By G. E. Agar, A. L. Mular

G. E. Agar (Manager, Minerals Processing Research, International Minerals & Chemical Corp., Skokie, III.) — The author notes a discrepancy between the parameters a and ß which are the slopes of the size distribution and energy-size modulus plots respectively. The reason for the discrepancy and the systematic decrease in the magnitude of a with grinding time is abundantly clear from the work of Fuerstenau8 on dry grinding. Fuerstenau shows very clearly in his Fig. 5 that at short retention times the parameter a is the same as that obtained by sizing over the complete size range. From this figure, it is obvious that sizing to only 400 mesh gave distribution curves similar to Mular's - that is, the slope apparently decreased systematically with increased grinding. As a consequence of the improper determination of a, the magnitude of ß given by Mular must be larger than the true value. In order to demonstrate this, the following Fig. 6 was taken from Mular's paper (his Fig. 1). Fuer-stenau's results show that we can approximate the correct value of K by drawing lines parallel to the short retention time curves through the 400-mesh

Jan 1, 1963

By Mrs. V. J. DeCarlo, G. P. Salvo, H. W. Schadler, L. M. Osika

The lattice parameter of the inlerrnetallic compound Nb3Sn has been measured as a function of temperature from 80° to 1290°K. The results are compared with published data on the thermal ex- ThE recent interest in the intermetallic compound, Nb3Sn, as an engineering material for the production of superconducting devices has necessitated that certain engineering data be obtained. Because of the difficulty encountered in producing bulk pansion of niobium and indicate that the compound when made by diffusion of tin into niobium at 1000°C, would be subjected to a tensile strain of about 0.1 pct when cooled to room temperature. material which is single phase, the coefficient of thermal expansion has not been measured by dilata-tional methods. Therefore the lattice parameters of fine-grained samples of Nb3Sn produced on the surface of a niobium sheet by heating in molten tin at 950°C have been obtained as a function of temperature. The results are compared with published data on niobium2 and Nb3Sn3 and with lattice-parameter measurements made on small single crystals of Nb3Sn.

Jan 1, 1964

By R. A. Swalin, B. W. Roberts

ONSIDERABLE controversy has centered about the existence of an order-disorder transformation in alloys in the composition vicinity of 75 atomic pct Ni and 25 atomic pct Cr. All the evidence to date for such a transformation is of a rather indirect nature, since direct X-ray confirmation is difficult to obtain as a result of the small difference in X-ray scattering factors between nickel and chromium. As a result, superlattice lines would be very faint if present. Several investigators1-5 have observed anomalies in the electrical resistivity vs temperature curves of alloys in the vicinity of 25 atomic pct Cr. The observed change is characterized by a rather broad resistivity peak at about 540°C. A discontinuous drop in resistivity is normally associated with ordering. However, Taylor and Hin-ton4 have rationalized that the discrepancy could conceivably be caused by changes in the Brillouin zones upon ordering. The same investigators measured the specific heat as a function of temperature and have also observed anomalies in the vicinity of 540°C. Nordheim and Grant5 have proposed, because of the absence of superlattice lines and the absence of a discontinuity in the resistivity vs temperature curve, that long-range order is improbable and that the results could be better explained by short-range ordering. To date, however, the question has not been resolved satisfactorily. Neutron diffraction techniques provide a method for partially resolving the question since nickel and chromium have considerably different atomic scattering factors in the case of neutrons and, therefore, superlattice peaks, if ordering occurs, should be readily discernable. The results of a neutron diffraction investigation* coupled with a dilatometric in- vestigation are reported here. An alloy containing 28.0 atomic pct Cr was prepared from carbonyl nickel and electrolytic chromium in the form of a 1-in. diam x 10-in. ingot. Melting was done in an alumina crucible and casting in a graphite mold. The ingot was homogenized at 1250°C for seven days, after which a 5-in. long piece was cut into shavings in order to obtain a suitable neutron diffraction sample. Hardness samples and samples suitable for dilatometric analysis (% in. diam x 2 in.) were prepared from the remainlng piece. The neutron diffraction sample, along with a hardness sample, was annealed at 501°C for seven days, at which time the temperature was lowered to 479°C and held at this temperature for twenty-four more days. The hardness was observed to increase from 133 to 147 Vhn during the course of the annealing treatment, in qualitative agreement with Nordheim and Grant." Neutron diffraction traces taken at room temperature and at 42 °K are shown in Fig. 1. The insert shows the trace taken at room temperature with short counting times and thus only fair statistical accuracy. No evidence for superstructure reflections of Cu3Au-type ordering is observed. The statistical accuracy of the 4.2°K trace was improved by using longer counting periods. Several weak intensities are observed at small angles, including an aluminum reflection from the cryostat assembly and a very

