By E. O. Lilge, H. Siebert

A design of a multiple-bomb leaching unit particularly suited for the study of heterogeneous reactions, i.e. sol id-liquid-gas interfaces at high temperatures and pressures is presented. The component parts and overall design are described and illustrated in detail. The system has been tested by a limited number of experiments and found to work satisfactorily. Heterogeneous reactions at solid-liquid-gas interfaces, at high temperatures and pressures, are studied in either autoclaves1'4 or bombs5'9. Autoclaves are usually fairly large vessels which have a stirring arrangement incorporated in the design. Mechanical design limits the use of these vessels to relatively low temperatures and pressures. They are particularly well suited to rate or kinetic studies. Bombs can be designed to be operated at high temperatures and pressures, and are smaller vessels; because of this, stirring arrangements are not easily incorporated. In this paper a multiple-bomb system is described, that has been designed to incorporate the desirable features of both the autoclave and the bomb. The described unit has flexibility for an over all study of leaching. Most of the component units in this assemblage are standard equipment, designed and produced by well known manufacturers. No claim is made to the design of this equipment, and although described in some detail, this is done merely for clarity in the elucidation of the system presented. The general layout of the multiple-bomb assemblage is shown in Fig. 1A and 1B. The basic units in this system are: 1) 6 stainless steel 100 ml bombs (Fig. 4)

Jan 1, 1964

By O. N. Carlson, A. L. Eustice

The tensile properties of iodide vanadium were determined as a function of hydrogen concentration. It was shown that the presence of 10 ppm H is sufficient to cause embrittlement of vanadzum over a limited temperature range. The temperature of the observed ductility mininlum is approximately -l00°C, this being a function of strain rate and hydrogen concentration. The yield stress of hydrogenated vanadium is raised sharply in the brittle temperature range. THE present investigation was initiated to determine the effect of hydrogen on the tensile properties of high-purity vanadium as a function of temperature and the role of hydrogen in the brittle-ductile transition. Loomis and Carlson&apos; reported a change from ductile to brittle behavior in iodide vanadium at -110°C with a return of ductility at temperatures below -140°C. Vanadium wire containing 270 pprn of hydrogen was brittle at room temperature while wire containing 100 ppm was ductile under the same conditions. Roberts and Rogers&apos; reported a ductile-brittle-ductile fracture sequence in vanadium containing 400 to 600 ppm of hydrogen. Their data show that hydrogenated vanadium is ductile at 150"C, brittle at room temperature and ductile again at -196°C. Magnusson and Baldwin found a minimum in ductility in vanadium containing 80 ppm hydrogen from tensile tests performed at several strain rates. Information available on the vanadium-hydrogen equilibrium system4 is somewhat incomplete. The absorption of hydrogen is exothermic in accordance with the decline in solubility with rising temperature. The limit of solid solubility at temperatures below 400°C has not been determined due to the difficulties in obtaining equilibrium at these temperatures. Data on the hydrides of vanadium are rather limited. Roberts6 studied the structure of VD,., by neutron diffraction, and observed the ordering of the deuterium atoms below -65°C into a primitive cubic cell with a lattice constant about twice that of the disordered bcc vanadium solid solution. EXPERIMENTAL PROCEDURE Vanadium of 99.9 pct purity was prepared by the iodide refining process6 for use in this investigation. This vanadium contained the following analyzed impurities; <20 pprn calcium, 150 ppm carbon, 200 ppm chromium, 30 ppm copper, 10 ppm hydrogen, 200 ppm iron, <20 ppm magnesium, <20 ppm nickel, <5 ppm nitrogen, 150 ppm oxygen, <50 ppm silicon, and <20 ppm titanium. specimen Preparation—Tensile specimens were machined from swaged rods of iodide vanadium. The

Jan 1, 1962

By John B. Mertie

More than 200 minerals are known that contain the rare-earths and thorium. Monazite and bastnaesite, however, are the principal commercial sources of the rare-earths, and monazite is the principal source of thorium. Monazite was in demand in earlier years mainly for its content of thorium, which was used in the manufacture of Welsbach gas mantles; but beginning in the latter part of the nineteenth century, the rare-earths became progressively more important than thorium. Recently, however, the tenor of thorium in monazite has again become a matter of commercial interest. Rare-Earths and Thorium The rare-earths proper are defined by spectroscopists as the oxides of 14 elements with atomic numbers ranging from 58 to 71; but more commonly lanthanum, with an atomic number of 57, is also included, in which case these 15 elements are often designated as the lanthanides. Chemists also include scandium and yttrium as elements of the rare-earths. A second group of elements, beginning with actinium and including thorium, protactinium, uranium, and all the transuranium elements so far produced, with atomic numbers ranging from 89 upward, are chemically and structurally related to the lanthanides, and are known as the higher rare-earths or actinides. Berzelius discovered that the lanthanides could be separated roughly into three groups, based upon the solubility of their double salts, R2(SO4)3-K2SO4-2H2O, in excess of K2SO4. This separation, with the substitution of sodium for potassium, is still used commercially. The double salts of the cerium earths were found to be almost insoluble; the terbium earths, partly soluble; and the yttrium earths, completely soluble. Based upon the degree of solubility, scandium belongs with the cerium earths; and yttrium belongs with, and gives its name to, the yttrium earths. These three groups with their atomic numbers are shown below. [ ] The prevailing state of oxidation for the rare-earths is R2O3, but cerium may readily be oxidized to the tetravalent state, in which condition it may be separated chemically from the other cerium earths. Praseodymium and terbium may also exist with the valence IV, and samarium, europium, and ytterbium may have the valence II. Most of the elements of the rare-earths, however, are very difficult to separate, and their initial isolation required the work of many chemists over a period of 150 years.20 Fractional crystallization, fractional precipitation, and ion exchange are the principal methods so far used, and fractional precipitation is now employed commercially on a large scale. Ion exchange columns are

