By Chen Song

In the experiments of purifying the solution of chlorine leaching from nickel concentrate with N235, the effects of organic phase composition on purifying efficiency have been studied. From the results obtained, the optimal organic phase composition is found to be 25%N235+12%isomerous alcohol +63%sulfonic kerosene (VIV) and the saturated content of cobalt in organic phase is7.95 g*dm3. And then the serial experiment is carried out. The results show that at the given organic phase composition, the purified solution contains p(Ni) >200 gm dm3, p(Ni)l p(Co) >50000 and the contents of Cu, Fe, Mn, Zn meet the technical criterion of standard nickel electrolyte. The cobalt chloride solution contains p(Co) >I10 g L-1, p(Co) lp(Ni)>50000 and the enrichment of cobalt has been achieved.

Jan 1, 2006

By Chunlin Chen

Nickel-sulfide minerals are normally associated with copper and iron sulfides and often contain a minor amount of valuable metals such as cobalt and detrimental impurities such as arsenic. Metal losses in slag vary from process to process during the pyrometallurgical production of nickel and, depend on the feed composition, slag chemistry and operating conditions. Maximiz the metal recovery is one of major considerations to optimize operating condition for nickel smelting/ converting processes. At the same time, the deportment of minor elements between various phases during nickel smelting is of great importance by smelter operators. The Multi-Phase Equilibrium (MPE) is a thermodynamic package developed by CSIRO for simulating reactions between phases in multi-component and multi-phase systems [1]. Over the years the capability of the MPE model has been extended to cover the behavior of a large number of elements in high temperature systems. The sulfide smelting module of the MPE, which covers the minor elements such as As, Bi, Sb, Pb, Se, Te, Sn, Co and Zn, is capable of modeling the deportment of major and minor elements between various phases during nickel smelting. In this article the application of the MPE model in modelling the nickel smelting process is presented. The modelling results on the majors and minors are compared with the plant data. The deportment behaviour of arsenic in nickel smelting was analysed and the impact of slag chemistry on slag properties was modelled. These results can assist process metallurgists in exploring the optimum fluxing strategy for smooth operation and the potential practices for improving arsenic removal.

By Aiyuan Ma, Kun Yang, Weiheng Chen, Jinhui Peng, Shiwei Li, Feng Xie, Libo Zhang

In this thesis, a new process of recovering zinc sulfide ores was developed. The novel synthetic coordination leaching process mainly included two steps: microwave assisted phase reconstruction and compound coordination leaching. By applying various techniques, such as chemical composition analysis, X-ray diffractometry (XRD) and Raman spectroscopy, it could be concluded that sulfide phases would directly oxidized to zinc oxides under the 500 ºC microwave roasting and adding 30% Na2O2. What’s more, zinc leaching rate reached to 61.16% within 2 hours. Compared to the current technologies, this procedure had the advantage of avoiding SO2 emission, high leaching efficiency, simple process, manipulate easily, and low cost, which could be expected tremendous application potentials.

Jan 1, 2016

By C. J. Boreiko

Traditional patterns of lead and zinc utilization are being evaluated in accordance with new paradigms that seek to ensure the long-term compatibility of global industrial activity with precepts of sustainable development and sustainable consumption. As a consequence, both industry sectors are experiencing intense scrutiny from the international community, and numerous regulatory options are being considered that may impact upon international industry practice. This paper reviews the growing expectations being placed upon industry, and highlights some of the common regulatory concerns being expressed regarding both metals despite their differing toxicological profiles.

Jan 1, 2000

By Takuya Shinagawa

After vitrification of the residues from a municipal solid waste incinerator, the vitrified products can be used as a construction material, and the dust can be used as raw materials for the non- ferrous industry. The NKK electric-resistance furnace is operated under a reducing atmosphere, and heavy metals such as zinc and lead in the ash vaporize to form dust. Also, dust from the NKK electric-resistance ash melting furnace is composed of water insoluble zinc and lead components and water soluble NaCl and KCI. This is why, The concentration of zinc and lead in the dust after washing is sufficiently high for the dust to be used as a raw material for the zinc and lead industry. NKK developed a heavy metal recovery process in which zinc and lead in the dust are reclaimed as a raw material for smelting by making the best use of the characteristics of the dust.

