By Herbert Hoover

I HAVE been greatly honored as your unanimous choice for President of this. Institute, with which I have been associated during my entire professional life. It is customary for your new President, on these occasions, to make some observation on matters of general interest from the engineer's standpoint. The profession of engineering in the United States comprises not alone scientific advisers on industry but, in great majority, is comprised of the men in administrative positions. In such positions, they stand midway between capital and labor. The character of your training and experience leads you to exact and quantitative thought. This basis of training in a great group of Americans furnished a wonderful' recruiting ground for service in these last years of tribulation. Many thousands of engineers were called into the army, the navy, and civilian service for the Government. Thousands of high offices were discharged by them with credit to the profession and the nation. We have in. this country, probably, one hundred thousand professional engineers. The events of the past few years have greatly stirred their interest in national problems.' This has taken practical. form in the maintenance of joint committees for discussion of these problems and support to a free advisory bureau in ,Washington. The engineers want nothing for themselves from Congress.. They want efficiency in government, and you contribute to the maintenance of this bureau out of sheer idealism. This organization for consideration of national problems has had many subjects before it, and I propose to touch on some of them this evening.

Jan 1, 1920

By George Mixter

MINING, in contrast to manufacturing, deals with a wasting asset. That which is taken out of the ground is gone, the property is depleted to that extent, and will eventually become exhausted of profitable ore. So the life of a mining company is dependent upon the ability of its management to develop improved methods to permit extraction at a profit of the lower-grade ores which remain, to extend by intelligent exploration the limits of its known ore bodies, and to find and acquire new properties to take the place of those that, for one reason or another, are no longer operated. Its history is a story of constant change, of the working out of properties here and the acquisition and development of properties there, to maintain the vitality of the whole. It is a story of estimating with the tools and the knowledge available the location and extent of hidden ore bodies and of devising the means of extracting

Jan 1, 1948

By I. R. Kramer

The delay time for single crystals of iron, zinc, and pre-strained aluminum was measured under conditions of high-speed deformation. The delay time of aluminum was found to be affected by the orientation of the crystal. Under the dynamic conditions employed, tile calculated "activated volume" term appears to be very small for the three metals studied. IN a previous paper,1 it was shown that under dynamic testing conditions at 78° K, there was a delayed yield in single crystals of aluminum and copper which had been cold-worked prior to testing. The experimental results also indicated that the delay-time effect was not due to the interaction of dislocations with impurity atoms or vacancies, but rather to a dislocation-dislocation interaction since aluminum which has not been prestrained shows no delay-time phenomenon. In this paper, some data are reported on the effects of orientation on the delay time of aluminum single crystals; the delay time of zinc single crystals saturated with nitrogen and the delay time of iron single crystals also were measured. EXPERIMENTAL PROCEDURE Aluminum (99.997 pct) and zinc (99.999 pct) crystals, 1/2 in. in diam and 8 in. long were grown by the Bridgman technique. The iron single crystal was supplied by Dr. R. Maddin. The zinc crystals containing nitrogen were prepared by melting high-purity zinc in a graphite crucible and the nitrogen was introduced by additions of ammonium chloride. The liquid zinc was then drawn up into glass tubes of 1/2 in. diam and allowed to solidify. The rods were cooled to room temperature before the transfer to the mold for conversion into single crystals. The orientation of all specimens was determined by the Laue' back-reflection technique, Fig. 2 and Table I. To prepare for the delay-time measurements, the crystals were cut with a fine jewelers saw and the ends carefully machined. The specimens then were electrolytic ally polished to remove the cold-worked metal, mounted in a special fixture and hand-lapped. As a final step, the crystals were annealed in evacuated tubes. Specimens of aluminum crystals, Nos. 24 and 26, were compressed 0.5 and 2 pct, respectively, in the direction of the later impact. The zinc specimens were aged at 50°C for 15 min, In the case of iron, only two specimens could be obtained. To obtain sufficient data, it was necessary to resort to a reaging treatment. After each delay-time test, the specimens were aged at 65° C for 100 min. This treatment, according to Clark,2 is sufficient to restore the original delay time. It is believed that although the specimens were plastically deformed approximately 10-4 pct, after each test the delay-time values are reliable. The delay-time measurements were made in an apparatus similar to that described previously.' Single crystals approximately 1 in. long and having a diameter of 1/2 in. were placed in a pendulum which consisted of a bar 1/2 in. in diam and 8 ft long, designed with a crystal holder to accommodate the specimen at low temperatures. The crystal was held at a position 2 ft from the front part of the pendulum. This portion of the apparatus was supported on a fine molybdenum wire. A projectile bar of the same diameter and length comprised the other portion of the apparatus. This bar was supported on

