By J. J. Becker

Changes in magnetic properties with particle size are used to study the precipitation process in a Cu-Co alloy. In particular, the effect of a field during aging in producing anisotropy is shown to occur entirely during the growth of the particles, after precipitation is complete. HEAT-treatment in a magnetic field is done commercially to improve the magnetic properties of a number of materials. These can be divided into solid-solution alloys and precipitation alloys. The Permalloys are representative of the first type, and magnetic annealing greatly increases their maximum permeability. On the other hand, in precipitation alloys such Alnico 5 the important result is an increase in maximum energy product. The effect of the field in all cases is to bring about an additional magnetic anisotropy, uniaxial in nature, which makes the hysteresis loop more upright when measured in the direction in which the field was applied. The structural origin of the anisotropy brought about by magnetic annealing is not well understood. In the solid solution alloys, one possible explanation is based on ordering.' Another possibility is the orientation of like-atom pairs.' The precipitation systems known to respond to magnetic heat treatment are Alnico 2, in which the effect was first discovered," Alnico 5, cobalt ferrite (oxide),' and Cu-Co alloys.3 n these materials, the field affects the precipitation process itself in some way. Although there has been much work on Alnico 5. its nature is still incompletely understood. According to Geisler,' the precipitation reaction is of the

Jan 1, 1959

By Arthur Phillips

THE normal method of preparing metallic alloys for commercial use involves the preparation of a melt containing the given components in the chosen proportions and allowing the homogeneous liquid mass to solidify in a mold of the desired form. The solidification is frequently accompanied by a segregation of the alloying elements in different parts of the casting. When the segregation is occasioned primarily by marked differences in density of the solid and liquid phases, it is termed "gravity" segregation. When the segregation conforms to a. selective freezing in harmony with the teachings of the equilibrium diagram of the alloy system-i.e., the lower melting phases are concentrated in the regions of the casting last to freeze-it is often referred to as " normal" segrega-tion. However, in many cases the lower-melting part of the system is concentrated in the parts of the casting first to freeze and the result in this case is termed "inverse" segregation. To complete the. terminology of the subject, normal segregation in a single phase is usually called "coring" and the word will be used in that sense in this paper. Inverse segregation, particularly when the liquid phase is exuded or sweated out on the surface of the casting, is sometimes called "location." Unfortunately, some ambiguity has arisen from the use of this term and it is perhaps advisable to confine its use to the dictionary definition; namely, "The separation of two phases by heat sufficient to melt one but not the other." The gravity and normal types of segregation are both well understood and to some extent are controllable by taking advantage of the most favorable cooling rate for a given casting condition. Inverse segregation has received considerable attention from several investigators- but none of the theories offered seem to account in a convincing way for the many examples of this type. The observations made in the present work on segregation in single crystals, and in some other castings, tend to support one theory of the mechanism of inverse segregation and definitely to

Jan 1, 1937

By Thomas Watson

INTRODUCTION THE users of barite in the United States derive their supply partly from the domestic production and partly from the imports from foreign countries. According to the Mineral Resource division of the U. S. Geological Survey, the domestic production of barite in 1913 was 45,298 short tons, valued at $156,275, or $3.45 a ton, and the imports of crude barite were 35,840 short tons, valued at $61,409, or $1.71 a ton. These figures clearly show a decided advantage in cost of the foreign over the domestic barite to users in the United States. The difference in cost is the only advantage to the consumer of foreign barite, for there are large reserves of the mineral in the United States of good grade. The production of many of the operating mines is capable of decided increase, and it is believed that the operating mines together with the large reserves of undeveloped deposits of barite are entirely adequate to meet the demands of the users in the United States. Deposits of barite are known in California, Idaho, Nevada, and Alaska, but most of them are undeveloped because there is, apparently, no market for the .material in that region. The domestic production is derived from Missouri and the Appalachian States, the greater part being obtained from Missouri. Following the outbreak of war in Europe many users of foreign barite in the United States have been forced to seek their supplies at home. It seems opportune at this time, therefore, that a general review be given of the barite industry in the Appalachian States, one of the two areas from which the domestic supply of the mineral is derived, and that attention be directed to the undeveloped deposits in the region. Briefly, then, this paper reviews the barite industry in the Appalachian States, and describes the occurrence, preparation, and uses of the mineral.

