CONTENTS PAGE Rae, Colin C.-A Possible Origin of Oil. Discussed by S. Linker, Colin C. Rae... 2 Cottingham, Kenneth.-Subsurface Conditions on Portion of Arches Fork Anticline. Discussed by David B. Reger 6 Moyer, W. Irwin.-Time to Pay Out as a Basis for Valuation of Oil Properties. Discussed by H. J. Smith 9 Pogue, Joseph E.-Future Demands on Oil Industry of United States. Discussed by James O. Lewis 11 J. J. Walsh.-Coa-lmine Ventilation. Discussed by W. B. Daly, J. J. Walsh, R. R. Sayers, H. H. Stock, George S. Rice, James W. Paul, D. Harrington, T. D. Thomas 15 Longyear, Robert Davis.-Diamond-drill Sampling Methods. Discussed by Ira B. Joralemon, J. J. Rutledge, E. C. Harder 19 Joralemon, Ira B.-Sampling and Estimating Disseminated Copper Deposits. Discussed by J. Parke Channing, John E. Hodge, E.E. Hunner, B. B. Gottsberger, W. Y. Westervelt, W. O. Hotchkiss 20 Boericke, W. F.-Sampling and Estimating Zinc and Lead Orebodies in Mississippi Valley. Discussed by J. Parke Channing, Arthur Thacher 24 Daly, W. B. and Linforth, F. A.-Organization of Mine Sampling at Anaconda. Discussed by George A. Packard, W. B. Daly, B. B. Gottsberger 25 Norris, E. M. and Rahilly, H. J.-Mine Fires. Discussed by R. Dawson Hall, W. B. Daly, Frank Haas, D. Harrington, Robert E. Tally 26 Raymond, R. M.-Safety Practice for Hoisting Ropes. Discussed by B. F. Tillson, Graham Bright, Rudolph Kudlich, J. F. Howe, Robert Peele, H. G. Davis. 30 Howe, J. F.-Use of Wire Rope in Mining Operations. Discussed by Horace F. Lunt, J. F. Howe, B. F. Tillson 36 Tanner, W. N., and Jaccard, F. C.-Wire Rope and Safety in Hoisting at Butte Mines. Discussed by Horace F. Lunt, W. B. Daly, C. L. Colburn, William Kelly, Robert Peele, B. F. Tillson, Graham Bright, Charles E. Locke 38 Richardson, A. S.-Ventilation of Butte Mines of Anaconda Copper Mining Co. Discussed by D. Harrington, Chas. A. Mitke 42 Stuart, Charles E.-Storage-battery Locomotive as Applied to Mine Haulage. Discussed by Howard N. Eavenson, Charles E. Stuart, William Kelly, Arthur Thacher, W. H. Patton, Graham Bright 45 Woodward, C. D.-Electric Haulage Systems in Butte Mines. Discussed by William Kelly, Graham Bright, Howard N. Eavenson, C. E. Arnold, Gerard B. Rosenblatt, K. A. Pauly 47 Harrington, D.-Efficient Ventilation of Metal Mines. Discussed by R. E. Simpson 52 Otagawa, Masayuki.-Mining Methods at the Ashio Copper Mine. Discussed by Horace V. Winchell, D. W. Brunton 52 Stoek, H. H. and Clagett, Thomas H.-Coal Mining Methods. Discussed by P. D. Browning, G. L. Cox, Erskine Ramsay, Frank Haas, George S. Rice.

Jan 6, 1922

By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By M. J. Mullikin, J. B. Conway

Several different equation forms were studied to determine the extent to which each particular equation type yielded an accurate representation of a given set of first-stage creep data. Specially developed least-squares computer programs were employed to obtain unique solutions for the creep-equation constants. In studies of creep data for lead at 14.5"C, nickel at 70OCC, and arc-cast tungsten at 2400°C consistently good representations were afforded by a third-degvee polynomial in t113. Other effective correlations were obtained with the Andrade, Cottrell-Aytekin, and de Lacombe equations along with a third-degree polynomial in t112. A newly proposed creep equation involving a hyperbolic-sine term in t1'3 was also found to yield very satisfactory results. This appears to be the first use of such a functional relationship in the analysis of transient creep behavior. In general, the deformation behavior of a material subjected to a tensile load is described in a strain-time plot. Experiments have shown that, following the instantaneous elongation which results on loading, the instantaneous slope (i.e., creep rate) of the strain-time curve decreases gradually with time and approaches what appears to be a constant value. Equations, therefore, which are proposed to provide an analytical representation of such first-stage or transient creep behavior must be consistent with these observations. In other words, at time zero, these equations must yield a finite deformation value corresponding to the elongation on loading. Furthermore, the first derivative of these equations must exhibit a fairly high although finite value at time zero, and then values which decrease with time. It is also preferable, in general, that the derivative eventually assume a constant value at high time values. Although many studies of first-stage creep behavior have been made and numerous equation forms have been proposed for expressing this type of deformation behavior, it is still not possible to state with any assurance which functional relationship will be adequate for a given set of measurements. Parabolic relationships have been employed most extensively although logarithmic expressions have been shown to be applicable in some instances. Combined forms1 have been studied in considerable detail and have on occasion been found to be very effective. One such expression is that of iXndradea and involves a modified parabolic expression: where 1 is the instantaneous length, lo is the length immediately following load application, t is the time, and p and k are constants. Another combined form has been proposed by weaver3 as follows: where E is the instantaneous strain, is is the linear creep rate, t is the time, and a and b are constants.

