Search Documents

By Karl J. Dreher, Charles C. Hennig, Gregg A. Scott

INTRODUCTION Theodore Roosevelt Dam is a cyclopean-masonry, gravity-arch dam located on the Salt River northeast of Phoenix, Arizona. Construction of the dam began in 1903 and was completed in 1911. The dam is about 85 m high with a total reservoir capacity of about 1.7x109 m3. Raising the dam is now being considered to provide additional water storage and flood control. This paper describes preliminary analyses performed to assess foundation stability for increased loading resulting from raising the dam and reservoir water surface about 12 m. The foundation of Theodore Roosevelt Dam consists of variably metamorphosed limes tones, sands tones, mudstones, and shales. Bedding uniformly strikes nearly normal to the river (N 40º W) and dips upstream at 25 to 30º. The rock is cut by four prominent joint sets as indicated by the joint contour diagram shown in figure 1A. The diagram was developed from surf ace observations and vertical drill core oriented relative to the bedding. Sampling biases account for the differences in concentrations of various joint sets. However, field observations indicate that all sets are relatively prominent, planar, and continuous. SEEPAGE ANALYSES Consistent with practice at the time of construction, no foundation drainage was installed at Theodore Roosevelt Dam. Finite element seepage analyses were therefore performed to study the potential for large uplift pressures in the foundation. The dam has steep abutments and is curved in plan as shown in figure 1B. The effects of modeling the seepage two-dimensionally, radially symmetric about the dam's axis center, and three-dimensionally were therefore com-

Jan 1, 1982

By R. D. Carnahan, J. E. White

A study of dispersion strengthening in TD-Nickel (nickel plus 2 vol pct Tho2) was conducted employing microstrain techniques at ambient room temperature. It was found that optimum strength was due primarily to the incorporation of stored energy developed by a variety of thermal-mechanical treatments. The relatively low strength of the recrys-tallized condition implies that the dispersed particles themselves offer only token resistance to deformation. The development of resistance to large-scale recovery or recrystallization at temperatures near the melting point requires a more extensive sequence of strain-anneal cycles than does the development of optimum strength. A micro-Bauschinger effect was observed which appears to be related to the lattice resistance to the movement of free dislocations. The effect was nearly identical to that in pure nickel indicating that the presence of the dispersed phase and considerably increased dislocation density (stored energy) only alters the number or effectiveness of barriers. THE early stages of deformation of engineering materials can be conveniently studied by utilizing strain-gage techniques which permit resolution of strains less than 5 X 10-7 in. per in. for testing in four-point bending (Carnahan and white1). The present investigation, part of a continuing study on the very early stages of deformation, was designed to reveal the true role of a dispersed phase in promoting high strength in a commercially available dispersion-strengthened alloy. Although this technique has been used for some time to study microdeformation in pure metals and alloys, it has just recently received attention as a means of investigating dispersion strengthening. Studying the very early stages of deformation in alloys which depend upon a finely dispersed inert phase for strength may prove to be a very important method for a better understanding of these materials. It is essential to obtain considerable clarification of actual dislocation movement and the kinds of deformation barriers which exist before optimum properties can be designed into this type of material with any degree of confidence. Considerable research on a variety of dispersion-strengthened materials has resulted in two different schools of thought regarding the strengthening mechanism. One faction2-4 favors the idea that the particles themselves resist the motion of dislocations. The criterion for yielding is the fracture of the dispersed second-phase particles due to an array of piled-up dislocations. Other invesfigators5-a have shown that particles are effective primarily by allowing a greater buildup of stored energy or dislocation density through thermal-mechanical treatments in the composite than the pure matrix material. The particles themselves, then, are not exclusive obstacles, but the complex network of particles, dislocation tangles, subboundaries, and grain boundaries are strength determining. The development of such a complex dislocation network in SAP has been studied recently in some detail by Goodrich and Ansell. The ability of dispersion-strengthened alloys to resist softening or recrystallization is also of considerable importance; however, the criteria for maximum stability may not necessarily be those for maximum strength. In this study, in addition to the evaluation of the microstrain properties of TD-Nickel, it is felt that considerable clarification of the true dependence of strength and stability on the dispersed phase is shown. I) MATERIAL AND PROCEDURE TD-Nickel is a dispersion-strengthened alloy developed by the E. I. DuPont de Nemours Co., which contains 2 vol pct thoria (Tho2) in a pure-nickel matrix. The average ThO2 particle size is approximately 0.1 p and the interparticle spacing is less than 1 u. The material was supplied by DuPont in two conditions: hot-extruded bar stock, and stress-relieved cold-rolled sheet 0.025 in. in thickness. The bar was extruded at 2200°F from a cold-pressed and sintered billet. The sheet stock was prepared from the extruded material by a process involving ten or more 50-pct cold reductions by rolling with intermediate anneals at 1800° to 2000°F. Test specimens used in this study were prepared in the form of rectangular parallelepipeds measuring 0.375 by 1.375 in. in thicknesses ranging from 0.025 to 0.040 in. Samples prepared from sheet and extruded stock were mechanically polished before heat treatment and were handled with extreme

