By C. H. Li, R. J. Stokes, S. H. Bendel, J. A. Sartell, T. L. Johnston

The mechanism of the oxidation of high-purity copper has been studied at temperatures from 500° to 981°C employing gravimetric, high-temperature microscopic and inert marker techniques. An investigation of the adhesion of copper oxides was also made. The oxidation of copper is found to be parabolic at all temperatures. It is concluded that the controlling mechanism is the outward diffusion of CU+ ions through the Cu2O layer, but the mechanism of diffusion is modified by the state of compressive stress in the oxide layer at the oxidation temperature. At temperatures below the transition from elastic to plastic behavior of Cu2O the growth stresses reach a value sufficiently high to cause CuO whiskers to be extruded. The extrusion of whiskers results in the injection of a large number of vacancies into the CuO. The Cu20 layer grows by the advance of the CuzO/CuO interface into vacancy-rich CuO. Since there is an adequate supply of non -thermally created vacancies, the activation energy for oxidation is that required to move the Cu+ ion through the appropriate saddle point to a neighboring vacancy, which has been determined to be 20,000 cal per mole. At temperatures at which the Cu20 can deform plastically the stresses are never high enough to cause whiskers to form. thus vacancies must be supplied by themal activation and as a result the activation energy increases to 40.000 cal per mole. ALTHOUGH extensive studies of the oxidation kinetics of pure copper have been made in the past. the mechanism has received relatively little attention. As a result, certain features of the kinetic data have not been satisfactorily explained' For example, several workers1,2 have reported that the activation energy for oxidation in the range from 500° to 700° C was about 20,000 cal per mole whereas that above

Jan 1, 1960

By J. T. Norton, Joseph Gurland

IN spite of the extended use and high state of practical development of the cemented tungsten carbides, the structure of these alloys is still a matter of considerable controversy. The characteristic high rigidity and rupture strength of sintered compacts have been attributed to a continuous skeleton of tungsten carbide grains, formed during the sintering process. This view is based mainly on the work of Dawihl and Hinnuber,1 who reported that a sintered compact of 6 pct Co maintained its shape and some of its strength after the binder was leached out with boiling hydrochloric acid. After leaching, only 0.04 pct Co was reported to remain in the compact. They also showed that the assumed increasing discontinuity of such a skeleton, as the cobalt content is increased, could be made to account for the observed discontinuous increase of the coefficients of thermal expansion, the loss of rigidity, and the impaired cutting performance of alloys of more than 10 pct Co. Contradictory evidence was cited by Sanford and Trent,' who mentioned that a sintered compact was destroyed by reacting the binder with zinc and leaching out the resulting Zn-Co alloy. The skeleton theory also does not account for the observed change of strength of sintered compacts as a function of cobalt content. If the skeleton is responsible for the strength, the latter would be expected to decrease with increasing binder content. Actually, the strength increases and reaches a maximum around 20 pct Co. In addition, tungsten carbide is brittle and undoubtedly very notch sensitive. The highest value found in the literature for the transverse rupture strength of pure tungsten carbide prepared by sintering is 80,000 psi.3 herefore, such a skeleton does not easily account for a rupture-strength value of 300,000 psi and higher, commonly found in sint.ered tungsten carbide-cobalt compacts. In view of the conflicting data present in the literature, experiments were undertaken to determine whether the sintering of tungsten carbide-cobalt alloys leads to the formation of a carbide skeleton or whether the densification behavior and the properties of cemented compacts are consistent with a structure of isolated carbide grains in a matrix of binder metal. The specimens were prepared from powders of commercial grade. Tungsten carbide powder ranged in particle size from 0 to 5x10-4 cm. Mixtures of tungsten carbide and cobalt were ball milled in hexane for 48 hr in tungsten carbide lined mills. After milling, the specimens were pressed in a rectangular die (1x1/4x1/4 in.) at 16 tons per sq in. NO pressing lubricant was used. Sintering of the tungsten carbide-cobalt compacts was carried out in a vertical tube furnace equipped with a dilatometer (Fig. I), by means of which the change of length of the powder compacts could be followed from room temperature to 1500°C. An atmosphere of 20 pct H, 80 pct N was maintained inside the furnace. Decarburization of the samples was prevented by the presence of small rings of graphite inside the furnace tube. The temperature of the sample was measured by a platinum-platinum-rhodium thermocouple, which also was part of a temperature control system able to maintain a constant temperature within ±100C. Pure tungsten carbide compacts were prepared by sintering the carbide without binder or by evaporating the binder from sintered compacts in vacuum at 2000°C. Since complete densification of these samples was not desired, they were sintered only to 60 or 80 pct of the theoretical density of tungsten carbide. The specimens were prepared for metallographic examination by polishing with diamond powders and etching with a 10 pct solution of alkaline potassium ferricyanide. Cobalt etches light yellow and the carbide gray. The amount of porosity is exaggerated since it is difficult to avoid tearing out carbide particles, especially from incompletely sintered samples. Experimental Observations A number of specific experiments were carried out in order to study some particular aspect of the sintering problem. The details of these experiments, together with their results, are as follows: Electrolytic Leaching: The binder was removed by electrolytic leaching from sintered tungsten carbide-cobalt compacts for the purpose of determining the continuity of the carbide phase. The method used was based on the work of Cohen and coworkers4 on the electrolytic extraction of carbides from annealed steels. If the sample is made the anode, using a 10 pct hydrochloric acid solution as the electrolyte, the binder is dissolved, but the rate of solution of tungsten carbide is negligible. A current density of 0.2 amp per sq in. was applied. As shown in Fig.

