By Arthur G. Levy, Henry M. Howe

$1. Introduction.—Any given piece of metal is made up of a very great number of grains, usually microscopic, each of which is a perfect crystal save only in outward form, with cleavage planes of low cohesion, geometrically arranged quite as in fie familiar non-metallic crystals. The plastic deformation of such a mass occurs chiefly through the slipping of the crystalline blocks of which each grain is composed along these cleavage planes, causing steps called slip bands to form on a previously polished surface. In this slip, the metal immediately adjoining each of the cleavage planes along which the slip takes place is thought to pass extremely rapidly through a very mobile state into the amorphous state, in which it is harder than the remaining still crystalline metal between the amorphous layers thus formed along the slip planes. Whether the slip planes below the surface in ferrite can be detected by cutting, polishing, and etching sections is in dispute; but if this detection is possible at all, it is usually made impossible by heating the metal even gently. In short, the change along the slip planes does not persist through heating, and it is thought not to persist through time even at the room temperature, nearly all the amorphous metal recrystallizing. The network in Fig. 22 and the parallel N.-70-E. lines in Fig. 21 are slip bands in copper. When plastically deformed metal is heated, certain parts of certain grains may twin, that is, their component crystalline units may rotate into a position, or more exactly into an orientation, symmetrical with the initial orientation and hence with that of the remainder of that grain. As seen in a microsection of a metal the twinned areas usually have parallel sides. The existence of twinning is recognized in metallic sections either by the presence of such parallel-sided areas differing in brightness from the adjoining metal, especially when seen under oblique light after etching, or more surely by the zigzagging of the slip bands which form when twinned metal is itself deformed again. Hence the usual procedure in developing twins is to deform plastically so as to cause the twinning tendency; to heat so as to allow the tendency to assert

Jan 1, 1915

By Walter Herd

FOR the past eight years No. 2 mine of the Cumberland Railway & Coal Co., Springhill, Nova Scotia-a subsidiary of the Dominion Coal Co., Ltd.-has had an unenviable reputation for bumps. As the workings extended in certain directions under a greater cover, these bumps increased in severity and it became apparent that some change in the system of extraction was necessary if the mine was to continue to operate. In September, 1924, following several fatalities resulting from bumps, the Mines Department of Nova Scotia requested from the U. S.. Bureau of Mines the services of George S. Rice, Chief Mining Engineer of the Bureau, to report on the conditions then prevalent in No. 2 mine, Springhill. This request was promptly and courteously granted. Mr. Rice made a full investigation and a comprehensive and helpful report, which is embodied in the 1924 Annual Report of the Department of Public Works and Mines, Nova Scotia. Prior to 1925, the room and pillar method wasp employed and in January of that year (there being a cessation of work from March to August due to labor troubles) longwall retreating on the west side, on a limited scale, and in a small section on the east side of the mine was started. The major portion of the east side was not operated on this system till August, 1926, as there was developed a considerable area ready for pillar extraction between an arbitrary boundary and a point up to which bumps of any consequence had not been experienced. In the interval development work for longwall retreating below the 5900-ft. level was vigorously pushed. This longwall retreating system was suggested by Mr. Rice as a possible remedy and was heartily endorsed by the company officials. This paper describes the conditions and happenings subsequent to Mr. Rice's report and more especially the results with the longwall retreating system of mining under the peculiar circumstances pertaining to mining No. 2 Seam, Springhill, at depth, and records the conclusions which experience with several severe bumps under this mode of extraction would suggest. Except where necessary to make the paper intelligible as an entity any duplication of Mr. Rice's report will be avoided.

Jan 1, 1929

By W. L. Dennen, W. W. Wirth

Research looking toward the reduction of the cost of roof support by substitution of longer-life materials for wooden timber is fully justified by the fact that roof support is an important element of all production costs. Permanent or semipermanent roof support will reduce the expense of timber-maintenance crews during steady operations, but even more markedly during idle periods. The management, therefore, is faced with the important problem of timber renewals, which in times of regular operation are frequently obscured by more urgent problems of production. Increased use of timber in the Anthracite Region of Pennsylvania is caused mainly by increased percentage of coal obtained from robbing areas, which requires more timber for safety than development work, and maintenance of long haulageways through crushed ground despite the fact that less coal is transported over them. The timber reserve in the immediate vicinity of the mines has been depleted to such an extent that it is necessary to secure 70 per cent of the timber requirements from distant sources. Originally, mine timbering in this region was done by largely utilizing round props or legs with round collars. The whole cross section of the tree from which timber was cut was utilized by forming the joints between the legs and the collars with saw and adze, using plank or round saplings for lagging behind the legs and over the collars to prevent material falling between them. The Mine Inspectors' report of 1898 records an important digression from the use of round timber, when two tunnels at the Babylon colliery, near Pittston, Pa., were timbered with 12 by 12-in. square timber sets with mud sills, through quicksand for distances of 425 and 160 ft., respectively. The timbers were lagged with 3-in. plank to control sand. An early step toward the permanent type of roof support was the installation of "brick pillars or perfect arched brick rooms" instead of

Jan 1, 1940

By P. Payson

INTERGRANULAR corrosion in corrosion-resistant chromium-nickel steels has been widely discussed in the last few years. So far as the author knows, nothing has been published which definitely shows that this tendency can be eliminated, although suggestions have been made that a remedy is possible if certain specifications are satisfied. Strauss, Schottky and Hinueber1 suggested an increase in chromium content to an extent that would prevent the impoverishment of chromium on carbide precipitation sufficient to cause impaired corrosion resistance in the matrix. Pilling2 suggested an increase in nickel, so that the stability of the austenite matrix would be increased. Aborn and Bain,3 say that "intergranular attack-may be eliminated by preventing carbide precipitation (e. g., by lowering the carbon content or somehow raising its solubility) or by precipitating it permanently under conditions which will not remove chromium from solid solution so drastically at any points." In a later paper Aborn and Bain4 state that many different metallic elements, tungsten, vanadium, copper, aluminum, molybdenum, titanium and zirconium, have been added in small per-centages to increase the stability of these alloys, but that it has been reported that according to the copper sulfate test these added elements act only to retard the intergranular corrosion, and that increased nickel and chromium contents have similar effects. Newell5 showed that the lower the quenching temperature before reheating, the less severe was the intergranular attack.

