The current methodology to design stope support systems in South African gold and platinum mines is based upon the tributary area concept. The discontinuous nature of the hangingwall rock is not adequately addressed, and mechanisms leading to rock mass failures between adjacent support units are poorly understood. The work reported here aims to formulate a basis for quantifying support mechanisms and gain insights into the influence of rock discontinuities on stable hangingwall spans. Numerical models are used to qualitatively investigate the stress transfer from the support units to the discontinuous hangingwall. Stable hangingwall spans are quantified by considering two failure mechanisms, namely (i) beam buckling, and (ii) shear failure due to slip at the abutments. The output of the proposed design methodology is appropriate site specific support spacing, based on discontinuity spacing and orientation. The method is particularly suited to mines at intermediate and great depth, where typically the hangingwall is highly discontinuous due to face parallel mining induced fractures. Results of parametric studies show that with increasing in situ compressive hangingwall stress, beam thickness and friction angle, hangingwall stability is increased, leading to wider stable hangingwall spans between adjacent support units.

Jan 1, 2000

By J. Daavittila

In the latter part of the 1980s Outokumpu Chrome in Tornio, Finland, was in a situation when its twenty-year-old ferrochrome plant was becoming too inefficient to sustain economically sound production. The company made extensive studies on the then available processing methods to find out the best possible processing route. As a result, the whole plant was practically rebuilt and expanded. When equipment was proven in practical operation, an application for FeMn production was developed. Now as the Tornio FeCr-plant is considering expansion, the same type of exercise is to be performed with today?s challenges, which will be discussed in the paper. These challenges include increasing costs or decreasing quality of raw materials, increasing energy costs, stricter environmental regulations and demand for better working conditions. The possibilities of resolving to these challenges will be discussed in the paper. The future and continuing development with FeCr includes the better utilization of process dusts and a lower consumption of energy. By adapting the latest automation tools to better control the process, even higher efficiencies can be achieved with present technology. New processes are considered for development in the future and some possible technologies will be described.

Jan 1, 2004

The effect of composition on electrical conductivity (resistivity), viscosity and liquidus temperature of the slags encountered in electric smelting of PGM containing suphide concentrates is reviewed, along with the relationsip between slag composition, slag-matte separation and metal losses to slag. Optimization of slag composition at furnace temperature is attempted on the basis of opposite and parabolic trends of the viscosity-conductivity relationships of the slags. The importance of surface tension of slags is emphasized using available and estimated information which are grouped into a useful correlation. These values are coupled with or incorporated into slag viscosity plots to illustrate the correlation between the two factors, which influence slag-matte separation as well as refractory attack. The electrode in the slag-resistance furnace is the central factor in the design and operation of the furnace by its role of conveying the smelting power. The obvious parameters are the size and positioning in the slag bath, which are defined by slag resistively, furnace resistance, cell constant and power input. The flow of heat generated by the electrode current determines the energy distribution and furnace dimensions creating viscosity profiles, which in turn affect flow conditions. Thus the flow of slag and matte are discussed in conjunction with the furnace geometry, stirring action of the electrodes, buoyancy and electromagnetic effects. The action of the electric furnace as a settler is discussed. The rectangular furnace is considered as a channel reactor in this analysis, and the action of the electrodes is described to indicate a balanced settling rate in the area of electrode action. Discussion of the design and production capacity of the electric furnace, with reference too perating current, power input, furnace dimensions and electrode size, are based on considerations derived mainly from slag properties such as its resistively, viscosity and liquidus temperature.

Jan 1, 2004

By A. McLean, M. Iwase, K. Wakimoto, K. Katogi, Y. Kikuchi

One of the greatest obstacles to the application of physical chemistry principles to the elucidation of slag-metal reactions is a lack of knowledge of activities of the reacting species. To a large extent, oxygen potential of the slag phase governs iron and steelmaking practice. Without oxygen control by means of appropriate sensors, the behaviour of the other elements cannot be managed. In this paper, measurements of the FeO activity with various types of electrochemical FeO sensors will be described together with examples of their applications for improved strategies toward better practice for ladle metallurgy and sulphur and manganese distributions between slag and metal phases during steelmaking. Measurements of FeO activity have also been made in order to improve dephosphorization reactions. This type of work has led to significant reduction in volume of slag generated within the steelmaking vessel, which in turn has important implications for refractory wear, metal yield, alloy recovery and improved productivity. Finally, an on-line sensor is described that permits the oxygen potential to be determined for both the metal phase and the slag phase during steelmaking in the BOF.