Jan 1, 1964

Geological and Natural History Survey of Wisconsin, The University of Wisconsin, Madison, Wis - E. F Bean, State Geologist. A complete list of publications of this Survey will be sent upon request Only a portion of the Bulletins and Maps fall within the scope of this directory, and most of them are available They are: Bulletin 4, Building and ornamental stones of Wisconsin (1898), $2 50, 6, Preliminary report on the copper-bearing rocks of Douglas County, and parts of Washburn and Bayfield counties (1901), 50 cents, 7, The clays and clay industries of Wisconsin (pt 1) (1901), 50 cents; 14, Report on lead and zinc deposits of Wisconsin (the report is out of print but the 18 maps which accompanied it can still be had) (1906), 20 cents (a series of six maps, supplementary to these (1909), may be had for 6 cents), 15, The clays of Wisconsin and their uses (1906), 50 cents; 16, The geology of north-central Wisconsin (1907), $2, 17, The abandoned shore lines of eastern Wisconsin (1907), 50 cents, 19, Zinc and lead deposits of the Upper Mississippi Valley (1907), 25 cents; 34, The limestone road materials of Wisconsin (1914), 50 cents, 35, Underground and surface water supplies of Wisconsin (1915), $150, 36, The physiography of Wisconsin (new edition now in press) (1916), $125, 41, A study of methods of mine assessments and valuation (1914), 50 cents; 44, Mineral land classification in parts of northwestern Wisconsin (1915), $5, 45, The peat resources of Wisconsin (1915), 50 cents, 46, Mineral

Jan 1, 1933

By E. H. Edwards, J. Washburn, E. R. Parker

The mechanism of strain hardening was discussed in connection with some recent observations on the stress-induced motion of dislocation boundaries and on the simple shear deformation of zinc, cadmium, and copper crystals. THE nature of work hardening accompanying plastic deformation of metals has long been the subject of speculation. As early as 1925, Becker' suggested a thermodynamic process to explain slip based on the statistical probability for the occurrence of local glide steps. The theory that plastic glide was due to the presence of lattice defects known as dislocations was first introduced in 1934 by Taylor: and Orowan, and Polanyi.4 Taylor presented a rather complete analysis of the behavior and interaction of dislocations. He assumed a certain type of stress field to be associated with a single dislocation, and postulated that work hardening would result from plastic flow in two ways. First, dislocations following one another across a slip plane might encounter a barrier which would impede their movement, thereby gradually diminishing and eventually stopping plastic flow on that plane. The second mechanism involved the concept of dislocations traveling in opposite directions on nearby planes attracting one another to form a meta-stable lattice. The interaction of dislocations in such an array was shown to be large enough to require an increase in stress before plastic flow would continue. Kochendorfer5,6 extended the concept of work hardening involving a back stress due to an accumulation of like dislocations on a slip plane. He suggested that the formation of a new dislocation is hindered by those dislocations already present. The hardening resulting from the interaction of newly forming dislocations with bound dislocations was designated as "formative hardening," and indicated to be the only type of hardening necessarily connected with the slip process. In another detailed picture of work hardening, Mott and Nabarro7 assumed that sufficient dislocations are primarily present in the crystal as a consequence of growth irregularities (mosaic structure) to initiate slip. Work hardening resulted from the interaction of migrating dislocations with localized internal stresses produced during deformation. More recently, however, Mott8 as modified his treatment to include the generation of dislocations at Frank-Read sources and he accounts for the hardening by the formation of sessile dislocations. It has been widely accepted that metals of hexagonal structure, usually possessing only one set of glide planes, exhibit mechanical behavior markedly different from those having cubic structures. However, the differences in behavior of the two classes may be less fundamental than suggested. Rohm and Kochendorfer9 have shown that a single crystal of aluminum subjected to approximately simple shear gives the type of stress-strain curve associated with the hexagonal metals. Similar behavior has been demonstrated for gold and silver crystals by Andrade and Henderson.'" Thus when glide in cubic metals is restricted to one plane, the strain hardening characteristics closely resemble those of the hexagonal metals. It would appear, therefore, that an investigation of some of the strain hardening properties of single crystals sheared in simple glide might provide a more complete understanding of the phenomenon of work hardening. This report relates a number of recent observations made on single crystals of copper, zinc, and cadmium tested in simple shear. In addition, pertinent observations of effects accompanying stress-induced movement of dislocation boundaries are reported. Experimental Procedure and Results Details of the production and advantages of the type of single-crystal shear specimen employed for the following tests have been presented in a previous publication.n The method of testing makes

