By Vito J. Colangelo

The primary object of this study was to determine the effect of ferrite and its orientation upon the mechanical properties of a precipitation -hardening stainless steel with particular attention to the short-transverse properties. The investigation consisted of Jour major parts : the preliminary investigation of billet properties, the effect of forging reduction and ferrite content upon mechanical properties, the effect of notch orientation upon impact strength, and the relationship of heat composition to ferrite content. Low ductility and impact strength in the short transverse direction were found to he associated with the orientation and shape of- the ferrite plates. It was also determined that impact strength varied with notch orientation. The test values obtained with the notch perpendicular to the plane of the ferrite plate were lower than those obtained in the notch-parallel condition. The over-all investigation showed that high ferrite contents in general had a deleterious effect upon mechanical properties and that the ferrite content could he minimized by exercising rigorous control of the heat composition. A careful balance of elements, nitrogen in particular, must he maintained in order to reduce the formation of ferrite. THE precipitation-hardening stainless steels were developed to fulfill a need for high-strength corrosion-resistant alloys. In the annealed condition they are soft and ductile and possess many of the desirable characteristics of the austenitic stainless steels. In the hardened condition, the alloys exhibit the high strength and hardness of the martensitic stainless steels. The alloy under consideration in this investigation has a nominal composition as follows: C Mn Si Cr Ni Mo N 0.13 0.95 0.25 15.50 4.30 2.75 0.10 The hardening mechanism is identical to that of other hardenable steels in that it depends upon the transformation of austenite to martensite. This alloy because of its annealed structure and its ability to be hardened combines the desirable forming and corrosion properties of the austenitic grades with the high hardness and strength levels attainable with the hardenable grades. The reason for this apparent duplicity of proper- ties can be explained by considering a basic metallurgical difference between the hardenable stainless steels and those of the austenitic group. Both types are austenitic at 1800°F but, while the martensitic grades transform to martensite upon rapid cooling to room temperature, the austenitic grades remain austenitic even when cooled to temperatures below room temperature. The major difference then is in the degree of austenite stability. This stability can quantitatively be described by the Ms temperature. The Ms is defined as that temperature at which austenite begins to transform to martensite. The austenitic grades for example may be cooled to -300°F without producing significant quantities of martensite. The hardenable stainless steels on the other hand have an Ms temperature in the vicinity of 400" to 700°F. In cooling to room temperature, these alloys traverse the entire Ms-Mf range and show almost complete transformation to martensite. The semiaustenitic stainless steel, however, occupies an intermediate position with respect to its austenite stability. The analysis is so balanced that the Ills temperature lies at or slightly above room temperature. The resulting alloy retains much of its austenite at room temperature and yet responds to hardening heat treatments. Achieving this delicate balance of elements is therefore of great importance. Slight imbalances of the equivalent Cr-Ni ratios frequently result in the presence of 6 ferrite. It is the effects of this ferrit with which we are concerned, more specifically the effect of the quantity and ferrite orientation upon mechanical properties, particularly ductility. PROCEDURE A) Preliminary Investigation of Billet and Forging Properties. In order to determine the effect of ferrite on billet properties, billet stock from three heats with various ferrite contents was utilized. Tensile specimens were obtained in the transverse and longitudinal directions from this material and heat-treated as shown in Tables I and 11. Forgings were made from these same heats, the purpose being to determine what effect, if any, the ferrite might have upon the mechanical properties. These forgings were made in such a manner as to elongate the ferrite in the longitudinal and transverse directions. The method of forging was as follows. A section was cut from a 6-in.-sq billet of Heat A and flat-forged to 1-1/2 in. thick. Working was done from one direction only with no edging passes as shown

Jan 1, 1965

By G. F. Dillion, A. F. Armington

THE present method for the ultrapurification of boron involves the formation, distillation, and decomposition of boron tribromide.' However, the boron tribromide prepared contains several impurities in the ppm range, even after distillation. Some of these impurities, notably carbon, can be reduced after decomposition by zone refining. In this study, a comparison of the purity of boron tribromide at various formation temperatures is presented. The apparatus employed consisted of a bromine flask connected to a 22 mm ID horizontal quartz reaction tube packed with amorphous boron powder, which was in turn connected to a receiving flask cooled with an ice bath. Argon was used as a carrier gas. The approximate rate of passage of bromine to the reaction tube was 25 g per hr. The reaction was first investigated at several temperatures in order to determine the lowest temperature necessary to produce a colorless product which was assumed to be an indication of complete reaction of the bromine. The lowest temperature found in this study was 420oC. The amount of impurities found in the boron tribromide at various formation temperatures is shown in Table I. The data presented are emission spectroscopic results of boric oxide produced by the hydrolysis of 2 to 3 g of boron tribromide in 10 ml of distilled water. After hydrolysis, the samples were dried several hours on a hot plate. Assuming equilibrium conditions in the reactor, one can make approximate thermodynamic calculations estimatling the completeness of reaction of bromine with boron and its impurities at various temperatures. Data for these calculations were taken from Rossini,3 and must be taken as approximations since the T?S factor was not included in the calculations. The results of such calculations indicate that, with the exception of carbon bromina-tion, all impurities would react almost to completeness (> 99 pet) at all temperatures between 400" and 900oC. In the case of carbon, which cannot be accurately analyzed spectroscopically, it is estimated that only about one sixth as much carbon tetrabromide would be formed at 400" than at 900°C. Since some marked reductions in impurity content were observed at the lower reaction temperature which would not be predicted by thermo-

