By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.' There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.'j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

By M. P. Tixier, A. Poupon, M. E. Loy

Simple qualitative methods are explained for identifying those shaly sands in a well that are most likely to contain oil. A need for more precise measurement of the variables that enter shaly sand analysis is indicated. Field examples are given to illustrate the methods. A theoretical discussion of the quantitative interpretation of shaly sands is given as a basis for discussion and as a guide for the future. While not generally capable of practical application at the present time because of the lack of sufficient accuracy of the electric log data, these methods may become more feasible in the future as the result of the improved logging methods now being introduced. INTRODUCTION Experience has shown that for porous formations containing only a negligible amount of clayey material, reliable information on the fluid saturation and porosity of the reservoir rocks can usually be derived from the electrical logs. The interpretation is based on empirical formulae relating the true resistivity of a porous formation to its lithologic character, to the resistivity of the interstitial water, and to the proportions of water and hydrocarbons in the pores.' If the resistivity of the interstitial water is not known, its approximate value can be derived from the SP curve.2,3 The porosity can usually be determined to a good approximation from a MicroLog, or a MicroLaterolog.4,5 When the reservoir rocks contain an appreciable percentage of clayey material, an additional factor is introduced into the analysis. In a clean formation, the matrix is an electrical insulator, so that the ability of the formation to conduct current is due only to the conductivity of the electrolytes in the pores; in a shaly formation, the shale constitutes a part of the rock matrix able to conduct current, and influences the resistivity of the formation. On the other hand, the spontaneous emf's and the circulation of the SP currents are also responsive to the presence of the shaly material. All other factors being the same, the deflection of the SP curve opposite a shaly permeable formation is smaller than the deflection which would be observed if the formation were clean. The effects of the presence of shale on the resistivity and on the SP curves in a shaly formation are functions of the amount, of the specific resistivity, and of the geometrical distribution of the shaly material within the formation. The presence of shale therefore constitutes an important complication in electrical log interpretation. It is easy to realize, for example, that the presence of a large amount of clayey material in a sand may have such a predominant effect that the resistivity of the sand will not change very much, whether the pores are entirely filled with connate water, or contain a high saturation of hydrocarbons. Important research projects have been undertaken to investigate the influence of shales and to find a way to allow for this influence in the interpretation of a log. The problem of the SP in shaly sands was analyzed mathematically by H. G. Doll"' for the case of sands with shale laminations. Formulae expressing the resistivity of shaly formations were proposed by Patnode and Wyllie8 and de Witte.9 Other quite interesting theoretical and experimental results have been published by various authors.l0,ll,12,l3,14 The purpose of the present paper is to discuss an approach to electrical log interpretation in shaly sands. This approach is based partly on some of the theoretical and experimental data available in the literature and partly on observations made on actual field logs. Comparatively simple methods for qualitative and semi-quantitative analysis are described. These methods depend principally upon information provided by the electrical logs.

Jan 1, 1955

By J. D. Sudbury, J. E. Landers, D. A. Shock

The external corrosion of casing is one of the most important problems facing the present day production man. A 1953 NACE report' estimated the annual cost of casing corrosion at $2,200,000 in 22 fields studied. The fields represented only 10 per cent of the wells in the United States. It was significant that 77 per cent of the failures reported were due to external corrosion. A variety of means for combatting the casing corrosion problem have been discussed in papers such as the NACE survey' mentioned previously. No attempt to revicw these will be made in this paper. Thc scope of this paper has been limited to a discussion of the following major items: (I) an instrument for studying external electrolytic corrosion; (2) use of this instrument to determine the quantity of protective current required to prevent corrosion of casing; and (3) problem of accelerated external corrosion of the oil string at the base of the surface string. ELECTROCHEMICAL MECHANISM OF CORROSION It IS gcncrally belleved that one major cause of external corrosion is the existence of electrolytic cells operating between various formation waters. A theoretical discussion of the role of earth potentials in casing corrosion has been presented by L. de Witte and F. J. Radd.2 A brief picture of the electrolytic corrosion action between two differcnt formations (A and B) is presented in Fig. I. This picture is a review to many but is given to insure clarity. In the anode area, oxidation takes place as iron ions go into solution in formation A as a product of corrosion. In the cathode area. reduction takes place and hydrogen atoms are formed at the boundary between the pipe and formation B. The flow of electrons. as indicated. is into the pipe at the anode or corroding area and out of the pipe into the formation at the cathode. In order to conform with regulations of this journal, the flow of a conventional current (I! is also indicated in this sketch. All subsequent references will be to this so-called conventional current flow and will be indicated by the symbol (I). As this action takes place the layer of hydrogen developed on the cathode offers a resistance to the flow of current in the cell. It is said (hat the cathode has been polarized. This polarizing film can be rcmoved by addition of a so-called dcpolarizing agent which reacts with and removes this hydrogen film. Such an agent must be present in ordcr for this corrosion reaction to go at a rate sufficient to cause a severe corrosion problem. The two common depolarizing agents are: (I) oxy-sen. which readily reacts with hydro gen to form water, and (2) certain bacteria which use atomic hydrogen as part of their life process. It is not difficult to explain the presence of these agents. Oxygen may be present in some very shallow formations. Sulfate reducing bacteria are found to exist in nearly any ground where mud pits might be dug. THE CASING POTENTIAl-PROFILE Instrumentation A sketch of the equipment* uscd in determining casing potential profiles is shown in Fig. 2. The tool is run in the hole using a hoist truck with a three-conductor cable. This tool must be run with tubing and rods out of the hole and should be run with the flow line disconnected. By proper choice of electrode size it can be run in any size casing. The electrodes must be run in an open hole or a hole filled with oil. Measurements cannot be made while immersed in water. The tungsten carbide-tipped knives serve as the electrical robes and arc spaced 25 ft apart. The potential difference along a 25-ft section of casing is measured with a potentinmeter to an accuracy of about 5 mv. Current flowing in the pipe can then