Jan 1, 1953

By B. H. Kear

All the possible ways of forming simple two-dislocation boundaries in multiple slip orientations are deduced. It is shown that the principal differences in work hardening behavior of crystals plastically deformed in these orientations can he accounted for in terms of the likelihood of formation of diffuse boundaries, or deformation bands, consisting of the products of dislocation reactions of the Lomer type. Also, it is pointed out that the break-up of boundaries under the applied stress is more likely to yield interstitial jogs than vacancy jogs, whereas glide dislocations cutting throuqh dislocations trapped in particularly stable boundam'es can acquire both types of jogs. USING Frank's' grain boundary formula, Ball and Hirsch2 determined the parameters of all the possible boundaries that can be built from two sets of glide dislocations in the fee structure. This paper deduces the geometrical possibilities for the formation of these two-dislocation boundaries in the different multiple slip orientations, and discusses the role of boundaries in work hardening and in jog formation. Formation of Two-Dislocation Boundaries in Mutiple Slip Orientations. The parameters of the possible two-dislocation boundaries for any crystal orientation can be deduced most conveniently using the boundary formulae due to Amelinckx,3 in conjunction with the stereographic projection shown in Fig. 1. Suppose that slip occurs in a-BC and ß-CA. According to Amelinckx, when the two systems of glide dislocations are parallel, the rotation axis, u, of the boundary is parallel to (a x ß) and the unit normal, u, defining the boundary plane is parallel to (a x ß) x (BC x CA). On the other hand, when the glide dislocations form a crossed grid, u is parallel to (BC x CA) and u is parallel to (a x CA) x (ß x BC). In Fig. 1, (a x ß) is the pole of the great circle passing through a and ß, so that u is parallel to DC, i.e., parallel to [110]. Furthermore, (a x ß) x (BC x CA) is the pole of the great circle passing through DC and 6, so that u is parallel to [110]. Hence, when all the glide dislocations are parallel, the boundary is pure tilt with parameters u = [110], v = [ 110]. Similarly, it may be shown that the corresponding crossed grid of dislocations is a mixed boundary with u = [111], u = [111]. Consider the case of a crystal compressed in the [001] orientation. In this orientation, according to Fig. 1, there are eight available slip systems. In what follows, the different types of two-dislocation boundaries that are possible in this orientation will be examined by taking different combinations of two slip systems out of the available eight, with a-BC always one of the systems. Case (i)—Slip Systems a-BC and d-CB. The formation of a tilt boundary in (101), which consists of a crossed grid of edge dislocations with vectors BC andCB, is illustrated in Fig. 2(a). As the figure shows, slip is required in the system a-BC in one part of the crystal and in d-CB in the other part, with both sets of dislocations entering the boundary from opposite sides. The rotation axis of the boundary lies in (101), depending on the relative densities of the two sets of edge dislocations in the boundary. Case (ii)-Slip Systems a-BC and ß-CA. The two possible boundaries are shown in Figs. 2(b) and (c); boundary (b) is tilt with u = [110], u = [110], and

Jan 1, 1962

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending' upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2'3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn's early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By P. R. Sperry, P. A. Beck, Hsun Hu

As described by means of quantitative pole figures, the inside texture of highly rolled aluminum and copper strips may be approximately described by four equivalent ideal orientations near (123) [121]. If rolled in reversed passes, the surface texture of copper is also near (123) [121], that of aluminum is (100) [011]. The inside texture of highly rolled brass is (110) [112]. The surface texture is the same, if rolled in reversed passes. The surface texture of all three metals is related to the inside texture, but asymmetrical, if rolled without reversal between passes. MANY previous investigations dealing with the subject of the present work were reviewed by Wassermann.1 Barrett,2 Brick,3 and Richards.' The recent introduction of quantitative methods for pole figure determination by Decker, Asp, and Harker,5 Schulz5 and others made it possible to reinvestigate some of the finer points which the earlier more qualitative photographic methods left undecided. The rolling textures of silver and of 70-30 cartridge brass have been quite consistently characterized by the ideal orientation of (110) parallel to the plane of rolling and [112] parallel to the rolling direction. On the other hand, it has been recognized by several investigators that certain other face-centered cubic metals, such as copper and aluminum, developed rolling textures rather different from that of brass. These textures have been variously described by the following ideal orientations, singly or in combinations with each other: (110 [112]: (112) [111]; (135) [335]; (135) [211], etc. The discrepancies usually have been attributed to the lack of sharpness in the textures and to the attendant difficulty of associating "ideal orientations" with pole figures showing great scatter of orientations. It seemed desirable to investigate by the new quantitative methods to what extent the apparent lack of sharpness may have been brought about by the qualitative methods used previously, rather than by the textures themselves, and to decide, if possible. between the various ideal orientations which have been proposed. Another problem, not satisfactorily settled by earlier investigations. concerns surface textures in rolled metals. For instance, in rolled aluminum the surface texture in some cases appeared to be similar to the texture inside the sheet, whereas in other cases it was reported to be entirely different.' The conditions under which such differences may have arisen, and the possibility of the occurrence of different surface textures in other face-centered cubic metals do not appear to have been examined in detail. The present work was undertaken to investigate the above questions. Some of the results obtained have been described- riefly. Experimental Procedure Specimen Preparation: In the present investigation 2s aluminum, electrolytic tough-pitch copper, and commercial 70-30 brass were used. These materials were available in the form of cold-drawn rods. 1 in. diam for tough-pitch copper and commercial 70-30 brass and 11/2 in. diam for 2s aluminum. The cold-drawn bars were alternately annealed and rolled 30 pct lengthwise in several cycles until a penultimate thickness of 0.500 in. was reached. The intermediate and the penultimate anneals were carried out for 30 min at 380°C with 2s aluminum, and for 30 min at 550°C with 70-30 brass. For tough-pitch copper, the intermediate anneals were 30 min

Jan 1, 1953

By W. A. Wood, W. H. Reimann

A study is made of the creep that can be induced in armco iron at room temperature by superposing small amplitudes of alternating torsion on a tensile creep load. It is shown that the creep differs from that in comparable tests on copper in being trmsient only. At the same time, though transient, the creep can produce extensions of some 10 pct under creep loads less than the tensile yield stress of the material. The creep can be largely suppressed b$ applying cyclic strain of suitable amplitude before applying the creep load and the metal thereby stabilized. At room temperature, plastic flow in a metal under steady load is normally limited by strain-hardening processes. However, if a small cyclic stress is superposed on the steady load these processes may be more or less neutralized and, as shown in recent investigations,'-4 plastic flow may continue. In this way annealed copper, for example, can be induced to creep continuously to fracture under loads as small as 1 tsi. Dislocation mechanisms possibly responsible for this room-temperature creep have been usefully reviewed by Feltner.But discussion so far has been based mainly on creep as it is found in close-packed metals initially in the annealed state, and their behavior may not be general. In fact, recent work shows that the form of creep in annealed copper is different from that even in cold-worked copper;7 the creep thus depends on the dislocation pattern already in a metal as well as on the metal itself. This paper describes the creep in annealed armco iron, tested in the same way as the above-mentioned copper. One object was to see how creep in a typical bcc metal compared with that in the annealed close-packed metals. Another object was to utilize the fact that a bcc metal like iron has a more pronounced elastic range than close-packed metals like copper and to find to what extent the creep load or superposed cyclic stress had to exceed their re-

