By D. N. Seidrnan

In the present note we present thermal-analysis data for the liquidus curve from 0 to 76 at. pct Se and for the selenium-rich monotectic reaction in the Pb-Se system. We have previously reported that no expey-imental eviderzce was found for a lead-rich monotectic reaction, at -860°C with a monotectic composition of -20.5 at. pct Se, as found by Nozato and Igaki.&apos; Our additional data substantiated this earlier finding and extended the composition range studied. The alloys were prepared from semiconductor -grade lead and selenium purchased from the American Smelting and Refining Co. Both elements were 99.999+ wt pct pure as determined by the supplier. The impurities for lead were Fe (1 ppm) and Cu & ppm) while for selenium the impurities were Cu (< 1 ppm), As (< 1 ppm), Te (1 ppm), and C1 (<1 ppm). The general procedures used for thermal analysis were those specified by the National Bureau of Standards. A Pt/Pt-10 pct Rh thermocouple calibrated against the freezing points of zinc and copper purchased from the National Bureau of Standards and antimony (99.985 pct pure) purchased from A. D. Mackay, New York, was used for all the thermal analysis. The thermocouple electromotive force was measured with a Rubicon Type B potentiometer used in conjunction with a galvanometer with a sensitivity of 0.5 pV (mm) -&apos;. The absolute accuracy of this thermal-analysis system was *0.5"C. One-hundred-gram alloys of the desired composition were sealed in quartz crucibles, with a central thermocouple well, at a pressure of less than 10"1 Torr. The alloys were initially heated well above the liquidus curve and shaken vigorously to insure homogeneity. Cooling curves were then taken by the direct method at cooling rates ranging from -0.5" to 1.5"C (min)-&apos;. The phase diagram from 0 to 76 at. pct Se as determined by direct thermal analysis is shown in Fig. l.* An extrapolation of the selenium-rich portion of the liquidus curve to the monotectic reaction isotherm (678.3"C) gave a value of 76.1 at. pct Se for the monotectic composition. A tabulation of all the thermal-analysis data is given in Table I. As we previously reported no experimental evidence was found Fig. l—The partial Pb-Se phase diagram from 0 to 76 at. pct Se as determined by direct thermal analysis. For the sake of clarity the points for the 49.00 and 49.16 at. pct Se alloys were not drawn on this phase diagram, see Table I. for the lead-rich monotectic reaction found by Nozato and Igaki.&apos; This result was further substantiated by the fact that none of twelve lead-rich alloys, see Table I, examined for this monotectic reaction exhibited a thermal arrest in the temperature range (849" to 863°C) cited by Nozato and Igaki for the lead-rich monotectic reaction. Hence, our results tend to support the earlier qualitative work of ~elabon&apos; and Friedrich and ~eroux" in the 0 to 50 at. pct portion of the phase diagram, though the selenium-rich monotectic composition and reaction isotherm temperature were in agreement with the approximate values (75 at. pct Se and 672" to 680°C) given by Nozato and ~~aki. &apos;

Jan 1, 1967

By E. O. Jones, E. Whitehead

During the heating of cold-worked nickel silver, the tendcncy of the material to crack is well known. The present research deals with this question, and may conveniently be divided into the following sections: Changes in these alloys during heating and cooling, determination of the temperature at which cracking occurs, effect of grain size, quenching cracks, methods of overcoming annealing cracking. The work is far from complete, in particular the influence of impurities on this tendency has not been investigated, but the results so far obtained lead to certain definite conclusions, which are of theoretical and practical importance. Changes in Alloys During Heating and Cooling During the annealing of many metals at a temperature just below that at which recrystallization sets in, there is evidence of some change, the effect of which is to harden and embrittle the material. This effect has been most clearly demonstrated in the cases of aluminum, copper, brass, and nickel silver, and appears to be a common property of cold-worked metals and alloys, or, at any rate, the non-ferrous ones. The effect would obviously offer an explanation for certain types of annealing cracking, but the trouble is so much more common in the nickel silvers than in the other alloys that some special cause should be looked for. There is, however, fairly good reason for believing that similar cracking may occur in some of the brasses; D. Bunting1 suggests that the a brasses toward the saturation limit are subject to a transformation closely allied in nature to that known to occur in the nickel silvers at around 320" C. Although the existence of this critical temperature range was known, it did not necessarily follow that this transformation was responsible for the trouble under investigation, so the first portion of this paper deals with the attempts made to determine whether other critical changes might not occur in these alloys. There were already reasons for the belief that such would prove to be the case, as the mechanical properties of the nickel

