By Thomas T., Read

TWO American students entered the Ecole des Mines in 1856, Joseph Lesley of Philadelphia and Thomas Egleston of New York. Lesley remained there only one year, but Egleston completed the whole 'curriculum and received, in 1860, the certificate given to foreign students .in lieu of the official appointment and degree. awarded French students. Returning home he received, in 1861, an appointment by Secretary Henry of the Smithsonian Institution to sort, label, and arrange the collections of mineralogical and geological specimens which had been brought to Washington by the various government exploring expeditions in the West. Thomas Egleston, born in New York City on Dec. 9, 1832, was the son of Thomas Jefferson Egleston, who came to New York from Massachusetts some time before 1829. The first American ancestor of the family had settled near Dorchester. in 1630. T. J. Egleston and Joseph Battell established an iron-merchandizing business* at 166 South St., New, York, which prospered exceedingly; so much so that when Thomas J. Egleston died, July 12, 1861, his estate had a book value of over $500,000. Since an older brother was expected eventually to take over this business, Thomas, who had a liking for science, went to Yale,, where he completed the regular four-year course in 1854, and then remained another year for advanced work in chemistry under Silliman. I One biographer says he went to Europe, . early in 1-856, on account of his health. It was the custom at that time for wealthy young men to make a tour of Europe after completing their academic education. Whatever the precise reason, he began scientific work at the Jardin des Plantes in Paris but soon trans* It still operating as Egleston Bros. Inc., though no direct descendants of its founder are now living.

Jan 1, 1941

ALBERT SAUVEUR, Chairman. A. A. STEVENSON, Vice-Chairman. HERBERT M. BOYLSTON, Secretary, Abbot Bldg., Cambridge, Mass. John Birkinbine, William Kelly, J. S. Unger, William H. Blauvelt, Charles Kirchhoff, Felix A. Vogel, James Gayley, Richard Moldenke, Leonard Waldo, Henry D. Hibbard, Joseph ANT. Richards, William R. Walker, Henry M. Howe, C. F. W. Rys, William R. Webster, Robert W. Hunt, E. Gybbon Spilsbury, Frederick W. Wood. J. E. Johnson, Jr., For the meeting of the Institute which is to be held in New York City, Oct. 16 and 17, 1913, the following program has been arranged: October 16, 1913, 10 A. M W. A. Forbes, Blast Furnace Gas Cleaning. W. H. Blauvelt, The Slagging Producer. Prof. F. Peter (Leoben, Austria), The Generation of Steam by Waste Heat from Furnaces. G. C. Stone, The Generation of Steam by Waste Heat from Regenerative Furnaces. W. R. Shinier, Over-Oxidation of Steel.

Jan 10, 1913

Discussion of the paper of W. R. SHIMER, presented at the New York meeting, February, 1915, and printed in Bulletin No. 99, March, 1915, pp. 557 to. 585. WILLIAM R. WEBSTER, Philadelphia, Pa.-I would like to ask Mr. Shimer how the finishing temperature of the H-beams and other beams rolled on the Gray mill at Bethlehem compare with the rolling temperatures of the rails referred to in this paper. Also, how the reductions in the rolling of the beams compare with the reductions in the rolling of the rails. I would also like to know if any drop tests were' made on the rails referred to as having been allowed to cool and then annealed; in other words, what results, if any, were obtained from tests on rails after the internal strains of rolling had been removed; and in the matter of the rail blooms, I would like to ask if they are not often heated to a higher temperature than is desirable on account of the thin flanges in order to carry the heat through to the finishing pass. The tensile strength of the steel in these rails is given as 125,000 lb. per square inch, which is almost as high as tire steel. If some of these blooms were rolled into rounds of about the same section as the head of the rail, would you not get better results from tension tests than those from the head of the rail? In other words, in rolling rounds, whether you would not be able to control the rolling and finishing temperatures better than is possible in the rail, owing to thin section of the rail flanges. Some years ago I had experience with the rolling temperatures of tire steel, running from about 127,000 to 133,000 tensile strength. These tires had the tensile strength and the deflection specified. One of the manufacturers had no trouble whatever, after a little experimenting, in meeting the conditions of the specification. Another manufacturer who made some of these tires came to the office and stated that he had tried tires from three heats of steel and could not meet the specifications and