Jan 2, 1915

By S. R. Seagle, R. Schuhmann, N. A. Parlee

Rates of CO evolution and CO absorption were measured for liquid-iron alloys containing from 0.15 to 4.4 pet C, using a modified Sieverts apparatus. The alloys were held in alumina crucibles, so that both crucible-metal and gas-metal reactions occurred simultaneously. The data are interpreted on the hypothesis that the C-O reaction rate is controlled by oxygen diffusion across the boundary layers at the gas-metal and crucible-metal surfaces. CARBON-monoxide evolution from liquid Fe-C-0 alloys is a key reaction in steelmaking processes, both in the steelmaking furnace and in the ingot mold. Also, this reaction probably is an essential step in the desulfurization of iron under blast-furnace conditions, for which carbon is the principal reducing agent or deoxidizer present in the iron. The thermodynamic properties of the solutions of C and 0 in Fe and the equilibria of these solutions with gaseous CO and CO, have been investigated in some detail and are reasonably well understood. However, while these equilibrium data have accumulated in the laboratory, other data have accumulated to show that equilibrium conditions are often not achieved under plant operating conditions. Thus, an understanding of the rate and mechanism of the carbon-oxygen reaction not only has theoretical interest, but ultimately may assume considerable practical importance. Reaction Mechanisms and Rate Equations The over-all reaction under consideration is C (in liquid Fe) + 0 (in liquid Fe) + CO (gas) [I] Although this appears to be a straightforward heterogeneous reaction, involving just two phases (liquid metal and gas), a wide variety of reaction mechanisms has been proposed. Different authors have expressed divergent views as to the nature of the rate-controlling steps. Accordingly, a brief discussion of the possible reaction steps will be given. 1) Homogeneous Reaction Within Liquid Iron— Feild' and Jette2 have applied chemical reaction-rate theory as if the C-0 reaction were a homogeneous, second-order reaction occurring within the liquid-metal phase. This mechanism necessarily produces CO "molecules" dissolved in liquid iron. In order to yield CO gas, the dissolved CO must nucleate CO gas bubbles, and the dissolved CO also must be transported to the bubble surface where it enters the gas phase. However, this mechanism is inconsistent with present concepts of the structure of liquid-metal solutions. 2) Reaction at Gas-Metal Interface—At the surface of contact between gas and metal, a second-order reaction between dissolved C and 0 may occur to produce a CO molecule which enters the gas phase. This reaction presumably involves an "activated complex" structure in the interface. Some such surface mechanism appears essential because the carbon and oxygen do not occur in the same species in the two phases and therefore must react in some way at the surface. At liquid-iron temperatures, calculations based on reaction-rate theory indicate that the surface reaction must proceed extremely rapidly and thus cannot be a rate-determining step in the C-O reaction under ordinary conditions.3 ccordingly when the over-all reaction is measurably slow, the surface reaction may be considered at equilibrium; that is Cc* Co* = m'Pco [2] in which Co* and Co* are the concentrations of carbon and oxygen (weight per unit volume of metal), respectively, in the liquid-metal phase at the interface, Poo* is partial pressure of CO in the gas phase at the surface (atmospheres), and m' is the mass-action constant for Reaction [I]. Since activities of C and 0 are not strictly proportional to concentrations, m' is not a true thermodynamic equilibrium constant but varies with carbon content.' 3) Mass Transport—If the reaction is to proceed at the gas-metal surface, as described above, dissolved carbon and oxygen in the liquid iron must come to the surface and gaseous carbon monoxide must move away from the surface. Details of the mass-transport mechanisms depend on the kind of system under consideration. For a stirred metal bath in contact with a CO gas phase, the transport of C and 0 to the surface can be described by 1 Do Mols CO evolved per sec = — 1/16— Do/do Agm (CO-Co*) = 1/12 Do/do Agm *(Co-Co*) [3] In this equation, Do and D, are the diffusion constants for oxygen and carbon in liquid iron, 6, and 6,. are the boundary-layer thicknesses, A,,,, is the

Jan 1, 1959

By John F. Myers

Since the art of comminution has lain practically dormant for many years, it is very interesting that R. T. Hukki approaches the subject with a new concept. One is reminded of the research carried on by A. W. Fahrenwald of Moscow, Idaho, a few years ago. Fahrenwald mounted a steel bowl on a vertical shaft. The balls and ore placed in the bowl were rotated at fast speeds, thus simulating the supercritical speeds used by Hukki. The rolling action of the balls against the smooth shell liner has pretty much the same effect. The action is horizontal in one case and vertical in the other. Both researchers report good grinding activity.

