By C. E. Sims, C. A. Zapffe

AN investigation of the behavior of inclusions in steel several years ago1 led to the conclusion that some of the commonly occurring inclusions in steel have appreciable solubilities, particularly in liquid steel. In the belief that further study and clarification of this matter was warranted, a laboratory study of oxides in liquid steel was started. These oxides are generally the result of deoxidation treatment, and the basis of an understanding of their behavior must be, therefore, the behavior of the deoxidizer in liquid iron. The Fe-Si-O system was selected for the first study, and the apparatus used and experiments conducted are described herein. APPARATUS The apparatus is shown in Fig. I and the system is shown by diagram in Fig. 2. Furnace Atmosphere Commercial hydrogen (1) passes through an orifice (2) into a manometric system that measures the tankside pressure (3) and the back pressure (4) in the system. A water trap (5) guards against excess tankside pressure. A by-pass with stopcocks (6 and 7) is provided, so that the hydrogen can be routed directly from the tank to the furnace if desired. When stopcock 7 is closed and stopcock 6 is open, the gas proceeds through the conditioning train, of which the first unit is a furnace (8) that contains platinized asbestos at 350°C. The temperature is measured by a thermo-couple and potentiometer (9) and is controlled by a slidewire resistance (10). In [ ] this furnace free oxygen is converted to water vapor. The exiting gas passes over a water bath (11) kept slightly below boiling temperature by an auxiliary heating unit (12). This unit also heats a surrounding copper coil (13) containing water, and the heated water rises through a collar (14)

Jan 1, 1942

By M. Dubrovsky, J. W. Evans

A laboratory scale cell (approximately 50 amps current) equipped with a fluidized bed cathode was used in a study of the electrodeposition of cobalt from acidified aqueous sulfate solutions The effect of current density (in the range 0.1 to 1 amp/cm2 of diaphragm), cobalt concentration (4 8 to 100 glliter) and catholyte pH (1 35 to 6 2) on current efficiency and energy consumption were determined. Generally the current efficiency increased with increasing current density and cobalt concentration Current efficiencies were comparable to those reported in the literature for conventional electrowinning

Jan 1, 1981

By A. U. Seybolt

The solubility limit of oxygen in columbium has been determined in the range between 775' and 1100°C by means of lattice parameter measurements and microscopic examination. The solubility is a function of temperature and varies, in the range given above, from 0.25 to 1.0 pct O, respectively. BECAUSE of the marked deleterious effect of oxygen upon the mechanical properties of some of the transition metals, it is desirable to know something about the solubility of oxygen in these metals. The brittleness caused by oxygen in solution is particularly marked in the case of the group VA elements, vanadium, columbium, and tantalum. The solubility of oxygen in vanadium has already been reported in an earlier paper,' and Wasilewski2 has given a value (0.9 wt pct) for the solid solubility of oxygen in tantalum at 1050°C. Brauer3 in 1941 investigated the Cb-0 system up to Cb2O5, but made no real effort to investigate the extent of oxygen solubility in the metal. He made the observation, however, that this solubility must be less than 4.76 atom pct (0.86 wt pct) oxygen. This estimate was made from X-ray diffraction results on the alloys CbO, CbO, and CbO; all alloys consisted of the terminal (Cb) solid solution plus CbO, but the last alloy containing 4.76 atom pct 0 showed only three very weak CbO lines. It is surprising that Brauer, by examining only three alloys, arrived at an estimate of the solubility which agrees very well with the results to be reported herein. Experimental Procedure A columbium strip obtained from Fansteel Metallurgical Products was cut into strips, 0.020x1/2x2 in. Two holes, about 3/16 in. in diameter, were made near the ends of the strips in order to hold them against a flat steel block for mounting in a General Electric X-ray spectrometer for lattice parameter measurements. The same holes were used to hang the specimens inside a fused silica vacuum furnace tube which was part of a Sieverts' gas absorption apparatus. The apparatus and method of adding oxygen gas has been previously described.1 According to the supplier, the columbium obtained had the analysis given in Table I. After degreasing the samples, approximately 0.001 in. was etched from each side of the samples in order to remove possible surface impurities from the last rolling operation. For this purpose the following cold acid pickle was found satisfactory: 8 parts HNO3, 2 parts H2O2 and 1 part HF. Various Cb-O compositions were obtained up to 0.75 wt pct O by the gas absorption and diffusion technique. After the sample had absorbed all the oxygen gas added at 1000°C, an additional 24 hr was allowed for homogenization. This treatment appeared to be adequate, as shown by the linearity of the lattice parameter-composition plot. More concentrated alloys were prepared by arc melting mixtures of Cb and Cb2O5 since it was very time-consuming to make Cb-0 alloys in the neighborhood of 1 pct O, or over, by the diffusion method. When the flat strip specimens were used, they were ready for the X-ray spectrometer after cooling from the Sieverts' apparatus. The cooling rate obtained by merely allowing the hot fused silica furnace tube to radiate to the atmosphere (when the furnace was lowered) was sufficiently fast to keep the dissolved oxygen in solution. Arc-melted alloys were reduced to —200 mesh powder in a diamond mortar, wrapped in tantalum foil, sealed off in evacuated fused silica tubes, and then heat treated as indicated in Table 11. The fused silica tubes were quickly immersed in cold water without breaking the tubes after the heat treatments. The tantalum foil prevented reaction between the fused silica and the sample; there was no reaction between the powdered samples and the foil at 1000°C, but some trouble was experienced at 1100°C. At this temperature level a reaction between the sample and the foil was sometimes observed, which resulted in erroneous parameter values. Experimental Results Hardness Tests: Since most of the X-ray samples were in the form of flat strip, it was convenient to obtain Vickers hardness numbers as a function of oxygen content. Compared to the V-O case,' oxygen hardens columbium much more slowly, presumably because of the larger octahedral volume in colum-bium (about 12.0 compared to 9.3Å3 in vanadium), hence, requiring less lattice strain for solution. The plot of VHN vs wt pct O is shown in Fig. 1.