Jan 1, 1964

By Jr. W. L . Phillips

The deformation and fracture characteristics of lithium-fluoride single crystals stressed in compression at room temperature have been studied. In as-cleaved specimens the stress-strain curves were variable; two types of {110} fractures were observed in the vicinity of kink bands. The stress-strain curves of annealed crystals were reproducible; {100} cracks formed which propagated along the (100) and (110) planes. The deformation and fracture characteristics were affected by quenching and X-ray irradiation. STUDY of the mechanical behavior of nonmetallic materials has received considerable impetus in recent years because of the need to overcome the problem of brittleness before the refractory properties of nonmetallics can be fully exploited. Ionic crystals provide a convenient and simplified starting point from which to study the deformation and fracture processes in nonmetallic materials. Early investigations of the mechanical behavior of non-metals were restricted largely to determinations of the crystallographic indices of the cleavage and fracture planes and the glide and twinning elements. Until recently, only occasional systematic studies of the deformation characteristics of non-metals have been made; and investigations of the forces necessary to initiate plastic deformation and the factors which affect the flow characteristics have been restricted largely to studies of sodium chloride'-7 , magnesium oxides-l3 and lithium fluoride. 14-22 Fracture studies on alkali halide and metal oxide single crystals have been limited despite the fact that these materials have a number of advantages for fracture studies. Because they are transparent, the cracks which form can be viewed in three dimensions instead of in two dimensions as in metals. Also, they exhibit stress birefringence under polarized illumination, which enables the internal stress pattern and, therefore, the distribution of dislocations to be examined in the vicinity of the fracture. Early workers1-4 have shown that ionic crystals with a cubic structure fracture in tension along the (100) plane normal to the applied stress. These fractures were brittle at room temperature and propagated very rapidly across the cross section of the crystal. More recently, Stokes, Johnston, and Lil0 have studied crack formation in compressed magnesium-oxide single crystals. They found that the cracks, which were observed after about 3 pct strain, formed in the region of a kink band and lay on conjugate (110) slip planes instead of the usual(100) cleavage plane. Two different types of cracks were noted: stroh23 and secondary. The Stroh cracks did not exist merely on the surface but extended through the specimen in the form of tiny slits. A secondary

Jan 1, 1962

By A. Dubé, G. Letendre, C. E. Beaulieu

An experimental study has been made of the time dependence of internal .friction and modulus of rigidity in- freshly quenched steels at room temperature. The effects of frequency, composition, and various thermal treatments are given. The kinetic 1aws observed cannot be fully explained by the so-called first stage of tempering and the transformation of retained austenite. It is suggested that the observed phenomena are due to the progressive immobilization of dislocations introduced by the martensitic transformation. It is generally agreed that the conversion of tetraginal martensite into cubic ferrite and ce-mentite occurs in three stages which at moderate rates of heating take place in the following temperature ranges:'-3 a) The first stage involves mainly a partial loss of tetragonality of martensite and the formation of ?-carbide between 95" and 175oC. b) The second stage consists of the decomposition of retained austenite between 230 and 290' C. c) The third stage covers the formation of ce-mentite between 290o and 400' C. The kinetic laws of these heterogeneous reactions have also been the subject of isothermal studies. Thus, Roberts, Averbach. and cohen3 report a very low reaction rate with a eutectoid steel at room temperature. For example, less than 10 pet of the contraction associated with the first stage is observed after 50 hr at room temperature. Hollonlon, Jaffe, and Buffum4 show that under the same conditions less than 10 pet of the tetragonality is lost. These results have led to the belief that martensite is a relatively stable phase at room temperature. On the other hand, it is well known that important structural changes occur in martensitic steels during the first few minutes at room temperature after quenching. This pretempering has at least two important consequences. In the first place, freshly quenched steels have a tendency to crack at room temperature, a fact which leads to the necessity of tempering as soon as possible after the quench. Another important consequence of pretempering a steel for short periods of time at room temperature is the stabilization of the retained austenite. Thus, as shown by Cohen,5 a very pronounced stabilization is effected with holding periods of 30 min at room temperature. Since these two effects are apparently not caused by the heterogeneous reactions mentioned above, they must be related to the rearrangement of structural defects within the martensite and retained austenite. According to the modern theory of dislocations, the shears required to effect the austenite-marten-site transformation may be realized through the motion of dislocations at the austenite-martensite interface and within the martensite plates.6 In this way, a martensitic transformation closely resembles a plastic deformation. In cold-worked solids, high concentrations of dislocations are left immediately after the plastic deformation and it seems reasonable to assume that appreciable densities of dislocations should also appear in the wake of a martensitic transformation. A considerable part of the high hardness of martensite would then originate in the obstruction of dislocations in analogy