Jan 8, 1958

By G. S. Cole, G. F. Bolling

A series of Al-Cu alloys has been cast from constant superheat to solidify either with a hot top or with a free liquid/air interface. All the other variables which affect relative fluid motions were kept constant except the imposition of slow rotations m oscillations of the mold. Depending upon the exact circumstances, evi-dence could be found for the nucleation of equiaxed grains from dendrite bits detached from the columnar zone, or from the free surface, or from solid bits induced at pouring; a special experiment showed the solute buildup during ingot solidification and by inference the reality of constitutional supercooling. All methods of grain nucleation are thus supported. When solidification is arranged in a static mold the columnar- to-equiaxed transition occurs by one of these nucleation paths, subject to the natural decay of temperature gradients which promotes nucleation or the survival of nuclei. But when solidification is forced under special fluid flows it may display odd transitions. In one of these the equiaxed zone is synihesized from. dendrite bits detached from the solid/liquid interface. These survive under the concurrent lowering of temperature gradients and eventually cause transition by impeding columnar growth. GRAIN structure control is desired because real experience shows that specific properties are associated with specific cast grain structures. But since control is thus a matter of need and does not require understanding, much of casting remains art. For example, the manipulation of relative fluid motions in simple ingots provides a control of grain structure development,1-4 but theoretical insight is not required in order to broaden its potential applicability. Fortunately, however, once a variable like fluid flow is recognized it can also provide paths toward new insight. New observations using this variable have provided an insight which is curious. All the theories or descriptions of the columnar-to-equiaxed transition (CET) seem to be supported as long as the appropriate experiment is carried out. In order to develop this idea, let us ignore segregation, the chill zone (until a later section of this paper), and the origin and development of the columnar zone.= The details of questioning how equiaxed material forms in a casting may be divided in two. The first part is simply a questioning of the origin for equi-axed grains: are there fresh nuclei from heterogeneous nucleation, or dendrite bits broken off or melted from the columnar zone or elsewhere,6 or other solid bits surviving from the outset of freezing? The second is more complex, a questioning of the CET: does columnar growth slow down and allow the dominance of equiaxed grains, however they are formed, or do equi-axed grains take over and force columnar growth to stop? This "chicken-or-the-egg" second question can be quite useful, especially because it allows us to delineate the ordinary or NATURAL EQUIAXED ZONE and the induced or SYNTHETIC EQUIAXED ZONE. A natural equiaxed zone occurs if solidification proceeds in the absence of disturbances or extraneous forces such as ultrasonics, stirrings, and so forth. Both the CET theory proposed by Winegard and Chal-mers, 7requiring constitutional supercooling, and the CET theory suggested by Chalmers,8 requiring nuclea-tion only on pouring, pertain to the natural equiaxed zone. The best collating evidence to date for both these theories is contained in the work by Biloni and Chal-mers;9,10 the former theory7 is supported by special versions of the unidirectional growth experiment performed by Plaskett and winegardl1 and the latter theory' is supported in detail for the solidification of small ingots. An equiaxed zone can be synthesized when disturbances caused by forced fluid flows2-4 or other artificial means9,10 break off or melt off dendrite tips from an advancing solid/liquid interface,* if (and only if) temperature gradients in the melt are (forcibly) reduced enough to ensure the survival of these bits of dendrites, 2'3 Willful disturbances even so trivial as those produced by rapping a mold might be included here; as will be shown for example, this follows Southin's suggestion that the free liquid/air interface

Jan 1, 1970

By Paul Foote

MOST of the treatises on metallurgy intimate that simultaneously with the development by the atomic physicist of a really satisfactory theory of the atom will be inaugurated a new epoch in the science of metals. Metallurgically and metaphorically, we shall dwell in the Utopia of Sir Thomas More. It is my privilege this afternoon to demonstrate that this state has not arrived. An atom is a miniature planetary system consisting of a positively charged nuclear sun about which revolve electrons each carrying the negative charge e. The charge on the nucleus is + Ze where Z is the atomic number and the number of planetary electrons in a neutral atom is equal to Z. These electrons are arranged in several groups having different binding energies. Ordinary x-ray phenomena relate to processes occurring deep within the atom, usually with electrons in the so-called K or L shells. Such electrons in the heavier atoms are so closely bound to the nucleus that the forces exerted by neighboring atoms in a solid are relatively inappreciable. For most practical x-ray investigation, the atom may, be considered as in the gaseous phase completely isolated from its neighbors. The K radiation from an element in the gaseous state, in the solid or liquid phase, or even in combination with other elements in all its possible valences, is almost identical. ? Visual and ultraviolet spectroscopy is concerned with disturbances of the most loosely, bound outer or valence electrons of the atom, always in the vapor state. The remarkable progress of the last year in both theo-

