By Albert F. Schneider

The peculiar conditions under which lead and silver ores are now smelted in Salt Lake Valley, Utah, render it advantageous to make slags that are siliceous and carry a high percentage of lime. The ores treated come from Utah, Idaho, Montana, and Nevada; nine-tenths coming from Utah. These ores are siliceous, and contain but little fluxing material; the iron present scarcely sufficing for the sulphur and arsenic. Formerly ores high in iron were furnished from Cottonwood Canons, but this supply is meagre. The ores from Idaho, Montana, and Nevada are high grade galenas, more or less impure. They generally require a large amount of iron for the sulphur, arsenic, and antimony. In the winter and spring of 1880—'81, we were treating at the Germania Works principally Bingham Canon lead ores and silver ores from Tintic. The former contained 15 to 30 per cent. silica, and only 4 to 5 per cent. iron (generally as iron pyrites); they ranged high in lead and low in silver, and carried more or less alumina; the lead was present chiefly as carbonate. The silver ores from Tintic contained sulphides, and ran as high as 80 per cent. silica. We had been running on a slag approximating 40 per cent. FeO, 20 per cent. CaO, 10 per cent. other bases, and 30 per cent. SiO2, which had heretofore been very satisfactory; but with the class of ores then coming in it was of the utmost advantage to use less iron and more lime, especially as the iron ore (50-55 per cent. iron and 5-7 per cent. silica) cost four times as much as the limestone (50-55 per cent. lime, 3-5 per cent. silica). The large amount of alumina in the slag influenced them for the worse; the addition of lime to the charge helped them, and after many experiments regarding the proportion of FeO, CaO, and SiO2, a slag approximating 35 per cent. FeO, 25 per cent. CaO, 5 per cent. other bases, and 35 per cent. SiO2 seemed to answer

Jan 1, 1883

By J. Campbell

Long freezing range casting alloys are particularly susceptible to a type of porosity which is observed to form in layers parallel to the supposed position of the isotherms in the solidifying casting. Under favorable conditions (which appear to be typified by low-temperature gradients in the casting giving rise to a wide and more or less uniform pasty zone, and which arise from several factors, particularly: a) wide freezing range alloy, b) high thermal conductivity of metal, c) low thermal conductivity of mold, and d) high mold temperature3) layer porosity has been observed in many different casting alloys: copper,' aluminum, magnesium,' steels, and high-temperature alloys.3 Baker4,5 and later cibula6 argue that layer porosity occurs because of thermal contraction, in a manner analogous to hot tearing. In outline, the theory consists of the establishment of a coherent dendrite network by the impinging of dendrite tips. Subsequent shrinkage imposes tensile stresses on the network which tears perpendicularly to the stress, i.e., parallel to the isotherms. If these tears are not filled by the inflow of residual liquid then layers of porosity result. Baker7 attempted to test whether the porosity was the result of thermal contraction by casting test pieces in a mold designed to accentuate hot tearing. However, no significant increase in porosity was observed. This negative result of Baker's critical experiment appears to be substantiated by numerous observations, particularly the experiments by Lagowski and Meier8 on Mg-Zn alloys covering the range of zinc contents up to 30 pct Zn. These clearly reveal that the maxima for the incidence of hot tearing and layer porosity are well-separated, occurring at 1 and 6 pct Zn, respectively. Furthermore, the thermal contraction maximum occurred at 1 pct Zn, indicating that hot tearing is associated with contraction in the solid state, and not with porosity. These observations are further substantiated by the elementary consideration that the thermal contraction of the casting is likely to produce (if anything, since the temperature difference across casting of high thermal conductivity, such as aluminum and copper, is likely to be negligible) a compressive stress on the

