By Nicholas J. Grant, W. Michael Yim

The creep-rupture properties of nickel, in as-prestrained or prestrain-polygonized condition, were studied at 1300°F and 4000 psi, and also at 700°F and 26,000 psi. An improvement of strength was noted in both the as -prestrained and the prestrain-polygonized tests at each temperature. The as-prestrained tests, however, showed superior creep resistance to the prestrain-polygonized ones. From the results of X-ray and etch-pit studies, the strengthc gain was interpreted in terms of dislocation density and the stability of preformed substructures. COLD work is known to improve the strength properties of metals at low temperatures. At high temperatures, however, the strength improvement is often lost if gross structural changes, such as re-crystallization, take place prior to or during the test. Even in the absence of recrystallization, a prestrained metal may undergo structural changes— polygonization and the formation of well-defined subgrains—which importantly effect the resultant properties. The relationship between substructure and creep properties has received considerable attention in recent years. The work of wood1 indicated that the creep strength of aluminum and its alloys was closely related to the subgrain size. Hazlett and Hansen,2 and Ancker, Hazlett, and parker,3 working with nickel and nickel alloys, had shown that small amounts of prestrain at room temperature followed by a recovery anneal at 800°C (1470°F) improved the strength at both low and high temperatures. The strength gain was attributed to an increase in the number of subgrain boundaries as a result of the prestrain-polygonization treatment. More recently Coldren and Freeman4 studied the effect of substructures on the creep rate of nickel at 1550°F. Their conclusions indicated that the substructure size as measured by the number of boundaries was the factor that controlled the creep rate. In addition, the perfection of the subgrain boundary has been indicated to have an important role on the strength.' On the other hand, there are data which disagree with the above observations. Grant, Chaudhuri, Silver, and Ganow6 found no creep strength improvement by a prestraining treatment. In reviewing the role of subgrains on high-temperature creep, Shepard and Dorn7 concluded that the contribution of the subgrains to high-temperature creep strength was a minor one. Guard,8 in a recent study on poly-gonized nickel, has cast doubt on the validity of the postulate that subgrain size controls the creep rate. In the majority of the previous studies, the subgrain boundaries have been singled out as the most important factor in determining creep strength; however, there is no firm theoretical ground for the postulate that the subgrain boundaries act as effective barriers to dislocation motion.B910 Little effort has been directed toward the study of the relationship between creep strength and other structural variables, such as dislocation density, lattice strain,

Jan 1, 1963

By M. E. Grimes

A method of predicting uranium extraction rate in underground bacterial leaching of as-blasted ore has been developed. The method is based on the hypothesis that extraction is directly proportional to the volume of a piece of ore that is penetrated by the leaching agent, and that each piece of ore, regardless of size, has been penetrated radially from the external surface to the same depth at a given leaching time. Consequently, given an initial size and assay distribution, extraction should be predictable for a given penetration. Two laboratory bacterial leaching tests under simulated stope leaching conditions were carried out for a periods of 89 and 96 weeks. On completion, the residual ore was screened and analyzed. The information so obtained was employed to provide an elapsed time base for the penetration model, from which predictions of future extraction were made. The finding of solubilized uranium trapped within apparently sol id ore pieces was unexpected. However, it is not recoverable except after crushing, and hence does not affect calculations of underground leaching .

Jan 1, 1974

New Products Equipment

Jan 11, 1950

By AIME AIME

NEARLY two hundred 'engineers attended the dinner given at the Hotel Pennsylvania on Monday-evening, Oct. 10, to the delegation from the American l3nginiering Societies to Great Britain and France when the John Fritz Medal was presented to Sir Robert Hadfield and to Eugene Schneider. Representatives of the British and French Governments ' and of foreign engineering societies gave to the event an international aspect unique in gatherings of engineers. Messages from men distinguished in science, statesmanship and diplomacy were read. Medals struck by the French Government were presented to the general chairman of the deputation, to the chairman of each' individual delegation and to the president's of the four Founder Societies. The meeting was regarded by engineers as formally ushering in a definite movement for world unity in the engineering profession. J. Vipond Davies, president of the United Engineering Society, acted as toastmaster. The speakers ,were Ambrose Swasey, Charles F. Rand, F. B. Jewett, A. S. Dwight, John R. Freeman, all members of the deputa- tion; and M. Gaston Liebert, French Consul General; Captain G. H. Armstrong, British Counsel General; G. G. Clapperton, representing the British Institution bf Electrical Engineers, and Prof. Jacques Cavalier, spokesman for the French universities. Among the engineers from other cities was Governor. James Hartness of Vermont.

