By L.W. Eastwood, Arthur E. Bousu, C. T. Eddy

The recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presentcd in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers. Since the literature on the subject has been adequately and frequently reviewed, the only referenccs to it in this paper will be those necessary in the discussion of the data presented.

Jan 1, 1935

By Arthur E. Bousu, C. T. Eddy, L. W. Eastwood

The recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presentcd in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers. Since the literature on the subject has been adequately and frequently reviewed, the only referenccs to it in this paper will be those necessary in the discussion of the data presented.

Jan 1, 1935

By Earl W. Palmer, Cyril Stanley Smith

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors' conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935

By Cyril Stanley Smith, Earl W. Palmer

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors' conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935

By T. Lane Carter

It is a curious fact that while in our Transactions there are papers dealing with mining-districts in all parts of the world, in Europe, Asia, Africa, and Australia, there is not one which describes the mining possibilities of Nicaragua, our near neighbor. To be most interested in distant objects, like the moon, and to neglect what lies at our feet, appears to be a trait of human nature. The neglect of Nicaragua is not confined to the American Institute of Mining Engineers. In no other transactions am I able to find papers dealing with mining in Nicaragua, some parts of which are as much in need of discovery and research as the North Pole. I hope this paper will be the precursor of many others to be printed in our Transaclions, dealing not only with the miniilg possibilities of Nicaragua, but with the whole of Central America, where there are vast areas a,waiting skill and capital for their development. Much of this capital and skill should come from the United States in the future, although it is probable that European capitalists, when they appreciate fully the possibilities, will investigate more and more the mining-resources of Nicaragua and ot'her Central American republics. Fig. 1 is a sketch-map of Nicaragua showing the principal mining-districts. 11. History. Mining in Nicaragua did not begin yesterday. It was commenced by civilized man when the Spanish conquerors pene-' trated into the interior and forced the natives to procure the precious metal for them. It is strange that the Spaniards did not find more gold, and work on a scale as extensive as in Colombia and other parts of South America. Probably in Nicaragua the Indians covered up most of the rich prospects

Jan 1, 1911

By Paul D. Foote

Most of the treatises on metallurgy intimate that simultaneously with the development by the atomic physicist of a really satisfactory theory of the atom will be inaugurated a new epoch in the science of metals. Metallurgically and metaphorically, we shall dwell in the Utopia of Sir Thomas More. It is my privilege this afternoon to demonstrate that this state has not arrived. An atom is a miniature planetary system consisting of a positively charged nuclear sun about which revolve electrons each carrying the negative charge e. The charge on the nucleus is + Ze where Z is the atomic number and the number of planetary electrons in a neutral atom is equal to Z. These electrons are arranged in several groups having different binding energies. Ordinary x-ray phenomena relate to processes occurring deep within the atom, usually with electrons in the so-called K or L shells. Such electrons in the heavier atoms are so closely bound to the nucleus that the forces exerted by neighboring atoms in a solid are relatively inappreciable. For most practical x-ray investigation, the atom may be considered as in the gaseous phase completely isolated from its neighbors. The K radiation from an element in the gaseous state, in the solid or liquid phase, or even in combination with other elements in all its possible valences, is almost identical.‡ Visual and ultraviolet spectroscopy is concerned with disturbances of the most loosely bound outer or valence electrons of the atom, always in the vapor state. The remarkable progress of the last year in both theo-

Jan 1, 1926

By R. L. Templin

THE increasing use of aluminum and its alloys in commercial fields has demanded a better understanding of their machining properties. This fact is exemplified by problems that have arisen in the automotive and airplane industries, but many in other fields might be cited. As pure aluminum and its alloys in their various commercial conditions show appreciable differences in their machining properties, it is not surprising that quite divergent solutions have been offered for the machining problems encountered. However, if the fundamental requirements of the most suitable cutting tools for these metals are understood, these machining problems lend themselves more readily to satisfactory solutions. Since the machining of free cutting brass and mild steel is understood by most persons accustomed to working these metals, it may serve our purpose better to first make a general comparison of the tools more commonly used in machining these metals with the tools most suitable for machining aluminum, then proceed to a more specific discussion of the individual stools.

