Search Documents

By T. Ikeda, M. Maeda, K. Mita

Galvanized steel sheet is the major product for the automobile industry. Therefore, automotive recycling results in zinc-containing scrap that should be remelted in EAFs. Naturally, the EAF dust is a very important source of zinc for zinc recycling processes. The thermodynamic properties of the Fe-Zn intermetallic compounds formed on the surface of galvanized steel sheet should be clarified to make clear the evaporation mechanism of zinc; however, there are few reports on these compounds because of difficulties in their synthesis. There are various intermetallic compounds in the Fe-Zn system. We synthesized them at about 673K. A specimen was examined chemically and X-ray diffraction was applied to ensure the formation of intermetallic compounds. Material containing two phases was placed in a Knudsen type effusion cell and the mass spectrum studied to evaluate the vapor pressure of zinc. The thermodynamic property of intermetallics was then evaluated through measured intensity.

Jan 1, 2000

By Fangqing Yin, Qingyu Deng, Zhengfeng Qu, Mengjun Hu, Meilong Hu

Titanium bearing blast furnace slag, which contains 20%-30% TiO2, is a valuable secondary titanium resource. Based on the thermodynamics calculation effect of the temperature on the reduction of the slag in vacuum were studied at certain vacuum degrees. The results show that magnesium vapor and silicon monoxide vapor can be obtained at the condition of high temperature and low pressure. The purity of TiC increases with temperature increasing. When the temperature arrives at 1623K TiC can be obtained besides the reductant carbon. XRD result of the powder collected from the furnace cover show that magnesium and silicon in the titanium bearing BF slag leave the slag system during carbothermal reduction in vacuum. From the above it can be concluded that TiC can be obtained from the titanium bearing BF slag and silicon and titanium in the slag can be separated by carbothermal reduction in vacuum and acid leaching.

Jan 1, 2016

Train on Different Equipment - * Immersive?s interchangeable cabin controls technology - ?clip on & off? * Change Simulator from one machine to another in minutes * No technical expertise required to swap * Real, functioning, controls and displays are used to aid rapid learning Immersive has produced a range of Conversion Kits to suit most equipment. Modular design - Easy to convert from one machine model to another with a Conversion Kit. Caterpillar Models Trucks - 769D, 773D, 777D Trucks - 785B, 789B, 793B Trucks - 785C, 789C, 793C, 797 Excavator/Shovel - 5130, 5230 Front end loader ? 992, 994 Dozer ? D10, D11 Komatsu Models Trucks - HD325, 785-5, 985-5 Trucks - 730E, 830E, 930E Dozers - D375A-3, D475A-3 Shovel - PC8000 P&H Shovels - 4100A, 4100XPB, 4100BOSS Hitachi Shovels - EX2500, EX5500 O&K Shovel - RH200 Bell Articulated Truck - B40C

May 1, 2003

By M M. Pande, M Ishfaq

The effect of aluminium on nitrogen solubility was investigated by equilibrating melt comprising master alloy of Fe-Al with pure electrolytic iron in a controlled atmosphere (pure argon) at 1873 K. Nitrogen in the samples was measured by sampling technique using inert gas fusion absorptiometry. It was found that nitrogen content decreases steadily with aluminium concentration and gradually, becomes close to 1 ppm for very high aluminium steels. Wagner’s second order interaction parameter formalism has been used to estimate the equilibrium constant and interaction parameters. Scanning electron microscopy (SEM) investigation showed, dual-phase inclusions comprising AlN phase surrounding alumina core. The 3D morphology of inclusions was studied by extracting the sample from the top and the central bottom portion of the solidified ingot. A sparse distribution of nitrogen was found for most of the inclusions which manifested the presence of almost pure alumina inclusions with different morphologies and sizes.

Jun 19, 2024

By L. L. Oden

The Bureau of Mines has studied a number of processes to remove Cu from molten steel scrap with the objective of determining if any of the laboratory methods studied warranted in depth research investigations. Experimental approaches included oxidizing Cu from steel containing other metals that form stable mixed oxides with Cu (AI, Cr, Fe, Mn, Mo, and V), injecting the same metals as oxides to simplify the mechanism of complex oxide formation, partitioning Cu into alkali or alkaline earth silicate slags or oxide-moderated sulfides, and coremoving Cu and S by injecting active compounds of Ca and Mg. The most promising tests, producing nearly 0.3 pct Cu in the slag, used Ar injection of K20-moderated Na2S-FeS below the surface of molten steel containing about 0.6 pct Cu and protected by a CaO-SiOz slag; however, in depth research investigations currently are not felt to be warranted.

