Receipts General Funds: Initiation fees ' 6,008.50 Arrears of dues 1,772.69 Current dues 46,576.56 Advance dues 1,820.97 Sale of binding 10,554.43 Sale of advertising 6,003.42 Sale of Transactions 3,237.07 Sale of special editions ' 1,722.50 Sale of Bulletins and. pamphlets ' 2,263.95 Miscellaneous Receipts; Interest on investments and deposits 450.06 Sale of pins and fobs 312.80 For the collection of checks 161.84 From Finance Committee, Feb., 1916, Meeting 101.02. Subscriptions to the land fund 86.14 Arizona Meeting refund from N. Y. Central Railroad.. 52.48 Local Section refund from N. Y. Central Railroad.... 31.85 Miscellaneous 425.68 Total Receipts General Funds 81,611.96 Cash balance Dec. 31, 1913 1,063.39 $82,675.35

Jan 2, 1917

By A. L. Labbe, J. J. Donoso

Hard-won experience in the operation of smelting plants has pointed the way to the most efficient design and economical operation of a baghouse system for recovery of metallurgical fumes. This paper treats of the principles governing bag filtration and the factors most directly affecting bag life. Methods for temperature conditioning of smoke previous to filtering are described and the evolution of bag shaking mechanisms is brought up to date. THE history of the bag filter process, as applied to the recovery of metallurgical fumes, goes back to 1876, when the Lone Elms Works of Joplin, Missouri, erected a two-section baghouse for filtering fumes from Scotch Hearth lead smelting furnaces. By modern standards this installation was crude, but the basic operating principles remain essentially the same today. Great progress, however, has been made in the mechanization of the process by the use of devices for mechanically and automatically cleaning bags of adhering fumes, in the use of instruments for recording and controlling the variables affecting baghouse operation, and in the conditioning of the smoke previous to filtering. The principles governing bag filtration of fumes were investigated in 1929 by A. J. Seitz of American Smelting and Refining Co., and he arrived at the following conclusions: 1. Pressure on Bags at Constant Volume: The rate at which the pressure builds up in a bag with constant volume is directly proportional to the time, with the same kind of smoke and dust burden (fig. 1). 2. Pressure on Bags for Change in Volume: With equivalent smoke and dust burden, the bag pressure increases with the square of the increase in volume. The rapid increase in pressure is due to (1) increase in volume, (2) increase in amount of dust on the bag, and (3) more intense packing of the dust at higher velocity (fig. 2). 3. Effect of Intensive Filtering on Pressure: Since the pressure builds up directly as the square of the volume, with the same smoke and dust burden, it is necessary to shake the bags in that increased ratio, and vigorously, to keep the pores of the bag open and pressure down. This increases the wear on the bags and the dust losses. 4. Effect of Shaking on Dust Losses: The losses are in direct proportion to the frequency of shaking because the loss takes place immediately after shaking, before the bag seals itself. Tests show that with hand shaking the last 20 pct of the removable dust requires seven times more shaking per unit weight of dust than the first 80 pct. 5. Effect of Fineness of Dust on Losses: The fineness of the dust particle increases the loss in two ways: (1) When the bag is clean a greater percentage of it will pass through before the bag seals itself; (2) fine material penetrates farther into the bag pores, building up pressure faster and necessitating more shaking, thereby increasing the loss. The physical principle of operation of the bag filter is simply the separation of solids from a gaseous carrier through a porous medium, and is analogous to the filtration of solids from liquid carriers. Basically, the mechanics of the process are as follows: Fume-laden gases drawn from the operating fur-