Jan 1, 1927

By John L. JR. Schroder

INTRODUCTION-SYSTEM DESIGN The design of an underground mining operation requires the integration of transportation, ventilation, ground control, and mining methods to form a system which provides the highest possible degree of safety for mine personnel; the lowest cost per ton of product; the most suitable quality of final product, considering its intended use; the maximum percent recovery of the reserve, consistent with cost and subsidence rights ; and the minimum disturbance to the environment. The selection of mining method is generally the controlling factor in overall mine design. Some important considerations in the choice of mining method are : 1) Depth of cover over the coal seam. 2) Strength and thickness of rock strata in the overburden. 3) Characteristics of the coal seam, including thickness, nature and location of impurities or irregularities, dip (or pitch), nature and direction of cleavage, hardness, and structural strength of the coal. 4) Nature and strength of the immediate roof (top) over the coal seam. 5) Nature and strength of the floor (bottom) under the coal seam. 6) Presence and amount of explosive gas (methane). 7) Quantity of water likely to be encountered in the mining operation. 8) Any previous or concurrent mining in seams above or below the coal seam to be worked. 9) Any restrictions on recovery required for subsidence control. Topographical and geological reports and maps of the area are usually available from state and federal geological surveys, and contain excellent general information to guide more detailed investigations. Exploratory drilling, and the plotting and analysis of the information thus obtained, are essential steps in any development program, and aid in the correlation and evaluation of information gained by other means. Other good sources of information are operating coal mines that may be in the same

Jan 1, 1981

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,' magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By Robert B. Kistler, Ward C. Smith

The borate industry is one of the few sectors of the mining and mineral-processing industry which the United States still dominates. Since about 1927, the United States has supplied over half of the world's total boron and borate raw materials, and many of the chemical derivatives as well. Chiefly responsible for this record are companies producing sodium borates from two large deposits in southern California, at Boron (Kramer) and Searles Lake. The sodium borates, or products derived from borax and borax-containing brines, are the preferred borates for industry because they are soluble in water and combine readily with most other chemicals. Calcium borates are required for certain end uses, and these are produced from smaller colemanite-ulexite-probertite bodies. Sodium-free borate compounds also are produced from boric acid, which can be manufactured from either sodium or nonsodium borate minerals. During the past hundred years, the use of boron compounds throughout the world has risen from a few tons per year to the equivalent of over a million tons of B2O3. Leadership in supplying borates shifted from country to country and from region to region during this period, generally as the result of the development of newly discovered deposits that were better in quality, more accessible, or more economically exploitable than previous sources (Table 1). Primary Products and End Uses The principal borate products offered by primary producers in the United States are listed in Table 2. In general, these products are utilized worldwide by almost all consumers, regardless of the original source of the primary borates, In the United States, the primary borates all originate in southern California. Colemanite is produced as crude or processed crude ore from the Death Valley area and is utilized by the fiber glass and ceramic industries without further treatment. Production from Searles Lake, CA is from brines that are processed in chemical plants where borax and other compounds are recovered and the principal borate products are produced. At Boron, CA, the world's leading producer is mining a deposit of mineral borax and operating a chemical refinery. The mineral borax is mined together with included clay, and refined borax or "10-mol" is one of the refinery products. The mineral and the chemical compound are identical, Na2B4O7 • 10H2O. In addition to ship¬ping all major refined borate products from [ ]

Jan 1, 1983

By Martin E. Chenevert

The early work of Terzaghi1 showed that the true stress state of a rock can be expressed by the principle of effective stress. This principle states that effective stress is equal to total applied stress minus the pore pressure. Since the introduction of this principle, a great effort has been made to measure the pore pressure of rocks so that the true stress state can be determined. For clean, permeable sandstones, it is usually found that the effective stress principle can easily be applied. Direct measurement of the pore pressure is achieved with a hydraulic pressure device and the effective stress state thereby computed. However, for fine-grained rocks which contain large amounts of clay (referred to herein as shales), pore pressure measurements are usually quite difficult because of the adsorptive forces of the clay platelets, which produce negative internal pressures. No suitable device is known for measuring internal pressures of dry shales; the effective stress approach is therefore not feasible and data are usually presented in another form. As an example, data from compressive strength tests are presented as a function of rock wetness, rather than effective confining stress. The work of Belopoloskii2 and Colback and Wiid3 are examples of such data. It was pointed out by Lambe and Whitman4 that a better way must be found to express the effective stress of argillaceous rocks. The information presented herein is an attempt to fill that need. Various authors have been able to measure moderate negative pore pressures (0-240 psi) within rather wet, argillaceous rocks by means of various pore pressure devices. In 1961 Lambe5 resented information which shows that pore pressures in argillaceous rocks are indeed negative ; he presented values of suction pressure as low as - 14 psi. Likewise,