Jan 1, 1987

By S. Yuan

Oxygen ion conducting yttria-stabilized zirconia (YSZ) tube was used to remove oxygen from molten Cu at 1373K. Outer surface of the tube was in contact with the melt and the inner surface containing a thin layer of porous Ni-ZrO2 cermet electrode was in contact with a reducing gas. The migration of oxygen species (O2-) from the Cu melt through the YSZ tube is accompanied by an equal and opposite flux of electrons maintaining electroneutrality. Without applying an external EMF, the fluxes are maximized by short circuiting the melt with the cermet electrode. For efficient oxygen removal, the YSZ tube must be thin, contact resistances should be negligible, and the electrodes must be porous and cover the entire electrolyte surface for charge transfer. This refining process is environmentally sound, can use reducing gases such as H2, CH4 and CO without running the risk of increasing H or C content of the melt.

Jan 1, 1993

By Serdar Aktaş, Özgün Küçükoğlu, Burcu Nilgün Çetiner, Mehmet Hakan Morcalı

This study compares the cementation performance of metallic iron, metallic aluminum, and metallic tin in terms of the reaction conditions and parameters in synthetic antimony chloride solutions. The effects on the antimony recovery (%) caused by the cementators’ types, stirring speed, reaction time, and temperatures were explored thoroughly. The cementation kinetics of antimony were also explored for each cementator. The activation energies were determined to be 10.99, 9.09, and 13.58 kJ mol– 1 for Al, Fe, and Sn, respectively. The results reveal that the reaction is diffusion controlled, and comparable results were obtained for each cementator. At 25 °C, 40 mg of iron powder was found to reduce all antimony ions (i.e., approx. 99% recovery), but even when 100 mg of Al and Sn cementators were used, the antimony recovery did not reach 100%. This result shows that iron is the best candidate to cement antimony out of the solution.

Jan 28, 2022

By Bo Arvidson

SALA MAGNETICS, INC. is now operating a 15 tph continuous high gradient magnetic separator, the SALA-HGMS® Mark III Carousel, as part of a complete mineral processing pilot plant installed at Sala's Cambridge headquarters. The Mark III can generate a maximum magnetic field of 18 kG making it possible to process even weakly magnetic, finely ground ores and ore tailings on a continuous basis at the performance level achieved in Sala's cyclic high gradient magnetic separators. Test results on iron ores, clay, and decoppering of molybdenum concentrate will be discussed. Bench scale tests have been performed on all of these materials using the SALA-HGMS® Model 10-15-20 Cyclic Magnetic Separator. A direct correlation may be made between cyclic and carousel results. Sala's Mark III Carousel high gradient magnetic separator is designed to permit scale-up to machines capable of processing two hundred (200) tons of ore per hour and more.

Jan 1, 1976

By A. V. Tarasov

Investigations of thermodynamic properties of Cu-Ni and Cu-Ni-S systems and mattes have been conducted with the aid of a MC-1301 mass-spectrometer designed for studies-of processes of vapor formation of hardly volatile substances. The instrument comprised a combination of an evaporator of Knudsen chamber type with a mass-spectrometer for analysis of the vapor phase, In the process of studies of molten Cu-Ni-S systems and commercial-grade mattes within a temperature interval of 1400-1800 K the partial pressure of sulfur was measured by means of complete isothermal evaporation and the partial pressure of copper and nickel by comparison of ionic currents. The partial pressure values of the components above the molten Cu-Ni-S were used for calculation of activities of the respective components in the melt. The copper and nickel activity data obtained was used for assessing the amount of dissolved losses of these metals in autogenous smelting slags.

Jan 1, 2003

By A. V. Tarasov

Investigations of thermodynamic properties of Cu-Ni and Cu-Ni-S systems and mattes have been conducted with the aid of a MC-130 I mass-spectrometer designed for studies of processes of vapor formation of hardly volatile substances. The instrument comprised a combination of an evaporator of Knudsen chamber type with a mass-spectrometer for analysis of the vapor phase. In the process of studies of molten Cu-Ni-S systems and commercial-grade mattes within a temperature interval of 1400-1800 K the partial pressure of sulfur was measured by means of complete isothermal evaporation and the partial pressure of copper and nickel by comparison of ionic currents. The partial pressure values of the components above the molten Cu-Ni-S were used for calculation of activities of the respective components in the melt. The copper and nickel activity data obtained was used for assessing the amount of dissolved losses of these metals in autogenous smelting slags.