Jan 1, 1962

By F. G. Tahmoush, N. J. Grant, E. P. Abrahamson

The effect of grain size on the brittle -ductile transition temperature of pure iron and three dilute Fe-W alloys has been investigated by slow bend tests. The brittle-ductile transition temperature for pure iron increased with increasing grain sizes from 8000 to 500 grains per sq mm where the transition temperature then decreased with further increase in grain size. The dilute additions of tungsten lowered the transition temperature for fine grain sizes, suppressed a reversal of the curve in the coarse grained portion, and raised the transition temperature for this region. The frequency of twin occurrence increased with increasing grain size and decreasing temperature. The object of the present investigation was to re-examine the effect of grain size on the brittle -ductile transition of pure iron and several dilute Fe-W alloys. Current literature normally presents a simple relationship between grain size and the brittle-ductile transition temperature, namely, that the transition temperature increases with increasing grain size. Heslop and etch' have studied the transition temperature of mild steel by V-notch Charpy impact tests for the grain size range between 200 and 6000 grains per sq mm. The result was a linear plot of In 1-1/2 vs brittle-ductile transition temperature, where 1 is the grain diameter. Recent experiments by sipos2 revealed the possibility of a reversal in the slope of the grain size vs transition temperature plot for pure iron; however, his investigation was limited in scope, and the data obtained were insufficient to permit a definitive curve. The present investigation was undertaken in an effort to confirm or extend the grain size effect observed in iron by Sipos. PROCEDURE All alloys were vacuum induction melted, using 99.95 pct Fe containing 0.03 pct 0 and 0.004 pct C. Four ingots were made, ranging from pure iron to iron with 0.035 pct W. The chemical composition of each alloy, after processing, is given in Table I. The four alloys were prepared as 45 lb heats and cast into 4 in. diam by 16 in. molds. They were then extruded into 3/4 in. rods at 1800oF. Specimens for chemical analysis, taken from various positions along the rods, revealed no variation in tungsten content along the length. The extruded rods were reduced to 0.156 in. diam stock by a series of cold swaging operations involving intermediate vacuum annealing treatments. This procedure yielded a final cold reduction in area ranging from 10 to 90 pct. The swaged rods were chemically cleaned, cold pressed to a cross section of 0.10 by 0.18 by 1.0 in. long (2.54 by 4.73 by 25 mm). The specimens were wrapped in iron foil and vacuum sealed (10-4 mm Hg) in quartz. Various heat treatments at temperatures from 700" to 1300oC were utilized to produce grain sizes from 8000 to 1 grain per sq mm. Grain sizes were determined by measuring the average area of grains in a polished section. In specimens with grain size greater than 20 grains per sq mm, the total number of grains in the cross section was counted and then divided by the area to yield grains per sq mm. Grain size was measured both for longitudinal and transverse cross sections. The average of the two measurements was plotted vs transition temperature. An Instron Table Model testing machine was used to determine the transition temperature of specimens tested in three point horizontal bending. The specimen was supported by two 1/4 in. dowels one in. apart. Bending was accomplished with a push rod, the end of which had an 1/8 in. radius. The head speed was 50 in. per min. Temperatures were established through the use

Jan 1, 1963

By G. W. Tuffnell, S. Floreen

Three Fe-18 pet Ni-base ternary alloys cortaining carbon, molybdenum, or cobalt were aged to pgroduce hardening by carbides, Ni3Mo, or ordering, respectively. Each alloy was tested in rotating-beam fatigue tests after hardening to 195 ksi ultim.ate tensile strength. The fatigue properties of three alloys soere essentially identical. The results suggest that tlze fatigae strength of an igron-base alloy should depend primarily upon the tensile strength, and not iipon the hardening mecaanisrn. THE fatigue strengths of many steels have been found to be directly related to their ultimate tensile strengths. For ultimate strengths below 200 ksi, the fatigue endurance limit at 107 to 10' cycles is approximately half the ultimate strength. Essen- tially all of the steels that have been tested, however, have been hardened by carbon. Thus it is not certain whether the relationship between fatigue and ultimate strengths is a general one that applies for other types of hardening in steels, or whether it applies only for the particular method of hardening by carbon. The recent developments of the martensitic precipitation-hardened stainless steels and the marag-ing steels have shown that it is possible to achieve high strengths in iron-base alloys by other hardening mechanisms than that due to carbon. Therefore, it is now possible to compare the fatigue properties of several iron alloys having the same ultimate strengths but hardened by different mechanisms. For the present study a binary Fe-18 pct Ni martensite was selected as a base material. This particular matrix composition has been found to have deformation characteristics very similar to pure iron.' Three ternary alloys were prepared by adding either 0.23 wt pct C, 5 wt pct Mo, or 20 wt pct Co to this base composition. After suitable heat

Jan 1, 1965

By J. F. Butler

The degree and type of carbide dispersion resulting from changes in the cooling rate from austenite determine the amount of carbon remaining in solution after slow cooling- from a subsequent subcritical annealing treatment. A difjusion model has been proposecl to explain the effect of carbide dispersion on the amount of carbon retained in solution and the amount of carbon in solution has been related to the degree of carbon strain aging. COTTRELL and Leak' have shown that the rate of strain aging in low-carbon steels is dependent upon the amount of carbon and nitrogen in solution. Carbon can be effectively removed from solution as Fe , C by quench aging at temperatures of 200" C or lower; however, the relatively higher solubility of nitrogen at these temperatures prevents sufficient removal of nitrogen as iron nitrides. For this reason, nitrogen in solution has been considered the major cause of strain aging in rimming grades of commercial low-carbon steels. Nitrogen can be effectively removed from solution and nonaging steel produced through the addition of aluminum to form the stable nitride, AlN; however, the aluminum also causes deoxidation resulting in a killed steel. III an attempt to produce a rimmed steel which was also nonaging, Morgan and Shyne 2 investigated tile strain-aging properties of low-carban steels containing boron and found that strain aging was suplx-essed in steels containing as little as 0.007 pet B. The original purpose of this investigation was to determine the mechanism of strain-aging suppression by boron. Early in the study, the function of boron was discovered to be much like that of aluminum in that the formation of a nitride, BN, removed the nitrogen from solution.' However, during the course of the investigation, an effect of heat treatment upon the strain-aging properties and the amount of carbon in solution was found which could be related to the microstructure of the steel. The purpose of this paper is to examine these relationships among heat treatment, microstructure, carbon in solution, and strain aging in steels where nondetectable amounts of nitrogen are present in solution. EXPERIMENTAL PROCEDURE The investigation was carried out using 0.030 in. by 12. in wire specimens which had been cold swaged and drawn to the final diameter. Table I lists the compositions of the low-carbon steels used. Those with 'V' designations were vacuum melted and cast; the alloys designated 'AISI' were prepared from high-purity iron obtained from the American