Jan 1, 1958

By John V. Beall

What progress has been made in rapid excavation of tunnels and shafts? Where do we go from here? To get some answers to these questions was the reason that 500 tunnel men-contractors, geologists, professors, lawyers, mining engineers--came to the University of Minnesota May 15-17. The attendance of 500 astonished conference organizer Professor D. H. Yardley, who had anticipated half that number. They came from Japan, South Africa, Austria, Sweden, and Australia to name a few, and an officer of the Corps of Engineers thought all his people should have been there. The Civil and Mining Engineering Departments of the University combined for the program, which was staged by M. K. Cragun for the General Extension Division. The Saga of the Oso Tunnel The present state of the art of rapid excavation is "good." There is little controversy about where we go from here and what's more, this reporter finds that the technical know-how to automate excavation in any kind of ground is extant, even if it will take some years to achieve this state. In a nut- shell though, the present status can be seen in its various ramifications in the saga of the Oso Tunnel, as told by V. L. "Vic" Stevens of Boyles Brothers Drilling Co. :

Jan 7, 1968

By Robert H. Hafner, Irvin R. Kramer

In recent years considerable interest has been shown in surface-alloyed metals, particnlarly those of chromium (chromized steels), which have excellent corrosion resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high tem- peratures of 1200º to 1400ºC. (2200° to 2550°F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- mon salt, and heated for approximately three hours at 930º to 1040°C. (1700º to 1900ºF.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900º to 1000ºC., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a Chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1943

By Robert H. Hafner, Irvin R. Kramer

In recent years considerable interest has been shown in surface-alloyed metals, particnlarly those of chromium (chromized steels), which have excellent corrosion resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high tem- peratures of 1200º to 1400ºC. (2200° to 2550°F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- mon salt, and heated for approximately three hours at 930º to 1040°C. (1700º to 1900ºF.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900º to 1000ºC., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a Chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1943

By ELTCENE A. WHITE

WE are all interested in our ou7n lines of endeavor and consider ourselves the center of the universe. The farmer thinks he is the most important man because he feeds us. The doctor knows he is the real center because he keeps us well. The lawyer says that he is indispensable because he keeps the peace. The banker furnishes us a place to keep our money and tells us how to make proper use of it. The miner sags that without metals there would be no civilization. I think that my branch has sufficient interest and exhilaration. of accomplishment to fully occupy any man's mind and attention. Mining and metallurgy are as old as the human race. It did not have much, if any, importance in the stone age as there are not found remains of iron and copper, but in the bronze age, which was co-existent with the stone age, it came to the front. Iron and copper were the most important metals. Copper, as bronze, was known in ancient Egypt, I\~:IS important in Rome and other parts of Europe and in Asia; in South America among the Aztecs and farther North were the Mound Builders and the early inhabitants of Lake Superior. At a very early date the Egyptians conquered the Sinai peninsula for the sake of the copper produced there. The history of copper metallurgy can be compared to that of a flower. The seed is sown in darkness and in the Dark Ages the crude metallurgy of copper began. As the shoot comes up from the seed it may be compared to the age of alchemy; the branches of the plant can be compared to the Middle Ages; the flowering shoots to the 17th century, the budding to the 19th and the blossom to our own time from 1870 on.