Jan 1, 1921

By R. R. Vandervoort

The creep behavior of Nb(Cb), Ta, Mo, and W was determined under conditions of constant atomic dif-fzisivity, constant stress to elastic modulus ratio, and nearly equivalent grain size, and the steady-state creep rates obtained from these tests were correlated with calculated stacking fault energies for the metals. These results, in conjunction with similar data for several fccMetals,13 suggest that stacking fault energy may influence the creep strength ofbcc metals. The interrelationship between steady-state creep rate, subgrain size, and stacking fault energy was examined. It was found that the subgrain size for a given creep stress, increased as stacking fault energy increased, but that this relationship did not cormpletely account for the effect of stacking fault energy on creep rate. The crystallography and energetics of stacking fault formation in bcc metals has been discussed by a num-ber of authors,1-5 and impurity stabilized stacking faults on (112) planes have been observed in Nb,6,7 w,8,9 Fe,] and V" by transmission electron microscopy. However, a crucial question is whether or not stack-ing faults influence the mechanical strength of bcc metals. Potentially, stacking faults could increase strength by reducing the mobility of the partial dis-locations bounding the fault, by acting as barriers to slip dislocations, and by retarding the climb of dislo-cations during high-temperature deformation. The objective of this study was to seek a correlation be-tween creep strength and stacking fault energy for several bcc metals; namely, Nb, Ta, Mo, and W. The creep behavior of most polycrystalline metals and alloys at high temperatures and moderate stresses can be described by the following relation:11,12 im=Af(s) where i, = minimum creep rate, A = constant, j(s) = a function involving metallurgical structure, a = applied stress, E = average elastic modulus at the test tempera-ture, w = constant (equal to 5 for most pure metals), D = diffusion coefficient. One factor in the structure function F(s) which sig- R. R. VANDERVOORT, Member AlME is Research Metallurgist, Process and Materials Development Division, Chemistry Department, Lawrence Radiation Laboratory, University of California, Livermore, Calif. Manuscript submitted February 28, 1969. IMD nificantly affects the creep resistance of fcc metals is stacking fault energy, and creep rate has been shown to vary directly with stacking fault energy to the 3.5 power." In the latter investigation, four fcc metals of widely different stacking fault energies (Ag, Cu, Ni, and Al) were creep tested at a constant stress to modulus ratio of 1.21 x 10-4, at a constant diffusivity of 2.7 x 10-12 sq cm per sec, and at nearly equivalent grain sizes of about 0.7 mm. The creep data were then correlated with stacking fault energies. In the present study, a similar procedure was followed. All materials used in this work were consolidated by powder metallurgy techniques. Impurity contents in the as-received materials are listed in Table I. Chemical analyses showed that no measurable contamination of the test specimens occurred during pretest annealing treatments or creep testing. Specimens with a gage section 0.75 by 0.125 by 0.050 in. were creep tested in tension in a vacuum of less than 10-9 torr. Deformation at temperature was measured by tracking fiducial marks on the gage section of the specimen with an optical comparator. Optical deformation measurements also permitted observation of the macroscopic characteristics of the deformation Table I. Typical Specimen Impurity Content, ppm Nb Ta Mo W C 45 10 155 6 O 185 30 4 10 N 30 6 3 2 H 5 I 1 <1 als 3 10 2 15 Ca <5 I3 5 Cr 5 <3 10 <5 Cu 10 50 2 15 Fc 10 10 150 35 Ni 2 150 20 <5 Si <I0 1 3 <10 Ta 100 Ti 10 8 1 Zi 15 50 1 3 Table II. Test Conditions for Constant Stress-Modulus Ratio of 6 X 10.&apos; and Constant Diffusivity of 2.7 X 10-12 sq cm per see, and Grain Size Values for the Given Pretest Annealing Treatments Literature references Pretest Annealing for E and D Treatment Stress, Temperature, ___"&apos;Values__ Grain Tempera-Metal psi "C E D Size, mm ture, .C Time hr Nb 745 1525 14 15 to 17 0.83 1650 I Ta 1220 1770 18 19.20 O.91 1800 I Mo 1975 1630 18 21 0.77 2200 I W 2140 2265 18 22 040 2400 5