Jan 1, 1970

By Paul A. Beck, M. N. Parthasarathi

By determining the (220) pole figure for OFHC copper rolled to 96 pct R. .A., the occurrence of four texture components of the type (135) [211] was confirmed. It was found that the total volume fraction of material close to the four symmetrical orientations of this type is larger than the volume fraction of the other components put together. THE rolling texture of copper was described by early investigators1'" as a mixture of components of the (110)[l12] and (112) [11l] types. Other studies, still using the qualitative photographic method of texture determination arrived, instead, at orientations of the type (135) [533] or (135) [211] for copper3'4 and at the closely related "Z-texture" for a fee nickel-iron alloy.5 The prevalence of this type of orientation, near (123) [412], in the rolling texture of aluminum and of copper was later confirmed by means of quantitative diffractometer methods.' However, in a recent paper7 Jones and Fell stated that the (110) [112] and (112) [111] double texture was in better agreement with the measurements of Young's modulus for cold-rolled copper.' These authors also expressed their belief that the "roll texture" can be determined by means of two photographic quasi-fiber texture patterns taken with sheet specimens rotated around the rolling direction and the transverse direction, respectively. Jones and Fell found7 that the results obtained from such patterns for cold-rolled nickel did not agree with any of the orientations mentioned above, but they suggested that the observed diffraction spots may have been brought about by the overlapping of reflections due to the (110) [112] and (112) [11l] double texture components. Jones and Fell concluded that the (123) 14121 type orientation is inconsistent with their patterns. They also stated, without offering any supporting evidence, that this orientation is inconsistent with the (220) pole figure. "Ideal orientations" are often used for a very rough description of the principal orientations encountered in a texture, It is, however, well to remember the fact that, no matter how "accurate", these ideal orientations are only schematic representatives of a continuous distribution9, which often (as in the case of rolled copper) includes extensive orientation spreads. The attempt by Jones and Fell7 to use elastic modulus data in deciding between various ideal orientations in the rolling texture of copper neglects this fact. The inadequacy of two-dimensional "axis density figures" in describing orientation distributions in sheet textures was previously discussed.9 It was also pointed out9 that there is no reliable evidence to prove that orientation distributions derived by the "quasi-fiber method" from rotated sheet specimens are fully equivalent to the corresponding information obtainable from quantitative pole figures. The view that a sheet texture could be adequately determined by means of two photographic quasi-fiber texture patterns is obviously erroneous9. The question as to the consistency with the (220) pole figure of ideal orientations derived from the (111) and (200) pole figures is, on the other hand, certainly very relevant. Since no quantitative (220) pole figure for cold-rolled copper appears to be available in the literature, the following work was undertaken. EXPERIMENTAL METHOD An extruded rod of OFHC copper, 1 in. in diam, was given alternate rolling (30 to 35 pct R.A.) and