Jan 1, 2002

By G. R. Waters

NMR360 is developing a suite of chloride-based metals extraction processes, with the first commercial operation scheduled for commissioning late in 2018. It is critical, therefore, that with the introduction of any new technology, that the circuits do not suffer from mechanical failures which will compromise the operation. Although chloride leaching is at atmospheric pressure and relatively low temperature, the main challenge is preventing corrosion, since the high proton activity makes even a small amount of acid behaves as though it were concentrated. An additional challenge in concentrated chloride circuits is the potential for solids precipitation. In this context, therefore, correct valve selection is crucial, and NMR360 has partnered with CGIS to ensure that the Severe Service Valves (SSVs) needed will perform over and above the definitions of the Manufacturers Standardization Society (MSS) of the Valve and Fittings Industry. This paper outlines what the minimum requirements are for SSVs in chloride leaching applications, drawing on five decades of industry experience from one of Canada’s leading valve experts.

By Masao Miyake, Eiichiro Matsubara, Tetsuji Hirato, Yasuhiro Awakura

"Zn-Cr alloy coating with around 15 wt% Cr has been found to have much higher chemical corrosion-resistance to steel than conventional zinc plating, while· its structure has not been clarified. The Zn-Cr alloy plating is performed at high current densities around 1 A cm-2 and for 10 to 20 sec using acidic aqueous sulfate solutions with some additives in the iron-steel industry. Due to the high current densities, it seems reasonable to consider that the Zn-Cr alloy plating proceeds under an unsteady-state condition and that the resulting coatings have a non-equilibrium phase and have a structure change in the .direction of thickness. In this research, the crystal structure of the Zn-Cr alloy coating electrodeposited at high current densities and change of the structure in the direction of thickness were examined by X-ray diffraction. The coatings containing under 20 and 35-40 wt% Cr had hcp and bee structure, respectively, while the coatings containing 20-35 wt% Cr comprised two phases with the hcp and the bee structure. The structure of the coating varied in the direction of thickness; both the hcp and bcc phases coexisted in the vicinity of the substrate, while the hcp phase became predominant with increasing distance from the substrate.IntroductionRecently it has been reported that Zn-Cr alloy coating containing around 15 wt% Cr has much higher corrosion-resistance to steel than conventional zinc plating.1-3) The corrosion-resistanc·e of Zn-Cr alloy plated steel sheet with a plating amount of 20 g m·2 is, for example, superior to that of Zn plated steel with a plating amount in the range 60 to 90 g m·2 , which is widely used for automotive bodies today.4l The Zn-Cr alloy plating is obtained by electrodeposition at current densities over 0.5 A cm·2 from a sulfate solution containing zinc and trivalent chromium ions and some additives.5•6) The deposition current densities mentioned above are much higher than those for usual electroplating processes, e.g., Zn, Cu and Ni plating, carried out about 0.05 A cm·2 • Therefore, the time required for plating is very short; around 10-20 sec. Due to the high current densities, it seems reasonable to consider that the· Zn-Cr alloy plating proceeds under an unsteady-state condition and that the resulting coatings do not have a phase expected from equilibrium diagrams; no phase diagram of the Zn-Cr system with a full composition range has been available. 7). In other words, the alloy phase plated would be a non-equilibrium phase with unknown structures."