Jan 1, 1969

By Norman Pilling

THE solubilities of a series of experimental alloys covering the range 0 to 100 per cent. Ni, 0 to 30 per cent. Cr have been studied under conditions of complete submersion in several fully aerated acid solutions, and in solutions containing sulfurous acid. In nonoxidizing, hydrogen-discharging acids, if the nickel content is below a certain critical amount, chromium increases the rate of solution and nickel decreases this rate; this critical content of nickel is about 13 per cent. Alloys containing more than this corrode at a constant minimum rate independent of iron, nickel or chromium contents. Austenitic chrome-nickel steels may thus have a resistance to these acids equal to that of nickel-chromium alloys. In nitric acid and in unaerated sulfurous acid rather sharp limits of attack occur which are principally dependent on chromium content. In the former the limit of attack is not related to a particular chromium content but varies continuously with acid concentration. The action of sulfurous acid on these alloys is highly dependent on the presence of small amounts of other substances in solution, and many sulfurous acid mixtures rapidly attack alloys to which the pure acid is wholly inert. The observed effects are. not compatible with Tammann's theory relating corrosion resistance to lattice structure but are believed to be concordant with current views of the electrochemical nature of corrosion.

Jan 1, 1929

By J. W. Hickman

Most of the electron diffraction studies of oxide films which form on metals and alloys have been carried out by oxidizing the specimens in an auxiliary furnace, cooling down to room temperature and then inserting the sample in the camera and taking a diffraction photograph. Prior to the investigations at the Westinghouse Research Laboratories, no systematic study of the oxidation of any metal or alloy had been made over a wide temperature range with photographs taken at elevated temperatures except the investigation of iron by Jackson and Quarrell.' In order to interpret the electron diffraction patterns of the oxides which may form on alloys, it seemed advisable to make a comprehensive study of the oxidation of the purest metals available in the bulk form. Thus far studies have been completed on iron,2 cobalt,~ nickel,= chromium,= copper,z tungsten,s molybdenum,3 beryllium,' uranium,' thorium,' titanium6 and zirconium6 while investigations are in progress on tantalum and columbium. The next step in the study is concerned with the investigation of the oxides which form on binary alloys. Some of the alloys consist of a single phase while others contain more than one phase. The identification of the oxides on the surface of a binary alloy may be more difficult than on the metals since oxides containing both metals as well as those of each metal separately may form. Furthermore, it is possible that solid solutions of the various oxides may occur. In these cases the electron diffraction method may not be able to identify the oxidation products unequivocally. Examples of solid solutions which may present difficulties are MOO* and WOp, Fe304 and FeO.CrnOa since the diffraction patterns are so similar. Since electron diffraction can determine only the structure of the oxide, the chemical composition must be inferred from the diffraction data based upon X ray diffraction investigations of specimens of known composition. It is possible in some cases to decide whether a given solid phase reaction can occur on the surface of an alloy by a study of available thermodynamic data. Table I lists the equations for the formation of most of the oxides from the elements together with values of loglo Kg for the several temperatures. AF"B = -RT In KR AF°R and KR are the free energy and equilibrium constant of the reaction. Calculations may be made using the the given in I 1 to determine whether a given solid phase reaction is possible thermodynamically. For example, a solid phase reaction should occur between aluminum and chromium oxide to form

Jan 1, 1949

By Theodore Simons

(Butte Meeting, August, 1913.) DURING the last half century a great amount of ingenuity and energy has been devoted to the invention of appliances for the recovery of valuable minerals from very fine sands and slimes. The reason for this is that in almost every dressing plant the greatest losses of values, considered relatively as well as absolutely, occur in the treatment of slimes. The natural aim of mill operators to minimize these losses has in recent years received another impetus, from the fact that the gradually diminishing occurrence of high-grade ores makes a more intense recovery of values from existing resources absolutely necessary for profitable operation. The results of such attempts are found in the appearance of a great number of machines and appliances which make it profitable to-clay to rework old dumps, containing the tailings of older processes. A constantly growing difficulty of obtaining skilled labor and the increase in wages made it prohibitory to employ those types of machines which required much attention, and in the middle of the nineteenth century the various concentrating tables of the percussion type, which automatically discharge their products, began to take the place of the intermittent tables, on which, when the bed had reached a certain thickness, operation had to be stopped in order to allow the skimming by hand of the separate layers formed on the table. In the course of years, two general types of machines evolved for the treatment of fine sands and slimes : The so-called concentrators and vanners, on the one hand, and the buddies and round tables on the other.1 For the profitable treatment of the very finest slimes, round tables have as a last resort proved more satisfactory and economical than other machines.

