By Richard J. Borg

The vapor pressure of Cd in equilibrium with CdSb in the presence of excess Sb has been measured using the Knudsen effusion method over the temperature range 276° to 379°C. The free energy of formation of CdSb is given by AF° = -1.58 + 1.53 x l0-4 T, kcal per mole. The enthalpy and entropy are obtained from the temperature coefficient of the .free energy. CADMIUM and antimony have almost imperceptible mutual solid solubility but form a single stable intermediate phase, CdSb. This phase, according to Han-sen,l extends from about 49.5 at. pct to 50 at. pct Cd at 300°C and has the orthorhombic structure. The free energy of formation of CdSb can be calculated from the vapor pressure of Cd for compositions which contain less than 49 at. pct Cd. The appropriate reaction and formulae are given by Eqs. [I] and [2]- CdSb(s, ~ Cd(g)-, +Sb(s) [1] Since Sb is in its standard state, Af - N,,AF'-,, = NcdRT In a,, = NcdRT InP/PO [2] In Eq. [2], P, is the vapor pressure of Cd in equilibrium with the alloy, and Po is the vapor pressure in equilibrium with pure solid Cd. It is implicit in this calculation that the free energy only slightly changes within the narrow limits of the single phase field. Thus, the value obtained from the antimony-rich boundary is truly representative of the stoi-chiometric compound. The results reported herein are obtained from a mixture near the eutectic composition, i.e. 59 at. pct Sb. Only two previous investigations" of the free energy of formation of CdSb have been made. Both relied upon the electromotive force method, and measurements were made over relatively narrow temperature ranges which strongly influences the reliability of the values of AH and aS. EXPERIMENTAL The eutectic composition is prepared by fusing reagent grade Cd and Sb by induction heating in vacuo with the starting materials held in a graphite crucible having a threaded lid. The material obtained from the initial melt is pulverized, sealed under high vacuum in a pyrex capsule, and annealed at 420°C for two weeks. X-ray analysis"gives the following lattize parameters: a = 6.436A, b = 8.230& and c = 8.498A using Cu Ka radiation with A = 1.54056. These values are in fair agreement with the result? previously reported by Al~in:4 i.e. a = 6.471A, b = 8.253A, and c = 8.526A. Vapor pressures are measured using an apparatus which has been described elsewhere,= however, with a single important modification. Knudsen effusion cells are made of pyrex with knife-edged orifices made by grinding the convex surface of the lid on #600 emery paper. Photographs taken at known magnifications using a Leitz metallograph enable the determination of the orifice area. Numerous calibration measurements of the vapor pressure of pure Cd give close agreement with values previously reported5,= thus indicating that no significant error can be ascribed to the substitution of glass cells for metal cells used in previous work. Because the vapor pressure of Cd is reliably established and because it is difficult to obtain Clausing factors for the glass cells, the final values used for the orifice areas are calculated from the calibration measurements of the vapor pressure of pure Cd. Effusion runs are started in an atmosphere of purified helium which is quickly evacuated as soon as the cell attains thermal equilibrium. Less than one minute is necessary to obtain high vacuum after evacuation begins, and the temperature seldom varies by more than 0.5oC from the value obtained prior to pumping out the helium. RESULTS The results of this investigation along with other pertinent data are tabulated in Table I. Fig. 2 is the familiar graph of log P against T-10 K. At least mean squares analysis of the data presented in Table I yields the following equation: log1DJP = 8.790 - 6472 x T"1 [3] The deviations of the individual measurements from the values calculated with Eq. 131 are given in column six of Table I; the average deviation is 4.0% of the calculated value. Although the partial molal properties change significantly with composition within the single phase region, the integral thermodynamic value should remain relatively constant. Hence the results of the following calculations, which use the data obtained for the eutectic composition, are probably representative of the equi-atomic compound. Eq. [4] describes the vapor pressure of pure Cd as a function of temperature and may be combined with Eq. [3] to