Jan 5, 1915

By N. S. Stoloff, R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-Co and Fe- V alloys containing up to 25 pct solute have been studied in the temperature range 25° to - 196°C. The microyield stress is independent of temperature for all alloys studied, while the temperature dependence of the ordinary yield stress is large and comparable to that for unalloyed iron. An alloy-softening phenomenon is observed for many alloys relative to unalloyed iron, and appears to be a consequence of removal of inter-stitials from solution and their subsequent agglomeration. The ductile to brittle transition temperature is increased markedly by both cobalt and vanadium. Transmission electron microscopy observations reveal that cross slip and cell formation are restricted with increasing solute, which can account for many aspects of yielding and fracture behavior. IRON and other metals of bcc structure slip on many planes of the (111) zone at moderate and elevated temperatures, giving rise to wavy glide. At low temperatures, however, there is a tendency for slip to be restricted to planes of only one or two crystallographic types; in the case of Fe-Si alloys for example, (110) glide predominates, giving rise to planar slip bands."' Restriction of cross slip at low temperatures in iron has been linked by Brown and Ekvall3 to increased strain hardening in the preyield microstrain region, leading to an apparently large temperature dependence of the yield stress. Support for this view has been provided by Lawley and Gaigher4 from a transmission electron microscope study of molybdenum. They concluded that dislocations at lower temperatures, by virtue of their inability to change planes readily, are unable to interact and annihilate, leading to an increase in internal stress and work-hardening capacity. Restriction of cross slip at low temperatures has also been suggested to be an important factor in determining the ductile to brittle transition of single-phase solids, including metals of bcc structure.5 It is pertinent to note that most solute elements tend to raise the ductile to brittle transition temperature of poly crystalline ferrite,6,7 although in some cases, e.g., Fe-Cr7 and Fe-Al,8 the dilute alloys may actually yield at lower stresses than unalloyed iron. It appears, therefore, that solute elements may have an effect analogous to lowering the test temperature with regard to restricting cross glide. Such an effect has indeed been observed in the ionic alloy system KCl-KBr,9 in which bromine atoms, although causing little misfit and consequently little effect on the yield stress of KC1, have a pronounced effect in restricting wavy glide and inducing brittleness. The purpose of the present investigation was to determine the effects of selected solute atoms on the yield stress and fracture behavior of iron, and to elucidate in turn how the slip character was related to these properties. Since it is known that interstitial atoms exert a strong influence on the mechanical behavior of iron, the solute elements chosen for study were vanadium, which reacts strong with interstitials,10 and cobalt, which does not form highly stable interstitial compounds." EXPERIMENTAL PROCEDURE Four-pound ingots of each of the following alloys were vacuum-melted in zirconia crucibles: Fe-1, 5, 10, 25 at. pct Co, and Fe-1, 4, 10, 20 at. pct V. An ingot of unalloyed iron from the same original stock as that used for the alloy was remelted under similar conditions to eliminate variations in interstitial content arising from differing thermal histories. Chemical analyses of the iron, cobalt, and vanadium melt stock are listed in Table I. All ingots were rolled and swaged, commencing at 850°C, to 1/4-in.-diameter bar. The bars were then annealed at 850°C for 1 hr (except that the 10 and 20 pct V alloys were heated for 2 hr) to give a uniform equiaxed grain size of about 0.05 mm. Tensile samples of 0.125 in. diameter by 0.8 in. gage length were utilized for studies of the ductile to brittle transition. A second set of tensile samples were utilized for microstrain experiments in which strain sensitivity of 1 x 10"6 was achieved by a capacitance method.3 Cylindrical compression samples 0.250 in. diameter by 0.4 in. long also were prepared to study the influence of composition on the macroscopic yield stress, and for metallographic analyses of defor-