Jan 1, 1962

By K. M. Rolls, R. M. Rose, H. B. Shukovsky

Studies of the phase structure, critical current density, and resistive critical magnetic field of a 45 pct Nb-55 pct Zr superconducting alloy after final-size heat treatments are reported in this paper. A combination of optical metallography, X-ray diffraction, and electrical-resistivity measurements were used to determine the phase structure. Superconductivity measurements, made with heat-treated wires, are correlated with microstructure. Although no quantitative relationship between microstructure and critical current density is found, it is shown that SINCE Kunzler1 as well as Berlincourt, Hake, and Leslie2 first described the high-field, high-current-density superconductivity of Nb-Zr alloys, it has be- the critical current density is highest when the microstructure is finely divided by fibering, coring, precipitation, or fine-scale phase dispersions. The resistive critical field is very sensitive to the compositions of the phases present. Since the alloy investigated here is near the maximum resistive critical field for the Nb-Zr system, any phase decomposition results in a lower H,. Elimination of the effects of cold work lowers H, also. A possible interpretation of the latter in terms of internal surface superconductivity is suggested. come apparent that the resistive critical field and the current-carrying capacity of such alloys are, in large measure, dependent on composition and processing. The resistive critical magnetic field (Hr) for low current densities has been found to increase progressively with zirconium content until a flat maximum is reached between 50 and 65 pet Zr.3 For any single composition, a characteristic maximum value of H, is attained by heavily cold-drawn wire.4 critical current density (J,) depends not only upon cold work but also, apparently, upon microstructure. Heat treatments of cold-worked wires generally

Jan 1, 1965

By H. E. Biber

DURING the production of tin plate a thin layer of FeSn2, is formed at the interface between the steel sheet and the protective tin coating. Because excessive amounts of this alloy layer are undesirable, the kinetics of its formation is a subject of interest in the tin-plate industry. A recent study of this subject at our laboratory uncovered a relationship which should be of general interest to anyone studying kinetics of reactions in metallic systems. It had been previously concluded that, at any given temperature in the range 175" to 330°C, the Fe-Sn alloy layer would have a parabolic growth rate.1,2 However, our studies showed that this rule apparently holds only when the tin plate is heated very slowly to the "reaction" temperature; when the tin plate is rapidly heated, considerably different growth rates occur. An example of this effect of heating rate on growth behavior is contained in the accompanying results of alloy-layer growth measurements at 240°C in oil baths stirred at 10,500, 1800, and 0 rpm. The heating curves for these three conditions are given in Fig. 1, and the growth data are presented in Fig. 2. With the rapid heating rate, provided by the stirring at 10,500 rpm, the alloy layer had three distinct stages of growth. In the initial stage, which persisted well beyond the time required to heat the tin plate to bath temperature, the alloy layer formed very rapidly. The growth followed a rate law of the form w = ktn where n > 1. This initial stage was followed by a growth-retardation stage of about 50-sec duration in which little additional alloy was formed. In the third stage the growth again followed a rate law of the form w = ktn, but here « =0.3. With the intermediate heating rate provided by stirring at 1800 rpm, the three-stage nature was less pronounced and the slope of the third stage increased (i.e., n > 0.3). With the slow heating rate provided by the unstirred oil bath, the alloy layer grew in two stages. The initial rapid-growth stage persisted only until the specimen was heated to bath temperature, no growth retardation was observed, and the slope of the main portion of the plotted data was greater than in the stirred baths, having a value of almost 0.5. Similar results were obtained for other bath temperatures in the range 200" to 300°C. This effect of heating rate on growth behavior may be due to changes in the rate of nucleation of FeSn, crystallites. The iron and tin are in contact from the onset of heating. Thus the initial formation of FeSn, occurs not at the "reaction" temperature but rather while the tin plate is being heated to that temperature. Because nucleation is in general temperature-dependent, different heating rates could cause different over-all nucleation rates, which in turn could cause different growth behaviors. A more detailed discussion of the growth of Fe-Sn alloy layer and the effect of heating rate will be published shortly.