Jan 1, 1962

By A. J. Weinig

NEED for some simple method of determining tonnages in mill circuits has always been felt by operators and consultants alike. To meet this demand the following method was evolved and has been found accurate and practical after considerable testing on various mill flows. The essence of the method is to add a chemical at a uniform rate to a mill flow, such as a launder conveying pulp, and then determine the concentration of the added chemical in a sample of the pulp. From this procedure the tonnage can be calculated. Common table salt has proved the most satisfactory chemical for ordinary conditions. It has many decided advantages for use in tonnage determinations, among them being the following:

Jan 1, 1933

By HENRY M. HOWEL

1. Introduction.-The first part of this papers treats of the causes and the restraining of piping in steel ingots; the second& considers the causes and the restraining of -segregation; and the third proposes certain precautions in engineering specifications concerning these two defects. Into their causes I have looked carefully, with the purpose of arriving at rational methods of restraining them, and at efficient ways of detecting. and measuring the harm which they cause, so as to benefit the public by reducing this harm at once effectively and with the least expense to the manufacturer, and therefore in the end with the least expense to the consumer. In Part I., I infer that the pipe is chiefly due to what I, call the virtual expansion of the outer walls of the ingot in the early part of the freezing. I find that the upper and smooth-faced part of the pipe probably forms while the interior is still molten, but that the lower, steep, and crystal-faced part probably forms in metal which is already firm. Of the five causes which may co-operate to limit the depth of the pipe, I find that three-blow-holes, sagging, and the progress of freezing from below upwards-are usually effective. I find that the pipe may be lessened by casting (1) in wide ingots,; (2) in sand molds, especially if these are pre-heated (this is rarely expedient); (3) at the tops instead of at the bottom; (4) slowly; (5) and with the large end up; (6) by the use of a sinking-head or other means of retarding the cooling of the top; (7) by permitting blow-holes to form; and (8) by liquid compression.) Most of these I consider in some detail, and in particular I dwell on the advantages of casting with the large end up, and I propose certain administrative arrangements to permit this.

Mar 1, 1907

Lieut. Maxwell E. Erdory, now with the Army of Occupation in France, writes as follows: "The 602d Engrs., many of whose officers are members of the Institute, started its active service in France at Avocourt, where we built a road across `No Man's Land.' This road from Avocourt to Montfaucon started us on a career of road building which lasted from Sept. 26 to Nov. 9. The engineer in war has no working hours. Our first job meant 50 hr. continuous work, a layoff of 4 hr. and 18 hr. more. That was our initiation in this war game. "Back in the States we practised building trenches, dugouts, and underground shelters of all sorts. In France we were unfortunate enough to come upon the scene when the so-called open warfare started. That made all the above unnecessary. Roads was the cry and our job was to see that all the artillery got their roads and got over them. "I might mention here that the roads of France, which were in excellent condition except for numerous shell holes, w re one of the leading factors in the rapid termination of the war. "We built a narrow-gage railroad from Romagne to Landre St. George which cost us a few men. At Stenay we did our first bridge building. We built nine bridges across the Meuse, capable of carrying tanks, in 18 hr. The next day the American army crossed these bridges on their way to Virton, Belgium, and the Rhine. " Our course from Virton, Belgium, took us through Longwy, Musson, and Athus, in which towns I inspected the steel plants. In Musson as well as Longwy the Germans had destroyed most of the blast furnaces. This destruction began in August, 1917. In Athus the furnaces were in good condition, the Germans having removed all motors land electrical apparatus, rendering the plant inoperative. I have taken several photos of interest of these plants. "It is but fitting that I say that the engineer in this war has contributed much toward its success but the "Doughboy" is its hero and we engineers one and all say "All hail the Doughboy."