Jan 1, 1960

By Donald Barton

THE theory of gravitation is based on Newton&apos;s law that any two bodies exert a mutual attraction which is proportional to the product of their masses and inversely proportional to the square of the distance between them; i. e., A =KRM/R2 (1) where K is a constant, M and m are the respective masses of the two bodies, and R the distance between them. In the earth&apos;s gravitational system, the earth is one of the bodies; the other may be any body within or without the earth. In theoretical dis¬cussions and calculations in regard to gravity, that other body usually is taken as a unit of mass: in the C. G. S. system, a body of one gram in mass. GRAVITY AND LEVEL SURFACES Gravity is defined in geophysics as the force of attraction exerted by the earth, towards itself, on a body of unit mass. The intensity of gravity is usually expressed in dynes of force or in centimeters of acceleration. In geophysical work in America, most commonly it is expressed in dynes (per gram) with the "per gram" understood and not directly expressed. In geophysical work in Europe, most commonly it is expressed in centimeters per second per second (cm./sec.2) and less commonly merely as centimeter-gram-second units (C. G. S.). At sea level, the intensity of gravity amounts very nearly to 980 dynes. The vertical is the direction along which the attraction of gravity is exerted at any point. . In most cases, it is very nearly, but not quite, per¬pendicular to the earth&apos;s surface. The path that would be taken by a body falling freely through space toward the earth is vertical at each point and may be spoken of also as "the vertical," or as the line of the vertical, or as a line of force of gravity. At the earth&apos;s surface it com¬monly is very nearly, but not quite, a straight line.

Jan 1, 1928

The Telfer Project, one of the world&apos;s newest gold mines, is located about 300 km (190 miles) northeast of the Mt. Newman iron ore project in the northern part of Western Australia. The first mineral claims were staked in 1972; and by mid-1975 ore reserves of 3. 8 million mt (4. 19 million st) of 9.6 g per mt (0. 28 oz per st) ore had been indicated. It is interesting to note that Newmont spent more than 10 years and A$10 million in Australia for extensive mineral exploration before finding the Telfer deposit, and then spent approximately A$3 million in exploration and feasibility engineering on Telfer. Including this A$3 million, a total of A$27 million was spent to complete construction of the mine, village, gold treatment plant and associated roads, airport, water and services. Over 50% of the capital cost is in the metallurgical facility, or approximately A$10, 000 per ton per day. All economically significant gold mineralization at Telfer occurs in a series of layered quartz-limonite reefs in which the former pyrite has been oxidized to limonite to a depth of 100 m (330 ft). The most important gold reef occurs at the base of the siltstone-shale horizon within the enclosing sandstone dome -like structure. At the Main Dome structure the dipping ore horizons will be mined to a vertical depth of about 60 m (200 ft) by open-cut methods. The waste-to-ore ratio is approximately 12:1. Eventually 44 million mt (48. 5 million st) of ore and waste will be mined. Mining of the waste is by contract; however, the ore and a thin layer of waste is company-mined. Dilution from mining the geological ore reserve is about 10%. The ore is completely oxidized and the gold occurs free within the reef, material as discrete particles of varying but mainly fine grain size. Most of the gold is "free milling"; that is, over 50% of the gold is coarse enough to be recoverable by gravity concentration. Two duplex mineral jigs receive the two cyclone underflows from the grinding circuit. The rougher jig concentrate is up-graded on a continuous strake from which the concentrate is tabled to produce a final free gold product. Jig tailings are returned to the ball mill and the concentrates are amalgamated. Gold amalgam is pressed, retorted, and melted into gold bars. The gravity gold recovery circuit is the same as was used in many of the gold mills in California in the 1930s.

