By Toshiyuki Nohira, Eiichi Takeuchi, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The Dy-Nd-Pr-Ni alloy sample was prepared by cathodic potentiostatic electrolysis at 0.65 V (vs. Li+/Li) for 1 h using a Ni plate in a molten LiCl-KCl-DyCl3-NdCl3-PrCl3 system at 723 K. The highest mass ratio (Dy/Nd+Pr) in the alloy sample was observed to be 50 at 0.65 V. Anodic potentiostatic electrolysis at 2.20 V for 12 h was conducted using the Nd-Fe-B magnet electrode in a molten LiCl-KCl system. All elements were almost dissolved from the magnet, and the original form of the magnet disintegrated. After anodic potentiostatic electrolysis at 2.20 V, cathodic potentiostatic electrolysis was conducted at 1.00 V for 5 h using a Mo plate in order to remove the dissolved Fe from the bath. Finally, cathodic potentiostatic electrolysis was conducted at 0.65 V for 12 h using a Ni plate. The mass ratio of Dy/Nd in the alloy sample was determined to be about 18.

Jan 1, 2015

By Kinya Atsumi, Kanjana Khunathai, Hisaya Kato, Hidetka Kawakita, Keisuke Ohto, Katsutoshi Inoue

"Crosslinked microalgae were prepared from the residue generated in the production of biofuel, by crosslinking-condensation in concentrated sulfuric acid. These microalgae were tested for adsorption of various metal ions in hydrochloric acid medium. The crosslinked microalgae exhibited high selectivity for Au(III) over other precious and base metal ions. From an isotherm experiment, the maximum adsorption capacity was evaluated to be 3.25 mol/kg of dry gel for Au(III) which was many times higher than that of the original microalgae residue. SEM and X-ray diffraction confirmed the formation of metallic gold particles, suggesting the occurrence of a redox reaction between surface functional groups on the gel surface and trivalent gold ion.IntroductionSubstantial quantities of precious metals are being used by the electronic industry because of their excellent electrical conductivity and resistance to corrosion. In recent years, recovery of precious metals from secondary sources such as electronic scrap [1,2 ], and leach liquors is being favored because of environmental concerns. Of course, recovery is only practical, if its cost is lower than the value of the metals (gold, platinum and palladium) recovered.Traditional methods of separation and refining do not fulfill this requirement. In order to overcome this problem, attempts have been made in recent years to develop new processes including total leaching in hydrochloric acid containing chlorine gas or hypochlorite, followed by solvent extraction and ion exchange [3]. In the new processes, new solvent extraction reagents or ion exchange resins with high selectivity and high loading capacity are used to simplify the process and to reduce the operating costs."

Jan 1, 2011

By D. T. Smith, L. M. Hsiung, J. J. Schmitt, J. W. Golz, R. L. Lankey, H. N. G. Wadley, J. Z. Zhang, B. L. Halpern

"The microstructure and mechanical properties of Al/AI2O 3 metal-oxide nanolaminates fabricated by' a novel Jet Vapor Deposition (JVD) process at substrate temperatures of ~25° and -250°C have been investigated using transmission electron microscopy (TEM) and nanoindentation methods. The thickness of the oxide layer was held constant between 2 and 5 nm, whilst the Al layer thickness was systematically varied from -3 to -50 nm. Continuity of the Al layers was significantly improved when the nanolaminates were deposited at an elevated substrate temperature (-250°C). The yield strength of the nanolamintes with Al layers greater than -25 nm follows a Hall-Petch type relationship, whereas that of the nanolaminates with Al layers less than -25 nm is better predicted by a Koehler-Lehoczky strengthening model. IntroductionAluminum-aluminum oxide (presumably A12O3) nanolaminates have been recently fabricated using a novel Jet Vapor Deposition (ND) process developed and patented by Jet Process Corporation [1-4]. ND uses sonic, high purity helium (He) gas jets to entrain atomically dispersed vapor and deposit films. It is of interest here because it can deposit multilayered structures (laminates) inexpensively at high rates. Materials with a thin, multilayer structure are of interest because they potentially offer novel mechanical and physical properties [5]. Koehler in 1970 used an image force model to investigate the strength of laminated materials and proposed the use of alternating layers of high and low shear modulus metals to produce high strength composite materials [6]. He predicted that dislocations would have to overcome a large repulsive image force in order to move from metal layer B of lower shear modulus (uB) into metal layer A of higher shear modulus (uA)' The image force (F) is given by the relation:"