Jan 1, 1965

By D. Krammer, E. S. Machlin

The effect of a brior high-temperature creep strain on the low-temperature ductility of commercially pure nickel has been evaluated. The low-temperature (-196°C) ductility decreases linearly with an increase in prior high-temperature (920°C) creep strain. The effect is experimentally correlated to the formation of inter crystalline cracks and voids during the prior high-temperature creep strain. The magnitude of the effect is also believed to be a function of the notch sensitivity of the material. SEVERAL mechanisms have been presented to explain the process of inter crystalline cracking in metals undergoing high-temperature creep. zenerl has suggested that grain boundary relaxation of shear stresses could build up high stresses at ob- stacles to grain boundary shear and thereby nucleate a crack. Chang and rant' have experimentally demonstrated that cracks do form at obstacles to grain boundary shear such as lines where three grains meet. The role of vacancies in the mechanism of high-temperature inter crystalline cracking has been explored by Machlt with the conclusion that the nu-cleation of voids by vacancy condensation is almost

Jan 1, 1960

By Robert E. Hoffman, John B. Hudson

The self-diffusion coefficient of pure lead has been measured at five pressures between atmospheric and 40 kb. over a temperature range of about 150°C near the melting point at each pressure. Measurements were made using a radiotracer technique, samples being sectioned electrochemically after the diffusion anneal to determine the diffusion penetration curve. Pressure was applied in a "belt" type pressure device similar to that used by Hall et al., in the diamond synthesis. The self-diffusion coefficient, D, can be represented by an equation of the form at constant pressure, and an equation of the format constant temperature. An apparent correlation between the effects of pressure on self-diffusion and on the melting point of the material observed by Nachtrieb et al., at pressures below 10 kb. was found to be only approximate as measurements are carried to higher pressures. OVER the course of the past 30 years a large number of studies1-' of the rate of atom movements in solid metals have been carried out. These studies have in general been aimed at increasing the understanding of the detailed atomic process by which atom movements in metals can take place. The largest portion of these studies consisted of measurements of the self-diffusion coefficient, D, as a function of temperature. From such studies con- siderable information regarding the energetics of the motive process has been deduced. Recently such measurements have been extended to the pressure dimension. However, the existing work in this area is scanty and has in the past been limited to the pressures attainable in oil or gas bombs—i.e., up to about 10 kilobars (kb). In the present work, the self-diffusion behavior of pure lead has been investigated using the "belt" type high-pressure apparatus designed by Hall7 over a pressure range from atmospheric to 40 kb at temperatures extending over about a 150°C range close to the melting point at each pressure.

Jan 1, 1962

By B. C. Allen, R. I. Jaffee, D. J. Maykuth

Wrought unalloyed iodide chromium, containing 39 to 95 ppm total interstitials, has a tensile transition temperature of —15°C. Re crystallizing at 1100°C causes the transition to rise to 90° to 390°C, depending on the purity, grain size, and cooling rate after annealing. At about the 100 ppm level, individual additions of carbon or nitrogen raise the transition of both wrought and recrystallized chromium by as much as 210°C, while oxygen has a lesser effect, and sulfur essentially no effect. High transitzon temperatures are exhibited by recrystallized and quenched chromium, and appear to be associated with the amount and distribution of inter-stitials. The latter cm be either in solid solution or in the form of precipitates within the grains or at the grain boundaries. Quench hardening in chromium is primarily caused by nitrogen. The hardness, re crystallization, and grain growth behavior of chromium with and without impurity additions were also investigated. BECAUSE of low density and good oxidation resistance, chromium-base alloys are potentially useful for elevated-temperature applications. The main deterrent to the use of chromium in structural applications is its lack of low-temperature ductility, especially in the recrystallized condition. Accumulated evidence has shown that the ductility of chromium is sensitive to purity. The objective of the current study was to determine the effect of common nonmetallic impurities on the tensile properties of high purity chromium. The separate effects of carbon, oxygen, nitrogen, and sulfur additions on the ductile-to-brittle transition were evaluated for wrought and recrystallized material after various cooling rates. EXPERIMENTAL WORK Unalloyed iodide chromium and seven impurity alloys containing individual carbon, oxygen, nitrogen, or sulfur additions were prepared in rod form. Nominal additions were 100 ppm C, N, and S, and 100 to 500 ppm O. The additions were about a factor of ten greater than the residual amounts in the unalloyed material. The seven alloys and two unalloyed compositions were consolidated into four-pound ingots by conventional consumable arc melting of pressed and welded electrodes under 0.5 atm of helium. Impurity additions were made to the electrode in the form of crushed master alloys. The impurity alloys were double melted to improve homogeneity. The ingots were broken down by extrusion at 1200°C in evacuated steel cans at a reduction ratio of 18 :1, using a molten borosilicate glass lubricant and a ram speed of 80 in. per min. The cans were removed by acid pickling, and the chromium core ground free of surface undulations. Cut lengths were sheathed in mild steel and swaged at 900°C until the core was about 1/4 in. in diam. Two additional 15-lb ingots of unalloyed chromium (ICr-3, ICr-4) were prepared by arc melting and broken down by 26:1 extrusion at 1250°C without a steel can. The billet was lubricated and protected from contamination by a coating of molten glass. The resulting extrusion was then sheath swaged as described previously. Representative chemical analyses of each of the materials, after removal of a 10-mil surface layer

