Several of the current concepts of brittle fracture involve consideration of, the existence of defects or flaws. Griffith 1 observed that the tensile strength of brittle materials was several orders of magnitude less than might be expected from the calculated strength of the molecular bonds. He was able to show that the stress concentration at the tip of an elliptical crack is sufficient to raise the local stress level many fold. He therefore proposed that real materials do contain such stress risers in the form of minute cracks and that this accounts for the rather large difference between theoretical and actual strengths of brittle materials. The degree of stress magnification depends to a great extent upon the orientation of the crack with respect to the general stress system, and to the general geometry of the crack. It is but a small step to extend the theory to include flaws and defects of other sorts which, though they may be less tractable mathematically than cracks, may still function as stress risers in a real sense in real materials. Brace 2 proposed that the application of the Griffith theory to rock material could be tested in two ways: "(a) by finding the orientation of cracks from which macroscopic fractures have developed and (b) comparing failure strengths from tests at different conditions of loading." In 1963 the author and coworkers at the Bureau of Mines, Twin Cities Mining Research Center, working on a problem involving relationships between strength, sonic velocity, and microstructure "eveloped an experimental technique to examine several somewhat similar questions; namely. does the frequency of occurrence of actual or potential stress risers dictate the relative strength of the material as proposed by Weibull;4 can actual flaws or defects in the rock structure be identified and related to strength and perhaps other properties in accordance with Griffith's theory; and is the anisotropic strength and elastic behavior of certain rocks related to the preferred orientation of these actual or potential stress risers? The experimental approach developed to answer these questions appears equally applicable to the testing of Griffith's theory as proposed by Brace. Basically the approach consists of a series of point-load tensile tests followed by petrofabric examination of thin sections prepared from the specimens in order to identify and apply a quantitative measure to microstructural defects which may have contributed to the failure process. In the point-load test, tensile stresses are induced by a compressive load applied to the center of a disc-shaped specimen by means of two opposing hemispherical indentors. Failure generally occurs as a single fracture parallel to the axis of loading and bisecting the disc. Because of the geometrical symmetrical the induced tensile stresses are symmetrical about the loading axis

Jan 1, 1967

By J. D. Sullivan, Chester R. Austin, J. L. Nunes

IT is characteristic of most shales and surface clays that a bloated or vesicular structure is produced by burning to a sufficiently high temperature, usually about 150° to 200°F. above the normal maturing temperature used when making common brick of the same material. Early investigators recognized this phenomenon and attributed it to the release or expansion of gases in the vitrified piece. A number of theories have been advanced on the source of the gas and the manner in which it is evolved, but none has been proved conclusively. T. E. Jackson's1 early theory that bloating was due to oxygen evolved by ferric oxide in forming ferrous oxide or ferrous silicate was never substantiated by experimental work. Orton2 thought this explanation unlikely, as all clays should bloat at the same temperature, if this were true. He found that clays bloated in the range from 1100° to 1706°C. Also, many clays containing iron did not bloat at all, but fused. Orton also stated that oxidation of different types of carbon was a source of gas during burning of clay and should be expelled before vitrification was reached. Seger3 said that he had dissolved ferric oxide in glass with no apparent evolution of gas. Matson4 came to the conclusion that ferruginous days burned to vitrification in an oxidizing atmosphere did not have the iron in a ferrous form. According to Wilson,5 the gases responsible for bloating might be entrapped air, water, sulphur dioxide, carbon monoxide, oxygen, and hydrocarbons. He spoke of two causes of bloating: (I) incomplete oxidation below the vitrification temperature, and (2) decomposition of compounds and evolution of gases above the vitrification temperature. Decomposition of calcium sulphate was given as the principal example of the latter. Bleininger and Montgomery6 stated that if any time after vitrification began the evolution of gaseous matter was rapid enough so that pressure was produced within the day, bloating was certain to take place, and a vesicular structure would be formed. They recognized that initial structure, rate of heating, kiln atmosphere, and many other variables affected bloating. Work done by the Emergency Fleet Corporation7 indicated that clays suitable for bloating should be high in compounds of metallic oxides, carbon, sulphur, sodium, potassium, or other equivalent compounds, which either act as a flux or give off gas. Orton2 studied the chemical status of the carbon, iron, and sulphur in clays during various stages of burning, using a Huron shale that bloated under oxidizing or reducing conditions. He found that only a small amount of sulphur remained in the clay and that it could be detected only by dissolving the clay in hydrofluoric acid; i.e., the sulphur was in combination with the silica. Orton said that this sulphur was probably in the form of iron sulphide dissolved in the glass phase. The iron sulphide was not broken down by heating, but was dissolved in the basic slag or glass,