Jan 1, 2000

By Hiroyuki Matsuura, Fumitaka Tsukihashi

"Emission of CO2 gas from steelmaking industry covers more than 12 % of total CO2 emission in Japan. Though many efforts have been made to curtail energy consumption and high energy efficiency of Japanese steel production process has been achieved so far, further reduction of CO2 emission is strongly requested to develop sustainable steel production process and produce “green material”. Recently, authors have proposed the innovative hydrogen production process, in which water vapor is reacted with discharged steelmaking slag to produce hydrogen gas. This reaction can be achieved without any external energy source and operated by huge thermal energy associated with steelmaking slag and FeO or unrecovered Fe droplets that are relatively rich in the slag. In this paper, thermodynamic calculation results with various initial conditions in terms of hydrogen productivity were presented. Laboratory-scale experiments were also conducted to clarify the validity of thermodynamic calculation and the reaction rate in realistic conditions.IntroductionIronmaking and steelmaking process from iron ore through blast furnace and BOF is an essential steel production route for Japanese steel industries to supply high quality steel products in large quantity to society stably. Blast furnace – BOF process requires huge amount of fossil fuels such as mainly coal, resulting the emission of considerable amount of CO2 gas. Since the emission of CO2 gas from steel industries, about 147 Mt (FY2011), accounts for approximately 12 % of domestic CO2 gas emission in Japan (FY2011),[1] it is an urgent issue for steel industries to develop environmental-friendly ironmaking and steelmaking process and reduce CO2 emission. Various kinds of gases and by-products generated from ironmaking and steelmaking processes have been recycled as much as possible at present. Enormous thermal energy is also generated from processes and released to surrounding atmosphere as various forms such as sensible heats of gases, molten steels or by-products, and as heat losses. However, these energies are not utilized before final dissipation to atmosphere. Although various technologies to utilize thermal energy from ironmaking and steelmaking processes have been attempted to develop, practical application of these technologies has not been achieved because the thermal energy is not always useful as an energy source. In steelmaking process by BOF, fluxing agent such as CaO is added during reefing and thus about 100 kg/t-steel of steelmaking slag are generated. Since the steelmaking slag is discharged at temperature range between 1873 and 1923 K after discharge of refined molten steel, it also has large thermal energy. Amount of generated BOF slag is 11.0 Mt/y (FY2012) in Japan.[2] Assuming the amount of steelmaking slag is 10 Mt/y and its average heat capacity from room temperature to 1923 K is 1 kJ/kg·K,[3] unutilized heat is estimated to be 16 PJ/y, which is equal to annual energy consumption of 420 thousand families in Japan.[4]"

Jan 1, 2014

By Francois Reizine

Infrared sensors will include scanning detectors and positioning sensors. The focus will be on 1, 2, and 4-color wavelength pyrometer systems which allow the accurate measurement of emissivity and, consequently, of the true temperature even in the presence of scale, slag, and fumes. Such sensors are being used in blast furnaces, BOF's, and galvanizing lines. Laser sensors will be presented using different principles of physics, mainly time-of-flight, pulsed infrared lasers for level measurement and dimensional measurement; triangulation lasers for width and thickness measurements; and laser Doppler velocimeters for velocity and length measurements, including mass flow, elongation, and tension control, cut-to-length applications. These sensors and systems are based on state-of-the-art technical developments to improve productivity and quality and reduce maintenance and downtime.

Jan 1, 2001

By Susanne Pignolet-Brandom

Fourteen samples of crushed Duluth Complex rock were characterized by the QEM?SEM automated scanning electron microscope image analysis system to evaluate the application of the system to mining waste rock characterization. The system can reliably distinguish the iron sulfides, the copper-iron sulfides and the nickel-iron sulfides. Calcite was distinguished from all other minerals except fluorite. The volumetric abundances were verified by comparing elemental abundances calculated using the QEM"SEM volumetric percentages and appropriate mineral compositions with elemental abundances determined by standard laboratory procedure. The pH and sulfate concentrations of rinse water from laboratory leach experiments correlated well with the mineralogical data.