Jan 1, 1954

By C. F. Jr. Tolman

IN February 1913, Prof. L. C. Graton and Dr. Joseph Murdoch1 presented to the American Institute of Mining Engineers a notable contribution to economic geology under the title The Sulphide Ores of Copper. The value of the work was recognized by mine operators, and Mr. Graton was assisted in his plan to extend his investigations,. by the organization of a commission to undertake a "secondary enrichment investigation." In this work lie secured the cooperation of the Geophysical Laboratory of the Carnegie Institution of Washington. Their report 2 on the chemical phases of the investigation has just been published. Incidental to investigations 3 carried on in my laboratory by advanced

Jan 2, 1916

By J. J. Beeson

The second part of the paper includes a detailed account of the processes of secondary-enrichment which have been effective in producing the disseminated ores. While both parts present new features, it is hoped that the discussion on secondary chalcopyrite and bornite may be of interest to those who are engaged in the study of secondary processes in other districts. The excellent work' Economic Geology of the Bingham Mining District, by J. M. Boutwell, was published in 1905. Since that time the extensive development work-surface cuts and underground drifting-of the Utah Copper Co. has made possible the collecting of samples for more detailed microscopic study. The writer has taken advantage of this fact and presents the following work, not as a criticism, but as a' continuation of the work which was begun by Mr. Boutwell. b. Acknowledgments.-The present study was undertaken at the suggestion of Dr. A. F. Rogers; to him, and to Prof. C. F. Tolman and Prof. S. W. Young, the writer wishes to express his thanks for criticism in the preparation of this paper. The writer also expresses his thanks to D. C. Jackling, Vice-President and Managing Director of the Utah Copper Co., for permission to publish this paper, and to William Spencer, D. W. Wadleigh, T. S. Carnahan, J. A. Caulfield, Percy Dayer, and Edward Norsefall, for the courtesies extended to him while a co-worker in the mines.

Jan 11, 1915

By F. H. Wilson, E. W. Palmer

G. L. Bailey (British Non-Ferrous Metals Research Association, London, England)—I was glad to see this further work on the structure and properties of the Cu-Ni-Fe alloys of low nickel content in which we have been so interested in the United Kingdom since before the war." The authors' data on the variation in solubility of iron in both 5 and 10 pct Ni alloys with temperature is based on more detailed observations than we have made but is generally in line with our own work. The difficulty in these matters is in the identification of the structures obtained. The precipitation of the second phase which we presume to be the a' solid solution, richer in nickel and iron, from the a solution with which it is in equilibrium occurs in such a fine state of division that its resolution by ordinary micro-graphic methods is impossible in the early stages. We have published some electron micrographs which illustrate the effects observed more clearly but we agree with the authors when they say that dark staining characteristics when the alloys are subjected to sea-water corrosion are more sensitive in detecting the presence of the a' phase than is the microscope. After taking this point into consideration, however, I confess to some difficulty in understanding Fig. 4. I can only assume that the precipitates visible at such a low magnification as 150 diam in these relatively coarse forms are produced from iron-rich areas of the initial solid solution due to inadequate homogenization. If this is so I find it difficult to accept the authors' contention that such local variations in iron concentration as are capable of giving the heavy precipitates shown in Fig. 4 do not in fact materially affect the solvus surfaces of their equilibrium diagrams. I share the authors' enthusiasm about the resistance to corrosion of these alloys by seawater but I am not fully in agreement with them on the vexing question of the best iron content for these alloys. In Fig. 3 of ref. 8, we give many results showing that the resistance of these alloys to impingement attack in the Jet Test increases as the iron content rises to 2 pct. With higher iron contents pitting at shielded areas is likely to occur. Admittedly the addition of 0.75 pct Fe produces a large improvement in corrosion resistance compared with a pure 90/10 Cu-Ni alloy, but the further improvement on raising the iron to 2 pct is substantial. We recommend from 1.5 to 2 pct Fe as the desirable range from the point of view of corrosion resistance. While it is true that British practice generally uses a hard tube, the corrosion resistance of the 10 pct Ni alloys has in our work been little affected by the structural condition. Although the annealed alloys blacken in seawater, this effect seems to be superficial and not to be accompanied by any real decrease in