Jan 1, 1962

By R. F. Domagala, M. Hansen, D. J. McPherson

Iodide zirconium was combined with calculated amounts of nitrided zirconium sponge and arc melted to prepare alloys in the 0 to 6 wt pct N region. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat-treated specimens permitted construction of the binary phase diagram from 0 to 6 pct N. Features of the diagram include the peritectic formation of both a and ß solid solutions. The maximum solubility of nitrogen is 0.8 pct in 8 zirconium and 4.8 pct in a zirconium. An X-ray study of nitrided materials was made in the range 6 to 13 wt pct N region because serious nitrogen losses were experienced when attempts were made to arc melt these high nitrogen alloys. PHASE relationships in the Zr-N system have been determined. Due to the inability to retain nitrogen in nitrogen-rich alloys subjected to arc melting, definitive work was possible only in the range 0 to 6 wt pct (0 to 30 atomic pct) N. Sufficient complementary X-ray work was done to permit construction of the binary phase diagram up to 13.3 wt pct (50 atomic pct) N (ZrN). Small ingots were prepared by arc melting master alloys with enough zirconium to produce an alloy of the desired composition. Following pretreatment, alloys were annealed at temperature levels between 600" and 2020°C. Determination of the phase boundaries was then accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to corroborate solidus curves, and X-ray diffraction was employed to study the nitrogen-rich region of the a + ZrN phase field. Materials Westinghouse Grade 1 iodide zirconium crystal bar served as the base material for this investigation. The as-received bars were lightly sandblasted, pickled in a 20 pct HN0-5 pct HF aqueous solution, rinsed in water and acetone, and dried. They were rolled to about 1/32 in. strip and acid-pickled, followed by water and then acetone rinses. The material was sheared to approximately 1/4 in. squares, cleaned with acetone, and stored for use. Pure zirconium nitride is not commercially available, according to correspondence with possible suppliers. A literature survey indicated that nitrogen may be introduced into zirconium metal by passing nitrogen or ammonia gas over zirconium at an elevated temperature. After considerable experimentation, a train was devised whereby high quality nitrogen was passed through a series of bubblers to remove the last traces of oxygen, through an H,SO, bubbler and a cold trap to remove moisture, and finally over zirconium within a resistance furnace. Hand-picked Bureau of Mines magnesium-reduced zirconium sponge proved more amenable to nitriding than the crystal bar. The nitrogen used was extra pure gas purchased from Linde Air Products Co. The first two bubblers through which the gas was passed contained a solution suggested by L. F. Fieser" as being ideal for removing the last traces of oxygen from nitrogen. The solution contains 20 g KOH, 2 g sodium-anthraquinone ,9-sulphonate, and 15 g NaHSO, dissolved in 100 ml water. It is blood-red and turns brown when contaminated with oxygen. A saturated lead acetate solution, next in the series of bubblers, removed any H2S which might have formed in the 0, removal stage. An H,SO, bubbler and cold trap removed moisture before the nitrogen was passed over the zirconium. The zirconium was contained in a stainless steel screen within a Vycor or quartz tube in a resistance furnace. Unreacted nitrogen passed out of the system through a mercury bubbler. A nitriding run was performed in the following manner: Zirconium was placed in the screen within the furnace tube. The unit was assembled, suitably clamped off, and evacuated to remove the air and moisture within the tube and that trapped by the zirconium sponge. The unit was flushed with nitrogen and evacuated twice. After nitrogen was allowed to pass over the zirconium for about 30 min, the furnace was turned on; several hours were required to reach temperature. The reaction was allowed to continue at temperature for about 4 hr and the screen was then withdrawn from the hot zone of the furnace by means of a Nichrome or Kanthal rod. The screen and its contents were allowed to cool at the end of the tube and were then removed. At 800°C no more than about 5 pct N could be introduced into the sponge zirconium. This material was designated M-1 (master alloy No. 1) and reserved for the preparation of alloys in the dilute nitrogen region. A second set of experiments was conducted at 1000°C; no more than 7.2 pct N could be introduced into the zirconium at this temperature. Enough material (M-2) of this nitrogen content was prepared to produce a second set of alloys to complement the first and to provide alloys in the 0 to 6 wt pct N range. It was hoped that a diffusion anneal plus a re-nitriding might yield a material of higher nitrogen content. The material containing about 7 pct N was therefore given a homogenization treatment at 1000°C for 6 hr under an argon atmosphere. It was

Jan 1, 1957

By E. L. WOOD

IN ATTEMPTING to summarize briefly the reconstruction of the Hecla plant since the fire, three important facts must be held in mind; namely: a hurry-up job with the shadow of an insurance company in the background; restriction of working space in the narrow Burke Canyon; and building two-thirds of the plant on a filled area. Construction work was carried on without interruption through the winter season. These adverse conditions have contributed many obstacles not ordinarily encountered in mining work. The first problems immediately after the fire were organization and policy; the-former to create an efficient construction crew out of a mining organization; the latter to determine the type and extent of surface plant to be built. The new crew was organized from a nucleus of mine employees, 25 per cent. of the old crew remaining for construction work. Permanent fireproof buildings were decided upon, the general arrangement of the new plant to be similar to the old one as far as possible, at the same time enlarging it 100 per cent. in anticipation of the demands which would be made upon it when the Star Mine began operating. Cleaning up the wreckage was a big job, the extent of which is indicated by the fact that 30 carloads of scrap iron and steel were moved off the property. In re-establishing transportation facilities at the plant, a previous disadvantage of a steep grade on the high line was obviated by excavating 1600 yd. of solid rock; the fire having destroyed all town buildings below, made this work possible.