Jan 7, 1913

By John V. Beall

Hard as the Revett quartzite are conditions governing the deep mines of the Coeur d'Al6ne. In fourscore years of mining, heat and pressure have been the rewards of preseverance. Such obstacles are the natural concommitant to search for ore at depth. But high cost and shortage of miners is a creeping frustration of the decade. These grim observations were made on a trip to the mines of the Coeur d'Al6ne in the first week of May. But the bouncy optimism of competent mining engineers and geologists overrides by far the tough conditions. This is the story of what they are doing. I think they are setting the stage for the wonder mines of tomorrow. I didn't meet all the people or see all the mines, so there are unfortunate gaps in the story. Then too, sometimes the muck and water blotched my notes, or I couldn't write fast enough or I was too tired. No matter. There is much to tell and, because it is basically a human story, I am flouting the rules of technical journalism and couching it in the neglected "I" person. First then, a little history . . . .

Jan 7, 1966

By C. S. Barrett

THE crystal imperfections known as faults in stacking (stacking disorder) are of importance to both fundamental and applied science and are receiving increasing attention. On the theoretical side there have been recent advances in the analysis of diffraction patterns in terms of stacking faults, and on the experimental side it has been found that certain metals develop a faulted structure on cooling through a phase transformation. Beyond this, little is known of what may be called the physical and mechanical metallurgy of faulting, although there has been no lack of discussion and conjecture as to the presence of faults in metals and the effect of faults on mechanical properties and microstructures. In the close-packed metals the nature of faults can be described very simply. Face-centered cubic (FCC) crystals consist of close-packed layers of atoms, (111) planes, stacked above each other in a definite manner. If one layer is designated as the A layer, the next must be a B or a C layer; that is, every atom of the second layer lies not above the atoms of the A layer, but nestles in the hollows between these, using the hollows designated as the B positions, or the equivalent hollows designated as C. If the sequence of layers is ABCABC...., so that layers three spacings apart are directly over each other, the crystal is FCC; if CBACBA ... it is an FCC crystal that is a twin of the former; if ABAB........or BCBC..it is hexagonal close-packed (HCP). A fault is a break in the sequence, such as ABCABABC .. . which has the effect of inserting an HCP lamella into an FCC crystal. Regularly spaced faults spaced two layers apart would convert an FCC crystal entirely to HCP, or an HCP to FCC. A fault in an FCC crystal is also equivalent to creating an FCC twin of minimum thickness; in fact, the entire crystal would be converted to its twin if faults were introduced regularly. (In HCP crystals, however, twinning does not occur on the basal plane and a fault on this plane is not identical with a thin twin). Faults are one of the possible causes for annealing twins,' for the strain markings that are brought out by etching deformed metal,'," for the altered X ray reflecting power of metal at slip bands that is revealed in X ray reflection micrographs,' for the extinction of Kikuchi lines in electron diffraction patterns, and for the hardening of latent slip planes.' Since other explanations of these effects are also available," there has been no direct proof of faults from deformation; yet it has appeared likely that they would occur. Faults resulting from phase transformations in metals, however, have been clearly revealed by diffraction in cobalt" and lithium. It is to be expected that the faulting tendency is greatest

Jan 1, 1951

By George H. Gilman

THE campaign now being waged to improve the quality of the rock-drill bit is the natural outcome f the scientific development of the drilling machine during the past twenty years. In this development there has been a great increase of power output per unit of weight of machine. But the development of the rock drilling engine has been seriously hampered by the need of a drill bit that would withstand, without undue wear or breakage, the heavy rapid blows of the improved pneumatic hammer. This problem was difficult to solve because an increase in the weight or section of the drill-steel bar resulted in decreased cutting speed and higher operating costs of both the bit and its actuating engine. The solution, therefore, is to make the bit of steel that, for a given weight or section, will be more shock and wear resisting. In the attempt to meet these requirements, many of the drill-steel manufacturers alloyed the steel with vanadium, chromium, nickel, etc., on the assumption that such elements would improve the rock-drill bit but due to the sensitiveness of such steel to forging and heat treatment, higher cost, and lack f continuity of effort on the part of the steel manufacturer to perfect this product, but little progress has been made in the adoption of these steels and the so-called straight carbon steel is today recognized as the standard material for all rock-drill bits. The first step in improving drill-bit efficiency is the determination f the cause of breakage and wear. For this reason, in 1917, certain rock-drill manufacturers, in conjunction with some of the larger mining interests, conducted exhaustive tests in both the field and laboratory. It was then found that, in the main, the cause of drill-steel troubles is not attributable to the duty imposed upon it by the normal operation of the drilling engine, but to improper forging and heat treating of the bit and to the subjecting of the bit to improper use. The fact that it is possible to minimize the troubles attributable to improper heat treatment of the drill steel has been demonstrated and it is recommended that such knowledge be made available by teaching those interested in the production, use, and up-keep of drill bits the principles on which success in this direction may be achieved.