Jan 1, 1953

By R. E. Collom

VARIOUS chapters already written in the history of development of the North Dome of Kettleman Hills are monotonously identical in the one underlying theme of conservation of oil and gas. Discovered on Oct. 4, 1928, by Milham Exploration Co. with its wildcat Elliot No. 1, the field has been subjected to practically every modern form of produc-tion restraint in the name of conservation. The record thus far developed shows that conservation was had for a time, at a price; and that unitiza-tion must he blessed by single ownership or 100 per cent participation to be effective. In fact, incomplete unitization places a heavy handicap upon its participants in the competitive development that follows.

Jan 1, 1937

By H. M. St. John

MAINTAINING a satisfactory structure in brass and bronze castings has always been a foundry problem of great practical importance. While metallurgists and scientific investigators have not entirely ignored this matter, it has received less of their attention than has been given to iron, steel and the wrought copper and aluminum alloys. Investigation in this field has probably been discouraged to some extent by the complicated nature of the alloys involved. Hundreds of alloys are in more or less common use, most of them containing copper, zinc, lead and tin in-widely varying proportions. They also contain appreciable percentages of iron and antimony as impurities, and often phosphorus, which has been added as a deoxidizer and fluidifier. Small amounts of sulfur are usually present. It is not uncommon to find nickel, sometimes in rather substantial quantities. Traces of other metals are frequently present. So complicated and variable a mixture obviously offers difficulties in. any investigation of the various factors that influence the structure and other properties of the casting.

Jan 1, 1930

By John S. Johnson, Thomas Fraser

SIZING is the process of separating mixed particles into groups of particles all of the same size, or into groups in which all particles L range between certain definite maximum and minimum sizes. In coal preparation, sizing is generally accomplished by passing the coal over screens. Separation by differential settling in air or water currents has been adapted to the special field of separating very fine sizes, and these processes are in commercial use to a relatively small extent in the coal industry. Separation with screens is a very old industrial practice. Agricola 1 described the use of screens for ore treatment in the middle ages. In the literature of the British coal industry references were made to the screening of coal as early as 1589, but the practice of extensive sizing for the market did not become general until the last half of the nineteenth century. In America, the practice of sizing developed first in the Pennsylvania anthracite region, beginning with the use of rakes2 in the mine working places to recover coarse coal. This mining procedure left the fines in the mine. Preparation outside the mine started with the installation of stationary cast-iron plates with 4 to 6-in. square holes. The run-of-mine coal was dumped upon the platforms, the large pieces of rock were picked out by hand, and the large lumps of coal were broken with hammers. The term "breaker," which still applies to the anthracite-preparation plant, originated with this practice, but the term is no longer descriptive of the entire function of the plant. In 1884, the first power-operated anthracite coal breaker3 was erected by Gideon Bart at his colliery at Wolf Creek near Minersville, Pa. This plant utilized a system of rolls for breaking the coal and revolving screens for sizing. The plant was driven by a steam engine. It could handle

Jan 1, 1943

By Erwin S. Sperry

The presence of small amounts of tellurium in certain binds of copper, and its exceptionally deleterious* influence in producing red-shortness of this metal, led the author to conduct a few experiments on the influence of tellurium on the properties of brass. While these experiments were not intended to be exhaustive, they demonstrate that, as far as the rolling of brass is concerned, tellurium, unless it occurs in far greater amounts than exist in refined copper, cannot be called an injurious impurity. In comparatively large amounts it appears to impart cold-shortness to high-brass. Tellurium, the rare element that it is considered to be, has recently been extracted on a large scale from the slimes of an American electrolytic copper-works. They have, in attempts to discover some commercial use for it, sent it out promiscuously and gratuitously in quantities which would lead the young chemical student to fancy that a rare element exists only in name. Through the courtesy of Mr. R. L. Whitehead, of Baltimore, the author was able to obtain somewhat over 2 lbs.,? and use it in quantities which, at the market price, would be prohibitive. In order to add specific quantities of tellurium to brass, a rich alloy of copper and tellurium was previously made. The method was as follows, viz.: Nine and one-half lbs. of Lake copper were melted un-. der charcoal in a new plumbago crucible, and then pound of tellurium was added in small portions at a time. The mixture was stirred with a plumbago-stirrer and poured into