Jan 1, 1962

By S. Koski, J. Vanderbeek, J. Enriquez

"The Cerro Verde copper-molybdenum porphyry mine, majority owned and operated by Freeport- McMoRan Copper & Gold, is located 30 km southwest of Arequipa Peru. The concentrator, which produces copper and molybdenum concentrates, started operating in late 2006 with a 108,000 tpd design capacity, processing primary sulfide ore (mainly chalcopyrite and molybdenite). Plant capacity was recently increased to 120,000 tpd. The comminution circuit consists of one 60” x 113"" primary crusher, four MP-1000 secondary crushers in closed circuit with dry screens, four 2.4m x 1.6m High Pressure Grinding Rolls (HPGRs) in closed circuit with wet screens, and four 7.3m x 11m gearless ball mills in closed circuit with cyclones. The HPGR circuit is fed by the Secondary Crushing circuit product at a T80 of 35 millimeters, and the HPGR circuit product feeds the Ball Mill circuit at a T80 of 3000 microns.This paper describes operating experiences with HPGRs during these first four years highlighting improvements in operating practices and presentation of data regarding operational efficiencies, also discussed are the primary benefits provided by HPGRs such as production of micro fractured particles, reduced ore Bond Work Index, and reduced power consumption. Cerro Verde represents the first installation of HPGRs in both the copper industry and large scale hard rock mining."

Jan 1, 2012

By M. L. Free, N. Dhawan, M. S. Safarzadeh, J. D. Miller, M. S. Moats

"The drum agglomeration of nickel laterite and gold ores has been optimized through the design of experiments (DOE) using a Taguchi L16 (45) orthogonal array to determine the optimum conditions for maximizing average agglomerate size and minimizing the amount of fines. The effects of controllable operating factors including moisture content (nickel laterite ore: 34-37%; gold ore: 7-10%), retention time (2-3.5 min), drum speed (15-45% critical speed), drum load (nickel laterite ore: 8-32 %; gold ore: 6-22%) and acid concentration (150-600 g/L) on the performance of the agglomeration process were studied.For nickel laterite ore, maximum average agglomerate size and minimum percent fines (-1 mm) occurred under the following conditions: drum load (23.7%), moisture (36.5%), time (3 min), drum speed (30% critical speed) and acid concentration (150 g/L). Under the studied nickel laterite ore conditions, the most effective parameters for maximizing average agglomerate size and minimizing the amount of fines were found to be drum load and acid concentration, respectively. Drum speed had a statistically significant effect on minimizing the amount of fines. Maximum average agglomerate size and minimum percent fines (-1 mm) for gold ore occurred under the following conditions: drum load (19.3%), moisture (8.5%), time (2 min 15 s) and drum speed (40% critical). The most significant factors for maximizing average agglomerate size and minimizing the amount of fines for gold ore were found to be drum load, time and moisture.IntroductionSeveral heap leach operations have experienced problems in terms of poor recovery due to percolation issues caused by low-grade complex ores, tailings and clayey deposits. Poor percolation can lead to low metal extraction due to solution channeling or the development of impermeable/dead zones within the heap (Dhawan et al., 2012; Kappes, 2005). Improper heap building practices such as the use of loose agglomerates and inadequate attention toward the presence of clay minerals have been among the main reasons for percolation issues. During the transport of ore material, severe segregation of the material can occur. To overcome percolation problems, a major improvement was made through the introduction of agglomeration prior to ore placement. If the ore particles and agglomerates are of similar size, segregation can be avoided to a great extent (Dhawan et al., 2013; Kinard and Schweizer, 1987; McClelland and van Zyl, 1988). Agglomeration improves the uniform percolation of solution through ore heaps and is applicable to many ores, wastes and milled tailings (Bouffard, 2005; Dhawan et al., 2013). Manning and Kappes (2005) reported agglomeration/ stacking accounts for ~14% of the total heap leaching operating cost. The cost of binder is a primary contributor toward the total cost. Also, the lack of consistent quality control tests for agglomerate often leads to operational problems. The details are mentioned elsewhere (Dhawan et al., 2013). Considering the significant contribution of the agglomeration/stacking step toward the total heap leach operating cost, it is appropriate to study the agglomeration behavior and its optimization for two different ores. The reason to study the same parameters for different ores is the fact that significant variability in the agglomeration behavior of different ores has been reported to exist in industrial operations."