Jan 1, 1967

By John R. Low

A number of cases of low-temperature, intergranu2ar brittle fracture of metals containing small amounts of certain impurities, have now been identified. Some degree of understanding of this phenomenon exists for the simpler binary systems of a metal and a single impurity, but the profound effects of other impurities and alloying elements in modifying this type of behavior remain unexplained. Current research in this area is reviewed and some of the newer techniques of investigation which should make possible a more quantitative study of the structure and composition of grain boundaries in impure metals are described. To indicate the subject matter of this lecture, we may begin by reviewing the experimental observations concerning low-temperature intergranular brittleness in impure metals, particularly those examples in which the embrittlement appears to result from what has been called "equilibrium grain boundary segregation."' These are the systems in which it has been impossible, at least up to now, to detect the presence of any second phase film at the brittle interfaces. When second phase films are present they are usually readily detectable by fractographic methods, often appearing as epitaxial films in geometric or dendritic patterns. An example is shown in Fig. 1 for the case grain boundary carbides in a sensitized stainless steel which failed by intergranular brittle fracture at 78?k2 In contrast to this type of embrittlement there are numerous examples of low-temperature intergranular embrittlement in which the fractographs are essentially featureless, for example, that of an oxygen-embrittled iron shown in Fig. 2. The only second phase particles visible are the small, widely separated, round oxide particles typical of the bulk material. The fracture surface is extremely smooth and the fracture path appears to follow the intergranular interface without deviation. This type of fractograph also implies that crack propagation has occurred without plastic deformation at the crack tip, since localized slip or twinning ahead of the crack would be expected to distort the interface and be readily visible in the fractograph. Such indications are occasionally seen in these fractographs, but are not characteristic. A second example of this type of fractograph is shown in Fig. 3, which is from a temper-embrittled, carbon-free, Fe-Cr-Ni alloy containing Sb, broken at 1OO?C.3 The similarity to the oxygen embrittled iron case will be apparent. In the case of the temper embrittled Cr-Ni ferrite containing antimony, it is possible to remove the embrittlement by suitable thermal treatment. The grain boundaries may then be examined by thin film transmission in the electron microscope for the material in both the nonembrittled condition and in the embrittled condition. Two boundaries are shown in dark-field transmission in Fig. 4, one in the nonembrittled

Jan 1, 1970

By F. E. Buch

THE Smelter is designed for a production capacity of 10,000 short tons of blister copper per month, when operating on the present concentrate grade. The Smelter lay-out is shown in Fig I. The major units of equipment comprise two reverberatory furnaces, three 13 by 30 ft Peirce-Smith converters, two straight line casting machines, one being served by a 13 by 30 ft holding furnace and the other by a ladle tilting quadrant, two converter ,aisle cranes and two converter blowers. The plant is compact and the general arrangement of standard gauge railway tracks and conveyor belts provides for a smooth flow of incoming materials and metallurgical products. Concentrate is received by conveyor belts and fluxes in standard railway trucks. The local track system is covered by an electric trolley locomotive. The Smelter treats a wet (10 pct moisture) flotation concentrate containing approximately 53 pct total copper and 0.9 pct oxide copper. The predominating minerals are chalcocite, chalcopyrite and bornite accompanied by small quantities of malachite and cuprite. The gangue is highly siliceous and requires limerock as a flux. Metallurgy would be straightforward were it not for the necessity for eliminating k bismuth which occurs as an impurity in the ore along with the copper. Directly or indirectly most of the Smelter problems can be traced to the necessity for bismuth removal. Copper recovery, based on new copper treated, averages 97.5 pct. GENERAL DESCRIPTION Flotation concentrate, containing to pct moisture, is conveyed from the filter plant to the smelter storage bins by conveyor belts, the material being weighed in transit by a revolving drum type of weigh-hopper manufactured by Samuel Denison and Son, Ltd. The weigher consists of a steel drum with dished ends carried on a horizontal shaft and rotated by an 8 hp squirrel-cage motor through a worm and spur reduction gear. A feed mouth in the drum permits of filling and discharging. The whole unit is supported on a framework resting on weighing levers, which in turn connect to transfer levers, thence to an indicator of the steelyard type situated 16 ft from the centre line of the drum. The indicator is of the "Denison" patent equilibrium controlled ticket stamping type, insuring mistake-proof records by a combination of electrical and mechanical movements which prevent the operator from printing until the cover enclosing the steelyard is closed and until the poise-weights have been set correctly to the weight of the hopper and contents. The machine is capable of weighing 30 short tons at a time but the usual load is 28 tons. After obtaining the gross weight the drum is rotated and discharged into a receiving bin situated below it. The empty drum is weighed and the net weight re-