Jan 1, 1956

By L. Stone, H. Margolin

The Ti-C-N and Ti-C-O systems were investigated in the temperature range from 500° to 1400°C and in the composition range up to 2 pct C and 5 pct N or 0. Characteristic isothermal sections at 800°, 900°, 1000°, and 1300°C are presented. The Ti-N-0 system was studied in the temperature range from 900' to 1400°C with alloys containing up to 6 pct total alloying content. Characteristic isothermal sections at 1000° and 140O°C are presented. Melting-point data for all three systems are also included. THIS paper reports on one of a series of investi-gations which have been conducted on the phase diagrams resulting from interstitial alloying with iodide titanium. The other investigations involved delineation of the binary systems with carbon,' nitrogen and boron,h and oxygen. The Ti-0 binary system has also been investigated by Bumps et al.' In varying degrees, each of these interstitial elements has been shown to stabilize the low temperature a modification of titanium1-5 and each forms a face-centered cubic TiX compound (henceforth designated 6). In addition, the Ti-N and Ti-0 systems reveal a low temperature tetragonal phase (6) formed by a peritectoid reaction between a and TiX Experimental Procedure The development of experimental techniques for the study of titanium alloy systems has, to a large extent, become standardized. In this investigation, the equipment and procedures described in detail by Cadoff and Nielsenl have been used. Arc Melting: In general, binary alloys with carbon, nitrogen, and oxygen, prepared in the composition range of interest in this investigation, show negligible composition changes during arc melting. However, the possibility of the formation of some gaseous combination of alloying elements such as CO, CN, or NO during the preparation of these ternary alloys was considered. Calculations showed that the evolution of only 0.05 gram of such a gas would be detectable as a pressure change in the closed system used during preparation of these alloys. Such pressure changes were not observed. Consequently, nominal compositions have been used in plotting the data. The compositions of the materials used in the preparation of the alloys are shown in Table I. After melting for 3 to 5 min at 275 to 350 amp, the alloys were checked for homogeneity by microstruc-tural examination. Alloys containing up to 1 pct C were homogeneous in the presence of less than 3 pct N or 0. At higher alloying contents, some inhomo-geneities in the carbon distribution became evident. Alteration of the melting procedure toward longer times and higher currents did not improve the homogeneity of these alloys. Ti-N-0 alloys were homogeneous in the range to about 3 or 4 pct total alloying addition. Beyond this, almost all of the specimens showed as-cast microstructures consisting only of the phase. Consequently, inhomogene-ities could not be detected by examination of micro-structures. Ten alloys from each of the systems were analyzed for two of the elements present (oxygen being omitted in all cases and titanium being omitted in the Ti-C-N alloys). In all cases the analyses were found not to be sufficiently precise to serve as criteria for the total composition of these alloys. On the basis of phase distribution in heat-treated alloys, however, it appears that carbon is distributed throughout the alloys most uniformly, with oxygen and nitrogen following in that order. Heat Treatment: Specimens for heat treatment were wrapped in titanium sheet before sealing in the argon-filled quartz capsules. Heat-treatment times varied from 100 hr at 800°C to 0.5 hr at 1400 °C. After heat treatment the specimens were quenched by breaking the capsule in water. With the exception of alloys in the low composition region, heat treatment did not have an appreciable effect on the as-cast microstructures. Metallography: Following heat treatment, the specimens were prepared for metallographic examination by grinding on emery paper and electrolytic polishing. For the majority of the specimens a 10-sec etch with Remington "A" agent (25 pct HNO3, 25 pct Hf, and 50 pct glycerin) adequately

Jan 1, 1954

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2'3 and

Jan 1, 1969

By P. E. Busby, C. Wells, M. E. Warga

Fundamental data on the rate of diffusion of boron in austenite and solubility of boron in the a and y phases of iron and steel have been obtained from deboronizing experiments and provide partial explanations for some of the phenomena observed in boron steels. The rate of diffusion of boron is about the same as carbon in austenite. The solubility of boron in austenite at normal heat-treating temperatures is less than 0.001 pct. A partial tentative Fe-B phase diagram in the important low boron concentration ranges and an equation representing the diffusion of boron in austenite are presented. A LTHOUGH a search of the literature revealed ALTHOUGHthat boron diffusion had not been studied quantitatively and systematically prior to 1948, a few qualitative observations which were made by following the diffusion of boron into iron packed in ferro-boron1-3 suggest that boron obeys normal diffusion laws and that the rate of diffusion increases with increasing temperature. The claim of Cornelius and Bollenrath1 that boron does not appear to influence the rate of carbon diffusion has recently been substantiated by Wells, Batz, and Mehl.4 Calculations based on data from the paper by Campbell and Fayv indicated that the diffusion coefficient (D) for boron in iron at 900°C is approximately 3x10 sq cm per sec; a value of 2x10-7 sq cm per sec at 1038°C has been reported by Digges et al in connection with decarburizing experiments on a commercial boron steel containing 0.43 pct C. During the period 1948 to 1950 several diffusivity constant (D) values for the diffusion of boron in the y phase of iron and steel and a number of solubility values for boron in both a and y phases were reported. It was concluded tentatively as a result of Metals Research Laboratory studies that D values for boron in y and a phases are about the same as for carbon in the comparable phasesa and that carbon up to 0.4 pct did not affect the rate of diffusion of boron in y iron above 1000°C within the limits of experimental error. Whether saturation of the y or a phases with carbon would significantly affect rates of diffusion of boron through them was then and still remains in doubt. The best estimate of Q (activation energy) was reported to be about 25,000 cal, somewhat lower than that for carbon in y iron. The solubility of boron in y iron at 1000°C was thought to be higher than 0.004 pct B but not as high as a more recent analysis of available data shows it to be. The solubility of boron in a iron at 700°C was reported to be 0.0004 pct B, but it would not have surprised the authors if the true solubility value is actually lower than this. Breaks in diffusion curves which were not understood when first obtained prior to 1950 have now been recognized as indicating solubility limits, and these are included in the present paper. Experimental Procedure Two methods were employed in an effort to determine diffusion coefficients (D) for boron in austenite. Early experiments involved the use of welded couples prepared in accordance with the procedure of Wells and Mehl,' but when the results of these experiments proved to be unsatisfactory for calculating D values, studies were continued by means of deboronizing experiments. In both cases, boron analyses following the diffusion anneal were carried out spectrographically and all D values were computed using the Grube solution of Fick's law. The precision of the spectrographic method used proved to be about equal to that reported by Corliss and Scribner" —average deviation from the mean about 5 pct of the amount present when the boron content is 0.003 pct. Concentration-penetration curves obtained from spectrographic analyses of welded couples generally indicated that practically no boron was transported across the weld interface during the diffusion anneal. Furthermore the concentration-penetration