Jan 1, 1989

By Bingyi Bai, Lifeng Yang, Yanling Guo, Jieyu Zhang, Guoding Gao

In terms of special resources with iron, niobium and rare earth coexisting in Baiyuneboite, the new smelting technology of ferrocolumbite was studied. Reduction experients for the Baiyuneboite and explores ore phase change of Baiyuneboite in the process of reduction was conducted with graphitic carbon as the main reducer and a temperature below 1000 ℃. Moreover, it studies the influence of reducer, roasting temperature and grind fineness on the reduction as well as focuses on the evolution course of iron phase. Through the analysis on in-situ XRD of the raw ore and carbon addition ore, it also develops microstructure change rules of Fe ore phase and ore phase of paragenetic elements for composite ore(Ca, Si, Nb, F) in the process of reduction roasting. In addition, the impacts of temperature on the reduction process are also discussed. With regard to minerals of different particle sizes, the thesis will explore their ore phase changes and microstructures after 10 hours’ reduction under 900 ℃.

Jan 1, 2015

Studies of electric pulse (EP) disintegration were conducted on ores of disseminated precious minerals, 'on platinum-bearing chromitites of the Konder Complex, Russia, on diamond-bearing impactites of the Popigai meteoritic crater, Russia, and on and diamond-bearing metamorphic rocks of Northern Kazakhstan. It was shown that EP disintegration ~s a technology that achieves ideal liberation of disseminated minerals, and is a new efficient method to study accessory minerals.

Jan 1, 1991

By J. J. Kim

In a study of buildup in a green-feed reverberatory furnace, it was determined that approximately half of the crucible area has a moderate buildup of 25 in. or less, and that the area extending 45 f t from the burner end of the furnace has only a slight buildup. The false bottom, averaging 6 in. in thickness, was found to cover the entire crucible area. The stratification of Cr2O3, A12O3, and SiO2 occurs throughout the slag layer; this phenomenon is the principal reason for the formation of the false bottom in the green-feed reverberatory furnace. The false bottom is caused primarily by the settling of FeO*(A1,Cr),03 aggregates, which are derived mainly from returned converter slag. The false bottom can be transformed to a solid permanent buildup in the furnace, particularly when the matte is completely withdrawn. From the material balance of Al2O3 and Cr2O3 around the furnace, It is estimated that the average rate of aluminum chromite accumulation is approximately 0.3 ton per day or less.

Jan 1, 1976

By U. Lauwers

The influence of different waste materials in sinter blends on the quality and mineralogical composition of a sinter is described. As a result of partial preservation of the original textures of waste materials in the final product the degree of assimilation of the original material in the sinter product can be ascertained. Recycling of waste materials such as dolo char , arc-furnace slag, scrap fmes, mill scale and BOF-mud via the sintering process a saving on costs of raw materials such as flux and fuels, and a reduction on pollution can be achieved. A comparison of a typical sinter with a sinter produced through the utilization of waste materials showed a distinct correlation between certain types of waste material and some metallurgical properties. Dolochar in a sinter blend acts as part of the fuel and flux that are normally added to a sinter mix. Generally dolochar improves the quality of the sinter and decreases the consumption of coke. Other waste materials adversely influence the quality of the sinter. The glass and calcium ferrite content of a sinter when dolochar is used in the blend is similar to that of a sinter produced with only coke as a fuel in the sinter mix. The glass content is lower and the calcium ferrite content is higher, in a sinter produced from dolo char in the blend compared to a sinter produced with additions of other waste materials. Changes in the mineralogical composition are related directly to the metallurgical properties of the sinter product.

Jan 1, 1991

By M. Hashimoto

The equilibrium distribution ratios of sulfur between molten copper and CaO-fluxes containing caF2 and caC12 were determined in the range of 1300° to 1400° C under carbon monoxide. The rate of approach to equilibrium is rapid and increases with increasing CaCll concentration. In CaO-CaFl-CaCl2 fluxes, the distribution ratio varies in a complex way with temperature and CaFl concentration. The results are compared with those obtained with the binary fluxes of CaO with BaFZ and MgFl ?