Jan 1, 1947

By Ursula E. Wolff

Il.lechanica1 twins have been observed in brigsten single crystals of a variety of axial orientations defornzed at room temperature in tension or bending. The twins formed near the final fracture and were up to 3 p thick. The twinning plane was always of the type (113). Twinning at room ternperature occurred only after considerable prior slip. Twins usually preceded fracture and nucleated cracks. The crack surfaces often alternated between a (001) plane and the twin interfaces. Secondary twins could also nucleate from cracks. In the absence of twinning tensile samples failed by shear; twinned samples failed by cleavage. On the assumption that observed sudden load drops in the stress-strain curves are associated with twinning, a critical resolved stress for twinning of 60, 000 to 65, 000 psi was calculated. MeCHANICAL twinning has been observed in iron and iron alloys at low temperature by a number of investigators.'-7 Similarly, for high-purity tungsten, twinning has been reported for deformation temperatures below 211°K.8-10 In W-Re and Mo-Re alloys, 20 pct Re was determined as the lower limit for twin formation at room temperature." Since the twins are generally very narrow, they are usually identified only by etching techniques. The expected (112) habit plane has always been confirmed by angular analysis of the surface traces. Recently, however, a complete identification by X-ray analysis has been performed on twins in a Mo-35 pct Re alloy.12 During an investigation of the deformation charac- teristics of tungsten single crystals, twins were revealed in tensile and bend samples deformed at room temperature. This paper deals with the conditions for such twinning and the relation of twinning to fracture. EXPERIMENTAL PROCEDURE Tungsten single crystals, 1/8 in. in diam, of a variety of axial orientations were grown from un-doped material by four-pass electron-beam zone melting. A representative analysis is given in the following table: From these crqstals, tensile samples with 1 in. gage lengths were made by surface grinding, leaving shoulders for gripping. The diameter after grinding was 0.082 in. The distorted surface layer was then removed by ele1:trolytic polishing which reduced the diameter of the gage length to 0.080 in. Tensile tests were carried out at room temperature in an Instron machine under two different sets of conditions: a) Rigid mounting; strain rate 0.02 in. per in. per min. b) Gimbal mounting; strain rate 0.002 in. per in. per min up to a total strain of approximately 0.2 pct, then 0.01 in. per in. per min to fracture. Stress axis and growth direction coincided in all samples and are subsequently called orientation.

Jan 1, 1962

By E. A. Gulbransen, J. W. Hickman

IN a previous paper1 the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300° to 700°C. except for copper, where the range selected was 100° to 500°C. The results of these studies were presented in graphical form as existence diagram, of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviations in lattice parameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: I The existence diagrams of various alloys. [2.] The effect of the structure of the [ying] metal on the existence diagram of Iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body- centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K42B1 Nichrome V, Hipernik, Inconel, Stellite " 21," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1946

By H. W. Maynor, C. J. McHargue

DURING the course of an investigation of materials suitable for use as thermocouples at elevated temperatures by one of the authors, several nlolybdenum-rhenium alloys were prepared. Micrographs of an annealed alloy containing 25 pct Re (intended concentration; analysis not obtained) showed a number of twins, Fig. 1, suggesting a face-centered cubic structure. This note reports the structure and recrystallized wire texture of an alloy containing 25 wt pct Re. Alloys were prepared from 99.9 pct Mo (Fansteel Metallurgical Corp.) and rhenium obtained from the University of Tennessee (purity unreported). Powders were combined and briquetted at 56,000 psi and sintering was carried out at 2400°C for 5 hr in vacuum. Ingots so prepared were swaged at 982.2" to 1037.8oC into wires 0.036 in. diameter, a reduction in diameter of 85.6 pct. These wires were vacuum-annealed 1 hr at 2000°C. A North American Philips 114.59 mm powder camera and nickel-filtered copper radiation were used for structure determination. For the texture determination a Laue-type camera was used with zirconium-filtered molybdenum radiation and, because of the high background, aluminum foil was mounted next to the film. Exposures were taken with the wire perpendicular to the X-ray beam and tilted by 10". It was found that the X-ray pattern could be indexed on the basis of a face-centered cubic structure. Because of difficulties associated with obtaining a good X-ray pattern for this material, accurate parameter determinations were not made. An indicated parameter value of 3.70A was obtained. The X-ray data are given in Table I. The annealed wire texture was observed to be a sharp [111] texture. The spread about this fiber axis was k8" at the surface of the 0.036 in. wire. The annealed wire textures of aluminum have been reported as retention of the [Ill] deformation texture for anneals below 500°C and a new [1121 texture for anneals above 600°C.1 In copper wires, with a [Ill] plus [loo] deformation texture, results indicate a retention of this texture for annealing at lower temperatures and new components or the disappearance of components for annealing at higher temperatures.' The presence of the strong [I111 texture in the molybdenum-rhenium alloy after a 2000 °C anneal suggests that the deformation texture was the same. Acknowledgment The wires used in this study were prepared and heat-treated at the Institute for Atomic Research, and Ames Laboratory, Iowa State College, and the authors wish to express their thanks to the Institute for allowing the use of the material and permission to publish the results.