Jan 1, 1955

By John Dilworth

THIS paper treats primarily of the valuation of developed coal properties by the method of capitalizing their estimated average future earnings. However, in it reference is also made to valuations of undeveloped coal lands and to various methods of appraisal other than by future earnings. FUNDAMENTAL VALUATION PRINCIPLES Before discussing in detail coal property valuations, a few statements bearing on the general subject will be made to present certain of the writer's views on the question as a whole. 1. A certain property at a given time has but, one true value. This is not universally admitted. The appraiser rather frequently finds that a coal owner has in mind three valuations for his holdings; one, the figure at which he feels they should be appraised for taxation purposes; another, the much higher one that should be used if a loan is to he negotiated on the property; and a third, intermediate between the other two, the price for which he would be willing to dispose of his holdings were they for sale. The last is usually nearest to the true value, and because this is so the statement is generally accepted that the fair value of such a property is the price arrived at by negotiation between a willing seller and a willing buyer who are otherwise disinterested. 2. Notwithstanding the foregoing, it is only very generally and approximately true that the proper measure of the value of a given developed1 coal acreage is the unit or per-acre price for which one or more bodies of similar coal in the salve district have been sold recently. To give a few reasons why such a measure of value can not be strictly applied, it may be noted:

Jan 1, 1927

By C. E. Sims, C. A. Zapffe

AN investigation of the behavior of inclusions in steel several years ago1 led to the conclusion that some of the commonly occurring inclusions in steel have appreciable solubilities, particularly in liquid steel. In the belief that further study and clarification of this matter was warranted, a laboratory study of oxides in liquid steel was started. These oxides are generally the result of deoxidation treatment, and the basis of an understanding of their behavior must be, therefore, the behavior of the deoxidizer in liquid iron. The Fe-Si-O system was selected for the first study, and the apparatus used and experiments conducted are described herein. APPARATUS The apparatus is shown in Fig. I and the system is shown by diagram in Fig. 2. Furnace Atmosphere Commercial hydrogen (1) passes through an orifice (2) into a manometric system that measures the tankside pressure (3) and the back pressure (4) in the system. A water trap (5) guards against excess tankside pressure. A by-pass with stopcocks (6 and 7) is provided, so that the hydrogen can be routed directly from the tank to the furnace if desired. When stopcock 7 is closed and stopcock 6 is open, the gas proceeds through the conditioning train, of which the first unit is a furnace (8) that contains platinized asbestos at 350°C. The temperature is measured by a thermocouple and potentiometer (9) and is controlled by a slidewire resistance (10). In [ ] this furnace free oxygen is converted to water vapor. The exiting gas passes over a water bath (11) kept slightly below boiling temperature by an auxiliary heating unit (12). This unit also heats a surrounding copper coil (13) containing water, and the heated water rises through a collar (14)

Jan 1, 1942

By G. C. Gould

The nature of freckle segregation is determined by chemical analyses, microradiograplzy, and electron microprobe. In addition, the influence of chemistry variation on freckle formation is studied in laboratory experiments. It is demonstrated that controlled laboratory solidification can produce freckle segregation. "FRECKLE" segregation is a discontinuous, rod-like segregation observed in vacuum consumable -electrode ingots. Figs. 1 and 2 show this segregation as pencil-like, dark etching areas of segregation found in longitudinally and transversely sectioned consumable-electrode ingots. In most cases the segregation is perpendicular with respect to gravity and parallel to the longitudinal axis of the ingot. The segregation is most often encountered at or around midradius in large vacuum consumable-electrode ingots. The austenitic alloys, A-286* and 718, † have shown particular susceptibility to this mode of segregation. The origin of these rodlike pockets of segregation is not well-understood. It has been suggested that the segregation is a result of a portion of the electrode dropping off and passing through the arc un-melted. On the other hand, smeltzer1 has demonstrated the freckle segregation in A-286 to be comprised of low-melting constituents relative to the matrix melting point. The discontinuous nature of the segregation is the most perplexing facet of the freckle-segregation problem. It was to gain some insight into this part of the problem that this work was undertaken. I) PROCEDURE At the outset of the work identification of the phases present and the elements concentrated in the freckle areas was undertaken. The electron micro-probe was used to determine general enrichment as well as -specific phase chemistry. Microradiography using cobalt and chromium radiation was also used on the freckle areas again to determine the elements involved in the segregation. X-ray diffraction patterns were made from portions of these same foil specimens. Optical microscopy and Knoop hardness measurements were also used