Jan 1, 1951

By J. R. Szedon, T. L. Chu, G. A. Gruber

Amorphous adherent filnzs of silicon dioxide have been deposited on silicon substrates by the oxidation of silane at temperatures ranging from 650 to 1050C. Various diluents (argon, nitrogen, hydrogen) were used to suppress the formation of SiO2 in the gas phase. Deposition rates of the oxide were determined over the temperature range in question as functions of' re-actant flow rates. Etch rate studies were used for a cursory comparison of structural properties of deposited and thermally grown oxides. From electrical evaluation of metal-insulator-silicon capacitors it was determined that the interface charge density of deposited films is similar go that of dry-oxygen-grown films in the 850° to 1050 C temperature range. Deposited films exhibit several ionic instability effects which differ in detail from those reported for thermal oxides. Stable passivating films of silicon nitride over deposited oxides appear to be practical for use in silicon planar device fabrication. Such films can be prepared under temperature conditions which have less effect on substrate impurity distributions than in the case of grown oxides. AMORPHOUS silicon dioxide (silica) is compatible with silicon in electrical properties and is the most widely used dielectric in silicon devices at present. Silica films can be prepared by the oxidation of silicon or deposited on silicon or other substrate surfaces by chemical reactions or vacuum techniques. The ability of thermally grown silicon dioxide films to passivate silicon surfaces forms one of the practical bases of the planar device technology. Properly produced and treated films of grown SiO 2 can have low densities of interface charge (-1 X 10" charges per sq cm) and can be stable as regards fast migrating ionic sgecies. 1 To maintain these properties, even with an otherwise hermetically sealed ambient, the Sia layers must be at least l000 A thick. Such thicknesses require oxidation in dry oxygen for periods of 7.8 hr at 900°C or 2 hr at 1000°C. Although oxidation in steam or wet oxygen can reduce these times to 17 and 5 min, the resulting oxides must be annealed to produce acceptable levels of interface charge., Oxidation or annealing involving moderate to high temperatures for extended periods of time can be undesirable. Under some conditions, there can be changes in the distribution of impurities within the underlying substrate. A chemical deposition technique using gaseous am-bients is particularly attractive and flexible for preparing oxide films. With a wide range of deposition rates available, films can be produced under condi- tions of time and temperature less detrimental to impurity distributions in the silicon than in the case of thermal oxidation. The pyrolysis of alkoxysilanes, the hydrolysis of silicon halides, and various modifications of these reactions are most commonly used for the deposition of silica films.3 Silica films obtained in this manner are likely to be contaminated by the by-products of the reaction, organic impurities, or hydrogen halides. The use of the oxidation of silane for the deposition process has been reported recently.4 The deposition of silica films on single-crystal silicon substrates by the oxidation of silane in a gas flow system has been studied in this work. The deposition variables studied were the crystallographic orientation of the substrate surface, the substrate temperature, and the nature of the diluent gas. The electrical charge behavior of Si-SiO2-A1 structures prepared under various conditions was investigated by capacitance-voltage (C-V) measurements of metal-insulator-semiconductor (MIS) capacitors. The experimental approaches and results are discussed in this paper. 1) DEPOSITION OF SILICA FILMS The overall reaction for the oxidation of silane is: The equilibrium constants of this reaction in the temperature range 500° to 1500°K, calculated from the JANAF thermochemical data,= are shown in Fig. 1. In addition to the large equilibrium constants, the oxidation of silane is also kinetically feasible at room temperature and above. However, the strong reactivity of silane toward oxygen tends to promote the nucleation of silica in the gas phase through homogeneous reactions, and the deposition of this silica on the substrate would yield nonadherent material. The formation of silica in the gas phase can be reduced by using low partial pressures of the reactants. Argon, hydrogen, and nitrogen were used as diluents in this work. 1.1) Experimental. The deposition of silica films by the oxidation of silane was carried out in a gas flow system using an apparatus shown schematically in Fig. 2. Appropriate flow meters and valves were used to control the flow of various reactants, i.e., argon, hydrogen, nitrogen, oxygen, and silane. Semiconductor-grade silane, argon of 99.999 pct minimum purity, oxygen of 99.95 pct minimum purity, and nitrogen of 99.997 pct minimum purity, all purchased from the Matheson Co., were used without further purification. In several instances, a silicon nitride film was deposited over the silica film. This was achieved by the nitridation of silane with ammonia using anhydrous ammonia of better than 99.99 pct purity supplied by the Matheson CO.' The reactant mixture of the desired composition was passed through a Millipore filter into a horizontal water-cooled fused silica tube of 55 mm

Jan 1, 1969

By W. O. Philbrook, K. Natesan

A mathematical model was derived for the temperature change in a particle undergoing heterogeneous chemical reaction and heal exchange with a stream of fluid. The model has been applied specifically to the exothermic oxidation of spherical particles of zinc sulfide. Very good agreement was obtained between the theoretical prediclion and experimental observation. It was found that at no stage of the reaction was the particle subjected to a state of thermal instability. In studies of gas-solid reactions, it is generally assumed that the gaseous and the solid phases are at the same temperature throughout the reaction period. This is not strictly true since most of the reactions are either exothermic or endothermic in nature. This paper deals only with heterogeneous gas-solid reactions of noncatalytic type. In the case of exothermic reactions (e.g., roasting of sulfides), there may result an increase in temperature of the particle due to the release of the heat of reaction, and this increase in temperature may enhance the reaction rate and thus cause further release of heat. Such a "spiralling" effect may lead to a thermally unstable situation within the particle. On the other hand, in the case of endothermic reactions (e.g., calcination of limestone), there may occur a decrease in temperature of the particle as the reaction proceeds, leading to a virtual "quenching" of the reaction front. A general discussion of autothermic processes with emphasis on properties and reactor design is given by Van Heerden. 1 Levesque and cubicciotti 2 observed self heating of the sample in the oxidation of thorium. Anous et al. 3 observed self cooling of the sample in their dehydration studies on chrome alum. Cannon and Denbigh, 4 and Ong et al.5 reported self heating of the sample in their studies of the kinetics of oxidation of zinc sulfide. A typical plot of heat generation and heat loss rates with reaction temperature is shown in Fig. 1.'14 The Sigmoid curve represents the heat generation rate while the straight lines represent the heat loss rate. The main objectives of this analysis are to estimate the temperature increase of a single particle undergoing an exothermic reaction and to study the possibility of a thermally unstable situation within the particle. Also, a study of the dependence of the tempera- ture increase on different process variables has been attempted. A "she ll-by-shell" method has been proposed to analyze the problem. The shells may be made as small as necessary, and equations may be set up for heat transfer by various mechanisms. Such equations will have to be solved for each shell, with the boundary conditions for ith shell being obtained from the (i - 1)th shell, using a high speed digital computer. The oxidation of spherical particles of zinc sulfide is considered for this analysis, but the treatment is general enough to be applicable to other reactions and particle shapes. The oxidation reaction can be written as AH =« -115 kcal/mole ZnS [1] Such a reaction has been found to proceed in a topo-chemical manner; i.e., as the reaction proceeds, a progressively thicker outer shell of zinc oxide is formed, while the inner core of unreacted sulfide decreases. It has been found experimentally, both in the present work and in the previous investigations,4-6 that the particle retains its original dimensions. Therefore, at any given time, the particle may be