Jan 1, 1983

By Fuming Wang, Xin Lu, Hao Bai, Hebin Zhu

"In this study, CO2 emissions and carbon footprint of a typical steel works with integrated process and iron and steel industry in China was calculated and analyzed by a carbon footprint method based on the model of process CO2 emissions in iron and steel making. The carbon footprint of iron and steel industry from 1991 to 2010 in China showed a rapid increasing tendency. In 2008, the CO2 emissions of iron and steel industry in China was 1.289 billion tons, 19.71% of the national total CO2 emissions, and the corresponding carbon footprint was 159.13 million hm2 of green area. Carbon deficit of iron and steel industry also go up gradually if considering the carbon storage by green vegetation. Thus, the internal carbon reduction strategy, such as energy structure optimization and energy saving technology, was mainly encouraged for the sustainable development of iron and steel industry in China.IntroductionThe Global Warming resulting from the increase of Greenhouse Gases (GHGs), in particularly CO2, in the atmosphere has become the main reason of global climate change, and large emission reductions are required for sustainable development [ 1]. The iron and steel industry is the largest energy consuming manufacturing [2] in the world and the largest emitter of CO2 emissions. In 2005, it accounted for about 20% of global industrial energy use and 30% of energy and process CO2 emissions from industry [3]. In China, the crude steel has firmly been ranking at first of the world recent years and kept growing tendency year by year. With the production growth, the CO2 emissions of iron and steel industry also increased significantly and hence the steel industry has become one of the most sources of CO2 emission in China [4], which has attracted more and more attention to seek the carbon reduction strategies.Carbon footprint is an important and useful concept originating from Ecological Footprint, which was used efficiently to quantitatively analyze the impact of the human activities on ecological system, in particularly impact of the human energy activities [5]. In the view of Life Cycle, the carbon footprint is efficient to analyze the direct and indirect CO2 emission in the whole life of various products used in human activities. As to the iron and steel, the important materials and products in the human life, the carbon footprint analysis is quite necessary to evaluate the CO2 emission impact on the corresponding ecological system and global environmental."

Jan 1, 2013

By Z. Zak Fang, P. Fan, S. Middlemas

"Titanium dioxide (T1O2) has been widely used as pigment in paints, paper and cosmetic products, as well as high-tech applications such as PV Cells, semiconductors, biomedical devices and air purification. T1O2 pigment is primarily produced by the high temperature chloride process, resulting in considerable CO2 emissions. A novel hydrometallurgical process for making T1O2 pigment without direct CO2 emission is investigated. The new method promises to eliminate direct CO2 emissions, consume significantly less energy, and produce minimal environmental waste. The novel process involves molten salt roasting of titania slag, with subsequent washing, leaching, solution purification, hydrolysis, calcination and post-treatment stages, resulting in high-purity anatase or rutile pigments while realizing significantly reduced environmental impacts. Pigment whiteness is critically sensitive to trace amounts of discoloring impurities such as iron and chromium. Several methods for reducing the levels of these impurities are investigated. Energy consumption and emission models are also developed.IntroductionTitanium dioxide (T1O2) is one of the most commonly used minerals in the chemical manufacturing industry. It has been commercially processed since the early 1900's, and has a wide variety of applications. Pigment is used in paints [1], plastics and paper [2], sunscreen [3], cosmetics and even as a food additive [4]. T1O2 has also been used in photovoltaic cells [5], biomedical devices [6], and in air purification [7]. T1O2 pigment has a refractive index of 2.7, which imparts a high level of opacity (and hence whiteness) to whatever material it is added [8]."

