As a leading global company in the mining sector, we are committed to sustainable development. To this end, we invest in the responsible, integrated management of economic, environmental and social issues. Vale?s objective is for our businesses to produce local, regional and global prosperity, enabling the construction of a positive legacy throughout the lifecycle of our activities. This covers everything from talking with stakeholders and preventing failures to complying with legislation, paying constant attention to environmental issues and respecting ethics in business. Keywords: sustainable development

Sep 1, 2012

By Vasily V. Lodeischikov, Adolf F. Panchenko, Olga D. Khmelnitskaya, Vladimir E. Dementyev

Pilot plant tests of underground gold leaching from Maminskoye deposit oxide ores at a grade of 0,7 g/t Au were carried out. The underground leaching flow sheet includes Au dissolution by chlorine-containing solutions, Au adsorption from solution on active carbon, carbon concentrate ashing and calcine melting to produce high grade gold concentrate. The underground leaching system throughput was 15 m3 of solution per hour. Gold concentration in pregnant solutions was 0.12-0.13 mg/l. Gold recovery from solutions into carbon was in the range of 63-84%. It was demonstrated that the low Au recovery in the adsorption cycle was due to the presence in pregnant solutions of "active" chlorine, which destroys active carbon and causes a sharp decrease of the carbon loading capacity for gold. To improve the adsorption indices, previously dechlorinated pregnant solutions using bituminous coal or Na2S2O3, is recommended. Ion exchange process was tested as an alternative for gold extraction from dechlorinated solutions. In the testwork period, 4.4 kg of gold were produced with a chlorine consumption of 3.5 kg per 1 g of gold. During the tests a program of environmental protection measures was completed to provide the necessary safety precautions of the underground leaching works.

Jan 1, 2003

By M. Q. Xu

During the flowsheet development for a potential commercial Cu/Ni separation plant at the In-co?s Sudbury operation, extensive laboratory and miniplant studies were carried out. There are two potential feed streams for Cu/Ni separation at the existing operation. It is shown that Cu/Ni separation from the rougher concentrate is relatively simple without need of regrind. However, Cu/Ni separation can be difficult from the bulk concentrate because of the presence of excess flotation reagents in the bulk concentrate slurry and locked particles. Excess flotation reagents created excess froth increasing entrainment. By replacing the slurry water with tap water and with addition of some hydrogen peroxide, entrainment is minimized and good Cu/Ni separation is achieved on the bulk concentrate. Fine regrind is required to increase liberation of the locked particles for ultimately high copper recovery at the minimal nickel content.

Jan 1, 2014

By J. Roth

The increasing demand of the filler industry regarding fineness and better delaminated products led to the development of a series of different grinding machines, which differentiate basically by the grinding mechanism as well as the kind of classification. Spiral jetmills grind, as it is well known preferably by delamination, therefore a spiral jetmill with integrated dynamic classifier has been developed. Especially the enhancement of the functional properties of the used industrial mineral fillers is a factor of highly increasing importance. These properties are very often bound to the platy shape of the minerals expressed by the aspect ratio. The developed Spiral Jetmill shows sufficient ability for such delamination and therefore increases in aspect ratio. In a series of comparative tests the suitability and advantages of this system regarding achievable fineness down to the submicron range as well as the conservation or even improvement of the aspect ratio of different minerals has been studied. As an emphasis on the results application tests with certain materials in the plastics field have been conducted. Due to the fact that in this range the required specific energy for achieving the necessary fineness increases exponentially another target is to optimize the grinding efficiency. A special feed control system provides on one hand a sufficient load inside the mill to obtain maximum utilization of the applied energy and on the other hand to prevent the mill from overfilling and coming with this a poor classification. The integrated classifier is a combination of a high speed motor with directly attached classifier wheels. This unit on one hand grants the necessary high circumferential speed of up to 190 m/s for providing an exact top cut of the ultrafine products and on the other hand gives the required operational reliability for continuous operation. Hard grindable impurities, which enrich inside the mill chamber, can be rejected from the process leading to an even cleaner product. Comparative tests on a talc product with certain free quartz impurities showed a significant improvement of the final product with respectively low loss on rejected material. This effect again had a beneficiary impact on the suitability of the final product when used in plastics application.