Jan 1, 2004

By L. A. Cramer

Platinum metal was first utilized by the Inca civilization in South America where it was found in alluvial deposits along the San Juan and Atrato rivers that lie between the Andean mountain range in Colombia and the Pacific Ocean. The nuggets found in these rivers average between 77% and 86%platinum, 7%?8% iron and small amounts of copper, gold and other Platinum Group Metals (PGMs). The Incas often alloyed platinum with copper to increase its workability and fabricated various ornaments from it.

Jan 1, 2001

Threshold blasting involves the use of small amounts of high explosive to break and fragment hard rock without having to evacuate mining personnel. The method is easily assimilated and effective in rockbreaking, but requires rigid control on drilling, charging and timing. Current underground trials are aimed at fine-tuning the amount of explosive energy and blast hole geometry to allow the firing of multiple sets of shot holes in a continuous manner. Through correct procedures, the after-blast fumes, dust and fly rock can be contained so as to provide a safe working environment. Threshold blasting hugely reduces the volumes of explosives used in mining and brings to maturity the potential of the process begun by Alfred Nobel when he introduced nitroglycerine, and later dynamite, to mining. Its key contribution is its enabling of continuous mining operations with well understood and relatively low cost technologies. The use of batch blasting, employing large burdens holds the greatest potential for delivering high flow rates of ore at minimal cost. There is good potential for rapid evolution of the concept.

Jan 1, 2002

By J. Labuschagne

There are a number of factors that contribute to the profitability of a mine and its associated concentrator. Chief among these is the time taken from the first hoist of material from underground to the first batch of concentrate shipped. The main aim of this project was to integrate the mining model with a concentrator production schedule to minimize the time it would take to produce concentrate (without the concentrator having to stop because of a lack of feed material) in the most capital-effective manner. A secondary goal was to ensure detailed stockpiling requirements, as the concentrator is in an area where 'visual pollution' is to be avoided. To achieve these two goals a dynamic stockpile model was created by utilizing the mine production schedule and breaking it down to a daily production figure. Four different concentrator development models were then proposed. The difference between the mine production and concentrator consumption was integrated over the life of the mine to provide the accumulated stockpile tonnages for both Merensky and UG2 ore. To prevent a situation where the concentrator was operational without any feed, the stockpile levels were never allowed to fall below zero. When a development option was selected, the standard metallurgical performance calculations were used to derive a concentrate production schedule, which was used as a basis for commercial negotiations for the sale of concentrate.

Jan 1, 2013

By C. Balci

Specific energy is defined as the amount of work required to break a unit volume of rock and is used to predict the performance of mechanical miners. It is obtained from full-scale rock cutting experiments, which require large block samples, experienced personnel and expensive equipment found in only a few research centres in the world. Estimation of the optimum specific energy, at which a given geological formation is excavated at optimum cutting geometry in the most energy efficient manner, from mechanical rock properties to predict the performance/efficiency of roadheaders is the basic aim of this study. The mechanical rock property tests require only core samples, which are easier to obtain and to test. In this context, full-scale rock cutting tests are performed on 23 different rock, mineral and ore samples including sandstone, claystone, tuffite, chromite, trona and copper collected from some operating mines in Turkey. The optimum specific energy values are obtained for each sample. Physical and mechanical property tests are performed on the core samples obtained from the same samples to determine uniaxial compressive strength, indirect (Brazilian) tensile strength, static and dynamic elasticity moduli, Schmidt hammer rebound values, density, and Cerchar abrasivity index. The relationships between the optimum specific energy and the mechanical rock properties are analysed using statistical methods. The results indicate strong relationships between the optimum specific energy and the mechanical rock properties. The strongest relationships are found by using uniaxial compressive strength and tensile strength. The performance models developed in this study are in good agreement with the empirical models previously developed for roadheaders and can be used reliably for prediction purposes. Keywords: Mechanical excavation, roadheader, performance prediction, rock cutting, optimum specific energy, mechanical properties of rocks.