Jan 1, 1942

By D. J. McAdam

As shown in three recent papers by the author,6,7,8 in two papers by McAdam and Mebs,9,10 and in a paper by McAdam, Mebs, and Geil,11 the technical cohesive strength of a metal, in any particular state as regards mechanical treatment and heat-treatment, cannot be represented by a single stress value, but must be represented by a diagram with the principal stresses? as coordinates. Each point on the boundary of such a diagram represents a technical cohesion limit. The technical cohesive strength thus comprises an infinite number of technical cohesion limits, each representing fracture under a specific stress combination. Moreover, neither the yield strengths nor the ultimate strength can be represented completely by a single stress value, but must be represented by a diagram with the principal stresses as coordinates. All combinations of the principal stresses may be classified in three groups as illustrated by Fig. I. Fig. Ia shows three typical stress combinations with no two principal stresses equal. The magnitude of each principal stress is indicated qualitatively by the length of the arrow. Arrows pointing away from the cube indicate tensile stresses; arrows pointing toward the cube indicate compressive stresses. Typical stress combinations with two principal stresses equal are illustrated in Figs. Ib and Ic. Such stress combinations would be produced by subjecting a cylinder to combinations of uniform axial and radial stresses. The uniform radial stress may be resolved into two equal principal stresses, with the mutually perpendicular directions rotatable around the axis of the cylinder. Fig. Ib shows stress combinations with S2 equal to Sa. The greatest principal stress is in the axial direction, and the stress combination tends to cause either absolute or relative increase in length.* Fig. Ia shows stress combinations with Ss equal to Sl. The greatest principal stress is in the radial direction, and the combination tends to cause either absolute or relative decrease in length. The complete representation of either technical cohesive strength, yield strength, or ultimate strength generally requires a three-dimensional diagram. When two of the principal stresses are kept equal, however, the strength of a metal may be represented by a two-dimensional diagram with the coordinates representing the axial and radial stresses.6-11 In this paper, attention will be confined almost entirely to stress combinations with two of the prin-

Jan 1, 1944

By James Aston

Three years ago the writer presented a paper on the trend of development in the wrought iron industry,' wherein was described a process in the development of which he has been a factor, which at that time had passed through several years of progressive experimental development but which had not then been put upon a commercial scale of operation. The present paper deals with two years of observation and experience in the commercial operation of a plant by the A. M. Byers Co. at Warren, Ohio. It will not enter into the controversial field of the relative merit of wrought iron and steel in various classes of service, nor will it elaborate upon the characteristic services or fields of utility to which wrought iron is particularly adapted. It is sufficient to state that the wrought iron industry is upon a substantial basis and that the material finds service in pipe, where its advantages are in superior corrosion, fatigue, welding and threading qualities; in bar iron for staybolts, engine bolts, and rivets, demanding maximum service against corrosion and fatigue; in plates for corrosion service; and in chains, because of welding and shock-resisting characteristics. In short, ability to withstand the stresses of shock and vibration, or the ravages of corrosion, to hold protective coatings, and to give maximum efficiency in welding, are its features of relative superiority. If these features were not well recognized, the wrought iron industry would have shrunk to insignificance in the face of high costs and acknowledged limitations in manufacture. To charge that this industry is built upon a structure of assumption, psychology, and improperly weighed evidence is an impeachment of the integrity or belittling of the powers of observation of users through many centuries of service experiences. In a history which extends to prehistoric time, and which is linked up with the earliest records of ferrous products, the dominant method of manufacture, as we have known it for little over a century, occupies a very small niche in the span of years that mark production and use of wrought iron. Puddling, the outstanding manufacturing method of

Jan 1, 1929

By L. G. Austin

My first contact with industrial milling was during the time I worked in the electricity generating industry in the United Kingdom. In visits to power stations to investigate either deposits in the boiler furnaces or polluting deposits settling around the stacks. I had to check the performance of the vertical coal pulverizers, since poor pulverization aggravated both problems. Naturally, then, when I came to the USA in 1957 to take a PhD in fuel technology at Penn State, I was put to work to review the science of coal pulverization. After this reviewing, I was completely confused. On one hand, there was a well-developed understanding of stress-strain equations, and a rapidly developing knowledge of how stressed, brittle solids fractured, based on the Grifith crack theory. On the other hand, reading in the grinding literature gave me: -Kick's Law, which was clearly not correct in the light of modem fracture theory; -Rittinger's Law, which was also clearly not correct; -Bond's Third Law of Comminution, which was claimed to have something to do with the Grifith crack theory, but where the connection between the two was made by intuitive pseudo-scientific reasoning I could not accept; -the choice of mill motor power for the most common type of coal mill, the Raymond pulverizer, was calculated from the fan power required to move air through the mill. Although I could accept the empirical connection between the two, it made no sense from the point of view of fracture energy. Even today, most books or review chapters on size reduction start from these laws. Incorrect statements abound in the literature, such as "the Hardgrove Index is based on Rittinger's Law," which it is not, "The Bond theory states that work input is proportional to new crack tip length produced in particle breakage," which is not true, etc. My own test work showed that these "laws" did not fit the data for grinding of coal. At about this time, Epstein (1948) and Broadbent and Callcott (1956), following the original work by R.L. Brown (1941) at the British Coal Utilization Research Association, proposed describing breakage as a series of fracture stages. I took their concepts and developed the basic differential equation for a batch grinding process continuous in time, analogous to a batch chemical reactor. Robin Gardner then joined the project and did his PhD on treating batch grinding in the same way as a batch chemical reactor. He found that the basic equation had already been partially derived by Sedlatschek and Bass (1953) in Ger- many. We confirmed experimentally the validity of the equations for describing batch grinding (1962) and formulated the equation describing steady-state continuous grinding in a fully-mixed mill. At about the time this work was published, Gaudin and Meloy (1962) and Filippov (1961) independently published essentially the same equations, but without experimental proof of the validity of the concepts. I will give a brief overview of what these beginnings had led to in the design of mills for size and power, and show some of the results of this more detailed understanding of grinding processes. Concepts of Fracture Mills such as tumbling ball, rod, pebble and autogenous mills and vertical mills such as the Raymond, and E-type, apply compressive stress to lumps or particles relatively slowly. Compressive stress applied to a particle of an elastic brittle solid imparts overall strain energy to the solid and produces local regions of tensile stress, [(Fig. 1)] (Berenbaum and Brodie, 1959).