Jan 1, 2014

By V. V. Trusova, Shiyrav Gandandorzh, K. V. Fedotov, V. A. Domracheva

"In Russia, 1.1 million tons of mercury-containing waste are stored. The amount of mercury in soils and heaps of industrial enterprises is estimated at 3000 tons; in dumps, concentration tailings, sludge dumps of the gold mining industry up to 6000 tons have been accumulated. Mining is one of the main sources of mercury emissions in the natural environment that poses a real threat to the natural environment. At present, the process of amalgamation is prohibited and not applied in gold extraction. The application of amalgam technology in gold mining led to the accumulation of highly toxic products in the form of gold-bearing amalgam and metallic mercury, with a mercury content of dozens and even hundreds of times greater than the maximum permissible concentration for soil (1). Therefore, mercury-containing tailings constitute an ecological hazard to the environment. According to published data, at waste storage sites of industrial enterprises, up to 50 tons of mercury enter soil annually, and up to 3.5 tons pollute the air. At the same time, mercury-containing waste due to the reduction of the country's mineral resources is an additional source of mercury. Therefore, it is necessary to recycle mercury-containing waste. INTRODUCTION Paperobjective: demercurization of technogenic raw materials (amalgamation tails, discharge outlets of tailing dumps) to be recycled. Under natural conditions, the mercury usually migrates in the form of three most common compounds: elementary mercury (Hg); mercuric mercury ion (Hg+2); methylmercuryion (Hg (CH3) +. Chemical compounds Hg (II) are found in natural conditions much more often than Hg (I).The authors propose to conduct demercurization of technogenic raw materials (mercurial tailings) in two stages. At the first stage, the mercury in the form of small balls, the finest particles (drip mercury) can be extracted by applying the gravitational method. We propose a method for centrifugal processing of crushed waste in the apparatus of Itomak company, Novosibirsk, as the basis of the technological process for mercury recycling. The extraction of metallic mercury out of mercury-containing waste into commercial products, according to the technological characteristics of the Itomak apparatus, reaches 86.0% (2, 3). At the second stage, the extraction of mercury out of technogenic raw materials is performed applying a sorption method and using carbon sorbents based on fossil coals. Hard coal of the Kuznetsk Basin has been already used for industrial production of active carbons (carbon sorbents) of the KAD-iodine type, which is one of the prerequisites that determine the choice to use it for the aims of this study."

Jan 1, 2018

By Christopher Davey, Professor Emeritus, Marian Mazurkiewicz, Peter Kanjorski

The concept of a high pressure liquid jet mill with highly unsteady flow, has been developed and recently patented by Cornerstone Technologies LLC (CsT), for the purpose of micron and sub-micron particle production. The mill accepts feed sizes up to 15mm for some materials and is capable of sub-micron production. Successful material range from precious metals such as silver and palladium to dielectric components and substrates such as Barium Titanate slips, zirconia, titania and silica. The process has also succeeded in adequately reducing the size of materials for both composite and coating uses such as anthracite coal, graphite, chrome metal, wollastonite and more than 100 others. A unique design approach has been taken to highly maximize the energy flux in the mill’s chambers to create extremely high turbulence and destructive cavitation. This is assisted by shock waves, which cause particles to undergo ultra high frequency pressure pulsations, high frequency collisions and then abrasion, shattering, hydro-wedging, and cleaving. Due to these extreme properties the processing occurs in just fractions of a second allowing throughputs up to 1000 kg/h on a machine that would fit inside a 60 cm box. The technical solution and technological advance, as well as the environmental and economic benefits indicate rapid and wide spread acceptance of high-pressure liquid jet milling in modern industry.

Jan 1, 2003

By V. Sheikhzadeh, M. Saghaeian, R. Hejazi, M. Zare

High Pressure Grinding Roll (HPGR) plays a major role in increasing specific surface area of iron ore concentrate for producing pellet feed. HPGR grinding mechanism implies that material be compressed between the two rolls, therefore layer of material must be able to resist required pressure for achieving suitable grinding conditions. In this study for determining a simple relationship between material pressure resistance ability and HPGR main design parameters, piston press tests were performed on different iron ore concentrate samples along with HPGR Blaine increasing tests. Piston press tests results showed that by decreasing moisture content, material pressure resistance increased and in constant moisture content this parameter will change based on material specifications. HPGR Blaine increasing tests results showed that by decreasing moisture content, HPGR specific throughput and working gap increased and in constant moisture content this parameter will change based on material specifications. For all of the studied samples at worst condition, we got the results including: HPGR delta gap equal to zero, specific throughput lower than 200 ts/hm3.According to the tests results, HPGR Applicability Index (HAI) can be introduced at four different class types from 1 (weak) to 4 (excellent). This index determines achievable specific throughput and possibility of using HPGR according to material specifications, i.e. for HAI 1-4 the pressure resistance is <90, 90 to<125, 125 to <150 and = 150 bar, respectively. Similarly for HAI 1-4 specific throughput is <200, =200, =220 and =250, respectively. So based on design moisture content, if concentrate HAI is 3 or 4, HPGR is a correct choice. For HAI 2, HPGR can also be used. But for a material with HAI equal to 1, HPGR is not a good solution. As a result in order to apply HPGR for HAI 1, material condition such as moisture or slime content should be decreased.