Jan 1, 1965

By Klaus Schwerdtfeger

The equilibria in the Cr-N system have been investigated in the temperature range 1100° to 1310°C by reacting chromium powder with Nz-Hz gas mixtures. The solubility of nitrogen in chromium in equilibrium with chromium subsitvide ("Cr,N") is given by Chromium subnitride is nonstoichiotnetric; its nitrogen content is always less than that corresponding to the formula CrzN. The lattice paranzeters of quenched samples have been measured; c, and a. parameters are found to increase with increasing nitrogen content. The growth rate of the subnitride layer on chromium plates was measured by a thermogravimetric technique, using a silica spring balance. The self-diffu-sivity obtained from the theoretical analysis of the parabolic rate constant is found to decrease with increasing nitrogen content, i.e., with decreasing vacancy concentration in the nitrogen sublattice. The intrinsic nitrogen diffuivity is derived from another series of rate measurements using "CrzN" plates; the intrinsic diffusivity, DN = 3.2 X 10-a cmZ sec-' at 1200 C, is found to be essentially independent of- the subnitride composition. The concentration gradient was measured in a chromium subnitride layer by the X-ray method and found to be consistent with the derived diffusivity value. TWO chromium nitrides are known to exist:' the nonstoichiometric subnitride "CrzN" and the nitride CrN. In the present work the kinetics of the formation of chromium subnitride from chromium and nitrogen have been investigated at 1100" and 1200°C. In additional experiments the relevant equilibria have been measured. The data are used to evaluate the diffusivity of nitrogen in chromium subnitride. Since chromium nitrides are often found in chromium-containing steels, the results are expected to be helpful in the interpretation of the chemical reactions between chromium steels and nitrogen. Equilibria in the Cr-N system have been determined by several investigators.2"3 The rate of nitriding of chromium was measured by Arkharov et a1 .' in ammonia in the temperature range 800" to 1200°C. The parabolic rate law was observed. Due to the undefined nitrogen activity of the ammonia atmosphere, it is dif- ficult to interpret these rate data theoretically. An additional difficulty arises from the fact that the two-layer scale consisting of CrN and "Cr2N" was formed at the temperatures below 1030°C. The rate of nitriding of technical chromium (95 pct) was measured by Zaks in nitrogen at -1 atm in the temperature range 800" to 1300°C. EXPERIMENTAL METHODS The chromium samples were reacted with Nz-HZ gas mixtures in a vertical tube furnace, wound with Pt-10 pct Rh resistance wire. The gas-tight reaction tube was of high-purity recrystallized alumina. In nitrogen solubility measurements the nitrogen content of chromium was determined by the Kjeldahl method, on samples quenched in the cold part of the furnace. The nonstoichiometry of the subnitride and the nitriding rates were measured thermogravimetrically using a sensitive (+0.1 mg) silica spring balance. For the equilibrium measurements samples of 1 g of chromium powder contained in high-purity alumina crucibles were used. In order to remove most of the oxygen and nitrogen impurities from the chromium, the samples were initially annealed in purified hydrogen until a constant weight was obtained. The chromium plates (approximate dimensions 2 by 1 by 0.08 cm) used for the rate measurements were machined from ingots obtained by arc-melting of iodine-processed chromium. According to manufacturers' specifications the purity of the chromium powder was 99.9 pct Cr and that of the iodine-processed chromium 99.99 pct Cr. Our own spectroscopic analysis of the chromium powder yielded 0.02 pct Fe, 0.05 pct Mn, 0.05 pct Si, and 0.02 pct Ti as major impurities with all the other detectable elements below 0.005 pct. The nitrogen partial pressure of the gas phase was controlled by mixing prepurified hydrogen and nitrogen with constant pressure head capillary flowmeters. Oxygen and water vapor were removed from the mixed gas by passing it through columns of platinized asbestos (450°C) and anhydrone. The gas flowed upward in the furnace with flow rates of 300 to 500 cu cm per min (25"~). Gas tightness of the furnace system was ensured by pressure checks at regular intervals. The furnace temperature was controlled electronically in the usual manner. The reported temperatures were measured with a Pt/Pt-10 pct Rh thermocouple and are estimated to be accurate within ±$C The X-ray measurements were made with a Debye-Scherrer camera and a diffractometer using chromium radiation {\Ka = 2.29092A). EQUILIBRIUM MEASUREMENTS The experimental results of the equilibrium measurements are contained in Tables I to In. Fig. 1 shows the solubility of nitrogen in solid chromium in the temperature range 1100" to 1310°C. In Figs.