Jan 1, 1981

By H. I. Aaronson

ONLY limited studies have been made of pro-eutectoid a morphology in hypoeutectoid Ti-Cr alloys during previous investigations, 1-3 The nature of the eutectoid reaction, ß?a + TiCr2, has been considered in somewhat more detail.1,2,4,4 Inasmuch as the proeutectoid ferrite reaction in plain carbon steels has recently been extensively investigated in this laboratory, advantage has been taken of the opportunity to compare the morphologies developed in two rather different eutectoid systems in order to permit a preliminary estimate to be made of the degree of generality which may be ascribed to the various results obtained. Experimental Procedure The chemical analyses of the alloys used are given in Table I. The 7.22 pct Cr alloy was prepared by the Battelle Memorial Institute from iodide titanium and high purity chromium. The initial ingot was made by arc melting a master alloy and iodide titanium. The resultant ingot was twice remelted. by the consumable electrode technique. Upset forging at 950°C reduced the final ingot to 3/4 in. sq bars. The 10.94 pct Cr alloy was prepared by the Titanium Metals Corp. of America from sponge titanium and chromium of ordinary purity. This alloy was melted twice by the consumable electrode technique, forged at 1200° to a 3/4 in. sq bar, and rolled at 815°C to a 1/2 in. round. Specimens 1/4 in. x 1/4 in. x 1/16 in. were cut from the 7.22 pct Cr alloy; halves of disks 1/2 in. in dlam and 1/16 in. thick served as specimens of the 10.94 pct Cr alloy. These specimens were individually encapsulated in Vycor, Each capsule was evacuated three times to a pressure of 2 to 6 x lo-&apos; mm Hg and flushed twice with a reduced pressure of argon prior to sealing. The inclusion of two small packets of zirconium chips permitted the capsules to be outgassed and internally gettered, without heating the specimen, prior to heat treatment. The specimens were solution annealed for 40 min at 1000°C, isothermally reacted in deoxidized lead pots, and quenched in iced water. Most of the isothermal reaction treatments were carried out at 25" intervals between 725° and 550°C on specimens of the 7.22 pct Cr alloy and at 650°C on specimens of the 10.94 pct Cr alloy. Results and Discussion Morphologies of Proeutectoid a*—Kinetics of the ß?a Reaction: Fig. 1 shows the TTT-curves for the beginning of the proeutectoid a and the eutectoid reactions in the temperature range investigated in the 7.22 pct Cr alloy. The M, temperature in this alloy is below 0°C. The curve for the beginning of the proeutectoid a reaction is in good agreement with that of Frost, Parris, Hirsch, Doig, and Schwartz&apos; for a 7.54 pct Cr alloy, appears at considerably earlier reaction times than the corresponding curve presented by Rostoker4 for a 7 pct Cr alloy, and lies athwart the curve of Spachner and co-workers11 for an 8 pct Cr alloy. Differences in criteria for the beginning of the a reaction and the relatively high rate of this reaction at lower temperatures presumably account for some of these divergences and may also explain, in part, the apparent failure of an iodide-base 7.22 pct Cr alloy to react more slowly than sponge-base 7 to 8 pct Cr alloys. Grain Boundary Allotriomorphs: Crystals of this morphology nucleate at and grow preferentially and more or less smoothly along the matrix grain boundaries.5-7 Allotriomorphs are the first morphology to precipitate at most grain boundaries at reaction temperatures from 725°C, the highest temperature studied, at least through 575°C. Fig. 2 Shows typical allotriomorphs, formed during an early stage of transformation at 725°C. Grain boundary allotriomorphs are not the predc=iaant morphology at late reaction times at any temperature studied. However; from 725" through

Jan 1, 1958

By L. O. Brockway, W. C. Bigelow, J. A. Amy

Specimens of Inconel-X alloy solution-treated at 2050°F and aged for periods of 1, 10, 100, and 1000 hr at 1200°, 1400°, and 1600°F have been examined by electron microscopy and by electron and X-ray diffraction. Four minor phases were identified: titanium nitride, niobium nitride, an M23C6 complex carbide, and the intermetallic ? phase. The two nitrides were found in all of the aged specimens and in the solution-treated alloy, the y&apos; phase formed at all aging temperatures, while the M23C6 carbide formed only on aging at 1200° and 1400°F. Variations in the hardness, rupture strength, creep strength, and yield strength of the alloy have been shown to be related to variation in the size and distribution of the particles of the y&apos; phase within the matrix grains of the alloy, with maximum values of these properties occurring when there is a maximum amount of the phase present and a fine state of dispersion of the particles prevails. THE nickel-chromium alloys containing titanium and aluminum are widely used in applications requiring high strength at elevated temperatures. Studies on relatively simple ternary and quaternary alloys&apos;-4 have indicated that the favorable high-temperature properties of these alloys are related to the precipitation of an intermetallic ?&apos;-phase having a structure based On that of the Ni3A1 phase of the nickel-aluminum system. The present investigation was undertaken to identify the minor phases and to study the microstructural changes occurring in one of the more complex commercial alloys as a result of aging in the service temperature range, with particular emphasis on investigating the role of the ?&apos; -phase. The microstructural changes were studied by electron microscopy and the minor phases were identified by X-ray and electron diffraction. MATERIALS AND METHODS Inconel-X alloy was selected for this investigation because the previous studies of Frey, Freeman, and white6 provided extensive information on the variations in metallurgical properties of this alloy resulting from high-temperature aging treatments. Specimens aged 1, 10, 100, and 1000 hr at 1200°, 1400°, and 1600°F were made available for the present use. These were taken from 1-in. round-bar stock of a commercial heat having the following weight composition: 0.04 C, 0.56 Mn, 6.59 Fe, 0.007 S, 0.38 Si, 0.03 Cu, 73.22 Ni, 14.97 Cr, 0.78 Al, 2.38 Ti, and 1-02 Nb. They were solutjon-treated at 2050 for 4 hr and then water-quenched prior to aging. Powder X-ray diffraction patterns were obtained from insoluble minor phases which were separated from the alloys by digestion in the reagent of Mahla and Nielsen.6 Back-reflection patterns were obtained from electrolytically polished surfaces of the bulk search to detect the ?&apos;-phase&apos; Cu-K a radiation was used in both cases. In the electron-diffraction studies, the general method developed by Heidenreich, Sturkey, and