Jan 1, 1930

By Earl Oliver

IN times like these, the A. I. M. E. and similar societies have their greatest usefulness. . . . Individuals and companies acting alone in the development of public opinion are merely voices crying in the wilderness. United and organized they make a great force that can and does influence public action. . . . What part, if any, then, shall the A. I. M. E. take in these great stabilization processes of civilization? Shall it help to give direction and force to scientific knowledge which comes within its field of activity or shall it merely develop more of it? . . . Is it the A. I. M. E.'s function to help bring system, order and direction out of this situation so that the world can again have forward economic movement, or should it rest on its oars until other agenciess develop that public understanding and direction so necessary for economic progress? As we understand the functions of the A. I. M. E. Petro¬leum Division, they are to discover and promote knowl¬edge for the benefit of society on the mining of oil and gas. To the individual member of the Petroleum Division, there are certain advantages of social and professional contacts, but the collective purpose is that described. And the individual is benefited by membership only as the Division measures up to the purposes of its existence. Consequently, the welfare of this Division and that of its members depends on the extent to which it keeps pace with the needs of society on matters relating to the mining of oil and gas.

Jan 1, 1932

By A. T. Miesch, L. B. Riley

An error occurred in the preparation of Fig. 3, p. 249, of Basic Statistical Measures Used in Geo-chemical Investigations of Colorado Plateau Uranium Deposits. This figure shows the relation of the arithmetic mean: geometric mean ratio to the geometric deviation. Curves for the cases where n, the number of samples, is 100, 10, and 5 are too high with respect to the ordinate. The error is negligible at low geometric deviations, but becomes increasingly greater wi,th higher values of geometric deviation. Arithmetric mean values in Table I1 are not effected by the errors in Fig. 3. The authors will endeavor to supply copies of the revised curves on request; write to: A. T. Miesch, Geologist, Branch of Radioactive Materials, U.S. Geological Survey, Bldg. 25, Federal Center, Denver 25, Colo.

Jan 1, 1962

A. K. McCosh, Coatbridge, Scotland (written discussion*).-It is well known in Great Britain that oven operators in the United States have been able to reduce the coking time much below European standards by the employment of higher temperatures. Our linings have always been the factor that has prevented our doing the same, and it would be of much interest to coke-oven operators here if Mr. Blauvelt would give a typical analysis of the bricks his company uses for the linings of its ovens, and if he could see his way to send me a sample so that I could have the texture examined, I should personally be very much obliged. The lining brick which my company has found most successful is of a ganister variety, and has the following analysis: Silica, 80.8 per cent.; alumina and iron oxide, .17.8 per cent.; lime, 0.8 per cent.; magnesia, 0.07 per cent.; but with this brick the least carelessness on the gas regulator's part may destroy the lining. It would also be of interest if Mr. Blauvelt could give the temperatures of the air leaving these generators and also of the oven flues.