Jan 1, 1968

By Herbert Haas

CHEAP power is essential to large-scale mining and metallurgical operations, particularly where fine grinding of large tonnages has to be resorted to, as is the case with an increasing number of. mines treating disseminated copper ores, or low-grade gold ores, in the grinding of which considerable power is consumed. A comparison of the cost of generating power with Diesel engines and steam turbines and a brief discussion of the different factors governing the profitable use of either type of prime mover may be timely in view of the importance of. a cheap supply of power to the mining industry, and the prominence that has lately been given to Diesel engines in America. As many of our most important mines and largest producers of metals are located in sections where neither cheap coal nor water power is available, and the price of oil fuel is increased by long hauls, the Diesel. engine will. become a prime mover of increasing importance. This applies particularly to the Southwestern States, where an ample supply of cold water for condensing purposes is unusual and local climatological conditions interfere in securing the high vacua essential to high turbine efficiency. About 12 times as much water will be required for condensing purposes with steam turbines under general conditions as is needed for jacket-cooling of two-stroke, cycle Diesel engine; four-stroke cycle Diesel engines require only one-twentieth of the cooling water. Another condition favoring the use of Diesel engines is the high load factor at which most mine power plants operate. The influence of load factor on the cost of generating power is shown in Tables 1 and 2 and in Fig. 1.

Jan 7, 1916

By F. R. Hensel

ACCORDING to statements by Guertler,1 Smith and Hamilton were the first to study the copper-titanium alloys, but owing to the presence of large amounts of impurities their data are inconclusive. M. A. Hunter and I. W. Bacon later investigated the electrical conductivity and the temperature coefficients at room temperature. The present writers reported their results2 in November, 1930. Recently Droll published data on copper-titanium alloys3 which agree closely with those obtained by the authors. MATERIAL TESTED The titanium used was in the form of square sintered rods, the analysis of which runs as follows: titanium, 95.4 per cent; silicon, 0.7; iron,1.8; aluminum, 1.4; copper, 0.1; manganese, 0.05. . The ingots were prepared in a high-frequency induction furnace in air atmosphere. Their analyses are given in Table 1. Up to 5 percent titanium the alloys could be forged. Above that amount they were red short and broke up easily. Owing to their rapid absorption of nitrogen and oxygen from the air, the alloys with the higher amounts of titanium tend to form surface films which greatly increase the casting difficulties, especially when small masses of metal are handled. It was, however, possible to prepare sound ingots up to 25 per cent titanium.

Jan 1, 1931

By J. E. Chappelear

We are concerned with the problem of calculating the forces produced by passing waves on a submerged object (in particular a drilling barge) located on the ocean floor. We employ the linearized theory of waves (the Airy1 theory), since solutions are generally more easily obtained in such a theory. It will be indicated how an approximate solution to the problem can be obtained for waves of finite height by use of a linear combination of Airy waves. We shall assume the submerged object has an infinite length, thus neglecting diffraction and making the problem two-dimensional. We find that there is not a considerable difference between our solution and the usual engineering solution. The force, as a function of time, is plotted in Figs. 4 and 5, together with the usual solution for easy comparison. So far, no experiments have been found to compare with the results. As will be shown, the calculations can be extended to waves of finite height (Stokes2-Struik3 waves) in an approximate fashion. This can be done by calculating the force produced by each Fourier component of the wave, separately, and omitting the coupling between the various harmonics produced by Bernoulli's theorem. The problem and its boundary conditions will be briefly stated. We seek a function, +, the velocity potential, which is harmonic, ?2?=0...........(1) and which satisfies the boundary conditions ??/?n =0 .......(2) (the normal derivative of + is zero) on the ocean floor and the sides of the barge, and s??/?y = ?..........(3) on the ocean surface, where s = g/w2........(4) The physical reasons for these choices and an interpretation of ? are given by Lamb.' As previously stated, we assume also that the problem is two-dimensional. We set up our coordinates such that x = 0 is the center of the barge and y = 0 is the ocean floor. The coordinates are shown in Fig. 1, together with the location of the barge on the bottom. Our solution may be decomposed into a function which is symmetric about x = 0,?e, and one which is antisymmetric, +,, ? = ? + ?o...........(5) Thus directly above the barge we have as boundary conditions that for x = 0, ?o = 0, ...........(6) and ??e/?x = 0........(7) Now, far from the barge, we have that (for x positive and assuming the waves are incident from the left) ?e ? Ae cosh ky cos k (x + a) , . . . (8) and ?e ? Ao cosh ky cos k (x + ß) . . . . (9) where + means ". .. approaches ... for x large." Let us put Ae, Ao, and k equal to one, and remember that, in accordance with the derivation of Eq. 3, a sinusoidal time factor is to be supplied. Then we may rewrite Eq. 8 for ?e, and we find that