Jan 1, 1961

By T. E. Leontis, D. H. Feisel

MAGNESIUM alloys containing rare earth metals have received considerable attention during the past several years because of the need for light alloys having high strength and creep resistance at elevated temperatures. Although much of the work reported earlier has dealt with alloys containing Mischmetal, it has been shown in two previous papersl, V hat distinctly different effects are produced by various rare earth metals and rare earth metal mixtures on the properties of magnesium. For example, much higher strengths are obtained in magnesium alloys containing didym-ium (essentially neodymium plus praseodymium) than in alloys made with Mischmetal, which contains all the rare earth metals in the proportions in which they occur naturally in the monazite ore. Mg-rare earth metal alloys are characterized by a relatively coarse grain size, which greatly impairs castability. The addition of zirconium as a second alloying ingredient has been shown8,7 to refine the grain size, which also produces a distinct improvement in the strength properties. Certain Mg-Mischmetal-Zr and Mg-Mischmetal-Zn-Zr alloy compositions which are currently being produced commercially have been discussed in dytail by Nelson and Strieter,8,4 who also present some in- formation on a Mg-low Ce-Mischmetal-Zr alloy, and by Nelson.8 A patent issued to Jessup, Emley, and Fisher9 emphasizes the superiority of Mg-didymium-Zn-Zr alloys over the corresponding alloys made with Mischmetal. The purpose of this paper is to present the results of an extensive investigation concerned with the effect of increasing amounts of zirconium on magnesium sand casting alloys containing several different rare earth metal mixtures in varying amounts. The effect of the addition of zinc to some of these alloys is also being reported. Preparation and Testing of Alloys The alloys studied in this investigation were prepared in small laboratory melts according to the melting procedures described by Nelson1" as the Crucible Method. Electrolytic magnesium having the composition shown in Table I was used as the starting material. The rare earth metal alloying ingredients used in preparing these alloys were essentially of the compositions listed in Table 11. Some of the didymium-containing alloys were prepared using a Mg-didymium hardener. The rare earth metal content of this hardener analyzed 1.2 pct Ce, 10.4 pct Pr, 80.8 pct Nd, and 7.6 pct La. The zirconium was added in one of three forms: 1) as sponge zirconium obtained from the Bureau of Mines; 2) as a fused salt consisting of 50 pct ZrCl, and 50 pct alkali chlorides from which the zirconium is reduced by the magnesium; or 3) as a Mg-Zr hardener. The alloying procedures and melt hand-

Jan 1, 1958

By A. H. Daane, B. J. Beaudry

The Sc-Ti system was studied by thermal, metal-lographic, and X-ray methods. Scandium was found to transform at 1334 °C from a (hexagonal) to ß which was concluded to be bee since a continuous series of solid solutions is formed between ß scandium and ß titanium at elevated temperatures. There is a minimum in the solidus at 51 wt pet Ti and 1300°C, a monotectoid at 1050°C and 49 wt pet Ti, and a eutectoid at 875°C and 91.5 wt pet Ti. The maximum solubility of titanium in a scandium is 13.5 wt pet at the monotectoid temperature, while the maximum solubility of scandium in a titanium is 6.5 wt pet at 875°C. SCANDIUM, a member of Group 111 A of the periodic table, and now called a rare-earth metal,' has become of interest recently due to its low density (2.99 g per cc) and relatively high melting point (1539°C).Spedding,' et al. have described a method of preparation of pure scandium metal and have made a study of its basic properties. Since scandium is approximately 10 to 12 pet smaller in at. diam than the other rare earths while its electronegativity and valence are the same, a knowledge of its alloying behavior in contrast to these elements should be very helpful to fundamental alloy theory. Since scandium is quite scarce and difficult to prepare in pure form, its use as a structural material by itself seems quite unlikely. However, its use in special cases as an alloying addi- tive to other low-density materials is a possible application; the Sc-Ti system was chosen for this reason and for others of fundamental interest. Scandium was suspected of having a high temperature bee form as do some of the other rare-earth metals.3'4 Since titanium has a high-temperature bee form, a continuous series of solid solutions at elevated temperatures between ß scandium and ß titanium would prove the existence and structure of the high-temperature form of scandium. The existence of a continuous series of hexagonal solid solutions at room temperature was predicted by Burkhanov and Savitskiy,5 but Hias shown to be incorrect in early X-ray studies. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar titanium and distilled scandium prepared by the method described by Spedding,2 et al. The major impurities are listed in Table I in PPm. Alloy Preparation. All the alloys examined were initially formed in a nonconsumable electrode are-melting furnace under an atmosphere of purified helium or argon. A curve based on the observed weight loss of 0.6 pet* when titanium was melted

Jan 1, 1962

By Elmer Weber, W. M. Baldwin

Solid lead obeys a single parabolic weight increase vs. time law. In contrast, liquid lead undergoes three successive parabolic weight increases vs. time laws, the first of which has a low constant relative to the latter two. The conversion times for the change from one parabola to the next decrease with increasing temperature. IN recent reports on the subject,1,2 it was noted that zirconium and titanium scale in air by a complex mechanism. The scale first forming on the metal is protective to the extent that it gives a low constant, K, for Tammann's, and Pilling and Bedworth's parabolic equation: w² = Kt [1] relating weight increase, w, due to chemical reaction of the metal with the air, and time, t. After hundreds of hours of apparent stability in some cases the first scale yields to another that offers little protection to the metal. This transition from one scale to another, from a slow parabolic oxidation reaction to a fast one, was not due to impurities in the atmosphere or incidental effects (changing environment, etc.) but was a specific behavior of the metal itself, the transition occurring at definite times (dependent on temperature) and showing other reproducible traits. In view of this behavior how can long-time service behavior be predicted from short-time laboratory tests, not only in the case of these metals, but in any case? Certainly a systematic study of the type of scaling behavior described above—wherever it is found—would help to answer this question. The present paper is a report on the behavior as it is found in lead—the only metal to the authors' knowledge for which the behavior has been described at all, if inadequately, for our present purpose.* At least four oxides of lead are known, of which one occurs in two allotropic forms. They are ß (red) tetragonal PbO stable up to 486°C;8 a (yellow) orthorhombic PbO stable from 486°C up to its dissociation temperature in air at about 2300°C;9 minium or Pb3O4 which from the dissociation pressure data given in Fig. 1 decomposes to PbO at 540°C in air; lead sesquioxide or Pb2O3,; and lead dioxide or PbO2 which, according to Fig. 1, decomposes in air at 400°C to minium. In view of the high dissociation temperature of PbO, lead will scale up to at least its boiling point. Further, it is known that oxygen is almost insoluble in liquid lead.'V his implies a fair probability that an oxide scale would not dissolve in the molten metal and would afford the same protection to lead in the liquid state as in the solid. All of the oxides of lead for which specific gravity data are available are more voluminous than an equivalent weight of metal or a lower oxide from which they might form, hence the scales will be in compression. Lead oxides are known to be ductile, so it would be anticipated that they would form coherent nonporous scales. It is not surprising to learn, then, that both solid and liquid lead scale according to the Tammann, and Pilling and Bed-worth law.14,15 (Gruhl states that at 600°C and above lead oxidizes linearly with time because of "spitting" of the scale.) The parabolic constants K reported by various investigators3,14-16 are badly scattered, however, as shown in Fig. 2. The oxides formed on solid lead were described as being reddish-brown but were not chemically identified by Pilling and Bedworth.15 Gruhl's descripdin³ of the appearance of the scales On his liquid samples indicates that a (yellow orthorhombic) PbO is formed initially on the specimens but gives Way eventually—at least at temperatures below 486 °C— to .ß (red tetraunal) PbO, and that below 540°C minium—Pb3O4 :is firmed at an even later time as an overlay on either the red or yellow PbO. Fig. 3 is a graphical interpretation of Gruhl's description. Gruhl does not indicate any change in the parabolic scaling rate as yellow PbO converts to red. He does indicate that minium reduces the scaling rate, al-