Jan 1, 1959

By R. P. Smith

The diffusivity of carbon in iron, cobalt, and alloys of 89.7 and 79.3 wt pct Co has been determined by a decarburization method for the temperature range 850° to 1100°C. The Plots of log D us 1/T for the two Fe-Co alloys are linear through the region of the Curie temperature, showing that, unlike some cases of substitutional diffusion, carbon diffusion in these alloys is not affected by electron spin order. RECENT investigations1-&apos; have shown that for substitutional diffusion in iron the change in diffusivity with temperature does not follow an Arrhenius equation, at temperatures near the Curie temperature. Data on the diffusivity of carbon in a iron5"9 indicate that this anomaly does not exist for interstitial diffusion; however, this has not been definitely established. Since cobalt and Fe-Co alloys, 80 to 100 pct Co, have Curie temperatures in a temperature range convenient for carbon-diffusion measurements they are suitable systems for studying the relation of interstitial diffusion and the Curie temperature. EXPERIMENTAL The carbon diffusivity, D, was determined by a decarburization method. The diffusion cylinders, made from small vacuum melts of electrolytic cobalt and plastiron, were about 0.76 cm diam and 6.3 cm long. A small amount of carbon was added to each melt to keep the oxygen content as low as possible. The cylinders were first treated with a hydrogen-3 pct water vapor mixture at 1100°C to constant weight, then carburized to the desired initial carbon content with a suitable CO-C02 gas mix-

Jan 1, 1964

By J. E. Harris

By elimination of other possible nucleation processes, it has been demonstrated, for commercially pure magnesium and a Mg-Al alloy, that at stresses less than that necessary for triple-point cracking creep cavities are most probably nucleated heterogeneously at second-phase particles. Evidence for the existence of such particles is presented and the role of grain boundary sliding in the nucleation process is examined quantitatively. DURING creep deformation of polycrystalline magnesium and its dilute alloys in the temperature range 0.45 to 0.7 Tm (Tm = absolute melting temperature) cavities form mainly along grain boundaries oriented normal to the stress axis and failure eventually occurs by their growth and impingement.&apos; The possibility of low-ductility creep failure of magnesium-alloy reactor cans during service has prompted a number of studies of cavity formation in these materials.2-5 In this paper divergent theories of cavity nucleation6-10 are examined critically and conclusions drawn regarding the most probable mechanism of formation of cavities in magnesium. The paper is divided into two parts. The first section consists of the review and quantitative assessment of the possible role of grain boundary sliding in the nucleation process. In the second part an experimental program is described where an electron-microscope technique has been used to determine if second-phase particles exist in as-received commercially pure magnesium and in a magnesium alloy 1) THEORETICAL REVIEW Possible nucleation sites for creep cavities are: a) high-angle grain boundary triple points,11-14 b) subboundary/grain boundary intersections,15-18 c) ledges in the grain boundary, 19-25 d) second-phase particles. 9,26-30 Each of these possibilities is now considered with special reference to deformation of magnesium. 1.1) Triple-Point Cracking. The stroh31 condition to nucleate fracture is: " > vr [1] where ss = applied shear stress, ? = surface energy, C = shear modulus, L = length of sliding interface. This relationship is independent of the nature of the interface and it is possible to calculate the stress concentration at the end of a sliding high-angle grain boundary and thus deduce, approximately,* the minimum applied stress necessary to nucleate triple-point cracking. Such theoretical predictions for Nimonic alloys have been made by McLean13 and found to agree quite closely with the minimum stress determined by experiment. Stresses capable of nucleating triple-point cracking should also be sufficient to nucleate fracture at a grain boundary due to intragranular slip, for the lengths of sliding interface in the two cases are approximately equal. Thus the minimum stress for triple-point cracking should represent a demarcation between failure due to general "cracking" and that due to cavitation. Hauser, Landon, and Dorn32 have demonstrated that for polycrystalline magnesium in the temperature range 78° to 298°K the fracture stress is inversely proportional to the square root of the mean grain diameter. As pointed out by stroh31 this result indicates that Eq. [I] describes the fracture characteristics of magnesium at low temperatures. Heal3 has reported that for rapid deformation (112 pct hr-1) of polycrystalline magnesium the transition from cracking to cavitation occurs in the temperature range 175" to 275°C. He also presented the fracture-stress values for the same material tested under similar conditions. From Eq. [I] taking G = 1.3 x 10" dynes , ? = 600 ergs . cm-2,33 and L = 0.017 cm, a Stroh-McLean13,31 tensile stress of -266 kg. cm-2 is calculated, corresponding to a transition temperature of -190°C; this is in