Jan 10, 1918

By J. H. Frye, J. L. Scott, J. W. Woods

THERE are at least two effects of temperature on the stress required to produce plastic flow. 1) Metals plastically strained for the same amount at different temperatures possess different stress-strain curves and different internal structures (e.g., nature and density of imperfections). 2) There is both experimental and theoretical evidence that the stress necessary to produce plastic flow may vary with temperature even though the internal structure remains constant.1-5 Much of the data in the literature is difficult to interpret because these two effects are simultaneously present. In the work reported here, they are considered separately. Standard 0.505 in. tensile specimens were prepared from high-purity Mond nickel and OFHC copper. Nickel specimens were annealed in hydrogen at 1150°C for 30 min and furnace cooled. This produced an average grain diameter of 1.4 mm. Copper specimens were annealed in vacuum at 525°C for 6 hr and furnace cooled. This produced an average grain diameter of 0.11 mm. Nickel tensile specimens were prestrained in tension at 500°K, whereas copper tensile specimens were prestrained in tension at room temperature. All specimens were cooled to 74°K and heated to room temperature. After these treatments all of the tensile specimens of a given set possessed identical structures. All specimens were returned to the tensile machine and tested at various temperatures and constant cross-head speed. Many of the tensile curves showed well defined yields but, in order to minimize personal judgment, the yield was always chosen as the stress corresponding to 0.2 pct plastic deformation. Results are summarized in the graph of yield vs temperature of test, Fig. 1. All of the specimens corresponding to any one line have had identical treatments and, therefore, have identical internal structures. Thus, each line gives the relation between yield stress and temperature for one constant internal structure. The lowest line, which is for annealed nickel, shows no measurable variation of yield with temperature. This is similar to Blewitt's6 results on copper single crystals, but a variation in yield with temperature was found by Andrade and Henderson' in single crystals of nickel, and by Car-recker and Hibbard8 in annealed polycrystalline copper. The three other lines, which are for prestrained materials, show that there is a linear relation between yield stress and temperature when the internal structure remains constant. Such a relation might be expected from a rate equation such as that of Kauzmannl on the assump- tion that the activation energy is either independent of or linear with temperature. These results would also be expected if the shear moduli of copper and nickel are linear functions of temperature for, as Cottrell and Stokes have pointed out," in all dislocation theories of strength the flow stress appears proportional to the shear modulus of the material. In copper and nickel, since the modulus of elasticity decreases roughly linearly with increase in temperature," it is probable that the modulus of shear also decreases approximately linearly with increasing temperature. A detailed discussion of the effect of these and other factors on the temperature dependence of flow stress in face-centered-cubic metals has recently been given by Seeger.4

Jan 1, 1958

By L. C. Weiner

For zinc single crystals, xo = 3o, a surface coating raises both the cleavage and yield strengths over a large temperature range. The "brittle temperature," associated with slip after completion of twinning, does not coincide with the point of intersection of the flow and cleavage curves, which is associated with twinning. A surface film has no effect on the brittle temperature, while it lowers the intersection temperature some 20°. For crystals, yn = 83o, a coating decreases the cleavage strength, making it temperature independent, as well as increases the brittle temperature or its equivalent, the intersection temperature, 20°. These observations are described on the basis of a dislocation-pile-up-at-a-barrier model for brittle fracture; in crystals x,, = 3o the number and distribution of twins play a vital role. IN a recent investigation on the effects of solid environments on the brittle fracture of zinc single crystals,' it was demonstrated that the presence of a surface film changes the cleavage strength of these crystals, either increasing or decreasing it, depending on the crystal orientation. An increase in cleavage strength of some 43 per cent was found for coated crystals oriented x, — 3o K = 28",* while a decrease of 48 per cent was observed with crystals X" = y» — 83". Moreover, these effects were found