Jan 1, 1954

By Leonard L. Melton, Calvin D. Saunders

The design and performance of many operations common to the petroleum industry depend upon the unique properties of a class of materials known as non-Newtonian fluids. The art of measuring and describing these properties, called rheology, has fallen far behind the field applica-tion of these fluids in this industry. Empirical methods are still employed although theoretically sound methods of analysis are now available. This paper illustrates a completely general method of analysis of the rheological properties of non-Newtonian fluids which id independent of the type of viscometer employed and also the rheological type of fluid encountered except those of a thixo-tropic or rheopectic nature. Values of the rheological properties of a fluid obtained using this method of analysis are based upon an absolute scale of measurement, eliminating the necessity of employ-jng arbitrary concepts of the flow properties of non-Newtonian fluids, The fundamental nature of this method of analysis is further demonstrated by evaluating the precision with which measurements have been made of these rheological properties by employing a dimensionless criteric: —the Fanning friction factor-Reynolds number correlation. INTRODUCTION Non-Newtonian fluids are not new in the petroleum industry. Particular properties of non-Newtonian materials have been recognized and used to advantage in drilling fluids and have found excellent application in the hydraulic fracturing process.'.' While usage of these fluids is not new in this industry, the art of measuring and describing their rheological properties is still in its infancy. This is reflected in the accepted method of evaluating drilling fluids, API RP 29, (1950), which recommends a one point "viscosity" measurement. These shortcomings are recognized by various groups in the industry and more adequate methods have been prposed.3,4 The efforts Of these people are to be commended; but, at the same time, the limitations of their method of analysis and viscometer must be appreciated. This method Of analysis is applicable Only to Bingham plastic fluids as is pointed out early in their articles. The consistency of a Bingham plastic fluid must also lie within the range of the viscometer which is also well defined by the author. It is believed that the apparent simplicity of this method of analysis and the utility Of Operation Of their viscometer will soon make the terms non-Newtonian fluid and Bingham plastic fluid synonymous as used in this industry; a tendency which has already been encountered. Application of this method of analysis to a non-Newtonian fluid other than a Bingham plastic can lead to erroneous results. The field of rheology has long been hampered by the adherence to arbitrary concepts of Of of the flow properties Of non-Newtonian fluids. This has resulted in the design and operation of viscometers so as to fulfill these concepts rather than following the more logical method of analyzing experimental data so as to yield a fundamental truth. completely Bingham proposed the concept Of plastic flow and yield asu rement. data presented by Buckingham could hardly be interpreted so as to substantiate this theory; but rather succeeded in establishing the fact that compliance with this flow concept could never be realized in the capillary tube vis-cometer.5 Bingham, in reply, sug-gested "Rather than complicate our formula, it would seem to me a much better plan to so change the conditions of flow that the formula will be linear... Reiner0 stated .This plan has been followed by me in collaboration with Miss Riwlin. . . . From the present paper (Reiner and Riwlin, 1929) it will be seen that it is possible to choose the conditions of flow so that the formula based on Bingham's law of plastic flow remains linear. This is realized in the rotation viscometer," Thus, a viscometer, with design and operation based on the Reiner and Riwlin equation for plastic flow, is restricted to a specific range of flow

Jan 1, 1958

By R. F. Blakely, P. E. Potter

Any stratigraphic section or bedding sequence can be synthesized if there is a transition procedure from one lithology or bedding type to another, and if thickness distributions of the different lithologies are known. Stratigraphic sections of a fluvial sandstone body were synthesized with five bedding types: cross-bedding, massive beds, parting lineation, ripple mark and mudstone. The transition procedure from one bedding type to another used dependent, Markovian random processes which have a memory that extends one step backward in the depositional process. As observed in nature, median grain size and sand wave thickness (cross-bedding and ripple mark) decline upward in the synthesized sections as proportions of the different bedding types change. Grain size and permeability were also incorporated into the sections. By changing the transition procedures, bed thickness distributions, rate of upward decline or sand wave height and length, different types of sections can be synthesized, thus making it possible to model many different sedimentation problems. INTRODUCTION This paper describes a general method for synthesizing stratigraphic sections and bedding sequences of sedimentary, metamorphic or igneous origin. Synthetic generation is of interest for several reasons. Close correspondence between real and synthetic sections suggests that the factors used in the synthesizing model may indeed be the correct ones, thus giving the investigator a check on his assumptions. Rapid, inexpensive simulation of many stratigraphic sections permits one to synthesize a rock body (sandstone or carbonate reservoir) or, on a larger scale, the fill of a sedimentary basin. Harbaughl gives an example of mathematical simulation of a carbonate basin. He simulated the basin in the hope that improved prediction would follow better understanding of the depositional processes. From the petroleum engineer's viewpoint it seems reasonable to believe that the synthetic generation of rock properties and their distribution in a reservoir should be relevant in the study of reservoirs. Any stratigraphic section or bedding sequence can be generated provided there is a transition procedure from one lithology or bedding type to another, and provided the thickness distributions of the different units are known. The transition procedure involves random processes that are either independent or dependent. If the depositional process is independent, previous deposition will have no influence on present deposition. However, if it is dependent, past deposition will influence either present or future deposition. Such a dependent depositional process can be thought of as having a memory that extends backward in time through one or more pulses of deposition. A process with a memory can be described by a Markov process. Because the concept of memory or dependence appears to be in accord with our understanding of many depositional processes, Markov processes were used to synthesize the bedding sequences of this study (see Appendix). The above methods are perfectly general and are appropriate for any stratigraphic section or bedding sequence: bedding types in a beach deposit, an evolving carbonate bank or the changing lithologic fill of a thick geosyncline sequence. We chose to synthesize a vertical profile of a fluvial sandstone body because its characteristics were well documented, much was known about fluvial processes and fluvial-deltaic sandstone bodies constitute an important class of petroleum reservoirs. CHARACTERISTICS AND ORIGIN OF FLUVIAL CYCLE The fluvial cycle has been well documented in recent years by Bersier,2 Allen3-5and Visher.6,7 Deposits from fluvial cycles range from 10 to 150 ft or more in thickness and are characterized by a "fining upwards": coarse sandstones with occasional conglomerates grade upward into medium- to fine-grained sandstone, and hence into siltstone and mudstone. The dominant sedimentary structure is inclined bedding: thick cross-beds in the lower half