Jan 1, 1965

By R. W. Raymond

Alexander Brinton Coxe was born in Philadelphia, Pa., Jan. 19, 1838, the second of five sons of Hon. Charles Sidney Coxe and Ann Maria Brinton. A more extended history of his family and its important relations to the development of the United States will be found in my Biographical Notice of his younger brother, Eckley B. Coxe, published in 1895. It is therefore sufficient to say here that Dr. Daniel Coxe, a clis-

Jan 1, 1907

By S. D. Dahlgren

The plasticity of unalloyed P plutonium was studied by evaluating the strain-rate-hardening exponent, m, in the equation Values of m up to 0.33 and tensile elongations up to 680 pct were obtained for ß plutonium formed directly from the a phase. Casl bars that were cycled and tested had lower flow stresses and higher values for than uncycled bars , hut their total plastic elongations were not as great as expected because of premature failure at voids formed during cycling. Flow stresses were higher and m was lower (m = 0.15) for 9 plutonzutn formed from the y phase. ThE strain-rate-hardening exponent for plastic flow of p plutonium was determined as a function of strain rate, test temperature, and heat-treating history, and it was related to the rather large plastic elongation found previously for some plutonium tensile samples. Gardner and ~ann' obtained tensile elongations of up to 620 pct for P plutonium samples which had been completely transformed from the low-temperature a phase to the P phase before testing. Such a large percentage elongation is unusual for unalloyed metals or single-phase alloys.' The a phase is stable below approximately 112°C and (3 is stable between approximately 112" and 190"c.~ Both phases have mono-clinic structures. A temperature of 160°C is 0.58 of the effective absolute melting point, 475°C) of the p phase. The effective melting point is obtained by considering the enthalpy and entropy changes associated with the higher-temperature phase transformations and it is not the same as the experimental melting point of the highest-temperature allotrope of unalloyed plutonium. Nelson, Bowman, and Bierlein observed a striking difference between the ductility, as well as other mechanical properties, of p plutonium formed from the next higher-temperature phase (y) and the ductility of /3 plutonium formed from the a phase. The total elongation of /3 plutonium formed from the y phase was less than 5 pct. Earlier, the creep rate of 13 plutonium formed from the a phase was shown to be 200 to 500 times faster than the rate for 0 formed from y for the same test temperature and stress.

Jan 1, 1969

By C. P. Proctor

WESTERN Pennsylvania, eastern Ohio, and Illinois are carrying out experiments wherein much more slate and other impurities are loaded with the coal in the mine and hauled to the surface preparation plant for removal. In general everything is sent to the cleaning plant although there may be some gobbing in the mine. No conclusions have been announced as to the effect of such a mining system on clean coal costs. Such factors as ability of the surface plant to handle the impurities, land and facilities for disposing of the impurities, and the transportation facilities underground should be considered.

Jan 1, 1942

By J. S. Kirkaldy, R. C. Dorward

The solubilities of copper and gold in silicon and germanium have been determined by equilibration of the solid semiconductors with coexisting liquidus phases. The experimental results were combined with estimated activity coefficients of the liquidus alloys to determine the following partial molar enthalpies and excess entropies of solution for the systems: Solubility measurements were also carried out below the eutectic temperature of the copper-silicon system. The partial molar enthalpy and excess entropy of copper in silicon with respect to Cu3Si were determined to be 40.2 ±0.5 kcal per mole and 9.7 i 0.5 cal per mole — OK, respectively. It has been dentonstrated that nu-cleation and growth of intermediate compounds are retarded in copper-silicon diffusion couples. This points out the dangers of determining equilibrium solubilities by dijjusion methods. THE thermodynamic requirement for equilibrium between contiguous phases at constant pressure and temperature is that the chemical potential of each component be constant throughout the system. Equating expressions for the chemical potential of solute, component 2 say, in two phases, alpha and beta, gives