Jan 1, 1970

By John M. Hartman

TWO systems are used for heating air in blast-furnace operations: I. The double surface system, in which a cast-iron pipe is heated on the outer surface, and, at the same time, heats the blast from its inner surface. This is simple in operation and gives a continuous effect, but is limited by 1100" F. as a maximum temperature of the blast. 11. The single surface system, by which large surfaces of fire-brick are heated, and air passed over the heated surface, absorbing the heat and carrying it on to the furnace. This system is more comylex than the double surface, as it invoives the reversing of the air and gas every hour and a half. The single surface system has two advantages: 1. The blast can be heated to a temperature of 1800° F. 2. The stoves are indestructible. From recent experience it has been found that 1300" F. to 1400' F. is the best average temperature for economy of coal for safe working. This is equivalent to a saving of 11/2 to 2 cwt. of coal per ton of iron over the extreme limit of cast-iron stoves. Independently of this, it is a strong point in favor of this system that the blast can be raised to a temperature of 1800° F. within an hour when the hearth is getting cold. All furnacemen know the ralue of a hot hearth for quality and quantity of iron. Cooling of a hearth occurs from leaky tuyeres, scaffolds, or heavy burden. When there is not sufficient coal at the tuyeres to seize on the oxygen of the entering air and convert it at once to carbonic oxide, there will not be enough heat to liquefy the cinder. Black cinder and poor iron are the results. The remedy is additional heat from the blast. If the stoves will give 1800" in place of 1100°, it is obvions that the furnaces will get around sooner, and without waiting for a change of burden at the tunnel head to bring extra coal to the hearth. The heat absorption caused by a leaky tuyere will chill the hearth and drive the zone of fusion higher up in the furnace. This loss must be supplied, and the calorics lost to the hearth must be regained before good iron can be made. Take another case: A furnace carefully burdened on No. 1 iron, during a spell of damp weather, goes on to No. 2 or No. 3. Heat is lost to the furnace through absorption by the moisture, and less burden must be carried in order to get back on No. 1. When the

Jan 1, 1879

By John M. Hartman

(Read at the Wilkes-Barre Meeting, May, 1877.) Two systems are used for heating air in blast-furnace operations I. The double surface system, in which a cast-iron pipe is heated on the outer surface, and, at the same time, heats the blast from its inner surface. This is simple in operation and gives a continuous effect, but is limited by 1100° F. as a maximum temperature of the blast. II. The single surface system, by which large surfaces of fire-brick are heated, and air passed over the heated surface, absorbing the heat and carrying it on to the furnace. This system is more complex than the double surface, as it involves the reversing of the air and gas every hour and a half. The single surface system has two advantages: 1. The blast can be heated to a temperature of 1800° F. 2. The stoves are indestructible. From recent experience it has been found that 1300° F. to 1400° F. is the best average temperature for economy of coal for safe work¬ing. This is equivalent to a saving of 12 to 2 cwt. of coal per ton, of iron over the extreme limit of cast-iron stoves. Independently of this, it is a strong point in favor of this system that the blast can be raised to a temperature of 1800° F. within an hour when the hearth is getting cold. All furnacemen know the value of a hot hearth for quality and quantity of iron. Cooling of a hearth occurs from leaky tuyeres, scaffolds, or heavy burden. When there is not sufficient coal at the tuyeres to seize on the oxy¬gen of the entering air and convert it at once to carbonic oxide, there will not be enough heat to liquefy the cinder. Black cinder and poor iron are the results. The remedy is additional heat from the blast. If the stoves will give 1800° in place of 1100°, it is obvious that the furnaces will get around sooner, and without waiting for a change of burden at the tunnel head to bring extra coal to the hearth. The heat absorption caused by a leaky tuyere will chill the hearth and drive the zone of fusion higher up in the furnace. This loss must be supplied, and the calories lost to the hearth must be regained before good iron can be made. Take another case : A furnace carefully burdened on No. 1 iron, during a spell of damp weather, goes on to No. 2 or No. 3. Heat is lost to the furnace through absorption by the moisture, and less burden must be carried in order to get back on No. 1. When the