Jan 1, 1932

By W. van der Knapp

A theoretical and experimental ana1ysis is given of the change in volume of a porous medium due to changes in external and internal pressures. The result enable one to deduce directly the effect of large increlents in stresses. It is shown that the three-dimensional representation of the volume of a nonlinear porous system is a cylindrical rules surface, the generating lines of Which have a slope according to the solid rock compressibility. Analytical expression for such a ,surface is very simple. It follows that the bulk and pore compressihilities depend only on the difference between pore fluid and external hydrostatic pressure, i.e., the effective rock frame pressure. From measurements on a number of sandstones as well as limestones it can be conduded that for practical values of this effective frame pressure the pore compressibility falls in the range between the compressibility of water and that of undersaturated crude oil. In general, pore compressibility is found to be higher the lower the porosity. For a particular limestone reservoir pore compressibility and porosity could he related by means of a simple empirical formula. Results from the described study find a direct applicxtion in material balance calculations and in prob1ems of liquid flow through porous media. Since the elastic constants of the rock bulk material enter into equatiorls for velocity of acoustic waves, the results are also of importance for calculating rates of wave propagation in these media. It is shown for sandstones with 1.5 to -10 prr cent porosity that laboratory measured porosities may differ from those lender reservoir conditions by about I per cent of their value. The difference for low porosity limestotnes can be of the order of 10 per cent. The subsidence caused by elastic deformation of reservoir rock is shown to he very small. General formulas relating pore and bulk volume to external and internal pressure can be derived, as has been shown by Biot1, Gassmann2 and Geertsma.2 Their theories describe the differential change in volume caused by a variation in pore fluid tension and external hydrostatic tension. It has been known for a long timei that the stress-strain relations of a packing of spheres are essentially noninear. Our experiments show that for almost all reservoir rocks which arc elastically deformable the relation between volume and loading is also a nonlinear one, resembling that of a packing of spheres very closely. The behavior of these media is often described by using the linear stress-strain relations for small incremental stresses and strains in the vicinity of a pre-stressed condition." The present study differs from these considerations in that it enables one to deduce the effect of large increments in the stresses directly. In analogy to the stress tensor for a homogeneous body the stress tensor for a porous body can be written in the conventional way: where the tensor components, o, and t, represent the total forces acting on the faces of a unit cube of porous material. This tensor can be split into two parts. a hydrostatic and a deviatoric part, as follows2,3,1 where the component of the hydrostatic stress system, a. equals The hydrostatic stress causes a change in volume whereas the deviatoric stress system gives rise to a change in shape only. One of the difficulties in describing changes of volume occurring in reservoir rocks is that the relations connecting these volume changes with external and internal stresses are essentially non-linear. A complete description requires the bulk volume, V,,, as well as the pore volume,V,,. to be known as a function of both the changes in pore fluid tension (v) and the hydrostatic tension on the outer boundary.

By W. A. Klikoff, I. Fatt

The concept of fractional wet wattability is examined. Fractional water wettability of a reservoir rock is defined as the fraction of the internal surface urea that is in contact with water. Capillary pressure and relalive permeability of unconsolidated sand are shown to be functions of fractional wettability. INTRODUCTION The petroleum industry has long recognized that wettability of reservoir rock has an important effect on multiphase flow of oil, water and gas through reservoirs. As early as 1928 the American Petroleum Institute sponsored a study of wettability as part of API Project 27 at the U. of Michigan.' Despite 30 years of research, there is still little exact knowledge of the wettability of reservoir rocks. There are two parts to the wettability problem. After agreeing to a uniform nomenclature in regard to wettability,' the first question to be answered is, "What is the in situ wettability of a given reservoir rock?" If this can he answered the next question is, "What part does wettability play in determining the characteristics of multiphase fluid flow through the rock?" This paper represents an oblique attack on the problem of wettability. No attempt is made here to answer the basic question of wettability in situ. instead the consequences of the concept of fractional wettability are examined. Multiphase flow in sandpacks is shown to he highly influenced by fractional wettability. Jennings' has given 3 definition of wettability and the other terms used in discussing wettability. These terms must be applied to the physical situation existing In reservoir rock. A survey of the pertinent literature from 1928 to 1956 indicates that the concept of a contact angle was applied to reservoir rock in the same way it would be applied to a flat, homogeneous surface. Attempts were made to state quantitatively the wettability of a reservoir rock in terms of a contact angle which was presumably constant at all points on the very rough and heterogeneous interior surface of a porous rock. Calhoun, et al,3-6 prepared synthetic consolidated and un-consolidated porous media in which they claimed there was a known uniform contact angle. They then showed the effects on the capillary pressure and relative permeability characteristics of varying this angle. The API Project 47 at the U. of Texas' and others' have made extensive studies of an indirect approach to the contact angle through the use of heat of wetting data. Even if successful. however, this approach also states the wettability of porous rock in terms of a contact angle which is uniform over the entirc surface. If the angle varies from one part to another on the internal surface, there is no way of determining from the measurements the area distribution of contact angles. In 1956 Brown and Fatt5 suggested that the concept of a contact angle, as applied to reservoir rock, be abandoned. This suggestion was made because it is known that the internal surface of most reservoir rocks is composed of many different minerals, cach with a different surface chemistry and a different capacity to adsorh surface active materials from reservoir fluids. Furthermore, the operation of a contact angle in determining the form of a fluid-fluid interface is difficult to picture in the very complex geometry of a pore. Brown and Fatt proposed that the wettability of reservoir rock be stated in terms of the fractional internal surface area that is in contact with water or oil. All surfaces on which there is water are called water-wet; surfaces on which there is oil are called oil-wet. The fractional water wettability is then stated as a number which represents the fraction of the internal surface that is in contact with water. A symmetrical statement can be made for the fractional oil wettability. The concept of a fractional wettability as previously stated has in its favor the recognition of the heterogeneous mineral composition of most reservoir rocks. Another point in its favor is that fractional wettability can be measured quantitatively with relative ease. Hol-brook and Bernard10 se a simple dye adsorption test to obtain fractional wettability of reservoir rocks. Amott11 uses a combination of imbibition and displacement to arrive at a wettability index of reservoir rocks which seems related to fractional wettability in the range 0.25 to 0.75 fractional water wettability. Jennings" has shown the changes in relative permeability that take place when a porous material is changed from unity to zero fractional water wettability. He also shows that reservoir rocks in their natural state, but at room temperature and atmospheric pressure, have relative permeability characteristics which would indi-