Jan 1, 1970

New Products Equipment

Jan 6, 1953

New Products Equipment

Jan 8, 1951

By J. B. Wagner, p. Hembree

The iron tracer diffusion coefficient of umstite has been measured at 110(fC across the phase field and at a single composition at 800°C. Assuming a simple cation vacancy model the tracer diffusion coefficient was found to be a linear function of the cation vacancy concentration at 1100°C. The equation is D = 3 x 20 29 where denotes the concentration of vacancies in numbers per cc. The tracer work at 800°C was carried out to investigate the reported "pinning" of tracer to the wustite surface at low temperatures. No evidence for the "pinning" of the tracer was found at 800°C in COz-CO gas mixtures. HIMMEL, Mehl, and Birchenall,&apos; Carter and Richardson,2 and Desmarescaux and La combe3 have measured the diffusion of iron tracer in wustite at several temperatures and compositions. The present work was undertaken to extend the measurements over a large composition range at 1100°C and to resolve certain apparent discrepancies in the data, expecially at lower temperatures. EXPERIMENTAL Wustite was prepared by oxidizing rectangular iron plates* in C02-CO mixtures. The samples were •The iron was supplied by the Battelle Memorial Institute courtesy of the American Iron and Steel Institute. The analysis is presented in Table I. quenched. Due to the inward flow of cation vacancies during oxidation, the center of the sample contained a thin void. The edges of the wustite slab were sanded until the sample could be split into two parts. Each part was then sanded on the front and back flat area until a smooth surface was obtained. The specimens were then replaced in the furnace and equilibrated at llOO°C in a predetermined COa-CO mixture by methods described elsewhere.4"6 The specimens were again quenched and the surfaces were lightly sanded to remove any roughness following the first equilibration. The specimens were then reequi lib rated in the same C02-CO mixture for thirty minutes in order to relieve any mechanical damage on the surface due to the polishing. The specimens were then quenched and the tracer was applied by an electroplating technique. The work of Carter and ~ichardson&apos; demonstrated that there was no systematic difference in the iron tracer diffusion coefficient in wustite if the tracer was plated, dried, or evaporated on the specimen. In the present study a piece of filter paper was saturated with an iron chloride solution of pH <* 3 that contained the tracer FeS5. The wustite was placed on the filter paper and made the cathode. A current density of 0.4 to 0.6 ma per sq cm was passed for about five to ten minutes. The thickness of the tracer layer was estimated to be about 7 x lom6 cm. This estimate was made by considering the area plated, the current flow, and time for plating and the activity of the iron in the plating solution. Different areas of the specimen were counted using a collimator to determine the uniformity of the tracer. Any specimen which exhibited a variation from the initial count rate (about 1500 cpm) by more than 15 pct was rejected. An estimate of the time necessary to convert the thin layer of iron tracer to wustite was made using the data of Pettit and wagner." he estimated time was 1 sec at 1100°C assuming linear oxidation kinetics. The shortest diffusion anneals were 1800 sec. The samples were suspended in the hot zone of a furnace by two platinum wires. Two separate specimens were run at the same time. Only the edges of each sample were in contact with the wires. The C02-CO gas of the same composition as that used in the pre-diffusion anneals flowed freely around the samples at a linear velocity of 0.9 cm per sec. To initiate a run, the specimens were lowered from the cold zone of a furnace to the hot zone by a magnetic lowering device." bout 60 sec were required for lowering. To terminate a run, the sample was withdrawn from the hot zone to the cold zone. Time zero for the beginning of the experiment was taken when the sample blended into the red glow of the furnace and conversely for the end of the experiment. The surface decrease method of measuring the tracer diffusion coefficient was used to collect the data. This method requires that counting geometry be reproducible because the specimen is counted before the diffusion anneal and after the anneal. A special jig was constructed for each specimen so the specimen could be removed from the jig and returned to the jig such that the well geometry was reproducible.

