By Richard A. Mullins, James J. Merle

Systematic sampling and analysis in coal-washing plants results in product control and economical operation. A well-organized laboratory system reduces operating costs and increases sales if the operating and sales companies make full use of information it supplies. The operating cost of a control laboratory is less than 1 pct per ton of coal produced. THE system of laboratory control as practiced by the Ayrshire group of mines was begun with the construction and organization of the first laboratory in conjunction with the completion of its first wash-ery in 1941. The primary purpose of this laboratory was to maintain a check on the quality of the coal produced from the washing plant. The laboratory was equipped to determine proximate analyses, float-and-sink tests, and screen analyses, and was staffed by a chemist. an assistant. and a technician. Members AIME, are Assistant Preparation Manager and Chief Chemist, respectively, Ayrshire Collieries Corp. and Subsidiaries, Danville, Ill. Joint AIME-ASME Fuels Conference. French Lick. October 1949. TP 2855 F. Discussion (2 copies) may be sent to Transactions AIME before June 30, 1950. Manuscript received Aug. 22, 1949. Soon it became apparent (1) that product control could be accomplished, (2) that a substantial reduction in operating costs could be effected by close control of coal losses in the rejects, and (3) that information furnished by the laboratory was of continuous value to the operating and sales companies. Consequently the laboratory function was expanded to supply them with additional data as required. As the parent company expanded and new mines were added, control laboratories were established at each mine equipped with washeries, and a central laboratory was maintained at one of the mines that was located equally convenient to all of them. A well-planned control laboratory assures production of a uniform, high-quality product. Whenever coal of substandard grade is loaded inadvertently, the sales company can be informed and the proper channel of distribution made. Conversely only constant and strict laboratory supervision can insure proper production of the various grades. Knowing the product, the producer can keep out of many customers' arguments that may be both awkward and expensive. Double checking between customers and mine laboratories have solved many disputes' Some nager insist On buying coal On the analysis basis only, with penalties for substandard coal and premiums for coal above normal quality. A substantial percentage of the coal sold by the Ayrshire group is of this nature. The usual procedure is for the customer to sample and analyze the coal as it is unloaded at the plant, and the mine laboratory samples it as it is loaded at the mine for subsequent analysis by the central laboratory. Only the unloaded moisture is considered, rather than the average of mine and plant moisture, and the buyer sends duplicate samples to the central mine laboratory for this determination. The average of the two analyses determines the price of coal at the mine. In this particular case, the laboratory plays an important part in increasing realization for two reasons: (1) every attempt is made to maintain plant efficiency and product quality as high as possible, (2) check on analyses and sampling by the buyer or seller.

Jan 1, 1951

By R. D. Pehlke, J. V. Gluck

The limiting activity coefficient of zinc in a "binary " solvent has been described for several dilute ternary solutions by combining literature data from recent interaction studies in the terminal regions with thermodynamic data for the central regions. Results are discussed in terms of the Alcock and Richardson random solution model. The observed behavior agrees semiquantitatively with predictions using the model. RECENT efforts in the thermodynamics of dilute ternary liquid metallic solutions have been mainly concerned with the interactions between two dilute solutes, that is, the terminal region at an apex of the composition diagram.'-' A more general case is that of the behavior of a dilute solute over the full range of a ternary system, or, more specifically, the limiting activity of solute i as projected to the k-j binary side of the i-j-k composition triangle. An implication of this is that the interaction between i and j at the k apex should connect in some way to the interaction between i and k at the j apex. A model to characterize various types of expected behavior has been discussed by Alcock and Richardson.9,10 Such behavior can range from a simple linear relation for In yi over the 1-k binary to more complex curved relations which depend on various assumptions regarding the heat of solution in the j-k binary system and the presence or absence of clustering with solute i. Quantitative data to assess these concepts have been limited primarily to the cases of nonmetallic interstitial solutes in ferrous solutions. Alcock, Richardson, and various coworkers9-13 have discussed the behavior of oxygen, sulfur, silicon, or hydrogen in dilute solution over the range of iron + metal systems; however, the only data considered by them for substitutional nonferrous metallic solutions were the results of Elliott and Chipman concerning the activity of cadmium in the Pb + Sn, Pb + Bi, and Pb + Sb systems.9 These data were limited and did not cover the terminal regions in detail. An opportunity to extend the Alcock and Richardson considerations to the dilute solution of zinc in various "binary" solvents has been afforded by combining results of several of the recent investigations of ter-minal-region interactions with previous data from the literature for the same more concentrated solutions. RESULTS AND DISCUSSION The results of the analysis are shown in Figs. 1 to 5 where the log activity coefficient, (In yZn)xzn--o, is plotted vs the composition of the "binary" solvent. In these plots the end points are the values for In yzn in the appropriate binary solution with Bi, Pb, Sn, Cd, or In at the indicated temperature—usually 550°C (823°K). For the terminal regions the slopes were drawn using the first-order interaction parameters taken from various studies reported in the literature. The data points shown in the central regions were obtained by the short extrapolation to infinite dilution of the logarithm of the activity coefficient calculated from thermodynamic studies reported in the literature for the same systems. The sources of the data are indicated on each figure. Second-order effects were not considered. Reasonably smooth curves can be drawn to connect the central region with the terminal regions for the Zn-Pb + Bi system, Fig. 1, the Zn-Pb + Zn system, Fig. 1, and the Zn-Bi + Cd and Zn-Bi + Sn systems, Fig. 2. As shown in Fig. 2, where central region data are available from two independent investigations, the agreement is quite good. The Zn-Pb + Cd system does not appear to be as well behaved as the previous four, Fig. 3; however, this type of behavior has also been