Jan 1, 1903

By Royal Jackman

Two comprehensive papers have appeared regarding the forms of copper that occur in smelter slags, one by Frank E. Lathe1 and the other by C. G. Maier and G. D. Van Arsdale.2 These authors comment on other published results and draw conclusions from their own investiga-tions. The development of X-ray examination of minerals and improve-ment in high-power microscopic methods make it possible today to get additional evidence by means that were not available to earlier investi-gators. The present work was confined to reverberatory slags obtained from five different plants. Some definite conclusions were reached regarding the forms of copper present in these slags. In most cases these agree with some of the findings of Maier and Van Arsdale but new methods of attack were used in the investigation.

Jan 1, 1933

By F. N. Rhines, A. H. Grobe

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By M. L. Holzworth, Philip R. Sperry, Paul A. Beck

INTRODUCTION THE basic work of Z. Jeffries1,2,3 has long ago established the main features of grain growth in the presence of a dispersed second phase. Working with sintered specimens of initially fine grained tungsten, to which various amounts of thoria have been added, Jeffries found that grain growth was inhabited, that is, practically prevented, up to a certain annealing temperature. When this temperature, which increased with the thoria content, was exceeded, extremely large grains developed abruptly from the fine grained matrix. Such a "coarsening temperature" was later found by Gross mann13,14 in certain types of steel, while Bain showed" that in other steels grain growth was gradual, without inhibition and abrupt coarsening. Later work16,17,18,19,21 demonstrated the connection between coarsening and aluminum additions. The viewpoint that the direct cause of inhibition and coarsening in aluminum killed steels is a fine dispersion of aluminum oxide21 appears to be held quite generally, although some doubts have been voiced even very recently.20 In steels with Ti additions the titanium carbide phase is considered responsible for the inhibition effects found.20 The coarsening temperature increases, with the titanium content. That coarsening may occur, as a result of certain heat treatments, even in low carbon rimmed sheet steel, was shown by Samuels,22 He also detected coarsening in a steel ingot of similar composition, after giving it the same heat treatment as that used by him for the sheet material, In this instance the identity of the inhibiting phase has not been determined, However, Tangerding found 23 that even the few small carbide particles, which occur in carbonyl iron, have a very marked inhibitive effect. As a result of an oxidizing anneal at 850°C, large grains begin to form at the surface of the carbonyl iron specimen, and gradually grow inward as the subsurface oxidation of the carbide particles progresses and eliminates the obstruction, The carbide particles can be removed also by annealing in hydrogen, with similar results. But if the oxidizing anneal of 10 hr at 850°C in air, is followed by annealing in hydrogen for 75 hr at the same temperature, grain growth is more spectacular; usually the whole specimen is transformed into a single crystal (approx. 1,5 cm X 5 cm). The reversed procedure, that is, hydrogen annealing followed by oxidizing annealing leads to smaller grains. Tangerding arrived at the logical conclusion that there must have been in his specimens some additional obstruction to grain growth resulting from a minor impurity, other than carbon. It seems likely that this obstruction was caused by an oxide formed during the oxidizing anneal and gradually reduced during the subsequent hydrogen-annealing. Other instances of grain growth inhibition of varying severity, associated with a dispersed second phase, have been described by several authors. Notable examples: lead with 0.06 pct Cu or Ni,24 cartridge brass with 0.12 pct Cr,25 or with up to 0.15

Jan 1, 1948

By J. M. Hassler

NOWHERE can there be found a more misleading statement than the old one that "Iron can be manufactured cheaper in the South." During the past decade ironmakers and users of iron have heard varied and sundry stories of the wonderful resources of the Birmingham district, including abundant ore and coal fields, cheap labor, a wonderful climate and similar industrial Utopian statements. Birmingham represents the major portion of the iron business in the South, acid as Birmingham fares so goes the iron business of the South. The intent of this paper is to shed some light on the actual conditions surrounding ironmaking in the South, especially in the Birmingham, or North Alabama, district. By a presentation of facts it is desired to point out that the "cheap iron" of the industrial South is a thing of the past, primarily because of increased labor cost and because labor is radically different in performance to what it was years ago. Also, because most of the raw materials needed in ironmaking that would be classed better than inferior are gone.