Jan 1, 1994

By Jewel Gomes

Green rust is an important intermediate in oxidative transformation of Fe(II) phase. This unstable compound contains a mixture of ferrous and ferric hydroxides that belong to a family of minerals known as layered double hydroxides (LDH). Its general formula is [FeII(6-x) FeIIIx (OH)12]x+[Ax/n-*yH2O] x-, where A is an n-valent anion mainly Cl-, CO3-2 and SO4-2, and in which either the bivalent or the trivalent iron can be replaced for other trivalent or bivalent metal ions. It was first identified as corrosion product, later in soils as a product of interactions between microbes and metals in soils. Due to its high reactivity, it is used in the reduction of organic and inorganic compounds, As removal, and the treatment of acid mine drainage. In this paper, we described the method of electrochemical generation of green rust, its characterization by XRD, SEM and FT-IR, and its implications to electrocoagulation.

Jan 1, 2009

By J. H. Corrigan

A series of six papers describing the Falconbridge Dominicana Ferronickel project were presented at the International Laterite Symposium held as a joint project of TMS-AIME in February 1979 at New Orleans. A review of the ore mineralogy, as well as. the processing and environmental practices as they exist today at Falcondo with emphasis on modifications put into practice since 1979 are presented in two papers: Part I.- Mineralogy and Ore Dressing E.W. Lithgow - General Superintendent ? Mines Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Commercial volumes of nickeliferous laterite ores overlie part of a 90 km long belt of peridotites in central Dominican Republic. Protores are serpentinized harzburgites and dunites, with lesser serpentinite. The ore mineralogy consists mostly of goethite, serpentine-group minerals, quartz and poorly crystallized, X- ray amorphous materials. Minor constituents are hematite, gibsite, olivine and enstatite. In the Ore Dressing plant, the mine feed is subjected initially to proper sizing and blending to produce a homogenized mix. Subsequent drying and upgrading, by selective crushing and screening of rock kagments through a Barmac circuit, complete preparation of the ore for pyrometallurgical processing. Part II.- Pyrometallurgy, Fuel and Power Generation J.H. Comgan - Manager ? Production Falconbridge Dominicana, C. por A. Bonao, Dominican Republic Falcondo's energy requirements are based on oil which is refined on site to provide distillate to carry out drying and selective reduction of the nickeliferous ore in the shaft furnaces, plus bunker oil to produce electrical power for process melting, refining and ancillary use. The dryer product at 1.68% Ni is briquetted and passed counter current to hot reducing gas in 12 vertical shaft furnaces. The hot calcine discharge is melted in two high power electric furnaces at very high secondary voltage. The crude ferronickel is ladle refined and cast as 15 kg ingots or 125 gm ferrocones.

Jan 1, 1993

By R. E. Aune

In the present work, a critical assessment of the thermodynamic information available for the ternary system Ni-W-0 has been carried out; This was complemented by experimental measurements of the standard Gibbs energy of formation of the ternary compound NiWO, by solid state galvanic studies involving Zr02-CaO solid electrolyte. The assessed thermodynamic data, together with the phase diagram information available in literature, were employed to generate the ternary phase diagram for the system Ni-W-0 in the temperature range 1073-1273 K. The calculation of the phase diagram was carried out by computer optimization according to the "CALPHAD" method. The computed phase diagram has been confirmed at isothermal sections by identification of the phases present in samples equilibrated at defined temperatures.

Jan 1, 1994

By Bogidar Mihaylov

A laboratory study was conducted on continuous precipitation of copper, cadmium, mercury and arsenic using thiourea, thioacetamide, sodium sulfide and ammonium sulfide as precipitating agents. Depending on the experimental conditions the metals precipitate with the sulfide donors at different orders and rates. These differences were employed as a basis of several techniques for continuous separation of copper and arsenic, cadmium and arsenic, mercury and copper, and copper, mercury and arsenic. The separation of the metals from industrial waste solutions was also studied. The precipitates obtained were inspected using x-ray diffraction, scanning electron microscope, atomic absorption spectrometer and plasma particle counter.