Jan 1, 1970

By E. M. Porbansky

DURING the investigation of the electrical transport properties of copper, it became necessary to prepare large single crystals of the highest obtainable purity. In an effort to meet these demands, single crystals of copper have been grown by the conventional pulling technique—as has been used for the growth of germanium and silicon crystals.' Low-temperature resistance measurements made on these crystals show that, as far as their electrical properties are concerned, they are generally of significantly higher purity than the original high-purity material. The use of these pure single crystals with very high resistance ratios has made possible the acquisition of detailed information regarding the electron energy band structure of copper2-' and has stimulated widespread effort on Fermi surface studies of a number of other pure metals. It is the purpose of this note to describe our method of preparing very pure copper crystals by the Czochralski technique. Precautions were taken to prevent contamination of the melt from the crystal growing apparatus. A new fused silica growing chamber was used to prevent possible contamination from previous groqths of other materials such as germanium, silicon, and so forth. A new high-purity graphite crucible was used to contain the melt. This crucible was baked out in a hydrogen atmosphere at -1200°C for an hour, prior to its use in crystal growth. Commercial tank helium, containing uncontrolled traces of oxygen, was used as the protective atmosphere. A trace of oxygen in the atmosphere appears to be necessary for obtaining high-purity copper single crystals. A 3/8-in-diam polycrystalline copper rod of the same purity as the melt was used as a seed. The copper rod was allowed to come in contact with the melt while rotating at 57 rpm. When an equilibrium was observed between the melt and the seed (that is, the seed neither grew nor melted), the seed was pulled away from the melt at a rate of 0.5 mils per sec. As the seed was raised, the melt temperature was slowly increased, so that the grown material diminished in diameter with increasing length. When this portion of the grown crystal was -1 in. long and the diameter reduced to less than 1/8 in., the melt was slowly cooled and the crystal was allowed to increase to - 1-1/4 in. diam as it was grown. By reducing the diameter of the crystal in this manner, the number of crystals at the liquid-solid interface was decreased until only one crystal remained. Fig. 1 shows a typical pulled copper single crystal. The purity of the starting material and the crystals was determined by the resistance ratio method: where the ratio is taken as R273ok/R4.2ok. The starting material, obtained from American Smelting and Refining Co., was the purest copper available. Most of the pulled copper crystals had much higher resistance ratios than the starting material. The highest ratio obtained to data is 8000. Table I is an example of the data obtained from some of the copper crystals. Note that Crystal No. 126 had a lower resistance ratio than its starting material and this might be due to carbon in the melt. The melt of this crystal was heated 250" to 300°C above the melting point of copper. At this temperature it was observed that copper dissolved appreciable amounts of carbon. The possible presence of carbon at the interface between the liquid and the crystal will result in reducing conditions and negate the slight oxidizing condition required for high purity as discussed below. The possible explanations of the improvement in the copper purity compared to the starting material are: improvement in crystal perfection, segregation, and oxidation of impurities. Of these, the latter seems to be most probable. A study of the etch pits in the pulled crystals showed them to have between 107 and 108 pits per sq cm. The etch procedure used was developed by Love11 and Wernick.10 The resistivity of the purest copper crystal grown was 2 x 10-10 ohm-cm at 4.2oK; from the work of H. G. vanBuren,11 the resistivity due to the dislocations would be approximately 10-l3 ohm-cm, which indicates that. the dislocations in the copper crystals would contribute relatively little to the resistivity of the crystals at this purity level. Segregation does not seem likely as the reason for purification of the material, since the resistivity of the first-to-freeze and the last-to-freeze portions are approximately the same, as was observed on Crystal No. 124. On most of the crystals that were examined, the entire melt was grown into a single crystal. If the

Jan 1, 1964

By Milton Williams

It is generally recognized that fluid is lost from rotary drilling muds to permeable strata during normal drilling operations;1,2-3 but that this fluid is the filtrate from the mud, rather than the mud itself, has been shown by various workers.1,4,5 The presence of this filtrate in oil-bearing or gas-bearing strata is undesirable and harmful. The decreased permeability of the stratum to oil effected by the presence of water has been pointed out by several investigators,6,7 and since, in the production of the reservoir fluid, the greatest pressure drop occurs immediately adjacent to the borehole, it follows that infiltered water is particularly objectionable in this region. Again, this filtrate tends to make electrical logs less reliable, since oil in the proximity of the borehole is probably flushed out to an appreciable extent by the water.8 Observation of side wall cores may be misleading for the same reason. Drill-stem tests in low-pressure areas may be of doubtful value where no oil is recovered, unless sufficient time is allowed for production of water lost from the mud. The infiltered water may hinder drilling operations by softening shales and causing sloughing; the ['tight hole" occasioned by excessive deposition of filter cake in the hole is a common occurrence. The filter cake remaining on the face of the producing formation may itself sometimes be detrimental to production.9 In view of these implications of the importance of filtration of mud, an investigation was undertaken to determine the factors involved in the infiltration process, and to correlate these in such a manner that the values obtained in routine filter tests employing a conventional filter of the "wall-building tester" type,10 together with data on size of hole, drill pipe, and rate of mud circulation, could be used to estimate water loss and distance of penetration of the filtrate into strata. Quantitative relations of filter-cake permeability, filtrate viscosity, and rate of filtration have been developed for filtration in the simple laboratory filter.4a,11,12,13 It is obvious, however, that the conditions