By G. A. Vissac, R. G. Minet, N. E. Sylvander

R. G. Minet—The authors' description of the remarkable progress made in the last few years in applying the fluidized solids technique to the problem of lignite drying and carbonization clearly demonstrates that engineering techniques available today may make many processes practical and profitable which a few years ago were considered otherwise. As pointed out in the article, the future of the carbonization step hinges on the value and utilization of low temperature tar. On paper, at any rate, this tar looks like a valuable raw material for the chemical industry to use. Some 50 to 60 pct may be converted to pitch for electrodes, roofing, road tars, and other valuable products; the 25 to 30 pct tar acids could conceivably form a basis for a new low cost resin or plastic of the phenolformalde-hyde type. Yet these materials are so new and dissimilar from available sources that much work must be undertaken by the chemical industry before they will be accepted. Now that the work of Dr. Perry and his colleagues has made a large supply of low temperature tar a real possibility, I would expect the chemical industry to accelerate its work in this field. On the basis of certain data available in the literature it appears possible to produce a more aromatic tar, although in smaller yield, by operating at temperatures in the range of 1300" to 1500°F. Operating a fluidized bed process for lignite at these conditions should be technically possible, at least, and could produce a tar having more familiar characteristics. I wonder if Dr. Parry would care to comment on such a possibility. Incidentally, in our own work on carbonizing coking coals in fluidized beds, using Ohio, Pennsylvania, and West Virginia high volatile bituminous coals, we have obtained yields which agree with the correlation given for tar yields vs moisture and ash-free volatile Btu. Our data are slightly under the line, but certainly in the range of the correlation. We have also obtained evidence in support of the authors' statement as to the effect of air on the process. In our pilot plant all the heat required for carbonizing is released by internal combustion of char in the fluidized bed in normal operation. We are also equipped to obtain all carbonization heat by external electric heaters on the shell of the carbonizer while introducing only an inert gas to the process. We note no difference in tar yield or characteristics between the two operations. In the case of the gas, however, it appears that some hydrogen is consumed by the air combustion. We would be interested in hearing in a little more detail about the hot dust and char handling problems at Sandow. Have the authors found char subject to spontaneous combustion? Have they ever tried a coking coal in their pilot plant? V. F. Parry (author's reply)—Production of a more aromatic tar by operation of the carbonizer at 1300" to 1500°F does not appear to be economical. 1) The capacity of a reactor operating at 1500°F would be 30 to 50 pct less than the capacity at 932 °F and the cost of processing would increase materially. 2) The cracking of tar vapors in a reactor requires appreciable time to complete the reactions and it is doubtful that considering the very short time of residence of tar vapors within the reactor (4 to 10 sec after evolution) the basic character of the tar would be changed significantly. This is indicated from the data reported in Table XIV. 3) General studies have shown that it is advisable to operate at the minimum temperature to produce the maximum tar and minimum gas. 4) Operating problems and the maintenance of vessels and reactors, and the hazards of handling hot char, increase with the temperature of carbonization. It is technically possible to operate at temperatures as high as 1500°F, but in my opinion it is not economical or desirable. We believe that the primary tar must be won in the simplest way and then processed alone to change its character for production of desired products. It is interesting to have confirmation of our observations on the reaction of air with the products of carbonization. The major reaction is with the char, fol-

Jan 1, 1957

By P. Ramachandraraa, T. R. Anantharaman

THE technique developed by Duwez, Willens and Kle-ment' for rapid solidification of molten alloys in small quantities by ejecting them on to a highly conducting substrate with the aid of a shock wave has come to be known as "liquid quenching" or "splat cooling" in literature and has already been applied to alloys of many binary systems.' The very high cooling rates of the order of l060 to 1080 per sec obtained in this technique and the consequent drastic undercooling of the melt have led to such striking results as formation of new amorphous and crystalline metastable phases and extension of solid-solubility limits in many alloy systems. The cooling rates in these experiments can, however, be neither accurately measured nor effectively controlled and hence the occurrence of either more than one metastable phase or appreciable differences in constitution in splat-cooled alloys of the same composition cannot be ruled out.3 In fact, workers in two laboratories have reported formation of two different cubic metastable phases in liquid-quenched Au-Si alloys containing 17 to 20 at. pct si.4,5 The present note deals with some new and interesting results obtained in a Ag-21 at. pct Ge alloy and a Au-27 at. pct Ge alloy subjected to the liquid-quenching treatment at different cooling rates. Two alloys of nearly the same composition had earlier been rapidly solidified by the standard "gun technique" in the same laboratory and shown to solidify in nonequilibrium structures, viz., an hcp phase (a = 2.987Å;c =4.718Å) in the Ag-Ge system6,7 and both hcp (a = 2.885Å; c = 4.754Å) and tetragonal (a = 11.627A; c = 22.491Å) phases in the Au-Ge system.3 Apart from different substrates (copper and stainless steel), different melt temperatures (50º to 500°C above the liquidus), and different capillary sizes (0.4 to 1.5 mm diam) in the "gun technique", slower cooling rates of the order of l050C per sec were also obtained in the present work by replacing the substrate by water at room temperature in a modification of the technique due to Olsen and Hultgren.8 No attempt was made to measure the cooling rate in any experiment. The products varied from fine powder (>40 pct by wt—200 mesh) obtained by quenching in water to thin flakes and foils (11.0 sq mm to 4.0 sq cm) produced by splat cooling. They were subjected to the Debye-Scherrer method of X-ray examination in each case. In case of the Ag-Ge alloy, in addition to the expected metastable hcp phase,6 a coexistent tetragonal phase (a = 5.093,Å; c = 7.009Å) was detected in some experiments. Eight weak X-ray reflections from this phase could be identified, two of them being the same as reported earlier.7 With increase in the cooling rate, the dominant hcp phase seems to be first accompanied by traces of silver or germanium and then either homogeneous or mixed with traces of this new tetragonal phase. The splat-cooled Au-Ge alloy showed generally the expected hcp and tetragonal phases,3 but sometimes traces of germanium were also present. Further, two new tetragonal phases with the following lattice param ters could be clearly identified in samples quenched

Jan 1, 1970

By James Paul

BEGINNING in December, 1933, and continuing to the close of April, 1934, large sums of money were expended in the states of Pennsylvania, Ohio and West Virginia through the conduct of Federal and State Civil Works Administration, financed by the Government as a part of the President's recovery program to furnish employment to mine employees idle as a result of the economic depression. PURPOSE OF THE PROJECT The protection of the public health against the pollution of public water supply by acid mine drainage was the incentive that prompted the request that the sealing of abandoned bituminous coal mines be made a Federal project. A paper before the Central Section of the American Water Works Association, Wheeling, W. Va., on Aug. 24, by E. S. Tisdale, Chief Engineer of the West Virginia Department of Health, tersely says: In October, 1933, the combined experience of the U. S. Bureau of Mines and the U. S. Public Health Service and the States of Pennsylvania, Ohio, West Virginia and Kentucky resulted in a report being filed in Washington, first with the Public Works Administration and later with the Civil Works Administration, where it was favorably acted upon, calling for these governmental agencies under the direction of the U. S. Public Health Service to expend $1,500,000 in a unified effort to seal abandoned coal mines in Pennsylvania, Ohio, West Virginia, Kentucky and six other states farther down along the Ohio river. The report referred to was embodied in a petition that was signed by the chief engineers of the State Departments of Health of the several states contiguous to the drainage area of the Ohio River. The project as established under Federal supervision became interstate with respect to the several states involved, and upon the termination of the Federal project on Feb. 15, it was authorized as a State C.W.A. project, effective Feb. 20, under the supervision of the State Departments of Health and the State C.W.A. Administration, which continued to March 29, and was succeeded by the S.E.R.B. of the R.W.D. from April 2 to April