Jan 1, 2003

By R. G. Reddy

The effect of solid particles on viscosity behavior of Na2O-O-B2O3-SiO2 melts of composition XSio2/XNa2o =0.5 and in the temperature range of 900- 1150 K was studied. Samples were analyzed by X-ray diffraction and optical microscopy. The results showed that a crystalline phase (NaBO2) was formed and its amount increases with decrease in X,, from 0.50 to 0.25. The experimental viscosity values were compared with the predicted values using our viscosity model developed earlier. At low temperatures, for low content of B2O3 , the experimental values exhibits a large deviation from the predicted values. It was concluded that the deviation was due to the formation of solid particles in the molten slags. The existence of these solid particles increased the viscosity values significantly. A new viscosity model was developed to include the effect of solid particles.

Jan 1, 1993

By Charles de Abreu Martins

An experimental investigation was conducted using laboratory-processed, 0.12C–1.70Mn–0.2V steels with different Cr or Mo additions aiming to evaluate this influence on the microstructure and mechanical properties hot rolled steels. Steels were processed in a pilot rolling equipment, simulating a typical thermomechanical processing, with finishing rolling steps above Ar3, followed by accelerated cooling and 723 K (450 Celsius) coiling temperature. Microstructures and precipitates were analyzed using OM, SEM and TEM, while mechanical properties were evaluated by tensile and hole expansion tests. Since Cr and Mo increase hardenability of austenite, and as a consequence, the volume fraction of the acicular constituents increases with gradual additions of Cr or Mo. Moreover, Cr or Mo impacted V precipitation process, reducing average size of particles. At 0.50%Mo, V precipitation was inhibited. Effects of this microstructure evolution on the final mechanical properties were also analyzed, as well as a comparison between Cr and Mo effects, with Mo presenting more effective influence.

Jul 30, 2018

By Denis Yaychuk, Gary Billingsley

The economic eva luation of a mineral property or mining venture should include the quantification of ri k as part of the analy is. The re ults of such an analysis provide the decision-makers not only with the most likely financial outcome and the probability of achieving that or any other outcome. but al o with a ranki ng of the relative impact of all the ri sk factors. These type of resu lts offer more complete information for investment and technical deci ions than the traditional cash flow/ ensitivity analysis. In addi tion. by attempting to quantify ri sk. the personnel providing the va ri able input are forced to take a much clo e r look at the data involved, and are fo rced to work together. the reby increa ing substantially the awa reness of the impact their work and others· work has on th e outcome of the analysis.

Jan 1, 1986

Lonmin RoM ball mills are treating two types of feed ore produced by conventional mining and mechanised mining methods. It was reported that reduction in mill throughput was observed when treating the mechanised mining ore. Detailed grinding surveys were conducted for troubleshooting. Ore samples were collected for breakage characterisation using a JKRBT based on different particle density components. XRD analysis was conducted to investigate the association of minerals with density components. The plant surveys and the breakage characterisation tests all suggested that the two mining methods did not significantly affect either the ore breakage properties or the RoM mill performance. Instead, the mill discharge open area exerted a remarkable influence on mill throughput. The RoM ball mill operated at Lonmin K4 Concentrator has been proven to be a versatile mill that performed stably with variations in feed size distribution and feed ore changes by different mining techniques. The reasons are elucidated by the multi-component breakage characterisation and the plant surveys data.

Jan 1, 2012

By Tengfei Qi, Liqiang Fan, Huiqing Tang

A new method to process the oolitic high phosphorus iron ore for phosphorus removal has been proposed in this research. It is an integration of direct reduction and melting separation with carbon-containing pellets prepared using biomass char. Experiments of direct reduction were preceded using a tubular furnace and three parameters were investigated and they were reduction temperature, biomass char adding ratio(molar ratio of carbon to oxygen） and atmosphere. Results show that the optimum condition is of reduction temperature is 1373 K, biomass adding ratio 0.9, PCO2/PCO 1.0 and reduction time 15~25 min. Under this condition, the reduced briquettes with a metallization of 75.0~80.0 % and a residual carbon content of 0.69~0.11 wt% could be obtained. Subsequent melting separation experiments were conducted using a Si-Mo high temperature furnace. Results show metal with phosphorus content of about 0.4 mass% could be obtained from the reduced sample.