Jan 1, 1924

By A. J. Lanea

INDUSTRIAL MEDICINE bids fair to become one of the most important and highly developed branches of medical science. Mining companies, even in remote districts, have developed large and efficient medical organizations that comprise the best types of physicians and surgeons. Not infrequently, however, company medical departments have been influenced too much by local conditions-including the compensation laws, which differ widely in the various states. The possibilities of industrial medicine are just beginning to be generally understood, and the variations in the organization and aims of medical departments of mining companies are no more pronounced than in industry as a whole. The industrial physician should be as much a part of the organization as any other official and he should know intimately the various types and phases of work in the plant and should look at his work from the viewpoint of the needs and requirements of his particular industry and company. He should not-be on the outside looking in, but on the inside, working hand in hand with the superintendent, manager, foremen, employment director, safety director, and anybody else with whom in his work he might associate. In any industry it is essential that the doctor be-familiar with working conditions. The mine doctor who never goes underground must remain ignorant of the factors causing many of the disorders he treats as well as miss the best opportunity of gaining the respect and cooperation of the men he. serves. If the mine doctor remains unfamiliar with underground working conditions he bars himself from valuable preventive medical work. It is estimated that the time lost by industrial workers, as a whole, because of illness is about four times as great as that lost because of accidents. While the effort to determine the responsibility of working conditions for illness is often futile, there is a wide field, both for study and practice, in the lessening of sickness among industrial workers. The first step in this direction must be a knowledge of the factors involved.

Jan 2, 1921

By V. Jares

DESPITE the fact that a combination of metals-aluminum-zinc-tin, and sometimes aluminium-zinc-cadmium-is extensively used for aluminum solders, as well as for die-castings, the constitution of these alloys has not yet been made clear. I. BINARY SYSTEMS The system aluminium-zinc is the basis of the ternary alloys under consideration. Their composition was made sufficiently clear by the investigations of Roscnhein and Archbutt,1 Bauer and Vogel,2 Sander .and Meissner,3 Hanson and Gayler4 and Isihara.5 Only the temperature of decomposition of the crystals s seems still to be doubtful, whether it is considered as a compound of Al2Zn3 (according to Bauer and Vogel) or as an intermediate phase of variant composition (according to Hanson and Gayler). This temperature is given by most of the authors, as in the neighborhood of 256° C., only Isihara giving 280° C. As its accurate determination is of special importance in the study of the ternary alloys under consideration it was experimentally controlled in the following manner: An alloy corresponding in composition to the formula Al2Zn3 was made, in which the temperature effect was found to be the greatest. This was drilled and a silver-constantan thermoelement inserted into the cavity so as to be in direct contact with the alloy. The whole was then very slowly heated and the heating and cooling curves determined. The transition temperature from the heating curve was found to be 281° C., whereas-from the cooling curve it was 252° C.

Jan 10, 1926

By Nicholas J. Grant, Yoichi Ishida, Arthur W. Mullendore

An inert particle -marker technique was developed to provide a direct measurement of grain boundary sliding during creep in tile interior of aluminum specimens. Groin boundary sliding in the interior as measured by this technique was found to be nearly the same or slightly lower than that measured on the surface. These data disagree with those obtained by the grain-counting technique developed by W. A. Rachinger. In tests where both techniques were used, the grain-counting technique gave large and variable values of grain boundary sliding. It is shown that the grain-counting technique gines erroneozcs results because of a preferred direction of grain growth during creep. A question which has long plagued those who study grain boundary creep is whether or not surface measurements yield a true representation of the deformation in the interior of a specimen. The first attempt to measure grain boundary sliding in the interior of a creep specimen was made by Rachinger.1 His technique is based on the measurement of average grain diameters, both parallel and perpendicular to the tension axis, followed by a calculation of the grain elongation from these measurements. The difference between total elongation, Et, and the calculated grain elongation, Eg, is considered to be the result of grain boundary sliding, Egb. Surprisingly large values of Egb/ Et (90 pct) came out of creep tests of pure aluminum at temperatures above 250°C (480°F), utilizing the Rachinger technique. This value is very much larger than the values of 8 to 15 pct measured by numerous investigators on the surface of a specimen. Values obtained on the surface by Rachinger, however, were consistent with those measured by the displacement of reference scratches. Chaudhuri and Grant2 repeated the Rachinger method for A1-10 pct Zn, and found the same large values of Egb/Et inside the specimen. However, from purely geometrical considerations, grain boundaries cannot slide without grain deformation; therefore, they questioned the validity of Rachinger's grain-counting method. Several authors2,3 have suggested that grain boundary migration during high-temperature deforma- tion may tend to restore the equiaxed grain shape in order to minimize interfacial energy. Rachinger4 tested this hypothesis and found that it did not hold. Grains elongated by rapid extension retained their elongated shape during a subsequent slow creep test. It appears that some other factor was responsible for the abnormally high values of .Egb/El. McLean and Gifkins5 made a survey of the effect of grain size on the ratio Egb/ Et, and proposed that the high values were the consequence of a small grain size. They failed to explain the low value of Egb/Et which Rachinger observed on the surface of the small grain size specimens, and suggested that the surface effect on the value of Egb/Et does not always occur. Many of the disagreements arising from Rachinger' s work stem from the fact that there was only one method of estimating grain boundary sliding in the interior of a specimen, and that method was of an indirect nature. If a marker line of some sort could be introduced inside of the specimen, one could make measurements just as clearly as on the surface. In the present investigation, the technique utilizes a layer of finely dispersed oxide particles inside the specimen introduced by hot press-bonding of two pieces of aluminum. Rachinger attempted a similar technique but with the oxide distribution he obtained there was so much interference with grain boundary motion that quantitative measurements were not attempted. MATERIALS AND EXPERIMENTAL PROCEDURE A) Materials Preparation. Two pure aluminum rods (impurity content in percent: Si, 0.002; Cu, 0.004; Fe, 0.002; Mg, 0.000: Zn, 0.000; V. 0.001) 1 in. diameter by 2 in. high were jacketed end to end in a 4-in.-diam cylinder of commercial-purity aluminum, 4 in, high, which had a l-in.-diam hole. The l-in.-diam mating surfaces of the two pure aluminum rods had been electropolished initially. This interface provided the oxide-film internal -marker plane after the hot press-bonding process, see Fig. 2. The composite was annealed for 1 hr at 900 F and hot upset more than 50 pct reduction in height in one step. The resulting slab was then rolled to 1/2 in. thickness; the pure aluminum test material was cut out and annealed at 900°F for 1 hr and cold cross-rolled to 1/8 in. thickness. The sheet was machined into specimens with a 1/8-in.-square cross section and a 1/2-in. gage length. The following heat treatment was given the specimens: Specimen 5A series: annealed at 1000°F for 5 min for grain-size control and then cooled to 700°F and held for 15 hr for stabilization.