Jan 1, 1954

By S. Vela, R. M. McKinley, L. A. Carlton

Johnson et al. have described a new well-testing technique that measures formation flow properties between wells.' The technique, called pulse-testing, requires a sequence of rate changes in the flow at one well and measzcrement of the re.rulting pressure changes at an adjacent well with a very sensitive differential pressure gauge. This paper describes an extensive application of the technique in a producing oil field. Pulse-tests on 28 of 45 possible well pairs in the field provided a picture of the areal distribution of reservoir hydraulic diffusivity, trans-missibility and storage. The primary objective in presenting these data is to demonstrate the potential of the methcid for reservoir description. A second objective is to show in three ways the qualitative and quantitative accuracy of reservoir parameters determined from pulse-tests: (I) pulse-test data show a nonuniformity in the field, closely correlating with the oil-water distribution as given by production data: (2) pulse-test values for permeability are comparable with core va1ue.s; and (3) perhaps most important, the field responds to a conventional interference test in the manner in which pulse-test data predict it should. The pulse-testing technique by Johnson et al.' is an ideal source of data for purposes of reservoir description, for it provides a measurement of formation storage S = +ch, hydraulic diffusivity 91 = k/+cp and transmissibility T — This paper describes an application of this method in a producing oil field. Results were analyzed to give numerical values for the parameters 7, T and S. These values were compared with oil-water production data (for the effect of fluid saturation), with core data and with data from an interference test. The reservoir in which the pulse-test survey was run is the result of a structural trap formed by a fault along the east side of a north-south trending anticline. A down-structure aquifer providcs a natural flank water drive for the pool. The producing formation is a dolomitic lime- stone having mainly vugular permeability; the formation oil has a gravity of 29" API with negligible dissolved gas. The field contains 19 wells, all on pump, arranged on 40-acre spacing along the top of the anticline. Fig. 1 shows the location of all these wells except two at the south end of the field. The dashed line on the right-hand side of the figure represents the approximate location of the fault with respect to well positions. Pulse-Test Survey and Analysis of Data A pulse-test requires a pulsing well and a responding well. In the field, changes were made in the rate of flow at the pulsing well by stopping and starting the pump periodically and measuring the corresponding pressure

Jan 1, 1969

By C. E. Sims

The carbon-oxygen reaction without doubt is the basic reaction in steelmaking. It is important on several counts: In the first place, carbon is the element that distinguishes steel from iron. It is the principal element controlling properties, and its control is of prime concern. Although the principal objective of the carbon-oxygen reaction is to oxidize excess carbon, the accompanying boil should not be underrated. The mechanical agitation, stirring, and mixing resulting from the boil are so useful in the distribution of heat and in promoting uniformity of composition in the bath that, were it not a natural accompaniment of the carbon-oxygen reaction, it is probable that something would have to be invented to replace it. The open-hearth operation, for example, with the bath heated from above by radiation, would be impracticable without the carbon boil. The electric-arc furnace is somewhat less dependent on it, but every melter knows how much easier it is to gain temperature with minimum damage to refractories during the boil than with a dead bath The motor action of the induced current of the induction furnace makes the carbon boil unnecessary but even there a severe oxidation has been found useful in giving greater freedom from porosity in certain steels. The quantitative aspects of the carbon-oxygen reaction have been given considerable attention by a large number of investigators, and the principles of physical chemistry have played an important part in these studies. Physical chemistry is the science of the mechanics and mathematics of chemical reactions. It is possible to study the mechanisms of reactions in a qualitative manner writhout reference to mathematics and thus obtain valuable concepts as to the manner in which the wheels go around. When it is desired to express quantitative relations in these reactions, however, resort to mathematics is not only convenient but necessary. Mathematics may also be regarded as the shorthand language of physical chemistry. A basic relation whose description requires numerous words may be expressed very simply by a mathematical formula or equation. A good example of this is the equilibrium constant for a chemical reaction. Expressed verbally, it is: When a chemical reaction has reached a condition of equilibrium, the Product of the concentration of the reacting substances on one side of the equation, divided by the product of the concentration of the reacting substances on the other side, gives a quotient that is a constant at constant temperature For the carbon-oxygen reaction C + O ^ CO this is expressed simply as % C X % O -%co where K (from the German Konstant) is the equilibrium constant for the reaction. Although mathematics is such a necessary and useful tool, it is also a potential pitfall. Mathematics in itself is an abstract science, which is not inhibited by consideration of mechanisms or materials.