By W. L. Dennen, W. W. Wirth

Research looking toward the reduction of the cost of roof support by substitution of longer-life materials for wooden timber is fully justified by the fact that roof support is an important element of all production costs. Permanent or semipermanent roof support will reduce the expense of timber-maintenance crews during steady operations, but even more markedly during idle periods. The management, therefore, is faced with the important problem of timber renewals, which in times of regular operation are frequently obscured by more urgent problems of production. Increased use of timber in the Anthracite Region of Pennsylvania is caused mainly by increased percentage of coal obtained from robbing areas, which requires more timber for safety than development work, and maintenance of long haulageways through crushed ground despite the fact that less coal is transported over them. The timber reserve in the immediate vicinity of the mines has been depleted to such an extent that it is necessary to secure 70 per cent of the timber requirements from distant sources. Originally, mine timbering in this region was done by largely utilizing round props or legs with round collars. The whole cross section of the tree from which timber was cut was utilized by forming the joints between the legs and the collars with saw and adze, using plank or round saplings for lagging behind the legs and over the collars to prevent material falling between them. The Mine Inspectors' report of 1898 records an important digression from the use of round timber, when two tunnels at the Babylon colliery, near Pittston, Pa., were timbered with 12 by 12-in. square timber sets with mud sills, through quicksand for distances of 425 and 160 ft., respectively. The timbers were lagged with 3-in. plank to control sand. An early step toward the permanent type of roof support was the installation of "brick pillars or perfect arched brick rooms" instead of

Jan 1, 1940

By Eugene A. Mizikar

A mathetnatical model of heal transfer in continuously cast steel slabs is described. The model, consisting of a unidimensional transient conduction equation and boundary condition equations, has been pvogrammed for computer solution. Temperatuve and solidification profiles calculated for a 6-in. slab, being cast under several conditions of secondary cooling, are presented and compared. Calculated solidification profiles are in agreement with reported expevinle~ztal values. For the mold zone, the predicted slab shell thickness can be described by: Resuilts of the study indicate that multibank spray cooling followed by radiant cooling should be employed when solidifying thick slabs with minimum surface temperature of 1600°F. Under these conditions, a 6-in. slab can be expected to solidify in about 8.3 min. Computer results also indicate that radiant cooling can replace spray cooling during solidification of the final 30 pct of slab with little increase in overall solidification time. CONTINUOUS casting has come to the forefront of the steel industry in recent years because of economic advantages resulting from increased yields and elimination of several processing steps. Considerable work, however, remains to be done regarding modifications to the process and operating procedures. Both a lack of operating plants in this country and the experimental difficulties associated with direct measurements on moving castings have made determination of solidification rates and temperature distributions difficult. An alternate approach is to mathematically simulate heat transfer in a continuously cast section, and then calculate the temperature distributions as a function of the controllable variables of the process. Simulation of heat transfer during solidification requires that a nonlinear mathematical problem be solved. As pointed out by Ruddle,' there are two mathematical approaches to the problem- the analytical approach and the numerical approach. While the analytical approach is certainly the more elegant of the two, it does require a number of inexact assumptions because of the complexity of the problem. For example, noteworthy analytical treatments of heat transfer in continuous casting have been developed by Savage Hills,3 and pehlke4 only by making one or more simplifying assumptions such as invariant thermophysical properties, constant heat-transfer coefficients in the mold, and linear temperature profiles in the shell. Simplifying assumptions such as these can introduce considerable uncertainty in the validity of results calculated with analytical solutions. Numerical solutions, which are considerably more versatile, appear to be better suited for solving solidification problems. Complex variations in the boundary conditions and variable thermophysical properties can be handled readily with this technique. Whereas numerical computations can be long and tedious when done by hand, results can now be obtained quite rapidly with the use of either the digital or analog computer. Several numerical models of heat transfer in continuous casting have been published. In 1963, Adenis, Coats, and Ragones published a numerical model used to calculate temperature distributions in direct-chill-cast magnesium billets. More recently, Donaldson and Hess 6 presented results obtained with a numerical computer model of heat transfer in continuously cast steel billets. In the present study, a model of unidimensional heat transfer in continuously cast slabs is presented. The method of solution on a digital computer is also included. Calculated temperature distributions and solidification profiles for various schemes of secondary cooling along with attempts to verify the model are also discussed. MATHEMATICAL MODEL The schematic representation of the slab continuous casting process in Fig. 1 illustrates that the slab passes through three distinct zones of cooling. Accordingly, the mathematical model consists of three parts: 1) solidification in the mold; 2) solidification in the spray cooling zone ; 3) solidification in the radiant cooling zone. Heat-Transfer Equations. The model was developed bymaking a heat balance on a horizontal slice of slab over the time period required for the slice to proceed from the liquid metal meniscus in the mold to the cutoff station. As shown in Fig. 2, the imaginary slice extends from the center line to the surface of the slab. As the slice moves downward, heat is conducted from the center line to the surface of the slab at a rate governed by the surface boundary condition and thermophysical properties of the metal in the slice. The following partial differential equation describes the conduction of heat in a medium moving at velocity U in direction Z:

Jan 1, 1968

By C. S. Barrett

IT has been observed that deformation in iron takes place by slip on {110} + {112} + {123} planes1,2 but in silicon ferrite with low deforma-tion temperatures or high silicon contents (exceeding 4 per cent) the authors have found that slip is confined wholly to {110} planes, at least with small amounts of deformation. The purpose of the present inves-tigation was to determine the effect of this alteration of slip mechanism on preferred orientations in cold-rolled and recrystallized strips. Inci-dental observations on the effect of the recrystallization temperature were also made. The numerous determinations of the texture of cold-rolled iron and steel have been in satisfactory agreement as to the principal features of the texture. (with the exception of a few conclusions that apparently have been based on insufficient data). The texture is chiefly one in which [110] directions of the grains lie along tile direction of rolling, with a deviation of a few degrees, and in which the (100) planes lie in the plane of the rolled sheet, with a deviation from this position chiefly about the rolling direc-tion as all axis 3-9. This deviation about the rolling direction as an axis has been measured by different observers and lies between about 45° and 50° or 60° for iron5,6,9 and is usually in the neighborhood of 50° for mild steel6,7,8. The range of this deviation is a function of the percentage of total reduction 8, 10. Post' reported that it decreases with increasing percentage reduction, but apparently he .studied only the surface material, which Gensamer and Mehl7 found to be somewhat differently oriented from the material in the inside of the sheet. McLachlan and Davey10 found that the deviation also decreases with increasing percentage of total reduction for the material in the interior of the sheet and is independent of the percentage of reduction per pass.