Jan 1, 2015

By Jack T. Work

Spiraling costs in every segment of the open-pit mining cycle is a fact of life that every operator must reckon with. The introduction of various shock absorbing devices for rotary drilling is one recent innovation that may significantly reduce overall drilling cost, increase drill availability, and lower maintenance requirements. In a recent all-inclusive test in taconite ores, shock absorbers on Bucyrus-Erie BE 60R and Gardner¬Denver GD 120 rotary drills were directly responsible for overall savings of up to $41.06 per hour. What is It? A shock absorber is simply a device installed between the rotary drive head and drill steel that cushions the two. It functions in the same manner as springs and shocks on an automobile. Some benefits associated with use of the tool are readily apparent on a daily basis; other benefits are realized over longer time intervals and through continued use. A properly designed shock absorber will: •protect the drill from severe vi¬brations, improve rock bit performance, allow application of the best weight-on-bit and rotating speed under all drilling conditions, •function effectively over a wide range of applied bit weights, • have a spring rate soft enough to perform its primary function of absorbing both rotary and vertical vibrational forces generated by rough drilling, •be reliable and subject to as little maintenance as possible, •be easy to install and remove, and • be of such an economic benefit so as to offset the added expense of its application. A shock absorbing tool developed by BJ-Hughes Inc. was used in a recent test. The "Smoothdrill" is just one of the products currently available. This unit absorbs both rotary and vertical shock loads and has no mechanical parts so lubrication is unnecessary. A rebuild of the unit consists of removing the worn rubber element and inserting a new element, an operation taking less than one hour. Minimizing Vibrations Severe vibrations on a blasthole drill operating in broken and discontinuous formations have visible effects. These vibrations often cause structural damage when allowed to' continue, resulting in fatigue cracks in the mast and related structural components in the drill. When rough running formations are encountered, drilling must be interrupted and possibly shut down. Usually, the drill operator resumes drilling using less down pressures and various rotational speeds until firmer drilling is encountered. An effective shock absorber can substantially reduce these vibrational forces so more down pressure can be applied in bad ground. It is generally accepted that longitudinal vibrations and cyclic forces are more effectively reduced if a tool is designed to incorporate a relatively "soft" shock absorber. The softness of any shock absorbing tool is best judged by its spring rate-the weight required to produce a given amount of deflection, commonly expressed in units of kg per mm or pounds per inch of deflection. All shock tools use a resilient member such as rubber springs, steel springs, fluid, or gas springs to absorb

Jan 4, 1980

NEW MEMBERS The following list comprises the names of those persons who became members during the period of July 10, 1917, to Aug. 10, 1917. ARNOT, STANLEY L., Engr., Plymouth Cons. Gold Mines; Ltd., Plymouth, Amador Co .2 Cal. BARRETT, LESLIE PARK, Asst. Geol.... Michigan Geological Survey, Lansing, Mich. BENNIE, JOHN WILLIS Gen'l. Mgr., Shannon Copper Co., Clifton, Ariz. BRINTON, OWEN FUGATE Mgr., Admiralty Zinc Co., Quapaw, Okla. BRODERMANN, JORGE, Civil Engr., Compania Minera San Francisco, Havana,Cuba. BROWN, RICHARD HENRY JR., Sales Engr., Ingersoll Rand Co., 300 N. Broadway, St. Louis, Mo. BROWN, STANLEY Chile Exploration Co., Chuquicamata, Chile. BUDDECKE, WILLIAM A Pres., Point Milling & Mfg., Co. Mineral Point, Mo. BURGESS, GEORGE K., Physicist and Chief, Division of Metallurgy, Bureau of Standards, Washington, D. C.

Jan 9, 1917

By B. M. P. Pingua, M. Nabiullah

Number of mine accidents occurred in Indian surface mines are due to poor quality of explosives and blasting accessories. Amlori open cast project is one of the major coal producing projects in India. Standard drilling and blasting parameters are used to achieve desired productivity of the mine. 150 and 260 mm diameter blast holes are used for blasting in coal and overburden benches. Most of shovel benches are 12 to 16 m in height and dragline benches vary from 25 to 30 m. High-energy bulk emulsions are used for blasting. The cup density and velocity of detonation of bulk emulsion explosives are 1100 to 1200 kg/m3 and 3.8 to 4.5 km/s respectively. An incident occurred on fire bench of Amlori open cast mines during mucking of blasted muck.