Jan 1, 1985

By F. Osmond

When a metal (whether a simple substance, an alloy, or a compound) presents, in each of the smallest parts to which it can be redueed by mechanical division, a constant chemical composition, it is defined as chemically homogeneous. But chemical hombgeneity by no means necessitates mechanical homogeneity. There are no perfectly amorphous metals. Crystalline forces, on the one hand, and tensions or compressions, on the other band, determined by icequalities of temperature in the mass during heating or cooling, give rise in every metal to the formation of geometric elements of structure. These elements may, moreover, assume perfect crystalline forms, with their planes of cleavage; or embryonic crystalline forms, segregated in the midst of. a paste of confused organization; or pseudo-crystalline forms of expansion and contraction, like those produced in the drying of gelatinous precipitates or (most frequently) these different forms associated. 111 either case the adhesions between two adjoining structural elements, respectively homogeneous, may be very different from the interior cohesion of each of these elements. The mechanical properties of this complex aggregate cannot be simple, and, when it is submitted to strains sufficient to produce deformation, the results may be very different according to the type of structure or the manner in which it is affected by the strains. It may be fairly said that a metal does not present a single resistance to tension, or a single resistance to compression, etc., but in fact, at least theoretically, as many resistances to tension, compression, etc., as it may possess coexistent features of structure; only, in any single test, it is the weakest of the resistances involved which makes itself evident. For further explanation, let us imagine a cylinder A B (Fig. I), formed of two similar halves A and B, placed together upon their common base x y. Such a system evidently presents no resistance to axial tension, while it would resist axial compression like a single

Jan 1, 1894

By Tell Ertl

The term oil shale is defined. Foreign oil-shale developments are outlined briefly. The richest and most extensive oil-shale deposits in the United States lie in western Colorado. The Bureau of Mines is opening two adjacent areas for underground mining. in western Colorado. From the first area the oil shale is mined selectively as required by the retorting plant. The second area is being developed as a unit of a full scale oil-shale mine to ascertain the most practical methods of mining oil shale and to determine costs. In both of these mining areas, research will be carried on to develop new and improved practices for mining oil shale. Introduction Oil shale is a sedimentary rock containing a solid mineraloid of indefinite composition known as kerogen. On heating oil shale, the kerogen undergoes thermal decomposition and some of the vapor products of the decomposition can be condensed as shale oil. Oil from shale can be a major source of liquid fuels since extensive deposits of oil shale are known to exist throughout the world. The United States considers the establishment of an oil-shale industry only when doubt exists of the adequacy of the domestic supply of crude petroleum. On the other hand, oil shale is not strange to foreign oil men. The industry is an old one in other parts of the world. The French industry has been in existence since 1838, the Scottish since 1859, the Australian since 1860, the Estonian and Swedish The since World War 1, and the Manchurian industry since 1929. The most highly exploited oil-shale deposits are the Carboniferous shales of Scotland. About 20 seams ranging from 4 to I2 ft in thickness are worked. The yield during recent years in scotland has been 18 to 25 gal of shale oil per ton, from 3&"30'000 tons per year' The French and Swedish oil-shale deposits are of lower grade than the Scottish. The Estonian oil-shale deposits are 7 ft thick, and the oil yield averages 50 gal per ton. Over 1,000,-ooo tons are mined each year, half of which is used directly as fuel to substitute for coal and the other half is used for the production of oil. Immense deposits of oil shale that will yield 10 to 15 gal per ton exist in Germany. Because of the impending loss of the Rumanian and Polish oil fields and the bombing of synthetic liquid fuel plants, the Nazis in 1943 started a large-scale oil-shale program in Germany. By V-E Day, it is said, oil-shale production had reached the rate of 2500 tons per day and rapid expansion of the industry was imminent. Australian oil shale, known as torbanite, occurs in beds 2 to 6 ft thick. It is of a very high grade and on retorting yields 80 to 160 gal per ton. The oil-shale industry of Manchuria was the largest in the world during the past decade. The well-known Fushun coal deposit in Manchuria has an overburden of 500 million tons of oil shale about 450 ft thick that will yield 10 to 15 gal of shale oil per ton. The oil shale is