Jan 1, 1958

By P. A. Laxen, H. R. Spedden

WHEN a mineral particle is fractured, bonds between the atoms are broken. The unsatisfied forces that appear at the newly formed surface are considered to be responsible for the adsorption of ions at the mineral surface. A knowledge of the mechanism and extent of ion sorption from solution onto a mineral surface is of interest in the development of the theory of flotation.'*' Study of the adsorption of sodium from an aqueous solution oftheon quartz offers a simple approach to this complicated problem. The availability of a radioisotope as a tracer element meant that accurate data could be obtained."." Three main factors which appeared likely to affect the adsorption of sodium are: l—concentration of sodium in the solution, 2—concentration of onotherof cations in the solution, and 3—anions present in the solution. Hydrogen and hydroxyl ions are always present in an aqueous solution. By controlling the pH, the concentration of these two ions was kept constant. The variation in thesethe amount of sodium adsorbed with variation in sodium concentration was then determined under conditions standardized in regard to hydrogen ion. The effect of concentration of hydrogen ions and of other cations was also measured. A few experiments were made to get a preliminary idea on the effect of anions. The active isotope of sodium was available as sodium nitrate. Standard sodium nitrate solutions were used throughout these experiments except when the effects of other anions were studied. It was found that sodium adsorption increased with sodium-ion concentration, but less rapidly than in proportion to it. Increasing hydrogen-ion concentration, or conversely decreasing hydroxyl-ion, brings about a comparatively slight decrease in sodium-ion adsorption. Increasing the concentration of cations other than hydrogen or sodium decreases somewhat the adsorption of sodium ion. It would appear as if the kind of anion is a secondary factor in guiding the amount of sodium ion that is adsorbed. Materials and Methods Quartz The quartz was prepared as in previous work in the Robert H. Richards Mineral Engineering Laboratory' except for the refinement of using de-ionized distilled water for the final washing of the sized quartz, prior to drying." To minimize the laborious preparation of quartz, experiments were made to determine .whether the sodium-covered quartz could be washed free of sodium and re-used. The experiments were successful as indicated by lack of Na" activity on the repurified material and by its characteristic sodium adsorption. Table I gives the spectrographic analyses of the quartz used. The quartz ranged from 16 to 40 microns in size, averaging about 23 microns (microscope measurement), and had a surface of 1850 sq cm per g (lot I), 2210 (lot 11) and 2000 (lot 111) as determined by the Bloecher method." Radioactive Sodium Method of Beta Counting for Adsorbed Sodium: Na22, the radioisotope of sodium, possesses convenient properties.' It has a half-life of 3 years, thus requiring no allowance for decay during an experiment. On decay it emits a 0.575 mev ß+ radiation and a 1.30 mev r radiation. The decay scheme is illustrated in the following equation: ß+ NaR-------'8'77NeZ2 3 years The /3 radiation is sufficiently strong to penetrate an end-window type of Geiger-Mueller counting tube. This, in turn, makes it possible to use external counting, a great advantage in technique. Furthermore, it permits the assaying of solids arranged in infinite thickness, while assaying evaporated liquors on standardized planchets. The equipment used was standard and similar to that employed by Chang.R The original active material was 1 ml of solution containing 1 millicurie of Na" as nitrate. This active solution was diluted to 1000 ml. Five milliliters of this diluted active solution was found to give a quartz sample a sufficiently high activity for accurate evaluation of the sodium partition in the adsorption measurements. Also, 1 ml of final solution gave a sufficiently high count for precision on the liquor analyses. The sodium concentration of the diluted active solution was 1.2 mg per liter, so that 6 mg of sodium for 60 ml of test solution and 12 g of quartz was the minimum amount used. The active solution was stored in a Saftepak bottle. Procedure for Adsorption Tests: The method consisted of agitating 12 g of quartz with 60 ml of solution of known sodium concentration for enough time to establish equilibrium between the solution and the quartz surface. The quartz was separated as completely as possible from the solution by filtering and centrifuging. The activity on the quartz and in the equilibrium solution was measured and the partition of the sodium was calculated from the resulting data. The detailed procedure for the adsorption test is set forth in a thesis by Laxen." In brief, it included the following steps: 1—Ascertainment of linearity between concentration of Na" and activity measured. 2—Evaluation of factor to translate activity on solid of infinite thickness in terms of activity on an evaporated active film of minute thickness, on the various shelves of the counter shield. 3—Taking precautions to avoid evaporation of water during centrifuging