Jan 2, 1926

By C. E. Brown, D. C. Helms, O. W. Shimer

The early history and progress of anthracite stripping, from the first known operation at Summit Hill in 1821 through 1917, was covered in 1917 in a paper by J. B. Warriner,1 then chief engineer, now president of the Lehigh Navigation Coal Co., and stripping methods between 1917 and 1931 were the subject of a paper in 1931 by H. H. Otto,2 of the Hudson Coal Company. . The present paper is confined to methods used today on pitching beds in the western middle and southern anthracite fields. The anthracite industry, not unlike other large industries, had been affected for more than a decade by the adverse economic conditions of the country. High development and operating costs and the competition of other fuels caused some collieries to be closed temporarily, while others were permanently abandoned. In order to obtain a larger tonnage at a lower development cost, a larger stripping program was put into effect by many companies. In 1932, stripping operations accounted for 3½ million tons, or 7 per cent of the total anthracite production of the year, and in the next 10 years this increased until more than double that amount, or over 14 per cent of the total production, was from stripping operations. These figures represent the total production of the entire anthracite region; unfortunately, the figures have not been separated from the different fields. There are some operations in the southern and middle western fields where the tonnage obtained from stripping amounts to more than 30 per cent of the total colliery production. Stripping operations on pitching beds present difficult problems. Owing to the various geological formations, a different situation is encountered in nearly every stripping pit; and because of the proximity of an overlying bed, it is very often necessary to load the entire overburden into trucks and haul it out of the pit to the dump area, although back filling and casting is done whenever possible. Beds in the areas described in this paper pitch from 20" to 90 and some are on the invert in many sharp folds and faults. Planning The more successful strippings have had adequate engineering analysis. Some work is being done without much preliminary planning, but many strippings would have failed completely if close supervision by the engineering department had not been . maintained. Locations of stripping areas are determined as follows: I. By constructing cross sections over the areas and drilling sufficient diamond-drill or well drill holes to study the strata and to determine the location, thickness

Jan 1, 1944

By Zay Jeffries

It has been known for centuries that iron and steel could be hardened by cold hammering and that the metal could be restored to the normal condition by heating to a red heat arid cooling, either rapidly or slowly with nearly pure iron, but slowly with steels containing considerable carbon. The art of tempering steels is also very old. When a medium- or high-carbon steel is quenched from a cherry-red heat, the hardness is increased; this hardness can be reduced by heating to various temperatures below the lower thermal critical point,, which is near 700" C. The present paper will not consider these old and well known changes in iron and steel below the thermal critical range but will confine itself to the more unusual changes, some of which have been studied recently. Stromeyer,1 for example, In 1886, reports that both working steel and heat treatment of steel in the blue-heat range arc highly injurious. Recently, however, some metallurgists believe that the straiglltening of warped steel forgings at a blue heat produces a beneficial effect on the metal2 The Engineering Division of the National Research Council has constituted a committee on Physical Changes in Iron and Steel below the Thermal Critical Range, which has the following personnel: K. R. -Abbott, H. C. Boynton, William Campbell, J. V. Emmons, F. B. Foley, H. J. French, H. M. Howe, Zay Jeffries (chairman), F. C. Langenberg, J. A. Mathews, P. D. Merica, A. H. Miller, J. H. Nelson, G. A. Reinhardt, W. E. Ruder, H. F. Wood. This committee is studying several aspects of the physical changes in iron and steel. The results, reported in the literature and obtained by recent experimentation, will be given; this will be followed by a general theoretical discussion of the more important