Jan 1, 1926

Jan 1, 1967

By A Allen, J. A. Garcia

The large increase in the wages of mine workers makes it imperative that all factors tending to limit production per miner be eliminated, if possible. The trolley and storage-battery locomotive, mining machine, hoisting engine, mining system, etc., have increased the possible output per man. But this output is still limited by the capacity of the hoisting engine and cable and by the size of the mine car. The superiority of skip hoisting in metal mining is shown by its almost universal adoption. By varying the size of skip and the rope speed, any desired tonnage can be secured and, since frequently only one kind of material is handled and breakage is unimportant, the loading of the skips can be easily and cheaply effected from bins into which the cars are dumped. The cars may then be designed to fit the conditions in the mine instead of being a compromise between hoisting and mining conditions, very likely suiting neither. In coal mines, the usual practice has been to hoist the car to the surface, either on platform or self-dumping cages. Of late years the number of skip-hoisting plants in coal mines has been rapidly increasing, but there is more or less inertia to overcome in establishing so radical a change in practice; also the earlier skip operations were not uniformly successful. As a result, it became evident that metal-mining practice would require radical modification before skip hoisting could be successfully used in coal mining. Objections to Skip Hoisting Breakage Except where coal is used for coking, or for other purposes whcre breakage is unimportant, breakage of the coal is vitally important all the way from the face to the railroad car. The average selling price is seriously reduced when the percentage of screenings is increased. Following metal-mining practice exactly, the coal would be dumped into a deep pocket, cut off into a skip load by a measuring hopper or other means, dumped into a deep, narrow skip, and dropped into a bin at the top, all of which would contribute to excessive breakage.

Jan 1, 1922

By J. R. Kyte, L. A. Rapoport, R. J. Stanclift, S. C. Stephan

Experimental studies covering a wide range of core materials and fluid properties have been conducted to determine the mechanism of oil displacement by water in a partially gas-saturated porous medium. In all instances, the presence of a gas phase was found to have a beneficial effect in reducing residual oil saturations. The practical significance of this benefit is discussed, and a simplified procedure is outlined for evaluating the effects of free gas on water flooding by means of short core tests. INTRODUCTION In addition to oil and water, reservoirs subjected to water flooding frequently contain, also, a gas phase. Common engineering procedures account for the presence of this "free gas" only from the viewpoint of volumetric balance, implying that the only role of the gas consists of providing "fill up" space. It is usually visualized that during the initial stages of the water invasion, the oil, moving ahead of the water, displaces part of the gas and that subsequently the remaining portion of the gas phase is totally compressed and dissolved in the advancing oil bank. Thus, consideration of a two-phase, water-oil flooding mechanism supplies an adequate basis for predictions of oil recovery if the pressure build-up caused by the flood is sufficiently great, so as to reduce the free gas saturation to a negligible value in any portion of the reservoir by the time that portion is reached by the advancing flood water. In many in- stances, however, waterflooding operations are carried out when the reservoir pressure is still relatively high SO that the pressure build-up associated with the water flood may not result in complete dissipation of the gas phase. Under such circumstances it is necessary to ascertain whether or not the presence of free gas has an effect on waterflood behavior and, if so, to account for any such effect in the evaluation of field operations. The difficulties encountered in attempting to arrive at a comprehensive picture of the displacement mechanism of oil by water in the presence of free gas stem from the fact that most of the published data on this subject were obtained under conditions that were either not clearly representative of those existing in a reservoir or not sufficiently controlled to permit evaluation of the effects specifically caused by the gas phase. Some of the most precise data found in the literature were obtained in tests using a "static" gas phase created prior to each water flood by circulating oil through partly gas-saturated cores until a "trapped," residual gas saturation was established throughout the system.&apos; Other investigations were conducted under more representative conditions where the gas phase was free to move during the water flood: but in most cases the results of these tests were obscured by auxiliary phenomena which arise from the compressibility and solubility of the gas and preclude quantitative conclusions.2,3,4 Prior to water flooding, a reservoir usually contains oil and gas, distributed in a manner in which both are free to move. Thus, the principal objective of the present studies was to determine the type of displacement mechanism occurring when water invades a porous medium containing oil and a "mobile" gas phase. Further-