Jan 1, 1940

By Milton Williams

It is generally recognized that fluid is lost from rotary drilling muds to permeable strata during normal drilling operations;1,2-3 but that this fluid is the filtrate from the mud, rather than the mud itself, has been shown by various workers.1,4,5 The presence of this filtrate in oil-bearing or gas-bearing strata is undesirable and harmful. The decreased permeability of the stratum to oil effected by the presence of water has been pointed out by several investigators,6,7 and since, in the production of the reservoir fluid, the greatest pressure drop occurs immediately adjacent to the borehole, it follows that infiltered water is particularly objectionable in this region. Again, this filtrate tends to make electrical logs less reliable, since oil in the proximity of the borehole is probably flushed out to an appreciable extent by the water.8 Observation of side wall cores may be misleading for the same reason. Drill-stem tests in low-pressure areas may be of doubtful value where no oil is recovered, unless sufficient time is allowed for production of water lost from the mud. The infiltered water may hinder drilling operations by softening shales and causing sloughing; the ['tight hole" occasioned by excessive deposition of filter cake in the hole is a common occurrence. The filter cake remaining on the face of the producing formation may itself sometimes be detrimental to production.9 In view of these implications of the importance of filtration of mud, an investigation was undertaken to determine the factors involved in the infiltration process, and to correlate these in such a manner that the values obtained in routine filter tests employing a conventional filter of the "wall-building tester" type,10 together with data on size of hole, drill pipe, and rate of mud circulation, could be used to estimate water loss and distance of penetration of the filtrate into strata. Quantitative relations of filter-cake permeability, filtrate viscosity, and rate of filtration have been developed for filtration in the simple laboratory filter.4a,11,12,13 It is obvious, however, that the conditions

Jan 1, 1940

By R. S. Cartwright

TWO types of automatic drilling controls, the Halliburton and the Hild, are now available and are coming into more or less general use in deep drilling. The primary function of both is to maintain a safe limit of torque on the drill pipe, this being accomplished by automatically controlling the weight or pressure on the cutting tool. Neither type will necessarily increase drilling speed, but by permitting advantage to be taken of "breaks" in the hole higher average cutting speed may be maintained. The control is essentially a safety device, and should be considered as such. It is not the purpose of this paper to discuss the merits of drilling controls, although the advantages over manual feed at the brake drum are obvious, but rather to point out some of the limitations. The Halliburton Control The Halliburton control is designed to operate during drilling through the agency of the draw works. Automatic and constant control of the torque on the bit is governed by clutches on the control itself, and the line shaft to drum shaft drives on the draw works. In operations other than drilling the control is simply a jackshaft between prime mover and draw works. It is, of course, adaptable to any type of power. Because control of the torque on the bit is dependent on the various ratios or clutch combinations available on the Halliburton control and the draw works, it follows that there are certain limitations in points of control. Table 1 shows the possible ratios which can be obtained with the control and a popular type of three-speed draw works, it being assumed that the highest possible gear combination—the combination which when engaged will suspend the least amount of weight—has a value of 1.00. According to the table there are "blind spots" in the series. This is true particularly among the lowest ratios, which are most used to suspend the major part of the weight when great depths are reached. It will be noted that there is a difference of nearly three units in the value of the

Jan 1, 1929

By Richard Borg

The partial molal free energy of Cd in each of the four intermediate phases, Cd3 Cu, Cd8 Cu5, Cd3Cu4, and CdCu2 is determined using the Knudsen vapor pressure technique. Measurements are made also within the two-phase regions, and thus the variation in FCd is now known across the entire phase diagram. The absolute values are all less the 2.0 kcal and increase regularly with increasing Cd concentration. The small absolute value of the free energy precludes the possibility of obtaining highly accurate values; nevertheless, the results are compatible with those previously reported for the liquid phase. Additional results are reported concerning the lattice parameters of the 6, E, and b phases. THE elements Cu and Cd combine to form four intermediate phases which are designated* and E and which include respectively the following inter metallic compounds: CdCu2, Cd3Cu4, Cd3 Cu5, and Cd3 Cu. The extent of each phase with respect to temperature and composition is shown in Fig. 1 which is the equilibrium diagram drawn according to Hansen.1 All four phases are brittle, and most probably are true intermetallic compounds. Only the crystal structure of the 6 phase has been thoroughly investigated.2,3 The structure is cubic and isotypic with y brass. The structure of Cd3 Cu has not been previously reported, It is hexagonal with a = 8.11 and c = 8.76 0.02Å and the structure is presently being determined.* The compounds Cd3 Cu4 and CdCu, have been each previously the subject of a single investigation. Cd3Cu, is presumed to be cubic4 with the space group Fd3m, whereas CdCu2 is hexagonal2 with the C14-type structure. Cu2 Cd is found by X-ray analysis to be hexagonat with lattice parameters a = 5.00A and c = 16.17Å. The material appears to be pure Cu2Cd as all reflections could be indexed on the basis of the single hexagonal structure. These values disagree with those of Kripyakevich and coworkers5 who report a = 4.96Å and c = 7.98Å. Their investi-

Jan 1, 1962

By Herbert F. Miller

For a long time I have believed that the gas- and brick-costs of open-hearth furnaces using prodncer-gas could be greatly decreased by a change in the design of the port, which would materially reduce the first-cost of the furnace, the rebuilding-cost, and the repair-cost. The defects of the present type of such furnaces, which has clone duty for so many years, may be studied in Fig. 1, in which A A are the two air-uptakes, B is the gas-uptake, and C the end of the gas-port. In the present type of furnace, C is practically 011 the edge of the bath and therefore combustion begins to take place at that point, but has no effect until the gas passes from 5 to 10 ft. into the hearth. As the furnace grows older, C moves back by reason of the burning or falling down of the arch. The furnace reaches its highest efficiency when C has moved a certain distance, but is still near enough to the bath for the overhead layer of air to hold the gas down on the bath, and far enough back to permit combustion to take place at some distance from the bath. This latter fact means that the temperature is sufficient to melt steel at the edge of the port. From this time on, the furnace decreases in efficiency. What is the reason ? As C moves further hack, the gas is released from the gas-port at a point where there is little or no overhead layer of air. The result is that the gas floats along the roof, with the air mostly underneath it. Why the air does not stay over the gas is readily seen in Fig. 1. The lines of draft naturally run parallel to the length of the furnace. The air-uptakes being on the sides and the gas-port in the middle, most of the air will naturally be drawn along the sides of the furnace and the layer of air will be thinnest over the gas, where it is most needed.