Jan 1, 1953

By R. F. W. Pease, R. A. Ploc

A scanning electron microscope with a resolving power better then 100Å has been developed for the direct examination of surfaces. This instrument was used to study iron undergoing oxidation at 500°C. It was found that the electron current in the scanning electron microscope was low enough (about 10-atrzp) to have no observable effect on the growth of the oxide. "Armco " iron, when oxidized, exhibited an oxide film whose thickness and whiskey population varied with pain orientation; but purer iron, when oxidized, exhibited no such pain dependence and whisker occurrence appeared to be caused by impurities. UNTIL recently most surfaces of opaque specimens could either be studied with a light microscope or, if higher resolution was required, by viewing a replica of the surface in a transmission electron microscope. Direct electron microscopy of a surface has, in general, proved difficult owing to excessive foreshortening and the poor image quality obtained. The scanning electron microscope, however, offers an alternative method of directly viewing a surface without these disadvantages. At low magnification it offers a much larger depth of focus than the light microscope, and at high magnifications it offers much higher resolution (about 100Å). PRINCIPLE OF THE SCANNING ELECTRON MICROSCOPE A schematic diagram is shown in Fig. 1. The electron optical system consists of a gun followed by a series of lenses which focus the electron beam onto the surface of the specimen. The beam is scanned in a rectangular raster across the specimen surface and, by amplifying the secondary electron current from the 'pecimen, a picture of the specimen surface is built UP sequentially on the face of the display cathode-ray tube. The magnification of such a system is given by the ratio of the scan amplitude on the display cathode-ray tube to

Jan 1, 1965

By G. W. P. Rengstorff

In an effort to find an oxidation-resistant alloy of molybdenum, binary and ternary alloys containing aluminum, chromium, cobalt, iron, nickel, silicon, titanium, tungsten, vanadium, and zirconium were screened. Fourteen other alloying additions were also tested. Many of the alloys were more oxidation-resistant than molybdenum, but none were entirely satisfactory. MOLYBDENUM oxidizes extremely rapidly above 1450°F in air. At 1800°F, a loss of metal at the rate of 0.1 in. in 4 hr is typical. The high speed of this oxidation may be judged by comparison with the oxidation rate of 0.1 in. per year (0.00005 in. in 4 hr), sometimes taken as the maximum permissible oxidation rate at 1800°F for a satisfactory Fe-Cr-Ni alloy. Great strides have been made in the development of coatings and cladding to protect molybdenum from oxidizing atmospheres. These developments in surface protection will undoubtedly make it possible to take advantage of the excellent hot strength of molybdellum and its alloys in many new applications. Still, even the best coating can protect molybdenum only as long as the surface layer is unbroken. Research was undertaken to determine whether an alloy of molybdenum could be found which would resist oxidation. Such an alloy would not deteriorate suddenly when the protective surface layer was destroyed in a small area. In seeking an alloy of molybdenum to resist oxidation, the physical properties of molybdenum could not be sacrificed entirely. The development of an alloy with the desired resistance to oxidation was not achieved. The information obtained on the effect of a large number of elements on the oxidation of molybdenum is, however, of value in the development of coatings. Indeed, many of the alloys tested for oxidation resistance were already known to have poor mechanical properties but were tested to aid in the development of coatings. Oxidation of Molybdenum The rapid oxidation of molybdenum is usually attributed to the volatility of Moo,,. Gulbransen and Wysong have shown that molybdenum oxidizes very slowly up to 850°F, the temperature at which the oxide film begins to evaporate. Melting as well as evaporation of molybdenum oxides promotes the oxidation of molybdenum. MoO melts at 1465°F. MOO, the oxide which is believed to form at the metal-oxide interface, combines with MoO, to form a eutectic having a melting point of 1432°F.' The liquid oxide, even if nonvolatile, could cause poor resistance to oxidation by allowing easy transport of molybdenum and oxygen ions through the oxide. Actually, a sudden increase in the rate of oxidation of molybdenum at 1460°F has been observed to coincide with the appearance of a liquid phase. The formation of a volatile oxide is not unique with molybdenum. The problem is also encountered with vanadium, tungsten, and some of the Pt-Pd group of metals. Vanadium not only forms the volatile V2O3 but, like molybdenum, forms a liquid oxide coating. Few attempts have been made, however, to prevent the rapid oxidation of these metals by alloying. Oxidation of Molybdenum Alloys At the beginning of this work, very little was known of the oxidation resistance of molybdenum alloys. It was known that molybdenum disilicide (with 37 pct Si) has extremely good oxidation resistance,' but this compound is so brittle that it has few uses. It is an effective protective coating for molybdenum when allowance can be made for its brittleness. Chromium was known to retard the oxidation of molybdenum,' but at least 50 pct Cr was necessary to have an appreciable effect. Other, unpublished, reports show that a few other alloys have been given preliminary tests, but the results have not been promising." Choice of Alloys to be Investigated An alloying element might be expected to protect molybdenum in either of two ways: Its oxide might combine with molybdenum oxide to form a stable, nonvolatile complex oxide (a molybdate); or the oxide of the alloying element might form in preference to molybdenum oxide, developing an impervious layer which would prevent the formation of a volatile molybdenum oxide. The knowledge available about the formation of molybdates was meager. Therefore, the initial study was made on alloys of molybdenum with elements having especially stable oxides. On this basis, binary and ternary alloys containing the following six elements were investigated: aluminum, chromium, titanium, zirconium, silicon, and vanadium. Nickel was also added as an alloying element. Although it does not form a more stable oxide than molybdenum, it does impart some oxidation resistance to copper and iron. Its inclusion in the study was fortunate because its alloys proved to be the most promising of those first tested. Apparently nickel formed a stable molybdate. Because nickel was effective in reducing the oxidation rate of molybdenum, the elements iron, cobalt, and tungsten were added to the list. The ten alloying elements mentioned form ten binary and 45 ternary alloying systems with molybdenum. A series of alloys was tested in each of these systems. In addition, at least one test was made on the effect of each of the following alloying elements:

Jan 1, 1957

By F. H. Wilson, M. L. Kronberg

The low temperature recrystalliza-tion of very heavily rolled copper produces a fine grained structure with a high degree of preferred orientation. Additional heating to within a few hundred degrees of the melting point may induce an abrupt and pronounced increase in the grain size, with the resulting crystals having new orientations. This behavior at high temperatures is commonly termed "secondary recrystallization." Several investigations have dealt with the phenomenon arid have served to bare many features of the beha~ior.1-4 In general,observations have been made on the sizes and shapes of the grains, and data have been presented showing the existence of an induction period in isothermal experiments. Although it has been well established that the orientation before the change is statistically (100) 10011, the so-called "cubically aligned" texture, there is no such agreement on the orientation after the change. For example, Dahl and Pawlek1 describe it as being equivalent to an approximately 30" rotation about the [l00] axis of the ideal cubic texture which is parallel to the rolling direction, the resulting orientation being near (210)[001]; and Cook and Richards2 find an orientation of approximately (110)[L12]. Since the completion of most of the work to be reported in this paper, Rowles and Boas3 have published their ver] illuminating paper on "secondary recrystallization," in which they present convincing evidence for a third orientation and show that their esperiments give no evidence for either of the other two orientations. The orientation is described as equivalent to an approximately 30° rotation about a [ 111] pole of the ideal cubic orientation. The existence of a variety of reported orientations is not unique for copper, for a similar state of affairs exists for other systems that have been studied— aluminum, nickel, nickel-iron alloys, and others. It seems therefore that the existence of this variety does not necessarily constitute a contradiction, but rather indicates that different experimental conditions yield different results. The fundamental nature of the phenomenon has not been elucidated. However, it has been generally recognized that the large grains could be the end product of growth of a few select grains already existing in the sample in minor amounts—too small to allow detection—or that entirely new ones could be formed by a process of nu-cleation and growth. Existing experimental evidence does not distinguish between these two most apparent possibilities. Nevertheless, the former has been more generally favored largely because our current understanding of the state of an annealed metal has not made it seem reasonable to expect a nucleation event to occur at temperatures above those required for the primary recrystallization. Observations on the Preparation and Heating of Twin-bearing Cubically Aligned Copper The starting material used throughout. the investigation was a bar of OFHC copper, forged and annealed at 950°C. Visual inspection showed the grain size to be around 0.5 mm, and did not disclose any preferred orientation. A chemical analysis showed the following composition: Cu + Ag— 99.99 Pct S — 0.005 pct 0 — <0.005 pct For the preparation of cubically aligned copper, ¾ in. thick slabs were cut from the bar, heavily pickled in concentrated HNO3 and cold rolled to sheets about 0.012 in. thick. The reduction in thickness was approximately 98.5 pct. Standardized annealing techniques were followed. Samples to be heated were lightly dusted with alumina in order to prevent sticking and then sandwiched between 1/16 in. copper plates. The resulting sandwich was heavily wrapped with copper sheet, and then annealed in air. The protection was such that only very thin films of oxide were formed. That the associated light oxidation of the samples had no specific effect on the recrystallization behavior was shown by the similar results that could be obtained on annealing in highly purified and dried hydrogen. Two methods were used in bringing samples to temperature: (1) by placing the package directly in the furnace at temperature and (2) by placing the package in the furnace at room temperature, and then slowly increasing the temperature. The corresponding heating rates are illustrated in Fig 1, and will be referred to as "rapid" and "slow," respectively. Unless specified otherwise, all anneals will be of the former type. Metallographic examination was made on samples prepared by electrolytic polishing and etching as described in the Metals Handhook.* STRUCTURES FOUND BEFORE "SECONDARY RECRYSTALLIZATION" OCCURS Annealing the rolled material for 1 hr at 400°C produced a heavily twinned, cubically aligned structure, the grain size being of the order of 0.03

Jan 1, 1950

By Guido Bassi

IT is known&apos;" that secondary recrystallization occurs in copper sheet with at least 90 pct reduction after annealing at high temperatures, 700" to 1000°C. Turkalo and Turnbull4 have found recently that secondary recrystallization might occur even after annealing at such low temperatures as 500°C for a high purity, coarse-grained copper sheet. It will be shown in the following that in an electrolytic tough pitch copper wire, with a high degree of deformation, secondary recrystallization might occur at even lower temperatures. A hot-rolled rod of 9.5 mm diam (temperature at which rolling commenced was 850°C) was drawn in continuous drawing machines to 0.4 mm, corresponding to a cross-section reduction of 99.8 pct. The texture in the center of the wire (the sample for X-ray analysis was etched to 0.15 mm diam) is a mixture of the [111] and the [loo] direction, as can be seen from Fig. 1. This is in accordance with the result of Schmid and Wassermann.&apos; After a few minutes annealing of the wire at 200 °C, there is a noticeable recrystallization of the structure with a preferred orientation in the [l00] direction at the expense of the [Ill] deformation texture, as Figs. 2 and 3 show. Farnham and OINeill" reported a similar result. The final recrystallized structure shows mainly the [loo] orientation. There is however a small amount of [111] and random orientations. If the wire is annealed at 400°C, the recrystallized structure first shows a [loo] texture, Fig. 4, but as the annealing time is increased the fine-grained structure transforms into coarse grains, Fig. 5, giving a new preferred orientation, Fig. 6. The calculations show this to correspond to the [I121 direction. Even if the annealing that gives the primary recrystallization is carried out for six weeks at 20O°C, the same secondary recrystallization texture is obtained if the annealing is continued at 400°C. Schmid and Wassermann7 found the [I121 texture, but only after annealing at 1000°C or higher. The appearance of a secondary recrystallized

