By Jorge Gibson, P. Chris Pistorius, Megha Jampani

"The main reason for the significant carbon intensity of integrated steelmaking (approximately 1.8 tons of CO2 per ton of steel) is the use of carbon-based reductants in blast furnace ironmaking. Several changes to blast furnace ironmaking have been proposed as ways to reduce carbon intensity and cost. A conceptually simple two-zone blast furnace mass and energy balance can be used to quantify the expected impact of such process changes on coke rate, carbon intensity, and productivity. Examples to be discussed include top gas recycling, combining lower blast temperatures with increased coal injection to produce a rich top gas, using prereduced feed, and tuyère injection of natural gas. The use of the operating window – which illustrates how allowable flame temperatures and top-gas temperatures constrain feasible oxygen enrichment levels – is illustrated. Increased use of natural gas would lower the carbon intensity of blast furnace ironmaking.IntroductionBecause of the significant carbon intensity of steelmaking (approximately 1.8 tons of CO2 emitted per ton of steel produced) and the high production rate of steel (more than 1.4 billion tonnes per annum), steelmaking is responsible for a large percentage, approximately 6.7%, of world anthropogenic CO2 emissions [1]. By far the largest input of the carbon into conventional steelmaking is as coke, which is essential to blast furnace ironmaking. A typical fuel rate for blast furnace ironmaking is 450 kg of fuel per tonne of hot metal (THM). (""Fuel"" includes coke and injectants which partially replace coke; pulverized coal and natural gas are typical injectants.) Assuming the fuels to contain 90% carbon on average, and since nearly all of this carbon exits the steel plant as CO2, a fuel rate of 450 kg is equivalent to a CO2 intensity of 1485 kg/THM – by far the largest part of the total CO2 intensity of steelmaking.Blast furnace ironmaking is expected to remain the main source of new iron units; this paper gives some estimates of the extents to which further reductions in carbon intensity from blast furnace ironmaking is possible. A recent European assessment suggested that blast furnace process intensification options such as increased pulverized-coal injection or natural gas injection would yield only modest energy savings [2]. However, if the focus is on CO2 emissions rather than on total energy use, there would be an advantage to using fuels – such as natural gas – which have lower carbon contents relative to energy content."

Jan 1, 2014

By Jinqian Zhao, Jiarong Li, Shizhong Liu

"Creep cavitation of in single crystal (SX) superalloy was investigated. The constant load creep tests, in single crystal superalloys DD6, were conducted at the conditions of 800°C/700MPa, 850°C/550MPa and 900°C/450MPa, respectively. It was found that there were square facets on the stress fracture surface, and microscopic cavities in the ruptured specimens in the vicinity of the fracture surface. Both the square facets on the fracture surface and microscopic cavities in the section of the ruptured specimens show the morphology of the same thing at the different views, namely creep cavities, which are take the form of flatten cuboid. In fact, creep cavities are the longitudinally tensiled creep cracks slowly growing during the stress tensiling. The factors of creep cracks nucleation and growth conditions include: (a) enough high temperature to activate diffusion (b) casting pores as nucleation origination (c) high strains and strain rates. Eventually, the instantaneous fracture mechanism of creep specimen is cleavage fracture.IntroductionFor the materials used in elevated temperature service, creep behavior has to be accounted for. It is well recognized that creep rupture in polycrystalline materials at high temperature occurs principally by the nucleation and growth of microscopic cavities at grain boundaries, followed by microscopic cavities linkage to form micro- and eventually macro-intergranular cracks[l,2]. Without the usual grain boundaries, SX superalloys have superior capabilities at high temperatures to polycrystalline superalloys, and have become an established feature of gas turbine technology where they are commonly employed in the manufacture of high performance blades[3]. A considerable amount of work has been done over the past tens of years, and many models for nucleation and growth of creep cavities have been proposed, however, those are mainly for polycrystalline materials.In order to improve creep resistance that single crystal superalloys, in which grain boundaries are removed, have been developed. Because there don't exist grain boundaries in SX superalloy, the mechanism of nucleation and growth of creep cavities must be different from that in polycrystalline materials.Understanding the formation and characteristics of creep cavitation is crucial to model the lives of single crystal superalloys.M. Marchionni and L.G. Zhao et al. found that there were square facets on the stress fracture surface [4,5]. Roger C. Reed pointed out creep cavities lie in the necked region[6]. In this paper, the effects on the formation of creep cavities are discussed, as well as the morphology of creep cavities and fracture mechanism of SX superalloys."