Jan 2, 1919

By H. H. Power

THE PETROLEUM DIVISION of the A.I.M.E. continued with its diversified activities during 1.935. Sessions at the New York meeting in February were devoted to production engineering, domestic and foreign oil production, and petroleum economics. The symposiums on domestic and foreign production proved their increased usefulness. The data accumulated for 1935 were added to those published during prior years in "Petroleum Development and Technology." A joint session on the use of metals in the petroleum industry was held by the Institute of Metals, Iron and Steel, and Petroleum Divisions. W. S. Farish, chairman of the board of the Standard Oil Co. (N. J.), was the principal speaker at the annual dinner. The October meeting, held in Hous¬ton, was characterized by an excellent program and large attendance. Four sessions were devoted to problems in estimating reserves, reservoir energy, properties of drilling muds, electrical logging, water flooding, and other subsurface studies. Foreign representatives of the Anglo-Persian Oil Co. presented a paper on surface tension and specific gravity of crude oil under reservoir conditions. The address by President Buehler, the dinner at San Jacinto Inn, a trip to various lo

Jan 1, 1936

By I. W. L. Finlay, H. R. Ogden, R. Jaffee, D. J. Maykuth

Aluminum has been found to be soluble in a titanium to about 26 pct, and to raise the temperature range of transformation from a to 8. Two intermediate phoses exist in the system, a new face-centered tetragonal phase, designated as 7, which occurs between 34 and 46 pct Al, and TiAI Metallographic and X-ray diffraction data were used to determine the diagram. ALUMINUM is one of the useful alloying additions for titanium-base alloys. It is an important constituent in two commercial alloys released in 1950, one containing 4 pct A1 and 4 pct Mn, and the other containing 3 pct A1 and 5 pct Cr as the metallic alloy content. It is probable that, in the future, other titanium alloys containing aluminum will be released. In the course of alloy development work, some of the features of the constitution of titanium-rich Ti-A1 alloys have been developed. These are described in the present paper. The only available information on the Ti-A1 system concerns the aluminum-rich end of the diagram. In summarizing the early work, Hansen' indicated that there is little solubility of titanium in aluminum, and that a two-phase region exists up to the intermediate compound, TiA1a (37.2 wt pct Ti), which has a congruent melting point at 1355°C. Fink' has reported that a peritectic reaction occurs at 665°C between the melt and TiA1³ to form the terminal solid solution of titanium in aluminum. The solubility of titanium in aluminum has been established at 0.24 pct at 510°C and is estimated to be between 1 and 1.5 pct at the peritectic temperature. No information has been published on the diagram above TiAl,, other than a statement- hat aluminum raises the a to ß transformation temperature of titanium. Materials and Preparation of Alloys Iodide-type titanium and high-purity aluminum were used in this investigation. Typical analyses of these materials are given in Table 1. Alloys were prepared by arc melting on a water-cooled copper hearth, using the techniques described previously for contamination-free melting.' Weight losses during melting were very low, ranging from 0 to 0.02 g in a 10 to 15 g charge, indicating that little or no loss of aluminum occurred during melting. This permitted the use of nominal compositions for these alloys. Alloy ingots containing from 0 to 7.5 pct A1 were rolled in air at 850°C to 0.040 in. sheet. Alloys containing from 7.5 to 16 pct A1 could only be rolled about 25 pct reduction at temperatures up to and including 1200°C. Alloys containing above 16 pct A1

Jan 1, 1952

E. D. Peters, Jr., Dorchester, Mass.: This paper of Mr. Keller's seems to me a step in a direction that has been very little exploited, and iff likely to lead to valuable practical re-

Jan 1, 1899

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

By James K. Richardson

Today, the enigma of the "missing man" in the metal mining industry equals, and frequently surpasses in objective importance, the problems of ore development, drilling, sampling, pumping, milling techniques, geophysical prospecting, or any one of a hundred highly technical subjects. Unfortunately, as engineers, we have confined our attentions, in the main, to the scientific phases of mineral technology, relegating our man power problems to the background. But what good has all our scientific study and preparation been if we can't get the ore mined, milled, or smelted? What has happened to our labor supply? Where is the good old miner who could timber, drill a round, lay track, or do any job underground?