Jan 1, 2012

By Jorge Alberto Soares Tenório, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Franco Alves Lavacchini Ramunno

"The traditional process for recovery of metals from waste electric and electronic equipment (WEEE) usually involves pyrometallurgical processing. However, the application of this technology to processing waste printed circuit boards (WPCBs) might lead to the formation of dioxins and furans, due to thermal degradation of flame-retardants and polymeric resins present in the board substrate. Therefore, this paper proposes a hydrometallurgical route for the recovery of copper. The acid leaching behavior of copper has been investigated at three different temperatures (25°C, 50°C and 75°C) with and without the addition of an oxidizing agent (hydrogen peroxide - H202). The dissolution kinetics for acid copper leaching was calculated based on chemical analysis by ICP-OES (Inductively Coupled Plasma - Optical Emission Spectroscopy). At 50°C with 1 mol/L H2S04 added 10 mL H202 (30%) each half hour under pulp density of 1 g I 10 mL, 100% of copper was extracted after 3 hours. The dissolution kinetics of copper with H2SO4-H2O 2 followed 1 - (1 - X)113 =Ket, i.e. chemically controlled reaction model.IntroductionThe information regarding the generation of waste electric and electronic equipment (WEEE) are still difficult to obtain because the estimates should take into consideration the historical production and sale of various products and the rate at which they reach the end of their life cycle, whose duration depends on the behavior of consumers [1]. Thus, the estimated overall WEEE generation varies between 25 and 50 million tons each year, which corresponds to more than 5% of all municipal waste generated [2], and this amount will increase at a rate of 3 to 5% per year, approximately three times faster than other individual types of waste [3].Printed circuit boards (PCBs) are essential parts of electric and electronic equipment (EEE), being found in virtually all electronic products, as well as in weapons systems [4]. A PCB is a basic component, which consists of a board where copper tracks are deposited. While the board behaves as an electrical insulator, the tracks connect electrically the various components attached to the board [ 5]. In addition to glass fibers, paper and resins, the PCBs contain significant amounts of metals, such as copper, iron, nickel, lead, stain, silver, gold and palladium [6]. In general, the weight fraction of metal is around 28% and the remainder of the boards is composed of plastic (19%), bromine (as flame retardant - 4%) and ceramic material (49%) [7]."

Jan 1, 2014

By T. Innmi

The potential of the nickel matte anode was measured during the matte electrolysis in the commercial cell. The slime layer consists of elemental sulfur and was found to greatly influence the potential of anode. The measurements of porosity and permeability of the slime suggest that the voltage drop of the slime layer dominates the potential. Furthermore, the diffusion of the electrolyte through the slime layer is also one of the factors to determine the potential. In addition, the copper content of the nickel matte anode was found to affect the change in the anode potential during the electrolysis. The role of copper on the anodic dissolution of nickel matte is discussed in this work.

Jan 1, 1988

By Y. Ono

In lightweight metal processing such as aluminum (AI) and magnesium (Mg), metal cleanliness is a crucial process parameter for refining, part manufacturing and recycling in order to obtain high quality parts and products. In this paper, techniques for cleanliness evaluation of molten AI and Mg using ultrasonic probes with clad steel buffer rods having high signal-to-noise ratio (SNR) are presented. Due to the high SNR of the ultrasonic probes used, backscattered ultrasonic signals from inclusions, which may be oxide films and/or particles, in molten Mg and those from silicon carbide particles, having an average size of 50f.Ull, added in molten AI are successfully detected with reflection configurations of pulse-echo and/or pitch-catch modes at an ultrasonic frequency of 10 MHz. In addition, relative cleanliness evaluation of molten Al and Mg is demonstrated. In order to establish the procedure and to investigate the optimum system configurations for cleanliness evaluation of molten metals, particle flow simulation system using water and polyvinyl chloride (PVC) particles has been constructed. Counting the number and measuring the size distribution of the PVC particles, having an average diameter of 128um, suspended in water with the PVC volume concentrations of 5ppm and 10ppm are performed with ultrasonic pitch-catch mode. The counted numbers of particles by the presented method and system have good agreement with the calculated results with a count error of less than 10% or two counts. Based on the results obtained with water simulation experiments, the prototype system for cleanliness evaluation of molten Mg by counting and sizing inclusions has been developed. Keywords: Ultrasound, Clad buffer rod, Molten metal, Aluminum, Magnesium, Inclusion detection, Cleanliness measurement, Counting, Sizing

Jan 1, 2003