Jan 1, 1937

By D. J. Jr. McAdam

RESULTS of investigation of corrosion-fatigue of metals at the U. S. Naval Engineering Experiment Station have been presented by the author in four papers. 1,2,3,4 In those papers references were given to the work of Haigh in 1917.5 The investigation at Annapolis included a variety of ferrous and non-ferrous alloys. The experiments showed that even slight corrosion simultaneous with fatigue may cause failure at stresses far below the ordinary endurance limit. The experiments also showed that, for most metals, severe stressless corrosion prior to fatigue is much less damaging than even slight corrosion simultaneous with fatigue. The term "corrosion-fatigue" was restricted to mean the simultaneous action of corrosion and fatigue. The combined effect of corrosion followed by fatigue was called "prior-corrosion fatigue." A stress-cycle graph representing corrosion-fatigue is a curve approaching a horizontal asymptote, the ordinate of which may be called a "corrosion-fatigue limit." To avoid confusion in later discussion, the term "endurance limit" will be restricted to mean the fatigue limit obtained by tests in air with specimens as free as possible from stress concentration and from corrosion. The endurance limit as thus obtained presumably represents an inherent property of the metal.

Jan 1, 1929

By Milton H. Fies

Although pig iron from iron ore and red cedar charcoal preceded the mining of coal by many years, for tradition says that Alabama iron was used to shoe the horses of Andrew Jackson's soldiers, coal was not produced until 1830. In that year, coal was mined in Tuscaloosa County, in the vicinity of what is now the University of Alabama, and shipped on flat boats (obviously during the wet season, for there were many shoals) down the Warrior River to Mobile. About that time, the first railroad, the Decatur & Tecumseh, was being constructed in northern Alabama to overcome the obstructions to freight traffic caused by the now well-known Muscle Shoals in the Tennessee River. This railroad was patterned after a railroad at Mauch Chunk, Pa., which was used for hauling anthracite from the Panther Creek valley. The Alabama railroad, which required about four years to complete, was 46 miles long and was used solely for the transportation of cotton. Although it was a failure, it demonstrated the practicability of the undertaking, and the succeeding railroads, which were begun in 1834, 1848, 1852, and 1853, added immeasurably to the development of the coal resources of the state. Between the years 1830 and 1860, practically all the coal mined in the state was dug from the outcrop near the river or from the river beds, and shipped by boat to Mobile. Transporting coal down the Warrior River was an undertaking of great risk, required much skill, and frequently had heavy losses. It is recorded that this coal was sold to the gas company in Mobile in 1844; it was most likely mined from the Black Creek Seam. In 1914, on the completion of Lock 17, the Warrior River became a navigable stream from 9 miles above Cordova, Ala., to Mobile and offers a great opportunity for the future development of the coal resources of the state. Coke for foundry use was first made in Alabama in 1855. It was 21 years later, however, in 1876, that pig iron was made from Alabama ore with Alabama coal.

Jan 1, 1925

By George M. Fowler

THE Tri-State district, as outlined in this paper, refers to the entire mineralized area in southwestern Missouri, southeastern Kansas and northeastern Oklahoma (Fig. 1). The part of the district in Missouri and near Galena, Kans., is still sometimes referred to as the Joplin district (Fig. 2). The Picher-Miami area is that part of the Tri-State district located contiguously in Kansas and Oklahoma in the vicinity of Baxter Springs, Picher and Miami. This paper is confined almost wholly to the ore deposits of the Tri-State district and particularly to the Picher-Miami area. Our study of the ore deposits of this district dates from late in 1925 (by Fowler) and early in 1927 (by Lyden) to the present. Our work has been confined almost entirely to the search for ore for numerous companies and individuals. It was not possible for us to undertake numerous highly interesting investigations which presented themselves but which would not immediately help in finding ore. We particularly refer to the general structural geology of the Ozark uplift, the genesis of the ore, and other problems of a similar nature. The local and general structural problems of the district are being solved gradually as the work progresses. The factors that control the loci of the several orebodies are evident. This paper is based almost exclusively upon our own observations. Most of the important mines in the Picher-Miami area were studied in detail. A map (Fig. 5) is included which shows this area and the properties we have examined to date. When it was convenient we visited, studied and compared structural relations in numerous mines in states outside the district. Some of these observations are noted in this paper.

Jan 1, 1932

By D. C. Shelton

Eq. 4 and 5 on page 5 of the March 1965 issue of Transactions, and Eq. 12 on page 8 of the same issue should read respectively:

Jan 1, 1965