Jan 1, 1948

By C. E. Sims

The carbon-oxygen reaction without doubt is the basic reaction in steelmaking. It is important on several counts: In the first place, carbon is the element that distinguishes steel from iron. It is the principal element controlling properties, and its control is of prime concern. Although the principal objective of the carbon-oxygen reaction is to oxidize excess carbon, the accompanying boil should not be underrated. The mechanical agitation, stirring, and mixing resulting from the boil are so useful in the distribution of heat and in promoting uniformity of composition in the bath that, were it not a natural accompaniment of the carbon-oxygen reaction, it is probable that something would have to be invented to replace it. The open-hearth operation, for example, with the bath heated from above by radiation, would be impracticable without the carbon boil. The electric-arc furnace is somewhat less dependent on it, but every melter knows how much easier it is to gain temperature with minimum damage to refractories during the boil than with a dead bath The motor action of the induced current of the induction furnace makes the carbon boil unnecessary but even there a severe oxidation has been found useful in giving greater freedom from porosity in certain steels. The quantitative aspects of the carbon-oxygen reaction have been given considerable attention by a large number of investigators, and the principles of physical chemistry have played an important part in these studies. Physical chemistry is the science of the mechanics and mathematics of chemical reactions. It is possible to study the mechanisms of reactions in a qualitative manner writhout reference to mathematics and thus obtain valuable concepts as to the manner in which the wheels go around. When it is desired to express quantitative relations in these reactions, however, resort to mathematics is not only convenient but necessary. Mathematics may also be regarded as the shorthand language of physical chemistry. A basic relation whose description requires numerous words may be expressed very simply by a mathematical formula or equation. A good example of this is the equilibrium constant for a chemical reaction. Expressed verbally, it is: When a chemical reaction has reached a condition of equilibrium, the Product of the concentration of the reacting substances on one side of the equation, divided by the product of the concentration of the reacting substances on the other side, gives a quotient that is a constant at constant temperature For the carbon-oxygen reaction C + O ^ CO this is expressed simply as % C X % O -%co where K (from the German Konstant) is the equilibrium constant for the reaction. Although mathematics is such a necessary and useful tool, it is also a potential pitfall. Mathematics in itself is an abstract science, which is not inhibited by consideration of mechanisms or materials.

Jan 1, 1948

By J. E. Burke

Recent investigations have elucidated many of the phenomena of the grain growth process, but have also revealed some conflicting and unexplained results. Beck and his co-workers 1,2,3 have shown that grain growth continues with continued heating at one temperature until the average grain size approaches the thickness of the specimen. Plotting the logarithm of the average grain diameter, D, against the logarithm of the annealing time, t, they find the straight line relationship given by the equation: D = Ktm [,] with possible small deviations at short annealing times. K and n are constants at constant temperature. On the other hand, Wa1ker4 finds that, in alpha brass) the rate of growth falls off more rapidly than indicated by Eq i after long annealing, so that an equilibrium grain size is approached. Burke5 showed, using Walker's data, that time and temperature for grain growth are apparently related through an activation energy, H, according to the relationship: ] where h and tz are the annealing times necessary for the average grain size to increase from Do to D at temperatures T1 and T2 and R is the gas laws constant. In the case quoted, H had the value 60,000 cal per mol. The apparent validity of this relationship, at least up to 700°C, and the approximate value of H were later confirmed by Beck3 The results obtained by Beck Kremer, Demer and Holzworth2 for aluminum and aluminum-magnesium alloys could not be satisfied by such a relationship, since the slope of the isothermal curves increased with increasing temperature. These data indicate and Beck, Holzworth and HuV ater demonstrated expcrimentally that the only apparent factor controlling the rate of grain growth at constant temperature is the grain size. While many of the phenomena have been elucidated, a reasonably quantitative explanation of the process is lacking. There exists uncertainty even as to the primary driving force for grain growth, although there is a considerable body of indirect evidence that the interfacial energy of the grain boundary is responsible.7,8,io Making implicit use of this assumption, several authors14,16 have pointed out that grain boundaries should migrate toward their center of curvature. Harker and Parkerg have advanced this concept furthest, and show that one can expect grain boundary migration to occur only when the grain faces are curved, or when they meet at non-equilibrium angles. When the face is curved toward a grain A, for example, the atoms in the surface of grain B, on the other side of the boundary7 are on the average more surromded by the atoms of their lattice than the atoms on the surface of grain A. Because of thermal motion, the atoms at the interface will sometimes be attached to grain A and

Jan 1, 1949

By W. R. Hibbard

Although extensive pole figure studies have been reported by Brick1 and others2,3 showing preferred orientations in rolled and annealed 70-30 alpha brass, and by Hermann and Sachs4 in 70-30 alpha brass cups, comparatively little information has been published on textures in drawn 70-30 alpha brass tubes. Crampton5 reported a (110) , [111] texture in drawn brass tubes based on selected individual X ray photograms following the method of Norton and Hiller,6 but the extent and ease of developing this texture and the annealing texture have not been reported and pole figures of these structures were not found in the literature. The present investigation was further stimulated by the possible influence of textures on the mercury stress-corrosion cracking of brass tubes. According to Snoek,7 iron-nickel alloy sheet with a strong cubic texture was more resistant to corrosion than a randomly oriented sheet. Crampton5 reported that single crystals of 70-30 alpha brass drawn into tubes did not crack after 24 hr in a standard mer-curous nitrate test. Edmunds12 found that single crystals of 70-30 alpha brass did not crack in a standard mercurous nitrate test but did crack when subjected to ammoniacal vapor. Wasserman11 reported a similar failure of a single crystal of brass in ammonia. A tube with a strong texture might approach single crystal behavior and tend to resist mercury cracking if the differences in orientation between adjacent grains were sufficiently slight. Preparation OF Specimens Crampton's5 tubes drawn 28 pct reduction in area developed a slight degree of preferred orientation while in tubes drawn 48 pct it was more marked. Based on this information, in order to obtain specimens with markedly different degrees of preferred orientation but with the same final draw, two sets of 70-30 alpha brass tubes were made following the mill schedules shown in Table I. The final draw involved a large reduction in outside diameter, and a ratio of reduction in area to reduction in outside diameter similar to that reported by Crampton,5, 10 to cause mercury cracking of brass tubes. The brass contained 71.31 pct copper, 0.01 pct lead, 0.01 pct iron and zinc by difference. Determination of Pole Figures A 6-in. length from each tube was rotated rapidly by an electric stirrer in 25 pct nitric acid until the gauge was reduced to 0.003-0.005 in. The tubes were carefully cut longitudinally and the walls gently flattened. They were further etched in 25 pet nitric acid to 0.0015 in. thickness and (111) pole figures were determined using copper K-alpha radiation in the manner described by Brick.' The three general types of pole figures