Jan 1, 1914

By Jack White

MUFULIRA Copper Mines, Limited, conducted tests on the concentrator in 1942 to determine which type of ball mill, that is, Conical Trunnion overflow or Cylindrical Grate discharge, produced the greater quantity of finished product at the lowest cost. All the data which follows applies to Mufulira ore and to the particular degree of grinding produced with the classifiers installed at Mufulira concentrator. JACK WHITE, Member AIME, is Concentrator Superzntendent, Mufulira Copper Mines, Ltd., Mufulira, Nortltern Rhodesia. Sun Francisco Meeting, February 1949. TP 2729 B. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received Feb. 28, 1949. Test Procedure: The test was carried out using ball mills No. 1 to 9 (conical trunnion overflow) as the standard with which to compare No. 10 (cylindrical grate discharge mill). The conical trunnion overflow ball mills are 10 ft diam by 72 in., and the cylindrical grate discharge mill is a No. 99. Each mill runs in closed circuit with a Dorr type DSFX classifier 8 ft wide by 30 ft long. The feed is considered as being identical to all ten units. The figures for the test were derived as follows. Dry Tons Milled: For No. 10 unit (cylindrical grate discharge mill) this figure was taken from the ball mill weightometer, which was corrected for error, and then for moisture content. The weightorneter was checked twice a week during the test, and the error did not exceed 3 pct at any time. The moisture was obtained from a 24 hr moisture sample taken by the ball mill operator hourly, and placed in a closed bucket. The sample was cut where the conveyor drops the feed into the ball mill chute. The Mill Sampling Department made a daily moisture determination on this sample. To obtain the dry tons on units No. 1 to 9 the No. 10 figure was deducted from the month's dry tons milled figure, which, in turn, was taken from the crusher weightometer tons corrected for weightometer error and moisture. All tons reported in this test are short tons of 2000 lb. Ball Mill Hours: This was taken daily from the Shift Boss reports giving actual running hours for each unit. Screen Analyses: Coarse Heads (Ball Mill Feed): The monthly composite coarse heads screen analysis, done by the Mill Sampling Department, was used for the minus 200 mesh in the feed to the mills. F. X. Classifier Overflow: The ball mill operators took an hourly 24 hr sample of the overflows of units No. 1 to 9. This was a hand sample, but cut with a special cutter, and is believed to be very reliable. On No. 10 unit, an hourly 24 hr sample, and an hourly shift sample were cut in the same way. These five samples were split, filtered, and dried by the Research Department and were then wet screened on a 200 mesh screen. The average of the three shifts samples on No. 10 unit had to check the 24 hr sample within 1.5 pct to be acceptable. A weighted composite was cut each day from both 24 hr samples, and at the end of each month it was screened as follows: Wet screened through 325 mesh, the plus 325 then screened on a rotap for 15 min through 65, 100, 150, 200, and 325. This was done in duplicate. All splitting, drying, and screening of samples was done by one of the Mill Research staff, to insure accuracy. F. X. Classifier Overflow Densities: These were taken from the Shift Boss reports. Densities were taken by the ball mill operator every hour. Circulating Loads: These were taken a number of times during the test both by direct method (weighing a measured portion of classifier rake sand, and deducting moisture) and by calculation using the formula:

Jan 1, 1951

By Jack White

MUFULIRA Copper Mines, Limited, conducted tests on the concentrator in 1942 to determine which type of ball mill, that is, Conical Trunnion overflow or Cylindrical Grate discharge, produced the greater quantity of finished product at the lowest cost. All the data which follows applies to Mufulira ore and to the particular degree of grinding produced with the classifiers installed at Mufulira concentrator. JACK WHITE, Member AIME, is Concentrator Superzntendent, Mufulira Copper Mines, Ltd., Mufulira, Nortltern Rhodesia. Sun Francisco Meeting, February 1949. TP 2729 B. Discussion of this paper (2 copies) may be sent to Transactions AIME before Feb. 28, 1950. Manuscript received Feb. 28, 1949. Test Procedure: The test was carried out using ball mills No. 1 to 9 (conical trunnion overflow) as the standard with which to compare No. 10 (cylindrical grate discharge mill). The conical trunnion overflow ball mills are 10 ft diam by 72 in., and the cylindrical grate discharge mill is a No. 99. Each mill runs in closed circuit with a Dorr type DSFX classifier 8 ft wide by 30 ft long. The feed is considered as being identical to all ten units. The figures for the test were derived as follows. Dry Tons Milled: For No. 10 unit (cylindrical grate discharge mill) this figure was taken from the ball mill weightometer, which was corrected for error, and then for moisture content. The weightorneter was checked twice a week during the test, and the error did not exceed 3 pct at any time. The moisture was obtained from a 24 hr moisture sample taken by the ball mill operator hourly, and placed in a closed bucket. The sample was cut where the conveyor drops the feed into the ball mill chute. The Mill Sampling Department made a daily moisture determination on this sample. To obtain the dry tons on units No. 1 to 9 the No. 10 figure was deducted from the month's dry tons milled figure, which, in turn, was taken from the crusher weightometer tons corrected for weightometer error and moisture. All tons reported in this test are short tons of 2000 lb. Ball Mill Hours: This was taken daily from the Shift Boss reports giving actual running hours for each unit. Screen Analyses: Coarse Heads (Ball Mill Feed): The monthly composite coarse heads screen analysis, done by the Mill Sampling Department, was used for the minus 200 mesh in the feed to the mills. F. X. Classifier Overflow: The ball mill operators took an hourly 24 hr sample of the overflows of units No. 1 to 9. This was a hand sample, but cut with a special cutter, and is believed to be very reliable. On No. 10 unit, an hourly 24 hr sample, and an hourly shift sample were cut in the same way. These five samples were split, filtered, and dried by the Research Department and were then wet screened on a 200 mesh screen. The average of the three shifts samples on No. 10 unit had to check the 24 hr sample within 1.5 pct to be acceptable. A weighted composite was cut each day from both 24 hr samples, and at the end of each month it was screened as follows: Wet screened through 325 mesh, the plus 325 then screened on a rotap for 15 min through 65, 100, 150, 200, and 325. This was done in duplicate. All splitting, drying, and screening of samples was done by one of the Mill Research staff, to insure accuracy. F. X. Classifier Overflow Densities: These were taken from the Shift Boss reports. Densities were taken by the ball mill operator every hour. Circulating Loads: These were taken a number of times during the test both by direct method (weighing a measured portion of classifier rake sand, and deducting moisture) and by calculation using the formula:

Jan 1, 1951

By J. B. Newkirk, A. H. Geisler

Certain of the permanent magnet alloys provide ideal systems for the study of the kinetics of the precipitation reaction and the correlation of structure with properties. One such system, Cu-Ni-Fe, was found by Bradley1,2 to exhibit a coherent transition state in the precipitation process analogous to that reported for Al-Cu alloys somewhat earlier.3 The attractiveness of some perrnanent magnet alloys for study lies in the fact that vertical sections of the ternary phase diagram in certain regions of composition (Fig I) have as their prototype the binary Ni-Au diagram. Alloys of this type decompose into products that have the same crystal lattice type but only slightly different lattice parameters. The advantages that such alloy systems oA&apos;er for study over the usual in which an intermetallic compound is formed are many: 1. Since the precipitate has the same crystal strutture as the matrix, complex atomic movements are not required to form the new lattice. 2. Similarly, complex orientation relationships are not involved for both the matrix and the precipitate would be ex. petted to have the same orientation. 3, Small &,registry of the decomposition products at equilibrium (in contrast with Cu-Ag alloys) is conducive to extensive coherent growth in the transient state and thus the transition lattice can be detected by the usual X ray diffraction methods. 4. Finally, the relative quantities of precipitate and depleted matrix can be varied from 0 to 100 pet* thus permitting wide freedom for the study of the effect of cornposition on coherent growth and properties. In the Cu-Ni-Fe alloys of appropriate composition, the face-centered cubic precipitate and also the depleted matrix when first formed are coherent with the parent matrix.1&apos;2 The two have the same <Jo parameter as the original matrix but they are both tetragonal; the precipitate has an axial ratio c/a < I while that of the depleted matrix is c/a > I. When coherency is lost they assume the normal face-centered cubic structure with the depleted matrix having a lattice parameter greater than the original matrix and that of the precipitate less. Such a mechanism would also be expected for CU-Ni-CO alloys because of the similarity in constitution but this had not been demonstrated. The Present investigation was conducted on a CU-Ni-CO alloy. The constitution diagram and magnetic properties of these alloys have been fairly well established, however, no previous determinations of mechanism of precipitation and no correlation of structure with properties had been made. Thus, an alloy of this system Was chosen for a comprehensive investiga-

Jan 1, 1949

By M. M. Singh, H. L. Hartman

This paper reports on the results of a fundamental investigation of the behavior of rock under impact of a chisel-shaped bit. Drop-tester studies were conducted with strain gauges attached to the rock and striking bit-edge. It was established that rock behaves viscoelastically. Little correlation was found to exist between the strain waveforms detected on the rock surface and in the bit; thus, strain-time curves obtained with transducers mounted on the bit cannot be used to explain the sequence of events in rock breakage. It is estimated that nearly 1 per cent of the total energy of the blow is expended in permanent deformation of the rock. The strain- energy distribution on a rock surface as a result of chisel impact, which follows a simple law, is presented graphically. Experiments also were conducted with gauges embedded in the rock vertically below the line of impact and at an angle of approximately 45&apos; to the vertical. No essential difference was observed in the type of wave obtained with embedded gauges and with gauges on the surface, as may have been anticipated from theory. INTRODUCTION Through the ages great strides have been taken towards improvement of the various techniques applied in the breakage of rock. Indeed, numerous applications of the rock-failure process are an integral part of present-day industry, including oil well drilling. Yet, astonishingly, little is known regarding the behavior of rock under dynamic loading or the mechanism of rock failure. The value of impact loading studies from the point of view of drilling is evident, however, and requires little elaboration because impact of a chisel edge on rock forms the basic action constituting most common methods of drilling. RELATED STUDIES Impact studies of communition and fragmentation conducted by Fahrenwald, et a1,8 Poncelet,l7 Axelson, et a1,2 Piret,16 Hartman and pfleider,ll Charles and deBruyn,5 and others have been of considerable help in understanding rock-breakage phenomena. Further insight into the basic action of drilling and penetration has been obtained by the work of Irving,13 Cherkasov and Shlyapin,6 BOrcherdt,3 Shepherd,19 Shreiner and Pavlova,20 Drilling Research Inc.7 Hartman,10 Appl and Gatley1 and several other investigators. However, knowledge concerning the stresses and strains induced in the rock and bit during impact remains scant. Recent photoelastic studies by Tandanand and Hartman (1961. 1962)22, 23 have shed light on stress distributions and Fracturing produced in plastics by chisel-shaped bits. In the field of transient strain Pulses and their role in rock drilling, the only extensive work has been performed by Drilling Research Inc. (DRI). They attached strain gauges to the shank of a bit and conducted drop-tester studies, using a die-shaped bit to obtain force-time diagrams. Their work led to the conclusion that, for a given rock type, the first peak of force occurs at a fixed level regardless of the total energy in the system, provided it exceeds a certain minimum threshold level. Further, on this basis an explanation was offered for the sequence of events in crater formation as the result of a single blow on rock. PURPOSE OF PRESENT STUDY The investigations reported in this paper were conducted in a manner similar to the DRI approach, but with the objective of determining the strain distribution in the rock around the area of bit impact and, to a limited extent, the strain in the chisel-shaped bit itself. It was expected that a knowledge of the disposition of these strains, along with the rate of attenuation of strain energy in the rock