Jan 1, 1992

By Toshiaki Nakai, Kunihiko Takeda, Kimio Imaizumi, Hiroaki Shirasaka

"The new type of nano-porous silica particle was considered to be constructed by the spinodal decomposition-type process which was found to have narrower pores than those of conventional porous silica prepared from boron silicate or ""Shirasu"" balloon. Nano-porous silica particles were fabricated by the calcination of silica gel mixed with well-dispersed complex salts composed of phosphorous and molybdenum compounds. Both silica and inorganic salts were not perfectly dissolved in the suspension solution. After removing of the water, the silica-inorganic salts complex was volatized and successively calcinated at a temperature ranging from 650 °C to 800 °C. Then, the inorganic salts were removed by dissolving in hot water. Other inorganic salts such as potassium halides were also found to be effective as a pore-size controller.IntroductionControl of structure has an important role in the field of industry as well as in the separation and purification technology for metals and organic syntheses. Many studies on the control of material structures have been reported regarding porous materials with pores ranging from nanometer to micrometer scale. 1 ) One example is zeolite as a naturally yielded porous inorganic material. Various types of synthetic zeolites have been studied as ""molecular sieve"" materials with ordinary pore-size of less than one nanometer. In 1992, crystalline meso-porous material with a large surface area named MCM-41 was synthesized through the use of template synthesis. 2) In direct relation to our study, amorphous borate glass having 4 to 100 nm of fine pores known as Corning glass 3l or SiO2-Al2OrB2O 3-CaO porous glass having large pore dispersity ranging from 4 to 10,000 nm have been reported. 4 ) S) 6 ) Some examples of several reported studies are as follows: phase-separated porous glass consisting of B2OrAl2O3-ZrO2-RO-R2O complex oxide 7 ) glass with finer pore induced from hydrolysis of silane alkoxide, porous material attained by condensation polymerization through the use of sol-gel process 8), alumina meso-porous material 9 ) 10), silica-zirconia material 11), carbon porous material 12), etc.."

Jan 1, 2000

The 15m high Inco flash furnace uptake was designed as a reaction chamber with the objective of destroying the H2S contained in the furnace off-gas by combustion with oxygen at about 1300°C. Until recently, the oxygen required for this purpose was injected through afterburners located at the bottom of the uptake. An undesirable side effect of this practice was the formation of build up accretions on the inside walls of the uptake. This buildup had a negative impact on both the furnace on line time and the control of the flash smelting process. In late 200 I, the afterburners were relocated to the roof of the uptake. As a result, about 80% of the uptake accretion buildup disappeared with obvious beneficial effects for the operation of the furnace. This paper discusses key flash smelting aspects that affect the operation of the flash furnace uptake such as the dusting rate, the formation of H2S in the freeboard of the furnace, and the impact of using coke to supply some of the heat required by the process. The mechanism of buildup formation and its dependence 'on uptake afterburners location are also examined. Prof. Yazawa's sulfide smelting thermodynamic relationships proved instrumental in understanding the conditions that influence the formation and the elimination of H2S and uptake buildup.

Jan 1, 2003

By Wang Shuchan, Zhang Zimu, Zhang Dianhua, Liu Yan, Zhang Ting-an, Zhao Qiuyue, Lv Chao

Rare earth extraction tank has many adverse effects like big floor space and high production accumulation during industrial production. Current researches usually focus on changing the device structure without making a breakthrough towards gravity clarification. This paper attempts to achieve this goal by using both the action of clarification by gravity and clarification by stirring. Because many physical parameters affect the clarification and separation rates, the density, viscosity and surface tension of the two phases were determined at different temperatures and different concentration of aqueous solution. The innovation of this research involves adopting the Karl-Fischer method to investigate water content in oil phase during the stirred separation process. In this paper, the separation effect of different physical parameters was studied and the dimensional equation between water content and the physical parameters was established by combining with the experimental data.

Jan 1, 2014

By Lucas Nana Wiredu Damoah, Lifeng Zhang

"Increasing demand for Solar Grade Silicon (SoG-Si) due to rising interest in renewable energy has lead to increased SoG-Si Top – cut scraps generated from the multi-crystalline silicon making process. Due to the high cost of SoG-Si and the potential to use the top-cut scraps as feedstock material, there has been increased effort to develop cost effective and efficient technologies. As a result, several methods to recycle the top-cut scraps are currently been applied, and researched. These include settling under gravitation field, which is a slow process to be industrially applicable. Natural settling of inclusions by gravitational force is a slow process and not attractive to the industry. Recent experiments on Top-cut SoG-Si scrap under high frequency, high voltage, electromagnetic field showed that SiC inclusions settled within a short time to the bottom of the crucible and the characteristic rod-like morphologies of Si3N4 inclusions in SoG-Si were not detected. This study investigates the enhanced settling of SiC inclusions and the behavior of Si3N4 particles under the influence of high frequency, high voltage, electromagnetic field in Top-cut SoG-Si.IntroductionThe photovoltaic industry depends on silicon based PV materials either as single-crystalline silicon, or multi-crystalline Si (MC-Si), or amorphous Si [1] for over 90 % of its market share. [2] MC-Si produced by directional solidification of solar grade silicon melt dominates the silicon PV market. During the directional solidification process, SiC and Si3N4 particles within the melt are pushed by the solidification front to the top of the ingot which is the last to solidify. Therefore the top of the ingot is cut generating what is known as top-cut solar silicon scraps. The Si3N4 particles are mainly from the coating material at the inside surface of the silica crucible and from air absorption during the solidification process. The SiC particles mainly stem from the carbon reduction process of the primary production of silicon [3]. Due to the growth of the PV industry as a result of global demand for clean, reliable, and affordable energy [4], there is the need to develop new methods to compliment exiting ones to recycle SoG-Si waste (e.g. top-cut) for sustainability."