Jan 1, 1970

By P. M. Robinson, M. B. Bever

THE heats of formation at 273°K of the compounds InBi, In2Bi, and TIBi2 have been determined by metal solution calorimetry with bismuth as solvent. The published information on the thermody-namic properties of these compounds is limited. The structure of the compound InBi (mp, 383°K) is tetragonal of the PbO (B10) type.1 The compounds In2Bi (mp, 362°K) and TIBi2 (mp of highest-melting composition, 486°K) are now believed to have structures of the NizIn (B8) type273 and not the A1B2 (C32) structures reported earlier.4, 5 The compounds In2Bi and TIBi2 have limited homogeneity ranges at room temperature, while the compound InBi has no detectable homogeneity range.&apos; Samples of the compounds were prepared from 99.99 pet Bi (Mallinckrodt Chemical Works), 99.999 pet in (American Smelting and Refining Co.), and 99.99 pet Tl (Amend Drug and Chemical Co.) by melting the components in sealed, evacuated Vycor tubes. The compounds InBi and in2Bi were of the stoichiometric compositions. The compound TIBi2 contained 40 pet T1; this composition was chosen because at room temperature the alloy of stoichiometric composition does not lie within the homogeneity range.&apos; The melts were held approximately 50°C above the liquidus for 8 hr and then quenched into iced brine. The samples were homogenized for 48 hr at temperatures 20°C below the temperature of complete solidification. Metallographic examination of sections taken from the center and the ends of the ingots did not reveal second phases or segregation . The heats of formation were determined as the difference in the heat effects on solution of a compound and of a mechanical mixture of its components added from the reference temperature of 273°K to liquid bismuth at 623°K. The details of the calori-metric procedure and method of calculation have been described elsewhere? The calorimeter was calibrated by adding bismuth at 273°K to the bismuth bath at 623°K. The calculated values of the heats of formation of the compounds, listed in Table I, are based on a value of 4.96 keal per g-atom for the difference between the heat contents of bismuth at 273" and 623oK7 No published values are available for the heats of formation of the compounds InBi and In2Bi. Hultgren et a1.7 have calculated a value of -0.50 i 0.10 keal per g-atom for the heat of formation at 423°K of the compound TIBi2 containing 40 at. pet T1 from heat-content measurements in the range from 398" to 700°K and the heats of formation of the liquid alloy. The difference between this value and the value of -0.66 * 0.01 keal per g-atom at 273°K is too large to be attributed to a difference between the heat capacities of the compound and the components over the temperature range 273o to 423oK7 However, the direct determination of the heat of formation by a calorimetric method should give a more accurate value. The heats of formation at 273°K of the compounds InBi and In2Bi lie on a straight line when plotted as a function of composition, Fig. 1. The compound In2Bi, therefore, appears to be barely stable with respect to its neighboring phases. In order for the free energy vs composition curve to be concave towards the composition axis, the entropy change on formation of In2Bi must be more positive than that on formation of InBi. As the compounds are ordered,2, 3, 8 there is no configurational entropy change on formation. The difference between the entropy changes on formation of the two compounds, therefore, is probably associated with the vibrational entropies. In view of the low heats of formation, the changes in vibrational entropy, due to changes in bond strength on formation of the two compounds, are likely to be small. Owing to the volume contractions on formation of the two compounds,5 the vibrational entropies probably decrease slightly but the decrease of the vibrational entropy of InBi is expected to be larger than that of In2Bi.