Jan 1, 1953

By P. A. Laxen, H. R. Spedden

WHEN a mineral particle is fractured, bonds between the atoms are broken. The unsatisfied forces that appear at the newly formed surface are considered to be responsible for the adsorption of ions at the mineral surface. A knowledge of the mechanism and extent of ion sorption from solution onto a mineral surface is of interest in the development of the theory of flotation.'*' Study of the adsorption of sodium from an aqueous solution oftheon quartz offers a simple approach to this complicated problem. The availability of a radioisotope as a tracer element meant that accurate data could be obtained."." Three main factors which appeared likely to affect the adsorption of sodium are: l—concentration of sodium in the solution, 2—concentration of onotherof cations in the solution, and 3—anions present in the solution. Hydrogen and hydroxyl ions are always present in an aqueous solution. By controlling the pH, the concentration of these two ions was kept constant. The variation in thesethe amount of sodium adsorbed with variation in sodium concentration was then determined under conditions standardized in regard to hydrogen ion. The effect of concentration of hydrogen ions and of other cations was also measured. A few experiments were made to get a preliminary idea on the effect of anions. The active isotope of sodium was available as sodium nitrate. Standard sodium nitrate solutions were used throughout these experiments except when the effects of other anions were studied. It was found that sodium adsorption increased with sodium-ion concentration, but less rapidly than in proportion to it. Increasing hydrogen-ion concentration, or conversely decreasing hydroxyl-ion, brings about a comparatively slight decrease in sodium-ion adsorption. Increasing the concentration of cations other than hydrogen or sodium decreases somewhat the adsorption of sodium ion. It would appear as if the kind of anion is a secondary factor in guiding the amount of sodium ion that is adsorbed. Materials and Methods Quartz The quartz was prepared as in previous work in the Robert H. Richards Mineral Engineering Laboratory' except for the refinement of using de-ionized distilled water for the final washing of the sized quartz, prior to drying." To minimize the laborious preparation of quartz, experiments were made to determine .whether the sodium-covered quartz could be washed free of sodium and re-used. The experiments were successful as indicated by lack of Na" activity on the repurified material and by its characteristic sodium adsorption. Table I gives the spectrographic analyses of the quartz used. The quartz ranged from 16 to 40 microns in size, averaging about 23 microns (microscope measurement), and had a surface of 1850 sq cm per g (lot I), 2210 (lot 11) and 2000 (lot 111) as determined by the Bloecher method." Radioactive Sodium Method of Beta Counting for Adsorbed Sodium: Na22, the radioisotope of sodium, possesses convenient properties.' It has a half-life of 3 years, thus requiring no allowance for decay during an experiment. On decay it emits a 0.575 mev ß+ radiation and a 1.30 mev r radiation. The decay scheme is illustrated in the following equation: ß+ NaR-------'8'77NeZ2 3 years The /3 radiation is sufficiently strong to penetrate an end-window type of Geiger-Mueller counting tube. This, in turn, makes it possible to use external counting, a great advantage in technique. Furthermore, it permits the assaying of solids arranged in infinite thickness, while assaying evaporated liquors on standardized planchets. The equipment used was standard and similar to that employed by Chang.R The original active material was 1 ml of solution containing 1 millicurie of Na" as nitrate. This active solution was diluted to 1000 ml. Five milliliters of this diluted active solution was found to give a quartz sample a sufficiently high activity for accurate evaluation of the sodium partition in the adsorption measurements. Also, 1 ml of final solution gave a sufficiently high count for precision on the liquor analyses. The sodium concentration of the diluted active solution was 1.2 mg per liter, so that 6 mg of sodium for 60 ml of test solution and 12 g of quartz was the minimum amount used. The active solution was stored in a Saftepak bottle. Procedure for Adsorption Tests: The method consisted of agitating 12 g of quartz with 60 ml of solution of known sodium concentration for enough time to establish equilibrium between the solution and the quartz surface. The quartz was separated as completely as possible from the solution by filtering and centrifuging. The activity on the quartz and in the equilibrium solution was measured and the partition of the sodium was calculated from the resulting data. The detailed procedure for the adsorption test is set forth in a thesis by Laxen." In brief, it included the following steps: 1—Ascertainment of linearity between concentration of Na" and activity measured. 2—Evaluation of factor to translate activity on solid of infinite thickness in terms of activity on an evaporated active film of minute thickness, on the various shelves of the counter shield. 3—Taking precautions to avoid evaporation of water during centrifuging

Jan 1, 1953

By Arthur Knapp

OIL-WELL depletion curves, to be of value, should show when a well or lease may no longer be operated at a profit. The difference, at any time, between the total expenditures and the total income of a lease or well may be called the lease status. Plotting this lease status against time will give a curve subject to more accurate and different interpretations than the barrels-time curves. According to the hypothetical barrels-time curves shown in Fig. 1, well A, at the end of 16 mo., is producing twice as much oil as well B and will continue to produce for another year whereas well B will cease producing in about 6 months. DATA FOR LEASE STATUS-TIME OR DOLLARS-TIME CURVE TIME LEASE MONTHS STATUS Lease purchased for $3000 0 -$ 3,000 No expenses chargeable to lease for 3 mo 2 - 3,000 Well A is started; cost of drilling for month is $16,000 3 - 19,000 Well is completed at additional cost of $10,000 4 - 29,000 Well A is brought in and flows 10,000 bbl. first month (see Fig. 1). Necessary to invest in tanks, boilers, pipe lines, etc.: difference between expenditures and receipts gives profit for month of $5,000 5 - 24,000 Investment is small, cost of operating well A is small, so profits are $15,000 6 - 9,000 Well ceases to flow so there is additional investment for pumping equipment and additional operating expense; net earnings from 6,000 bbl. of oil produced is $4,000.... 7 - 5,000 Lease operation now becomes normal and curve becomes smooth 8 - 500 9 2,000 10 4,500 11 6,000 12 7,700 13 8,700 14 9,000 15 9,500 16 10,000

Jan 1, 1921

By B. T. Brady, Wilson Blake

One of the more widespread experimental procedures currently used in experimental rock and soil mechanics work involves the use of a short circular cylinder loaded axially between nonrigid end plates1-5 (Fig. 1a and b). It is widely recognized 6 that a number of undesirable features are connected with this test procedure ; the most noteworthy of these is the development of a nonuniform stress distribution throughout the specimen resulting from an elastic mismatch between the specimen and the end plates. In general, the end plates and specimen possess different elastic properties. As a result of this elastic mismatch, the uniform distribution of stress and strain applied to the end plates is altered at the interface, the degree of which is dependent not only on the magnitude of the elastic mismatch but also on whether there is any relative movement between the specimen and the end plate. A convenient measure of the elastic mismatch is the ratio (vp/Ep) / (v8/E3), where v and E are Poisson's ratio and Young's modulus and the subscripts s and p refer to the specimen and end plate, respectively. For most tests that use steel end plates, (v8/E8) is greater than (vp/Ep) ; i.e., the specimen tends to expand or contract laterally more than the end plates. Because of the frictional restraint offered by the end plates, shearing stresses are developed at the interface that, for compression testing, act inward producing a "clamping" effect (Fig. lc). The effect of this "clamping" is to produce a state of triaxial stress throughout the specimen. Fig. Id illustrates the coordinate system and stress nomenclature used. In a homogeneous, elastic two-dimensional plate loaded uniaxially at the edge, a uniform stress distribution is obtained at a distance from the