Jan 1, 1949

By Oliver Bowles

STRIKING new developments in the field of industrial minerals include the employment of lime, salt, coal, and air for the manufacture of stockings, and the substitution of paper for granite and marble in making tombstones. Certain minerals that have heretofore been regarded as valueless except as museum or laboratory specimens, are now being applied commercially. Serpentine, in forms neither fibrous nor ornamental, massive topaz, pinite, and zoisite are examples. For certain other minerals, notably pyrophyllite, bentonite, vermiculite, and sulphur, extension of established uses into new fields has occurred. Substitution takes a toll in many industries, but producers of industrial minerals as a class have gained more than they have lost in recent years. Encouraging progress has been made in developing at long last a suitable substitute for certain of the uses of mica, the only industrial mineral on the strategic list of commodities established by the War. and Navy Munitions Board. Some of the more important developments in process, equipment, and use .that have come

Jan 1, 1940

By Robert F. Mehl

EXTENSION of physical and chemical methods of research in the study of metallic behavior continues rapidly, particularly in the correlation of behavior with crystal structure, and in the analysis of elastic and plastic properties. The growth of the science of metals during 1933 calls for special comment; the need for special reviews and for textbooks and monographs is now acute, as might he supposed from the number of references appended to this article, a list which is much abbreviated.

Jan 1, 1934

By E. D. Levine

A study was made to delineate the dislocation mechanistns controlling prismatic and basal slip at low temperatu.ves in titanium containing approximately 100 ppm interstitial impurities. Mechanical tests were performed on single crystals prepared from electron-beam zone-refined crystal bar by a thermal cycling technique. Measurements were made of critical shear stress and activation volume as functions of temperature. The study revealed that, for prismatic slip, two overlapping thermally activated processes aye rate-controlling below 300°K. From absolute zero to 220°K, reasonable agreement is obtained between experiment and the mechanism which involves overcoming 01. the Peierl's stress by the formation of double kinks in dislocation lines lying in close-packed directions. Between 220°and 300°K prismatic slip is controlled by a difierent thermally activated process which is characterized by a stronger temperature dependence of critical shear stress. Above 300OK, prismatic slip is controlled by an athermal process. Basal slip is controlled by a thermally activated process between 195' and 400°K. An approximate analysis suggests that it is the Peierl's mechanism that is rate-controlling in this range. Below 195°K, the occurrence of mechanical twinning obscures the features of basal slip. Above '400 X, basal slip is controlled by an athermal process. TITANIUM, an hcp metal with a less-than-ideal axial ratio of 1.587, deforms primarily by {1010}( 1210) slip at low temperatures.'-3 The critical shear stress is strongly affected by the presence of interstitial impurities. For example, churchman3 reported that a decrease in the combined nitrogen plus oxygen content from 0.1 to 0.01 pct decreased the critical shear stress for prismatic slip from 9.19 to 1.4 kg per sq mm at room temperature. Basal slip, however, is less strongly affected by interstitials; Churchman's data for {0001}( 1210) slip show a smaller decrease in critical shear stress from 10.90 to 6.3 kg per sq mm at room temperature, for the same decrease in interstitial content. In the present study, an attempt has been made to delineate the dislocation mechanisms controlling prismatic and basal slip in titanium. In view of the strong effects that impurities may have on at least some of these mechanisms, experiments were performed on material of reasonably high purity, so that comparisons could be made with investigations on material of both lower and higher impurity contents. EXPERIMENTAL PROCEDURE Single crystals were prepared from 1/4-in.-diam electron-beam zone-refined crystal bar, furnished by Materials Research Corp. The analysis of the zone-refined material is given in Table I, indicating that the interstitial content is of the same order as the purer of the two materials investigated by Churchman. The Vickers diamond pyramid hardness number of this material was 85.6. This value agrees quite well with the correlation between hardness and interstitial content proposed by Ogden and Jaffee.4 On the basis of hardness, the material investigated in this study is, therefore, intermediate in purity between that studied by Churchman (Vpn = 97) and that studied by Spangler and Herman (Vpn = 62.4).5 Single crystals were grown by thermal cycling through the a-ß transformation. Two-in.-long by 1/2-in.-diam bars were heat-treated in vacuum for 4 hr at 1160°C. The temperature of the furnace was then lowered to 865°C, and the specimens were maintained at this temperature for 7 days. This procedure was repeated several times, resulting in the growth of individual crystals up to 14 in. in length. Specimens for testing in direct shear along either {l010}(1210) or {0001}(1210) were obtained by electrical-discharge machining. The specimens were in the form of cylinders 1/4 in. in diam by approximately 1/2 in. in length, with a reduced section 1/8 in. in diam and a in. in length. All specimens were electropol-ished subsequent to electrical-discharge machining. The ends of the test specimens were cemented in stainless-steel collars. Shear tests were conducted in an Instron Tensile Tester at various temperatures from 4.2° to 508°K. Measurements were made of critical shear stress and activation volume. The latter measurements were performed by measuring the change in flow stress upon cycling the strain rate between ?1 = 2.62 x 10-3 per sec and ?2 = 2.62 x 10-4 per sec. Activation volume, I)*, is defined as u* =ßkT [11