Jan 1, 1963

By Carl J. McHargue

Rods of 99.99 + pct Al which had initial orientatzons of <001>, <118>, <115>, <111>, and random were swaged at room temperature. Changes in orientation as a function of deformation were studied on axis distribution charts. The <001> orientation appeared to be relatively stable due to the inhomogeneity of the deformation process. near the <100> zone were quickly reoriented towards <001>. Orientations on the <110> zone between <118> and <115> appeared to be stable to reductions of about 50 pct, then were reoriented toward <001>. At very high reductzotzs. movement away from the <111> orientation was observed. the requirement that a circular cross section be maintained. In addition to these mechanical factors, there are grain-boundary effects in poly crystalline materials which are not yet understood. Hartmann and Macherauch conclude, for example, that multiple slip occurs for all orientations in fine-grained aluminum and copper and that the choice of operative slip systems has no simple relationship to orientation.? Many investigators have attempted to avoid problems of interpretation caused by an initial texture by treating the starting material to obtain as ran- IT has been generally accepted that the deformation texture obtained at high reductions, e.g. 90 pct, will not be noticeably affected by a prior texture; whereas, that obtained at reductions of 40 to 50 pct may be significantly influenced by the specimen history.&apos; Some recent studies, however, have been interpreted as showing that an initial texture strongly influenced the deformation textures in rods at reductions greater than 90 pct. Freda and Cullity suggested that the <001> texture in a heavily cold-worked copper rod was due to a <001> texture in the original casting. McHargue, Jetter? and Ogle concluded that the <001> component in an aluminum rod extruded at liquid nitrogen temperature was remanent from a <001> texture in the cast extrusion billet.3 Most of the published work on the effect of initial orientation on deformation textures has been for cold-rolled or compressed single crystals,4-6 The primary interest in these studies was to examine various orientations with regard to their stability under flow? thus determining the possibility of such orientations being stable end orientations. There appears to be no published studies on the effect of initial orientation on fiber textures in polycrystalline specimens. A recent study, however, is concerned with the reorientation of individual grains in polycrystalline specimens pulled in tension.? Although the reorientation of single crystals loaded in simple tension is well known, the movements in the forming of wires and rods would be expected to be different due to the circular array of radial-compressive stresses exerted by the die walls or the rolls, and to

Jan 1, 1962

By W. C. Winegard, E. L. Holmes

The effects of the solute elements lead and bismuth on grain growth in zone -refined tin have been investigated. At low temperatures, viz. below 160°C. or at high concentrations, viz. greater than 0.03 at. pct, the temperature dependence of grain growth was found to be constant. A correlation was found to exist between the rates of grain growth in the presence of solute impurities and the factor [C Ir - 1]2 , where C is the solute concentration, r is the radius of solvent atom, and r&apos; is radius of solute atom. It is shown that the Liicke and Detert theory does not give a satisfactory explanation of the results obtained. INVESTIGATIONS of grain growth in zone-refined lead and tin and some effects of solute elements on grain growth in these metals have been reported by Bolling and winegardly2 and Holmes and winegard? The present investigation is an extension of the previous work, and was undertaken to provide additional results which might make it possible to discover the mechanism whereby the rate of grain growth is affected by the presence of foreign solute atoms. The experimental procedure was exactly the same as that described previously.3&apos;4 Figs. 1 and 2 show the results obtained with lead and bismuth additions over the same temperature range, viz. 167" to 220°C, as that used for the investigation of grain growth in zone-refined tin.3 Fig. 3 shows the results obtained for zone-refined tin and for this tin with lead solute additions over an extended temperature range. DISCUSSION OF RESULTS As mentioned previously,3 the character of grain growth in the particular zone-refined tin used in these experiments appears to change as the temperature of annealing falls below about 160°C. The grain growth became somewhat irregular and was characterized by a jaggedness of many of the grain boundaries. The reason for this change is not known, but may be due either to residual impurity effects or possibly an oxide precipitation. It was obvious that normal grain growth only occurred in the zone-refined tin through the high-temperature range 167" to 220°C, and so the effects of solute atoms on grai11 growth over the two temperature ranges will be discussed separately. a) Effect of Impurity on Grain Growth in the Temperature :Range Above 167°C. It is apparent from Figs. 1 and 2 that, for low concentrations of solute, the rates of grain growth tend towards a common value as the melting temperature of tin is approached. As the concentration of lead is increased, the rate of grain growth close to the melting temperature is also reduced, and at high concentrations the temperature dependence of the rate of grain growth appears approximately constant. It should be noteil that the effect of bismuth is greater than that of the same concentration of lead, but both these solutes have a smaller effect on the rate of grain growth than silver, as seen from an earlier investigation of Holmes and Winegard. It should

Jan 1, 1962

By J. L. Lytton, T. E. Tietz

UNALLOYED arc-cast molybdenum sheet is typically supplied in the cold-rolled and stress-relieved condition, hereinafter denoted CRSR. Such processing eliminates the yield-point phe-

Jan 1, 1964

By J. L. Brimhall

Slip-line formation during bending has been studied on neutron-irradiated molybdenum single crystals. For equivalent strains, the slip lines are coarse and distinct in the irradiated molybdenum and not resolvable in the unirradiated molybdenum. The slip lines have been directly correlated with dislocation channels present in the irradiated and deformed thin foils. The heterogeneous distribution of the dislocations during deformation in the irradiated material results from dislocation interaction with the dejects produced during irradiation. Impurities , in the form of&apos; carbides, affected the dislocation channeling Principally by acting as dislocation sources. ALTHOUGH the mechanical behavior of irradiated materials has been studied extensively, the precise mechanism of irradiation hardening has not been established. Some information on the microstructural species responsible for hardening of irradiated materials has been derived from direct and indirect observations. The direct observation of the structure of deformed irradiated metals, particularly by transmission electron microscopy, is a relatively new and unexplored area. Slip-line studies in fcc metals have been restricted primarily to copper.1-3 Very coarse slip lines, representing slip on many closely spaced planes, have been observed in deformed, irradiated copper. Coarse slip lines have also been observed in irradiated aluminum.4 Clear channels in irradiated copper caused by dislocation motion through the defect structure have been seen by transmission electron microscopy and correlated with slip lines.5-6 To date, little work has been reported on the irradiated bcc metals. Eyre described the slip lines around hardness indentations on irradiated iron and found them to be more distinct than lines in unirradiated material.&apos; Mastel et al.&apos; have observed channels in deformed irradiated molybdenum similar to those reported in copper. As part of a program concerned with the effect of neutron irradiation on metals, the slip-line