Jan 1, 2013

By P. N. Anyalebechi

The effects of solidification rate on the cast microstructures of aluminum alloys 6009 and 6016 have been investigated with directionally cooled laboratory-size ingots, at 0.2-10.1 K/s and 0.4- 23.1 K/s, respectively. These ranges of solidification rate are within those observed in commercial-size ingots. In both alloys, the average dendrite cell size and second phase particle size decreased with increase in average solidification rate and with a decrease in average local solidification time. However, at comparable solidification rates, the dendrite cells and second phase particles are finer in the shorter freezing range alloy 6009 than in the longer freezing range alloy 6016. This is provisionally attributed to the earlier formation of second phase intermetallics at higher temperatures during solidification and to the formation of greater amount of the relatively coarse plate-like ß -phase (Al9Fe2Si4) phases in alloy 6016. In general, in both alloys, the types and relative amounts of the second phase particles in both alloys are independent of solidification rate.

Jan 1, 2006

By Jewel A. G. Gomes

Electrocoagulation (EC) has been performed with Al-Fe electrode system with changing polarity for the removal of arsenic from water. The removal process has been studied using ICP-AES and Anodic Stripping Voltammetry with a wide range of arsenic concentration (1-1000 ppm) at various pH (4-10) and residence times (1-60 min). Electrochemically generated by-products have been analyzed using XRD, FTIR, XPS, SEM/EDS and Mössbauer Spectroscopy. Results revealed expected crystalline iron oxides (magnetite (Fe3O4), lepidocrocite (FeO(OH)), iron oxide (FeO)) and aluminum oxides (bayerite (Al(OH)3), diaspore (AlO(OH)), mansfieldite (AlAsO4?2(H2O)), as well as some interaction between the phases. The amorphous or ultra-fine particular phase was also found in the floc. The substitution of Fe3+ ions by Al3+ ions in the solid surface has been observed, indicating an alternative removal mechanism of arsenic in these metal hydroxides and oxyhydroxides by providing larger surface area for arsenic adsorption via retarding the crystalline formation of iron oxides.

Jan 1, 2006

By Patricia Martínez Nicolás

Nickel and ferronickel are some of the major components in the production of special alloys; however, the energy consumption for their production greatly increases their price. A cheaper option could be to use NiO and a reducing agent. This work presents experimental and theoretical analysis to estimate the effect of slag basicity and amount of reducing agents on the NiO reduction from the slag which interacted with molten steel at 1600 °C in an EAF. The slag system contained CaO, SiO2, CaF2 and NiO together with a reducing agent, ferrosilicon or carbon. The NiO content in the slag was 25 mass%. The amounts of the reducing agents (Si and C) were 1 to 4 times the stoichiometric mass to reduce NiO. The CaO/SiO2 ratio was 1.5 and 2.5. The kinetics of the process was very fast since after few minutes the maximum nickel yield was obtained. The slag basicity had a negligible effect on the reduction of NiO.

Jan 1, 2006

By Agnes Y. Lee

he U.S. Bureau of Mines developed a method to treat lead-contaminated soil and ebonite battery casing wastes to produce a nonhazardous material. The cleanup procedure involves wet screening to separate a minus 18-mesh soil fraction; removal of metal1ic lead, rocks, wood, etc. ; carbonation to change lead sulfate to acid-soluble lead carbonate; size reduction; acid leaching; and rinsing. The casing wastes undergo size reduction and washing to remove the lead sulfate sludge before carbonation. Similarly, the minus 18-mesh soil is carbonated, then acid leached and rinsed. In leaching, fluosilicic acid (H SiF,) and hydrogen peroxide (H20,) are used to dissolve lead compounds. An electrowinning method is employed to strip lead from the lead-rich leachate. The acid content in the leachate is replenished with fresh H,SiF, acid prior to recycling. Treated casing wastes and soils pass the Toxicity Characteristic Leaching Procedure (TCLP) test and can be reclassified as nonhazardous materia1s. Based on this process, a conceptual pilot plant has been designed which will be demonstrated on wastes from two Superfund sites.

Jan 1, 1993

By Peter Ehren

Global Geoscience is developing a Rhyolite Ridge project, a shallow boron-lithium resource deposit, located in Nevada about 25 km from Albermarle’s Silver Peak operation. The main minerals of interest are the boron mineral searlesite (40%wt) and lithium containing clay minerals. These minerals are found among principally calcite, feldspar, muscovite, dolomite, and quartz. The equivalent commercial value is about 7–9% boric acid (H3BO3) and 0.8–1.0% lithium carbonate (Li2CO3) equivalents. Selective agitated leach tests at SGS Lakefield laboratory showed that searlesite can be acid leached between 20 and 75 °C and at a pH lower than 4. On the other hand, lithium can be leached between 20 and 75 °C and at a pH lower than 1. In other words, lithium can be recovered at low temperatures if sufficient free acid is available, which gave the motivation to investigate heap leaching of the mineral. The PLS contains boric acid, magnesium, sodium, lithium, potassium aluminium, and iron sulfates.

