphite as carbon source up to 1080°C. An activation energy close to 300 kJ/mol was calculated within the temperature range of 950°C to 1087°C. In his study, Fruehan [1] determined the rate of reduction of Fe2O3 and FeO by coal, coke and coconut charcoal as carbon sources within the 900°C to 1200°C temperature range. He found that the reduction of Fe2O3 by carbon occurs in two stages and that the reduction of Fe2O3 to FeO is faster than that of FeO to Fe. This is due to the fact that the CO2/CO equilibrium ratio is higher, and hence, the rate of oxidation of carbon is faster. Fortini and Fruehan [3] have studied the reduction reaction of wustite by graphite and wood charcoal. They found that the wustite reduction can have a significant effect on the overall rate of reduction in composites at high temperatures or in the presence of a large excess of carbon. The calculated activation energy of the reduction reaction by wood charcoal was close to 368 kJ/mol, while the activation energy of the reduction reaction by graphite was 444 kJ/mol."

Jan 1, 2011

By Jintao Gao, Zhancheng Guo, Chong Li

A new approach to enrich MFe and RO phase from the converter slag by super gravity was investigated. The samples obtained by the gravity coefficient G=600 and cooling rate V=5K/min from 1623K to 1373K appeared significant stratification and the MFe gathered at the bottom of sample. With the help of metallographic microscopy and X-ray diffraction, it is found that large quantity of white RO phase gathered at the lower part of the sample as the concentrate, with volume fraction appearing gradient distribution along the direction of super gravity, while the upper part was mainly composed of dicalcium silicate as the tailing. The mass fractions of the FeO, MgO and MnO in the concentrate are up to 40.46%, 6.9% and 3.91%, while that in the tailing are just 11.65%, 2.15% and 1.55%. The recovery ratios of FeO, MgO and MnO in the concentrate are 60.35%, 58.45% and 72.24%, respectively.

Jan 1, 2016

By Dengfu Chen, Yi Yang, Chunmei Chen, Mujun Long, Shikai Gong, Junhao Sheng, Tao Liu

The relationship between thermo-physical properties of petroleum coke and temperature is of importance for determining of the operating parameters during the calcining graphitization process. In this paper, the variations of thermo-physical properties of petroleum coke versus temperature were investigated, such as the DSC-Tg curve, the specific heat capacity, the thermal diffusion coefficient, the thermal conductivity, and so on. The thermal analysis curve of petroleum coke showed synchronous thermal hysteresis at higher heating rates, indicating that a larger heating rate will cause delay of thermal effects. The thermal diffusivity of petroleum coke decreased during the calcining process. With increasing temperature, coefficient of heat conductivity and specific volume heat of the petroleum coke increased with a decreasing variation rate. The research provides a database for the calcining graphitization process of petroleum coke.

Jan 1, 2015

By P. Henry

A novel electrochemical cell has been developed for the recovery of MnO2 from residue of pyrolusite ore leading loaded with Fe, Al Ni, Co and Si impurities, This new process can be considered as an alternative to the traditional methods : S02, H2O2 or bioleaching. It has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. Electrochemical characterization and kinetic studies have shown that MnO2 is effectively leached by electrogenerated ferrous ions at high current density from a pulp containing less than 5 g8 Fe. The chemical reactions are : Cathode (inox) : 2F23+ + 2e ? 2 Fe2+ Bulk: MnO2 + 2 fe2+ 4H+ ? Mn2+ + 2 Fe3+ + 2 H2O Anode (Pb-Ag) : H2O ? ½ O2 + 2H+ + 2e Global: MnO2 +2H+ Fe2+ = Mn2+ + H2O + 1/2 O2 The catholyte (MnO2 pulp) circulates upward in the expanded mesh cathode separated from the sulfuric acid solution anolyte by a separator which shows high mechanical resistance, low porosity, low potential drop, and reasonable cost. Laboratory and mini-pilot tests have led to the construction of an OT crating pilot plant (100 kg/hr) able to leach more than 95% of Mn, Ni, Co at 1000-1200 A/m2, 50°C with high faradic yield (> 95 %) and low power consumption (3.2 kWh/kg kWh/kg &4D). New applications like the treatment of spent Zn-Mn batteries, polluted soils, spent catalysts and oxide ore (cobalt, nickel) with electrogenerated redox species are now investigated at a laboratory and mini-pilot scale.

Jan 1, 2000

By Shunhong Huang

Thirty-five soils were sampled from three sites at different distances from chromium slag heap of a Iron-alloy factory, namely, nine from site A located under the chromium slag and eighteen from Site B in the vicinity of the factory and eight from site C far from the factory. The contents of total Cr in these soils from site A, B and C were 1666.0±1310.9 mg? kg - 1,1136.2±1844.6 mg? kg - 1 ,300.4 ±165.1 mg? kg ? 1, respectively. The contents of water soluble Cr were 59.3±77.57 mg? kg ? 1,0.6 ±0.3 mg? kg - 1 ,0.5±0.3 mg? kg - 1 , respectively. In order to evaluate soil health, the activities of four soil enzymes (catalase, polyphenol oxidase, dehydrogenase, alkaline phosphatases) were analyzed. The results have shown that dehydrogenase activity was greatly depressed by conditions in the heavy chromium-contaminated sites. Negative correlation was observed between dehydrogenase activity and the distance from the chromium slag heap, however, the activities of catalase, polyphenol oxidase, alkaline phosphatases in soils from the three sampling sites mentioned above did not differ significantly. The result imply that of dehydrogenase activity could be used as an indicator for the chromium pollution level in the area of Iron-Alloy factory and for the stability level of the soil ecosystem.

Jan 1, 2008

By Ju Shao-hua

Although nowadays gold extraction methods are very abundant, none of them is satisfying, especially, in the field of heap leaching of low grade gold ore. The traditional heap leaching method of cyanide method plays an inglorious role of badly environmental pollution. In this paper, a bran-new and innoxious method of gold extraction system, metal-ammonium-chloride-ammonia (MACA), was proposed, and also analyzed both thermodynamically and practically. Thermodynamically, according to the principles of simultaneous chemical equilibrium and electronic charge neutrality, the thermodynamics of Au-NH4Cl-NH3-H2O system was studied by using the exponential computation method and through MATLAB programming, and the solid figure of its potential - c(NH4Cl) - c(NH4OH) was drawn. The results showed when the concentrate of ammonia is higher than 0.6 mol?L-1, fAu+/Au is only about -0.2 v. Practically, the leaching results of a cuprous gold ore showed that the extraction of gold can reach to 80% in this system. The preliminary results of reduction of the rich solution with copper and zinc powders showed that with deoxygenizing, the reduction effects were relatively good. These new findings and results have established a theoretical and practical base for developing a new process for heap leaching of low grade gold ores in this system. And the new process owns a series of merits such as, non-cyanogens, nontoxic, broader applicability.

Jan 1, 2006