Jan 1, 2018

By S. M. Saghaeian

The studies on the product finer than 12 mm due to crushing and sizing plant of Gol-e-Gohar Iron Ore mine showed which this material contains significant amount of valuable iron minerals. Based on the carried out experimental studies on representative samples of fine hematite iron ore, a processing flow sheet was designed to upgrade iron content. This plant is known as first hematite iron ore enrichment plant in Iran which the dry medium intensity magnetic separators (with magnetic field intensity 4500 gauss and high gradient) has been used. The main objective of the plant is production of high iron product with iron content more than 61% and weight recovery more than 55% from the feed with iron content of 54%. In this plant, at first material are screened by a single deck screen (6mm), then oversize particles is separated at one stage by magnetic separator, while undersize ones at two stages. Based on the results of experimental tests, a final high iron product with iron content of 62.4% and weight recovery 63.9% can be achieved. It should mention which the iron content can be enhanced through increasing the speed of magnetic separators especially at the part of separation of finer iron ore.

Jan 1, 2014

By Hamid-Reza Manouchehri

"Sustainability calls for maintenance, rational use and enhancement of natural resources as well as balance consideration of ecology, economy, and social justice. The challenges in mining industry call for a sustained global effort using the leverage of available technologies and emerging new technologies. The industry uses significant amount of energy with the highest portion in comminution. To conserve energy, attempts have been made to improve the efficiency of the conventional crushing and grinding equipment. Nevertheless, the new and energy efficient comminution technologies are favorable through a longer term strategy. Since crushers are more energy efficient than mills, it is logic to conduct part of milling, in the crushing stage. After years of research and development, Sandvik introduces a new crushing technology, VibroconeTM, to change traditional crushing concepts. The new crushing device is able to crush and grind particles with a higher reduction ratio, more than two fold, than that of conventional crushers. By implementation of the new technology, a suitable feed size for milling can be provided to conserve energy as well as media and liner consumption, to reduce milling circulating load or increase mill capacity. There are other benefits associated with this machine, one of them being providing a higher surface area. This paper discusses the performance of the machine and its applications for comminuting different ores."

Jan 1, 2014

By X. Q. Wu

Magnetization in slurry (MIS) of weakly magnetic minerals by iron ions was investigated. The magnetic seeds (strongly magnetic particles) were synthesized by ferruginous chlorides directly in slurry instead of previous preparations of magnetic seeds by finely grinding mineral magnetite or specially synthesizing them separately in an aqueous solution. In this way, the growth of the seeds and their adsorption on the minerals simultaneously take place in the same slurry. That after MIS the recovery of weakly magnetic mineral limonite in a magnetic separator increased means the formation and adsorption of magnetic seeds on the surface of iron mineral limonite. The magnetization effect was evaluated by limonite recovery at a magnetic strength of 3.500 Gs in a magnetic separator. Mineral limonite was properly magnetized in the following slurry condition: molar ratio of Fe3+ to Fe2+1:3, slurry temperature of 45 °C and pH 10.5. The selectivity of the magnetization between minerals limonite and quartz was improved by adding surfactant sodium oleate.

Jan 1, 2014

By Tohru Kamo, Shigeyuki Katano, Hideki Nakagome, Maiko Adachi, Shingo Nakamura, Kaneshi Taniguchi, Zar Zar Hlaing, Takaaki Wajima