Jan 1, 1957

By A. N. Winchell

In connection with law suits between mining companies at Bingham, Utah, a few years ago, the writer made petrographic studies of more than 1400 rock and mineral samples in thin sections, and also careful studies of their field relations. In petrographic studies, even when an area is studied intensively, attention is commonly centered very largely on the unusual features of special interest, so that the relative abundance of rock types (or minerals or textures) can only be determined by a study of map areas outlined largely by field methods, and cannot be based directly on microscopic work. It is very uncommon, and usually impossible, to take samples at regular short intervals along and across formations. It is precisely because such methods were used at Ringham that the work presents a rare opportunity for determining, on a microscopic basis, the relative abundance of rock types and the continuity of gradations between rock types. At the same time, a study was made of the alteration of sediments under the influence of igneous intrusions, with results that are believed to be of interest and importance. • Sandstone-limestone Gradation The sedimentary rocks of the Bingham district are chiefly sandstones, with some beds of limestone, all now lying with their strike nearly east and their dip nearly north at an angle of about 30°, near the surface. The limestone beds are remarkably irregular in thickness in some places, but usually change very slowly in composition along the strike. However, the most interesting results are obtained from a study of a section across the beds at right angles to the strike. In some places, such sections show the usual alternation of pure sandstone with nearly pure limestone, in the simple manner assumed in most geological discussions.

Jan 1, 1924

By H. P. Moore, R. W. Fenn, Harold Margolin, W. R. Hibbard

Deformation lines, also called etch markings or strain markings, are non-effaceable lines developed in individual grains by etching a metal specimen which has been cold worked sufficiently to cause atomic non-conformity or slight orientation differences within the grains. Etching occurs more rapidly at these lines of high chemical reactivity to produce a result similar to that revealing grain boundaries. Wider etching effects forming bands have been found. They are believed to be bands of deformation lines which form areas of measurably different orientation from the crystal matrix. The crystallite rotations causing these bands have been shown by Barrett2 to contribute to deformation textures. Although deformation lines have been observed in many metals, the amount of deformation requireti for their appearance has been established only in general terms. Mathewson and Phillips3 observed the first appearance of deformation lines in cold-rolled alpha brass at about 20 pct reduction in thickness using the standard ammonium hydroxide hydrogen peroxide etchant. Price and Davidson4 noted defor- mation lines in common high brass after 26.5 pct reduction by cold rolling using the same etchant. Johnson6 observed dark thick forklike lines in 99.99 pct pure copper reduced 31.8 pct. Adcock6 observed deformation lines in 80-20 copper-nickel alloy rolled 50 pct. Samans7 found no deformation lines in alpha brass single crystals cold rolled 9.5 pct but they did appear after 25 pct reduction using ammonium hydroxide and hydrogen peroxide etchant. Barrett and Levenson8 observed deformation bands in drawn polycrystalline iron at very small reductions in area and noted that their initial appearance perhaps depends on grain size and other conditions. They reported deformation bands in a single crystal of iron reduced 6 pct by drawing. Brickg noted that deformation lines in 70-30 brass apparently associated with I I I I ) planes appeared after reductions of from 20-50 pct by cold rolling. Brick and Williamson10 noted that in single crystals of 70-30 alpha brass "as in polycrystalline brass, no deformation markings appeared until reductions exceeded 20 pct." Cook and Richards" reported that in Copper cold rolled less than about 50 Pet few strain markings were apparent but for higher reductions many strain markings appeared transverse to the rolled direction. In a review article Brick and Phillips12 noted that previous studies had not shown deformation lines in cold rolled alpha brass below 20 pet reduction and added that 4

Jan 1, 1949

By Walter McKee

WHEN mixed with common cast steel in quantities ranging from 11 to 13 ½ per cent. and properly treated, manganese increases the ductility of the metal and adds greatly to its toughness and resistance to abrasive action, which properties comprise the distinctive characteristics that make manganese steel so valuable for many purposes at the present time. Manganese steel has been manufactured for about 26 years. .It was first made in a small way in England and subsequently produced in the United States in 1892. At present the manganese-steel foundries of this country have an annual capacity of about 60,000 tons and most of the growth has occurred within the past 10 years. In the early days of the industry it was impracticable to make manganese castings weighing over a few thousand pounds, but at present crusher heads, rolling-mill pinions, and similar castings weighing up to 30,000 lb. each are produced, and it does not appear that the limit of weight has been reached by a considerable margin. Manganese steel is similar in analysis to ordinary first-class converter metal except that it is high in carbon and contains from 11 to 13 ½ per cent. of manganese. From one standpoint manganese steel is similar to malleable iron in that the casting as it comes out of the sand is hard and brittle and must be made ductile by a heat-treating process. The heat treatment is an essential part of the process of making manganese-steel castings and must be properly carried out to secure satisfactory results. The necessity for heat treatment limits the thickness of sections which may be made of manganese steel. Originally the annealing depth was comparatively small, but researches carried on during the past few years have resulted in an increase in the thickness of section up to 5 ½ in., which it is possible to treat successfully. Large castings are cored out to a minimum thickness of 5 ½ in., thus not only eliminating some of the internal stresses which are invariably set up in a very thick casting, but also reducing the weight and inertia of the piece, an