Jan 1, 1949

By F. H. Kihlstedt

THE Larap iron deposits, 125 miles east of Manila, are the biggest high-grade iron deposits in the Philippines, and have in seven years produced nearly 4 million tons of 6o per cent ore. Magnetic surveying followed by churn and diamond drilling cheaply developed a score of million tons. The ore zone is a wedge of metamorphic rocks in fresh, Miocene sediments overlain by agglomerates, which seem to have filled a river valley eroded in the sediments. A mild overthrust of the competent agglomerates crumbled the shale in front. Solutions gradually turned it into more competent hornfels and deposited pyrite, then magnetite and pyrite in the pores. As the temperature rose large bodies of magnetite with some pyrite were deposited by replacement and in open cavities in tensional areas of overthrust shears. At still higher temperature magnetite and calcium-magnesium silicates formed other bodies in similar cavities, and finally the thrust zone was invaded by syenite porphyry, causing high-temperature alteration products. Possibly, as temperature abated, more high-grade ore was deposited. The complicated faulting indicates dynamic, chronological and spatial changes of mineralization rather than zoning in a static system. Noncommercial copper, molybdenum and some gold accompanied the iron mineralization. In the thirties the Philippines gained a justified reputation as a country of considerable mineral wealth. Traces of Chinese workings show that these earliest travelers and traders had in a small way exploited the latent gold resources in the Islands. The Spaniards continued this for centuries, but did not succeed in establishing any steady mining industry. Modern technology was required to get it started. The rapid development in the last decade before the war got its impetus from several financial factors, the return to sugar growers of previously collected taxes, the influx of Spanish capital during the civil war in [ ] Spain, the influx of Chinese capital when the Japanese started their "China incident," and others. Directly or indirectly much of this capital reached the mining industry; in particular, gold mining. Out of the turmoil of an exceptional mining boom emerged a sufficient number of good and well managed gold properties to send the production to a level above that of any single state in the United States at the time. Other ore deposits besides those of gold also received their share, and for a country without any heavy industries at

Jan 1, 1946

By Orville R. Lyons, A. C. Richardson

DURING the past few years there has been a growing demand by coal operators for detailed information about the performance characteristics of the various dryers now being manufactured, preferably in such a form that the information could be used to determine the type of dryer best suited to a particular drying problem. A few operators have been desirous of going even further, because they are of the opinion that present-day dryers are not properly designed and that fundamental studies of dryer design should be undertaken. This growing demand for a method of dryer evaluation and the indicated need for fundamental research resulted in the sponsorship by Bituminous Coal Research, Inc. of a project at Battelle Memorial Institute to investigate the thermal drying of coal. In investigating this problem, the most feasible method of attack appeared to be a survey of active operations to determine the present status of the thermal drying of coal. Data were obtained, usually by actual plant tests with the cooperation of the various preparation engineers and their staffs, for Q screen-type dryers, 8 rotary- type dryers, 3 continuous-pallet-type dryers, 2 flash-type dryers, I tray-type dryer, and I cascade-type dryer. The testing program provided: (I) data for 24 coal- drying operations, (2) information about dried, (3) information about the previous treatment that the coal had received, and (4) information about operating costs. The data obtained through the dryer survey and relationships determined from the data make it evident that all of the types of dryers included in the survey can be operated with the same degree of effectiveness if each type of dryer is used to dry the sizes of coal for which it is best suited. It should be noted that it is usually undesirable and often impossible to dry different sizes of coal in one type of dryer. By use of the data in the report, any prospective dryer user, having determined the surface moisture percentage and screen- size analysis of the coal to be dried, the tons of water to be removed per hour, and the final surface moisture percentage desired, should be able to determine with a fair degree of accuracy: (I) the difficulty of the drying problem, (2) the approximate cost of drying, (3) the required dryer inlet gas temperature and volume and exhaust gas temperature and volume, (4) the type of dryer to use, and (5) the size of dryer required. The method of testing the dryers and determining the difficulty of drying can be used by operators already having dryers to check the performance of their particular dryer and determine whether they are operating effectively. Considerably more information was obtained from the survey of thermal drying than was anticipated when the survey was first considered. However, a great deal of work still remains to be done in the field