Jan 1, 1922

By Zay Jeffries

It has been known for centuries that iron and steel could be hardened by cold hammering and that the metal could be restored to the normal condition by heating to a red heat arid cooling, either rapidly or slowly with nearly pure iron, but slowly with steels containing considerable carbon. The art of tempering steels is also very old. When a medium- or high-carbon steel is quenched from a cherry-red heat, the hardness is increased; this hardness can be reduced by heating to various temperatures below the lower thermal critical point,, which is near 700" C. The present paper will not consider these old and well known changes in iron and steel below the thermal critical range but will confine itself to the more unusual changes, some of which have been studied recently. Stromeyer,1 for example, In 1886, reports that both working steel and heat treatment of steel in the blue-heat range arc highly injurious. Recently, however, some metallurgists believe that the straiglltening of warped steel forgings at a blue heat produces a beneficial effect on the metal2 The Engineering Division of the National Research Council has constituted a committee on Physical Changes in Iron and Steel below the Thermal Critical Range, which has the following personnel: K. R. -Abbott, H. C. Boynton, William Campbell, J. V. Emmons, F. B. Foley, H. J. French, H. M. Howe, Zay Jeffries (chairman), F. C. Langenberg, J. A. Mathews, P. D. Merica, A. H. Miller, J. H. Nelson, G. A. Reinhardt, W. E. Ruder, H. F. Wood. This committee is studying several aspects of the physical changes in iron and steel. The results, reported in the literature and obtained by recent experimentation, will be given; this will be followed by a general theoretical discussion of the more important

Jan 1, 1922

By Charles T. Holland

In connection with the problems of bumps in coal mines, much has been written concerning the manner in which roof action and methods of mining enter into the pressure effects observed but little has been written upon the relationship between the physical properties of coal and associated rocks and the cause of bumps. The question of the strength of bituminous coal, of its elasticity, and the energy it can absorb and store has been neglected to a considerable extent in connection with this problem. It is generally agreed that one of the necessary conditions for bumps is a strong coal.' Therefore, since the strength of coal is an important factor, a study of this property should be made. several investigators have conducted laboratory experiments upon the strength of coal, using small cubical or rectangular test pieces. An attempt will not be made to go into all of these investigations, but they are briefly summarized in Table I. Experiments of the U. S. Bureau of Mines and of Lawall and Holland (pp. 27 and 34 of ref. 9), however, indicate that regardless of whether the coal is a soft and weak semihituminous (Pocahontas No 3) or a hard and strong bituminous (Stockton) coal, the maximum ultimate unit stress developed in laboratory tests is higher in small cubes than in larger cubes of the Same coal.

Jan 1, 1942

By Charles T. Holland

In connection with the problems of bumps in coal mines, much has been written concerning the manner in which roof action and methods of mining enter into the pressure effects observed but little has been written upon the relationship between the physical properties of coal and associated rocks and the cause of bumps. The question of the strength of bituminous coal, of its elasticity, and the energy it can absorb and store has been neglected to a considerable extent in connection with this problem. It is generally agreed that one of the necessary conditions for bumps is a strong coal.' Therefore, since the strength of coal is an important factor, a study of this property should be made. several investigators have conducted laboratory experiments upon the strength of coal, using small cubical or rectangular test pieces. An attempt will not be made to go into all of these investigations, but they are briefly summarized in Table I. Experiments of the U. S. Bureau of Mines and of Lawall and Holland (pp. 27 and 34 of ref. 9), however, indicate that regardless of whether the coal is a soft and weak semihituminous (Pocahontas No 3) or a hard and strong bituminous (Stockton) coal, the maximum ultimate unit stress developed in laboratory tests is higher in small cubes than in larger cubes of the Same coal.

Jan 1, 1942

By Calvin Pierson, R. S. Dean, E. P. Barrett

MANY studies have been made of the properties of steel produced by adding varying amounts of sponge iron to the charges used in steelmaking furnaces.1-3 The results of these previous studies, however, have failed to disclose a reason for the belief of steelmakers that steel made in this way is definitely different from steel made entirely from scrap or iron melting stock. This paper deals chiefly with the structure of the sponge iron, of the wrought iron made by welding the sponge iron into blooms, and of the steel made by melting the forged and rolled blooms. It is believed that the structure of the final steel is inherited from the ore and that this inherited structure produces marked differences in the properties of the steel and explains the feeling of steelmakers which is based on their experience. Three kinds of sponge iron were used in this investigation: One made from a limonite ore reduced with natural gas, one made from a hematite ore reduced with natural gas, and one made from a magnetite ore reduced with charcoal. The sponge iron made by reduction with natural gas