Jan 12, 1915

By William Johnson

IT is now recognized that several important types of reactions in metallic systems proceed by the formation of nuclei and the growth of these nuclei. The process, of freezing is a simple example of this, as Tammann pointed out years ago.1Tammann held that the rate of freezing is determined by a rate of nucleation, expressed as the number of nuclei formed per unit volume of unfrozen liquid per second, and a rate of growth of these nuclei, expressed as the linear rate of radial growth in units of length per second. For isothermal freezing the conception is simple; for ordinary freezing, extending over a range of temperature, it is not as simple, for the values of the two constants must change with change in temperature. There is ample evidence that the postulated mechanism is correct even though a quantitative derivation of the rate of isothermal or of ordinary freezing in terms of the two constants has been lacking. In recent years other reactions have been found to proceed in a similar fashion. It has been well established, particularly by Bain,2-8 that the formation of pearlite from the eutectoid decomposition of the solid solu-tion austenite proceeds in such a way, and Polanyi and Schmid, Tammann and Crone, Parnop and Sachs, and others&apos;-1 have shown that the process of recrystallization proceeds in a similar way. Isothermal reaction rates have been determined for eutectoid decom-position by a number of investigators. Bain&apos;s2-8 work on the formation of pearlite from austenite is especially valuable in this respect-the type of isothermal reaction curve obtained, as illustrated in Fig. 13, showed an initial slow rate, accelerating to an intermediate maximum rate which then decelerated to the completion of the reaction; similar curves have been obtained by Wever and his collaborators.&apos; Other eutectoid decompositions show similar behavior: for example, the decomposition of the beta eutectoid in the copper-aluminum system, studied by Smith

Jan 1, 1939

By R. S. Busk, E. G. Bobalek

The relation between gases and metals has been a subject of increasingly active investigation during the past years, principally devoted to the study of metal-hydrogen systems. It has been found that hydrogen is soluble in most molten metals to an appreciable extent and somewhat soluble in most solid metals.l,2 In every known case there is a sudden decrease in solubility at the melting point. Thus a freezing mass of metal containing hydrogen in excess of the solid solubility must in some way expel that excess during the freezing process. This leads to internal blowholes, and such effects as pinhole porosity. Gas trapped in metal that is to be fabricated by a working process such as extrusion or rolling may be the cause of blisters. For some cases, notably in copper and iron alloys, the presence of hydrogen can lead to extreme embrittle-ment of the metal. The aluminum-casting industry has long recognized the importance of hydrogen in its techniques. Excess gas in molten aluminum alloys often leads to the formation of "pinhole porosity" in the solid casting.= To prevent this hydrogen pickup it is necessary to avoid overheating the melt and to protect it from such sources of hydrogen as water. In spite of all precautions, it is sometimes necessary to extract hydrogen from the melt just before pouring by bubbling with a gas such as chlorine or nitrogen. Reccntly it has been found that somewhat similar effects are possible with magnesium alloys, in that the presence of hydrogen can induce or aggravate micro-p~rosity.4-6 This paper is primarily concerned with a presentation of some facts concerning the solubility of hydrogen in magnesium and its alloys, with some discussion of the significance of these facts in a practical sense. In any study of gas-metal systems it is important to bear in mind a clear distinction between adsorption on surfaces and absorption within the lattice.&apos; Considerable attention has been directed toward determining whether hydrogen is truly soluble in any solid metal, or whether the gas extracted from a sample was present at surfaces (external and internal) only.7 Most present day evidence supports the idea of true solution in addition to adsorption. A second important factor when dealing with gas solubility is the dependence of such solubility on external pressure. For diatomic gases such as H², solubility in both liquid and solid metals apparently is proportional to the square root of the pressure, indicating a breakdown to a monatomic gas before diffusion into the lattice.= For true equilibrium values of solubility, therefore, the pressure at the the surface must be constant and, preferably, known. Very little has been published concerning the hydrogen-magnesium system. Winterhager has presented the most