Jan 1, 1969

Geology, by O. D. Von Engeln and Kenneth E. Caster, McGraw Hill Book Co., Inc., $7.00, 730 pp., 1952.The authors desired to write a book which would supplement the work of the teacher. The effort presents the facts of historical geology as an outgrowth of the understanding of physical geology-a method in keeping with the fundamental law of geology that "present agencies and forces, acting through enormous time, have shaped the world as we see it-the law of uniformitarianism." Narrative continuity is maintained throughout the text. Each historical geology period is made distinctive, provided with an identity, and shown to have particular characteristics. Elementary Heat Power, second edition, by Harry L. Solberg, Orville C. Cromer, and Albert R. Spalding. John Wiley & Sons, 1952. $6.50, 624 pp. The authors attempt to develop an understanding of the functions, principles of construction, and actual performance of heat-power machinery as a preliminary to the study of engineering thermodynamics. Matter and energy, fuels, and combustion are considered first, followed by chapters on internal combustion engines, fuel burning equipment, and steam engineering and utilizing installations. Pumps, compressors, gas turbines and refrigeration are also dealt with.

Jan 1, 1952

By K. A. Natarajan, I. Iwasaki

The influence of dissolved oxygen and the Pt - Pt-O reaction on the measurement of redox potentials in solutions containing ferrous-ferric couple was examined. Current-potential curves were used to illustrate the shift in measured potentials toward the oxygen potential in oxygenated and deoxygenated systems at low concentrations of ferrous and ferric ions. The ranges of concentrations of the ferrous-ferric couple, in which the interference from oxygen and the platinum-oxygen reactions becomes significant, are illustrated through the mixed potential mechanism.

Jan 1, 1975

By J. R. Long, C. E. Armantrout, A. H. Roberson, T. R. Graham, R. S. Dean

THE general program of the Federal Bureau of Mines on the study of alloys made with electrolytic manganese has been extended to copper-manganese-aluminum alloys. The initial results of the work are presented in this report and concern a determination of the mutual solubilities of these three metals to form the alpha solid solution. The principal studies of this system, reported in the literature, have been focused on the Heusler alloys containing 10 to 30 per cent Mn with 9 to 15 per cent Al. These investigations concern the ferromagnetic properties and the determination of the crystallization contours, with little emphasis on the phases present in the solid state outside of this area. Heusler1 recognized a breakdown of the beta solid solution of the magnetic alloy, which he says decomposes into the alpha, beta, and gamma phases of the copper-aluminum system, somewhat modified by the presence of manganese. Rosenhain and Lantsberry2 examined alloys ranging up to 10 per cent Mn and io per cent Al but were unable to reach definite conclusions concerning the phase boundaries in that area. Krings and Ostmann3 made magnetic studies and examined the system by thermal analysis. They present contours of the liquidus surface but do not place any of the phase boundaries. Corson4 [ ] has drawn a hypothetical boundary for the alpha field with few data to support such construction. The binary systems involved have received considerable attention by numerous investigators, and their general features are well established. The hopper-aluminum system (Fig, I) has been thoroughly examined by Stockdale,5 who places the limit of solubility of aluminum in copper at 7.4 per cent at the liquidus and 9.5 per cent at room temperature. Smiths established the eutectoid temperature at 570°C. by a study of isothermal decomposition of the beta phase. The copper-manganese system (Fig. 2) has been recently reviewed by Dean and co-workers.7 Using high-purity alloys, they place the solubility of alpha man-

Jan 1, 1946

By H. S. COOLEY

TO talk about a "factor of economy" in connection with the wire ropes used in mining practice may be coining a new phrase. If such be the case it needs no other apology than that economy in wire rope usage is so bound up with the factor of safety as to justify a similarity in naming that makes one suggest the other. At the latest Wire Rope Research Conference, held under the auspices of the A. S. M. E., Re- search Committee and Engineering Foundation, data were introduced covering mine ropes working under

Jan 1, 1930

By O. G. Lellep

IN every country economic circumstances prescribe the method used to produce a commodity at lowest cost. In Pennsylvania a man's wages for working 4 hr buys a ton of coal wholesale; in Germany a laborer must work 40 hr, or ten times as long. In western Europe, therefore, conservation of fuel is of primary importance, and recent practices of burning lime and cement differ from those employed in the United States. This paper presents data collected during a trip through western Europe in 1953. Considered uneconomical, shaft kilns for burning cement disappeared in the United States two generations ago. But because required capital investment is low and operation greatly improved, shaft kilns are still used to some extent in Europe, where fuel costs are high, and are even included in designs for plants under construction. During the last 50 years shaft kilns have been maintained at the same physical size, while their output has been increased at least four times.