Jan 1, 1878

By P. S. Kotval

THE nominal composition of "hconel" alloy 718 is 53 pct Ni-19 pct Cr-19 pct Fe-3 pct Mo-5 pct Cb-0.8 pct Ti-0.6 pct A1-0.05 pct C. The nature of the fine strengthening phase in this alloy has been open to debate. iseelstein' has identified the strengthening phase in the matrix of "Inconel" alloy 718 as a colum-bium-rich fcc y' precipitate. Wagner and Hall2 have noted that the metastable y' precipitate overages to an orthorhombic Ni3Cb precipitate which manifests itself as an acicular phase. These authors thus clarify Kaufman and Palty's earlier suggestion3 that the strengthening phase is orthorhombic NisCb. Wagner and Hall's review also reports work by cometto4 which suggests that the fine strengthening phase is not fcc / but bct with a Ni3V type structure and based on the Ni3Cb composition. Kir man and warringtons have shown by analysis of electron diffraction patterns that the metastable strengthening phase in a 55 pct Ni-15 pct 0-25 pct Fe-5 pct Cb alloy is bct and based on the Ni3Cb composition. Raymond~ has provided electron diffraction evidence which indicates that "y'" in "Inconel" alloy 718 is bct in structure. This note presents unambiguous data on the structure of the strengthening phase in "Inconel" alloy 718* ihe samples of this alloy were provided by courtesy of the ASTM task group on phase identification in 'superalloys. after prolonged aging. The electron diffraction patterns presented show that strengthening phase is not y' but bct as was proposed by cometto,' supported by Raymond,~ and identified by Kirman and warringtons in a similar system. Fig. 1 shows a selected-area diffraction pattern taken from a thin foil of "Inconel" alloy 718. The sample had received a final aging treatment of 1118 hr at 1200°F to precipitate the strengthening phase in the matrix. Fig. 2 is a schematic representation of the features in the diffraction pattern. The matrix orientation is (0i2)~,, as is shown by the indexed zone in Fig. 3. Figs. 4, 5, and 6 illustrate that the pattern, Fig. 1, is composed of three bct zones, viz., (0i4), (2i0), and (i01), respectively. These three zones correspond, respectively, to the alignment of the c axis of the bct unit cell with the [001], [loo], and [OlO] directions of the fcc matrix and serve to illustrate the fully coherent relationship of the precipitate structure with the matrix. The streaking of certain reflections is also consistent with the above orientation relationship. The interpretation of the diffraction effects presented here shows the metastable strengthening precipitate in "Inconel" 718 alloy to be bct in structure and demonstrates that it is not an ordered fcc y' phase.

Jan 1, 1969

By M. D. Hassialis

THE claim is made in a number of patents1,2,3,4 that some compounds of the class known as aryl sulphides have collector properties. One of these patents generalizes the claim to include all aryl sulphides, whose generic formula is R-S¬R[=]-R’ (where x = r,2, . . . ), with the restriction that if the aromatic radicals R, R' contain substituent groups these groups may not contain nitrogen or oxygen. Moses, Hess, and Perkins cite as evidence for their claims the results of flotation tests on Anaconda and Miami copper ores using Biphenyl sulphide, ditolyl disulphide and dinapthyl disulphide as collectors. The use of alkyl sulphides as collectors has also been reported5 with the conclusion that the alkyl sulphides are better collectors than the corresponding aryl sulphides. The experimental work cited appears to confirm this contention. In order to test these claims with respect to diphenyl sulphide, a sample, purchased from the Eastman Kodak Co., was tested against Anaconda ore. The procedure followed was that of Moses, Hess, and Perkins. A sample of ore weighing 500 grams was placed in a laboratory ball mill. To this was added 220 grams of water, 0.06 grams of commercial diphenyl sulphide (1/4 lb. per ton of ore), and 0.8 grams of lime (3 lb. per ton of ore). The material was ground until 93 per cent passed a 65mesh screen. This pulp was diluted to 16 per cent solids. A sample of the diluted pulp was placed in a Minerals Separation type of laboratory flotation cell. After a 2-min. agitation period, pine oil was added and the froth collected for a period of 15 min. This test recovered 68 per cent of the copper, with a ratio of concentration of 6.8: 1. The tailing assay was 0.3 per cent Cu. Moses, Hess and Perkins attained a recovery of 75 per cent, with a ratio concentration of 12: 1. Although these results do not compare too well with those of Moses, Hess and Perkins, subsequent tests showed an improvement, as judged by vanning of the tails. It is concluded, therefore, that the patent results are confirmed. CONTACT-ANGLE TESTS In order to study the response of the various minerals, found in Anaconda ore, to commercial diphenyl sulphide, some contact-angle tests were made. Polished particles of bornite, chalcocite, chalcopyrite, pyrite and quartz were conditioned for 15 min. in a suspension of diphenyl sulphide in water. The concentration of this suspension was 0.284 grams per liter, this being the concentration of this reagent in the ball mill. The conditioned particles were rinsed with water (not rubbed with filter paper or boiled linen) and then tested against an air bubble in the bubble machine, with the following results: born-