Jan 1, 1949

By W. R. Hibbard

Although extensive pole figure studies have been reported by Brick1 and others2,3 showing preferred orientations in rolled and annealed 70-30 alpha brass, and by Hermann and Sachs4 in 70-30 alpha brass cups, comparatively little information has been published on textures in drawn 70-30 alpha brass tubes. Crampton5 reported a (110) , [111] texture in drawn brass tubes based on selected individual X ray photograms following the method of Norton and Hiller,6 but the extent and ease of developing this texture and the annealing texture have not been reported and pole figures of these structures were not found in the literature. The present investigation was further stimulated by the possible influence of textures on the mercury stress-corrosion cracking of brass tubes. According to Snoek,7 iron-nickel alloy sheet with a strong cubic texture was more resistant to corrosion than a randomly oriented sheet. Crampton5 reported that single crystals of 70-30 alpha brass drawn into tubes did not crack after 24 hr in a standard mer-curous nitrate test. Edmunds12 found that single crystals of 70-30 alpha brass did not crack in a standard mercurous nitrate test but did crack when subjected to ammoniacal vapor. Wasserman11 reported a similar failure of a single crystal of brass in ammonia. A tube with a strong texture might approach single crystal behavior and tend to resist mercury cracking if the differences in orientation between adjacent grains were sufficiently slight. Preparation OF Specimens Crampton's5 tubes drawn 28 pct reduction in area developed a slight degree of preferred orientation while in tubes drawn 48 pct it was more marked. Based on this information, in order to obtain specimens with markedly different degrees of preferred orientation but with the same final draw, two sets of 70-30 alpha brass tubes were made following the mill schedules shown in Table I. The final draw involved a large reduction in outside diameter, and a ratio of reduction in area to reduction in outside diameter similar to that reported by Crampton,5, 10 to cause mercury cracking of brass tubes. The brass contained 71.31 pct copper, 0.01 pct lead, 0.01 pct iron and zinc by difference. Determination of Pole Figures A 6-in. length from each tube was rotated rapidly by an electric stirrer in 25 pct nitric acid until the gauge was reduced to 0.003-0.005 in. The tubes were carefully cut longitudinally and the walls gently flattened. They were further etched in 25 pet nitric acid to 0.0015 in. thickness and (111) pole figures were determined using copper K-alpha radiation in the manner described by Brick.' The three general types of pole figures

Jan 1, 1949

(The paper by L. H. De Wald-Tech. Pub. No. 429 was presented at the Boston meeting, September, 1931.) W. A. SCHEUCH, Chicago, Ill.-Since starting up our Hawthorne copper wire plant we have found that wire bars from certain suppliers perform quite differently from those of other suppliers. In attempting to evaluate these bars, we made cross-sections, and in making these cross-sections we found considerable variation in the crystal structure. Indications were that there was some preference in the type of crystal structure. In attempting to find the reason for that we discussed it with the various producers and-also reviewed the literature. Mr. DeWald was assigned to determine the various factors that enter into copper wire bar crystal structure, on the basis that the product was a horizontally cast wire bar of practically identical composition and of recognized good composition for the present quality product sold in the market. Mr. DeWald has asked me to say that he should have made reference to Mr. Dalzell's paper on a theory concerning gases in refined copper. D. K. CRAMPTON, Marion, Conn. (written discussion).-Mr. DeWald has set forth an interesting and thorough exposition of the factors controlling macrostructure of this material. It is particularly interesting to us as it somewhat parallels work we have done on macrostructure of round copper billets for piercing into tubes. Our findings as to the effect of the several variables on macrostructure check Mr. DeWald's. The general principles underlying the two are precisely the same. The fact that we worked with copper deoxidized with phosphorous instead of tough-pitch copper, and round billets cast on end instead of wire bars, does not influence the results. We have found that round billets cast so as to produce large radial grains have greater soundness and density than those with a fine macrostructure. Further, and more important, we have found that the billets with large radial grains show markedly different performance on piercing from those having a fine equiaxed structure. With a given temperature of billet and adjustment of piercing machine, the coarse-grained material requires appreciably lower power for piercing and goes through the operation inn appreciably less time. These two differences are of sufficient commercial importance to warrant exercise of great care in maintaining the coarse structure. It seems probable that much the same phenomenon should hold in the hot rolling of tough-pitch wire bars. We would expect that, other things being equal, the coarse-grained wire bars would roll more readily and require less power than fine-grained ones. Moreover, we believe the differences in initial structure of the wire bars should be largely eliminated in the hot rolling process and during the subsequent drawing and annealing, of wire would be entirely eradicated.