Jan 1, 2008

By Albert L. Toenges

The State Division of Geology Arkansas Resources and Development Commission, and the Arkansas-Oklahoma Coal, Operators Association requested assistance from the Bureau of Mines in a study of coal-mining methods and practices in .Arkansas coal mines with the objective of reducing production costs. On October 7, 1946, a joint meeting was held by representatives of the Arkansas Resources and Development Commission, approximately 30 coal-mine Operators of the Arkansas -Oklahoma Coal Operaters Association, and representatives of the Bureau of Mines. The many problems confronting the coal industry in Arkansas, including mechanical mining in thin beds, costs, labor, and working time were discussed. Following this Meeting, a joint letter from Harold B. Foxhall, State geologist, and -P. R. Stewart, commissioner, Arkansas-Oklahoma Coal Operators Association, was addressed to Dr. R. R. Sayers; former ,Director of the Bureau of Mines, requesting that mining conditions in Arkansas be studied.

Jan 1, 1949

By V. M. S. R. Murthy, Biswaraj Dash, Somnath Chattopadhyaya

Tunnel boring machine (TBM) has been in focus for the last few decades and is currently the most preferred excavation method for metro, hydro and irrigation tunnels. Tunnelling in hard and abrasive rock conditions, in particular, is adversely affected by a very low advance rate coupled with increased TBM disc cutter failures and cutterhead jamming, seeking an in-depth understanding of the design and operational processes of the boring components of the TBM. The cutterhead and disc cutter are the critical boring components of the machine, influencing the boring process significantly. These components directly interact with the rock and hugely influence the machine’s efficiency. This paper encapsulates a review of prior studies related to disc cutter design and the cutterhead design for hard rock TBM tunnelling. A design methodology for designing and selecting a disc cutter and a cutterhead is suggested. The design methodology has been applied for a hard rock tunnelling case, and suitable design specifications for the boring components were arrived at. The disc cutter and cutterhead specifications designed based on the suggested methodology closely match with that of deployed TBM specifications. It may be observed that except for the case of high-strength and high-abrasive rock (greyish quartzite), for the rest of the rocks, the suggested design can meet the desired advance rates.

Jan 31, 2024

By Donald P. Tuchman, Robert P. Vinson, Jon C. Volkwein

Research by the National Institute for Occupational Safety and Health (NIOSH) has pursued quartz analysis for the specialized ?lter assemblies of a new worker-wearable personal dust monitor (PDM). The PDM is a real-time instrument utilizing a tapered element oscillating microbalance (TEOM®). Standard ?berglass TEOM ?lters cannot accommodate the desired P-7 infrared analytical method used by the Mine Safety and Health Administration (MSHA). Novel ?lter materials were tested with the objective of demonstrating this type of analysis. Low temperature ashing and spectrometric examination were employed, revealing that nylon ?ber candidate ?lters left minimal residual ash and produced no signi?cant spectral interference. Avoiding titanium dioxide in all ?lter materials proved to be a key requirement. Fine quartz particulates were collected on prototype ?lters in a Marple chamber, either open-faced or through PDMs during test runs. The ?lters were then subjected to MSHA P-7 analysis and the spectrometrically based analytical results for quartz mass were compared to reference measurements. Also, PDM instrumental mass readings were compared to ?lter gravimetric measurements. Results suggest that the P-7 method is adaptable to variations in ?lter materials and that quartz dust analysis by the P-7 method when utilizing the new ashable PDM ?lters can have accuracy and precision within 10% and 4%, respectively. This is within the declared 13% accuracy and 7–10% precision of the P-7 method itself. Instrument mass readings had modest positive bias but met NIOSH accuracy criteria. Continued work with specialized PDM ?lters is merited, as they are a new type of TEOM sample amenable to ashing analysis of particulates.

By William E. Ford, Edward Salisbury Dana

Normal phosphoric acid is H3P04, and consequently normal phosphates have the formulas R3PO4, R3(P04)2 and RPO4, and similarly for the arsenates, etc. Only a comparatively small number of species conform to this simple formula. Most species contain more than one metallic element, and in the prominent Apatite Group the radical (CaF), (CaCI) or (PbCI) enters; in in the Wagnerite Group we have similarly (RF) or (ROH).