Jan 1, 1935

By Arne Bergholm

Australian rutile was chlorinated in the presence of CO or carbon. The chlorination velocity in CO was found to be strongly influenced by temperature and proportional to the CO concentration, but independent of the Cl, concentration. In the presence of carbon, the reaction velocity is much higher. The reactivity of the carbon and the distance between the carbon and the rutile surfaces are important variables. The reaction velocity is approximately proportional to the Cl, concentration and independent of the CO concentration of the surrounding atmosphere. Experiments with fluidized-bed chlorination of carbon-rutile mixtures indicate that the motion of the bed has little influence on the reaction velocity. At low temperatures, the chlorination velocity of dense tablets is much greater than that of TiO, coke mixtures suitable for fluidization. The reaction mechanism is discussed. In the industrial production of TiCl, rutile is chlorinated in the presence of carbon. Disregarding intermediate steps, the reaction may be expressed by the following equations: The ultimate object of this study was to find out whether the reaction velocity was higher in fluidized bed operation compared with chlorination of pelle-tized carbon-rutile mixtures. From a literature survey and preliminary experiments it was learned that some basic knowledge about the reaction mechanism was needed for a good experimental design. Therefore the following sets of experiments were carried out: 1) Studies on the reaction velocity in the chlorination of rutile with CO as the only reducing agent. 2) Chlorination of separate rutile-carbon tablets. 3) Chlorination of rutile-carbon tablets at different temperatures with various kinds of carbon, various grain sizes, and various tablet-making techniques. This series of experiments was carried out not only with pure chlorine but also with mixtures of chlorine with argon, CO and CO,. 4) Chlorination of rutile-carbon tablets made in a strictly standardized manner. 5) Chlorination of static-bed rutile-carbon mixtures. 6) Fluidized-bed chlorination of the same mixture. The experiments 4 to 6 formed the final and direct test of the main question: Static bed vs fluidized bedo. Although there are many patents and papers dealing with the general aspects of chlorination, only few experiments from which detailed information can be obtained have been reported in the literature. Pamfilov and coworkersl3 have studied chlorination of TiO, with CO or carbon as the reducing agent. They found that the weight decrease per hour at 600o to 800°C amounted to 11 to 14 pct with CO and 45 to 51 pct with carbon. They suggest that phosgene might be an intermediate in the chlorination of TiO,. Takimoto and Hattori have chlorinated reduced titanium oxide (TiO) and found a very high rate of TiC1, -production. They proved that the composition of the gas from the chlorination of rutile-carbon mixtures contained mainly CO. They reported for instance 74.7 pct CO, and 5.6 pct CO at 800°C at which temperature the Boudouard equilibrium composition is 12 pct CO and 88 pct CO. Seligman and Segerchano6 have studied the chlorination of TiO. They proved that Ti0 and chlorine react rather rapidly at temperatures as low as 300°C. Above 400°C, the reaction was complete. At 500°C the velocity of this reaction was much higher than was chlorination of TiO, + C. McTaggart,7 Nishimura, et al. and Wilskam have chlorinated mixtures of carbon and various kinds of rutile or beneficated ilmenite. Nishimura, et al. also report the results from reduction of TiO, with H2, CO, or carbon. At 900°C only 1 pct Ti O is formed in 2 hrs. At 1100°C 23.1 pct Ti, 0, was formed if elementary carbon was present. No carbide formation occurred below 1400°C. McIntosh and Cofferll have observed that the CO, content of the exit gases from chlorination of rutile and calcined petroleum coke is appreciably higher than found in the Boudouard equilibrium. At 900°C the ratio (CO, /CO + CO) is about 80 pct, whereas the equilibrium value is about 2 pct. W. E. Dunn12 has studied the chlorination rates of several TiO,-bearing minerals with CO + Cl, or COCl . Chlorinations were carried out either in a fluidized reactor or a fixed-bed reactor, both having a 30-mm diameter. The results obtained in both reactors were comparable. It was proved that benefi-ciated ilmenite (i.e., ilmenite from which the iron oxide had been removed by chlorination) was chlorinated 10 times faster thanrutile. Sore1 slag showed an intermediate rate. When phosgene is used, the