Jan 1, 1937

By P. D. Merica, J. R. Freeman, R. G. Waltenberg

Contents Page Constitution of Commercial Aluminum.................. 4 Solubility of CuAl2 in Aluminum at Different Temperatures........ 9 Effect of Magnesium on Solubility of CuA12 in Aluminum ......... 15 Solubility of Mg4Al8 in Aluminum at Different Temperatures........ 15 Solubility of Metals and Metal Compounds in Aluminum.......... 20 Summary and Conclusions......................20 Aluminum and its alloys have been the subject of much investigation1 during recent years, in the course of which the principal features of the constitution of most of the binary alloy systems with aluminum have been determined. Except in the case of a few metals—silicon, bismuth, cadmium, lead, zinc, and tin—an aluminum-rich compound is formed in each binary system, which forms a eutectic with the aluminum or its solid solution with this compound: Thus such compounds as FeAla, CuA12, Mg4Al3, and NiAls are formed, which are found in aluminum-rich alloys of their respective series as eutectics with the aluminum solid solution. These compounds are, in all cases, hard and brittle and their presence affects profoundly the physical properties of the alloys in which they occur. Within the zinc-aluminum system a compound, Al2Zn,, is formed that decomposes at lower temperatures. Silicon and tin each form a simple eutectiferous series with aluminum; bismuth, lead, and cadmium are only partly miscible in the liquid state with it. The extent of the solubility in aluminum, in solid solution, of these compounds or of the elements themselves, in the case of those series in which compounds are not formed, is of the greatest importance in

Jan 1, 1921

By J. G. Eenink, R. A. Cunningham

One phase has been completed of a laboratory invesrigation of formations with relatively high permeability under conditions of overburden, formation and mud coltrmn pressures. The following statements are based on these tests within the limitations described. Drilling rate decreased when mud column pressure was greater than formation pressure. The decrease was primarily due to a layer of cuttings and mud particles held to the hole bottom by the difference in pressure. Much of the force of the bit was wasted in this layer and was unavailable for penetrating virgin formation. Adequate jet velocities helped clean the filter cake and chips away and resulted in increased drilling rate — the higher the jet velocity the faster the drilling rate. Drilling rate increased slightly when formation pres sure was greater than mud column pressure. The i11(reuse resulted from cleaning the hole bottom as formarion fluid flowed into the borehole. Overburden pressure had practically no effect on drilling rate. INTRODUCTION Some formations are difficult to drill in a wellbore hole but are easily drilled under atmospheric conditions in the laboratory. The reasons for this apparent difference in drillability are not fully understood. An increase in formation compressive strength causes a reduction in drilling rate. It has been shown by Griggs1, Handin2 and others3-1 that formation strength increases under conditions of high hydrostatic stress. Based on these results, a decrease in drilling rate would be expected with increased drilling fluid pressure in formations of low permeability having low formation fluid pressure. Such a decrease has been shown by Murray. et a1 and Eckel" This effect holds even when using nitrogcn under high pressure as the drilling fluid (unrc-ported tests from the Hughes laboratory). Poor bottom-hole cleaning may account for decreased drilling rates. Even though it may not be easily explained, evidence of poor cleaning can easily bc seen. One evidence is the increased drilling rate that accompanies decreased balling obtained with addition of oil in some muds used to drill shales.4,7,3 Many variables can affect drilling rates. These may include mud composition and properties, formation properties, bit types and operating conditions, formation fluid, mud column and overburden pressures. These must be studied a few at a time under carefully controlled conditions which simulate actual conditions as closely as possible. The purpose of this work was to investigate effect of overburden, formation and mud column pressures on drilling rates in permeable formations. These tests were suggested by conditions shown in Fig. I. Represented is a borehole drilled into a formation with relatively high permeability. In the vicinity of the hole bottom there exists a mud column pressure, P a formation fluid pressure, P and an overburden pressure, The mud has low water-loss properties and sufficient weight to more than overbalance the formation pressure. Laboratory investigation included a range with formation pressure greater than mud column pressure. NOMENCLATURE Pm mud column pressure = pressure of drilling fluid or mud at hole bottom Pf, formation pressure = pressure of fluid in intersticies of formation

By J. T. Lapsley, I. I. Cornet, A. E. Flanigan, R. Hultgren, J. E. Dorn

With the greatly expanding use of magnesium during the war, it appeared necessary to the War Metallurgy Committee that procedures of heat treating common magnesium casting alloys be investigated systematically. Accordingly, the National Defense Research Committee of the Office of Scientific Research and Development placed a research contract with the University of California, supervised by the War Metallurgy Committee. Research on the solution heat treatment and aging of magnesium alloy AZg2, (formerly ASTM No. 17; also known as Dowmetal C or AM26o) which was done under "Restricted" Project NRC-2I, in 1942-1943, and reported in detail in a final report to the OSRD on September 3, 1943, is the basis of this paper, which has been released for publication by the OSRD. American experience with magnesium alloys prior to World War II was limited, although some of these alloys had been in commercial use since 1909. Requirements of the aircraft industry for light alloys made it imperative to understand and utilize the advantageous strength-weight properties of magnesium castings. Magnesium casting alloys are commonly solution heat- treated to increase their ultimate tensile strength and ductility; this treatment may be followed by an age hardening at elevated temperatures, which raises the tensile yield strength but diminishes the ductility. In the present investigation, AZp was studied to determine the effects on properties of various solution heat treatment and aging schedules. The principles of heat treatment of magnesium alloys are the same as for other non-ferrous alloys. The alloy studied, AZp, has a nominal composition of 9 pct aluminum, 2 pct zinc, and minor constituents. Fig I shows, by the projection of isothermal sections on the concentration plane, the solubility surface1 of the ternary magnesium-rich solid solutions as determined by X ray 'analysis. From this figure it may be seen that above approximately 375°C (707OF), AZp alloy is a single phase alloy at equilibrium; below this temperature the equilibrium condition is a two phase alloy. The beta constituent which precipitates from the solid solution exerts a hardening effect. Because the zinc concentration is only 2 pct, ancl because of its solubility relations, AZqz resembles a binary alloy of magnesium with aluminum. The solubility curve1 of Fig 2 shows how rapidly the solubility of the beta phase decreases with decreasing temperatures. Unlike many aluminum alloys, magnesium alloys do not age harden at room temperatures; precipitation hardening of AZ² alloy is performed at about 177°C (350°F). At this temperature about 3 pct aluminum