Jan 1, 1922

By R. F. Miller, R. F. Campbell

Sixteen steels containing different combinations of chromium and molybdenum, in amounts up to 5 per cent of each element, were examined for microstructure and hardness after air cooling and after furnace cooling from suitable austenitizing temper- atures. Diagrams summarizing the structnres and hadness resulting from these two cooling rates are presented (Figs. 3, 4, 7).t Data were also obtained on the influence of these two elements, individually and in combination, on the depth of decarburiza-tion observed after furnace cooling (Fig. 8). Composition of Material The chemical composition of the steels investigated is given in Table I. The plain carbon steel was made in a 2 5-ton Heroult electric-are furnace, while the alloy steels were made in a 4.5-ton Ajax-Northrup elec- tric induction furnace. The cast ingots were hot-rolled to 1.75-in. bars. Air-cooled Series The I.75-in. bars were forged to flat plates, 0.25 in. thick, from which specimens 0.5 in. wide by 2 in. long were cut. The specimens were pretreated to improve their homogeneity by heating to 1830°F. (I000°C.) for 20 min. and oil-quenching. They were then reheated to 1740°F. (950°C.) for one hour and air-cooled, after

Jan 1, 1942

By R. F. Campbell, R. F. Miller

Sixteen steels containing different combinations of chromium and molybdenum, in amounts up to 5 per cent of each element, were examined for microstructure and hardness after air cooling and after furnace cooling from suitable austenitizing temper- atures. Diagrams summarizing the structnres and hadness resulting from these two cooling rates are presented (Figs. 3, 4, 7).t Data were also obtained on the influence of these two elements, individually and in combination, on the depth of decarburiza-tion observed after furnace cooling (Fig. 8). Composition of Material The chemical composition of the steels investigated is given in Table I. The plain carbon steel was made in a 2 5-ton Heroult electric-are furnace, while the alloy steels were made in a 4.5-ton Ajax-Northrup elec- tric induction furnace. The cast ingots were hot-rolled to 1.75-in. bars. Air-cooled Series The I.75-in. bars were forged to flat plates, 0.25 in. thick, from which specimens 0.5 in. wide by 2 in. long were cut. The specimens were pretreated to improve their homogeneity by heating to 1830°F. (I000°C.) for 20 min. and oil-quenching. They were then reheated to 1740°F. (950°C.) for one hour and air-cooled, after

Jan 1, 1942

By Yingcai Han

The dynamic behavior of pile foundations is investigated in both theory and practice. The computation method for vibration of pile foundations and DYNAN computer program are introduced comprehensively. With a model of non-reflective boundary between the near field and far field, the Novak's method of soil-pile interaction is improved. The dynamic analysis and design of foundation for a reciprocation compressor with driver power 15,000 HP are described to illustrate the computation method of soil-pile interaction. Different design options for the piles are compared to limit the vibration of foundation and produce a safe, economic system. The design with 16 - 0.9 m piles is adopted rather than that with 25-0.5 m piles, since the larger damping is provided by the piles with larger diameter. Both field and laboratory tests were carried out to investigate the soil properties including down hole seismic tests to provide soil shear wave velocities at different depths. The method and procedure used in this study can be applied to the design of pile foundations for tall buildings, bridges and offshore platform with soil-pile interaction under seismic, blast, sea wave and other dynamic loads.

Jan 1, 2002

The Effect of Ionic Strength of Plant Water on Valuable Mineral and Gangue Recovery in a Platinum Bearing Ore from the Merensky Reef