Jan 1, 2015

By Nathalie Neveux

For the first time, dehydrated ferrous sulfate was successfully used for the dry synthesis of potassium ferrate. In addition, ferrate ion is stabilized as a solid solution where hexavalent iron is partially substituted by S(V1) leading to a sulfato-ferrate having the following formula K2(Fe,S)04. This substance has an efficient life time of about six months. Ferrate ion is a powerful oxidant ( EO = 2.2V ), a bactericidal agent and possesses coagulant, flocculant properties. Its reduction generates nascent oxygen, hydroxyl groups and Fe(OH)3. Alkali metal ferrate is probably the future global agent for water treatment. Applications of this material in the field of urban and industrial effluents treatment have been investigated. Heavy metals cations such as Cu, Cd, Mn, Ni, Pb, Zn, ... were successfully removed. The results of sulfato-ferrate use for cyanide destruction, decrease in COD, soil, discoloration of pulp and paper effluents will be summarized.

Jan 1, 1999

By Fatma Arslan

The lateritic nickel ore sample subjected to this experimental study was taken from Çalda ore deposit (Turkey) and contains 1.43% Ni and 0.105% Co. Mineralogical investigations showed that the ore sample contains asbolane, chromite, limonite, hematite, goethite, lepidocrocite, magnetite, serpentine, and clay type minerals together with chalcedon, quartz, calcite, and chlorite. In the acidic leaching experiments, the effects of temperature, acid (H2SO4) concentration, and leaching time on nickel leaching recoveries were investigated. Leaching recovery versus time curves showed a parabolic trend and increasing the temperature shifted that curves to the higher values. The dissolution of nickel from lateritic ore can be explained by a shrinking core model and the apparent activation energy was found as 47.34 kJ/mol in the range given by the literature. The highest Ni and Co leaching efficiencies as 90.2% and 96.8% respectively were obtained at 80°C temperature, 200 g/L H2SO4 concentration, and 8 hours of leaching time.

Jan 1, 2006

By Ryosuke Matsuoka

Keywords: Tantalum capacitor, Scrap, Recovery, Titanium, Chlorination A recycling process for tantalum from capacitor scraps using an oxidation process followed by mechanical separation and chemical treatment was investigated. This study demonstrates that sintered tantalum electrodes inside the capacitor scraps can be mechanically collected after the oxidation of the scraps in air, and high-purity tantalum oxide powder (Ta2O5) was efficiently recovered after chemical treatment. By reducing the Ta2O5 obtained through magnesiothermic reduction, tantalum powder with 99 mass-% purity was obtained. Using the chlorination for tantalum recovery was also investigated, and the tantalum or tantalum compounds were reacted with chloride wastes such as FeClx. It was found that tantalum was effectively separated and purified when tantalum powder is reacted with FeClx at 1100 K under an argon atmosphere. This recycling process utilizing chloride scrap has now been extended to other reactive metals such as titanium.

Jan 1, 2004

By Anxiang Wang, Kunhua Wu, Yifu Li, Junjie Xu, Yongnian Dai, Bin Yang, Lingxin Kong

In this study, the saturated vapor pressures of tin (Sn) and antimony (Sb), the separation coefficient and the vapor-liquid phase equilibrium of Sn-Sb alloy were theoretically analyzed, which demonstrate that it is possible to separate Sn and Sb by vacuum distillation. The process parameters of vacuum distillation, including the distillation temperature, distillation time and alloy mass (thickness of raw materials) on the direct yield of Sn and the content of Sn in liquid phase were investigated by using single factor experiments. The preliminary results show that the direct yield and the content of Sn are 98.77 wt.% and 96.01% with the optimized distillation conditions of a distillation temperature of 1473 K, a distillation t ime for 45 min and a Sn-Sb alloy mass of 125 g ( thickness o f 8 mm). The distillation parameters in the study provide effective and convenient conditions on separation of Sn-Sb alloy.

Jan 1, 2016

By J .. Carignan, Y. Dembele, J .. Guha, A. Fowler, A. Gobeil

The Barlow Lake stratigraphic section comprises the top of the Gilman Formation, the Blondeau Formation and the three sills of the Cummings Complex. Representative samples were analysed to allow characterization of the chemo-stratigraphic profile and geochemical affinity of the six rock facies found in the section. All the mineralized horizons are associated with sedimentary units. Geochemical signatures associated with the mineralizations are either very weak or very localized and shown by increases in K20 around the mineralizations and Fe203 near them. The mineralizations are stratiform, synvolcanic but resedimented and remobilized by regional metamorphism and possibly by hydrothermal activity initiated by the intrusion of the Cummings Complex. The evolution of the sedimentary basin with the decrease of its depth is confirmed by the chemo-stratigraphic profiles. Stratigraphic position in the section is important in order that the chemo-stratigraphy may serve as a guide for mining exploration in the distal facies of the Blondeau Formation.

Jan 1, 1984