Jan 1, 1949

By Walter C. Lawson

The primary objective in laying track in panel sections is to reduce the number of track laborers required. This is possible because the work is mechanized. Moreover, because the work is mechanized and each of the operations needs only a few men, and each is self-contained, the work can be carried on at night as well as in daylight; therefore, the method provides a means of preparing tracks on more than one shift. The laying of tracks in open pits and quarries in panel sections is not new but new methods have been made possible by the introduction of new types of equipment. The purpose of this paper is to describe the methods that are followed in the Morenci open pit. General Mining Operations Full-scale ore production at Morenci is about 50,000 tons daily. The normal yearly output of ore and waste is 32,000,000 tons, of which 30,000,000 tons is handled by rail haulage. This requires the building of approximately 47 miles of loading and other temporary tracks during a 12 months' period (Fig I). Broken ore and waste is loaded into 90-ton capacity dump cars with 5-cu-yd full-revolving electric shovels. Shovel banks are uniformly 50 ft high. They are blasted with churn drill holes and the broken material from a blast is loaded out with two shovel cuts, the first one being called (locally) the "splatter" cut and the second one the "clean-up" or "face-up" cut. When a shovel is making its clean-up cut, the loading track is about 70 ft from the toe of the bank and, under normal conditions, a bank is blasted against it without removing the track. It is thus evident that each track is used for two shovel cuts before relocation is necessary, inasmuch as a single position serves for both the clean-up cut prior to blasting and for the splatter cut following the blast. The normal advance of a solid bench by a single blast is 40 ft (Fig 2). Preparation OF Panel Grade In preparation of panel grades bulldozers and rooters are used for the bulk of the work and an auto-patrol road grader for the final stage. At Morenci, bulldozers have always been used for track-grade preparation, but before the introduction of the other two types of equipment grades were uneven and irregular at best, and always necessitated a big gang of track laborers to hand-block under the ties with rocks after a track was laid into place. High blocking also made poor track because of instability and caused frequent derailments. Under these conditions derailments were generally bad as re-railing became difficult. Much track was torn up and many tics broken in the process. The inadequacy of the hand-blocked track, together with the inefficiency of hand blocking, constantly pointed, to the desirability of reducing the amount of labor required, so various means were tried to improve conditions, such as wood

Jan 1, 1949

By H. I. Aaronson, S. Toney

When the component grains of .ferritic hicrystals of an Fe-1.55 pct Si alloy are disoriented through an angle "6 " about a conzmon [ll0] axis, the tendency for preferential growth of austenite crystals along the grain boundary during transformation at elevated temperatures is small when 11 deg, but increases rapidly at larger angles. This type of orientation-dependence indicates that grain boundary diffdsion promotes preferential growth along large-angle boundaries. Morphological differences between austenite crystals formed at small-angle [1101 and [loo] boundaries suggest that precipitate morphology can be dependent on the dislocation structure of the boundary. ThE morphology of precipitate crystals nucleated at a grain boundary can be significantly affected by the structure of the boundary.' The limited amount of experimental evidence available in the literature indicates that the morphological effects of boundaries made up of arrays of dislocations, such as subbound-aries and small-angle grain boundaries, are different from those of boundaries having essentially disordered structures, i.e., large-angle grain boundaries. On the basis of indirect evidence, it has been concluded that large-angle grain boundaries give rise to the formation of grain boundary allotriomorphs (crystals which nucleate at grain boundaries, and grow preferentially and more or less smoothly along them)2 in the proeutectoid ferrite and the proeutec-toid cementite reactions in plain-carbon steels, and apparently also in many non-ferrous alloys.' At small-angle grain boundaries in a plain carbon steel, on the other hand, ferrite crystals were found to take the form of primary side plates. Similarly, Guinie, loys. Primary sideplates formed at a subboundary with a constant orientation tend to be parallel to only one, or occasionally two matrix habit planes, and a marked change in the orientation of the boundary is accompanied by a change in the habit plane. Previous studies on the morphological effects of grain boundary structure were performed on poly-crystalline aggregates. Information on the disorien-tation of the pairs of grains forming the boundaries at which the various morphologies appeared in these specimens was largely either qualitative or semi-quantitative. Precipitate morphologies accordingly could not be accurately and systematically correlated with grain boundary structure, and thus theories which have been proposed for the various morphological effects could not be satisfactorily tested. This investigation was undertaken in an attempt to remedy these deficiencies by studying the morphological effects of grain boundary structure with a method in which the boundaries are formed by matrix grains whose disorientations are known and controlled with reasonable accuracy. EXPERIMENTAL PROCEDURE The crystallographic requirements of this study were fulfilled by means of oriented bicrystals of silicon-iron. Disorientation of the component ferrite crystals was carried out about common, major crystallographic axes through angles ranging from 1/2 to 44 deg. The silicon content was low enough SO that the bicrystals could be partially transformed to austenite by heating to elevated temperatures. The silicon-iron used had the following initial composition: 1.55 pct Si, 0.04 pct C, 0.0031 pct N, 0.17 pct Mn, 0.020 pct S, and 0.002 pct P. The alloy was obtained in the form of 0.036-in. sheet. The procedures employed to prepare seed crystals in strips of this sheet, to reorient the seeds, and to grow them into bicrystals are essentially those described by Dunn and Nonken and aynes." The characteristics of the bicrystals are given in Table I. The "bicrystal type" indicates the crystallographic plane parallel to the broad faces of the strip in both grains and the crystallographic direction which was parallel to the long edges of the strip in both grains prior to disorientation. The angular disorientation of the grains, 8, which was performed about the direction normal to the plane of the broad faces of the strip, was measured between the [ 00l] directions. Orientation of the grain boundary, , was taken as the angle between the plane of the grain boundary and a plane containing the axis of disorienta-