Jan 1, 1965

By C. E. Ells, A. Sawatzky

The effect of neutron irradiation on tensile properties of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy has been evaluated for integrated neutron fluxes up to 3 x 1020 n per sq cm (E > 1 Mev). Specimen temperature during irradiation was normally 300°C. The material was studied both in annealed and in quenched and aged conditions. When the alloy (fab-ricatedfrom sponge zirconium) is quenched from a temperature =40°C below the a + ß/ß transformation and aged 6 hr at 535oC, neutron irradiation up to the maximum studied has little effect 071 reduction in area, although there is a drop in uniform elongation and the yield strength is increased by = 25 pct. Conversely, irradiation of the alloy in an annealed condition can result in much greater changes in properties, with yield-strength increases of up to 200 pet. The dose dependence of irradiation hardening obeys the saturation equntion proposed by Makin and Minter to explain hardening in copper and nickel: Act = C[1 - exp(-Døt)/1/2 A rnodel is proposed to explain the effect of niobium content and metallurgical condition on irradiatiotz behavior. THE Zr-Nb alloys form a class of material susceptible to marked strengthening by quench and age heat treatment. With niobium concentrations as low as 2.5 wt pet, strengths can be developed which are double those of annealed zircaloy-2.1 Since the neutron-capture cross section of the Zr-2.5 wt pet Nb alloy is nearly identical to that of Zircaloy-2, significant gains in power-reactor neutron economy could be obtained by replacing stressed in-reactor components of Zircaloy-2 with the heat-treated Zr-Nb alloy. When the solution heat-treatment temperature is in the high (a + ß) phase, then the tensile properties of the quenched (and aged at 500°C) material have been shown to be relatively insensitive to neutron irradiation.1-3 Addition of small quantities of copper to the binary Zr-2.5 wt pet Nb alloy gives a useful reduction to the corrosion rate in air and carbon di- oxide,&apos; and a ternary alloy of composition Zr-2.5 wt pet Nb-0.5 wt pet Cu was chosen for one component in the Douglas Point Reactor. This application utilizes both the corrosion resistance to a moist air-carbon dioxide environment and the strength developed by a quench and age heat treatment. By suitable choice of solution heat treatment and aging temperatures, tensile properties of the ternary alloy can be made nearly identical to those considered as optimum for the binary alloy. One effect of the copper addition, however, is to give marked changes in the aging kinetics of the alloy.&apos; For this reason, it appeared that neutron irradiation might promote overaging in the ternary alloy, particularly at the elevated service temperature (=300°C). This paper describes the effect of neutron irradiation on the tensile behavior of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy in several metallurgical conditions pertinent to its use as a reactor material. The metallurgical conditions included those for which aging occurs in the unirradiated material, and fully annealed conditions for which a higher degree of thermal stability could be expected. 1) EXPERIMENTAL Two batches of alloy were used, both made from sponge zirconium. The fabricator&apos;s analysis of principle constituents showed no significant difference between the two batches, Table I. The rod material was rolled to 1.5 in. diam, and then swaged to final sizes of 0.5 to 0.375 in. diam at nominal temperatures of 785" and 625°C for the AM and AS batches, respectively. Subsequent hydrogen analyses at CRNL confirmed that the hydrogen concentration of the as-received rod was indeed <20 ppm. However, it was found that the (a + ß)/ß transus for the AM material was approximately 25°C lower than that of the AS material, indicating rather more difference in oxygen concentration than given in Table I. Except for a small difference in yield-point behavior, the tensile prop-

Jan 1, 1965

By O. N. Carlson, K. E. Solie

The brittle-ductile transition temperatures of single and poly crystalline chromium metal were studied as a function of nitrogen concentration and chromium nitride distribution. It was observed that In recent years there has been an increasing interest in chromium-base alloys for high-temperature applications. The principal disadvantages, however, have been the difficulties of fabrication and the design problems associated with a material of such limited ductility. Various studies have been the effects noted in the poly crystalline material are essentially reversed in the single crystals. These observations are discussed in terms of existing theories for the brittleness of chromium. conducted recently directed toward a determination of the cause of this brittleness and to find ways for minimizing its effects. Allen et al.,&apos; Wain Abrahamson and rant,&apos; and weaver4 have carried out studies on the effects of interstitial impurities on the brittle-ductile transition of chromium metal of various degrees of purity. These investigations have shown that oxygen has little or no effect on the transition temperature of chromium in all conditions studied but that carbon increases the transition temperature under all conditions tested. Nitrogen was found to increase the transition temperature in the wrought condition and in the quenched or cast conditionS but reportedly has no effect in the furnace-cooled condition.