Jan 1, 1943

By J. K. Stanley

Knowledge of the diffusivity of carbon in the low temperature form of iron (alpha iron existing below 910°C) is at the moment of considerable interest in the study of the decomposition of austenite and martensite, the elastic after-effect,123 the magnetic after-effect4 and the decarburization of steel below 910°C. Information on the solubility of carbon in iron, and to a lesser extent its diffusion, is also important in consideration of such phenomena as blue-brittleness, temper-brittleness, "magnetic" aging, quench-aging, strain-aging, and possibly the yield point. In order to obtain more information on these subjects more fundamental knowledge is necessary. It is the purpose of this work to present data on the diffusion and solubility of carbon in the alpha iron. The high temperature form of iron (gamma; face-centered cubic) existing above 910°C is capable of dissolving relatively large amounts of carbon, up to 1.7 pet at 1130°C, while the low temperature form (alpha, body-centered cubic) existing below 910° dissolves only a limited maximum amount of less than 0.02 pet carbon at 725°C, according to data obtained here. Since the solubility of carbon in the face-centered or gamma iron is large, relatively speaking, no great analytical difficulties have been encountered in the determination of the solubility lines5 or of the diffusion of carbon.0 The limited solubility of carbon in alpha iron offers difficulties because experimental procedures and analytical methods for low carbon contents below say 0.01 pet have to be more refined than techniques used for work with gamma iron. Because of the difficulties of applying conventional methods to the determination of the diffusion of carbon in alpha iron, virtually no work has been done on this subject. However, by proper refinement of the analytical method for small amounts of carbon, the determination of the diffusion coefficient can be made readily using modified procedures. The solubility of carbon in alpha iron has been determined over a temperature range by various investigators, but the agreement among them is poor. The present investigation establishes the limits quite accurately. Information of this kind is useful in establishing the correctness of equilibrium diagrams but, more significantly, such information on maximum solubilities, especially when extended to alloyed ferrites, should be extremely important in the study of aging and related phenomena. Literature The literature existing on the diffusion, in particular, and on the solubility of carbon in alpha iron is not extensive. The data which exist are not of a high order of accuracy, much of them being in the realm of conjecture. THE DIFFUSION OF CARBON IN ALPHA IRON Whiteley7 made the qualitative ob- servation, using metallographic techniques, that the rate of diffusion of carbon at the A1 (725°C) point was very rapid and that its diffusion was still rapid at 550°C. Snoek,4 studying the magnetic aftereffect in high purity iron, arrived at the conclusion that the after-effect could be explained by the presence of small amounts of carbon diffusing under the influence of magnetostrictive strain (lattice distortion due to magnetic interaction). In later work, Snoek8 made an estimate of the ratio of carbon diffusion in alpha to its diffusion in gamma iron, and concluded that for a temperature of 910°C the ratio of Da/D? was 2600. Polder,9 basing his calculations of D on relaxation phenomena in the elastic after-effect, estimated that Da is about 1/3 of D? at 910°C (1183°K) and is about 1/12 of Dy at 727°C (1000°K). Polder's equation for the diffusion of carbon in alpha iron was calculated to be 18000 D = 5.2 X 10-4 e-RT cm2 per sec Ham10 obtained data for the diffusion and solid solubility of carbon in alpha iron at two temperatures by using one technique similar to that employed in this study. He found a D of 8.0 X 10-7 cm2 per sec at 702°C and of 2.7 X 10-7 at 648°C. THE SOLUBILITY OF CARBON IN ALPHA IRON Although pearlite is absent in steels containing 0.06 pet,11 0.05 pet,12 or 0.045 pet C,13 it appears that the carbon in these steels cannot be in solution in ferrite. The solubility of carbon at the A1 (725°C) point was first determined by Scott14 on the basis of cooling curves, and was found to be between 0.03 and 0.04 pet C. Tamura15 by interpolating between the solubility of carbon in delta iron at 1400°C and in alpha at room temperature (assuming zero solubility) ar-

Jan 1, 1950

By R. C. Hall

In the present work, experiments determined the effect of the order-disorder reaction near the Fe,Al composition on the magnetic anisotropy and magnetostriction of single crystals: A material which is more difficult to magnetize in one direction than in another is anisotropic, that is, the ease with which ferromagnetic materials may be magnetized in different crystallographic directions determines the anisotropy. Two investigators have estimated the anisotropy of the aluminum iron alloys from poly-crystalline data;1,2 however, these estimates should not be considered to be reliable. Siege1 made two accurate measurements of the first anisotropy constant* from single crystals of 4.0 wt pct aluminum sotropy throughout the ferromagnetic aluminum iron system have been described. These results were obtained from single crystals which were slowly cooled and, hence, ordered near the Fe3Al composition.4 Magnetostriction is the change in length per unit length resulting from applying a magnetic field to a ferromagnetic material. For the purpose of this report, the saturation magnetostriction was measured. This is the maximum change in length per unit length resulting from an applied magnetic field large enough to saturate the material in a given direction. This magnetostriction has been determined for single crystals of the ferromagnetic aluminum-iron system.' The crystals near Fe3Al were also ordered. PREPARATION AND TREATMENT OF SINGLE CRYSTALS Single crystal bars were grown from the melt.' The raw materials for these crystals were iron and aluminum of 99.9 and 99.99 pct purity, respectively. From the bars, crystals in the shape of circular