Jan 1, 1947

By Charles Goodale

With notes on other mines of the Marysville district by WALTER McDERMOTT, London, England, and F. L. Sizer, Dos Cabezas, Ariz. (Salt Lake Meeting, August, 1914) THE purpose of this paper is to review the history of the Drumlummon, one of the famous old mines of the West. Mining engineers, when sent to examine new mines in old districts, or to decide whether an old property, under new conditions, will pay to re-open, have had difficulty in learning anything authentic regarding workings which are under water, and historical facts about the working character of the ore, the total production, and the value of the ore with increasing depth. Not many years elapse after the pumps are pulled, before maps, books and records are destroyed, and the value of the publications of the Institute would be increased if they contained the history of many old mines now abandoned. The unsuccessful efforts of the writer quite recently in trying to obtain reliable information about a gold mine which was reported to have produced several million dollars between 1880 and 1888, the workings of which are now partially caved and under water, impressed upon his mind the desirability of having a permanent record of old properties. In this particular case, the owners insisted that under present conditions of improved methods of treatment -particularly by the use of cyanide, which was not an applied process when the mine was operated, the property. could be made to pay a handsome profit on ore left in sight in the old workings, but no assay records could be found to confirm these assurances, and even the records of bullion shipments had been destroyed. If surveys and maps were made as the work progressed, no trace of them could be found, and therefore opening of the ground through a new shaft and drifts therefrom would be attended by some risk while exploring near the old workings. Fatal accidents by flooding under these conditions have occurred, and as an evidence that miners have fears of such dangers, it was urged upon the Mining Committee during a recent session of the Montana Legislature, by a delegation of

Jan 8, 1914

By John V. Beall

Tsumeb has added a chapter to its absorbing history with the beginning of copper smelting operations this month. This development will be followed shortly by another one when lead smelting and refining plants go on the line next year. In our own milieu these events would be common- place enough (although a new lead smelter certainly would be cause for wonder), but in the sparsely settled remote regions of northern South West Africa they are a dramatic industrial expansion. They are also, however, a sound businesslike extension of policies which have marked the tenure of Tsumeb Corp. Ltd. The historical data given in Table I are a drab listing of factual bones without the corporeal splendor which should surround the denouement of the Tsumeb bonanza. When Sir Francis Galton traversed the country, his was an expedition which was in keeping with the then blooming era of heroic explorations. The Otavi highlands in the interior were unexplored and the reception of the natives uncertain. While the exploratory work was in progress during the turn of the century the Hottentots and Hereros were successively in open bloody rebellion. The suppression of these uprisings, particularly the Hereros, by German soldiers so decimated the tribes that a labor shortage ensued for many years, hampering the development of the colony. To these troubles may be added difficulties In obtaining mining supplies. However, there should have been no shortage of meat from wild game judging by conditions prevailing even today.

Jan 12, 1962

By E. F. Ketterer, D. B. Collyer, A. B. Wilder

AISI constructional alloy steels are a series of steels in which a numbering system signifies the chemical composition limits. SAE (Society of Automotive Engineers) and AISI (American Iron and Steel Institute) use basically the same numbering system. The steels contain, in part, alloy additions of chromium, molybdenum, nickel, and vanadium. They are used widely in the automotive industry but have not been adopted for high temperature service. The purpose of this investigation was to study changes in microstructure observed in typical AISI constructional alloy steels in the welded and un-welded conditions after exposure for 34,000 hr at 900" and 1050" and, in several instances, 1200°F. The tensile and creep rupture properties after exposure for 10,000 hr were also evaluated. The investigation is a continuation of the work previously discussed. Little was known concerning the existence of graphite in medium or low carbon steels before 1943. It is important to note that continued exposure at elevated temperature is required in order to develop graphite in steels. Interest in the presence of graphite in steel, and also in changes in the properties of steels after long service at elevated temperatures, developed after 1943 when a failure of a welded joint of high temperature piping was associated with the graphitization of a relatively low carbon content steel with 0.50 pct Mo,8,0 Numerous investigations have beeen made in recent years studying the relationship of this type of failure to changes in properties. Attempts have been made to evaluate the performance of a number of steels, particularly in the heat-affected zone of welds. It was the unfortunate failure of a weld-heated zone in high temperature piping in the steam-power industry which focused attention upon possible failures, and upon the need for improved steels for high temperature piping service. Investigation by the National Tube Div., U. S. Steel Corp., Lorain Works, has included a wide variety of steels in an attempt to learn the effects of numerous factors and elements upon the long time performance of steels, although many of the compositions studied will never be used at elevated temperatures.1,4-7 Included were the well established AISI steel series, which offered opportunity to test moderately high carbon content steels as well as observe the effect of nickel, chromium, molybdenum, etc., upon the properties of these well known steels. The properties of the AISI steels were also studied for comparison with the previously reported properties of the Cr-Mo steels, now used by the steam-power industry.5,7 Materials and Testing Procedure The AISI alloy steels in Table I were exposed for 10,000 and 34,000 hr at 900°, 1050°, and 1200°F.