Jan 1, 1962

By E. S. Machlin

The possibility that formation of voids under creep-rupture conditions may take place by the condensation of vacancies has been investigated theoretically. It has been concluded that nucleation of voids under creep-rupture conditions by vacancy condensation is highly improbable. However, growth of pre-existant voids by vacancy condensation is probable. A number of predictions made in this theory have been verified by the data. It has been predicted and checked that the product of rupture life and steady-state creep rate for preannealed metals and single phase alloys is an approximately invariant quantity, independent of stress, temperature, and atomic number for a given type structure. The direction of the effect of cold work on this product has been predicted and found in agreement with experiment. A number of experiments to evaluate the vacancy condensation mechanism further are described. SEVERAL papers have appeared recently which speculate on the origin of voids formed at grain boundaries under stress.' ' The object of this paper is to examine quantitatively the proposition that the voids produced in a creep test are a result of vacancy condensation. A result of this paper is a theory of creep-rupture. Void Nucleation Application of standard nucleation theory" to the problem of void nucleation leads to the following conclusions: 1—Homogeneous nucleation of voids requires a supersaturation ratio (concentration of vacancies in supersaturated to that in saturated solution) of 400 for a reasonable surface energy of 1000 erg per cm-and 1.4 for the improbably low surface energy of 10 erg per cm. 2—Heterogeneous nucleation of voids at plane interfaces between two phases requires a supersaturation ratio of 2.5 for a typical contact angle of 145 3-—Void nucleation about a solid particle may be accomplished at a supersaturation ratio of 1.17 for a typical value of work of adhesion? of 60 erg per The work of adhesion is the surface work 10 replace two solid-vauor surfaces by a solid-solid interface. enr ' between an oxide and a metal in the presence of a surface active element such as sulphur. Estimates of the supersaturation ratio at which voids are produced in diffusion experiments yield a maximum of 1.01. Inasmuch as the foregoing mechanisms of void nucleation probably will not operate at this level—too low a surface energy is required—the investigatol. is led to the conclusion that voids must already exist. That is, nucleation of voids probably does not occur. Rather, existing submicroscopic voids grow out to visible size. Already existing voids might be produced during solidification or working. Supercritical sized parlicles which contain cracks may act as heterogeneous void nuclei. Gas pockets may act as void nuclei. Experiments are desired to determine the nature of the heterogeneous void nuclei which grow out to voids in both diffusion and creep experiments. Void Growth Void growth might occur in at least two possible ways, depending upon whether the already existing void nuclei are at grain boundaries or within the grains. In the case of a spherical void far from a crystal boundary, vacancies are generated during creep as a consequence of the migration of suitable dislocation jogs' and are also annihilated at sinks. Under these conditions, a steady-state concentration of vacancies is built up in the crystal, defined by the condition that for any differential volume the rate of generation of vacancies in that volume equals the rate of annihilation of those vacancies." This equality would lead to the development of a gradient of vacancy concentration radially outward from the void surface up to a radius where the vacancy lifetime becomes equal for all directions of vacancy migration. The distance over which this vacancy concentration gradient extends equals about 2vD,T* where D, is the vacancy diffusivity and T:' the vacancy lifetime in a crystal outside the gradient in a zone of constant vacancy concentration. The vacancies generated in the region over which the gradient exists will annihilate more often at the void than elsewhere. Approximately a little over one-half the vacancies generated in the gradient zone will annihilate at the void. Hence, the growth rate of the void is given by on where R is the radius of void in centimeters, is the atomic volume, and R is the rate of generation of vacancies, number per centimeter" per second. R D and T* may be estimated in terms of other physical parameters." In particular, R = n.j e/b [3] where n is the average number of vacancy produc-

Jan 1, 1957

By R. J. Brison, O. F. Tangel

The development of a new method of mineral separation was sponsored by the International Salt Company, which requested Battelle Institute to investigate means for improving the quality and appearance of rock salt from the Company's Detroit mine. Although developed specifically for removing impurities from rock salt, the general method may be applicable to other separation problems. The principal impurities in rock salt from the Detroit mine are dolomite and anhydrite which represent 2 to 5 pct of the weight of the mined salt. In the size range from 1/4 to M in. (the range of primary interest in this project) the impurities are only partially liberated from the halite in normal production. Further size reduction to improve the liberation of impurities is not practicable in view of the market requirements for the coarse grades of rock salt. Laboratory separations in heavy liquids showed that, to improve the quality and appearance of the rock salt substantially, it would be necessary to remove not only free gangue particles but also a large proportion of the locked-in particles. Because rock salt is an inexpensive commodity, a low-cost process was required. Gravity methods were, of course, considered. The heavy-liquid separations indicated that a split at an effective specific gravity of 2.2 to 2.3 would be required. (The specific gravity of pure halite is 2.16.) Heavy-media separation was investigated but had the disadvantages that it was necessary both to operate with saturated brine and to dry the cleaned salt, and that the cleaned salt was darkened by the magnetite medium. Air tabling was tried but did not give the desired separation. It soon became apparent that established methods would not provide a satisfactory solution and work was undertaken on the development of a new process to solve the problem. PROCESS DEVELOPMENT Preliminary Experiments: At the start of the investigation, an analysis of the problem indicated that the diathermacy of rock salt—that is, its ability to transmit radiant heat—might form the basis for an efficient separation process. Under this theory, the impurities might be selectively heated by radiant heat. The particles could then be fed over a belt coated with a heat-sensitive substance so that the warm impure particles would adhere preferentially to the coating. After the initial experiments, made by heating the rock salt with an infrared lamp and separating the product on small sheets of resin-coated rubber, proved encouraging, a small continuous separation unit was set up. This comprised 1) a simple heating unit consisting of a vibrating feeder covered with aluminum foil and an infrared lamp mounted above the feeder and 2) a separation belt 6 in. wide and 36 in. long. A sketch of the device is shown in Fig. 1. Results with this apparatus confirmed the fact that a good separation was possible. It was apparent, however, that a considerable amount of experimental work would be needed to develop the scheme to a practical and economical process. The Process: Basically, the process consists of two main steps: 1) selective heating by radiation and 2) separation of the heated particles on a heat-sensitive surface. Because neither of these steps had previously been utilized commercially in mineral processing, it was necessary to do basic research on both aspects. Factors studied in the investigation included type of heat source, design of heating unit, design of separation belt, selection of heat-sensitive coating, removal of heated particles from the belt, contact between particles and coating, and maintenance of the heat-sensitive surface. Part of the experimental work was carried out on a small-scale unit consisting of the 36x6 in. belt and auxiliary apparatus, and part on a larger unit. For simplicity, discussion of work on both of these units is grouped together. SELECTIVE HEATING Radiant-Heat Source: The essential requirements for a radiant-heat source were 1) that the radiant heat be in a wave length range which is effectively absorbed by the impurities but not absorbed appreciably by the rock salt and 2) that it be dependable, practical, and economical. Selection of a heat source of suitable wave length range was one of the first considerations. It is well known that pure halite is highly transparent to radiant energy in wave lengths from 0.3 to 13 microns. However, the available data on infrared transmission by dolomite and anhydrite, particularly in the range below two microns, were not complete enough to serve as a reliable basis for selection of a heat source. Although it may have been possible to obtain sufficient data on infrared transmission and absorption to enable one to select the best heat source, a more direct procedure was used. This consisted simply of exposing the crude rock salt to each of several types of radiant-heat source on the small continuous separation device. The heat sources investigated, approximate source temperature used, and calculated wave length of maximum radiation are tabulated in Table I. Of the two types of tungsten-filament lamps investigated, both the short wave length photoflood lamps and the longer wave length infrared lamps were satisfactory from the standpoint of selectivity