Jan 1, 1967

By R. M. S. B. Horta, W. T. Roberts, D. V. Wilson

Evaluation of results obtained by the Harris method for inverse pole figures is discussed. Two existing analyses and a new approach are compared. In the most frequently used analysis, different reflections are accorded equal weight. A second method involves area-weighting of reflections, mainly to take account of nonuniformity of Pole distribution. In the new method, reflections are weighted according to their multiplicity factors. Intensity ratios obtained from a sample of steel sheet by the three methods are compared. INVERSE pole figures offer a convenient method of depicting the proportions of material with various orientations referred to a unique specimen axis. The technique was first applied to fiber textures, but it is now frequently used as a description of texture in sheet metal, the unique axis in this case usually being the sheet normal. The Harris method' for the determination of inverse pole figures has the great merit of simplicity. It suffers certain intrinsic limitations, but provided that these are borne in mind, the results allow useful conclusions to be drawn regarding the effects of texture components on certain mechanical properties. Much thought has been given to alternative methods of texture description, aimed at eliminating the ambiguity in the simpler methods.2"6 Refinements in the method of description are obtained at the price of increasing complexity, and it seems clear that a simple method, such as that of Harris, will continue to find application. The original derivation by Harris1 has been corrected by Morris7 and later by Mueller, Chernock, and Beck.2 Since the latter reference is more accessible, it is referred to more frequently than the work of Morris. Most users of the inverse pole figure method present their results on the basis of the treatment by Mueller et al., and it is the purpose of the present communication to comment on this treatment and to suggest a simple modification to the method of presentation which enhances the meaningfulness of the results. It will be convenient first to summarize the Mueller analysis as follows: The intensity Ihkl of a hkl reflection from a textured specimen is: Ihkl=CI0AL\Fhkl\2NhklPhkl [1] where C is a constant for a given sample I, is the intensity of the incident beam A is an absorption factor. With usual diffrac-tometer geometry and a flat specimen, A is inversely proportional to the density of the specimen. L is the Lorenz polarization factor Fhkl is the structure factor for the hkl reflection Nhkl is the multiplicity factor phkl is the fraction of crystals in the polycrystal-line aggregate with any particular (nkl) plane parallel to the surface. The corresponding equation for a specimen with randomly oriented grains is lR,hkl=CRl°ARL\fnkl\2Nnklk [2] the subscripts R indicating the factors that are different for the random sample, which will, in general, have a density different from that of the textured one. The intensity ratio is hkl , c A Phkl [3] IR,hkl CR AR PR The constants are eliminated by summing over all the measured reflections ^iRMi °R AR PR ljPkkl and from Eqs. [3] and [4] T IR,hkl The only unknown in Eq. [5] is Yj phkl and before this can be evaluated, it is necessary to adopt some form of normalizing procedure. Mueller et al. assume that when a large number, n, of reflections is used, the average value of p as defined by Eq. [6] below will be unity ? = £j**l3l [6] and the final result of their analysis follows: hkl Pkkl = i I&Jf~ [7] ±y* Ihkl ^ in,hki The normalizing procedure used by Mueller et al. involves an unrealistic assumption since it gives equal weight to each of the hkl reflections. Other normalizing procedures can now be examined with a view to selecting a more appropriate one. For an infinite number of reflections, the function p can be averaged over a continuous range of orientations covering the complete solid angle 4p by the integral relation: p =1 jp(a)dQ = l [8] This is the only exact procedure, but in practice a

Jan 1, 1970

By M. L. Requa

EVERY forward step in civilization brings with it an increase in population and increasing demand for raw materials. Modern civilization, because of its industrial development, depends more and more for its well-being on ample supplies of raw materials; the higher the type of that civilization, the greater its dependence. No fact is more obvious than that the raw materials should be put to use with greatest prudence and efficiency. National life is not a matter of a decade or a century. Conservation is no longer a matter for political discussion; it is a vital element in the future welfare of all nations. Unfortunately, to the minds of many, conservation means the locking up of natural resources, their arbitrary withdrawal, bringing about, in short, a condition of industrial stagnation. This has occurred in past centuries through misdirected governmental effort. Two eminent engineers have variously defined conservation as follows:

Jan 1, 1925

By H. I. Smith

THE recently developed potash industry in southeastern New Mexico, though based on a relatively new discovery, marks the latest and perhaps culminating phase of the effort to obtain a domestic source of potash that began with the leaching of wood ashes more than 300 years ago. In the search for mineral potash in America, the Geological Survey has played a conspicuous part and has paved the way for much of the private activity that now bids fair to free the nation of foreign domina¬tion in supplying the nation's potash requirements. HISTORICAL REVIEW A pamphlet published by Thomas Stephen in 1758 pictures the industry in its early struggling condition.1 Just before the Civil War, a deposit of mineral potash had been found in Germany and its value as a fertilizer had been discovered. On this account and because the supply of wood ashes had decreased, the Ameri-can potash industry gradually lost its importance. During the next 50 years, with European potash available with little effort and with satisfactory substitutes on the market for the manufacture of soap, the interest of the American people in American potash declined. In 1910 this interest was suddenly revived by the abrogation of American potash contracts in Europe. Congress passed an act, approved by President Taft March 4, 1911, providing for "researches with a view to determining geological conditions favorable to the presence of deposits of potash salts." Appropriations were made to the Geological Survey and the Bureau of Soils to carry out the provisions of this act. The work of the Survey was directed toward the finding of commercial bodies of natural soluble potash salts; the Bureau of Soils was more concerned with the processes of extracting potash from industrial wastes and organic sources. Private agencies also became interested in the program. The Geological Survey has continued its search throughout the ensuing period of more than 20 years and has studied many types of deposits in many parts of the country.

Jan 1, 1933

By C. A. Fisher

THE discovery of petroleum in Pennsylvania in 1859 marked the birth of an industry of paramount importance. Spreading from - Oil Creek, this remarkable industry may be said to have embraced the earth in a little more than half a century. Those who made the discovery little realized its deep significance or far reaching influence on our national life. For over sixty years, during which time this nation has created and developed the oil industry to a high state of efficiency and' carried its activities to all parts of the world, we have' at all times been the leaders in the production of crude oil and in the development of its technology. During the unprecedented growth and expanse of the oil industry there has been an increasing dependency of our basic industries on, petroleum, until at present it has become essential to our national existence. To meet the ever increasing demand for petroleum and its products, we have explored, at one time or another, for their oil possibilities, practically all parts of the sedimentary rock area in the United States. Furthermore, detailed surface and, in many places, subsurface studies have been made of all the promising regions; over 640,000 jewells have 'been drilled for. oil since the beginning of the industry; $12,000,000,000 have been spent in this work; seventeen major fields exceeding 100,000 bbl. daily production and more than a thousand minor pools have been opened up, and 8,000,000,000 bbl. 'of oil have been produced, or an amount nearly equal to the estimated future reserves of the United States made in 1921.

Jan 1, 1925

By P. H. Dudley

A Discussion of the Paper of Prof. Howe. (Bi-Monthly Bulletin, No. 14, March, 1907, pp. 169 to 274.) P. H. DUDLEY, New York, N. Y. (communication to the Secretary*) :-The characteristics of Prof. Howe's metallurgical papers are, that he is able, from the mass of confusing evidence on the subject, to make an analysis and present hypothetical and essential principles in concrete form for consideration and discussion. I can appreciate, from the practical side of the subject, the arduous labor of collecting and investigating the data that is essential to prepare the paper. Much of the data necessarily came from material of preceding years. of manufacture in which there was allowed time for chemical reactions of the recarburizer, and for the elimination of the oxidation-products before teeming the ingots. This condition gave a favorable tinge-element to free the metal from slag- and other impurities, but, in allowing the. ingot to cool before charging in the furnace, the time-element entered as a detrimental factor in the development of the pipe or shrinkage-cavities, which gave an ingot-structure deficient in soundness. The interpretations from such material must be made with due allowances for the methods of manufacture, and must be given proper weight, as general facts, in subsequent arguments. The difficulties under which investigators labor are not easily surmounted in differentiating between reliable and unreliable data incident to variables of methods of manufacture, chemical composition of the alloys of steel, mediocre practice and that of the highest state of the art. Modern practice and large outputs in Bessemer steel have reversed the effects of the time-element-by cutting short the chemical reactions of the recarburizer and the elimination of

Jan 5, 1908