Jan 1, 1958

By William Waters Van Ness

The Pierrefitte mines, situated in the South of France, in the district of the Hautes-Pyrenees, owe their name to the fact that the first mining operations of any extent, and of comparatively reccnt date, were carried out in the neighborhood of the village of Pierrefitte, which is a branch terminus of the Midi railway. The Pierrefitte mines, however, embrace a wide extent of country and several different concessions, on most of which comparatively little exploration-work has been done. The portion of the property presently to be described is a zone running roughly E—W., over a distance of about 5 miles from the valley of Cauterets to the valley of Estaing, the ridge dividing these valleys being a spur of the main chain of the Pyrenees, and running more or less at right angles to it. According to local tradition, which various indications tend to confirm, these mines are of ancient date, the first workings being attributed to the Romans, who are supposcd to have sought not only the lead but also the silver which is contained in the ore. Old slags have been found in the neighborhood which might well have been produced from the cupellation of lead-ores. These old workings, while of considerable extent at times, do not seem to have extended beyond a depth of 100 ft., even this depth being somewhat exceptional. The old notarial records of the district show that mines were known to exist, and that they were even worked, in the sixteenth century, but since the mines were abandoned (by the Romans or others) considerably prior to this period, very little

Jan 1, 1909

By R. G. Davies

Above 500°C, where dislocation climb is rate controlling, it is observed that the activation energy for creep is independent of the apblied stress, although it varies from 62 kcal per mol at 15 pct A1 to 73 kcals per mol at 20 pctA1 due to the change in short-range ovdw with composition. Below 500°C, when the nonconservative motion of jogs upon dislocations is thought to be rate controlling, the activation energy is stress dependent. A sudden increase in the creep rate, for which no explanation is availab2e, occurs at the highest stress at all temperatures. CREEP has been the subject of numerous research publications during the past decade with most of the attention focused upon high temperature steady state creep, i.e., above 0.5 TM, where TM is the absolute melting temperature, as it is the most amenable to theory. Many of the proposed theories involve the climb of dislocations out of their slip plane, which allows them to circumvent obstacles or to annihilate dislocations of opposite sign on other slip planes.&apos; For pure metals it is observed that the activation energy for this creep is equal to the activation energy for self diffusion.&apos; The position is much more complicated in alloys as there are many possible microcreep mehanisms, as well as dislocation climb, which could be rate controlling. There has been little systematic investi- gation of alloys, but Weertman (lead and indium base alloys)3 and Lawley, Coll, and Cahn (Fe-A1 alloys)4 suggest a microcreep process as the controlling factor. A Cottrell-Jaswon atmosphere mechanism is proposed for the lead and indium alloys, and a mechanism involving crystallographic order for the Fe-A1 alloys. Lawley et al. showed that the formation of a super-lattice, either of the FeAl or Fe3A1 type. decreased the rate and increased the activation energy for creep. From the measurements of lattice parameters,= resistivity,&apos; magnetic properties,7&apos;8 internal friction: and dilatometry10 the ordered region is thought to commence at -19 at. pct Al. However, a recent investigation by the author indicates a value

Jan 1, 1963

By Harmon D. Nine

DISCONTINUITIES in the strain vs cycles to failure (S-N) fatigue curves have been reported for polycrystalline materials by Porter and Levy for copper,&apos; by Benham and Ford for mild steel,&apos; and by Williams and Stevens for 18/5 stainless steel.3 However, the considerable scatter of the points for polycrystalline materials have made a statistical analysis of the data necessary to confirm the discontinuities. By using oriented single crystals of high-purity material and low grown-in dislocation content, the reproducibility has been improved to a degree which makes statistical analysis unnecessary and clearly shows discontinuities in the S-N curves. A recent publication4 reports an abrupt change of slope in the S-N curve for ( 100) axially oriented copper single crystals fatigued in torsion. The reported discontinuities in the S-N curve, along with a different mode of failure in the two branches of the curve, have been interpreted as being due to two different amplitude-dependent mechanisms. Further work on copper single crystals of (111) axial orientation has now been completed which supports the existence of an amplitude-dependent change in the mechanism of fatigue. In the present study torsional-fatigue experiments were performed at room temperature in air on (111) axially oriented single crystals. The crystals were grown and prepared as reported in Ref. 4. Two different methods of growing the crystals also discussed in Ref. 4 produced crystals of two different perfections: Type I with dislocation density of >l06 per sq cm and Type I1 with dislocation density of <l05 per sq cm. In accordance with the accepted hypothesis that crystal flaws are primarily responsible for the scatter of fatigue lifetimes, particularly at low amplitudes, the values for the three lowest amplitudes for Type I crystal are believed to be uncertain. They are marked in braces in Fig. 1. On the other hand, at amplitudes above a surface shear strain (SSS) of *0.003, the data for both types of crystals are in agreement. Most remarkably the S-N curve for torsional fatigue of (111)-oriented single crystals is composed of three segments separated by rather large discontinuities, Fig. 1. Metallographic and X-ray measurements indicate that the lower branch corresponds to the low-amplitude (F) region of the (100) copper single-crystal results as discussed in Ref. 4, and the two upper branches correspond to the high-amplitude (H) region. The lower discontinuity in the (111) S-N curve and metallographic evidence give further support to the hypothesis that different mechanisms of failure operate for high and low strain amplitudes. Reference to the resolved shear stress diagram, Fig. 2, shows that the highest stressed systems in