Jan 7, 1954

By D. E. Thomas

Oxidation rate constants were determined for Cu-Pd and Cu-Pt alloys as a function of alloy composition and temperature. Reaction products were identified. Relationship between oxidation rate constants and diffusion constants in the reaction zones is discussed. THE mechanism of oxidation of alloys is consider--'¦ ably more complex and not so well understood as that of pure metals. The oxidation of a one-phase binary alloy of which one component is a noble metal should logically be the simplest case of alloy oxidation, for in this case one is concerned presumably only with the oxidation of the base metal and the diffusion process by which it reaches the reaction site. This had led a number of investigators to study such systems. Probably the earliest work was that of Tammann and Rienacker' on the tarnishing of Cu-Au alloys at temperatures up to 300°C. These alloys oxidize according to the logarithmic law, that is, the film thickness is proportional to the logarithm of the time. The rate of film formation was found to decrease with increasing gold content. Raub and Engel² investigated the oxidation of Au-Cu, Cu-Pd, Au-Ag-Cu, Au-Pd-Cu, and Ag-Pd-Cu alloys at 750°C in air. These alloy systems form a continuous series of solid solutions at the temperature of oxidation with the exception of those containing silver. Au-Cu alloys oxidize parabolically, the rate constant decreasing slowly with increasing gold content up to about 15 atomic pct* Au, and more rapidly thereafter. An alloy with 14 pct Cu forms only a very thin layer of CuO on the surface and probably also a subscale.† Alloys containing more than 14 pct Cu have scales consisting of CuO and subscales of Cu,O embedded in nearly pure gold. The Cu-Pd alloys obey the parabolic law except for slight deviations for alloys containing 53 and 84 pct Cu. The overall oxidation rate decreases rather smoothly with increasing palladium content. A scale consisting of a thin layer of CuO and a thick layer of Cu²O and a subscale of Cu²O embedded in nearly pure palladium was observed for alloys containing 84, 53, and 30 pct Cu. An alloy with 19 pct Cu formed only a subscale of CuO embedded in nearly pure palladium, and an 8 pct Cu alloy formed only a thin film which was presumed to be PdO. The ternary alloys considered by Raub and Engel oxidized in much the same way as did the binaries. Wagner and Grunewald³ found that Ni-Au alloys, oxidized at 900°C in oxygen, formed a scale of NiO and a subscale containing NiO and gold. The overall oxidation rate increases with increasing gold content, passes through a maximum and then decreases to zero for pure gold. The fact that gold increases the oxidation rate was attributed to "pores" in the scale. Kubaschewski' investigated the air oxidation of alloys of platinum or gold with up to 10 pct Cu or Ni at temperatures in the range 300" to 1550°C. Parabolic behavior was noted for all alloys except Au-Ni, with rates decreasing in the order Au-Cu, Au-Ni, Pt-Ni, Pt-Cu. The diffusion coefficients for the latter three systems are known, and they decrease in the same order. However, activation energies for the oxidation of these alloys do not agree with the activation energies for diffusion in the respective alloy systems. Kubaschewski and Goldbeck7 nvestigated the oxidation of Ni-Pt alloys in air at temperatures of 600"