Tantalum capacitor is a small-sized and has large capacity, and is indispensable for electric equipment. The demand increases year by year, and a quite large number of used tantalum capacitors is generated. Recovery of tantalum from tantalum condenser is recently important since production of tantalum have not been stable for the price and the quality. However, recovery of tantalum from tantalum-condenser is difficult since tantalum parts strongly cover with the flame retardant resin made of halogenated compound (mold resin). This research investigated recovery of tantalum parts from tantalum condenser using steam gasification with mixed molten carbonate. Mixed molten carbonate (Na2CO3:K2CO3:Li2CO3 = 1:1:1) (3 g) put into the reactor, and heated with electric furnace while flowing nitrogen (160 mL/min) and steam (1 mL/min) warmed by heater. After heating to setting temperature (450 - 650 oC), tantalum condenser (3 g) was put into the reactor, heated for 5-10 min, and then cooled to room temperature to recover the reacted capacitor by filtration after treating with distilled water. At relatively low temperature (550 oC) heating for 10 min, mold resin can be decomposed by using steam gasification with mixed molten carbonate, in comparison with using pyrolysis and steam gasification without carbonate, and decomposition reaction occurred over 500 oC by using steam gasification with mixed carbonate. Recovery of tantalum parts from capacitor is successful using steam gasification with mixed molten carbonate at 530 oC for 5 min, due to the effective decomposition and removal of mold resin from capacitor. Furthermore, most halogen gas generated from decomposition of mold resin can be trapped in molten carbonate not to exhaust halogen gas. These results suggested that recovery process of tantalum parts from used condenser using steam gasification with mixed molten carbonate is expected as a feasible way to recycle the rare metal in electric equipment.

Jan 1, 2014

By S. S. Lu

In sodium oleate and salicylhydroxamic acid systems, sequence of floatability of three sulfate minerals is: barite>celestite>gypsum, in lauryl amine system is: gypsum>celestite>barite. XPS and infrared spectrum analysis are used to find that it is chemical reaction between sodium oleate and three minerals, physical adsorption on the surface of minerals for lauryl amine, and it is chelating reaction between salicylhydroxamic acid and three minerals possibly. Theoretical calculation on chemical bonds in crystal structures of three minerals is carried out, finding that breaking degree of Mn+?O2- in crystal structures of three sulfate minerals is closed related with floatability.

Jan 1, 2014

By Rogerio C. Guimarães, Antonio E. C. Peres

The production of phosphate concentrates (phosphate rock) from slimes represents a challenge to the phosphate industry worldwide. In Brazil, this challenge is particularly relevant due to the consistently low P2O5 grades and the igneous origin. The first industrial experiences of producing phosphate rock from slimes (-44µm or -325#) fraction started at Arafertil, currently Bunge Fertilizantes SA, in Araxá, in the 1980.s. This production corresponds, nowadays, to 35% of the total production of concentrates in the company (830,000t/year) in a circuit consisting of desliming in 40mm microcyclones and concentration in flotation columns, corn starch and fatty acids being utilised as reagents. The performance of slimes flotation and the process control, at Bunge´s concentrator, were improved after the introduction of column flotation technology, in the first half of the nineties. The column flotation technology for slimes recovery was expanded to other Brazilian concentrators still in the nineties: Ultrafértil (Catalão - GO), Bunge (Cajati - SP), Fosfértil (Tapira - MG) and Copebrás (Catalão - GO). At present the Brazilian production of phosphate rock is approximately 4.5Mt/year, with a strong trend for a market increase. Genuinely Brazilian technology is utilised for the processing of slimes, the concentrates representing 11 to 13% of the overall production. The production of apatite concentrates from slimes was relevant to increase phosphate recovery and reduce costs, contributing to the growth of the fertilisers industry.

Jan 1, 2003

By Arkady Senchenko, Yuri G. Seredkin, Alexander Aksenov

"This paper describes the development of efficient technology for the treatment of complex ores containing gold and copper as major valuable components, where silver is present as well. Copper is mostly represented by oxidized minerals in these ores; however, copper sulfides are also present. Gold is present in its free form and in associations with oxidized and sulfide minerals; silver usually accompanies gold. Complex composition of the ore requires complex solutions for their treatment. The results of searching for the techniques to recover valuable components are described in this paper. Gravity methods allow for free gold recovery, flotation methods allow one to recover major part of copper and precious metals in associations; and in the result of leaching process additional amount of copper, gold and silver is reported to solution. Combining all these methods help achieving high levels of valuable components recovery. When implementing a combined technological flowsheet about 80 % of copper goes to concentrates from gravity and flotation of sulfide and oxidized copper minerals; and sulfuric acid leaching allows increasing total copper recovery up to 90 % and higher. Major part of precious metals (up to 90 % of gold and 80 % of silver) is recovered to these concentrates, and after hydrometallurgical treatment it is possible to increase gold recovery up to 96 %, silver recovery - up to 90 %. The suggested technology helps solving the problem of precious metals recovery from complex gold-copper ores, and allows treatment of the ore with different proportion of sulfide and oxidized minerals, and at different valuable components grade."