By Nobuhiro Kuriyama

Electrochemical activation behavior of an AB2-Laves-phase type hydrogen storage alloy, Zr0,9Ti0.lNi1.lCo0.1Mn0.6V0.2 was studied to make clear activation process of pellet-type metal hydride electrodes. An alkaline treatment of the electrodes with heated alkaline solution gave alloy surface enriched with nickel, and the treated electrode was more easily activated. The treated electrode desorbed more hydrogen during the first charge-discharge cycle, and was activated without induction period. A cross sectional view of the activated electrode showed finer pulverization of alloy particles than the annealed alloy, and impedance spectroscopy indicated larger surface area of the electrode using the as-cast alloy. Since the as-cast alloy contains inhomogeneities, multi-phase microstructure and stress in the particle, the finer pulverization of alloy particles with hydrogenation are considered to increase surface area in an earlier cycle in the case of the as-cast alloy, which leads larger reaction area and faster activation of the as-cast alloy electrode.

Jan 1, 2002

By Hong Yong Sohn, Miguel Olivas-Martinez, Zhixue Yuan

A novel flash ironmaking process that directly reduces iron oxide concentrate particles by gas is under development. The goal of this work was to study the possibility of reoxidation of iron particles in various gas mixtures. As the product iron cools down in the lower part of the flash reactor, conditions may become favorable for reoxidation because of equilibrium and high reactivity of iron particles. The effects of temperature (823 – 973 K) and H2O partial pressure (40 – 100 pct., Ptotal = 86.1 kPa) on the reoxidation rate were examined. The pressure dependence was first order with respect to water vapor, and the activation energy was 146 kJ/mol. A complete rate equation that adequately represents the experimental data was developed. For oxidation in O2-N2 mixtures, the effects of temperature (673 – 873 K) and O2 partial pressure (5 – 21 pct., Ptotal = 86.1 kPa) were determined. Reoxidation in pure CO2 was also investigated at 873 – 1073 K for comparison.

Jan 1, 2014

By Jianhua Xin, Min Chen, Cuihuan Huang, Shan Yu, Xiaoao Li, Nan Wang, Guanghao Chen

Copper enrichment behavior in continuously cast slab induced by scale formation after continuous cooling in H2O vapor atmosphere and consecutively in air has been experimentally investigated by combining with SEM-EDS analysis, for the purpose to examine the effects of initial slab surface temperature and contents of copper and nickel. For Slab 1 with copper content of 0.1 percent, no visible copper enrichment is found at scale-substrate interface irrespective of the various scale microstructures formed at different initial slab surface temperatures. For Slab 2 with higher contents of copper and nickel, copper-rich phase accumulates and stays at scalesubstrate interface under the condition of lower initial slab surface temperature; while Cu-rich phase in the porous scale formed at higher initial slab surface temperature is noted with simultaneous Ni-enrichment appearing in front of the steel-scale interface. Both a porous scale and high nickel content work together to provide pores for copper-rich phase migration away from interface and occlude within the scale layer.

Jan 1, 2016

In low carbon TRIP steels, the formation of carbide-free bainitic ferrite is crucial for the stabilization of austenite. Based on experimental investigations modeling the bainite reaction is examined adopting diffusional and displacive mechanisms, as well as the semi-empirical JMAK approach. Transformation tests were carried out to study the isothermal austenite decomposition into bainitic ferrite for a model steel containing 0.6wt%C, 1.5wt%Mm and 1.5wt%Si which replicates the composition of remaining austenite at the start of the bainite reaction in a classical C-Mn-Si TRIP steel. In the diffusional approach, classical nucleation theory is employed and subsequent growth of bainite plates is modeled using the Zener-Hillert theory. In the displacive approach, the autocatalytic nucleation of bairtite plates is assumed to be rate controlling. The predictive capability of all models is evaluated for temperature ranges where different morphologies of bainitic ferrite have been detected, The shortcomings and inherent challenges associated with either of these modeling approaches will be delineated.