By Will Mitchell, T. G. Kirkland, C. L. Sollenberger

BENEFICIATION of a Korean scheelite ore has been studied during the past year in the Basic Industries Laboratory at Allis-Chalmers Manufacturing Co. A flowsheet has been recommended including flotation, gravity separation, and a final cleaning by a magnetic separator. The investigation was continued in the field of flotation in order to establish the effect of certain variables on recovery and grade of rougher concentrates. The results of this investigation are recorded here. Mineralogy The scheelite ore was obtained from Korea and was mined from the Sang Dong deposit. This deposit is described as lying in gently dipping metamorphosed sedimentary beds of Cambrian age.&apos; The metamorphism was probably either metasomatic replacement or recrystallization, or both, with subsequent hydrothermal deposition. Igneous bodies in the form of granite porphyry have been found within 7 km of the main shaft and are considered to be a possible source of the mineralizing solutions. The Myobong formation, the host for the Sang Dong deposit, was laid down in middle Cambrian times and consists of series of mudstone, siltstone, shale, and marl, with local stratification of mica schists, hornfels, and tactites. The scheelite is found in quartz bands in the tactites. Although there are six of these bands, only one, the "main bed" averaging 1.75 pct WOs, has been mined to any extent. The ore sample as received in the laboratory was the product of a cone crusher and was all —2 in. The rock appeared to be even textured, medium to fine grained, and gray green in color. No scheelite could be recognized by the unaided eye. However, under ultraviolet light of 2537 A, the scheelite fluoresced and could be distinguished from the gangue. Under the black light, the scheelite showed no definite vein structure but was disseminated throughout the specimen. The raw ore had a specific gravity of 2.96 and weighed about 125 lb per cu ft at —20-mesh Tyler. The —2-in. material was stage crushed through 20-mesh, and samples were cut for mineralogical, chemical, and spectrochemical analyses. Several polished sections were cut from hand specimens. Figs. 1 and 2 show quartz to be the matrix for scheelite. It was reported by Kim2 that the greatest scheelite concentration in the mine is found with a high concentration of quartz and a decrease in the abundance of garnet. Diameters of scheelite particles ranged from 1.2 mm down to less than 50 microns. Spectrochemical analysis showed the ore to be high in aluminum, bismuth, calcium, iron, magnesium, manganese, silicon, tungsten, and with lesser amounts of beryllium, chromium, lithium, sodium, and titanium. Chemical assays showed the —20-

Jan 1, 1952

DURING the past year the Committee on Coal and Coke has been collecting data concerning various points in the bituminous industry about which a large amount of misinformation circulates through the press and, in some cases, through the coal trade papers. The data presented have been compiled by various members, from the most authentic sources available, and where possible cover the period 1913-1924. They will enable comparisons to be made within the industry, and of this and other industries, and will explain some of the differences between conditions existing now and in the prewar period. CAPACITY AND OVER-DEVELOPMENT The capacity of bituminous mines is frequently stated at figures ranging between 800,000,000 to 1,400,000,000 tons per year. Table 1 shows statistics for the industry, mainly from U. S. Geological Survey sources but partly from U. S. Coal Commission reports. Column 3 gives the mine capacity with equipment and labor as of given date, as estimated from the data published by the U. S. Geological Survey. This is calculated for each State by obtaining the total man days worked as. reported by the operators (multiplying average men employed by total days worked at each mine) and dividing this figure into the total production, getting the production per man day; this figure times number of men employed times 308 (a theoretical full working year) equals estimated- full-time capacity. Two major objections are made to this method-one that the total number of men employed is used, instead of the number actually working, and the other that the number of days used only deducts Sundays and five holidays. The first objection is answered by the fact that the same number of men is used in estimating capacity as is used in actual production, and while this number is always from 12 to 20 per cent. more than are actually working, this condition exists at all times, although it is worse at times of maximum output. Few coal men will agree with the conclusion that the use of 308 days is correct, as it is practically impossible to keep any mine working full time at the same

Jan 2, 1926

By Wolfgang Pitsch

INVESTIGATIONS on the above topic have recently been published by Shapiro and Kraussl and Jana and wayman in this journal and by Kessler and Pitsch.- Parts of the results in these papers are in good agreement with each other but there are also some results which are substantially different. The main points of these differences shall be briefly discussed in this communication. Shapiro and Krauss&apos; measured single-surface traces of the habit planes of reversed austenite plates formed within the martensite crystals and deduced from these measurements two distinct habit planes A = (0.174; 0.309; 0.935) and B = (0.375; 0.545; 0.749) within 3 deg. Kessler and pitsch4 found instead by two-surface analysis7 one habit plane n = {0.23; 0.62: 0.75) with a real scatter of 6 deg. The latter observation of a single habit plane apart from a certain scatter is in agreement with most of the investigations of martensite transformations. The differences between these two results are so great that they cannot be explained by experimental error. The purpose of this communication is to show that the A- and B-poles of Shapiro and Krauss are due to an erroneous interpretation of a single-surface trace analysis. The difficulties in the interpretation of such single-surface trace analyses are due to the high symmetry of cubic lattices, from which it follows that there are in general twenty-four equivalent possibilities of plotting a single-surface trace in a pole figure. All these possibilities must be taken into account, when putting different traces from different plates together in order to construct the habit plane. Alternatively the poles of all the traces may be plotted in a unit triangle. This is done in Fig. 1 with twenty-nine traces of different reversed austenite plates, all of this were measured by Shapiro and Krauss in the same plane of a single martensite ther traces taken from Fig. 13 in the Shapiro and Krauss paper&apos; which were determined by electron diffraction. The traces in Figs. 1 and 2 have to be compared with the habits A, B, and n which are under discussion. Therefore the great circles of the poles A, B, and n are plotted in Figs. 3, 4, and 5 together with a 3-deg scatter region for poles A, B and a 6-deg scatter region for pole n. Comparing Figs. 1 and 2 with Figs. 3, 4, and 5 one finds the statements which