Jan 1, 1935

By Carlos E. Roggero

The influence of high temperatures on the zinc roasting practice has been investigated by full-scale tests in fluid bed reactors operating at temperatures from 950° to 1150°C. It was definitely shown that, throughout the range, an increase in tem perature resulted in a 2 to 3 pct increase in zinc solubility because of decreased content of zinc fer-rite and lowered sulfide sulfur. The former is attributed to thermal decomposition of ZnFe,O,, and the latter to increased oxidation rates, ad longer retention times. Data on the gveatly increased volatilization of lead, cadmium, and silver above 1000°C, are presented. A considerable fraction of the iron present in the feed was also transferred at high temperatures from the coarse roaster discharge to the flue dusts. AS part of its metallurgical complex1-3 situated in a 12,000 it Andean valley at La Oroya, Peru, Cerro de Pasco Corp. (a wholly owned subsidiary of Cerro carp.) operates a 150 short ton per day electrolytic zinc refinery. Electrolysis is carried out at a cathode current density of 65 amp per sq ft with an electrolyte content of 55 g per liter of Zn and 150 g per liter of su lf uric acid. Due to the high iron content of the marmatitic concentrate used, a large fraction—about 15 pct—of the zinc reports in the leach residues. To minimize such losses, efforts have been exerted toward improving calcine solubility. One method, as noted in the literatre,, is to retard zinc ferrite formation by decreasing the roasting temperature. Unfortunately, such a procedure tends either to reduce the roaster throughput or increase the sulfide sulfur in the calcine. Consequently, this approach was discarded in favor of experimental work in the opposite direction, i.e., high temperature roasting. Full- scale tests were promising and resulted in the granting of a patent to Cerro de Pasco carp.' After a brief account of plant equipment and operating procedure, this paper describes the tests made and attempts to assess the results obtained. GENERAL PLANT LAYOUT AND OPERATION The Roasting Plant, see Fig. 1, comprises an agglomerating plant feeding three fluid bed roasters with a combined capacity of 10,000 tons per month. The Peruvian patent rights on this process were purchased from the New Jersey Zinc Co. The concentrate, assaying: is pelletized to a -3 +14 mesh product and fed to the fluid bed roasters. The roaster exhaust gases pass through a waste heat boiler, cyclones, a fan, and an electrostatic precipitator. Approximately half of the dust collected in the cyclones returns to the pellet-izing plant as one of the binding ingredients, the remainder joins the cooled bed discharge ('overflow') and is conveyed to the grinding plant. The -35 mesh product obtained, together with the dust collected in the electrostatic precipitator constitute the feed to the leaching plant. Batch leaches are made in vessels with mechanical and air agitation, the residues are separated and washed in Burt Filters, and pumped to storage ponds. THE FLUID BED ROASTERS Two reactors are as shown in Fig. 2, and the third,' of about the same configuration, is approximately 40 pct smaller. The total grate and freeboard (just below the gas outlet) areas measure 170 and 426 sq ft respectively. The feed, continuously weighed and controlled by Merrick Weighto-meters fitted with variable speed motors, enters the reactors at the top of the expanded bed level. The coarse calcine overflows through the opposite end by

Jan 1, 1963

By E. B. Olds, B. P. Burt

The mines of the Consolidated Gopper-mines Corporation are at Kimberly, in the Robinson mining district, White Pine County, Nevada. The blanket-like ore body is a disseminated copper deposit occurring in monzonite porphyry and, in general, is thoroughly fractured, altered, and soft. Contained in the porphyry ores of the extreme westerly end of the ore body are pendants of hard garnetized limestone. A younger monzonite porphyry underlies the ore-bearing porphyry, which in turn rests on limestone and shale. Block caving is the standard method of mining. Because of the undulating top and bottom contours of the ore body, the main haulage level was selected and driven at an elevation calculated to be the most economic depth below the major tonnage sections of ore. Fig. I shows a general section of the Emma Nevada ore body taken through its long axis, which lies roughly in an east-west direction. Mine openings in either type of porphyry require heavy timbering and constant maintenance and repair, particularly in horizons at or near the ore body contact. Where the ore lies close to the haulage level, slusher hoists and scrapers are used to transport horizontally the ore to the main haulage drift (Fig. 2). For the extraction of high-lying ores, a system of branch raises is used; and the ore is mined by gravity. Slushing methods are used also on the high-lying ore-body fringes. Slusher drifts are often driven from the fringe branch raises that have already served their purpose, in order to minimize the cost of the preparatory work in mining the thinner portions of the ore body (Figs. 3 and 4). When a block of ore is developed and undercut, it is economical to mine it as rapidly as the ore will cave efficiently; and this procedure often presents safety problems because of men with equipment working in a relatively congested area. The single-track main haulage drift is about 11/2 miles long, and lateral haulage drifts are driven under the ore body at intervals determined by the height of the ore body above the haulage level. In order to minimize repair and maintenance, the

Jan 1, 1949

By James T. Waber, Allen C. Larson, Karl Gschneidner, Margaret Y. Prince

The original graphical method proposed by Darken and Gurry for predicting which elements are soluble in a given element was slightly modified and was used to predict terminal solubilities in 1455 known binary combinations. it was found that the modified Darken and Gurry method had a reliability of 61.7 pct in predicting extensive solid solubility (greater than 5 at. pct) and of 84.8pct in predicting limited solid solubility (less than 5 at. pct), an over-all reliability percentage of 76.6. Using the same experimental data, it was found that using only the simple Hume-Rothery size-effect criterion was 50.1 pct reliable in predicting extensive solid solubility, only slightly better than a purely random choice. and 90.3 pct reliable for predicting limited solid solubility, an over-all reliability percentage of 67.6. THE first rational rules for determining a priori whether two metals are not freely soluble in the solid state were announced by Hume-Rothery and coworkers.1,2 These well-known rules have been accorded a special place in metallurgical literature. Since the "electronegative" and "relative valence effect" rules of Hume-Rothery were only qualitative in nature it was difficult to use them in a quantitative analysis. The next major step was made by Darken and gurry3 and apparently went unexplored for a number of years. They prepared graphs illustrating the influence of both electronegativity and size difference on the solubility of elements in silver, magnesium, and aluminum, and they drew elliptical figures, whose maximum width was ±15 pct of the solvent radius and the maximum height was ±0.4 electronegativity units. The purpose of the present paper is to assess and compare the effectiveness of using the simple size-factor and the Darken-Gurry criteria to predict which elements will be soluble and insoluble in a given solute. In 1957, waber4 prepared Darken-Gurry plots for determining the solutes that were likely to be soluble in 6 and plutonium and introduced an inner ellipse as an aid to determining which elements should be soluble to a considerable extent. As illustrated in Fig. 1, the major axis of the outer ellipse corresponded to ±0.4 electronegativity units (OD) while the minor axis corresponded to ±15 pct of the radius of the solvent phase (OB). This simultaneous "action" of the two Hume-Rothery criteria was used to indicate which elements would have little or no solubility in the host lattice, namely those elements whose points lay outside this ellipse. An inner ellipse, "centered" over the same point of the solvent was drawn with ±0.2 electronegativity units (OC) and ±8 pct (OA) as the major and minor axes. Solutes with points lying within the inner ellipse were expected to be capable of forming extensive solid solutions with the host element. Use of this method of applying the earlier Hume-Rothery criteria was moderately successful for plutonium. For 6-phase plutonium, only one element out of the eight predicted to be extensively soluble was known to be almost insoluble, and of the sixteen elements predicted to have more restricted solubility, five were known to be essentially insoluble. The success of discerning solubility in the E phase by this method was comparable. One prediction made on the basis of this analysis was that the heavier rare earth metals, such as holmium, erbium, and thulium, should be soluble in the 6 phase, whereas the lighter rare earth elements, such as lanthanum or