Jan 1, 1965

By R. D. Pehlke, J. V. Gluck

The limiting activity coefficient of zinc in a "binary " solvent has been described for several dilute ternary solutions by combining literature data from recent interaction studies in the terminal regions with thermodynamic data for the central regions. Results are discussed in terms of the Alcock and Richardson random solution model. The observed behavior agrees semiquantitatively with predictions using the model. RECENT efforts in the thermodynamics of dilute ternary liquid metallic solutions have been mainly concerned with the interactions between two dilute solutes, that is, the terminal region at an apex of the composition diagram.&apos;-&apos; A more general case is that of the behavior of a dilute solute over the full range of a ternary system, or, more specifically, the limiting activity of solute i as projected to the k-j binary side of the i-j-k composition triangle. An implication of this is that the interaction between i and j at the k apex should connect in some way to the interaction between i and k at the j apex. A model to characterize various types of expected behavior has been discussed by Alcock and Richardson.9,10 Such behavior can range from a simple linear relation for In yi over the 1-k binary to more complex curved relations which depend on various assumptions regarding the heat of solution in the j-k binary system and the presence or absence of clustering with solute i. Quantitative data to assess these concepts have been limited primarily to the cases of nonmetallic interstitial solutes in ferrous solutions. Alcock, Richardson, and various coworkers9-13 have discussed the behavior of oxygen, sulfur, silicon, or hydrogen in dilute solution over the range of iron + metal systems; however, the only data considered by them for substitutional nonferrous metallic solutions were the results of Elliott and Chipman concerning the activity of cadmium in the Pb + Sn, Pb + Bi, and Pb + Sb systems.9 These data were limited and did not cover the terminal regions in detail. An opportunity to extend the Alcock and Richardson considerations to the dilute solution of zinc in various "binary" solvents has been afforded by combining results of several of the recent investigations of ter-minal-region interactions with previous data from the literature for the same more concentrated solutions. RESULTS AND DISCUSSION The results of the analysis are shown in Figs. 1 to 5 where the log activity coefficient, (In yZn)xzn--o, is plotted vs the composition of the "binary" solvent. In these plots the end points are the values for In yzn in the appropriate binary solution with Bi, Pb, Sn, Cd, or In at the indicated temperature—usually 550°C (823°K). For the terminal regions the slopes were drawn using the first-order interaction parameters taken from various studies reported in the literature. The data points shown in the central regions were obtained by the short extrapolation to infinite dilution of the logarithm of the activity coefficient calculated from thermodynamic studies reported in the literature for the same systems. The sources of the data are indicated on each figure. Second-order effects were not considered. Reasonably smooth curves can be drawn to connect the central region with the terminal regions for the Zn-Pb + Bi system, Fig. 1, the Zn-Pb + Zn system, Fig. 1, and the Zn-Bi + Cd and Zn-Bi + Sn systems, Fig. 2. As shown in Fig. 2, where central region data are available from two independent investigations, the agreement is quite good. The Zn-Pb + Cd system does not appear to be as well behaved as the previous four, Fig. 3; however, this type of behavior has also been

Jan 1, 1970

By B. H. Bergstrom, Will Mitchell, T. G. Kirkland, C. L. Sollenberger

IN a previous article&apos; the authors outlined a study of the variables in rod milling and also reported data from a series of open circuit grinding tests on a massive limestone in a 30-in. x 4-ft end peripheral discharge rod mill. As a second part of the experimental program, an analysis is now presented for the 30-in. x 4-ft overflow rod mill grinding under identical conditions, except that discharge ports on the periphery of the mill shell have been sealed so that the products from the present series overflowed through a 9-in. diam .opening in the center of the end plate. A variance analysis has been made of the combined data for the two experiments, and performances of the two mills are compared here. Included in the first report&apos; were descriptions of feed preparation, rod mill circuit, instrumentation and controls, and techniques used to evaluate data. Dependent and independent variables were defined, and variance analyses were made to test the relative significance of variables and to establish magnitude of error for the experiment. Significant data were plotted in various combinations, and conclusions were drawn from the graphs. The procedure and analysis in this series of tests follows the first tests and is not repeated. Data from the second series are recorded in Table I. Listed in the first three columns are the independent variables of feed rate (1000, 2000, 3000, 4000, and 5000 1b per hr), mill speed (50, 60, 70, 80, and 90 pct of critical), and pulp density (50, 60, 70, and 80 pct). The dependent variables, Pso, P100, reduction ratio, slope of the log-log sieve analysis curve, power demand, and Bond work index follow. Of these, only the reduction ratio and the Bond work index were analyzed for significance. Production of new surface as calculated from sieve analyses has not been included for this series because of the questionable assumptions that have to be made to satisfy the formulas involved. The large number of products obtained during the runs precluded the use of surface measurement techniques by the gas adsorption methods at this time; however, samples of all products have been stored for future reference. To test the consistency of the reporting of the sieved products, an averaged sieve analysis was calculated from the wet-dry plots obtained from the three product samples of each run. The resulting averaged analysis was plotted and the P80, selected. The relative deviations of the P80&apos;s from each of the three product samples with respect to the P80 of the averaged analysis were then calculated. In only two sets were the relative deviations (6.2 and 9.9 pct) considered excessive. In each of these two sets, one sieve analysis was obviously out of line; hence that analysis was ignored and new averages were computed. This reduced the relative deviations to 1.2 and 2.7 pct respectively. The relative deviations of the product analyses with respect to their averages ranged from 0.1 to 1.4 pct at 1000 lb per hr, 0.0 to 1.1 pct at 2000 lb per hr, 0.2 to 3.0 pct at 3000 lb per hr, 0.3 to 4.3 pct at 4000 lb per hr, and 0.5 to 5.2 pct at 5000 lb per hr. The relative deviation of the 80 pct passing point for 96 dry sieve analyses of the feed with respect to that of the averaged analysis was 7.6 pct. This slightly higher percentage can probably be attributed to a greater proportion of tramp oversize in a crusher product than is ordinarily found in a rod mill product. The last column on Table I lists the adjusted work index, which has been used as the measure of efficiency for the various combinations of operating conditions investigated. Efficiency increases as the index becomes lower. It was reported in the previous paper that the work indexes for the Waukesha limestone used in these experiments decreased as the product size decreased (as calculated from Bond grindabilities). That is, this limestone becomes easier to grind as the material becomes finer. This is unusual, because the work index for most materials as calculated from the Bond grindability has remained constant as the product size decreased or has increased slightly. Table II lists the results of Bond grindability tests at all mesh sizes from 3 to 200 and the work indexes calculated from them. To remove this variation of work index with product size from the data so that results would apply to any material of constant work index, the work index values shown in Table II were plotted against product size on log-log paper. From this curve (a straight line function in this case), the expected work index for the product size for each of the runs of the experiment was obtained. The work indexes as calculated from the reduction ratio and energy consumption were then divided by the corresponding expected work index. The results obtained are reported in percentages on Table I as adjusted work index and are actually percentages of the work index for the Waukesha limestone at the size in question. Multiplication of the work index value for a material of constant index by these percentages should allow the application of the adjusted work index curves to the material. Only the adjusted work index values, not the actual experimental values, were used for the variance analyses and for the graphs.