Jan 1, 1959

By Freeman Bishop

Mercury is the latest ecological disaster. It was believed to be no pollution problem because it is heavier than water and expected to fall to the bottom of streams. But the Food and Drug Administration (FDA) found that mercury in a dozen states and several Canadian provinces was being ingested by fish. A Deadly Dose First to sound the alarm was Canada when a graduate student's research revealed that mercury contamination in Lake St. Clair had reached 1.4 pmm. which is almost three times the 0.5 ppm the FDA's allowable maximum.

Jan 1, 1970

By Oliver Halston

THIS paper reports the results of the use of salt in some research work carried on during the past 3 years at the Salt Lake City Station of the Bureau of Mines, which is quartered in the University of Utah, whose Metallurgical Research Department cooperates with the Bureau. Only the work involving the use of salt is described. The authors wish equal credit given to J. F. Cullen, C. L. Larson, C. Y. Proutz, C. E. Sims, H. C. Neeld, R. W. Johnson, F. G. Moses, N. C. Christensen, and G. H. Wigton, who have all in some way contributed toward the success of this work. Lead Metallturgy Popularly Supposed to be Without Problems In bead metallurgy it is difficult at first to find metallurgical problems, as the prevailing conception has been that bead is so easily concentrated in its various ores and so easily reduced to its metallic form that the only progress possible is that involved in cheapening methods of mining and of reduction. Most of the problems usually considered are of minor nature and do not involve radical metallurgical changes. During the 3 years of work of the Salt Lake Station, the following classification of problems in the metallurgy of bend has been made: Those involving Oxidized Ores. 1. Ores containing only bead. s. Ores containing bead and silver or gold. 3. Ores containing bead and zinc, with or without silver. Sulphide Ores. 1. Ores of pyrite carrying some bead. 2. Ores of complex zinc-bead-iron sulphides. 3. Complex sulphides containing in addition precious metals.

Jan 8, 1917

By R. E. Robbins, H. R. Brager

THIS note describes an unusual result obtained in an electron microscope investigation of cavities produced in commercial type 304 stainless steel irradiated in a thermal reactor (ETR) at 290°C to a high neutron flu-ence, 6 x loz1 n per sq cm. The analysis of the steel used is given in Table I. The unusual result is that the calculated quantity of helium gas produced by transmutation during the irradiation, 12 ppm, is less than one-tenth the amount of gas necessary to balance the surface tension of the observed cavities produced in the steel during ETR irradiation. Therefore, the cavities would be expected to behave like voids; however, they behave like "gas filled" bubbles. The maximum quantity of helium produced in the steel by B" transmutation was 8 ppm. In addition, the amount of helium formed by (n, (1) fast neutron reactions with the major alloy constituents and nitrogen was calculated to be 4 ppm based on the tabulated differential or effective fission-averaged cross sections of elements in type 304 stainless steel irradiated in typical thermal reactors.', In previous investigations concerning commercial austenitic stainless steel irradiated in a thermal reactor, the amount of helium gas calculated to be produced by transmutation has always been significantly greater than the amount calculated on the basis that the bubbles were gas filled, PPs= 2y/R. The balance of the gas was assumed to be in bubbles smaller than could be detected on the electron micrographs. Accordingly, the bubbles were attributed to helium produced from transmutation of impurity boron by thermal neutrons. These bubbles were not uniformly dispersed in the matrix but were located principally at grain boundaries, or were radially positioned around a few precipitates located in the matrix and at the grain bundaries., 4 Voids have also been observed in austenitic stainless steel irradiated at high temperature to high neutron fluences in the EBR-I1 and Dounreay Fast Reactors. The voids were uniformly distributed throughout the matrix. The amounts of helium gas produced by transmutation during these irradiations were less than one-tenth the amounts needed to balance the surface tension of the voids formed by the fast reactor irradiation. The fast reactor results are quite analogous to those reported here for the ETR irradiated steel. Electron microscope examination of the fast reactor irradiated material after a 1 hr postirradiation annealing at 900°C disclosed that essentially all the voids had been eliminated. The authors stated that the voids had developed due to the high concentration of vacancies produced during irradiatin., 6, ' The microstructure of the ETR irradiated material as-tested at 75O°C, Fig. 1, contained about 2 X lot5 cavities per cm3 with an average diameter of 110A. With the Van der Waals b correction and y = 1500 ergs per cm2, 300 ppm He would balance the surface tension of the observed cavities. Stereoscopic examination of the electron micrographs showed that the cavities were neither preferentially located near the grain boundaries nor highly concentrated at specific regions or precipitates. The cavities were nearly uniformly distributed throughout the matrix, on dislocations and at grain boundaries. These observations imply that the cavities were not the sole results of B'O