Jan 1, 1965

By D. H. Turner, F. A. Crossley

The titanium-rich corner of the system Ti-Al-Si has been studied to determine the phase relationships in the temperature interval 600° to 1200°C. Metallographic examination of long time isothermally annealed specimens was the means of investigation. PART of a program on phase relations and transformation processes of titanium alloy systems included the study of the titanium-rich corner of the Ti-Al-Si system. The investigation covered ternary compositions in the range 2 to 8 pet A1 and 0.1 to 2 pet Si and binary compositions in the range 0.2 to 2 pet Si. Temperatures were in the range of 600" to 1200°C. Alloys containing 6 pet A1-0.1 to 0.5 pet Si were investigated down to 400°C. Partial vertical sections are presented for 2, 4, 6, and 8 pet Al. The Ti-Si system has been reported by Hansen et al.&apos; It is characterized by a eutectoid decomposition, ß = ± a + Ti3Si3, at 860°C. The maximum solubility of silicon in a is reported to be about 0.5 pet at the eutectoid temperature. The solubility of silicon in 0 increases from 0.9 pet at the eutectoid temperature to approximately 3 pet at the eutectic temperature, 1330°C. Several investigations in the composition range of interest have been reported for the Ti-A1 system."&apos; These investigations are in agreement on the phase fields, but differ to small extents on boundary positions. However, very recent, and as yet unpublished, findings" " indicate that there are perhaps two phases which occur at lower aluminum contents than the ? (TiA1) phase, and that the solubility of aluminum in a titanium is less than 6 pet. In the present investigation phase relations found are in agreement with the published literature exemplified by the work of Bumps et al.3 Therefore, it is probable that the partial system reported herein is metastable and does not represent true equilibrium. Experimental Procedure High purity Bureau of Mines titanium sponge of 103 Bhn hardness, granulated aluminum shot of 99.7 pet purity, and silicon powder of 99.8 pet purity were used in making the alloys. For the work in the range from 600" to 1200°C, 100 g ingots were prepared by arc melting. Melting losses were negligible and spot checks by chemical analysis showed good agreement between nominal and analyzed results. Nominal compositions are used throughout this paper. Ingots were forged to 3/8 in. rounds and cut into specimens for heat treatment. Isothermal anneals in the range from 600" to 900°C were preceded by solution treatment at 1000°C for 1 hr, followed by furnace cooling to the annealing temperature. Samples were sealed in evacuated Vycor bulbs for heat treatments up to 1000°C. Higher temperature anneals were done with the samples sealed in quartz bulbs under a partial pressure of argon.

Jan 1, 1959

By Charles W. Goodale

The principles and theory on which the U. S. mining law of 1872 was based are well understood, and have been discussed at great length by many writers. The papers by Dr. R. W. Raymond1 in the Transactions of the American Institute of Mining Engineers have covered the subject very fully, with explanations of practical results in many adjudicated cases. It is believed that the following instance of the application of the law in recent years will have some weight in a discussion of proposed changes in our mining laws. The litigation between the St. Louis Mining & Milling Co., and the Montana Mining Co., Ltd., a British corporation, over portions of the Drumlummon lode covered more than 20 years, and resulted in a judgment for damages in favor of the St. Louis Co. of such an amount that the Montana Co. declined to pay the judgment, and therefore lost the entire property. The Drumlummon lode claim in the Marysville district, Mont., was located in 1876 by Thomas Cruse. When he staked out his claim, he assumed that the discovery on the Drumlummon vein, and another showing of mineral about, 200 ft. distant, were on the same vein, and the center line of the claim was given a course of N. 579" E. Development of the Drumlummon vein soon showed that its strike was about N. 15" E., and that the other outcrop was on the North Star lode; so it was inevitable that the Drumlummon vein would cross one or both side lines of the location, and the Montana Co. found it advisable to acquire adjoining claims on both sides of the Drumlummon, in order to avoid possible litigation over apex rights. They bought the Marble Heart, but would not purchase the Hopeful (see Pigs. 1 and 2), at the terms proposed for the reason that exploration in the Cruse level had shown the vein to be barren in that region. The owners of the Hopeful were sinking an incline from that claim in 1889, and the Montana Co. enjoined them, contending