Jan 1, 1963

By Harvey T. Kennedy, Charles R. Olson

In many investigations of the performance of petroleum reservoirs the assumption is made that the liquid, if below its bubble-point pressure, is at all times in equilibrium with gas. On the other hand, observations by numerous investigators have indicated that gas-liquid systems including hydrocarbon systems, may exhibit supersaturation to the extent of many hundred psi in the laboratory. Up to the present, there has been no reliable data on which ti judge the actual extent of supersaturation under conditions approaching those existing in petroleum reservoirs. The work reported here deals with observations and measurements on mixtures of methane and kerosene in the presence of silica and calcite crystals. Bubbles were observed to form on crystal-hydrocarbon surfaces in preference to the glass-hydrocarbon interface or to the body of the liquid. Statistically, it was found that the number of bubbles formed per second per square centimeter of crystal surface was a function of the supersaturation only. and the function was evaluated graphically. Supersaturations were observed up to 770 psi, under which condition bubbles formed quickly and with considerable violence. With decreasing degrees of supersaturation, the frequency of bubble formation became less, until at 30 psi supersaturation and lower, no bubbles were observed to form, even though the observation at 30 psi was continued for 138 hours. It was found that silica and calcite crystals had identical effects, within experimental error, in accelerating the formation of bubbles, and that small amounts of water and crude oil had no effect on the results. It is shown that the maximum supersaturation that can exist in a reservoir may be calculated from the data presented and from the area of the rock surface. It is also shown that the number of bubbles formed in the reservoir, in order of magni- tude, may be calculated for any rate of pressure decline imposed on the reservoir by production. The bearing of the number and distribution of bubbles on reservoir performance is discussed. INTRODUCTION A liquid system is supersaturated with gas when the amount of gas dissolved exceeds that corresponding to equilibrium at the existing pressure and temperature. The degree of super-saturation may be conveniently expressed as the difference between the bubble-point of the mixture and the prevailing pressure. Thus, if a mixture having a bubble-point of 1,000 psi at a given temperature exists in single liquid phase at 700 psi at the same temperature. it is supersaturated to the extent of 300 psi. There are many examples of high supersaturations, mostly in aqueous solutions, reported in the literature. Thus, Kenrick, Wismer and Wyatt1 showed that water may be saturated with oxygen, nitrogen or carbon dioxide at 100 atmospheres, and the pressure reduced to one atmosphere without producing bubbles immediately. When liquids are in a state of tension, they may be considered as supersaturated at least to the extent of the tension. The tensile strength of water has been reported as 30 atmospheres by Meyer,1 60 atmospheres bv Budgett. 30 to 50 atmospheres by Temperley and Chambers,4,5 200 atmospheres by Dixon6. and 223 atmospheres by Briggs.7 Vincent8,9 determined the tensile strength of a mineral oil as 45 psi. Gardescu1 maintained pressures for short times in a model reservoir at 115 psi below the bubble-point. It should be noted that the high supersaturations observed were obtained on systems carefully purified to remove particles or surfaces which might promote the formation of bubble; These "nuclei" were considered as contaminants which interfered with the determination of a property of the liquid. In

Jan 1, 1952

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

A. U. Seybolt (General Electric Research Laboratory)—The authors should be commended for adding some important information to our knowledge of the solubility of interstitial elements in metals. It is becoming increasingly evident that the effect of even traces of such elements have very far-reaching effects upon the mechanical properties of the body centered cubic metals. Those who have worked in this area know that the accurate determination of the small solid solubility limits in systems of the type reported by the authors is a quite difficult task, and it is therefore not surprising that frequently the results of different workers are not in agreement. It is instructive, and usually helpful, to plot the solubility results on log weight or atomic percent -1/T coordinates to find out if a straight line is obtained. A straight line is expected because in systems displaying solubilities of the order of 1 to 3 at. pet or less, Henry's law is usually obeyed—or at least well enough obeyed so that the deviation from linearity is not very appreciable. If Henry's law is obeyed, one canthen use the Van't Hoff Equation in the form In N = ?H/RT + C, where N is mole fraction, at. pet, or wt pet for small values, and AH is the partial molal heat of solution of the solute. R and T have the usual significance, and C is an integration constant. If one plots the reported nitrogen solubility values as indicated above, the three points fall reasonably well on a straight line. The oxygen values for the two upper temperatures fall very closely to the nitrogen values as shown in the authors' Fig. 15. However, the value at 500°C departs widely from the straight line established by the data at 1500" and 1000°C. It is, of course, true that one cannot place too much emphasis on the significance of a line established by only three points, but in the absence of reasons for anticipating deviations, data exhibiting wide departures from linearity should at least be examined closely. Fig. 16 shows the log at. pct -1/T plots for the authors Ta-O and Ta-Ndata including a solid circle point at 500°C and 1.8 at. pet for Ta-O, which is simply extrapolated from the two higher temperature points. In addition, the data of R. P. Elliott9 for Nb-O are shown. These points were picked off his curve and are not very exact, but as can be seen they line up well on a straight line. It is interesting, and probably significant, that the slope of Elliott's results is not far from those of Vaughn, et al. This is probably to be expected because one would anticipate that the partial molal heats of solution of oxyten in these two very similar metals should be not too far apart. AH for Ta-O is about -1900 cal per mol, while for Nb-O it is near -2300 cal per mol. Hence, this lends some support to the thesis that the point at 500°C for Ta-O is much too high. The data of Gebhardt and Preisedanz10 are also plotted, and it is seen that their data while lying on a linear plot, have an appreciably steeper slope. The possible reasons for this will not be discussed here except to point out that their pressure-composition data show anomalies which suggest that they may have been dealing with a different equilibrium from that being discussed. There is another consideration which would also suggest that the solubility at 500°C is lower than shown. The solubility values were obtained by the classic method of first establishing a lattice parameter-composition curve. This the authors did, and there is probably little doubt that it is quite accurate. Such a plot is generally almost error-free because it has a self-correcting feature in that any deviation from linearity makes a data point immediately suspect, and subject to confirmation. Unfortunately, this is not true with respect to the actual solubility values. These are obtained ordinarily by taking an alloy containing more solute than is soluble at some temperature and then thermally