Jan 1, 1952

By Jean Howard

THERE are two mechanisms by which secondary crystals can develop in bcc alloys, namely 1) impurity inhibition and 2) strip-thickness inhibition. This paper reports some studies of each mechanism; the alloys were Si-Fe, A1-Fe, Cr-Fe, Mo-Fe, and Ge-Fe, as well as iron itself. All the alloys, which were of interest as part of a program of work on soft magnetic materials, were made by a powder-metallurgy process, using carbonyl iron (Grade MCP) as the starting material. Earlier phases of the work have already been published. Work described previously1 shows how the oxygen content of the sintering. atmosphere can be used to produce silica in the material which acts as a grain-growth inhibitor. Since then it has been found more convenient to make use of the oxide in the iron powder to control the silica content of the material. The compacts are sintered in vacuum which allows a direct reaction to take place between the iron oxide and the silicon. Details are given elsewhere.4 By this method, and by suitable adjustment of the rolling schedule, material with cube-on-edge secondary crystals has been produced in thicknesses from 0.1 to 0.001 in. in iron containing from 2-1/2 to 4-1/2 pct Si. It was also found possible to process 6-1/2 pct Si-Fe to 0.001 in. This was achieved by refinement of the sintered-compact grain size by using fine-particle silicon (i.e., <200 mesh). The brittleness of the material necessitated hot rolling to 0.020 in., from which thickness cold rolling was possible. If the conditions of sintering and the cold-rolling schedule were correct (i.e., as given elsewhere4 for 3-1/4 pct Si-Fe) secondary crystals of (110) [001.] orientation could be developed. The size of the secondary" crvstals" could not be

Jan 1, 1965

By T. V. Philip, R. E. Lenhart

When commercial silicon iron sheets of varying magnetic quality are isothermally annealed at high temperatures, extremely large grains develop in the material having good magnetic properties. These grains are of the (110) [001] orientation and are formed by secondary recrystallization. The primary driving force for this secondary recrystallization is grain boundary free energy. For the secondary grains, activation energies of 103 kcal per mole for nucleation, and of 75.5 kcal per mole for growth, were obtained. The activation energy for nucleation of the secondary grains is consistent with a model involving redistribution of a precipitate acting as the primary grain growth inhibitor. SINGLY oriented silicon iron sheet was first produced in 1935.1 The material as commercially produced today has a very highly developed preferred orientation or texture; up to 95 pct of the grains are crystallographically oriented with their (110) planes in the plane of the sheet and their [loo] directions parallel to the rolling direction. This texture, usually written as (110) [00l], is referred to as the "GOSS" or the "cube-on-edge" texture. Because the magnetic properties of this material are superior to those of the nonoriented sheets in the direction of rolling, the oriented silicon iron has acquired tremendous industrial importance especially in the manufacture of transformer cores and other electrical equipment. The commercially produced material is essentially an iron-silicon alloy containing about 3 1/4 pct Si with minor impurities totaling less than 0.15 pct. The silicon steel heat is melted in the open hearth or electric furnace. The ingots are hot rolled, with or without being slabbed, to strips of 0.100 to 0.080 in. thickness. They are then cold reduced to an intermediate thickness, recrystallized, cold reduced to final thickness, decarburized, and finally annealed at a high temperature. During this high-temperature anneal, extremely large grains with the cube-on-edge texture are produced in the sheet. Several papers have appeared in the literature2-10 relating to the production of the Goss-textured material. Most of these describe the textures produced on cold rolling and on subsequent annealing of single crystal or polycrystalline silicon iron. May and Turnbull11,12 have recently shown the necessity of a second-phase dispersed impurity in the material for the production of the Goss texture. However, none of these papers describes in detail the nucleation and growth kinetics of the (110) [001] grains during the final high-temperature anneal.* The present work, therefore, is an attempt to understand the nucleation and growth kinetics of the cube-on-edge grains in the silicon iron sheet during the final high-temperature anneal.

Jan 1, 1962

By T. V. Philip, R. E. Lenhart

C. G. Dunn(General Electric Research Laboratory)— It is well recognized that understanding of the formation of the cube-on-edge texture in annealed commercial cold-rolled Si-Fe strip is important industrially as well as scientifically. I would like to make a few remarks on this subject, discuss some points in the present paper, and list two remaining problems that appear to be particularly outstanding. Attention should be drawn to the paper by P. K. Koh,23 which also considers the kinetics of secondary recrystallization in 3 pet Si-Fe, produced commercially by the Allegheny Ludlum Steel Corp. Koh covered a much larger temperature range than do either the present authors or P. N. Richards, whose work is mentioned in a footnote. Koh found an induction period (of short duration) even for isothermal anneals at 1260oC (2300°F). Koh and Dunn24 also found a change in texture during the 1260oC anneal for the same material. On the other hand, the material in coil D, according to Philip and Lenhart, underwent no sec-condary recrystallization, only continuous grain growth. The grade classifications of the four coils studied would suggest, however, that all four materials had developed the cube-on-edge or (110) [001] texture, but to varying degrees. Since no data on this are given and since watt loss depends