Jan 1, 2003

By Yuanbo Zhang, Huanpeng Mi, Guanghui Li, Binjun Liang, Zhiwei Peng, Tao Jiang

Ludwigite ore has not yet been utilized on an industrial scale due to its complex mineralogy and fine mineral dissemination. In this study, sodium salts were employed to enhance the separation of iron and boron by reductive roasting-magnetic separation. It was found that the separation of iron and boron as well as the iron grade and recovery were significantly improved b y the addition of Na2SO4 or Na2CO3. Under the reduction temperature of 1050 °C, reduction time of 60 min and magnetic intensity of 0.1T. Compared with the inexistence of sodium salts, the iron grade and recovery of the magnetic concentrate increased from 83.3% and 88.6% to 93.2% and 95.1%, respectively, by adding 6% Na2CO3. The XRD and microstructure analyses indicated that the iron oxides were transformed into metallic iron and the average metallic iron grains were grown to over 40μm which was beneficial for separation of metallic iron from gangue.

Jan 1, 2016

By G. Van Weert

Refractory gold ores and auriferous concentrates containing silver tend to form refractory silver jarosites during pressure oxidation. Earlier work with pure Ag2S has shown that the addition of iodine species to the autoclave feed yields cyanide soluble iodargyrite (Agl) instead. Near complete silver extractions from the autoclave product were obtained at a I-/Ag+ ratio of 5 or more. This paper reports on the pressure oxidation and cyanide leaching of two industrial refractory (arseno) pyritic silver-bearing concentrates: 1. from Peru (sulphosalts) and 2. from the USA (pyrite, with acanthite occlusions). While using a I-/Ag+ mol ratio of only 1 in the feed, it has been possible to obtain 98 and 97% Ag extraction from the two autoclave products by cyanide leaching, respectively. This compares to 11 and 54% Ag extraction from the as-received concentrates and 4 and 15% Ag extraction, respectively, after pressure oxidation without KI present. The results of the testwork are discussed in terms of concentrate mineralogy and pressure oxidation conditions.

Jan 1, 1994

By Marcos Aurélio S. Costa, Nilton F. Nagem, Andreia B. Henriques, Herman S. Mansur, Alexandra A. P. Mansur, Antonio E. C. Peres, Valeria G. Silva

The superfine material generated in the Bayer process was used in one innovatively way as a precursor to geopolymerization techniques because of the presence of Gibbsite. Gibbsite can play a role in system adjustment because of the SiO2/Al2O3 ratio. Furthermore in the geopolymeric system it was studied the influenceof the additives such as kaolin, metakaolin and sodium trisilicate in an alkaline media. Others conditions to form the geopolymer were also evaluated such as solid/liquid ratio, SiO2/Al2O3 ratio and total alkaline. The raw materials and geopolymeric products were characterized by several techniques e.g. XRD, DSC, FTIR and SEM. Through the FTIR technique it was observed an increase in intensity and bandwidth in the region centered at 1010 cm-1, which is related to the asymmetric vibration Si(Al)-O, this is an indicating of the possible geopolymer formation This broadening of the band promotes a relative disappearance (overlapping) peaks at 965 and 935 cm-1 associated with raw material (ESPDust).

Jan 1, 2015

By Onuralp Yucel, Ahmet Turan, Murat Alkan, Hasan Ozer

SHS (Self-propagating High-temperature Synthesis) is one of the important methods to synthesize B4C powders. The process contains the reaction of boron oxide powders (B2O3) with magnesium reducing agent and carbon black carburizer. SHS products are leached in HCl media to purify synthesized B4C powders in the following step. In the present study, effects of various functional additives (KClO3, KHSO4, MgSO4.7H2O, NaCl, MgO and Na2SO4) in the SHS stage were carried out. Various proportions of the additives were mixed with the initial SHS charge mixtures. Two different molar ratios were employed in the initial SHS mixtures as 1:3:0.8 B2O3:Mg:C and 1:2.5:0.8 B2O3:Mg:C. After the SHS step, HCl leaching process was applied to the SHS products. Filter cakes were dried and characterized by using X-Ray Diffraction Spectroscopy, BET and chemical analysis techniques.

Jan 1, 2015

By Hai-Peng Guo, Lu Jiang, Xiao-Man Yan, Bing Xie, Hong-Yi Li

Traditional, calcium compounds cannot be used in vanadium extraction processing due to the limitation of sodium roasting technology, which results in unsatisfied dephosphorization for vanadium-containing hot metal in converter and thus increasing the dephosphorization burden for subsequent steelmaking. The calcium roasting technology is an alternative for vanadium extraction and allows adding lime into vanadium slag in converter. In the present study, vanadium was leached by soda from roasted vanadium slag with high calcium content. Effects of roasting temperature and time, leaching temperature, Na2CO3 concentration andliquid to solid ratio on vanadium leaching rate were studied. The results show that 94% of vanadium was extracted by roasting the vanadium slag at 950℃ for 2.5h and then leaching in 160g/L Na2CO3 liquid at 95℃ for 1h with liquid to solid ratio of 10:1 ml/g. Impurities of Si and P reacted with calcium and formed insoluble Ca2SiO4 and Ca3(PO4)2 respectively.