Jan 1, 2004

By L. Holappa

Ferroalloy production is an energy-intensive industrial sector with significant CO2 emissions. In this paper the current situation in ferroalloy processes is discussed from the standpoint of global environmental issues, trends and development. Progress and data of ferroalloys production are frequently compared with the steel industry, which is a closely related sector and the main user of ferroalloys. Emission factors of processes and electricity production are examined as well as possibilities and future scenarios of how to diminish CO2 emissions. As a part of this study a questionnaire was submitted to experts in the field of ferroalloys worldwide to survey opinions on the ferroalloy industry today and in the near future (2020). Eighteen questions concerning raw materials, energy, environmental aspects, by-products and economic aspects were responded to by seventeen experts, the answers were analysed and conclusions were drawn. Keywords Ferroalloys, energy, CO2 emissions, electricity, sustainability, questionnaire.

Jan 1, 2010

By L. Forsbacka, L. Holappa

Viscosities of quasi-ternary CaO-SiO2-CrOxmelts in contact with metallic chromium were measured by the rotating cylinder method up to 1750ºC. Twelve slag compositions were selected in the composition range 20–55 wt% SiO2, 10–45 wt% CaO and 10–60 wt% CrOx. Estimation of the amounts of CrO and Cr2O3was made by regression analysis based on the earlier data. Professor Iida’s (Osaka University) viscosity model was applied and model parameters (0CrO,CrOand Cr2O3) were evaluated. The Iida model gave good consistency with the measured viscosity values.

Jan 1, 2004

By K. Blaski

his paper reports an investigation aimed at optimizing the compaction of granulated hard-metal powder for the production of cutting tool inserts. The optimal compaction is that which yields optimal shrinkage during sintering, i.e. minimum porosity in the sintered part. Extensive compaction tests on 23 different hard-metal powders have been carried out and have shown that the ideal ?green density? of a hard-metal compact, i.e. the density after compaction, increases linearly with the apparent density of the powder. On the basis of this result, an equation has been derived, which allows one to predict the optimal shrinkage that a hard-metal compact undergoes during sintering once the following data are known: the required sintered density, the volatile content of the powder and the apparent density of the powder. Since these data are available to the tooling designer, this equation allows one to design tooling for the compaction of hard-metal, which leads to optimal shrinkage

Jan 1, 2007

By P M. Bradbury

The nature of aggressive process chemical requirements typically in the Platinum Refinery Industries, lend themselves to the use of Polymer Composite Glass Reinforced plastics for pipework and other associated equipment in these types of Plants. This paper discusses the basic characteristics of a Polymer Composite glass reinforced piping system and gives sample examples of applications in current present day use.

Jan 1, 2006

By A. T. Haile

Detailed monitoring of the response of the rock mass between rockbolt reinforcement units subjected to a simulated seismic source has been successfully conducted. This work has shown the increase in amplification of the Peak Particle Velocity (PPV) with distance from a rock bolt unit, and, a minimum PPV for rockburst damage for the given site characteristics. This understanding, at this site, will allow the design of a suitable rock bolt spacing to prevent unravelling of the rock mass between the rock bolt units for a given level of seismicity. Or, alternatively, an estimation of the requirement for a suitable fabric support system, for the anticipated level of seismicity, can be made.