Jan 1, 1965

By Ervin E. Underwood

IT has been recognized for many years that dis-persed particles have great value in raising the creep resistance of metallic alloys. In fact, some of the most successful high-temperature alloys owe their superiority to this factor above all others. A recent observation by Glen1," indicates that even better high-temperature resistance to deformation results in alloys capable of two successive precipitation reactions. The ramifications of this finding are of great interest. Unfortunately, our understanding of the reasons for such notable improvements has not kept pace with technical developments. In an effort to uncover some of the basic facts governing strengthening by particles, a program was initiated at the Battelle Memorial Institute with the primary goal of comparing creep strengths in single-phase and two-phase (precipitating) alloys. The effects of precipitation from solid solution on the creep properties of alloys are generally such that the resistance to creep is increased. However, if alloys are heat treated to different degrees of hardness before creep testing, it is often found that those possessing the maximum hardness initially do not necessarily have the maximum creep resistance. Depending on the stresses and temperatures involved other structures may prove more desirable. Considerations of the above nature indicate the importance of defining the initial state of the alloy. Here, it was decided to start with quenched single- phase alloys in which precipitation and creep deformation proceed concurrently. Equipment and Experimental Procedures Preparation of the Specimens—Four 25 lb ingots were prepared from 99.999 pct Cu and 99.996 pct Al to compositions of 1, 2, 3, and 4 wt pct Cu. Spec-trographic and chemical analyses are listed in Table I. After heat treatments and intermediate reductions, the alloys were cold rolled to 1/8 in. thick sheet. The final cold reductions amounted to 50, 40, 20, and 10 pct for the 1, 2, 3, and 4 pct Cu alloys, respectively. The specimens for creep testing were machined into tensile flats 7 in. long, 3/4 in. wide (at the shoulders), and 1/8 in. thick. The reduced sections were 1/4 in. wide and 21/2 in. long. After heat treatments at 540°C to an ASTM grain size of 1 1, the specimens were quenched into water at room temperature, then electropolished in a glacial acetic acid and perchloric acid solution. The gage marks were Knoop impressions placed 2 in. apart on the reduced sections. Blanks of 1 x 1 in, were cut from the same sheets for the age hardening runs and were given the same grain size heat treatments. The specimens and blanks were stored in a refrigerator at —40°C until needed for testing. Creep Measurements—Creep tests were conducted in a constant temperature room which was maintained at 26° ±1°C. A split-type, hinged, vertical-tube furnace was mounted on a horizontal track so that the specimen could be enclosed suddenly. Thus, it took about 15 min for the specimen to come within 5°C of the test temperature. The temperature variation along the specimen was controlled to about

Jan 1, 1958

Jan 5, 1976

Jan 6, 1976

Jan 4, 1976

By D. R. Walker, M. C. Shaw

Dimitri Kececioglu (Allis-Chalmers Manufacturing Co., Milwaukee)—The idea of applying metal cutting theory to comminution and vice versa is very impressive. Among others, the demarcation of wheel-grinding data into two regions, namely Kick&apos;s and Rittinger&apos;s, draws attention here. A study of Figs. 6 to 9 shows the following: In Fig. 6, 1 point out of 8; in Fig. 7, 4 points out of 26; in Fig. 8 only 1 point out of 13; and in Fig. 9 practically none out of 13 points fall out of curve No. 2. Also when grinding particles smaller than 5x10." in. it is difficult to measure very accurately the grinding forces, chip geometry, and particle size. In view of the above it would be difficult to make a positive and distinct demarcation of the Wheel-grinding data into two regions, namely, Kick&apos;s and Rittinger&apos;s. The idea of using machine grinding to determine the comminution properties of materials is indeed unique. The following cautions come to mind, however, regarding applicability of machine grinding data to comminution: 1—Grinding gives uniform particle size, whereas comminution gives a variety of particle sizes in the same process. The fact that grinding gives uniform particle size is not necessarily an advantage because in comminution the overall energy under actual comminution is desired and comminution invariably results in the production of a variety of particle sizes. 2—In grinding, a small particle is ground off a comparatively large surface. In comminution small bodies are broken down to smaller bodies. This makes it difficult to establish a concept of reduction ratio in machine grinding. 3—The mechanics of machine grinding involve direct shearing action under very high strain and comparatively high compression at the shear zone, whereas: comminution involves direct dynamic compression and surface friction with comparatively little strain and shear. Consequently the mechanics of machine grinding appear to be different from those involved in comminution. Hence one might arrive at erroneous con- clusions when comminution characteristics are eval-uated from machine grinding results. It is noticed also that functions other &apos;than Eq. 16 which do not involve the concept of direct proportionality of useful energy input to new surface area created (Eq. 2 and particularly Eq. 12) may be derived to fit the, data of curve No. 2. One such relationship may be u = ct-", where c is a positive constant and n is a positive constant less than unity. This, of course, is made possible because data of a very small range. of particle size are being fitted by the curves of No. 2 and the hereby suggested relationship. A sound comminution theory should be applicable to a relatively large range of particle size. George B. Clark (Department of Mining Engineering, University of Illinois)—While the experimental work of Walker and Shawin this article is of intrinsic value in revealing certain fundamental aspects of machine grinding, milling, and related processes and in adding to the store of information concerning the comminution of solid materials by this particular process, it appears doubtful that the results of their research can be employed to verify either Kick&apos;s or Rittinger&apos;s theories. Both these laws were originally developed and proposed on the basis of very simple, idealized hypotheses. The creation of parallel idealized physical laboratory conditions which would be required for either their proof or disproof appear to be well beyond the scope of human ingenuity, at least at present. One great weakness of the imputed verification is that the spread of the points plotted on the graphs is not sufficient to permit accurate &apos;curve fitting. The range of particle sizes included in the belt and wheel grinding is not extensive enough to show any general trends, particularly for the horizontal portion of the curves, said to represent Kick&apos;s laws. That the milling; grinding, and turning data obtained by Walker and Shaw for both metals and minerals happen to comply with. certain interpretations of these two theories under certain specialized conditions