Jan 1, 1959

By M. A. Cook

Sutherland used an ion-pair adsorption model to derive the author's hy-drolytic pee-acid) adsorption equation for the contact bubble curves of Wark and Cox. To do so it was necessary to postulate that the sum of coverages of surface anion sites by the collector and depressant anions is practically unity. It is here shown that the free energy of Sutherland's postulated collector ion (x-)-depressant ion (OH-) exchange reaction (for no other than the OH- to compete with X-), namely EX + (OH-) Z SOH- + X-, is in some cases positive and X- should not even adsorb. Also, in many cases the (OH-) adsorption must be quite negligible even though the collector covers only about a sixth of the mineral surface at the threshold of air bubble contact. This, however, contradicts the postulate that permits one to derive the correct bubble contact eqwztion for the ion-pair model. Furthermore, the requirement for charge neutrality leads in the ion-pair model to the (impossible) constancy of the ratio @+)/(OH-) along a contact bubble curve in which pH may change by more than seven units. HYDROLYTIC ADSORPTION EQUATION Hydrolytic (free-acid or free-base) and ion-pair (H', X-, or R', OH-) adsorption models of the collector in metal sulfide and similar flotation systems are superficially alike and somewhat difficult to differentiate. This is because they yield, under seemingly valid assumptions, equivalent forms of the equations describing the distribution of the collector between the aqueous solution and the mineral surface. This has been discussed by the author and associates1-4 and more recently by Sutherland,' both for simple collector-mineral and for more complicated collector-depressant-mineral systems. In the hydrolytic adsorption model the equations describing the contact bubble curves of Wark and coxeJ7 are as follows :2 Here X is the collector anion, D- the depressant anion, 9, and On are the fractions of the free-acid sites S on the surface of the mineral covered by collector and depressant free acids, respectively, and @ is the fraction of uncovered sites. Kx is the free-acid collector dissociation equilibrium con- stant, K1 that for the free-acid collector adsorption, KD that for the free-acid depressant dissociation, and K2 the equilibrium constant for the free-acid depressant adsorption. Eqs. 1 to 5 yield upon simultaneous solution the result is the critical free-acid concentration for bubble contact in the absence of depressant-free acid. Eq. 8 expresses the conditions along a simple collector-mineral contact bubble curve for the case HD = 0, or V = 0. Last and Cook showed that Eq. 6 applies generally and with good accuracy in the collector-depressant-metal sulfide mineral systems. Inci-dentally, it has been shown by infrared absorption studies that in some cases the free-acid adsorption process splits out water.' In this case, Eq. 2 might be written SHOH + HX Z SHX + H20, with a similar equation replacing Eq. 4 for depressant-free acid-water exchange. This possibility does not change, however, the basic equations or considerations of the hydrolytic adsorption model. Indeed, this type of free acid-water exchange reaction was predicted for fluorite and iron ore flotation by oleic acid in the dry grinding and boiling processes.410

Jan 1, 1961

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

Hydrogen forms a beta-stabilized system with titanium, with a beta eutectoid at about 300°C and 44 atomic pct H2. 'The solid solubility of hydrogen in alpha decreases from about 8 to about 0.1 atomic pct from 300°C to room temperature. Hydrogen has little effect on tensile properties, but decreases notch-bar toughness to a large degree. This latter effect appears to be the result of increased notch sensitivity. PRIOR to this investigation, only a small amount of information was available on the effect of hydrogen on the mechanical properties of titanium. The effects of the other interstitially soluble elements, carbon, oxygen, and nitrogen, had received detailed study. Jaffee and Campbell1 indicated that hydrogen up to 1 atomic pct did not affect tensile properties deleteriously. Pitler' indicated that 1 atomic pct H, in titanium reduced the impact strength appreciably, but his alloys contained appreciable amounts of oxygen, and it was difficult to attribute the embrittlement entirely to hydrogen. The high temperature portion of the equilibrium diagram for the Ti-H system was established by McQuillan," and his data generally corresponded with the results of Kirschfeld and Sieverts," Gibb and Kruschwitz," Bevington, Martin, and Mathews," and other investigators. The lower concentration limit of the hydride phase varied considerably among investigators, and Gibb and Kruschwitz9 ad shown that small amounts of contaminants in either titanium or hydrogen caused considerable variation in this lower limit. In view of this pronounced effect of contaminants, the extrapolated value of McQuillan's, about 48 atomic pct at the 325°C eutectoid, appeared the most reasonable. McQuillan's lowest experimental value was 54 atomic pct at a temperature of 450 °C. The density of titanium had been shown to decrease with increasing hydrogen content, but discrepancies were noted among the various investigations. The best values indicated that the density was decreased from 4.56 grams per cc at 0.27 atomic pctl to 3.84 grams per cc at 61.3 atomic pct? This investigation was conducted to determine the effects of hydrogen on a titanium, both in high purity and commercially pure metals, and on high purity a titanium alloys. Material and Fabrication The literature indicated that impurities in either the hydrogen or the titanium must be kept to a minimum. For this reason, the initial studies were made with high purity iodide-refined titanium. The vendor's analysis of the iodide titanium and the hydrogen content of the as-fabricated Y4 in. diameter rods are shown in Table I. Two 1 lb ingots were prepared by arc melting under argon in a water-cooled crucible, using a water,cooled tungsten electrode. This equipment has been described.' As-cast Brine11 hardness numbers of 88 and 58 for these ingots were low enough to insure that the high purity of the metal was maintained during arc melting. The ingots were hot forged to % in. diameter rods at 800°C, cleaned by grit blasting, and then cold swaged to Yz in. diameter rods. The rod was then air annealed at 725 "C, ground to remove scale, and cold swaged to Y4 in. diameter (75 pct reduction in area). The material was then annealed for 1 hr in argon at 800°C to develop an equiaxed a grain size of about 0.05 mm. Micro tensile specimens and microimpact specimens were machined from this rod prior to treatment in the Sieverts-type absorption apparatus. Two lots of commercially pure RC-55 titanium were also used in this investigation to determine the effects of hydrogen and the normal impurities on mechanical properties. The commercially pure RC-55 alloy was obtained in the form of % in. diameter rod. The analysis of this material is also given in Table I. The % in. diameter rods were hot swaged