Jan 1, 2012

By Kouji Mimura, Manabu Kishida, Minoru Isshiki

"Purification of metallurgical grade silicon (MG-Si) by the plasma-arc zone melting method (PZM) has been examined. The process consisted in the horizontal displacement of a molten zone heated by Ar- and 10%H2+Ar- plasma-arc under atmospheric pressure. This technique, especially using hydrogen plasma-arc, promoted the segregation of impurities from the head to the tail of the bar and the vaporization of impurities of higher vapor pressures. Metallic impurities such as Fe, Ti, Cr, Mn,. Cu, Al and Ca were reduced to less than 1 mass ppm at the head side of the Si bar. Non-metallic impurities such as boron, phosphorous, carbon and oxygen were also reduced by the zoning effect and, furthermore, by activated hydrogen atoms dissociated in the high temperature plasma-arc according to the following reaction: Q (in liq.Si) + 2H = H20. Plasma-arc zone melting with hydrogen plasma has been recognized to become an effective purification technique of MG-Si for the production of a low cost solar grade Si (SOG-Si).IntroductionDemand of high-purity Si for solar grade silicon (SOG-Si) is supposed to be further growing in the near future. The purity of SOG-Si required for the photovoltaic cell is more than six nines. An expensive semiconductor grade silicon (SEG-Si) with the purity of around eleven nines has been used to satisfy the demand. Development of techniques and processes for the production of a low cost SOG-Si is therefore necessary [l]. Although many purification techniques, such as directional solidification, plasmaarc melting and electron beam melting [1-6], and processes, such as carbothermic reduction of high purity silica [7], have been examined and proposed for this purpose, a more efficient and practical purification technique is still required.In the present work, the purification of MG-Si has been investigated using a plasma-arc zone melting (PZM) technique developed by the authors. Plasma-arc melting, which is well· known as a useful melting method for various metals and alloys, has been recognized to be efficient for refining and degassing several metals if hydrogen is added to the plasma generating gas, resulting in the so-called hydrogen plasma-arc. For example, deoxidation of Fe, Co and Ta [8,9], decarburization of Fe [9] and removal of metallic impurities from Zr, Ta and Fe [10-12] have been reported. This excellent refining effect is considered to be caused by dissociated and activated hydrogen atoms formed in the high temperature plasma-arc."

Jan 1, 2000

By Patrick R. Taylor

Thermal plasma technology has a wide range of applications in extractive and process metallurgy. Beneficiation of complex ores, oxide reduction, melting/remelting of refractory metals and scrap, and the recovery of precious metals from waste products are some examples of potential uses for plasma technology. The highly concentrated enthalpy provided by plasma torches is a cleaner energy source and may give higher processing rates per reactor volume than conventional technologies. Some of the other advantages may be: controlled furnace atmosphere, ability to treat fine feed materials and rapid quenching. A review of some of the uses for plasma processing in non-ferrous process and extractive metallurgy is presented.

Jan 1, 1993

By Kazuaki Mita

There are various intermetallic compounds in the Zn-Fe system. We synthesized them at about 673K. A specimen was examined chemically and X-ray diffraction was applied to ensure the formation of intermetallic compounds. Material containing two phases was placed in a Knudsen type effusion cell and the mass spectrum studied to evaluate the vapor pressure of zinc. The thermodynamic properties of intermetallics was then evaluated through measured intensity.

Jan 1, 1999

By T. P. R. de Jong

Dual energy X-ray transmission imaging is extensively applied for safety luggage inspection. Its advantages are its rapid scanning rate (25 to 100 cm/sec) at approximately I mm resolution and simultaneous thickness independent metal identification. This is especially advantageous for secondary scrap metal inspection and automatic sorting. Other applications include metal product inspection, bale control, and waste processing. Recent progress in development of an automatic on-line sorter for bulk solids is presented and discussed. Besides various non-metal applications (solid fuels, wastes etc.) it appeared particularly effective in light metal sorting. As inspection tool better control of difficult to monitor solid bulk streams, batteries, bales and other related metals becomes possible.