Jan 1, 1955

By AIME AIME

THE Petroleum Division will hold its first fall meeting in Tulsa, Okla., Thursday and Friday,&apos; Oct. 2 and 3, preceding the. International Petroleum Exposition that opens there on Oct. 4. Headquarters will be at the Hotel Mayo, and members planning to attend should make reservations promptly because of the large attendance expected at the Exposition. The program for Thursday will feature production engineering problems and that for Friday the unit operation of oil pools. The principal papers planned for the various sessions are as follows:

Jan 1, 1930

James W. Malcolmson died suddenly on Dec. 26, 1917, at Kansas City, Mo., where he had made his home for the past ten years. He was born at Dover, Kent, England, on Oct. 6, 1866. He graduated from the Royal School of Science, London, England, in 1889, and almost immediately after graduation came to Mexico, accepting a position with the Michoacan Railway and Mining Co., as mining and mechanical engineer. His work in the mining profession was carried on principally in Msxiac and the United States. • In 1888, he married Katherine Haden Krause, of Woolwich, Kent, England, and leaves, besides his wife, five sons and one daughter. During Mr. Malcolmson&apos;s long and successful career as a mining engineer, he was connected with the following companies: from 1889 to 1893, with the Michoacan Railway and Mining Co., as mining and mechanical engineer; from 1893 to 1898, in various capacities with the Kansas City Smelting & Refining Co.; after the consolidation of the Kansas City Smelting & Refining Co. with the American Smelting & Refining Co., he remained as manager of the mining department in Mexico of the American Smelting & Refining Co. until 1902. In 1902, he located in El Paso, and took up the practice of his profession as a consulting engineer. While there, he was consulting engineer for the famous and rich Pedrazzini mines at Chispas, in the State of Sonora. He was instrumental in organizing the La Republics mine in Chihuahua, and for a time acted as consulting engineer for the property. He remained in El Paso until 1907 and then moved to Kansas City and became associated with the United States & Mexican Trust Co., as consulting engineer. In 1909, he became connected with The Lucky Tiger Combination Gold Mining Co., as its consulting engineer, and continued in this connection and in the general practice of his profession as consulting engineer until his death.. His general policy in connection with the Lucky Tiger company was always a progressive one and the success of the enterprise can be largely attributed to him and his good judgment. Mr. Malcolmson contributed several articles to the Institute at different times, one of them being on the ore deposits of the Sierra Mojada Mining District, in 1901. Much of his work was in Mexico, and during his long residence in that country he acquired a very thorough knowledge of the Mexican people and their customs. During the revolution, from 1910 to 1916, this knowledge was of great value in connection with his work for the Lucky Tiger company, and often assisted greatly in keeping the property going. Mr. Malcolmson was one of the very widely known men in his profession; he was everywhere held in the very highest regard, and his position among men in the mining profession was an enviable and honorable one. At the time of his death, besides being consulting engineer for the Lucky Tiger company, he was interested in mines in the Miami zinc fields and was acting as consulting engineer for two of the operating properties there. He invested to quite an extent in real estate when he moved to Kansas City in 1907 and his investments in this line proved successful.