Jan 1, 1955

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By R. R. Angel

Drilling rate is a parameter that should be considered in determining the volume requirements for air and gas drilling. The use of past methods which ignore the effects of the solids content upon the pressure and velocity of the annulus flow stream can result in undercalculation of the required volurne by as much as 50 per cent. A vertical-flow equation is presented for determining volume requirements. This equation includes the effect of the solids that are transported up the annulus in the flow stream by incorporating the drilling rate as one of the parameters. The effect of down-hole temperature on required circulation rates is also ana-lvzed. A simple approximate method of determining volume requirements is presented. This method is more accurate than the methods used in the past. Hole cleaning difficulties are analyzed for a recent air drilling job where past methods indicated that - excess air was being used. Sample curves of calculated boitom-hole pressures are presented for air and gas drilling in several hole sizes. INTRODUCTION In certain areas the use of air or natural gas as a circulating medium for drilling oil and gas wells is becoming a common practice. Large increases in penetration rate and bit life are achieved through the use of these media in preference to mud or water. Drilling rates as high as 90 ft/hr have been obtained in shales. The importance of maintaining adequate circulation rate is generally recognized; however, much disagreement exists among drilling operators as to what constitutes "adequate" circulation rate. In quarry drilling, where annular velocities can be accurately determined, an annular velocity of 3,000 ft/min of standard air is required for best results in rocks having approximately the same density as those commonly penetrated in drilling oil or gas wells'. Although this standard air velocity has proven satisfactory for quarry drilling, some oil and gas well drilling operators believe that an equivalent annular velocity of more than 4,000 ft/min is required; others believe that as little as 2,000 ft/min . is sufficient. Much of this disagreement results from determining the required circulation rates with methods which fail to incorporate the drilled solids in an equation which is applicable to vertical flow. Hughes Tool Co. Bulletins No. 23' and 23-A3 present data for determining circulation rates based on the Weymouth formula. These data do not include the drilling rate as a parameter and, therefore, neglect the effect of the solids being transported up the annulus. In spite of this apparent defect and the fact that the Weymouth formula is not applicable to vertical flow, the Hughes data have well served the drilling industry in many areas and are important and timely contributions to the science of air and gas drilling. The Hughes data purposely omit a correction for increasing down-hole temperature. At slow drilling rates this effectively compensates for the use of a formula which is not valid for vertical flow; however, volumes determined by the Hughes method are not sufficient to support rapid drilling rates at moderate and great depths. For example, Phillips Petroleum Co.'s Cauthorn "D" No. l in the Vinegarone field for Val Verde County, Tex., was air drilled from 1,500 to 9,300 ft using a compressor delivering 1,400 cu ft/min. The 8 3/4-in hole was drilled with 5-in. drill pipe, and drilling rates as high as 90 ft/hr were obtained between 7,000 and 9,300 ft. No water or caving hole was encountered. At 7,728 ft it was necessary to wash-out 60 ft of cuttings to reach bottom after a trip to change bits. At 8,130 ft a twist-off occurred and the drill col-lars were stuck in drill cuttings. These difficulties indicate that the 1,400 cu ft/min of air was not sufficient to keep the hole clean. Hughes data indicates that 1,180 cu ft/min is sufficient to produce an annular ve-