Jan 1, 1948

By E. W. Cawthorne, R. I. Jaffee, C. M. Craighead

SOLUTION of a solid metal or alloy in a molten metal bath is used daily in melting operations, extractive metallurgical processes, and in brazing. It is generally recognized that temperature, time, agitation, and the composition of the solute metal and the solvent bath all affect solution rate. However, there is little information available in the literature on the kinetics of the process or the relative effect that these variables have on solution rate. In connection with an aluminum brazing study, data on the solution of aluminum in an A1-Si* bath to promote rapid solidification. The chemical analyses were made on drillings taken from the cast plates. The results of this work are listed in Table I. The thermal-analysis data were obtained on 200 gram samples cooled at approximately 1.5" per min. A calibrated chromel-alumel couple was used. The thermal arrests were recorded autographically on a General Electric photoelectric potentiometer recorder. The instrument was calibrated to 22.5 pct. The thermal emf was bucked with a Leeds and Northrup semiprecision potentiometer so that 1 mv represented the full scale of the GE recorder. Referring to Table I, it will be noted that the analytical results tend to be lower than the intended compositions by about 0.3 pct Si in the higher ranges. In view of the known difficulties in obtaining accurate silicon determinations by wet analysis when the silicon content is high and in view of the care that was employed in weighing and preparing the alloys, the intended compositions are believed to be more accurate than the analyses. Furthermore, when the thermal-arrest data are plotted against the intended compositions, a smooth curve is obtained, as shown in Fig. 1. This is not the case when the data are plotted against the analytical results. It will be noted from Table I that the 12.5 pct Si alloy (melt 4) showed a primary arrest at 577.6"C and the eutectic at 576.l°C. The metallographic examination of this chill-cast plate sample showed a small amount of primary silicon. These results, Fig. 1, place the eutectic at slightly less than 12.5 pct Si and are in rather good agreement with the unpublished Hanford data. In all of the subsequent work, the composition of the A1-Si dipping baths was determined by thermal analysis (spread between the primary arrest and the eutectic temperature) employing 12.5 pct Si and 577.2 °C as the composition and temperature of the eutectic. Material Preparation and Selection of the Techniques: At the beginning of this work, it was anticipated that, owing to oxide film present on the surface of the aluminum, difficulty would be encountered in obtaining rapid uniform wetting of aluminum specimens dipped in the A1-Si bath. The following etchants were investigated as possible methods of providing a thin uniform oxide film on the specimen surface: 1—phosphoric acid (H³O4), 2—fluoboric acid (HBFI), 3—sodium hydroxide (NaOH), and 4—hydrofluoric acid (HF). Tests with sheet .specimens (2x½x0.06 in.) of 2s aluminum prepared with these etchants indicated that the fast uniform wetting required for this work could not be obtained if any oxide film existed on the specimen surface. Tests were then conducted by dipping similar specimens etched in 5 pct NaOH and given a thin

Jan 1, 1956

By R. G. Jones, W. L. Kinney, R. E. Schilson, R. S. Wilson, G. A. Clark, H. Suralo

This paper describes the field opeturluns at the Fry in situ combustion project in Crawford County, 111. Field operations may be divided into three phases—-preliminary engineering studies of 1960 and 1961, ignition, and, finally, operation of the test. The Fry combustion project was a pilot test of cocur-rent in situ combustion on a 3.3-acre inverted five-spot. In the summer of 1960, air injection tests were conducted using old wells in the area and a new air injection well drilled especially for the test. In the summer of 1961, four new oil wells were drilled on a 3.3-acre pattern for the pilot test. All old wells in the near vicinity of the pilot test were abandoned to preclude any possibility of gas escaping to adjacent formations. A compressor plant was also installed at the test site in 1961. Air injection tests and other engineering studies were made. At the conclusion of these tests, ignition was accomplished with a 40 kw electrical igniter. Operation of the Fry combustion test was little different from the usual oilfield operation with the exception of the high rate of air injection. No difficulty was found with the openhole completion. There were no unusual corrosion or emulsion problems until bottom-hole temperatures exceeded 150F. Four cores were drilled into the burned-out portion of the reservoir with no mechanical difficulties. INTRODUCTION A cocurrent or conventional in situ combustion test was conducted on the Fry unit of the Marathon Oil Co., in Crawford County, Ill. Besides testing combustion in the Fry type of reservoir, the test was intended to evaluate various operating procedures. This paper presents a discussion of the Fry combustion test field operations. The geology of the reservoir and the test performance are discussed in other papers.'.' HISTORY OF THE FRY UNIT The Fry unit consists of 11 leases totaling 337 acres in an area in which oil was originally discovered in 1906. Production from this reservoir, as from all Robinson sand reservoirs in the area, was very high during the first few years. As the dissolved-gas energy was dissipated, early attempts to retard the decline consisted of vacuum, air, and gas repressuring, and recently, most of the area has been subjected to water flooding. Following early air repressuring, the Fry waterflood unit was formed and water flooding initiated in July, 1952. In the area in which the Fry combustion test was conducted, a peripheral water flood of a 160-acre area was developed as shown in Fig. 1. Between 1956 and 1960, it became apparent that the water flood was unsuccessfd. In looking for a suitable site for an in situ combustion test, the Marathon Oil Co. selected the Fry unit as possessing those features most desirable for such a research project. Field operations associated with the Fry combustion test began in the spring of 1960.