Jan 1, 1915

(SECRETARY&apos;S NOTE.) The following discussion of the papers of Van Hise, Emmons, Lindgren and Weed, read at the Washington meeting, February, 1900, and printed on pp. 282 to 498 of this volume, comprises communications to the Secretary, received at various times before the Richmond meeting, February, 1901, and, for the most part, presented at that meeting. These communications are introduced at this point in the present volume, in order that they may precede the papers of Vogt, hemp, Lindgren, Rickard, etc., presented at Richmond, and therefore not forming part of the material considered in them. Since many of the contributors have mentioned in one communication several of the papers referred to, no attempt is here made to divide their remarks and distribute the fragments under separate headings. In each contribution, however, the several topics are indicated by subtitles. R. BECK,* Freiberg, Saxony : Prof. Veal Hise&apos;s Paper.-The paper of Prof. Van use (p. 282) represents a great step of scientific progress, in that the circulation of underground waters has never before been presented with such clearness, ill the light of modern chemical and physical knowledge. The theories of the formation of ore-deposits which follow the author&apos;s general survey of the currents and solvent power of atmospheric waters in the earth&apos;s crust do not, indeed, seem to be novel, being essentially an amplification of Le Conte&apos;s views; but the proofs adduced in their support are in many particulars so original that no one can read without profit this portion of the paper. Entirely new (though largely in agreement with the papers of Emmons and Weed, presented at the same meeting of the Institute) are the sections dealing with the formation of the rich sulphides of the precious metals, and especially the regeneration of normal sulphides, such as galena, etc., in vein-zones immediately beneath the ground-water level. Nevertheless, it appears to me that Prof. Van Hise, in the course of his most instructive exposition of unquestionable, yet still locally limited, phenomena, has been too much biased in favor of the " descensionists." This is indicated by the small importance which he attaches to the intimate genetic relation between epigenetic deposits and the plutonic hearths of the earth&apos;s interior.

Jan 1, 1902

By R. F. Krueger, L. C. Vogel

A design is presented for an electrical analog computer which can solve non-steady state heat transfer problems in an extensive radial forrnation containing a moving cylindrical source. The computer is used to simulate a .simplified thermal oil recovery process in which heat transfer from a moving, constant temperature source takes place radially by conduction only. Temperature distribution curves are .shown for several different assumed modes of travel for the heat source. The data are used to estimate the residual fuel requirements necessary to maintain a self-propagating isotherma1 front for the particular system being studied. Although the computer is designed to represent an unique system. conversion factors can he adjusted to show the effects of changing the assumed values of system constants, such as thermal conductivity of the formation and temperature of the source isotherm. Examples are given to illustrate the relative influence the assumed values of these variab1es will have upon the quantity of fuel required to maintain the source. The maximum effect of heat transfer by the flowing air stream is estimated mathematically, and full requirements for this system are shown to he markedly reduced. Inasmuch as the examples discussrd refer to a simplified process, the results are not directly applicable to a practical field operation. It is believed, however, that the data il1ustr-ate some general trends which are important in thermal recovery processes. Data from laboratory and field experimentation can he used to modify the computer to take into account the influence of heat transfer by various mechanisms, for example, by injected air and by fluids ahead of the hot zone. With .such refinements it would be possible to estimate more accurately the limiting values for the rate of travel of the high temperature front and for the required air- injection rates. Use of this computer should aid in evaluating the economic feasibility of oil recovery by various thermal processes. It is hoped this paper will stimulate further work by others to help accomplish this objective. As the costs of exploration for and development of new oil fields rise. increasing the recovery of oil from established fields becomes more and more important. In fields containing low gravity crude oil, ultimate recoveries by primary means are sometimes less than 10 per cent and often total only 10 to 20 per cent of the oil in place. Conventional secondary recovery methods are not always effective in increasing this total. Methods which have been proposed for increasing the recovery of viscous oils include thermal processes for increasing the mobility of the oil. One method is to provide a moving heat source generated within the formation to heat the oil and a flowing gaseous medium (for example, air) to sweep the oil to the producing wells. The possibility of such a process has intrigued engineers for many years.&apos;. &apos;." but little or no information has been available in the literature relative to the technical or economic feasibility of this method. Recently, however, interest has been revived by publication of laboratory and field test results indicating the feasibility of maintaining

Jan 1, 1956