Jan 1, 1969

By Harold Markus, Arthur H. Grobe, Gerhard Derge

THE high corrosion resistance possessed by tin under most circumstances, combined with its generally satisfactory appearance and useful physical properties, has led to many and varied uses for the metal. These uses have been partly limited by the fact that tin is an expensive metal, therefore many applications have been developed in which tin has been employed in combination with lead, either by coating, as in tin-lined collapsible tubes, or by the formation of alloys containing various proportions of tin-rich and lead-rich phases, as terne plate. A detailed knowledge of the corrosion characteristics of the tin-lead couple therefore is of general interest and has become specially important at the present time, when every effort is being made to conserve tin as much as possible. The present study. has been limited to carbonate solutions with a pH range from 8.4 to 11.2 so that the results may be related to earlier work on the corrosion of tin and its alloys.1-3,6 In these papers, the effects of a number of anion and cation additions to these solutions have been observed. APPARATUS AND METHOD The electrodes for the corrosion cell were cut from rolled sheet about 1/16 in. thick. The length of all specimens was held constant at 7 in., while the width was varied from 1/2 to 2 in. These electrodes were fastened to brass electrode supports, which were attached to rubber stoppers fitting into tall-type one-liter Pyrex beakers that contained the electrolyte. The lead electrodes were prepared from Omaha pig* and the tin was rolled from a slab of Chempur.? After cutting to size, the sheets were polished with No. I emery paper and cleaned with carbon tetrachloride. The edges, back and upper parts of the specimen were coated with a synthetic lacquer, which was supplemented with beeswax for the lead electrodes. The binding posts were coated with beeswax after the electrodes had been damped. The pH of the electrolyte was controlled? by adjusting the ratio of carbonate to bicarbonate. Approximately 600 ml. of electrolyte was used in each beaker. The entire assembly was placed in an oil bath thermostatically adjusted to operate at 30°C. ± 0.10. Potentials were measured against a saturated calomel electrode connected. to the cell by an agar-agar salt bridge. The carbonate solution used in the salt bridge was the same as that used in the corrosion cell. Currents were measured with a milliam-

Jan 1, 1942

By L. D. Wooddy, Robert Moscrip

The simultaneous solution of the volumerric balance and the unsteady-state equation has been used for several years to make performance calculations for combination drive reservoirs. This method makes possible the calculation of volumetric changes of fluids in the gas cap, oil zone, and aquifer which occur as a result of withdrawals and reservoir pressure changes. It does not provide a means for the determination of reservoir fluid distribution changes corresponding to these vollrmetric changes. A knowledge of the fluid saturation distribution in the reservoir at various stages of depletion is important for the determination of the efficiency of gas and water as oil-displacement media and, therefore, for the reliable predicrion of ultimate oil recovery. To provide this knowledge, the displacement equations are solved simultaneously with the volumetric balance and unsteady-state equations. The described calculation procedure has been used satisfactorily to analyze the past performance and to predict the future behavior of combination drive reservoirs under both primary and pressure-maintenance operations. INTRODUCTION The three basic mechanisms by which oil is displaced from a reservoir are: (1) dissolved gas drive—the displacement of oil by the expansion of liberated solution gas, (2) water drive—the displacement of oil by water which enters the oil zone from the aquifer, and (3) gas cap drive—the displacement of oil by gas which ex- pands into the oil zone from the gas cap. The action of gravitational forces may be effective in increasing the efficiency of the basic drive mechanisms. Gravitational forces favor the segregation both of gas and oil and of oil and water, thus tending to shorten the transition zone between oil and displacing fluids. Most reservoirs produce under the influence of a combination of these drives and are designated "combination drive reservoirs". Fig. 1 is a cross section of a typical combination drive reservoir. A calculation procedure for analyzing the performance of combination drive reservoirs has been developed by combining the displacement equations&apos; with the volumetric balance equation&apos; and the unsteady-state equations. The pressure-production performance and the positions of the gas-oil and oil-water contacts are calculated for several stages of reservoir depletion by solving these equations simultaneously, thus affording a basis for: 1. Determining instantaneous and ultimate oil, gas, and water production under various operating conditions. 2. &apos;Establishing a maximum efficient rate of production, 3. Determining the advantages of pressure maintenance and unitization, and 4. Designing surface installations necessary for primarv and pressure-maintenance operations. DEFINITIONS The calculation procedure for combination drive res-