Jan 1, 1932

By Walter R. Hibbard

ALTHOUGH extensive pole figure studies have been reported by Brick1 and others2,3 showing preferred orientations in rolled and annealed 70-30 alpha brass, and by Hermann and Sachs4 in 70-30 alpha brass cups, comparatively little information has been published on textures in drawn 70-30 alpha brass tubes. Crampton5 reported a (110), [III] texture in drawn brass tubes based on selected individual X ray photograms following the method of Norton and Hiller,6 but the extent and ease of developing this texture and the annealing texture have not been reported and pole figures of these structures were not found in the literature. The present investigation was further stimulated by the possible influence of textures on the mercury stress-corrosion cracking of brass tubes. According to Snoek,7 iron-nickel alloy sheet with a strong cubic texture was more resistant to corrosion than a randomly oriented sheet. Crampon5 reported that single crystals of 70-30 alpha brass drawn into tubes did not crack after 24 hr s in a standard mercurous nitrate test. Edmunds 12 found that single crystals of 70-30 alpha brass did not crack in a standard mercurous nitrate test but did crack when subjected to ammoniacal vapor. Wassermann reported a similar failure of a single crystal of brass in ammonia. A tube with a strong texture might approach single crystal behavior and tend to resist mercury cracking if the differences in orientation between adjacent grains were sufficiently slight. PREPARATION OF SPECIMENS Crampton's5 tubes drawn 28 pct reduction in area developed a slight degree of preferred orientation while in tubes drawn 48 pct it was more marked. Based on this information, in order to obtain specimens with markedly different degrees of preferred orientation but with the same final draw, two sets of 70-30 alpha brass tubes were made following the mill schedules shown in Table I. The final draw involved a large reduction in outside diameter, and a ratio of reduction in area to reduction in outside diameter similar to that reported by Crampton,5,10 to cause mercury cracking of brass tubes. The brass contained 71.31 pct copper, 0.01 pct lead, 0.01 pct iron and zinc by difference. DETERMINATION OF POLE FIGURES A 6-in. length from each tube was rotated rapidly by an electric stirrer in 25 pct nitric acid until the gauge was reduced to 0.003-0.005 in. The tubes were carefully cut longitudinally and the walls gently flattened. They were further etched in 25 pct nitric acid to 0.0015 in. thickness and (III) pole figures were determined using copper K-alpha radiation in the manner described by Brick.1 The three general types of pole figures

Jan 1, 1947

By Donald L. Katz, Leo B. Bicher

A correlation is presented for predicting the viscosities of light paraffin hydrocarbon mixtures such as natural gases for temperatures from o° to 4o0°F. and for pressures fro1 atmospheric to I0,000 lb. per sq. in. The correlation is based on the viscosity data for the methane-propane system and requires only a knowledge of the molecular weight of the naturaI gas. The viscosities of natural gases reported in the literature up to 2500 lb. were reproduced by the correlation with an average deviation of 5.8 per cent. Introduction The viscosity of a natural gas is required whenever calculations are made of the pressure drop that occurs while the gas flows through pipes or porous media. Methods of predicting the viscosities of gases at the present operating pressures are not available. This paper presents a simple method of predicting the viscosity of a natural gas in the single-phase region from its molecular weight, temperature, and pressure. Viscosity oF Methane-propane Mixtures The viscosity of methane, propane, and four of their binary mixtures, 20,40, 60, and 80 mol per cent, have been determined for pressures from 400 to 5000 lb. per sq. in. and temperatures from 77" to 437 F., with an experimental accuracy of 3.2 per cent.2 The apparatus used in the investigation was a modification of that employed in previous studiesaJ4 on the viscosity of normal paraffin hydrocarbons. It consists of a viscosimeter of the rolling-ball, inclined-tube type,5>k7 with auxiliary equipment for making up and charging binary mixtures into the viscosimeter.~ The viscosity data on the methane-propane mixtures have been plotted as a function of molecular weight with lines of constant pressure, charts of constant temperature in Figs. I to 3. These charts are extrapolated at temperatures below 77°F. and at pressures above 5000 lb. per sq. inch. Prediction OF Viscosity from Molecular Weight of a NaturaI. Gas At atmospheric pressure the viscosity of light hydrocarbon gases increased with increased temperature, contrary to the change of viscosity of liquids with temperature. The atmospheric viscosities of the normal paraffin hydrocarbons have been determincd by several investiga-tors 3,4,9,10,12,15,16,17,19 and are plotted in Fig. 4 as a function of molecular weight, with extrapolation to 896'F. and to 220 molecular weight. Data for isopentane and normal pentane show less than 2 per cent difference in viscosity, indicating that Fig. 4 can be used for isomeric parafin hydrocarbons with an accuracy of approximately 2 per cent. Trautz and Sorg'7 determined the atmospheric viscosities 01 methane-propane mixtures and showed that they are proportional to the molecular weight. The viscosities of these mixtures