Jan 1, 1958

By S. Sumski, M. B. Panish, R. T. Lynch

The liquidus isotherms in the gallium-rich corner of the Ga-Al-P phase diagram have been determined from 1000" to 1200°C and at I100°C the corresponding solidus isotherm was obtained. A simple thermody-namic treatment which permits calculation of the solidus and liquidus isotherms is discussed. A technique which was previously used for the growth of GaxAl1-xAs was used for the preparation of solution epitaxial layers of GaxAl1-xP and ALP. An approximate value of 2.49 i 0.05 ev for the band gap of Alp at 300°K was obtained and the ternary phase data were used to estimate a value of 36 kcal per mole for the heat of formation 0f Alp at that temperature. The Gap-A1P crystalline solid solution is one in which there exists the possibility of obtaining crystals with selected energy gaps, within the limits imposed by the energy gaps of Gap and Alp. Such crystals are of considerable interest because of their potential value for optoelectronic and other solid-state devices. Furthermore, it has been amply demonstrated for GaAs and GaP,'-7 that device, or bulk materials grown from gallium solution generally have more efficient radiative recombination than materials prepared in other ways. This presumably due to the lower gallium vacancy concentration in such material.= Small crystals of GaXAl1-xP and A1P have been grown from solution,8-10 and A1P has been grown from the vapor," but neither have previously been grown by liquid epitaxy. In this paper we present the ternary liquidus-solidus phase diagram of the Ga-A1-P system in the region of primary interest for solution epitaxy, and discuss the thermodynamic implications of that phase diagram with particular reference to the liquidus and solidus isotherms in the gallium-rich corner of the GaxAl1-xP primary phase field and to the A1-P system. Several measurements of the absorption edge of GaxAl1-xP crystals have been made and the width of the forbidden gap of A1P has been estimated from these measurements. EXPERIMENTAL The differential thermal analysis technique used to determine the liquidus isotherms and the optical measurements used in this work are similar to those described previously12 for the Ga-Al-As system, ex- thermocouples in the thermopile for added sensitivity. The materials used were semiconductor grade Ga, Gap, and Al+ The composition and temperature range at which DTA studies could be done was quite restricted. The upper temperature was limited by the chrome l-alumel thermopile to about 1200°C, and the highest aluminum concentration to about 5 at. pct by low sensitivity caused by the reduced solubility of Gap with increasing aluminum concentration in the liquid. DTA studies were not possible at 1000°C and below because of the low sensitivity caused by low solubility of Gap in the Ga-A1-P system. The cooling rate for these studies was about 1°C per min. No heating studies were done because of limited sensitivity. Supercooling probably does occur, but our experience with other 111-V systems indicates that it is no greater than about 10 to 15.c. Solid solubilities were determined by analyzing epitaxial layers of GaxAl1-xP grown from the liquid, with an electron beam microprobe. The layers were grown on Gap seeds by a tipping technique in which the layer is grown over a short-temperature range (20" to 50°C) on the seed from a solution of known composition. The tipping technique reported by Nelsson1 for GaAs could not be used, particularly for solutions containing appreciable amounts of aluminum, because of the formation of an A1203 scum on the liquid surface. A system was therefore designed, which would effectively remove the oxides mechanically, so that uniform wetting and crystal growth could occur. This tipping technique has already been described in detail." The best control over the composition of the re-grown layer was obtained when the tipping was done at a temperature which corresponded to the temperature of first formation of solid for the solution being used. Generally, therefore, a solution was prepared by adding the amounts of Ga, Gap, and A1 required to yield a solution which would be completely liquid above the tipping temperature with solid precipitating below that temperature. For most of the work reported here, the 1100°C isotherm of the ternary was used. It was generally necessary to heat the solution to 50" to l00. C above the tipping temperature to dissolve all of the Gap in a reasonable length of time. The epitaxially grown layers were used both for optical transmission measurements to aid in the estimation of the way in which the absorption edge changed with aluminum concentration, and for the electron beam microprobe analyses to provide data for the determination of the solid solubility isotherm. RESULTS AND DISCUSSION Liquidus Isotherms in the Ga-A1-P Ternary Phase Diagram: Thermodynamic properties of the system. The only thermal effect studied in this work was that