Jan 1, 1920

By C. D. Tedmon, D. P. Ferriss

THE yield stress, o of low-carbon steel has been shown to vary with the average grain diameter, d, according to the relation1-3 where o is taken to be the lower yield-point stress Of is the friction stress on an unlocked dislocation, and ky is a constant. The interpretation2,4 of ky in terms of dislocation theory relates this constant to the stress to unlock a source across a grain boundary. cottrel14 predicted that ky would increase with decreasing temperature. This was observed to be the case by Adams and coworkers5 in their investigation of niobium (columbium). However, petch6 and Backofen: both working with low-carbon steel, found ky insensitive to temperature. In his work with high-purity niobium, Johnson&apos; found ky equal to zero. Evansg showed that k, was essentially zero for niobium containing nitrogen in an appreciable concentration range. The present experiments were designed to check this apparent anomaly in the value of ky in another Group V metal. Yield points were determined as a function of grain size at several temperatures for tantalum and a tantalum-tungsten alloy. The material used was double are-melted tantalum and a double are-melted alloy of 90 pct Ta and 10 pct tungsten (by weight), both obtained as unannealed, swaged rod. The impurity content of the materials is given in Table I. The tantalum was annealed at 1325"C. in a vacuum resistance furnace using a tantalum boat. The alloy was similarly annealed at 1660°C. Annealing times varied from 15 min to 2 hr, depending on the desired grain size. Nominal pressure in the furnace was 3 X 10~4 mm of Kg. Metallographic examination showed that the annealing treatment produced grain sizes ranging frorn 0.021 to 0.200 mm in the tantalum, and 0.060 to 0.160 mm in the alloy. Tensile bars were made by centerless grinding the annealed specimen;, and then electropolishing to remove all grinding marks. The specimens were than pulled :it 2 1/2 pct per rnin in an Instron testing machine. The tantalum specimens were tested at 77", 195", and 300°K. The alloy was tested at 300°K only. All specimens exhibited a yield-point phenomenon at all temperatures. Typical load-elongation curves at the three test temperatures are shown in Fig. 1. The lower yield stress is plotted as a function of (grain size) in Figs. 2 and 3 for tantalum and the 90 pct Ta-10 pct W alloy, respectfully. The position and slope of the curves was determined by least-

Jan 1, 1962

By A. W. Ashbrook

There are essentially three main classifications for extractants: acidic, basic, and neutral. The acidic and basic are also referred to as cationic and anionic, respectively. Some extractants are shown in Table 11-1. Acidic Extractants Acidic extractants which are of use, because of cost and/or insolubility in water, are alkylphosphoric, sulphonic, aliphatic monocarboxylic acids and naphthalene derivatives.

Jan 1, 1978

By R. S. Shoemaker, F. W. McQuiston

CARLIN GOLD MINING COMPANY 1974 Operating Data to October MINE LOCATION: 40 miles from Elko, Nevada ORE DESCRIPTION: Gold with minor amounts of mercury occurring in siltstone and carboniferous limey shales. TYPE OF MINE: Open pit ORE HAULAGE TO MILL: By trucks up to a distance of 12 mi1es MILLING CAPACITY: 2500 tons per day ORE GRADE: 0.20 oz per ton oxide ore 0.25 oz per ton carbon type ore PRODUCTS: Gold bullion 993 fineness, by product quicksilver RECOVERIES: Oxide ore 887&apos;0 Carbon ore 83% POWER FOR GRINDING: 7 Kwh/T POWER, other than grinding: 14 Kwh/T WATER SUPPLY: Pumped from wells 2- 112 miles through 13,000 ft of 8" buried pipe 6 ft underground. Consumption 0.60 tons of new water per ton of mill feed. TAILINGS: By 10" woodstave pipe a distance of 2500 ft to mine waste filled dam. RUNNING TIME: 10 ft x 10 ft mill on oxide ore, 98% 7 ft x 8 ft mill on carbon ore, 937&apos;0 Principal causes of lost time, power outages and problems of feeding gaseous chlorine to carbon ore agitators. LABOR, TONSIMAN SHIFT: See detailed data sheet ILL BUILDING DESCRIPTION: Framed structural steel with sandwich type walls of marine plywood, then packaged pre - fabricated insulation and outer sheeting of galvanized corrugated steel.

Jan 1, 1975

By D. C. Jackling

I BESPEAK your indulgence for a brief expression of the views of a patriarch in the field of mineral industry technology relative to young men&apos;s problems in that sphere of education and endeavor. Wherever hereafter I employ the terms "technical education," "engineer," "technologist," or similar expressions, these are intended to be understood as relating to the broad field of the sciences and arts applicable to the mineral industries. First, the usefulness of technical education to either the possessor of it or those to whom its services may be made available industrially depends primarily upon the quality of the education and the capabilities of the educated to put his talents to effective and constructive employment in his chosen field of applied science.

Jan 1, 1940