Jan 1, 1962

By J. D. Grace

Screening by centrifugal force is a unique subject, for all vibrating screens, with but one exception, depend on gravity alone to pass material through a sizing mesh or screen cloth. Centrifugal screening is one of the greatest advancements made in screening since the development of vibrating screens. It makes possible sizing in a range previously im-practical by mechanical methods. The centrifugal screen is specially designed for fine sizing from No. 4 separations to finer than No. 100 separations. Centrifugal force provides a positive control of factors that make fine particle separation practical and effective as opposed to gravity which is a fixed force acting only in a fixed direction, The centrifugal screen provides a control of the force of material against the screening surface, and also controls the distance of departure of the material from the surface and its rate of return. The centrifugal screen has a rotating drum that becomes a natural fan blowing air outward through the material being screened and carrying float dust and fines through the apertures with it. Screening by centrifugal force is an unique subject, for with the exception of only one vibrating screen presently on the market, all vibrating screens depend upon gravity to pass material through a sizing mesh or screen cloth. This one screen that sizes by centrifugal force and utilizes gravity only to convey material along the screen, is the Symons V-Screen. The requirements of the industrial minerals industry to meet ever-increasing stringent fine sizing specifications by a practical mechanical method accentuates the weakness of gravity, a fixed force acting in a fixed direction, as a prime force for fine sizing. It was apparent a force other than gravity was needed. This led to the development of a centrifugal screen to meet modern demands for practical fine sizing operations. Gyratory-type screens in use today were originally designed in a day when a 1/4-in. separation was normally considered fine sizing and 1/8-in. separations were extremely fine sizing. Although gyratory-type screens are sometimes used for separating below 1/8-in., they are not practical screens for this purpose. They were not designed to do this type of work. A growing demand for a practical means of making positive mechanical separations in a range of from 1/8 in. downward led to the development of the vibrating screen. These screens utilize higher speeds and lower amplitudes of vibration than

Jan 1, 1967

By W. B. Boggs, J. N. Anderson

An account of the operation of the Noranda smelter covering the period from December, 1927, when the smelter started, until December, 1929, was given in a paper published by the Canadian Institute of Mining and Metallurgy early in 1930.' The object of the present paper is to review matters of interest in the original paper and to describe the present construction and operation of the smelter, with particular reference to the reverberatory-furnace practice. The Noranda smelter was built by Noranda Mines, Ltd., from the designs of A. E. Wheeler, consulting metallurgist of New York, for the reduction of ores and concentrates from the Horne mine and to treat, on a custom basis, ores and concentrates from other mines in the Rouyn district. The smelter is at Noranda, about 330 miles directly north of Toronto. Construction work was started in June, 1926, and copper was first produced in December, 1927. The smelter was built throughout as two duplicate units, each with a rated capacity of 500 tons of ore per day. Operations were started with one unit and after several months it was found that one unit alone could smelt 1000 tons of ore a day. At that time there was only one hoisting shaft, No. 3, and its hoisting capacity and the capacity of the original crushing plant were insufficient to supply ore for the two units at the increased tonnage. Accordingly No. 4 shaft was sunk and a new crushing plant provided to handle the ore hoisted there. Operating two units at capacity also required the installation of two more converters to treat the additional quantity of matte produced. This work was completed in the latter part of November, 1929, and since then both smelter units have been operating continuously. In 1928, a mill to treat 500 tons a day of concentrating ore was completed. Since then the concentrator capacity has been increased twice, and at present 2000 tons a day of ore are being concentrated. The layout of the surface plant of the mine, concentrator and smelter is shown in Fig. 1 and the general plan in Fig. 2. The smelter is shown in more detail in Fig. 3. The original hoisting shaft, No. 3, is now used only for handling men, supplies and waste rock, and the original crushing

Jan 1, 1934

By L.W. Eastwood, Arthur E. Bousu, C. T. Eddy

The recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presentcd in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers. Since the literature on the subject has been adequately and frequently reviewed, the only referenccs to it in this paper will be those necessary in the discussion of the data presented.

Jan 1, 1935

By Arthur E. Bousu, C. T. Eddy, L. W. Eastwood

The recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presentcd in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers. Since the literature on the subject has been adequately and frequently reviewed, the only referenccs to it in this paper will be those necessary in the discussion of the data presented.