Jan 1, 1964

By J. B. Clark, A. J. McEvily, R. L. Snyder

The nonuniform distribution of precipitate particles has been recognized as a leading factor contributing to the relatively low fatigue resistance of aluminum alloys. The structure of many of these alloys is characterized by narrow precipitate-free zones adjacent to the grain boundaries. Alloys with such zones exhibit a tendency for brittle inter crystalline fracture. The interrelation between this type of structure and mechanical properties was investigated in an Al-10 wt pct Mg alloy. It was found that deformation during fatigue occurs preferentially along these zones and cracks initiate there. In Al-10wt pct Mg, the zones were found to be supersaturated even after extensive general precipitation and are due to the absence of proper precipitate nuclei in the region near the grain boundaries. Cold working the alloy prior to aging improves the mechanical properties by inducing precipitation within the zones and also by jogging of grain boundaries. The mode of fracture is changed from brittle inter crystalline to more ductile trans granular fracture. THE process of fatigue is highly structure sensitive, with the strength of the whole often dependent upon some localized discontinuity, either geometrical or metallurgical in nature. Much has been learned about the role of geometrical discontinuities, e.g., notches, in fatigue, but with the exception of the effects of inclusions or the shapes of carbides, relatively little is known about the specific effects of discontinuities in metallurgical structure such as nonuniform precipitation. In most age-hardening aluminum alloys, metallo-graphic studies have shown that the extent of precipitation adjacent to grain boundaries is much less than that which occurs in the interior of the grains. The width of these almost precipitate-free regions, which are sometimes called denuded zones, and the extent of solute depletion within them, are dependent upon the particular alloy and its aging treatment. It has been observed1 that these zones are relatively soft with the result that plastic deformation takes place preferentially within them. It has also been shown 2-4 that there exists a tendency for intercrys- talline cracking in fatigue when such zones are present. It is of interest to note that Broom et al.2,3 were able to reduce the incidence of this type of failure in an A1-4 wt pct Cu alloy by stretching the material 10 pct prior to aging. In the present study, the effects of precipitate-free regions on the fatigue properties of an A1-10 wt pct Mg alloy were studied in detail, and the effects of deformation prior to aging on the nature of the precipitation process as well as on fatigue properties were also investigated. MATERIAL AND PROCESSING An A1-10 wt pct Mg alloy was selected for this study, because it was known that well-defined precipitate-free regions along the grain boundaries are readily obtained in this alloy after aging at 200oC.5 The starting materials were 99.998 pct A1 and singly sublimed magnesium of about 99.9 pct purity. The aluminum was induction melted in a graphite crucible, and then the magnesium addition was immersed until dissolved. Chlorine gas was then bubbled through the molten alloy for 4 min to degas the melt, after which the melt was cast at a pouring temperature of 730" to 760°C into a cold, graphite-coated, tapered steel mold. Since A1-Mg alloys are difficult to homogenize,5 special care was taken to obtain a uniform composition. Two-in. cubes were cut from the ingot and heated at 446°C for 30 min. These cubes were then hot forged approximately 35 pct in each of the three cube directions and homogenized for 16 hr at 446°C. Sheet specimens were then obtained by pressing 40 pct and rolling 35 pct per pass with reheating between reduction steps to a final thickness of approximately 0.10 in. The sheet was then solution treated for 16 hr at 446°C and water quenched. The age hardening behavior of this material at 200°C was then determined, and the results are shown in Fig. 1. The age hardening of this alloy when subjected to cold work prior to aging is also shown in this figure. Preliminary work indicated that extensive deformation after quenching was required to affect drastically the precipitate-free regions in this alloy, and a rolling reduction of 50 pct was chosen. For purposes of comparison the following three conditions were studied: a) Solution treated, quenched, and aged 20 hr at 200°C

Jan 1, 1963

By C. G. Dunn, F. Lionetti

The energy associated with grain boundaries in polycrystalline aggregates is believed to play a major role in grain growth processes and, when growth ceases, to determine the final equilibrium grain boundary angles. Further, the energy of grain boundaries of recrystallization nuclei is a factor in nucleation processes. It is important to know, therefore, how the energy per unit area of a grain boundary, that is, the grain boundary surface tension y, depends on the difference in orientation of the two lattices of the grains producing the boundary. Although the problem is important, surprisingly little has been done toward a quantitative evaluation of the effect of orientation difference on grain boundary energies. C. S. Smith1 recently has discussed this problem and in addition to showing effects of orientation difference on equilibrium angles has shown a variety of interesting effects of surface tension on the appearance of microstructures. Fig 1 and the following relations expressed in Eq 1, which connect equilibrium grain boundary angles and surface tensions, illustrate equilibrium conditions which are believed to hold true in metals. ?l2 _ ?23 _ ?l3 [1] sin ?3 sin ?1 sin ?2 Clearly any two of these surface tensions can be expressed in terms of the third when the equilibrium angles ?1, ?2, and ?3 are known. Applied to the present problem for solid state equilibrium of three grains, the angles ?1,?2 and ?3 must be measured in a plane perpendicular to the line of junction of the three grains. Normally a direct determination of these angles from random microsections is impossible. Consequently Harker and Parker2 and Smith1 (except for some measurements on flat specimens) resorted to a statistical method to determine equilibrium grain boundary angles. Smith reported that grain boundaries meet the surface of a piece of metal nearly perpendicularly. He reported also, in connection with direct angle measurements on flat specimens with grains extending through the thickness, that angles varied appreciably from 120" and concluded that there was a measurable effect of orientation difference on surface tension. Another direct way of determining equilibrium angles and a method adaptable to studying particular configurations, recently suggested by Dunn,³ is to use a three-grain flat specimen with orientations of grains so chosen that the junction line of the three grains will be straight throughout the thickness and perpendicular to the surface of the specimen. Choice of orientations is possible when individual grains of each group can be grown to predetermined orientations through the reorienting and growth of " seed crystals " as described.³ Not only is it possible, for example, to have grains with the same crystallographic plane in the plane of the specimen, but a given orientation difference between two grains can be made a common factor to an unlimited number of three-grain groups while a series of orientation differences is investigated. Any effect of anisotropy of gas-solid surface tension due to grain orientation should be minimized by having all gains oriented the same with regard to crystallographic plane in the plane of the specimen. Another feature of the three-grain group is the notched grain boundaries as shown in Fig 2 for one specimen (S4). The notches serve to anchor the end positions of the grain boundaries (especially at high temperatures) while the central and junction point of the grains moves toward an equilibrium position. Final equilibrium should produce straight grain boundaries if the notches are very narrow and if changes in orientation* of the grain boundary do not alter the surface tension.† If one assumes the straight line condition and no change of surface tension with small changes in grain boundary orientation and finds the equilibrium configuration by a minimization of the grain boundary energy, one obtains the relations given in Eq 1. The approach to straight line boundaries or to minimum energy configurations in specimens containing large grains, such as those used in the present investigation, may be very slow compared with the approach to equilibrium conditions for the grain boundary angles. It may be desirable, as proved to be the case in the present investiga-