Jan 1, 1969

By Harold E. Thomas, Samuel S. M. Chan, Nicholas Bada

The U.S. Bureau of Mines has developed a technique for locating and evaluating bedding plane cracks in mine roof by an air-injection and hot-film flow logging technique. It is ultrasensitive to cracks and is especially useful for detecting the early stage of crack development. Potential applications include: (1) correlation with roof sag measurements, (2) locating cracks for grouting, (3) comparison of mechanical and resin roof bolt effectiveness, and (4) possible delineation of the fracture zone to confirm the arch hypothesis. The required equipment is inexpensive and simple to operate.

Jan 1, 1975

By R. W. Kraft

The normal Mg-Mg,Sn eutectic is a classic example of a Chinese script eutectic. When the alloy is unidirectionally solidified, a much simpler topo-logical arrangement of the phase particles can be produced although individual grains still usually consist of two or more interpenetrating lamellar systerns. Specimens from unidirectionally solidified ingots were analyzed metallographicall~ and crys-tallographically, and it was found that the interfaces between the lamellae had a common crystallograPhic character describable by: Lamellar interfaces II {220}Mg2Sn 1) {1011}Mg Arguments are presented to explain why this particular orientation relationship tends to occur and it is shown that this criterion can be nearly satisfied simultaneously on up to four different lamellar systerns between two interpenetrating single crystals. Finally, on the basis of this work ad other similar work which has previously been done on Al-CuAl2 eutectics, a general principle pertaining to low-energy interfaces between two crystalline Phases is proposed. WITHIN the past few years several investigators1-4 have demonstrated that the microstructures of many eutectic alloys can be significantly altered by uni- directional solidification. If appropriate control is exercised over the purity of the alloy, the growth rate, and the thermal gradient during unidirectional solidification, ingots can be made in which the phase particles are aligned predominantly parallel to one another throughout substantial portions of the ingot. The present author has also shown for at least one of the alloys that the parallel lamellae tend to assume a unique crystallographic relationship during

Jan 1, 1963

By Clemens Jones

A FORM of apparatus for volumetric determinations which shall possess the features requisite for the constant use of potassium permanganate, is a very desirable fixture in a well-appointed laboratory. Expedients to economize time and insure accuracy are generously employed for various other reagents, while the permanganate seems to have been consigned to the use of an ordinary burette, and a black bottle of the standardized solution. But the introduction of new, methods dependent on the permanganate, and the urgency of technical requirements where it has long been indispensable, require a revision of practice more scientific and convenient. The apparatus designed by the writer for the laboratory of the Thomas Iron Company at Hokendauqua, Pa., is so simply contrived and works with such entire satisfaction that a description of it may be of use. It may be prefaced that the characteristics of a suitable device offer some mechanical difficulties when combined in a continuous appliance. The burette, B (50 C.C. to 1/10 c.c.), shown in Fig. 1, consists of the graduated tube proper and an arm, E, fused to it below the 50 c.c. mark. At its top are rubber connections with the blast-aspirator, shown in the cut (Fig. 2) of the front view. By means of an extra stopcock, D, connection through E is established with the reservoir F. The burette is clamped Securely to a slide, C, which is counterpoised and moves freely on guides between two parallel sides, L, suitably

Jan 1, 1887

By J. M. Snook, F. C. Langenberg

FOR a better understanding of the melting and refining processes, the oxygen content of the steel bath should be determined. The oxygen content influences many process and product variables such as the efficiency of alloy recoveries, the ingot structure (through reaction with carbon in the steel), certain reaction rates, cleanliness (formation of indigenous oxide inclusions), and mechanical properties. Many methods of sampling liquid steel for oxygen have been devised. These methods can be divided into two main groups: 1) taking samples directly in the furnace or ladle;'-'0 2) removing the metal from the furnace or ladle in a sampling spoon and pouring it into a mold, or drawing the metal from the spoon into a sample holder.11-l4 The advantages and disadvantages of the two general sampling methods are presented in Table I. The bomb-sampling technique described by Huff, Bailey, and Richards8 has been used by the Crucible Steel Co. in certain research projects where oxygen contents were needed. It was recognized that a localized boiling condition could result when the mold is introduced into the steel bath, although the work of Gilbert and Bailey9 seems to indicate that the carbon boil occurring in the bomb-sampler cavity has a negligible effect on the oxygen content. In order to confirm the reported negligible effect of a carbon boil, additional work was done with adaptations of the conventional bomb sampler. The methods used are shown in Fig. 1 and are as follows: 1) Type A: aluminum wire (0.125-in. diam) coil in cavity; steel cap over mouth 2) Type B: aluminum cup in cavity; aluminum cap over mouth, 3) Type C: aluminum cup in cavity; steel cap over mouth, 4) Type D: fine aluminum wire (0.013-in. diam) in cavity; steel cap over mouth. The amount of aluminum wire in the Type A and D samples varied from 0.8 to 1.2 pct of the sample weight. The aluminum cups averaged 2.0 pct of the sample weight; the latter were used to ensure that the steel contacting the walls of the bomb cavity was fully killed. Samples were taken from plain carbon heats made in open-hearth furnaces. This grade of steel before silicon additions is essentially an Fe-C alloy and the effects of other alloying elements on the oxygen activity can be neglected. The results of sampling with the bomb samplers is shown in Fig. 2 where the percent oxygen is plotted against the percent carbon on log-log paper. Spoon sample results on the same grade of steel where the sample was killed in the spoon are shown in Fig. 3. The oxygen contents were determined by the vacuum fusion method. A comparison of Figs. 2 and 3 shows that the oxygen concentrations obtained with the spoon-sampling method (metal killed in the spoon after slag removed