Jan 1, 2014

By B. Gorain, O. A. Bascur

"The advent of digital revolution has now enabled us with numerous tools that could be leveraged to transform our operational data into actionable insights. Key opportunities with digitization include better visualization, transparency, integrated planning and execution for value-chain optimization, that results in smarter production, intelligent response to changes in ore, process and equipment conditions, reduce energy and waste along with prevention of asset breakdown, safety and environmental issues. It is important to realize that these digital tools have limited value, from a metallurgical operational context, if we cannot bring-in the appropriate domain expertise along with getting the basics right. The focus within Barrick is to ensure that there is adequate depth of different disciplines built into our platforms along with breadth to integrate other disciplines such as geology and mining for an effective Mine-to-Mill integration. A gold recovery improvement strategy based on optimal Gaudin size distribution, leaching performance monitoring and guidance via feed grade maps is discussed. Simultaneous identification of process and equipment constraints enable finding the best overall conditions for Gold recovery. This paper discusses the methodology, findings, and challenges in the ongoing journey of implementing a Metallurgy Analytics platform that evolves from being retrospectively descriptive to anticipatively prescriptive.INTRODUCTION The last few decades have seen some remarkable advancement in information technology, but recently various digital technologies have resulted in several synergies to deliver innovation in diverse applications. The mining industry has been relatively slow in adopting these technologies compared to the other industries, but this scenario is changing fast. Mining companies globally are going through a series of challenges such as declining ore grades with complex metallurgy, increasing depth of ore bodies, high capital and operating costs, lower productivity, shortage of technical resources, significant pressure from stakeholders to deliver, along with growing environmental and corporate social responsibility issues. Improvement in profitability would need significant improvements in operational performance."

Jan 1, 2018

By Shuji Owada, Yang Geng, Natsuko Kuroki

Micro-bubble flotation is considered to be an ideal method for the separation of fine or ultra-fine particles, which are difficult to be separated with conventional flotation and other solid separation technologies. Micro-bubble flotation can increase the probability of bubble-particle collision more than conventional milli-bubble flotation. However, there are also some problems. For example, it is known that the rising velocity of micro-bubble is quite low; therefore, the flotation rate reduces. And also, the bubble-particle adhesion probability becomes lower than that of milli-bubble flotation, which is proved in our prior research. In this paper, we applied ultrasonic irradiation to the micro-bubble flotation system in order to solve the above problems and focused on the bubble-bubble and bubble-particle interactions. For clarifying the behavior of bubble-bubble interaction, bubbles behavior was recorded by high-speed camera under irradiation of various ultrasonic frequencies. As a result, in the case of bubble-bubble interaction, it is proved that bubbles are highly coalesced by ultrasonic irradiation especially in the lower frequency and it can enhance more precise separation. In the case of bubble-particle behavior, it is found that the floatability become higher with the ultrasonic irradiation of higher frequency, and it is indicated that ultrasonic irradiation might improve the bubble-particle adhesion probability. Additionally, it is also found that the apparent CMC of the micro-bubble flotation under the ultrasonic field become much lower with higher frequency than with lower frequency, and it is suggested that the dramatic improvement of hydrophobization is achieved.