Jan 1, 1957

By Harold Markus, Gerhard Derge, Arthur Grobe

THE high corrosion resistance possessed by tin under most circumstances, combined with its generally satisfactory appearance and useful physical properties, has led to many and varied uses for the metal. These uses have been partly limited by the fact that tin is an expensive metal, therefore many applications have been developed in which tin has been employed in combination with lead, either by coating, as in tin-lined collapsible tubes, or by the formation of alloys containing various proportions of tin-rich and lead-rich phases, as terne plate. A detailed knowledge of the corrosion characteristics of the tin-lead couple therefore is of general interest and has become specially important at the present time, when every effort is being made to conserve tin as much as possible. The present study has been limited to carbonate solutions with a pH range from 8.4 to 11.2 so that the results may be related to earlier work on the corrosion of tin and its alloys.1-3,6 In these papers, the effects of a number of anion and cation additions to these solutions have been observed. APPARATUS AND METHOD The electrodes for the corrosion cell were cut from rolled sheet about 1/16 in. thick. The length of all specimens was held constant at 7 in., while the width was varied from ½ to 2 in. These electrodes were fastened to brass electrode supports, which were attached to rubber stoppers fitting into tall-type one-liter Pyrex beakers that contained the electrolyte. The lead electrodes were prepared from Omaha pig* and the tin was rolled from a slab of Chempur.† After cutting to size, the sheets were polished with No. I emery paper and cleaned with carbon tetrachloride. The edges, back and upper parts of the specimen were coated with a synthetic lacquer, which was supplemented with beeswax for the lead electrodes. The binding posts were coated with beeswax after the electrodes had been clamped. The pH of the electrolyte was controlled by adjusting the ratio of carbonate to bicarbonate. Approximately 600 ml. of electrolyte was used in each beaker. The entire assembly was placed in an oil bath thermostatically adjusted to operate at 30°C. ± 0.1°. Potentials were measured against a saturated calomel electrode connected to the cell by an agar-agar salt bridge. The carbonate solution used in the salt bridge was the same as that used in the corrosion cell. Currents were measured with a milliam-

Jan 1, 1942

By B. A. Cheadle, C. E. Ells

The ovienlalion of hexagonal a-zirconium crystals in cold-drawn Zircaloy-2 tubes and in both as-extruded and heat-treated Zr-2.5 wt pcl ND tubes has been rrleasured using the inverse Pole - figure technique. Uniaxial tensile tests hare shown the Zil-caloy-2 lubes to hare highly anisotropic delovmation behavior whereas heat-treated Zr-2.5 wt pet Nb tubes are nearly isotropic. The differences in deformation behavior are esbloilred from the observed textures of the tubes and the deformation systems known to oberate in Zircnloy,-3. Tlze vcsults lead to an explanation of the high effective strain observed fov the Zircaloy-2 tubes as colrzpared to heat-treated Zr-2.5 wt pet Nb tubes in restrained end burst tests at 280° to 300°C. THE Zr-2.5 wt pct Nb alloy. when heat-treated by quenching from temperatures slightly below the (a + p)/P phase boundary and subsequently aged at 500°C, has tensile strengths about 50 pct greater than those of 20 pct cold-worked Zircaloy-2.1 There is. therefore, considerable economic incentive to replace Zircaloy-2 with the heat-treated alloy in some in-reactor applications. notably for pressure tubes, where strength is a prime consideration. However, when tubes of Zr-2.5 wt pct Nb fabricated by extrusion and drawing prior to heat treatment were subjected to restrained end-burst tests at 300 °C. the circumferential expansion at failure1 was only 10 pct that of cold-drawn Zircaloy-2 tubes in similar tests,2 Table I. This result was not predicted from uniaxial tensile tests in which the ductilities of the two materials were quite similar.&apos; The detailed requirement for ductility in pressure vessels has not yet been worked out. and comparison of the relative merits of cold-worked Zircaloy-2 and heat-treated Zr-2.5 wt pct Nb is further complicated by the irradiation-induced loss of ductility and hydrogen pickup each will undergo from reactor operation.1,2 Nevertheless. the lower circumferential expansion of the Zr-2.5 wt pct Nb tubes raised serious doubts on the advisability of their use as pressure vessels. For this reason, an investigation to determine the cause for different ductilities of the two types of tubes was initiated. From a study of uniaxial tensile properties and crystallographic orientation it has been found that the fracture ductilities observed in the burst tests can be related directly to the crystallographic ori-

Jan 1, 1965

By Gerhard Derge, Arthur H. Grobe, Harold Markus

The high corrosion resistance possessed by tin under most circumstances, combined with its generally satisfactory appearance and useful physical properties, has led to many and varied uses for the metal. These uses have been partly limited by the fact that tin is an expensive metal, therefore many applications have been developed in which tin has been employed in combination with lead, either by coating, as in tin-lined collapsible tubes, or by the formation of alloys containing various proportions of tin-rich and lead-rich phases, as tcrne plate. A detailed knowledge of the corrosion characteristics of the tin-lead couple therefore is of general interest and has become specially important at the present time, when every effort is being made to conserve tin as much as possible. The present study has been limited to carbonate solutions with a pH range from 8.4 to 11.2 so that the results may be related to earlier work on the corrosion of tin and its alloys. 1-3,6 In these papers, the effects of a number of anion and cation additions to these solutions have been observed. Apparatus and Method The electrodes for the corrosion cell were cut from rolled sheet about 1/16 in. thick. The length of all specimens was held constant at 7 in., while the width was varied from M to 2 in. These electrodes were fastened to brass electrode supports, which were attached to rubber stoppers fitting into tall-type one-liter Pyrex beakers that contained the electrolyte. The lead electrodes were prepared from Omaha pig* and the tin was rolled from a slab of Chempur.† After cutting to size, the sheets were polished with No. I emery paper and cleaned with carbon tetrachloride. The edges, back and upper parts of the specimen were coated with a synthetic lacquer, which was supplemented with beeswax for the lead electrodes. The binding posts were coated with beeswax after the electrodes had been clamped. The pH of the electrolyte was controlled by adjusting the ratio of carbonate to bicarbonate. Approximately 600 ml. of electrolyte was used in each beaker. The entire assembly was placed in an oil bath thermostatically adjusted to operate at 30°C. + 0.1". Potentials were measured against a saturated calomel electrode connected to the cell by an agar-agar salt bridge. The carbonate solution used in the salt bridge was the same as that used in the corrosion cell. Currents were measured with a milliam-

Jan 1, 1942