Jan 1, 1965

By Caner Zanbak, Erdogan Yüzer, Mahir Vardar, Kemal A. Erguvanli

The Hasancelebi iron deposit in Eastern Turkey is a very low grade (average 20% oxide) magnetite body consisting of 720 million longtons of proven reserve at a 10% cut-off limit. The ore-bearing scapolitic oclcs cover an area of approximately 4300m x 300m, and the thickness of the outcropping deposit exceeds 300m. Prefeasibility project studies revealed that a one degree decrease in a 45° final slope angle of the proposed pit would require excavation of approximately 10 million cubic meters of excess waste material, for a projected pit bottom 300 meters below the valley floor. There- fore, determination of the final slope angles of the open pit was considered to be the most important task in the feasibility analysis of this project. In this investigation, the main emphasis was given to collection, compilation and evaluation of the engineering geological, hydrogeological and rock mechanics data of the highly fractured and weathered rocks. Due to the presence of intense fracturing, the rock wedge analysis method was used for projected 30m-high benches and the circular failure analysis method was used for the stability of the projected final pit slopes. The proposed bench slope angles ranged between 60° and 80°, whereas the projected final slope angles varied between 30° and 48°, depending on the slope heights and groundwater levels.

Jan 1, 1983

By I. R. Kramer

The stress associated with the surface layer was deter-minedfor iron and molybdcnum. These measurements show that the surface layer plays a very important role in the plastic deformation of bcc metals. From the relationship between strain arui the surface layer stress and the back stress imposed by the internal obstacles, it is Proposed that the term of of the Hall-Petch equation is related only THE large number of studies on plastic flow of bcc metals have failed to delineate clearly the nature of the obstacles influencing dislocation movement. Since there have been numerous articles which have reviewed the mechanisms proposed to explain various aspects of plastic flow of bcc metals (for example, conrad1 and Keh and weissmann2), no attempt will be made here to discuss their conclusions. However, it should be to the surface stress while the term Kfd is the stress required to move dislocations through internal obstacles. Further, it was possible to derive the well-known empirical equation C = , and it is shown that the terprz a is comprised of two terms: a term Cs associated with the surface layer stress and Ci related to internal dislocation obstacles. pointed out that in all of these publications it has been tacitly assumed that plastic flow occurred uniformly throughout the cross section of the specimen (except, of course, for the Luders band region), It has generally been further assumed that the nature and distribution of the obstacles opposing the motion of dislocations are of the same type throughout. The role of the surface layer in bcc metals has not, as yet, been considered even though its role in fcc metals has been shown clearly to be of primary importance.3-5 Investigations on fcc metals have shown that at the onset of plastic deformation a surface layer acts to

Jan 1, 1968