Jan 1, 1972

By Woolsey McA. Johnson

Independently of the recognized chemical reactions involved in the production of metallic zinc, the process is affected by physical conditions in efficiency, and by commercial as well as technical economy. To offer some observations concerning these conditions is the purpose of the present paper. Among the important elements of this problem is the physical nature of the particles constituting the mass of zinc oxide to be reduced. This may be the result, either of the manner of the original deposition of the mineral, or of the treatment to which it has been subjected in the roasting-furnace. The physical character of the reducing-agent is another important factor, since the carbon of some coals is much more active in reduction than that of others. The degree of fineness, whether of ore or coal, or both, likewise plays a significant part. These factors, together with the physical admixture of foreign substances with the ore, may give rise also to chemical " side-reactions," sometimes hindering or retarding, and sometimes accelerating, the reduction. Finally, thermal conditions, including the relative conductivity of the materials, deserve to be taken into account. In firing a furnace with retorts charged with a mixture of roasted ore and coal, the first reaction is naturally the boiling-off of the contained water; the next is the distillation of the light hydrocarbons from the coal; the next is the reduction of the iron oxide to protoxide and sub-oxide successively, and then to metallic sponge; and the final reaction is the reduction of the zinc oxide in the ore by the carbon to metallic zinc. This reaction commences at 1,022o to 1,060o C., according to the physical nature and condition of the coal and ore. Since the retort and the charge are far from being good con-

Jan 1, 1908

Commonwealth of Pennsylvania, Department of Internal Affairs, Topographic and Geologic Survey, Harrisburg, Pa George H. Ashley, State Geologist All available printed Bulletins may be obtained through the Commonwealth of Pennsylvania, Division of Documents. Where a price has been set on the publication, checks should be made out to the Commonwealth of Pennsylvania. A Syllabus of Pennsylvania Geology and Mineral Resources has recently been published by the Survey as Bulletin G1, and consists of a general survey of the state An appendix of this bulletin also gives a complete bibliography of Survey publications It will be sent upon request. The State Geological Survey has gone through several phases and reorganizations, publications of three of them being numerous and important A fire, in 1927, destroyed supplies of many of the papers of the present Survey. Available bulletins of the present Survey are: Bulletin M6: Bituminous coal fields of Pennsylvania, in 4 parts available as follows: pt 1, General description of coal, 50 cents; 3, Bituminous coal resources, 25 cents, 4, Analyses of bituminous coals, 25 cents Bulletin M10, Fire clays of Pennsylvania; Mll, Molding sands of Pennsylvania; M12, Anthracite culm and silt (1928); M13, Feldspar in Pennsylvania; M14, Magnetite deposits of French Creek (1931); County Report C1, Adams County, pt 1, Geology and geography (in press), County Report C2, Geology and mineral resources of Greene County (in press); Topographic and Geologic Atlas A5, New Castle Quadrangle (1929), $1; Topographic and Geologic Atlas A27, Pittsburgh Quadrangle (1929), $1; Topographic and Geologic Atlas A168, Lancaster Quadrangle (1930), $1. The present Survey has also issued a number of short mimeo¬graphed bulletins any of which will be sent upon request Briefly they are: No. 15, Mineral resources of Pennsylvania; 20, Iron ores; 28, Magnesite; 40, White clay deposits, Monroe County; 45, White clay deposits, central Pennsylvania; 47, Manganese, Eastern Pennsylvania, 48, Pyrite from bituminous coal mines; 59, Bog

Jan 1, 1933

By S. E. Bronisz, J. O. Brittain

Experiments have been carried out to study the effect of an applied stress on strain aging in steel. It was found that the stress-induced strain aging reaction proceeds rapidly in the temperature range of 0° to 60°C. The variation of stress-induced strain aging with plastic strain, aging time, and temperatures is reported. The activation energy for the stress-induced strain aging was found to be 10,000 cal per mol for the steel used in this investigation. VARIOUS observations1-5 have been made of the influence of an applied stress upon the yielding of iron and steel. However, there have been only cursory studies of the effect of an applied tensile stress upon strain aging in iron and steel1,2 The following represents the results of a preliminary study of strain aging as influenced by the application of an external tensile load during the aging process. For the most part, previous experimental work on strain aging can be classified into two parts. First, the experimental technique involved a direct determination of mechanical properties of a suitable specimen that has been plastically deformed to a constant strain and aged generally at a temperature of the order of 200°C, with the aging times varying from about 1/10 to 2 hr.6-8 The second classification of strain aging experiments involves an indirect determination of strain aging by means of physical property such as electrical resistivity or internal friction as a function of the aging time at a constant temperature and strain.9-12 The latter results have