Jan 6, 1921

By Joel Watkins

THE terms kaolin, china clay, ball clay, and paper clay are more or less loosely and interchangeably applied to a large class of white-burning clays. These clays are made up chiefly of hydrous amorphous (colloidal) aluminum silicates with variable amounts of free silica and other impurities in small quantities. Occasionally also the term kaolinite is wrongly applied to a white-burning clay, for kaolinite, is a mineral of definite chemical composition and definite crystalline form which occurs but sparingly in nature. It is not the purpose of this paper, however, to define or classify clays, or to enter into a discussion of the chemistry of clays. It is rather a general description of the occurrence and methods of mining of a kindred group of clays, and a discussion of their future economic aspect. In the Southern Appalachian States, the mining of white-burning clays has in recent years become an important industry. Although these clays are of several distinct types, which occur in as many localities under different geologic conditions, they are for the most part. primarily of the same origin. They are essentially the same in elementary constituents, and are largely consumed in the same industrial arts. From the standpoint of a mining engineer, therefore, and for convenience in comparison and correlation, it should be interesting to discuss them under one heading.

Jan 2, 1915

By E. B. Hughes, F. G. Norris

Oxidation is characteristic of all processes for making steel from pig iron. This thought has been aptly expressed by H. W. Graham13 in the recent Howe Memorial Lecture, "The process of steel-making consists of using iron oxide to reduce the carbon content of the pig iron to the desired level." Direct oxidation refers to the reaction that results from introducing oxygen either alone or mixed with other gases directly into the steel bath. In working a heat, oxygen in some form is added to the steel to remove the undesirable constituents as oxides. There are two general methods of supplying this oxygen to the open hearth bath. The method in which the oxygen is added as a compound such as Con or iron ore is designated an indirect method because the steel bath must first decompose the compound to attain oxygen in a usable form. The other method in which oxygen is added to the bath in the elemental or gaseous form, more or less diluted by other gases such as nitrogen, is a direct method because no decomposition is necessary before the oxygen reacts with iron to form FeO which is dissolved in the bath in a usable form. Bubble formation (at least of a macroscopic size) presents no problem in case of direct oxidation because the reacting agent (oxygen) is in the form of bubbles when entering the metal. Regardless of whether oxygen is intro- duced into the bath directly or indirectly, several reactions proceed concurrently. In the presence of the bath of molten iron, FeO is formed either by oxidation of iron by oxygen or reduction of oxides by iron. This FeO dissolved in the molten iron is the source of oxygen for the oxidation of manganese, carbon, silicon, and phosphorus if these are present. The oxidation of carbon from steel is the controlling steelmaking reaction. The introduction of oxygen into the bath, its reaction in the elimination of impurities, and its control by the use of de-oxidizing additions have been subjects of importance since steel was first made by the bessemer process. Direct oxidation is, in a sense, an application of the bessemer principle to the open hearth process. Graham13 states: "The use of oxygen or air jets introduced into the metal bath is essentially an effort to approach in the open hearth the turbulence, rapid interface reaction, and high production rate per hour that exists in the bessemer process." The general subject, "Oxygen in Steel-making," was given new life by the studies of Herty and associates starting about1925. The current interest in elemental oxygen is intimately related to the large scale production of oxygen developed during the war period. Some of the first applications were made during the early summer of 1946 at the Steel Co. of Canada using oxygen with the fuel. Such a use is of considerable interest and importance in contributing to faster heats but is not the subject of the present discussion which deals entirely with the introduction of elemental oxygen directly into the open hearth bath.