Jan 1, 1950

By C. H. Li, S. H. Bendel, J. A. Sartell

Small additions of Mg to a 62 Cu-38 Ni alloy reduce the oxidation yates drastically between 500° and 850°C. Metallographic examination of the oxide scale disclosed a continuous network, identified by X-ray diffraction as (Ni, Mg)O solid solutions, located along the former alloy grain boundaries. This network acts as a barrier to diffusion. It is thought to result from the segregation of mg to the alloy grain boundaries. Oxidation occurs preferentially in these regions because of the presence of this more active element. To substantiate these ideas, homogenized alloys ulere oxidized. No oxide network was produced and oxidation rates were the same as for the parent 62 Cu-38 Ni alloy. An interesting aspect of the oxidation of the 62 Cu-38 Ni alloy previously described by the present authors, is the relationship between oxidation kinetics and changes in the microstructure of the oxide.&apos; The oxide scale on these alloys consists of two layers: a thin layer of CuO outside a much thicker layer of Cu20 in which particles of NiO are dispersed. In addition, immediately beneath the oxide-metal interface there is an internally oxidized zone in which NiO particles are dispersed in a copper-rich alloy matrix. Experimental observations on the growth of the individual layers under isothermal conditions have led to the conclusion that the rate-determining step in the oxidation of this alloy is the diffusion of anions through the Cu20 layer. It has been found that this diffusion rate is increased by the recrystallization of the outer CuO layer. Willardson and Gorton have reported that the addition of magnesium to the 62 Cu-38 Ni alloy causes a decrease in the oxidation rate.2 The present investigation was undertaken in order to determine the mechanism by which magnesium additions improve the oxidation resistance of the 62 Cu-38 Ni alloy. EXPERIMENTAL PROCEDURE Fifty-gram ingots of Cu-Ni alloys were prepared by vacuum melting materials of 99.999+ pct purity. These ingots were then remelted in a He atmos- phere and magnesium added in the form of a previously prepared and analyzed Cu-Mg master alloy. This procedure was necessitated by the high reactivity of pure magnesium at high temperatures. The proportion of the alloying elements was adjusted so as to obtain alloys with the desired magnesium content while maintaining a Cu-Ni ratio of 62 :38 by weight. (All alloy compositions will be given in weight percent.) Since it was considered desirable to study the oxidation of only single-phase, solid-solution alloys, it was necessary first to determine the approximate limit of solid solubility of magnesium in the 62 Cu-38 Ni alloy. A series of melts with various magnesium contents was made, homogenized by annealing for 48 hr at 975OC, then cooled in the furnace. Metallographic samples were prepared, etched in a potassium dichromate solution and examined at XI500 for the presence of a second phase. The alloys were then chemically analyzed and it was found that the approximate limit of solid solubility of magnesium in the 62 Cu-38 Ni alloy was 1 pct Mg. The ingots containing less than 1 pct Mg (0.19, 0.29, 0.58, and 0.87 pct Mg) were cold-rolled down to thicknesses suitable for oxidation experiments and specimens for gravimetric studies were cut to dimensions of 3.0 by 1.5 by 0.05 cm, specimens for inert marker studies, 0.6 by 0.6 by 0.17 cm. These were heat-treated in a protective atmosphere at a temperature (975" C) well above the oxidation temperatures and furnace-cooled to insure structural stability of the alloy during oxidation. Immediately prior to oxidation, the specimens were chemically cleaned by immersion for 1 min in a solution of 2 parts nitric acid, 1 part acetic

Jan 1, 1961

By N. A. D. Parlee, I. D. Shah, W. C. Phelps

THIS note reports on a continuation of a program on the thermodynamics of Fe-S-X systems in the "steel-burning" temperature range begun by Bock, Barloga, and parlee.&apos; Small coils of 0.039-in.-diameter pure iron (Ferrovac-E) wire were equilibrated with Fe-S-0 melts in ingot iron crucibles under argon at 1324°C in the assembly shown in Fig. 1, the lower part of which was heated in a large Globar furnace. Fig. 1 shows (R) the coiled iron wire sample, (M) the Fe-S-0 melt prepared from desired proportions of ferrous sulfide and ferric oxide, (K) the iron crucible, (I) a mullite guide tube, (J) an alumina crucible, (L) alundum sand, (N) crushed mullite, (Q) hollow cylinders of K30 brick, (C) a steel rod, (B), (El, (F), (G), (P), and (O), details of brass water-cooled head, and (H) a mullite tube 2-3/4 in. ID and 26 in. long. The rod (C) bearing the sample could be removed at will and be replaced by a tube for sampling the melt, or by a thermocouple for comparing the melt temperature with a control thermocouple not far from the 2-3/4-in. mullite tube. After equilibration the iron coils were treated with acid to remove the outer layer of metal and then they were analyzed for sulfur by a standard combustion method. The melt samples were analyzed for oxygen by a variation of Lander&apos;s2 hydrogen-reduction method for mattes, and for sulfur by the ASTM combustion-iodometric method NO. E 30-47. When the results of some forty-two runs were examined it was found that the sulfur and oxygen contents of the equilibrated melts showed good consistency, in that the plotted compositions fell along the smooth curve shown in Fig. 2. The points on this curve represent the experimental compositions of melts in equilibrium with ?-iron (Fe-S-0) solid solutions. These solid solutions are saturated with sulfur and oxygen with respect to the melt and therefore have the same sulfur and oxygen activities as the melt. The curve drawn through the points therefore delineates the ? liquidus. It falls in such a position as to roughly confirm the liquidus curves of Hilty and crafts3 at 1200" and 1300°C which are

Jan 1, 1965