Jan 1, 1952

By Y. L. Yao

A scale based on existing data for the mutual solid solubilities of metals in binary systems has been compiled. This scale is useful for estimating the relative magnitude of two solubilities, provided that these two metals do not form a continuous series of solid solutions. In his classic work on the theory of metallic solid solutions, Hume-Rothery proposed that, other things being equal, a metal of lower valency should be regarded as more likely to dissolve one of higher valency than vice versa. He called this the "relative valency effect". Later he found that the application of this general principle was limited to the three univalent metals: copper, silver, and gold. In dealing with alloys of these metals with metals of higher valency, Hume-Rothery stated, it is usually found that the solid solution of the univalent metal is of the greater extent.&apos; The question of whether there is a systematic trend in comparing the relative magnitude of mutual solubilities, if valency is not considered a criterion, naturally arises. The present paper proposes a "mutual solid solubility" scale on an empirical basis. The order of its arrangement is determined by the relative magnitude of mutual solid solubilities. Some applications of and inferences from this scale are given. ORIGIN AND SCOPE OF THE SCALE An extensive survey of over 400 binary phase diagrams shows that, with certain exceptions and within certain limitations, metals can be arranged in the following order: Na Zn Cd Ga Bi Ge Sb As Hg Sn Si Mg Li Ba In Tl Pb Al Ca Be Mn Cr Re W Mo Cu V Ta Fe Ru Cb Co Ti Hf Ni Os Zr Ir Pt Au U Rh Ce Pd Ag Th so that a metal higher on the scale tends to have a higher solubility in a metal lower on the scale than vice versa. some experimental solubility data are given in Table I. These data, unless otherwise specified, are taken from Hansen and Anderko.6 Throughout this paper, the term "solubility of A in B" is taken to mean the maximum solid solubility of A in B in atomic percent, while the maximum solid solubility of B in A in atomic percent is called "reciprocal solubility". The exceptions found in the above-mentioned survey are: Al-Ag system, 20.34 at. pct Al in Ag, 23.8 Ag in Al; Mg-Pb system, 5.9 Mg in Pb, 7.75 Pb in Mg; As-Sn system, vanishingly small amount of As in Sn, a large As primary solid solution; Cd-Hg system, Cd in Hg <Hg in Cd; Mg-T1 system, 5(?) Mg in ßT1, 15.4 T1 in Mg; W-Ti system, -21 W in ßTi, -25 Ti in W; Zr-Ag system, probably small amount of Zr in Ag, 20 Ag in ßZr.7 Considering the large number of examples, the exceptions are few. It is remarkable that metals may be so arranged without considering other factors such as size, crystal structure, electronic structure, and so forth. A limitation to the use of the scale is the fact that it cannot be tested for two metals forming a continuous series of solid solutions. It is interesting to point out that when the continuous solid solutions have a miscibility gap the critical composition is

Jan 1, 1961

By J. A. Bownocker

THE Pittsburgh is one of the most important coal beds of Ohio. It was the last of the great coal beds to be worked extensively in that State, has the largest area of virgin coal, and will in all probability be the last of the great deposits to be exhausted. The line of outcrop sweeps nearly southwest in a sinuous line from Jefferson County on the north to Lawrence on the south, a distance on a bee-line of at least 150 miles. (Fig. 1.) The maximum width of the area under which this coal is due is about 55 miles, but in most places it is less than half that and in the two southern counties it is in places restricted to narrow ridges. Here as elsewhere the Pittsburgh coal forms the base of the Monongahela formation, and the following section taken from Condit shows the position of this bed with reference to certain higher ones in this field:1 FEET INCHES Shales and thin beds of limestone 24 5 Coal, Meigs Creek, No. 9 4 0 Shale, sandy 11 0 Coal 0 8 Shale, clayey 6 0 Coal, Lower Meigs Creek 3 0 Shales,clayey 2 0 Limestones and thin layers of clay 25 0 Unseen 11 0 Coal, Redstone 2 0 Unseen 11 0 Coal, Pittsburgh, No. 8 8 0 Clay 5 0 Limestone 4 0 From the standpoint of continuity the Pittsburgh coal of Ohio must be classed with the patchy type. As the map shows, the coal is thin or wanting along many miles of the line of outcrop. The large deposits form three separate areas, which, in order of their importance, are generally known as (1) the Belmont, (2) the Federal Creek, and (3) the Gallia fields.