Jan 1, 2014

By K. Sasaki, H. Miki, Y. Muta, T. Hirajima, G. P. W. Suyantara

"Selective flotation of chalcopyrite and molybdenite is continuing problem since its selectivity is not perfect and current NaHS process needs closed system flotation plant because of hydrogen sulfide emission on acidic condition. Some alternative additives investigated as chalcopyrite became hydrophilic and molybdenite kept hydrophobic. XPS analysis indicated chalcopyrite became hydrophilic since iron and copper sulphate, hydroxide was covered on the surface whereas molybdenite kept hydrophobic since only molybdenite can be seen. Flotation experiments of chalcopyrite and molybdenite mixture sample indicated excellent separation that 95% of molybdenite can be recovered as froth and 93% of chalcopyrite can be recovered as sink. Flotation experiments with real bulk flotation concentration indicated similar separation result compared with current NaHS additive system. Possible mechanisms and detailed phenomenon were investigated based on the surface analysis and thermodynamic calculation etc. this alternative additive is easy to handle compared with NaHS since it does not emit effluent gas and commercially preferable.INTRODUCTIONMany copper mine often associates molybdenite (MoS2) as trace mineral. It is important to separate molybdenite and copper mineral efficiently since molybdenite is valuable mineral and also contamination of molybdenite into copper concentrate decrease concentrate value. Conventional separation of copper sulfide and molybdenite has been achieved with sulfide bulk flotation followed by selective molybdenite flotation with NaHS addition since NaHS works as a depressant for copper sulfide (Bulatovic, 2010; Ansari and Pawlik, 2007b). However, this current process shows imperfect molybdenite recovery (Liu et al., 2012, Zanin et al., 2009) and depressant such as NaHS needs to be used under specific flotation plant since it might be environmental contaminant (Ansari and Pawlik, 2007a). there are still unknown on the effect of depressant NaHS, but one of the theory is NaHS reductant effect. It is worth to investigate the effect of other reductant as depressant on chalcopyrite. On this research, typical reductant, Na2SO3 are added to utilize for selective flotation of chalcopyrite and molybdenite."

Jan 1, 2018

By Ray Everson, Henry Kasaini

"Adsorption of Pd (II) anions on the surface of activated carbon (Norit 0.8) occurred at high proton concentration (0.01 – 2.5M, HCl) in the feed and averaged 27 mg/g. The adsorption process was interpreted in terms of surface ionisation and adsorption model. Enthalpy of adsorption averaged 0.4 kJ/mole indicative of an instantaneous physical adsorption process. We found that the Toth isotherm fit the adsorption data fairly accurately. A combination of the Langmuir and Freundlich equations yields an effective three-parameter Toth equation (1) which is frequently used to describe adsorption on heterogeneous surfaces.Figure 1 shows the comparison between experimental results and the model isotherms. We found that Langmuir isotherms underestimated the adsorption capacity on the porous surface while the Freundlich isotherm overestimated adsorption. Furthermore, the surface coverage at equilibrium was well described by both the Langmuir and Toth isotherms. But, Freundlich isotherm predicted a surface fraction coverage that was higher than unit. Based on better prediction of surface coverage and a reasonable fit to adsorption data, we concluded that the Toth isotherm best described the adsorption data of palladium. The adsorption process was limited by mass transfer resistance through the external film. We estimated the rate constant from equation (2), where e, ?b, and rp are porosity, fluid density and particle radius, respectively"

Jan 1, 2003

By P. Somasundaran

While sustainability itself needs to be redefined in a selfless way, methods of measuring and optimizing it also need to be reformulated. Gone are the days when we had the luxury of abundant resources and the freedom to extract values in self-centered ways. In the past, focus has been mostly on reagent performance, processing operations, and upgrading of tools to maximize rather than optimize value extraction from the earth&apos;s crust. Today we as extractors face a new set of challenges that include value separation from low quality resources including wastes, but within the energy, environment, and societal constraints. Development of such technology depends on understanding the role of entities and concepts such as bio-molecular interactions at surfaces, forces involved in inter-granular versus intra-granular fracture in new fragmentation methods, robotic in-situ or extraterrestrial mining, exploiting new membrane and nano technology, use of new sensors and actuators for detection and separation and computation capabilities for faster and economical processing. Equally importantly, we need to communicate with everyone what we foresee and anticipate when we extrapolate the type-performance-cost relationship of ores to the era ahead of us and establish viable schemes for ecological survival. Keywords: sustainable mineral extraction

Sep 1, 2012

By C. Y. Sun

Flotation of chalcopyrite and unactivated malachite with xanthates (ethylxanthate, butylxanthate, octylxanthate and dodecylxanthate) is studied in this paper. Minerals interacted with xanthates are detected by FTIR, and simulated by molecular mechanics. It shows that chalcopyrite can be floated with 4 kinds of xanthates, and unactivated malachite can?t be floated with ethylxanthate but can be floated directly with later 3 kinds of xanthates while characteristic absorption peaks of those four kinds of xanthates are all detected by FTIR on chalcopyrite and malachite surface. After simulating the interaction between xanthate and mineral, it shows that H2O and OH-can interact with chalcopyrite and malachite, and their interaction energy may be so called energy bulwark which must be overcome by collector when collector interacts on minerals; the two sulfur atoms in xanthate group interact with copper and neighbor iron atoms on chalcopyrite. It also shows that molecular mechanics results with logP of collectors can interpret the mechanism of xanthate-mineral on atom scale.

Jan 1, 2014