Jan 1, 1962

By Jean Howard

ALTHOUGH zone melting has found favor in recent years because of its convenience and its faster rate of production of single crystals, the older technique of strain annealing still has a number of advantages. It has been reported1 that the lattice of a crystal prepared in this manner has fewer defects than one grown from the melt and, of course, the control of the external geometry is easier. Also, the diameter of the crystal which can be grown by zone melting has a theoretical limit determined by the surface tension, thermal conductivity, and specific gravity of the material, while the size of that which can be grown in the solid state is limited only by practical considerations. In a program for the study of the structure-sensitive properties of niobium and its alloys it was desirable, for ease of handling, to have available single crystals of large diameter. This requirement dictated the choice of the strain-anneal technique. Induction heating was chosen in the present work in preference to other methods because of its deep penetration of large-diameter sections. A five-turn coil, powered by a motor generator operating at 10,000 cps, is contained in a vacuum chamber. The work is lowered through the coil for both the recrystallization and the crystal-growth steps. Starting with electron-beam melted material, the bars are cold-swaged, recrystallized, strained in a tensile machine, and then subjected to the growth step. Single crystals have been grown under the following conditions: Reduction in area during swaging— 79 to 99 pct, recrystallization temperature—1500o to 1667°C at the rate of 1.25 in. per hr, strain—1.0 to 2.5 pct, growth temperature—1600o to 2400°C at rates from 0.15 to 1.25 in. per hr. Starting grain sizes achieved after the recrystallization step varied from 0.6 to 1.55 mm. The starting grain size was found to be critical; if it is too fine and has any residual cold work, as shown by the presence of a fiberlike texture, a single crystal cannot be grown. Using this technique niobium single crystals have been grown from 0.250 in. diameter and 12 in. long to 1.00 in. diameter and 5 in. long as shown in Fig. 1. The 1-in. crystal is the largest to be reported for a refractory metal as compared to 0.500 in. for molybdenum grown by zone melting.2 As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and Smallman,3 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point ahead of the interface between the single and polycrystalline portions. Finally, it is returned to the chamber and growth is continued "around the corner". The amount of bending which can be imparted to the rod is limited by coil geometry which up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. The perfection of these single-crystal specimens as a function of process variables is being measured by X-ray and metallographic techniques and the results will be reported in a forthcoming paper. This work was partially supported by the Advanced Research Projects Agency.

Jan 1, 1964

By Jean Howard

ThE formation of the (100) [001) texture in 3-1/4 pct Si-Fe strip was first reported by Assmus ef a1.l in 1957. Since then much experimental work has been carried out with a view to establishing the mechanism involved. The papers cited above state that the (100) [001] texture was developed in strip rolled from material melted and cast in vacuum. (The impurity content of the ingot is reported as 0.005 pct.) The present note records that similar results can be obtained in material processed by powder metallurgy. A processing schedule is described.which enables the texture to be formed in strip up to 0.010 in. thick, but there seems no reason why this should not be achieved in thicker strip, provided that large grains are developed after sintering. The materials were prepared from Carbonyl Iron Powder Grade MCP (particle size 5 to 30 p) of the International Nickel Co. (Mond) Ltd. The powder contains about 0.15 pct 0, 0.01 pct C, 0.004 pct N, <0.002 pct S, $0.005 pct Mg and Si, and 0.4 pct Ni— that is, it is substantially free from metallic impurities other than nickel, which is thought to be unimportant in the present work. The silicon powder was 99.9 pct purity, or material of transistor quality (ground in pestle and mortar). The mixed powders (3-1/4 pct Si to 96-3/4 pct Fe) are heated in hydrogen at 350" and 650°C to deoxidize the iron before sintering loose at temperatures between 1350" and 1460°C (depending upon the ultimate thickness of strip required) for up to 24 hr. The object of the high-temperature sinter is to develop a large grain size at this stage. Alternatively, the loose sintering can be done at a lower temperature followed by rolling or pressing and then annealing at temperatures between 1350" and 1460°C. Both methods produce large grains, which remain large throughout the process. The compact is then hot-rolled to approximately 1/8 in. with high-temperature interstage anneals if necessary. This step is taken to avoid intercrystalline cracking which would occur if the material of such large grain size were cold-worked. The bar is then annealed at 1050°C and reduced to its final thickness by approximately 50-pct reductions and 1050°C interstage anneals. Throughout the process the dew point of the hydrogen furnace atmosphere is maintained at about -40°C. Samples were annealed in hydrogen at various temperatures and times. Secondary recrystalliza-tion to (100) [001] was developed on the thinner material (i.e., up to 0.002 in.) by annealing in hydrogen at 1050" to 1200°C with a dew point of - 40°C or in vacuum (10-5 Torr) at 1050°C. With the thicker materials (i.e., up to 0.010 in.) the best results were obtained by annealing in hydrogen at 1200°C with a dew point of - 55°C. Complete secondary recrystal-lization to (100) [001] textures was obtained. Above these temperatures secondary recrystallization to (110) [001] tended to develop. The final annealing of samples was normally carried out with the samples placed between recrystal-lized alumina plates, but some experiments were performed with the samples suspended so that their surfaces were not in contact with anything except hydrogen, and these were equally successful in developing secondary crystals. An approximate determination of the proportion of material (before secondary recrystallization took place) having crystals with the (100) or (110) planes in or near the rolling plane showed that 11 pct of the sample had (100) and 16 pct (110). The method used for the determination is described below. A sample was annealed at a temperature just below the secondary recrystallization temperature and etched to reveal the (100) planes. The approximate area covered by crystals having (100) or (110) in or very near the surface was measured on the screen of a Vickers projection microscope. This was repeated for twenty positions chosen at random and a mean of the results calculated. The main hindrance to developing the secondary crystals in the thicker materials was the difficulty of obtaining a large enough initial primary grain size before secondary recrystallization. This was overcome by increasing the particle size of the silicon powder used. During the course of the work, it had been observed that the larger the grain size after sintering the more likely it was that the material would be successful in developing secondary crystals at a later stage. An experiment was therefore carried out to determine whether the material with the larger grain was more successful in developing secondary crystals due to the large grain produced at the sintering state per se or whether it was due to the greater reduction of silica brought about when the sintering temperature was raised in order to increase the grain size. A comparison was made between two compacts, one of which was made with silicon powder of 60 to 100 mesh, the other with silicon powder which was finer than 200 mesh. F?r this experiment, use was made of a phenomenon previously observed that the larger the particle size of the silicon powder employed in making a compact, the larger is the grain size of the compact. The silicon powder was ground

Jan 1, 1964