Jan 1, 1966

By John Griffen

THE modern anthracite breaker or washery uses almost completely a wet method of preparation, which requires, roughly, 1 gal. of water per minute per ton of production per day. The entire anthracite industry uses about 320,000 gal. per min. of water for this purpose or 800,000 tons of water per day. As this water leaves the breakers, it contains fine solids-coal, slate, pyrite, and clay-and is then called silt or slush; as slush is the term most commonly used, it will be employed throughout this paper. The solid content of the slush will be referred to as solids. In the earlier days of anthracite mining, little coal was washed, less crushing was employed, and virgin coal was mined exclusively. As a result, the slush problem was not acute because of the relatively small quantity and the coarseness of the solids. Such slush as was produced could usually be easily impounded and retained or could be discharged into streams without any appreciable pollution being apparent. The character of the fine waste from the breakers, changed materially as its quantity increased until now about 40,000 tons of slush solids are produced daily. Second mining and robbing operations materially increased the quantity of fine solids delivered to the breaker in the mine car. The demand for chestnut, stove and egg sizes, to the exclusion of grate, steamboat, and lump sizes, require finer crushing of the mine-run coal with a consequent increase of fine solids in slush. The use of rice and barley sizes removed a considerable tonnage of coarser solids from the slush but left great quantities of fine solids difficult to retain completely and store and long considered of no possible fuel value. Despite the efforts of the coal operators, the slush solids have found their way into the streams causing, in some cases, serious pollution. The Water Supply Commission of Pennsylvania published, in 1916, a report on Culm in the Streams of the Anthracite Region,1 from which the following is taken: About 40,000,000,000 gal. of water carrying 10,000,000 tons of fine culm are discharged into the water-courses direct, flushed into the mines, or disposed of by various means on the surface. The extent to which the very small sizes of anthracite

Jan 9, 1921

By R. W. Jordan, J. Winter, A. J. Goldman

Kirkendall diffusion of copper and nickel atoms across the bond interfaces, as well as oxygen diffusion in the core to the interfaces, are the mechanisms which control the variation in bond strength with annealing time at 1600°to 1800°F in the cupro-nickel clad copper Mint composite. The unequal mass transfer resulting from the high diffusion rate of copper in cupro-nickel compared with that of nickel in copper caused void formation in the core. Small voids also formed in the cladding after short annealing times. These may have been nucleated by nickel oxide particles which are formed by the dissociation of the cuprous oxide in the core and the movement of oxygen to the cupro-nickel interfaces. The bond strength drops to very low values for annealing time up to 3 hr when the void density is greatest. The increase in bond strength after 16 to 72 hr at 1600°F is a result of the decrease in the void density in the cupro-nickel cladding and the growth of grains across the interface. The void density decrease is attributable to grain boundary diffusion of vacancies to the surface. The abnormally large grains in the copper preclude a similar process from taking place in the core. THE solution to many engineering materials problems that cannot be satisfied by using a single metal or alloy is often attained by combining two or more metals in such a way that each component performs a different function, while the composite meets the overall requirements. The Coinage Act of 1965 authorized a changeover from the traditional 90 Ag-10 Cu dimes and quarters to a bimetallic laminate of 75 Cu-25 Ni clad on a copper core. Economic considerations as well as physical, chemical, and mechanical properties provided a basis for the selection of this composite as a substitute for the silver-bearing alloy. An extensive survey of alloys suitable for use as coinage was prepared by Battelle Memorial Institute for the U.S. Mint.1 It was found that the cupro-nickel/cop-per/cupro-nickel composite satisfied the required color, density, mechanical properties, corrosion resistance, electrical properties, and magnetic properties to make it completely acceptable to the general public and the vending machine industry. This investigation is part of a program to determine the feasibility of reclaiming composite scrap by thermally degrading the bond strength of the cupro-nickel clad copper laminate. The composite exhibits bond degradation and subsequent bond improvement during annealing in the temperature range 1600" to 1800°F. A study of the operative diffusion processes and the resultant structural changes was made in order to explain the observed variations in bond strength with annealing time. EXPERIMENTAL PROCEDURES AND RESULTS Bond Degradation. A measurement of the forces required to peel the cupro-nickel cladding from the

Jan 1, 1969

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.' In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator's Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By F. Keller, R. H. Brown