Jan 1, 1962

By Kefton H. Teague

Olivine is a mineral containing a mixture of forsterite (Mg2SiO4) and fayalite (Fe2SiO4) in solid solution. The name olivine was first applied by Werner in 1790 (Hunter, 1941) because of the olive-green color of the mineral. Olivine is the principal component of the rock dunite, which itself is a member of the peridotite group of ultrabasic igneous rocks. European uses of the terms olivine and dunite are somewhat different than US usage. In commerce European usage defines dunite as containing 36 to 42% MgO, 36 to 39% SiO2, and loss on ignition of approximately 10%. The term olivine is used to designate a material containing approximately 85% forsterite, with a chemical composition of approximately 45 to 50% MgO, 40 to 43% Si02, 5 to 8% Fe2O3, and ignition loss of 1 to 2%. Uses The principal use of olivine is in various applications involving hot metal. Table I shows the best estimate available as to the amount of olivine consumed by various industries worldwide. In excess of 90% of world uses involve hot metal, with approximately 75% as a slag conditioner in the blast furnace production of pig iron. Approximately 15% of total olivine usage is as a special foundry sand in mold making for the brass, aluminum, magnesium, and manganese steel foundries (Schaller, 1957, 1958; Snyder, 1957; Anon., 1977). Olivine was first used as an industrial mineral in the early 1930s for a refractory material (Anon., 1970; Hunter, 1941). As a refractory raw material, olivine was first introduced in the United States as hand-cobbed, selected, shaped blocks of crude olivine. This use met with limited success. More recently, finely ground olivine blended with MgO and pressed into bricks, which are then fired, has found use in glass tank furnaces and open-hearth furnaces. Ramming or gunning mixes for basic furnace linings also utilize olivine. Olivine has been used in ladle linings with varied success. In Europe, substantial tonnages of olivine are utilized in refractory brick for night storage heaters (Anon., 1970). A limited amount of olivine has been used in the past as a fertilizer (magnesium source) and has been fused with rock phosphate to produce a magnesium phosphate as a plant food. The relatively high magnesia (MgO) content of olivine also attracted attention to it as a potential source of both magnesium compounds and as a source of metallic magnesium (Bengston, 1956; Hunter, 1941). The use of olivine as an additive in the blast furnace is relatively new, having been developed during the last decade. J.W. Currier (Private communication, 1978) describes the behavior of olivine in the blast furnace as follows: Olivine (Mg, Fe2, Si04) represents a unique lime-free source of magnesia and silica as a blast furnace charge component. Only recently has the magnesia-rich mineral been recognized as beneficial cleaner for blast furnace experiencing the problems associated with excessive alkali inputs and/or low coke stabilities. For some time it has been known that alkalis tend to recycle and accumulate in blast furnaces. In the high temperature region of volatilization the elemental alkalis formed attack the integrity of the graphite structure. This alkali attachment is enhanced when poor coke is used. Higher in the furnace stack volatile alkali cyanides condense and oxidize. This accumulation of alkalis tends to agglomerate the burden materials, producing scabs and scaffolds. These structures not only inhibit the downward movement of burden materials and the upward passage of wind, but also lead to erratic furnace performance

Jan 1, 1983

By Harlan W. Nelson, James B. Purdy

A study of data obtained during laboratory tests to determine the suitability of bituminous coals for use in residential underfeed stokers of the clinkering type has led to the following general conclusions: 1. Performance data obtained during the test furnish useful and practical information upon which to judge the performance of stoker coals. 2. Conclusions derived from the results of evaluation tests are in general agreement with use experience of the coals in the field. The method is of practical use in this regard. 3. Few direct relationships were found between data furnished by the evaluation test and determinations by standard laboratory tests. This is particularly true with regard to coke formation and clinker formation, two of the most important factors in determining the degree of satisfaction to be obtained in applications of the small underfeed stoker. It has not been the intention in this paper to prescribe this evaluation test as the best method for the evaluation of coals for use in residential stokers. That there are other test methods having similar objectives serves to point out the necessity for full-scale laboratory tests. At the present time, a standard test procedure for the evaluation of coals for use in residential stokers is not available. For the past several years a joint committee, appointed from the membership of the Residential Stoker Committee of Bitulninous Coal Research, Inc., and from the Engineer- ing and Research Committee of The Stoker Manufacturers Association, has been working to develop a standard procedure for testing and evaluating bituminous stoker coals. This procedure has been completed to the extent that it has been drawn up in tentative form. It is now planned to install the equipment in several laboratories and to run check tests, using portions of identical lots of coal, to determine the degree of reproducibility offered by the method. Completion of this standard test procedure should greatly facilitate the evaluation of coals for use in residential stokers. Acknowledgments The cooperation of coal operators sponsoring the coal evaluation tests, in granting permission to use data and results from their tests, is gratefully acknowledged. Acknowledgment is also made to Carroll F. Hardy, Chief Engineer, Appalachian Coals, Inc., for his interest and timely suggestions on the preparation of this paper. Special thanks are due to Ralph Sherman, Assistant Director, Battelle Memorial Institute, who was largely responsible for development of the evaluation procedure, for helpful suggestions and advice. References I. H. A. Sherman: The Evaluation of Coal for Use in Domestic Stokers. Univ. of Ill., Eng. Experiment Station, Circular No. 39 (1939). 2. . Q. Shotts: The Relation of Free- swelling Indexes to Other Characteristics of Some Alabama Domestic Stoker Coals. TP 2314, Coal Tech., (Feb. 1948); Trans. AIME (1948) 177, 502. 3. . J. Helfinstine and C. C. Boley: Correlation of Domestic Stoker Combustion with Laboratory Tests and Types of Fuels 11. Combustion Tests and Preparation Studies of Representative Illinois Coals. Ill. State Geol. Survey, Re1. of Zntlestigations No. 120 (19467 ) p. 35. DISCUSSION E. R. Kaiser*—AS a former fuel engineer assigned to residential stokers at Battelle, the writer has read with considerable interest the paper by Messrs. I'urdy and Nelson. It is gratifying to note that earlier test techniques have been developed and that criteria found important in the years 1935 to 1938 are still important in judging the performance of stoker coals for residential heating. The authors have plotted a number of the primary coal data singly against performance data of the stoker in an effort to establish relationships. Unfortunately, wide scattering of points usually resulted, which did not illustrate what experience generally indicates to be the case. For example, Fig 3 indicates almost no trend in the percentage of released ash converted to clinker with change in ash-softening temperature. Other factors, such as fuel bed temperatures and zones of heat release must have influenced the results. In the present state of our knowledge, we cannot explain all of the reasons why suitable stoker coals perform satisfactorily, nor why one satisfactory coal may be better than another. It would therefore