Jan 1, 1961

By C. N. J. Wagner, E. N. Aqua

The bee alloys of the terminal solid solution of rhenium in niobium were investigated by X-ray diffraclion methods. The analysis of the broadening of the powder pattern peaks from the niobium-rich alloys, cold-worked by filing, showed evidence for faulting on (211) planes. The alloys with larger rhenium concentrations were brittle, and fractured when filed. The analysis of the shapes of the diffraction profiles from powders produced by hammering with steel plates) of these brittle alloys indicated that the broadening was due predominantly to platelets bounded by clibe planes. This result was consistent with the Laue patterns from single-cleazlage facets which showed evidence for clearage fracture on {100} planes. The influence of faulting on the mechanical properties of face-centered cubic (fcc) metals and alloys, i.e., how faulting affects the various dislocation configurations in fcc metals, is well-known.' The important question is whether or not faulting occurs in body-centered cubic (bcc) metals and alloys, and, furthermore, if faulting does occur, to what extent it affects the mechanical properties. Theoretical calculations indicate that the stacking-fault energy is rather high in most bcc metals.2 The results of sev-eral studies using transmission electron microscopy have indicated that faults are present in well-annealed and lightly deformed bcc metals and alloys, such as tungsten,3 vanadium,4 and Mo-Re alloys.5,6 These faults, as have been observed, may be stabilized by the presence of interstitial (C,N,O) atom segregation to the extended dislocations. In addition, there is considerable X-ray diffraction evidence for faulting in bee metals,7-8 using the same techniques that were successful for the study of faulting in fee metals and alloys.7 This X-ray diffraction method is currently the only technique applicable for the investigation of faulting in metals with high stacking fault energies, i.e., when severe amounts of deformation are required to produce sufficient amounts of faulting to be detectable by X-rays. The thinned films of heavily deformed metals will become opaque in the electron microscope due to the high dislocation densities present. In a previous investigation of faulting8 in bee metals of group Vb and VIb, the authors observed that niobium was ductile when filed at room temperature, and showed the highest density of faults on the (112) family of planes. A niobium-base alloy system was therefore chosen to study the effect of alloying on the occurrence of faults in a bcc alloy. There is a large range of terminal solid solubility of rhenium in the alloys of the bee refractory metals. All of the Group VIb-rhenium alloys, i.e., Cr-Re, Mo-Re, and W-Re, exhibit solid solution hardening without loss of ductility.9 In fact, the ductility reaches a maximum for alloys with compositions near to the limits of solubility. This enhanced ductility has been attributed to the lowering of the stacking-fault energy in the alloy; i.e., the increased amounts of twinning provide an additional mode of deformation, resulting in the observed high ductility.' Because of this demonstrated effect of rhenium in bee alloys, it was decided to study a series of alloys of Nb-Re. Using the same X-ray diffraction methods as described in the previous investigation,' one is able to identify the possible causes of broadening of the powder pattern peaks, e.q., particle size, microstrains, stacking faults, and/or twin faults. The separation of these various contributions to the measured peak shape is accomplished by the Warren-Averbach analysis.7 I) EXPERIMENTAL PROCEDURE A series of seven bee solid solution alloys containing from 2.5 to 21.5 at. pct Re (remainder niobium) were prepared at the General Electric Research Laboratory. Buttons, weighing 25 g, were alloyed from electron-beam-melted niobium chips and random rhenium sheet by arc melting in a water-cooled copper crucible, under an argon atmosphere. The buttons were inverted and completely remelted to promote homogenization. The nominal alloy compositions are listed in Table I. Samples of the cold-worked alloys were obtained by filing to produce a powder for the X-ray study. Alloys too brittle to be filed were hammered with steel plates. The resultant filings or brittle impactings were screened through 150-mesh classifiers and compacted to the required shape for the diffractometer holder. The X-ray diffraction peaks were automatically recorded by fixed time counting at uniform 28 intervals, or by continuous registration with a ratemeter. In all cases, the (110)-(220) and (200)-(400) pairs of peaks and the (211), (310), (222), and (321) reflections were measured on a GE-XRD5 diffractometer using CuKa radiation with nickel filter or MoKct radiation and a LiF monochromator in the diffracted beam. The first part of the data reduction, completed with the aid of a series of programmed computations,10 was the analytical resolution of the Kol component of the diffraction profile. Subsequent computations were then made with reference only to the resolved Kol peak shape. These included the measurement of the

Jan 1, 1967

By K. G. Wikle, J. G. Klein, W. W. Beaver

Consolidation of hydride process, electrolytic, calcium reduced, and comminuted thorium powder, as well as saw chips and lathe turnings, by vacuum hot pressing and by cold pressing-vacuum sintering was studied. The mechanical properties of the consolidated material in the extruded form are compared with those of wrought castings. AT present there little little industrial use for thorium metal, although it has some important though small scale applications in electronic equipment. Despite its high inelting point—about 1750°C —a low modulus of elasticity, 11.4xl0 si at 20°C;' relatively low mechanical properties coupled with a high density, 11.7 g per cu cm; and an unusually high chemical activity with normal atmospheres limit any structural applications. The metal is utilized as an alloying element principally in magnesium. Pure thorium finds utility as electrodes in gaseous discharge lamps such as the high intensity mercury lamp' because its low work function and high electron emissivity provide lower starting potentials and more uniform operating characteristics than other available materials. The metal is also found in photoelectric tubes used for the measurement of the ultraviolet spectrum." Thorium metal has been used in germicidal lamps of the cold cathode type as sputtered coatings on nickel in order to provide a low work function surface and a low starting voltage. Other applications have involved the radioactive properties of thorium for the production of ionized particles." The potential value of thorium is much greater than its present use pattern because of possible utility in the field of nuclear power. Th may be converted through nuclear reaction to a fissionable element U which should be capable of acting similarly to U in the g'eneration of atomic power. Thorium has been reported to be about three times as plentiful as uranium in the earth's crust, placing it in the order of abundance of lead and molybdenum." Thus, it is of interest in augmenting the potential supply of fissionable material for nuclear power. Because of its high melting point, thorium is usually produced as a powder through the calcium reduction of its oxide or thermal reduction of halides by sodium, magnesium, and calcium. It may also be produced in flake form by electrolysis of fused alkali or alkaline earth chloricles and fluorides. Therefore, powder metallurgy assumes importance in the fab- rication of thorium metal shapes. Furthermore, it is rather difficult to obtain pure thorium by melting, as the molten metal reacts readily with graphite as well as oxide, carbide, and nitride refractories. These contaminate the melt with oxides, carbides, and metallic impurities." The current investigation was undertaken to examine the fabrication of thorium by powder metallurgy methods which have been used for the commercial production of beryllium and other metals.' A sparcity of data concerning the comparative cold and hot compaction of thorium powders of different derivation existed. Therefore, all commercially available types were examined along with other experimentally produced thorium powders in order to round out the comparison of consolidated thorium powders with melted reguline metal. Review of the Literature By heating a mixture of ThC1, with potassium, Berzelius made the first thorium metal as an impure powder in 1828. Improvements in the basic process, increasing thorium assay to 99 pct, were made by several investigators including Arsem," Lely and Hamberger10 and Von Bolton." Calcium reduction of Tho, to make powders was investigated by Berger," Huppertz,'" Kroll," and Kuzel and Wedekind.'" A thorium powder produced by this method using a CaC1, fluxing agent assayed 99.7 pct, as reported by Marden and Rentschler.'" Compacted and sintered, this product was found to be ductile, and could be fabricated into wire and sheet. Improvements of the calcium reduction process were made later" wherein CaCl, was eliminated from the reaction, producing metal assaying 99.8 pct Th. Further work by Lilliendah118 howed that a coarser metal could be obtained by the substitution of ThC1, or ThOC1, for oxide with consequent advantage of stability to atmospheric reaction. Reports on the technology of thorium developed in Germany during World War II have been made by Espe."' Thorium powder of 99.5 pct Th was obtained by reduction of the oxide by calcium. Screening to —200 mesh, compacting with about 20 tsi, and sintering in vacuo at 1320" to 1360°C for 3 hr resulted in a porous sinter cake. The sinter cake was sufficiently ductile to be worked into bar, wire, and sheet which could be employed as electrode materials.