Jan 1, 1949

By E. B. Hughes, F. G. Norris

Oxidation is characteristic of all processes for making steel from pig iron. This thought has been aptly expressed by H. W. Graham13 in the recent Howe Memorial Lecture, "The process of steel-making consists of using iron oxide to reduce the carbon content of the pig iron to the desired level." Direct oxidation refers to the reaction that results from introducing oxygen either alone or mixed with other gases directly into the steel bath. In working a heat, oxygen in some form is added to the steel to remove the undesirable constituents as oxides. There are two general methods of supplying this oxygen to the open hearth bath. The method in which the oxygen is added as a compound such as Con or iron ore is designated an indirect method because the steel bath must first decompose the compound to attain oxygen in a usable form. The other method in which oxygen is added to the bath in the elemental or gaseous form, more or less diluted by other gases such as nitrogen, is a direct method because no decomposition is necessary before the oxygen reacts with iron to form FeO which is dissolved in the bath in a usable form. Bubble formation (at least of a macroscopic size) presents no problem in case of direct oxidation because the reacting agent (oxygen) is in the form of bubbles when entering the metal. Regardless of whether oxygen is intro- duced into the bath directly or indirectly, several reactions proceed concurrently. In the presence of the bath of molten iron, FeO is formed either by oxidation of iron by oxygen or reduction of oxides by iron. This FeO dissolved in the molten iron is the source of oxygen for the oxidation of manganese, carbon, silicon, and phosphorus if these are present. The oxidation of carbon from steel is the controlling steelmaking reaction. The introduction of oxygen into the bath, its reaction in the elimination of impurities, and its control by the use of de-oxidizing additions have been subjects of importance since steel was first made by the bessemer process. Direct oxidation is, in a sense, an application of the bessemer principle to the open hearth process. Graham13 states: "The use of oxygen or air jets introduced into the metal bath is essentially an effort to approach in the open hearth the turbulence, rapid interface reaction, and high production rate per hour that exists in the bessemer process." The general subject, "Oxygen in Steel-making," was given new life by the studies of Herty and associates starting about1925. The current interest in elemental oxygen is intimately related to the large scale production of oxygen developed during the war period. Some of the first applications were made during the early summer of 1946 at the Steel Co. of Canada using oxygen with the fuel. Such a use is of considerable interest and importance in contributing to faster heats but is not the subject of the present discussion which deals entirely with the introduction of elemental oxygen directly into the open hearth bath.

Jan 1, 1949

By Gustaf Ising

For relative gravity measurements, the author in 1918 described an instrument1 of which the essential part consists of a highly astatized, standing pendulum turning about a horizontal elastic axis. This type of instrument has been used recently in practical field work, therefore a description of its principle and technical development is given herein. Part I, describing the principle, is a direct translation of the original Swedish paper.1 Part II gives an account of the practical elaboration of the instrument, together with some description of measure-ments performed.

Jan 1, 1937

By Wilbur I. Duvall, Thomas C. Atchison

Over the past ten years a series of investigations have been conducted to determine some of the physical processes involved in breaking rock with confined concentrated charges. Detailed discussions of many of these investigations have been published elsewhere.1-6 Laboratory experiments made by other investigators using Hopkinson pressure-bar techniques have shown that solid materials are fractured in tension by the reflection of an incident compressive stress pulse at a free surface.7-12 In these tests a small charge of explosive is placed in contact with one end of a bar. Detonation produces some plastic flow and crushing of the bar near the charge and generates a compressive stress pulse that travels along the length of the bar. At the free end of the bar the compressive stress pulse is reflected back into the bar as a tensile stress pulse. If the tensile strength of the bar is exceeded during this reflection process, a tensile fracture normal to the length of the bar is produced, and the broken end of the bar moves forward with a constant velocity equal to the average particle velocity trapped in the broken fragment. The new surface formed by the fracture becomes the new free end of the bar that reflects the remaining portion of the incident compressive stress pulse. This process is repeated any number of times until all of the incident stress pulse is reflected.