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

By K. H. Adams, T. Vreeland

The basal stress-strain behavior, dislocation density, and strain vale sensitivity of the flow stress uqere measured at room temperature on single crystals oj-zone-refined zinc , 99.999 pct Zn, and zinc containing 0.0025 and 0.02 wt pct Al. No significant change in the stvain rate sensitivity of the flow stress occurs with the addition of aluminum. Changes in dislocation substructure and nonbasal dislocation density were obserrled with the addition of aluminum. The effect of aluminum on the basal slress-strain behavior is explained in terms of changes in nonbasal dislocation density which determines the separation distance of junctions between basal and nonbasal dislocations. The onset of basal slip is associated with the breaking of attractive junctions. The chunge in basal dislocation density was found to be proportional to the one-third power of the plastic shear strain, indepedent of purity. THE effect of impurities in solid solution on the stress-strain behavior of single crystals has been the subject of many theoretical studies. These studies have generally concentrated on the interactions between impurities and dislocations to explain the hardening effeet of impurity additions. The theories that have been proposed include those of yott and Nabarro,&apos;l&apos; Cott-re11; Suzuki; and Fisher. In practice, it is generally difficult to predict the relative importance of the vari- ous effects due to impurities. In addition, secondary effects of impurity additions such as induced changes in dislocation density and substructure in the as-grown crystals have received little attention. Many experimental investigations have been conducted on the effect of impurities on the stress-strain behavior of fcc crystals. Hcp crystals have not received much attention except for the extensive work of Levine et a1.= on magnesium alloy crystals. Stuwe~&apos;&apos; has studied the effect of copper impurity on the critical shear stress of zinc crystals and has interpreted the results in terms of the impurity atmosphere model of Cottrell and Jaswon. This report presents the results of an experimental study of the effect of aluminum additions to zinc on the basal stress-strain curve and the strain rate sensitivity of the flow stress. Etch pit techniques were used to measure and characterize the dislocation density and substructure in the zinc alloy crystals. EXPERIMENTAL PROCEDURE Specimen Preparation. Compression test specimens of four different purities of zinc were prepared from CP grade zinc of 99.999 pct purity obtained from the New Jersey Zinc Co. An analysis of this material furnished by the supplier indicated the following impurities in wt ~ct: Pb = 0.0002; Fe = 0.0002; Cd = 0.00005; other <0.60011. A quantity of material of this grade was further purified by zone refining. Zone refining was carried out under a helium atmosphere by passing a double &apos;One furnace Over a 6-ft-10ng charge at the rate of 2 in. Per hr. * total of ten double zone passes were made before the charge was removed from the furnace. The first one third of each charge was used to grow single crystals. Quantities of two

Jan 1, 1969

By R. V. Smith, E. J. Dewees, R. H. Williams

Before this paper was presented, the terms "f" and "v1/f in flow equations had been called "friction coefficient" and "friction factor," respectively. However, many authors have used the names for the terms interchangeably, with the result that considerable confusion has existed in the literature on flow of fluids. In an effort to establish a clear and concise terminology for these terms, the authors have designated f as "resistance coefficient" and dm as "transmission factor." Transmission factors for the flow strings of gas wells were determined by tests on wells in six fields of Oklahoma, Texas, and Louisiana. Data were collected on 14 gas wells while gas was flowing through 1 1/4, 2, 21/2, and 3-in. tubing and 51/2 and 7-in. casing. The transmission factors developed from these data were found to follow the resistance equation published by Nikuradse1 for turbulent flow in "rough" pipes with an average absolute roughness of 0.000,65 in. This average absolute roughness is believed to be representative generally of the flow strings of gas wells with the exception of those that have been exposed to corrosion or other conditions causing undue roughness. Also, use of an absolute roughness of 0.000,65 in. probably will result in transmission factors that are more representative of gas-well conditions than those in common use today, provided that the transmission factors are calculated by the methods outlined in this report. The authors believe that use of these transmission factors will permit calculation of more accurate subsurface pressures in gas wells than those in use today. Engineers use transmission factors in flow equations to compute subsurface pressures in flowing gas wells from measured wellhead pressures. These subsurface pressures are necessary for determining the productivity of gas wells from "back-pressure" tests. The methods of calculating pressures in flowing gas wells, as outlined by Rawlins and Schellhardt2 in Bureau of Mines Monograph 7, are based on the transmission factors in the well-known Weymouth formula" Natural gas engineers have realized that errors introduced by using transmission factors as given by the Weymouth formula are relatively unimportant in testing low-capacity gas wells; but they also know that such factors are important considerations in testing large-capacity wells. Accordingly, the research described in this report was undertaken to fulfill the need for more accurate means of calculating subsurface pressures in gas wells. This report is part of the Bureau&apos;s study of the flow of natural gas through pipe and commercial pipelines. Several of the conclusions regarding flow in the flow strings of gas wells were influenced by the results of the study of flow in horizontal pipelines. These instances are mentioned in the text of this report. METHODS OF COMPUTING TRANSMISSION FACTORS Methods and procedures for computing transmission factors for turbulent flow in circular pipes from test data taken on gas wells have been derived and explained in detail in a paper by Smith4. As these methods were used to calculate the transmission factors presented in this report, a summary is included. Starting with

Jan 1, 1955

By J. W. Gwinn

The underground haulage system in the lead-silver mine of the Bunker Hill & Sullivan Co., situated at Kellogg, Idaho, is the most extensive in the Cæur d&apos;Alene district, comprising about 35,000 ft. of tunnels, drifts, and cross-cuts where locomotive haulage is in use. The main working adit, known as the Kellogg tunnel, or No. 9 level, is approximately 10,000 ft. in length from the portal to the main working shaft and extends beyond that about 4,500 ft. in each of two directions. On this level all the ore from the Bunker Hill & Sullivan, the Sierra Nevada Consolidated, and the Caledonia Mining Co.—an average of 44,600 tons per month—is hauled to the mills, located a short distance from the portal. Electric haulage by the trolley-type locomotive is used on this level throughout. Below this level, at intervals of 200 ft. vertically, are five other working levels (Nos. 10, 11,12,13, and 14); and the total haulage distance on these, where electric locomotives are used, is approximately 16,000 ft. No. 13 level has but recently been opened up and is not working to capacity; while the main cross-cut on No. 14 has just been started, and has no need of power haulage. Of the four levels equipped with electric haulage, Nos. 11, 12, and 13 have storage-battery locomotives, and No. 10 still retains the trolley type by reason of the small and decreasing tonnage produced. Electrification - Electric power is supplied to the mine by two systems. The first, the 500-volt direct-current trolley, was installed in 1897 when the Kellogg tunnel was started, and was extended as the tunnel advanced, being used for the first trainload of ore on Nov. 17, 1902, since which time it has been in continuous service. The current for the line is transmitted on a No. 00 copper wire as far as the shaft, and on No. 0 wire throughout the remaining length of the Kellogg tunnel; and until the installation of the storage-battery locomotives it was used in practically all the cross-cuts and drifts on each level below No. 9.