Jan 1, 1956

In 1973, US Borax & Chemical Corp. began investing three days wages and about $20 in training materials in every new employee before having him report to his first job. The result? Accidents involving new employees in the past two years have dropped by more than half from the 1972 level. What made this success possible was safety training done with programmed instruction materials-which, incidentally, US Borax also uses for vocational training.

Jan 4, 1976

By Bernard Kopelman

The particle size of tungsten metal powder used to make tungsten wire for use in radio tubes and incandescent lamps must be closely controlled if the highly desirable feature of nonsagging is to be achieved. Our knowledge of factors affecting the particle size of tungsten powder has been limited by lack of any extensive literature on the subject. There are no publications in the English language discussing this problem in any but the most general terms. In this paper the published experimental information on this subject is reviewed. Based on the published data and some experimental data obtained by the author, a general theory of factors affecting the particle size of tungsten metal powder obtained by reduction of the oxides in hydrogen is offered. The various forms of the tungsten oxides and tungsten metal used in the experiments described were those prepared by commercial processes, so that the experimental results obtained on a laboratory scale would be more directly applicable to actual commercial reduction conditions. The effects of time of reduction, temperature. and concentration of water vapor in the hydrogen were observed by counting microscopically the particle distribution obtained. Such a method is very time-consuming, but the data obtained by this method are more reliable and more fundamental than those obtained by any of the several instruments available for measurement of particle size. Review of the Literature Until the year 1912, tungsten powder was prepared commercially by reducing tungstic oxide in the presence of carbon or one of its compounds (such as glycerin or ethylene glycol), usually by firing the mixture in a closed fire-clay crucible. The resultant powder contained about 95 per cent tungsten.&apos; When reduction of tungsten oxides by H² was introduced Commercially,²,³ several investigators became concerned with the equilibria between tungsten metal and its several oxides in an atmosphere of hydrogen and water vapor.4-l3 While these many investigations were in fair agreement on the equilibria WO³ + H2 = WO2 + H2O and WO2 + 2H2 = W + 2H2O there arose considerable controversy as to the chemical composition of the oxide between WO³ and WO², because of very poor agreement on the equilibrium constant of this intermediate oxide reduction reaction. The controversy on this intermediate oxide has been in progress for more than 100 years. Thus Malguti,14 in 1835, decided it was WO2.56 In 1857, Riche15 proposed the formula W³O8. Usler,16 in 1865, confirmed the existence of WsO8 and further proposed W1O1l. In 1897, Desil7 agreed upon W²O8 but also found W5O14.

Jan 1, 1947

By Bernard Kopelman

The particle size of tungsten metal powder used to make tungsten wire for use in radio tubes and incandescent lamps must be closely controlled if the highly desirable feature of nonsagging is to be achieved. Our knowledge of factors affecting the particle size of tungsten powder has been limited by lack of any extensive literature on the subject. There are no publications in the English language discussing this problem in any but the most general terms. In this paper the published experimental information on this subject is reviewed. Based on the published data and some experimental data obtained by the author, a general theory of factors affecting the particle size of tungsten metal powder obtained by reduction of the oxides in hydrogen is offered. The various forms of the tungsten oxides and tungsten metal used in the experiments described were those prepared by commercial processes, so that the experimental results obtained on a laboratory scale would be more directly applicable to actual commercial reduction conditions. The effects of time of reduction, temperature. and concentration of water vapor in the hydrogen were observed by counting microscopically the particle distribution obtained. Such a method is very time-consuming, but the data obtained by this method are more reliable and more fundamental than those obtained by any of the several instruments available for measurement of particle size. Review of the Literature Until the year 1912, tungsten powder was prepared commercially by reducing tungstic oxide in the presence of carbon or one of its compounds (such as glycerin or ethylene glycol), usually by firing the mixture in a closed fire-clay crucible. The resultant powder contained about 95 per cent tungsten.&apos; When reduction of tungsten oxides by H² was introduced Commercially,²,³ several investigators became concerned with the equilibria between tungsten metal and its several oxides in an atmosphere of hydrogen and water vapor.4-l3 While these many investigations were in fair agreement on the equilibria WO³ + H2 = WO2 + H2O and WO2 + 2H2 = W + 2H2O there arose considerable controversy as to the chemical composition of the oxide between WO³ and WO², because of very poor agreement on the equilibrium constant of this intermediate oxide reduction reaction. The controversy on this intermediate oxide has been in progress for more than 100 years. Thus Malguti,14 in 1835, decided it was WO2.56 In 1857, Riche15 proposed the formula W³O8. Usler,16 in 1865, confirmed the existence of WsO8 and further proposed W1O1l. In 1897, Desil7 agreed upon W²O8 but also found W5O14.