Jan 6, 1959

By S. C. Herold

Considerable interest has been shown, during recent years, in the possibilities of developing oil fields in the South American Republics, now that the exhaustion of our present fields can be seen in the not very distant future. The demand for fuel 011 and its products has been increasing far more rapidly than our increment of production during the last few years. Increase of consumption has been largely curtailed by the lack of sufficient supply. The main factors that have contributed to our previous neglect of the southern fields have been as follows: (a) Lack of sufficient demand for the product. (b) Competition with producing fields, having large production, low cost, and better geographical position, such as Tampico, Mexico. (c) Greater interest in home fields with ready market at hand. (d) Our ignorance of southern economic and geologic conditions, due to the distance between those areas and our financial centers. (e) Economic conditions in the southern countries, necessitating high costs of exploration and exploitation of the fields. (f) Our lack of understanding of the business methods of the Latin-American. It must be borne in mind that the oil-development work done to the present time in South America has, with one exception,' been undertaken upon lands which possessed direct evidence of oil in seepages or asphaltic deposits, occurring either immediately upon the lands or in their close vicinity. The development of oil fields in South America is therefore in the pioneer stage. It is not at all improbable that "hidden fields" will be uncovered in future work, as has occurred notably in the mid-continental field of this country within recent years. Location The areas grouped as a unit under the title of North Argentine-Bolivian oil field extend in a narrow belt from the north-central part of

Jan 1, 1920

By W. O. Borcherdt

THE 650-ton underground mill of The Empire Zinc Company of Colorado (a subsidiary of The New Jersey Zinc Co.) serves the Eagle mine at Gilman in the Battle Mountain mining district of Colorado. The topography is rough, the mine and mill being under Battle Mountain and the alit entrance in the north wall of the canyon of the Eagle River, which is here a steel) gorge. The town of Gilman stands on a shoulder of the mountain at altitude 8975 ft., above sea level, along the Pike's Peak ocean to ocean highway and contains the company office and the usual facilities of a modern mining town. The railway contact is at Belden, altitude 8370 ft., at the bottom of the gorge directly below Gilman, where the westbound track of the Denver and Rio Grande Western Railroad is cut along the north bank and the eastbound track along the south bank of the river. A general description of the mine, mill and service facilities, with an account of the geology, character of the ore and methods of mining and milling having previously been published in a series of articles1, this paper will discuss with as little repetition as practicable the reasons for building the mill underground rather than as a conventional structure, the methods of construction employed and the experiences gained in what is apparently the pioneer plant of this type and extent.

Jan 1, 1937

By H. O. Hofman

WITH the exception of lead sulphate, all common metallic sulphates are completely decomposed upon heating into metallic oxide, sulphur trioxide, sulphur dioxide and oxygen. Some give up their trioxide readily at a low temperature, others require considerable heat and much time to be completely freed from sulphur. Kerl in 1881 arranged the principal metallic sulphates as they are decomposed by a rising temperature in the following order: silver, iron, copper, zinc, nickel, cobalt, manganese and lead, lead sulphate being decomposed only slightly at a white heat. The researches of Bradford, published in 1903, show, however, that ferrous sulphate is decom¬posed at 590° C., cupric sulphate at G53° C. and argentic sulphate at 1,095° C. By the present investigation it will be seen that zinc sulphate is decomposed at 739° C. As far then as our present knowledge goes, the order in which the decomposition of the leading metallic sulphates takes place is the one given in Table I.

Jan 1, 1905

By S. W. Zanolli

The history of labor relations in the coal industry of the United States is a study of its collective bargaining. This study of collective bargaining is largely the history of the United Mine Workers of America and its contractual relations with the various coal mining employers who have produced this country's coal over the years under a free enterprise system. There have been other unions in the picture from time to time and some coal miners have mined coal without representation by any union. Even today some 25% of the nation's coal is produced outside of the collective bargaining relationship with the UMWA. However, more than 100,000 coal mine wage employees - well over 75% of the total in the industry - are covered by labor agreements negotiated for them by the UMWA. Practically all of these work in bituminous mines.