Sep 13, 2010

By J. Mackintosh Bell

External trade strongly influences the well being of all nations. In the modern economic mechanism, no country is so well endowed that it has not to import commodities from others and to export its products in turn to make good its deficiencies, to rectify or improve its financial structure. From the standpoint of international commerce, Canada is strategically well placed. On the south she is bounded by the richest country in the world. On the east she faces the Atlantic, on the west the Pacific. On both coasts there are fine harbours to which lead great lines of railway that span the continent. Canada is now fifth among the exporting nations of the world. For disposal abroad, she has enormous quantities of primary commodities and substantial amounts of manufactured goods as well. But she is far from being self-sustaining. She is unusually dependent on foreign trade, not only because of the commodities she has to sell but because of the lack of many essential articles she does not or cannot produce. To Canada, external commerce is vastly more important than internal trade. The wealth of nations is decided by their ability to produce more than they need, to sell more than they buy, and to build up favourable balances resulting from trade or services. With few countries, however, are returns perennially satisfactory. Fruitful periods are followed by leaner years. In times of prosperity foreign credits are increased, monetary systems strengthened, reserves accumulated to withstand recurring days of strain. Today, the foundations of financial systems are being re-examined, "dogmas hitherto accepted as canonical are being questioned" . It is not only in Europe and America that men search for illumination in problems arising from monetary restrictions.

Jan 1, 1933

By H. X. Yan, J. X. Zhang, F. S. Niu

"The analysis on influencing factors of hydraulic conditions in fine hematite flocculation, such as stirring speed, stirring time and axial distance of particle size and fractal dimension of floc was investigated. Furthermore, response surface methodology(RSM) has been applied according to the Box-Benhnken center-united experimental design principle to optimize parameters of hydraulic conditions as a response index to indicate the fractal dimension of floc. The results show that when the agitation speed is 900r/min, the axial distance is 2.0cm, and the stirring time is 3.0min, the particle size reaches the maximum value of 35.44µm and the fractal dimension is 1.6594. The interaction between the axial distance and the stirring speed is highly significant, but the interaction with the stirring time is not obvious. The experimental data and model predications match well, which indicates that the established model has high accuracy and practicability. INTRODUCTION With the exhaustion of iron ore resources that are easy to be mined and the vigorous demand for iron and steel, the exploitation and utilization of fine-grained embedded iron ore resources have drawn attention from the industry and the government [1~2]. Flocculation flotation is one of the effective methods for separation and recovery of fine granular minerals. In 1975, the method was first applied and succeeded in Tilden Concentrator, USA. Flocculation and desliming became the key technology of the Tilden to raise its annual treatment capacity from 4 million tons to 8 million tons at that time [3 ~ 4]. In 2008, the selective flocculation and desliming-reverse flotation technology was successfully used to treat 2.8 million tons of Qidong iron ore. Under the conditions of 28.36% raw iron grade and 98% grinding fineness -0.038 mm, the ideal index of 62.5% iron concentrate grade and 68% recovery was obtained [5]. Dr Kitchenner of the Royal College of Mining and the Ore Processing Research Group of Wallenstein Laboratory first proposed the use of flocculation to separate minerals. After that, many scholars conducted a great deal of theoretical and practical researches, but mostly they focused on chemical theories, mathematical models and selectivity differences in the flocculation process, while the research on the influence of the pulp flow state on the separation effect in the flocculation process started later [6~9]. The results show that the motion of the agitated flow field has a significant influence on the formation of flocs. The fluid morphology will change with the change of hydraulic conditions. The change of fluid morphology will not only affect the movement behavior of particles, but also change the action of chemical agents on the surface of mineral particles[10~12]."

Jan 1, 2018

By C. A. Heberlein

C. A. HEBERLEIN, New York, N. Y.-The results stated by Rey and Brevers are so startling that they are of great interest, as the concentration of a low percentage of cinnabar by differential flotation yields a high-grade concentrate in the presence of either arsenical or iron pyrite. The authors say: "Cyanide can thus be used to depress arsenopyrite and make a good cinnabar-arsenopyrite separation. A cinnabar-pyrite separation could probably be effected in the same way." Corrosive sublimate at the present price of mercury would be a very expensive reagent but the expense would be justifiable if a high rate of concentration could be obtained with a high extraction. On my request, special tests were made in the Punitaqui mill in Chile along the line suggested by the authors, without any improvement of either grade or extraction. As the recovery of the cinnabar in a complex sulphide of chalcopyrite and pyrite gave unsatisfactory results, I had tests made at the testing laboratory of the American Cyanamid Co. at Stamford, Conn. As these tests turned out to be highly satisfactory, not only at Stamford but later at the mine, they are presented here. [ ] The pulp had a density of 22 and a pH of 7.8. Total time of conditioning was one minute. The reagent added was Texas fuel oil, 0.116lb. of 33.7 Bé. gravity containing 0.9 per cent sulphur. Frother, 0.062 lb. of No. 5 pine oil. Rate of concentration of mercury was 25.7: 11. [ ]