Jan 1, 1915

By Noel H. Stearn

To the successful functioning of the geomagnetic method of exploration in engineering and geological practice there are two prime prerequisites : the measurability and the interpretability of significant magnetic anomalies. A magnetic anomaly may be defined as a permanent distortion of the earth&apos;s magnetic field, in order to distinguish it frog the distortions, either cyclic or irregular, which vary with time. So far as known, time fluctations have no directly assignable geologic significance in terms of rock formations, while anomalies may be considered to be directly caused by the difference in the magnetic properties within and between the formations of the substances that make up the earth&apos;s outer shell. As is effectively pointed out by L. B. Slichter,1 the effects which these differences produce on the magnetic field may be extremely minute or extremely great, depending upon the magnetic properties of the formations. Thus the actual anomalies may range from the infinitesimal to a magnitude considerably greater than that of the earth&apos;s field. The geomagnetic method of exploration has shared in the deluge of experimental effort which has lately swept geophysical prospecting to its present important place in engineering and geologic practice. But to date more of this effort has been expended upon the measurability of anomalies than upon their interpretability. The tendency has been to strive for the development of instruments and especially field techniques capable of measuring minute anomalies with a precision far beyond that for which there can be any hope of adequate interpretation other than as interesting phenomena having numerous possible causes. Such efforts, of course, are highly commendable in the field of so-called pure science, which includes the accumulation of undigested detailed observations and admits of interpretation by multiple hypotheses, but in engineering practice the factor of economy must enter. Those instruments and techniques are most desirable which can most rapidly measure the interpretable range of anomalies with the precision necessary

Jan 1, 1932

By Howard A. Meyerhoff

IN western Argentina, in the Province of Mendoza and the Territory of Neuquén, there is a series of solid bitumen deposits which are claimed to be the most extensive in the world. In a linear belt 500 km (311 miles) long, roughly paralleling the axis of the Andes but occupying a variety of positions with respect to the orogenic structures, more than 100 outcrops have been reported. Approximately 70 of these have been prospected, and some mining has been planned or attempted for about half this number. Limited tonnage, high sulphur content, inaccessibility, labor shortages, and disastrous fires have taken a heavy toll among these operations, and in 1947, only 4 deposits were being actively mined, but 8 more were being explored and developed with a view to placing them in production. Inasmuch as these deposits are currently yielding a substantial fraction of Argentina&apos;s limited domestic supply of solid fuels, a brief account of the deposits and of the small industry based upon them will provide a commentary on Argentina&apos;s fuel problem. CHARACTER OF SOLID BITUMENS The solid bitumens of Mendoza and Neuquén are petroleum derivatives, as is indicated by the following ultimate analysis: [CONSTITUENTS PER CENT Hydrogen6.8 Carbon82.4 Nit.rogenI.6 Oxygen2.7 Sulphur2.2 Ash4.3 100.0] In physical appearance they bear a close resemblance to coal and are commonly called carbón. Their specific gravity has an extreme range of 1.10 to 1.777 in 36 samples weighed, but the average is between 1.14 and 1.24. The material is black, lustrous to dull, with blocky to sub-conchoidal fracture. Though brittle, the purest material is softer than anthracite and exhibits slightly more cohesion. This bituminous material is generally known as asfaltita or asphaltite, but definitive chemical studies indicate that the term asphaltite or grahamite can be applied correctly only to the exceptionally pure material of the Auca Mahuida district in Neuquén. Some other name should be used for the chemically variable bitumens found in all other districts, and the designation "asphaltitic pyrobitumen" has been proposed by Carlos A. S. Piscione.1 At the present time these bitumens, are finding favor as solid fuel and as a gas-producing medium. They yield heat values of 8650 to 9750 cal,2 or 14,500 to 16,750 Btu per pound, and in consequence of their excellent heating qualities and the scarcity of imported coal, they are marketed as far away as Buenos Aires at a price of go to 95 pesos, or approximately $22 to 23, per metric ton. In burning, the material swells and decomposes into solid, fluid, and gaseous fractions which burn violently though nonexplosively. Its combustibility has been responsible for disasters and virtually complete destruction at Mina La Esperanza and Mina Santa Marta, and for minor mishaps elsewhere, as at Mina Escondida in August 1947.

Jan 1, 1947