Jan 1, 2015

By Hassan Saalman, Mahmoud Mahmoud, Omneya El Hussaini

The Ferruginous sandstone ore was obtained from Ramlet Hemeyir area, Southwestern Sinai, Egypt, was found to contain 10% rare earth elements (REE). A representative sample has been subjected to sulfuric acid agitation leaching. About 93% of the REE content was released by mixing the ground sample to -100 mesh with concentrated H2SO4 at solid/liquid (S/L) ratio of 1/2 for 5h at a temperature ranged from 250 to 300o C. The REE was precipitated from the prepared sulfate leach liquor of pH 1.0 by adding 35% oxalic acid at 25o C. The precipitation yielded 98% REE. For selective separation of yttrium, the rare earth cake was leached with 31.5% nitric acid. Next, the aqueous solution was contacted with di-(2-ethylhexyl) phosphoric acid (D2EHPA) where 98% yttrium extraction was achieved. Stripping was done with hot H2O (80o C). Finally, a precipitation with oxalic acid was done followed by ignition at 950o C. A yield of 95% yttrium oxide was produced.

Jan 1, 2014

By Haotian Xue

A new process to extracted antimony directly from stibnite concentrate by reductive sulfur-fixation smelting in sodium molten salt has been presented. The influences of sodium salt content and composition, ferric oxide addition, temperature and time was investigated, respectively. The optimum conditions was determined as follows: W????: ??concentrate=40%, W??alt: ????concentrate =88.75%, WFe2O3 :Wconcentrate =55.13%, W??aCl: ????alt=40%, 1123K, 1h. Under above-mentioned optimum conditions, the average direct recovery ratio of antimony can reach 91.48%, and the main chemical composition of obtained crude antimony is Sb 94.31%, Fe 4.436%, Pb 0.502%, Au 0.0236%. In comparison to traditional antimony pyrometallurgical process, the smelting temperature of present process is reduced from 1423~1473K to 1123~1173K. During the smelting operation, SO2 emision can be avoided completely due to sulfur-fixation as FeS. Furthermore , S0 can be obtained when the molten slag is handled by water leaching with conditions of 323K, L/S=5/1, 2h.

Jan 1, 2014

By T. L. Baum

External oxidation during in-line heat treatment of TRIP steels can cause problems for the subsequent coating process. This research aims to elucidate the kinetic rates of internal oxidation, external oxidation and decarburization and their interdependence under different gas atmospheres and temperatures. A rolled steel sample chemistry of 0.14 wt.% C, 1.8 wt% Mn, 0.6 wt.% Si and 1 wt.% Al is used as a case study. Thermogravimetric techniques are used to examine the net mass change in a sample during heat treatment and the results show an initial mass decrease and later an increase for particular partial pressures of H2O. SEM-EDS, optical microscopy and glancing-angle x-ray are used to quantify the microstructure. The cross-section of the samples have 4 distinct zones: (i) an external scale, rich in fayalite, (ii) an internally oxidized region with Al, Si and Mn oxides in an Fe matrix, (iii) a decarburized steel region, characterized by large ferrite grains and low carbon content, and (iv) a relatively unaffected steel core with a structure similar to the starting material.

Jan 1, 2006

By Mahmood Alemrajabi

When LKAB processes their iron ores in northern Sweden, they generate apatite as a by-product. The apatite has been recovered by flotation and the concentrate contains about 0.4 wt% rare earth elements (REE). Both phosphate rock and REE are listed as critical raw materials for the European union. In the present study, the recovery of REE within the nitrophosphate process of fertilizer production has been studied. In the first stage, the REE are precipitated and isolated as a phosphate concentrate. For further purification and individual separation of REE by solvent extraction, removal of phosphorous from the concentrate to enhance the dissolution of REE in mild acidic solutions is essential. In this study, thermal treatment of the concentrate with sodium hydroxide at elevated temperatures followed by water leaching has been studied in order to separate the phosphorous and thereby facilitate dissolution of the REE. The results show that 95% of total phosphorous initially present in the REE phosphate concentrate is removed after thermal treatment with NaOH 1:1 mass ratio, at 400 °C.