Jan 1, 1947

By G. Sachs, G. Espey

Simple methods can be used for the determination of the residual stresses in thin walled tubing if the stresses consist of high tensile stresses at the one surface and high compressive stresses at the other surface. Such a stress distribution is approximated in sunk tubing and in deep-drawn shells. It is possible to cut sections from such articles in such a manner that a major part of the residual stress is relieved by a bending of the Part that is separated from the adjacent metal. The circumferential stress is evaluated from the change in diameter D, occurring on splitting a length of tubing (Fig. Ib) or from deflection resulting from the cutting out of a circumferential tongue (Fig. Ia) .6 The bending moment M released by such a flexure is. M - EI (I-I) = EI R1-R0 I - u2(R0-R1) I -V2 R0XR1 where E = modulus of elasticity, v = Poisson&apos;s ratio, I = moment of inertia of the section, R0 =. mean radius before splitting, R1 = mean radius after splitting. The release of this bending moment corresponds to the release of stresses, which, in a thin section, vary linearly from one surface to the other, and have the following value in a particular fiber a certain distance (x) from the surface: S = c d I - V2 x c x d 2 2 RI - R0____E (d ) R1 - R0 X R0 X R1 ~ i - u2 (2 x) Ro X R1 where C is the section modulus and d is the thickness of the section, the ratio M:C being d: 2 for a rectallgular section.* The maximum stress values at the surfaces are. Smax = +E X d X R1-R0 I — u2- 2 R0 X R1 For most purposes the simpler equations: EXd AD1 = ± I - u2 x dm2 and will be satisfactory, where D,, is the aver. age of the mean diameters of the tubing

Jan 1, 1942

By G. Sachs, G. Espey

Simple methods can be used for the determination of the residual stresses in thin walled tubing if the stresses consist of high tensile stresses at the one surface and high compressive stresses at the other surface. Such a stress distribution is approximated in sunk tubing and in deep-drawn shells. It is possible to cut sections from such articles in such a manner that a major part of the residual stress is relieved by a bending of the Part that is separated from the adjacent metal. The circumferential stress is evaluated from the change in diameter D, occurring on splitting a length of tubing (Fig. Ib) or from deflection resulting from the cutting out of a circumferential tongue (Fig. Ia) .6 The bending moment M released by such a flexure is. M - EI (I-I) = EI R1-R0 I - u2(R0-R1) I -V2 R0XR1 where E = modulus of elasticity, v = Poisson&apos;s ratio, I = moment of inertia of the section, R0 =. mean radius before splitting, R1 = mean radius after splitting. The release of this bending moment corresponds to the release of stresses, which, in a thin section, vary linearly from one surface to the other, and have the following value in a particular fiber a certain distance (x) from the surface: S = c d I - V2 x c x d 2 2 RI - R0____E (d ) R1 - R0 X R0 X R1 ~ i - u2 (2 x) Ro X R1 where C is the section modulus and d is the thickness of the section, the ratio M:C being d: 2 for a rectallgular section.* The maximum stress values at the surfaces are. Smax = +E X d X R1-R0 I — u2- 2 R0 X R1 For most purposes the simpler equations: EXd AD1 = ± I - u2 x dm2 and will be satisfactory, where D,, is the aver. age of the mean diameters of the tubing

Jan 1, 1942

By R. T. Mishler

Silver-gold. mine, in northern Mexico, with arrow veins in rhyolite. One fourth area developed has been ore. Deposits average 20 in. wide and 73 oz. silver per ton; diluted in mining to 40 oz. per ton. Developed by drifts and raises at 100-ft. intervals. Samples cut every 5 ft. Ore and waste sampled separately to make combined stoping width 3 or 3 1/2 ft. Ore reserves figured to sloping width; high assays not modified. Tonnage and assay of ore extracted higher than estimates. Ore stoped principally by cut and fill method. Cars from each stope counted and sampled. Cars check tonnage to concen¬trator within 1 per cent.; silver assay 9 per cent. high. Tonnage and assay from scopes corrected to agree with feed to concentrator. Profit or loss for each slope estimated monthly. THE Lucky-Tiger mine is a silver-gold property, situated at El Tigre, in the northeastern part of Sonora, Mexico, at, an elevation of 6000 ft. in the Sierra Madre Mountains. It is 30 miles by wagon road from the Esqueda station on the Nacozari railroad. Since its discovery in 1903, the mine has produced forty million ounces of silver. The ore has averaged 40 oz. silver and 0.25 oz. gold per ton. Copper, lead and zinc have been of minor importance, having averaged 0.4 per cent., 1.1 per cent., and 1.5 per cent., respectively. The richness of the ore,, combined with its occurrence in narrow veins, required the use of the more expensive methods of mining.