Jan 1, 1960

By A. C. Heath, E. H. Dix

THE importance of aluminum-silicon alloys in the light alloy field is now generally recognized. Where silicon was once considered detrimental to the properties of aluminum, useful alloys now contain as much as 13 per cent. Furthermore, silicon is present as an impurity in aluminum of even the purest grades. Iron is another important impurity in aluminum and like silicon is found in small quantities in the purest aluminum available today. The manner of occurrence of iron and silicon in commercially pure aluminum and many of its alloys exerts a very pronounced influence upon their properties. The effect of large quantities of iron in aluminum-silicon alloys is so detrimental that it has been found necessary to limit the allowable maximum percentage to as low a figure as is consistent with quantity production and satisfactory physical properties. The intimate relation existing between iron and silicon in aluminum and aluminum alloys makes necessary a more complete knowledge of this ternary system. This paper is divided into two principal parts, dealing respectively with aluminum-silicon solubility equilibria and the constitution of aluminum-iron-silicon alloys. PART I.-ALUMINUM-SILICON ALLOYS The early work on this system was largely confined to determining the general form of the diagram and in this respect the results are in good agreement. Briefly, aluminum and silicon form a simple eutectiferous series without compounds. Until recently the solid solubility of silicon in aluminum had not been accurately determined. Fraenkel1 (1908) stated that aluminum will retain 0.5 per cent. silicon in solid solution. Rosenhain, Archbutt and Hanson2 gave the maximum solubility as about 1.50 per cent. and added that "this solubility does not appear

Jan 1, 1928

By Frank Fahrenwald

INTRODUCTORY A COMPLETE list of the elements as given for 1915 includes 18 that melt above 1,700° C. There does not exist one complete thermal equilibrium diagram for any pair of these 18 elements. Several of these elements have been combined, in relatively small proportions, with metals of lower melting point: e.g., tungsten, molybdenum, and vanadium, in steels, or with nickel and cobalt; but of this refractory group, platinum is the only one that has been extensively studied in this connection. When one considers that, with few exceptions, the industries have made use of alloys to the exclusion of pure .metals, it is reasonable to expect that alloys of this refractory group will invade fields in which the pure metals have found little application. The past neglect of this class of metals has, no doubt, been partly due to the rarity of some of them, for even though alloys of very valuable properties should be developed, their cost, unless in exceptional applications, would be prohibitive. There is also a well-founded reluctance to undertake research involving very high temperatures which, in the case of most of these elements, must be accompanied by an inert atmosphere as well. This combination of high temperatures* and control of atmosphere within the heating chamber of any furnace of present design is a difficult problem. It is the purpose of this paper to give results,1 of an investigation of one binary series of this group, in which methods were employed that avoided the usual difficulties accompanying high-temperature alloy investigation.

Jan 6, 1916

By E. H. Jr. Dix

OF all the alloying elements used in commercial aluminum alloys, copper stands out as by far the most important, and it is perhaps for this reason that the constitution of the aluminum-copper system has received the attention of a number of experimenters covering a period of approximately 20 years. It would be expected that during this time the equilibrium relations had been thoroughly and exactly worked out. In a general way this is true, but there is a surprising lack of agreement in the details of the high aluminum end of the diagram, particularly in regard to the solid solubility of copper in aluminum, which has been given variously as 2 per cent. to 5 per cent. at the eutectic temperature. The importance of this is much greater than might at first appear to one unfamiliar with modern commercial aluminum alloys. This is true because, with one exception, the susceptibility of the strong alloys to heat treatment depends, in part at least, upon the solid solubility relations of copper in aluminum. In 1919, Merica, Waltenberg, and Freeman1 published the first detailed information on these solubility relations. They found that the solubility of copper decreases with falling temperature from about 4 per cent. at 5.25° C. to about 1 per cent. at 300° C. and is apparently still diminishing at lower temperatures. In 1921 there was published a brief account of the results obtained in the National Physical Laboratory, Teddington, England.2 This laboratory, however, reported that 5 per cent. of copper is soluble in aluminum at 540° C., and that this amount decreases to about 3 per cent. at 20° C.

Jan 2, 1926