Jan 1, 2003

By Halvor Dalaker, Pål Tetlie

The decomposition of methane has been studied experimentally in contact with various oxides at elevated temperatures. For each oxide, the temperature at which the cracking starts has been determined. No correlation was found to exist between the temperature for the onset of cracking for a given oxide and the affinity for carbon of the oxide's metallic component. In terms of potential for using methane as a reducing agent, calculations are presented that indicate that the suitability of an oxide for such reduction depends on the desired methane+oxide reaction being more energetically favourable than the methane+methane=ethylene/acetylene reactions.

Jan 1, 2014

By Shuichiro Okada

Various efforts to reduce energy consumption and smelting cost are made at Tamano Smelter. Production of anode copper has been increased by about 30 % and energy requirement has been decreased about 50 % respectively. Challenges toward more higher goal are being continued. Details about the following are described in this paper. 1 Waste heat recovery Steam recovery at up-take of FSFE Heat recovery from waste gas of anode furnaces 2 Application of tonnage oxygen 3 Application of pulverized carbonaceous fuels to the flash smelting furnace with furnace electrodes ( FSFE ) 4 Application of computer control system to copper smelting 5 Improvement of the fugitive gas collecting system 6 Improvement of the mechanical tuyere puncher for the converter furnace

Jan 1, 1983

By Marcela C. Santini, Luiz A. Teixeira

"Surface conditioning (also referred as etching) of plastics prior to metallization is generally conducted with sulfuric I chromic acid solutions. Although these baths perform well technically, the presence of Cr (VI) imposes serious operating problems of an environmental nature. The present work reports ·the results of a study of surface conditioning o(ABS using solutions based. on sulfuric acid, with hydrogen peroxide and/or nitric acid, replacing chromic acid, as oxidants. Process performance was evaluated by SEM and by the uniformity and adherence of electroless nickel coatings applied on selected conditioned samples. The results showed that the evaluated types of solutions could be optimized to perform as well as the chromic-based baths, with a much superior environmental quality.IntroductionMetallization of plastics is normally undertaken for either decorative or functional purposes. Through metallization, the specific properties of plastics such as light weight, design flexibility, and low-cost of manufacturing are enhanced by the addition of properties usually associated with metals. These include reflectiveness, abrasion resistance, electrical conductivity, and a variety of decorative effects (1).The available processes that can be used for metallization of plastics are vacuum metallization or vapoµr deposition; indirect metallization and plating (1). Plating can be sub-divided into electroless plating and electroplating. In electroless plating, metal ions in aqueous solution are deposited on the .activated plastic surface by oxi-reduction reactions without the aid of an external electric potential, forming a thin metallic layer. This electroless deposited film has two functions: (a) it provides an electrically conductive substrate that allows further coating by electroplating; and (b) provides a secure bond between the plastic substrate and the electroplated layer (1,2). In case the electroless metallic part requires an additional layer for finishing purposes, or just an increase in thickness, the part can be additionally electroplated with a· variety of metals - in most cases those are copper, nickel or chromium (3)."

Jan 1, 2000

By Jay R. Hitchings

A technique that enables excellent color photograph production from black and white negatives of electron microprobe x-ray images is described in this paper. The photographs are made by superimposing one, two or three negatives of black and white x-ray images individually through assigned primary color filters directly onto color print paper. When used to examine metallurgical or geological microstructures, the resulting color photograph provides detailed, qualitative information about spatial arrangements, elemental associations and relative concentrations of at least three elements. The technique is simple and straightforward, requiring only standard darkroom equipment. The use of color to display or present complicated microprobe data also allows a non-technical reader or audience to better understand the data.

Jan 1, 1981

By J. B. Cocanour

Pioneering work at the U.S. Bureau of Mines (USBM) has produced a personal computer (PC)-based, software-driven video photometric color sensor for real time process control of metallurgical streams. The video photometer is an inexpensive optical sensor which operates in the visual area of the electromagnetic spectrum and collects color information through plastic optical fiber. The red, green, and blue (R/G/B) voltage components of the color video signal are digitized and characterized through software and then presented as the control variable for software-based proportional-integral-differential (PID) control. This sensor has been successfully employed in the control of a laboratory copper electrolytic circuit. With this sensor, copper solutions were analyzed on-line without the need for sample removal, dilution, mixing or reagent addition, thereby allowing for the real time control of the circuit.

Jan 1, 1994