Jan 1, 1944

By Leo B. Bicher, Donald L. Katz

A correlation is presented for predicting the viscosities of light paraffin hydrocarbon mixtures such as natural gases for temperatures from o° to 4o0°F. and for pressures fro1 atmospheric to I0,000 lb. per sq. in. The correlation is based on the viscosity data for the methane-propane system and requires only a knowledge of the molecular weight of the naturaI gas. The viscosities of natural gases reported in the literature up to 2500 lb. were reproduced by the correlation with an average deviation of 5.8 per cent. Introduction The viscosity of a natural gas is required whenever calculations are made of the pressure drop that occurs while the gas flows through pipes or porous media. Methods of predicting the viscosities of gases at the present operating pressures are not available. This paper presents a simple method of predicting the viscosity of a natural gas in the single-phase region from its molecular weight, temperature, and pressure. Viscosity oF Methane-propane Mixtures The viscosity of methane, propane, and four of their binary mixtures, 20,40, 60, and 80 mol per cent, have been determined for pressures from 400 to 5000 lb. per sq. in. and temperatures from 77" to 437 F., with an experimental accuracy of 3.2 per cent.2 The apparatus used in the investigation was a modification of that employed in previous studiesaJ4 on the viscosity of normal paraffin hydrocarbons. It consists of a viscosimeter of the rolling-ball, inclined-tube type,5>k7 with auxiliary equipment for making up and charging binary mixtures into the viscosimeter.~ The viscosity data on the methane-propane mixtures have been plotted as a function of molecular weight with lines of constant pressure, charts of constant temperature in Figs. I to 3. These charts are extrapolated at temperatures below 77°F. and at pressures above 5000 lb. per sq. inch. Prediction OF Viscosity from Molecular Weight of a NaturaI. Gas At atmospheric pressure the viscosity of light hydrocarbon gases increased with increased temperature, contrary to the change of viscosity of liquids with temperature. The atmospheric viscosities of the normal paraffin hydrocarbons have been determincd by several investiga-tors 3,4,9,10,12,15,16,17,19 and are plotted in Fig. 4 as a function of molecular weight, with extrapolation to 896'F. and to 220 molecular weight. Data for isopentane and normal pentane show less than 2 per cent difference in viscosity, indicating that Fig. 4 can be used for isomeric parafin hydrocarbons with an accuracy of approximately 2 per cent. Trautz and Sorg'7 determined the atmospheric viscosities 01 methane-propane mixtures and showed that they are proportional to the molecular weight. The viscosities of these mixtures

Jan 1, 1944

By Joseph J. Yancik, Leonard L. Felts, George B. Clark

LITTLE information has been published concerning the actual or useful amount of energy obtained from explosives when they are used for blasting. To provide more data on this subject, 8-in. neet cement cubes were blasted in a steel plate box and the breakage energy evaluated by comparison with drop crusher results using Rittinger's,1,2 Kick's: and Bond's' theories. Theories by Bond and Wang," Lineau," Hatch,' Roller,' and others0-11 were not considered applicable. Those used in this investigation may be expressed mathematically as follows: Rittinger Theory E = KrS2, pet,—--------------- [1] 40 d1 d0 Kick Theory TV 1 1 E = =K, [S pct. log1/d+ 100 log d0] [2] 40 d1 L. L. FELTS, Junior Member AIME, was formerly a Graduate Assistant, University of Illinois. G. B. CLARK, Member AIME, was formerly Professor of Mining Engineering, University of Illinois, and is now Chairman, Dept. of Mining Engineering, Missouri School of Mines and Metallurgy. J. YANCIK, Junior Member AIME, is a Graduate Assistant, Missouri School of Mines and Metallurgy. This paper, TP 4213A. is revised from a thesis submitted by L. L. Felts in partial fulfillment of the M.S. degree in Mining Engineering, University of Illinois, 1954. Discussion may be sent (2 copies) to AIME before May 31, 1956. Manuscript, Dec. 27, 1954. Bond's Third Theory E = Kb [S pct. log1/d1+ 100 log d0] where E — energy used in breakage, d, = average diameters of screen fractions of broken cement particles, pct, = percent weight of diameter d;, and 2 pct, = 100 pct. The above equations were employed to determine values of Kr, Kk, Kb for particle size distributions similar to those obtained from the blasting curves. These values were in turn used as a means of approximating the specific energy of the blasted material. The efficiency of crushing by blasting was then determined by dividing this specific energy by the maximum available work of the explosive per gram of cement. Knowledge of the failure of solids under static loads is developing very rapidly. Their failure under impact loads has been investigated and reported in the literature only to a limited extent. Theories of failure' hnder static loading include 1) the maximum stress theory, 2) the maximum strain theory, 3) the theory of constant elastic strain, 4) theory of maximum shearing stress, and 5) Mohr's theory of strength. All of these have elements of usefulness in establishing an applicable theory for blasting. For highly strained and compressed material such as that surrounding a detonating charge of high explosive, the Mohr theory and its implications appear to be the

Jan 1, 1957