Jan 10, 1926

By W. A. Backofen, G. Y. Chin, W. F. Hosford

The ductile fracturing process was studied in single-crystal and poly cvystalline aluminum deformed in tension over a temperature range from 295° to 4.2°K. At temperatures as low as 77°K, the fracture of "inclusion-free" material, including zone-refined aluminum, was by rupture (-100 pct RA). At 4.2 OK, fracture was brought on by adia-batic shear. Metallographic examination did not disclose any voids or slip-band microcracks, thus negating for inherently ductile metals any mechanism of void nucleation by vacancy condensation or of cracking due to dislocation pile-ups. In Izigh-purity aluminum not treated to be inclusion-free, fracture at temperatures as low as 45°K was of the double-cup type and a result of void formation. The reduction-of-area decreased as temperature was lowered, corresponding to the earlier appearance of voids. Such behavior was rationalized in terms of a larger increase, with decreasing temperature, in the .flow stress relative to the strength of the inclusion-matrix interface. Evidence for low-temperature adiabatic shear was found in discontinuous flow at 4.2"K, in the transition to a localized shear fracture at low temperatures, and in the suppression of shear fracture with an elastically hard pulling device. A simple analysis for the initiation of adiabatic shew permitted a general correlation of the various contributing factors. It has been pointed out that the duration of shear depends upon effective mass and elastic stiffness of the deformation system. IT has long been recognized that fracture* may Throughout this paper, the term "fracture" is taken to mean any process that results in the separation of a material into two (or more) parts. Thus rupture as it may be encountered in a tension test leading to 100 pct reduction-of-area is included in this category. occur in a ductile mode, and that the process can be of great practical as well as general interest. Much information about ductile fracture has also been accumulated over this period, but only recently has an understanding of mechanism begun to appear. Ludwik,&apos; in 1926, first reported fracture in a tensile specimen starting with a central crack in the necked section. Since then, other studies have disclosed that such cracks may form by the coalescence of voids nucleated in this region where hydrostatic tension is highest.2-4 Rogers and Crussard et al.&apos; have emphasized void formation and reori-entation along localized shear bands as a mode of crack propagation. pines6 has considered the tensile rod as a bundle of fibers joined by weak interfaces, which subsequently separate to allow individual fiber contraction. The notion of cavity growth and coalescence by purely plastic processes was discussed by Cottrell: who added that the tensile reduction-of-area ought not to be sensitive to temperature. On the other hand, it has been observed that the reduction-of-area is greatly increased if tests are carried out at high temperaturesa or under high hydrostatic pressure.&apos; Fracturing anisotropy in wrought products lends support to the idea of void formation from preexisting flaws strongly aligned by earlier processing.&apos;&apos;-l2 There is evidence that many voids result from the fracturing of inclusions or separation at the inclusion-matrix interface Another possibility is that voids grow out of pore volume produced in the initial solidification and never fully removed in later working. In general, a structure 3f particles, pores, and weak interfaces can be expected, at least in materials of engineering interest. Vacancy condensation has been suggested as an alternative mechanism of void formation for materials considered to be inclusion-free.13 Yet experience has shown that tensile reduction-of-area increases with purity, to the extreme of rupture as so often observed in single crystals. Adiabatic shear has an important bearing on ductile fracture. It occurs when the decrease of flow stress, as a result of local temperature rise from heat generated during straining, becomes larger than the increase due to strain and strain-rate hardening. As demonstrated by experiments on punching of plates,14 a large temperature rise may be brought about by rapid straining. Adiabatic flow as a result of the high strain rate reached in an ordinary tensile specimen just prior to separation may account for the cone formation in cup-and-cone fracture;14 evidence of such local heating has been presented.15 For geometrical reasons, however, pure sliding along the conical surfaces is unlikely, and separation under tensile forces is probably an important accompanying feature of the shear.7 In deformation processing operations, a high shear-strain rate may exist at boundaries between plas-