Jan 1, 1961

By Charles Barrett

RECRYSTALLIZATION textures-the orientations of grains after recrys-tallization-have been studied extensively not only because of their metallurgical importance but also because of the information they yield regarding the atomic movements during recrystallization. Recrystallized grains must possess the same orientations as the submicroscopic nuclei from which they have grown, and thus they offer a direct road by which experimenters can penetrate the submicroscopic realm. Many perplexing results have come of these studies, but one of the most striking has been the apparent difference in behavior between single crystals and polycrystalline grains. For example, Burgers and Louwerse have shown' that when single crystals of aluminum are deformed by compression and are recrystallized (at 600° C.) the new grains appear with orientations that are different from the orientations of the deformed crystal in which they grew; but polycrystalline specimens, on the other hand, appear to have a [110] fiber texture both before and after recrystal-lization and thus to retain their texture during recrystallization. This apparent difference between the habits of single crystals and small grains is the subject of the first part of the present research and has been explained by findings reported herein. A similar situation appears to exist for aluminum when elongated or drawn into wires, for single crystals alter their orientation2,3 and polycrystalline wires retain their texture 4,1 6 upon recrystallization after elongation (at least with high-purity alumi-num), and it is possible that the explanation found in this paper for compression can be extended to cover elongation and other types of deformation as well. The second part of this paper deals with the theory of recrystallization textures. In the most successful theory for aluminum recrystallized after compression,1 much weight is given to the orientation of highly stressed nuclei in the deformed material. Taylor's "local distortions" are assumed to exist along the slip planes where displacement has occurred, consisting of fragments rotated in a specific way with reference to the slip plane and slip direction; namely, about an axis lying in the slip plane perpendicular to the slip direction. 1,7,8,9

Jan 1, 1940

By Charles S. Barrett

Recrystallization textures—thc orientations of grains after recrys-tallization—have been studied extensively not only because of their metallurgical importance but also because of the information they yield regarding the atomic movements during reerystallization. Recrystallized grains must possess the same orientations as the submicroscopic nuclei from which they have grown, and thus they offer a direet road by which experimenters can penetrate the submicroscopic realm. Many perplexing results have come of these studies, but one of the most striking has been the apparent difference in behavior between single crystals and polyerystalline grains. For example, Burgers and Louwerse have shown1 that when single crystals of aluminum are deformed by compression and are reerystallized (at 600' C.) the new grains appear with orientations that are different from the orientations of the deformed crystal in which they grew; but polycrystalline specimens, on the other hand, appear to have a [110] fiber texture both before and after reerystallization and thus to retain their texture during recrystallization. This apparent difference between the habits of single crystals and small grains is the subject of the first part of the present research and has been explained by findings reported herein. A similar situation appears to exist for aluminum when elongated or drawn into wires, for single crystals alter their orientation 2,3 and polycrystalline wires retain their texture"5*" upon recrystallization after elongation (at least with high-purity aluminum), and it is possible that the explanation found in this paper for compression can be extended to cover elongatioil and other types of deformation as well. The second part of this paper deals with the theory of reerystallization textures. In the most successful theory for aluminum reerystallized after compression,1 much weight is given to the orientation of highly stressed nuclei in the deformed material. Taylor's "local distortions" arc assumed to exist along the slip planes where displacement has occurred, consisting of fragments rotated in a specific way with reference to the slip plane and slip direction; namely, about an axis lying in the slip plane perpendicular to the slip direction.1,7,89

Jan 1, 1940

By Charles S. Barrett

Recrystallization textures—thc orientations of grains after recrys-tallization—have been studied extensively not only because of their metallurgical importance but also because of the information they yield regarding the atomic movements during reerystallization. Recrystallized grains must possess the same orientations as the submicroscopic nuclei from which they have grown, and thus they offer a direet road by which experimenters can penetrate the submicroscopic realm. Many perplexing results have come of these studies, but one of the most striking has been the apparent difference in behavior between single crystals and polyerystalline grains. For example, Burgers and Louwerse have shown1 that when single crystals of aluminum are deformed by compression and are reerystallized (at 600' C.) the new grains appear with orientations that are different from the orientations of the deformed crystal in which they grew; but polycrystalline specimens, on the other hand, appear to have a [110] fiber texture both before and after reerystallization and thus to retain their texture during recrystallization. This apparent difference between the habits of single crystals and small grains is the subject of the first part of the present research and has been explained by findings reported herein. A similar situation appears to exist for aluminum when elongated or drawn into wires, for single crystals alter their orientation 2,3 and polycrystalline wires retain their texture"5*" upon recrystallization after elongation (at least with high-purity aluminum), and it is possible that the explanation found in this paper for compression can be extended to cover elongatioil and other types of deformation as well. The second part of this paper deals with the theory of reerystallization textures. In the most successful theory for aluminum reerystallized after compression,1 much weight is given to the orientation of highly stressed nuclei in the deformed material. Taylor's "local distortions" arc assumed to exist along the slip planes where displacement has occurred, consisting of fragments rotated in a specific way with reference to the slip plane and slip direction; namely, about an axis lying in the slip plane perpendicular to the slip direction.1,7,89

Jan 1, 1940