Jan 12, 1972

By H. P. Allen

The Achotla mill of the Cia. Minera de Penoles is of special interest in that it is one of the few still employing the chloridization process. The ore milled comes from the Suriana mine and consists of both oxide and sulphide, from neither of which can the gold or silver be extracted by a simple cyanide treatment. The mill was built in 1927, after several years of study in the development of the process1, and operated from December of that year until October 1930. Operations were resumed in February 1935, and have been continuous since, treating approximately 5000 tons per month, while the mine is getting up to full tonnage of 6500 tons per month. Transportation of Supplies The property is in Guerrero, Mexico, some 175 km. by airline southwest of Mexico City. The mill site is at Temisco (Fig. I), 8 km. from the Balsas River and 4.8 km. by aerial tram from the mine. At Temisco are the general office, shops, warehouses and laboratory serving both mine and mill. Here sufficient water is available either from a small creek running through the property or from the Balsas River, also convenient and ample storage space for the tailings. With the exception of the mine timber and a few native building materials which may be obtained locally, all supplies for both mine and mill are brought down the Balsas River from Balsas, the terminal of a Mexican National Railway line out of Mexico City. The method of transportation on the river is interesting. Rapids with very fast water are numerous, prohibiting the use of mechanically propelled boats. Those used resemble large, flat-bottomed rowboats some 22 ft. long by 8 ft. wide (Fig. 2). They are manned by two oarsmen sitting in the bow, each handling one large oar, and usually another man in the stern who, with his oar, assists in steering the boat, especially when the rapids are run. From 3 to 7 tons of freight are carried on each boat, depending upon the stage of the water, which governs also the time

Jan 1, 1939

By H. P. Allen

The Achotla mill of the Cia. Minera de Penoles is of special interest in that it is one of the few still employing the chloridization process. The ore milled comes from the Suriana mine and consists of both oxide and sulphide, from neither of which can the gold or silver be extracted by a simple cyanide treatment. The mill was built in 1927, after several years of study in the development of the process1, and operated from December of that year until October 1930. Operations were resumed in February 1935, and have been continuous since, treating approximately 5000 tons per month, while the mine is getting up to full tonnage of 6500 tons per month. Transportation of Supplies The property is in Guerrero, Mexico, some 175 km. by airline southwest of Mexico City. The mill site is at Temisco (Fig. I), 8 km. from the Balsas River and 4.8 km. by aerial tram from the mine. At Temisco are the general office, shops, warehouses and laboratory serving both mine and mill. Here sufficient water is available either from a small creek running through the property or from the Balsas River, also convenient and ample storage space for the tailings. With the exception of the mine timber and a few native building materials which may be obtained locally, all supplies for both mine and mill are brought down the Balsas River from Balsas, the terminal of a Mexican National Railway line out of Mexico City. The method of transportation on the river is interesting. Rapids with very fast water are numerous, prohibiting the use of mechanically propelled boats. Those used resemble large, flat-bottomed rowboats some 22 ft. long by 8 ft. wide (Fig. 2). They are manned by two oarsmen sitting in the bow, each handling one large oar, and usually another man in the stern who, with his oar, assists in steering the boat, especially when the rapids are run. From 3 to 7 tons of freight are carried on each boat, depending upon the stage of the water, which governs also the time

Jan 1, 1939

By Robert H. Richards, Richard W. Lodge

A great deal of speculation, as well as actual experiment, has been devoted to ascertaining the changes in the materials (luring their descent in an iron blast-furnace, affecting (1) the chemical constitution, (2) the mechanical condition, and (3) the arrangement of the materials. With a view to throw some light upon the third question, we constructed a model and tried experiments which are here described. Our model is a vertical section of a furnace, with the lines of the Edgar Thomson furnace D of 1885 for the use of which we arc indebted to Mr. Gayley. The model is 40 inches high, and made to scale (1/2 inch equals 1 foot), and the horizontal section of the space through which the charge falls at any point in the descent is 11/2 in. x d, d being the diameter of the furnace at that place. We are unable to say just where the idea of making this model came from ; perhaps, partly from The Principles of the Manufacture of Iron, and Steel, 1884, I. Lowthian Bell, p. 124 ; partly, also, from

Jan 1, 1888