Jan 1, 1941

By Wan Entong, Xie Junlin, Jiann YangHwang, Yang Chengwei, Chen Junfu, Zhang Jianjun, Cao Tongyou, He Feng, Peng Zhugang, Fang De

During the solidification process of peritectic steel (PS), the peritectic reaction often causes volume contraction which associated with surface longitudinal cracks, and using mould flux with low heat flux density help for alleviating surface longitudinal cracks. New peritectic steel mold flux with Co2O3 doping reduced the heat flux density, and the optimal content was found to be 2.0 wt %. Furthermore, basicity and Na2O addition were designed, and the minimum heat flux density required basicity of 1.4 and 10.0 wt %. Na2O content. As a result, the optimal peritectic composition was CaO(35.67wt% ), SiO2(25.48 wt %)，Al2O3(3.7 wt %)， MgO(2.53 wt %)，Na2O(10 wt %)，CaF2(14 wt %)，Co2O3(2 wt %).

Jan 1, 2015

By Glenn E. Johnson

The Bureau of Mines investigated the production of hydrogen cyanide by reacting powdered coal (minus 300 mesh) with ammonia at 1,250° C in a bench-scale study. Both metallic and ceramic reactors were used. Yields up to 0.7 cu ft of hydrogen cyanide per cubic foot of ammonia consumed r- obtained. The resulting ammonia conversion of about 75 volume-percent approximates conversion obtained commercially in processes utilizing natural gas and platinum catalysts. The coals that had higher volatile-matter contents gave the best yields of hydrogen cyanide. Allowing the coal to adsorb ammonia before reaction resulted in increased yields of hydrogen cyanide. Cost studies for a plant with a 40-million-pound-per-year capacity indi-cate that hydrogen cyanide can be profitably coproduced with carbon black, from coal and ammonia, at the current market price of hydrogen cyanide (11.5 cents/lb). These figures are based on heating the reactor electrically. If a cheaper heating method were devised the economics of the process would be more favorable.

Jan 1, 1967

By Khalid Hattar, Alexander McGinnis, Buchheitm Thomas, Paul Kotula, Luke Brewer

"Understanding the effects of extensive radiation damage in structural metals provides necessary insight for predicting the performance of those metals considered for application in the extreme radiation environment. Predicting mechanical performance after long term radiation exposure is of great importance to extending the life of current nuclear reactors and for developing future materials for the next generation of reactors. A combination of finite element modeling, nanoindentation, and TEM characterization were used to rapidly determine the microstructure and mechanical properties influences of ion irradiation on a standard 3 l 6L stainless steel sample. The results of this study found that ion irradiation and small scale mechanical property testing can be used to characterize extensive levels of radiation damage structure, only when significant consideration is given to ion irradiation depth, surface roughness and polishing condition, the irradiation temperature, and many other experimental parameters.IntroductionFor either the success of next generation nuclear reactors or the extension of current nuclear reactors significantly beyond their designed lifetimes, research is needed into the degradation of the microstructure and mechanical properties governing the performance of the reactor alloys exposed to extreme environments. Although the exact dose and temperature of these nuclear reactor plans may vary, the cladding and other structural components will be exposed to greater dose and at elevated temperatures. To acco=odate these severe exposures, established cladding materials are being testing to longer exposure and new alloy compositions are being considered. [1-3] For neutron test facilities to reach 100 dpa level, exposure times often span several years, significantly limiting the down-select process of potential new materials for extreme radiation environments. Ion irradiation has been used as a technique to provide a look at the effect of irradiation damage on materials in a significantly shorter time frame. Previous work using proton irradiation provides a deep, broad, and relatively uniform defect profile compared to heavy ion irradiation; however, using this type of radiation still requires weeks to months to reach the 100 dpa level. [4] In this research, we investigated the feasibility of using heavy ion (nickel) irradiation and small scale mechanical testing to provide in a few days a first order screening technique for potential alloys that are being considered for advanced testing."

Jan 1, 2012