Jan 1, 1950

By H. Warlimont

Precipitation of cementite plates from carbon-rich austenite gives rise to localized formation of martensite in the matrix next to the precipitate upon quenching. The growth of this martensite is urmsually restricted. A distinct lattice relationship is found between this martensite and the cementite phase. It is concluded that the martensite is nacleated in the region of lowest carbon concentration at the austenite-cementite integace, with low-energy matching to the cementite lattice. The restriction of the growth of the martensite phase to the vicinity of the cementite plates can be explained by misfit in the austenite -martensite glissile interface and the uphill carbon gradient in the austenite. The investigation was carried out by light- and electron-microscopy and by electron-diffraction of thin foils. THE precipitation of cementite from carbon-rich austenite gives rise to a localized formation of martensite in the matrix next to the precipitate upon quenching. This behavior has been described previously by A. B. Greninger and A. R. Troiano1 for a 1.78 pct C steel ("pseudomorphic martensite"), and by A. Hultgren2 for a Fe-0.99 pct C—5.20 pct Mn steel. By measuring the axial ratio of the martensite phase,' it was found that the carbon content of this martensite was lower than that of the martensite which formed without prior partial transformation to cementite. Therefore, it was concluded that lowering of the carbon concentration in the matrix next to the precipitate raised the M, temperature locally and thus led to nucleation of martensite at the ce-mentite-austenite interface. However, the restriction of the growth of the martensite phase to the vicinity of the cementite plates cannot be explained by localized carbon impoverishment alone. Under ordinary conditions a martensite plate which has been nucleated in a favorable site can continue to grow until it encounters a physical barrier, or until it encounters a compositional barrier in the matrix, where the total free-energy change for the reaction is not negative, since it has been shown by numerous experiments that the activation energy for growth of ordinary martensite is virtually zero.' An investigation was conducted by transmission electron microscopy and electron diffraction to study this extraordinary martensite. It was expected that crystallographic in addition to compo- sitional conditions caused this abnormal mode of martensite formation. MATERIAL AND PROCEDURE An Fe-C-Mn alloy containing 1.15 pct C and 5.1 pct Mn was used for most of the experiments. For metallographic work, specimens 15 by 15 by 3 mm were used. For preparation of thin films, the initial specimen size was 15 by 15 by 0.7 mm. The heat treatment of each specimen consisted of austenitizing for 1/2hr at 1100'~ in an argon atmosphere, subsequent isothermal holding in a lead bath at one of a series of different temperatures, and, finally, quenching into brine at room temperature. For metallographic examination, the specimens were mounted in bakelite (slight tempering effects resulted from the heat in the mounting press) ground, polished, and etched in nital. Thin films for transmission electron microscopy and electron diffraction were obtained by grinding the specimens to approximately 0.2 mm thickness and subsequent electrolytical thinning. The orientation relationships were evaluated from sets of electron micrographs and selected-area electron diffraction patterns of single units of the transformation products and the adjacent matrix. RESULTS In the alloy which was used for the experiments, proeutectoid carbide precipitates over a wide tem-

Jan 1, 1962

By W. B. Gogarty, H. R. Bailey

Methods are presented for determining molecular diffusion coefficients by using data from, capillary flow experiments. These methods are based on a numerical solution (presented in a previous paper) of the partial differential equation describing the combined mechanisms of flow and diffusion. Results from this numerical solution are given and compared with the approximate analytical solution of G. I. Taylor. The numerical solution is valid over a much larger time range. These methods are applied to experimental results for the fluid pairs water-potassium permanganate solution and amyl acetate-orthoxylene. Both of these fluid pairs have approximately equal densities and viscosities. Graphical and numerical techniques are presented for deter mining diffusion coefficients from the flow data. Values obtained by these techniques are compared with values obtained by other methods. INTRODUCTION The molecular diffusion coefficient is known to be a variable in determining the amount of mixing in a miscible displacement process. The effect of molecular diffusion on dispersion in longitudinal flow through porous media -has been examined by different investigators. These investigators concluded that at low velocities of flow, the amount of dispersion is approximate1y proportional to the molecular diffusion coefficient. The influence of diffusion on fingering, channeling, and overriding has been mentioned by other investigators.4 Recent studies5,6 have been made on the effects of molecular diffusion in connection with the problem of gravity segregation. Many different methods have been developed for the experimental determination of molecular diffusion coefficients? These methods differ mainly according to boundary conditions selected and analytical procedures used. Nevertheless, all of these methods have the condition in common that the bulk fluids in which diffusion is occurring are stationary with respect to each other. In connection with a series of papers on mixing in capillary flow,8-10 Taylor suggested the use of a flow method for determining molecular diffusion coefficients. Additional studies 11-13 have been conducted on miscible displacements in capillary tubes, but the data from these studies were not used for the specific purpose of determining diffusion coefficients. The flow method proposed by Taylor results in a single value of the diffusion coefficient for the fluid pair used in the displacement experiments. This single value represents the true value for the fluid pair when the diffusion coefficient is independent of concentration. If the diffusion coefficient is a function of concentration, the single value obtained by the flow method gives an average value for the coefficient of the fluid pair. These average values are based on diffusion taking place over the entire range of concentration, i.e., from 0 per cent of one fluid to 100 per cent of that same fluid. In field applications of the miscible displacement process, gradients occur over the same range of concentration as are found in the displacements in capillary tubes. Molecular diffusion coefficients obtained from the capillary flow method should, therefore, be especially relevant to field operations. This investigation was undertaken to evaluate the feasibility of obtaining molecular diffusion coefficients from capillary -flow experiments. In making this evaluation, diffusion coefficients were first determined for two systems from data obtained in capillary flow experiments. These values of the diffusion coefficient were then compared to values obtained by other methods. MIXING IN CAPILLARY FLOW—THEORETICAL The theoretical basis for determining molecular diffusion coefficients from capillary flow experiments is the partial differential equation relating the mechanisms of flow and diffusion. For the case of laminar flow and with a fluid pair having equal densities and viscosities, the equation is given by