Jan 1, 1970

F. E. Thompson, Pottstown, Pa.: If Mr. Webster's endeavor to open up the subject of cast-iron should prove as prolific of results as did the discussion on " The Physics of Steel," he must certainly feel richly repaid. His remarks concerning the secretiveness and conservatism of the average foundry-man recall to my mind an instance of a blast-furnace which, for the last year, has been producing much foundry-iron. The manager, believing that much more of his product could be used in the foundry than the foundry-men were will-

Jan 1, 1896

By L. Sturkey

Quantitative X-ray diffraction studies of the precipitation of thorium in a Mg + 3.3 Th + 0.51 Zr alloy (HK31A) in both the as-cast and cold-worked states show that the precipitation may be described by f = 1 - e(t/T)1/2 over most of the aging period. The effects of cold work and temperature changes are determined. The precipitation of tile equilibrium Mg-Th compotund is Preceded by the formation of a transition phase of higher thorium content, with the cowposition Mg2Th and with a Laves-phase structure. Thorium-containing alloys of magnesium have assumed considerable commercial importance, especially for applications requiring exposures to temperatures greater than 500°F for appreciable lengths of time. The principal commercial wrought alloys in this system are HK31A, containing nominally 3 pet by weight thorium and about 0.7 pet by weight zirconium: and HM21A. containing 2 pet by weight thorium and 1 pet by weight manganese. These two alloys retain a high level of properties even after exposures of 100 hr at 600°F, while the more common alloys containing aluminum and zinc are badly overaged by these conditions. Therefore, in order to obtain some insight into the mechanism by which thorium produces high temperature stability in these wrought alloys, it seems desirable to investi- gate the effect of temperature and mechanical working on the precipitation processes involving thorium. Since the scattering power of a thorium atom for CuKa X-ray radiation is about ten times that for a magnesium atom, the magnesium alloys containing about 3 pet by weight thorium are ideal for quantitative measurements by X-ray diffraction of the amount of Mg-Th compound present at any time. Such quantitative measurements should be of theoretical importance in the study of the effects of time, temperature, and deformation on precipitation and precipitation hardening. Of the two commercial alloys, HM21A and HK31A, the latter is certainly the most suitable for study: In the Mg-Th-Zr2 system, only Mg-Th compounds need be considered, since no ternary compounds or binary Th-Zr3 and Mg-Zr4 compounds exist. The Zr is added to this alloy as a grain refining agent and probably plays a secondary role in precipitation. On the other hand. thorium and manganese form many

Jan 1, 1961

By Charles H. Fulton

FOR some time it has been thought that there should be > closer relationship between the members' of the Institute engaged in education in the mining schools, the mining, metallurgical, ceramic, and geological departments of universities, and the members of the Institute actually engaged in the production of mineral products and the operation and direction of works. The American Society of Chemical Engineers and the American Ceramic Society have for some years past devoted especial attention to the educational matters of their respective fields. The Engineering Foundation, representing the great engineering societies of the country, is deeply interested in technical education and maintains a Committee on Educational Research.

Jan 1, 1932