Jan 2, 1925

By Eugene P. Pfleider, Claus Freyberger

Generally, the different methods of financing new mining projects are not well understood by the engineers and supervisory personnel. Nor are the effects of these alternatives on depletion, taxes and profitability readily apparent to even the sophisticated management personnel without the aid of cash flow studies. Fortunately, with the advent of the computer it is possible now to simulate many different combinations of 1) equity, 2) loan and 3) production payment financing with little effort. A general computer program for cash flow analysis of mining ventures has been developed and applied as a case example to a 1967 feasibility study of the Underground Mining of Minnesota Taconite. The effects on profitability as measured both in rates-of-return and present value are presented for various financing combinations. In addition, percentage depletion rates were altered so as to measure the impact of this statuatory allowance. Based on the cost data as presented in the aforementioned 1967 feasibility study, and assuming 7% loans, the rates-of-return vary from 9. 9% to [00] % on equity variations and from 9. 9% to 11.4% on total invested funds.

Jan 1, 1969

By Jr. W. L . Phillips

The deformation and fracture characteristics of lithium-fluoride single crystals stressed in compression at room temperature have been studied. In as-cleaved specimens the stress-strain curves were variable; two types of {110} fractures were observed in the vicinity of kink bands. The stress-strain curves of annealed crystals were reproducible; {100} cracks formed which propagated along the (100) and (110) planes. The deformation and fracture characteristics were affected by quenching and X-ray irradiation. STUDY of the mechanical behavior of nonmetallic materials has received considerable impetus in recent years because of the need to overcome the problem of brittleness before the refractory properties of nonmetallics can be fully exploited. Ionic crystals provide a convenient and simplified starting point from which to study the deformation and fracture processes in nonmetallic materials. Early investigations of the mechanical behavior of non-metals were restricted largely to determinations of the crystallographic indices of the cleavage and fracture planes and the glide and twinning elements. Until recently, only occasional systematic studies of the deformation characteristics of non-metals have been made; and investigations of the forces necessary to initiate plastic deformation and the factors which affect the flow characteristics have been restricted largely to studies of sodium chloride&apos;-7 , magnesium oxides-l3 and lithium fluoride. 14-22 Fracture studies on alkali halide and metal oxide single crystals have been limited despite the fact that these materials have a number of advantages for fracture studies. Because they are transparent, the cracks which form can be viewed in three dimensions instead of in two dimensions as in metals. Also, they exhibit stress birefringence under polarized illumination, which enables the internal stress pattern and, therefore, the distribution of dislocations to be examined in the vicinity of the fracture. Early workers1-4 have shown that ionic crystals with a cubic structure fracture in tension along the (100) plane normal to the applied stress. These fractures were brittle at room temperature and propagated very rapidly across the cross section of the crystal. More recently, Stokes, Johnston, and Lil0 have studied crack formation in compressed magnesium-oxide single crystals. They found that the cracks, which were observed after about 3 pct strain, formed in the region of a kink band and lay on conjugate (110) slip planes instead of the usual(100) cleavage plane. Two different types of cracks were noted: stroh23 and secondary. The Stroh cracks did not exist merely on the surface but extended through the specimen in the form of tiny slits. A secondary

Jan 1, 1962

By AIME

The following corrections (in italics and bold face) were received too late for the September issue of Transactions: Page 270, Abstract, line 1, spelling should be goethite. Page 270, column 1, authors&apos; box, authors&apos; affiliations should read: L. A. BAKER, formerly Principal Research Scientist, is Pellet Plant Superintendent, Cliffs Western Australian Mining, Cape Lambert, W. A., Australia. C. G. THOMAS is Experimental Officer, Minerals Research Laboratories, C.S.I.R.O., North Ryde, N.S.W., Australia. R. J. CORNELIUS and K. S. LYNCH are General Superintendent, Product and Process Development, and Superintendent, Pellet Plant, respectively, Hamersley Iron Pty. Ltd., Dampier, W. A., Australia. G. J. ARMSTRONG, formerly Chief Metallurgist, Hamersley Iron Pty. Ltd., is Mill Superintendent, Samin Ltd., Burra, S. A., Australia. Page 271, column 2, line 41, should read "highest possible spalling temperature and to adjust the. . :&apos; Page 275, column 1, line 1, should read "(LOI) figures are shown in Table 1 and vary from 2.61..." Page 275, column 1, line 16, spelling should be goethite. Page 276, column 2, line 6, should read "Predicting Grate Speed and Production Rate: The cor-..." Page 276, column 2, line 8, should read "basis of Blends A, B, C, D, and Plant Ore 1, shown in Table..." Page 276, Table 3, heading under "Prediction Method" should read Blend E. Page 277, column 1, line 38, should read "=293 tph of specification pellets (see Table 1 for loss-..." Page 277, column 2, replace caption for Fig. 14 with the following: Fig. 14-Example of calculation of hood temperature profile during downdraft free-water drying, given plant free-water drying time. Page 277, column 2, replace caption for Fig. 15 with the following: Fig. 15-Example of calculation of hood temperature profile during drying, given plant goethite drying time.

Jan 1, 1974