Jan 1, 1964

By G. P. Chatterjee

HARDNESS is one of the most common properties of metals and alloys but is one of the most difficult to define or express in terms of the fundamental units. In the Brinell or Vicker&apos;s hardness test, the hardness number N is defined as N = L/A where L is the load in kilograms and A is the area in mm&apos;. This does not necessarily imply that a pressure of N kilograms per mm2 actually acts on the specimen.&apos; It is essential that for a true comparison of hardness values the angle of indentation be kept constant,&apos; a which is not done in the Brinell test. For this and other reasons, the Brinell hardness value is not based on a satisfactory physical concept.&apos; The concept of hardness based on the work done per unit volume of indentation3-6 offers a simple and scientific definition. An attempt has been made here to develop this concept (at constant angle) and to compare the values so obtained with the Bhn for different metals and alloys. In Fig. 1 a vertical load L is applied to a compara- tively hard ball of diameter D creating an indentation of diameter 6 and depth h on the specimen S. The work done, W, is then given by W = So Ldh. [I] Since L is not independent of h, Honda and Takahasip and Matsumura" assumed different functions leading to equations which do not apply equallye to a wide variety of metals and alloys. A better relation is obtained from Meyer&apos;s Law L = ad" [2] where A and n are constants depending on the nature of the material but independent of the ball diameter D. From Fig. 1 it is obvious that h = R(l — cosq) and d = 2R sin 8.

Jan 1, 1957

By Earl Ingerson

BORE surfaces of used guns commonly show a pattern of cracks in various degrees of development. It has been suggested that these cracks may aid erosion by providing channelways for the gases, eventually leading to the tearing out of blocks of metal. Under the general studies of gun erosion conducted at the Geophysical Laboratory it appeared desirable to consider this factor, and to determine the resistance to surface cracking offered by gun steel and by various other materials that might be used in the bores of guns. METHOD AND APPARATUS In order to make such a determination it is necessary to have (I) an arrangement in which the surface to be studied can be subjected to conditions similar to those in a gun with respect to temperature, pressure (developed by explosion gases), composition of the gases and length of time the surface is exposed to the gases; and (2) a specimen that can be examined readily after any number of shots, and then fired again, if necessary. The first of these conditions can be met by using an explosion vessel designed by H. S. Roberts of the Geophysical Laboratory. Fig I shows a cross section of the apparatus. The "gun" G from which the charge is fired is made from the receiver of a caliber 0.30 army rifle, M1903, and the charges are prepared in caliber 0.30 cartridge cases. The test specimen S is held in place by a cone-shaped plug P and by a steel ,bridge B which is bolted to the outside of the explosion vessel on either side of the section shown. The plug, in turn, is held in place by a screw collar C. Maximum pressure is controlled by a brass rupture disk R. Part of the explosion gases flow past the two flat areas on S. st the two flat areas on S. Temperature and composition of gases, and the time before the rupture disk breaks, can be controlled by amount and kind of powder used, and pressure can be controlled by using rupture disks of different thickness. While the explosion vessel used was not designed so that temperature and pressure could be measured, in other vessels of closely similar size and shape containing proportionate charges of the same kind of powder as that used for standard testing procedure, values of 2700°K and 5000 psi were obtained. Since the orifices past the flat areas on the plug are small compared to the rupture disk hole (1:16), most of the gas goes out through the rupture disk when it breaks. The amount that goes by the plug depends on (I) the pressure attained before the rupture disk breaks and (2) the time it takes for this pressure to be built UP. The second condition (examination at will after any firing) is met by using for specimens short rods that have flat areas ground on opposite sides. These flat

Jan 1, 1947

By Per Kofstad, Hallstein Kjöllesdal

The oxidation behavior of niobium (columbium) has been studied in the temperature range 500° to 1200°C and at oxygen pressures of 760,100, 10, 1, and 0.1 mm of Hg. The work comprises kinetic studies of the oxidation as well as structural investigations of the oxidized specimens by means of X-ray diffraction, electron diffraclion, electron microscopy, and metal1ographic techniques. The oxidation reaction has a highly irregular temperature dependence and is unusually sensitive to changes in the oxygen pressure. The complex oxidation behavior is suggested to be due to formation of different Nb2O5 modifications in different temperature regions. During oxidation oxygen is also dissolved in the metal. Formation of oxide whiskers take place on the oxide surface at temperatures above approximately 800°C. VARIOUS aspects of the oxidation of niobium have been studied.l-12 The investigations show that niobium has a complex oxidation behavior, and the oxidation

Jan 1, 1962