Jan 1, 1935

By Thomas C. Wilder, Walter E. Galin

Measurements of the electromotive force of the cell at 995°C have shown that the cell may be used to detennine the zinc content of molten Cu-Zn alloys to the nearest 0.05 wt pct. The cell is used for brass melts to which no ZnO is added intentionally, because essentially all oxygen in the Cu-Zn-O system is present in the form of ZnO. The cell is also used to detev,nine the thernodynamic activity of zinc for Cu-Zn al1oys of the brass composition range, from which the equilibrium partial pressure of zinc for such alloy may also be calculated. The electrochemical measurement of the concentration of the most active metal in other engneering- alloy systems by a similar technique is also considered. IN recent years there have been many studies concerning the direct electrochemical measurement of oxygen content in molten engineering metals.' These investigations employ galvanic cells in which the electrolytes are various solid mixed-oxides which conduct current by movement of oxide ion vacancies under the influence of an oxygen potential gradient. Similar cells have also been used to measure the thermodynamic properties of mixing of solid alloys,' one component of which has a much greater affinity for oxygen than the other component(s). One alloy system of obvious engineering importance comprised of two metals of greatly differing affinity for oxygen is copper-zinc. At the casting temperature of molten brasses, the zinc concentration is very difficult to control not only because its vapor pressure is very high, but also because of its high affinity for oxygen to form ZnO. Inasmuch as brass castings may be required to have a zinc concentration within very narrow limits, it would be advantageous for the brass industry to have a means for quickly measuring the zinc content in the molten alloy just prior to pouring. A calculation based on earlier thermodynamic studies of oxygen and zinc in dilute solution in binary Cu-O and CU-Z' alloys indicates that the oxygen concentration of molten 70 wt pct Cu-30 wt pct Zn brass must be much less than 1 ppm for the separate phase ZnO not to exist in the ternary Cu-Zn-O system. Thus it can be assumed that all molten brasses, both in the laboratory and in the foundry, are sufficiently saturated with oxygen for the separate phase ZnO to be present. In view of the foregoing reasons, the cell investigated at 995°C for the purpose of measuring the zinc concentration in molten copper-zinc alloys, particularly those of brass compositions. In this cell the left hand electrode is a reference electrode comprised of a mixture of the pure powders of nickel and nickel oxide, to which a platinum contact is made. The electrode of interest is a molten Cu-Zn alloy of unknown zinc concentration with a tantalum wire contact. The electrolyte is the commercially available (Zircoa) calcia stabilized zirconia. The ZnO in the Cu-Zn electrode compartment is not intentionally added, but is naturally present as a result of the infinitesimal amount of oxygen required for its formation in this alloy system. In cell [A] nickel oxide is reduced at the cathode where O= represents the electrolyte. At the anode dissolved zinc of the Cu-Zn alloy is oxidized to form ZnO(s) in its standard state Thus the overall reaction is for which the molar free energy change is where 5 is the Faraday equivalent (23,063 cal per v equivalent), is the electromotive force of the cell in volts after correction for the Pt-Ta thermocouple, FOf (ZO) and AFF (NO) are the standard molar free energies of formation of the respective oxides, and a2n is the thermodynamic activity of zinc in the molten Cu-Zn alloy. The reference state of zinc in this case is taken to be the pure liquid. At constant temperature all the terms of Eq. [I] are constant except and azn Thus since all other participants in the electrochemical reaction are in their standard states, the change in the electromotive force of Cell [A] is represented only by a change of the thermodynamic activity of zinc at constant temperature. The zinc concentration is related to the activity by sampling the alloy for chemical analysis after cell measurements are taken. EXPERIMENTAL A typical cell construction is shown in Fig. 1. This and other experimental details were similar to that described earlier with the exception of some minor modifications which are detailed below.

Jan 1, 1970

By C. H. Herty

The reactions that occur in the basic open-hearth process are complicated and are subject to many different factors such as temperature, slag composition and rate of boiling of the bath. It is difficult, therefore, to present an extended theoretical discussion of open-hearth operations without confusing the theory of the process with the application of the theory. This paper attempts to present some of the theory of the open-hearth process without mentioning theory at any point, simply giving some of the practical applications of results founded both on theory and practice and on experimental work both in small and large furnaces. It is hoped that an answer to a number of questions commonly asked by the open-hearth operator may be found in this paper. Discussion of the subject matter is taken up more or less in the order in which a heat ie worked, beginning with the oxidation of the scrap charged, sulfur absorption by the scrap, calcination of the limestone, and extending into the pig iron for the charge, the slags formed during the process, and some of the phenomena occurring in deoxidation of the steel and in its action in the molds. Oxidation of Scbap When scrap is charged into a furnace it immediately begins to oxidize, Oxidation is carried out by.three reactions: Fe + H20 + FeO + Hz (absorbs heat) (1) Fe + C02 + FeO + CO (absorbs heat) (2: Fe+ ½O2 + FeO (gives off heat) (3: The product of oxidation contains some Fe3O4, but FeO usually predominates on account of the iron present in close contact with the scale formed For a given type of scrap the amount of oxidation is controlled by thc fuel and by the excess air being carried in the furnace, the temperature 01 the furnace, and the length of time that the scrap is in contact with the furnace gases. In general, less oxidation occurs when the furnace is rur hot so that the scrap melts rapidly. More important in operation thar the two variables atmosphere and temperature, is the type of scrap being

Jan 1, 1929