Jan 1, 1957

By G. U. Greene

The various lead producers have given the subject of lead drosses much attention in recent years but the problem of their economical treatment is yet to be solved. Formerly the copper in the furnace feed was removed from the furnace in the form of matte. The speiss at that time consisted principally of the iron arsenide. The practice today is to roast off most of the sulphur and the copper in the feed forms a dross in the furnace, which is removed from the furnace with the lead. This material is poured into the drossing kettles and allowed to cool down to but slightly above the freezing point of lead. The copper dross, containing almost all of the arsenic and part of the antimony, is skimmed off and treated in a small reverberatory furnace at most plants. This is essentially a liquation process. The skimmed dross contains from 70 to 80 per cent lead, and much of this lead is liquated out. The products from this treatment are: (1) impure lead, (2) speiss and (3) matte. The speiss from the reverberatory furnace was studied in this research. The literature on the subject is of very little assistance, as almost no work has been done on the problem of establishing the exact identity of the various phases present. One author(1)† states that speiss consists of a series of isomorphous compounds of the general formula FexAsy in which the Fe may be replaced by Ni, Co, Cu, Pb, Ag, Au, Pt, Zn, Cd and the As replaced by Sb, S and Bi. Hofman(2) states that the iron arsenide present is Fe5As. Experimental Work In the present research, the author used for methods in an attempt to determine the composition of the various phases: (1) chemical, (2) microscopic, (3) roentgenographic and (4) thermal. Previous to this research, considerable time had been spent making analyses of different speisses, but unfortunately no very definite conclusions could be made as a result of these analyses.

Jan 1, 1937

By T. F. Bower, M. C. Flemings, H. D. Brody

A series of experiments are reported which show thai reasonable assumptions for analysis of solute redistribution in solidification of castings and ingols illclr(de: negligible undercooling before nuclcation of solid phases, negligible increase of solute in advance of the tips of growing dendrites, complete diffusion within the Liquid oer distances the order, of dentrite arm spacings, platelike dentrite t/o?$holog?.. Qzmli/ali,e and periment is obtained JOY Al-Cu alloys front measurements of amount of nonequilibrium second phase, minimum solute content at the centers dentrites arms (after solidification), and 3) change in minimum solute content in dentrite arms during solidification. In a previous paper' analyses were given describing solute redistribution in dendritic solidification. The analyses were undertaken primarily to permit prediction of "severity of microsegregation" in a casting or ingot after solidification and cooling to room temperature, but can also be used to predict "local fraction solid' as a function of temperature in the solidifying alloy. Numerical results were given for Al-Cu alloys. The aims of this paper are to examine the validity of some of the assumptions of that analysis, and to compare predictions of the theory with experiments. All experiments reported are on Al-Cu alloys, the bulk on Al-4.5 pct Cu alloy. EXPERIMENTS Experiments conducted were on small ingots, 41/2 in. in diam by about 10 in. high. solidified in a controlled thermal environment (i.e., in a resistance-heated, re-circulating air furnace, whose temperature could be controlled to 1°C). In one series of experiments, the ingots were solidified very slowly (solidification time was varied from 8 to 1000 hr) and at constant rate of heat extraction. In a second series of experiments the ingots were solidified ( 'unidirectionally". Fig. 1 is a sketch of the method of making the two different types of ingots. The unidirectionally solidified ingots were fully columnar, and the slowly solidified ingots had equiaxed structures, Fig. 2. In making the slowly solidified ingots, the mold employed was carbon steel, coated with inert refractory. Typically the mold and its environment were heated to 700°C. The molten alloy was then poured into the mold and the temperature of the system equilibrated above the liquidus. The environment of the mold was next cooled with a controller responding to a differential thermocouple that measured the difference between the temperature of the melt and the temperature of the mold environment. The differential thermocouple consisted of one chromel-alumel junction in the melt connected in opposition with a second junction in the furnace. The potential across the differential thermocouple was input to the controller which acted to keep this potential at a set. constant value; hence the temperature difference between the two junctions was maintained nearly constant. Major resistance to heat flow in the above apparatus was between the metal surface and the furnace atmosphere, not in the metal itself. By maintaining a constant temperature difference between the metal and the furnace atmosphere, the controller maintained an essentially constant rate of heat extraction during solidification, regardless of amount of heat released by the metal per unit temperature change. When the metal temperature dropped just below the eutectic temperature. the ingot was removed from the furnace and water-quenched. The unidirectionally solidified ingots were cast in a similar mold to the foregoing except that provision was made to extract heat through the bottom face of the mold by passing air or water through the mold base, Fig. 1. For these experiments, metal and mold temperature were again equilibrated above the liquidus. Temperature of the mold environment was then held

Jan 1, 1967