Jan 1, 2001

The influence of varying amounts of magnesia, silica, and alumina in iron ore sinter on its mineralogy, reducibility index (RI), reduction disintegration index (RDI), physical breakdown (AI and TI), and production properties (coke breeze rate) were examined. It was found that the mineralogy of iron sinter can more easily be predicted from its chemical composition than from the RI, RDI, AI or TI. Anticipating the consequence that varying amounts of MgO and SiO2would have on sinter properties is complex, and not necessarily predictable. High concentrations of Al2O3in the sinter result in high concentrations of the SFCA phase, but with drastically deteriorated properties. This study also confirmed that the form in which fluxes are added to the raw material sinter mixture affects the mineralogy and properties of the produced sinter.

Jan 1, 2010

By S. Sridhar, R. E. Aune, M. Hayashi

Thermophysical properties of silicate melts are strongly structure dependent. It is well known that the viscosities of slags increase with increasing the degree of polymerization of silicate anions. Even the thermodynamic properties of slags are dependent on the types of species and the population of the same in the melt. Thus, a link between the thermophysical and thermochemical properties of silicate melts is logically expected. The present paper elucidates the salient features of Darken?s excess stability approach to the Gibbs energies of solutions as applied to the viscosities of silicate melts. It is demonstrated, that the second derivatives of the viscosities of binary silicate melts with respect to composition indicate a maxima corresponding to the existence of stable compounds in these systems. The concept was successfully applied to the following systems: Al2O3-SiO2, CaO-SiO2, FeO-SiO2, MgO-SiO2and MnO-SiO2. In all the cases, the second derivative plots of viscosities with respect to composition showed peaks corresponding to the metasilicates. The second derivatives of the activation energies of viscous flow with respect to temperature has earlier been shown to reflect the formation of associates/embryos in the homogeneous silicate melts, indicating the readiness of the melt to separate a solid phase. Thermodynamic coupling of thermal diffusivities in the case of the system CaO-Al2O3-SiO2from the laser-flash measurements of these slags as a function of temperature are examined as part of the present study. Densities are estimated from integral molar enthalpies in the case of silicate systems and the results are presented. Keywords: silicate melts, viscosity; activation energy, thermal diffusivity; density

Jan 1, 2004

By P. Rosario

The application of high pressure grinding rolls (HPGR) has been growing in the mining industry for the last 10 to 15 years. The major benefits supporting this trend are better energy efficiency, improved grinding capacity, and higher metal recovery in downstream processes such as heap leaching and flotation. In general there is limited quantitative knowledge on the true benefits of HPGRs relative to SAG mills in comminution, and about which situations one deals with better than the other. This paper will present a structure for comparison of the energy requirements for HPGR versus SAG mill considering complete circuits for comminution of precious and base metals hard ores. The work presented is from the design of four complete circuits based on ore data from two sites.

Jan 1, 2010

By H. A. D. Kirsten

Shotcrete has become a strategic component of support in underground mines. The ductility of reinforced shotcrete makes it a safe and economic means of surface support under adverse static and dynamic loads. The ability of ductile shotcrete to sustain load at large deflections enables excavations in squeezing conditions to be stabilized and the safety in excavations subject to rock bursting, to be assured. A Shotcrete Working Group was formed to find the configurations of fibre reinforcement that would give shotcrete the same ductility as when reinforced with mesh. Beams and panels reinforced with various types and lengths of fibre were accordingly tested. A single mix design consisting of river sand, ordinary Portland cement, fly ash, condensed silica fume and gunite dust and segregation suppressant was used. Steel and polypropylene fibre varying in length from 25 to 50 mm were used in nominal contents of 5 % and 0.5% by mass respectively. Beams, panels and control specimens were shot into specially made formers. Suitable mixing procedures were developed for the different types of fibre. The test specimens were shot in a semi-dry mix process. The shotcrete was cured until tested 28 days after shooting. The fibre contents and uniaxial compressive and Brazilian tensile strengths of the shotcrete were determined from the control specimens. The beams and panels were tested in bending in specially manufactured test rigs. The beams were examined for simple supports and fixed ends. The panels were fixed in a manner that simulated underground conditions and were loaded statically under uniform pressure. The beams were loaded and the corresponding deflections measured up to failure. The panels were loaded up to mid-span deflections of 150 mm. The results are presented in the form of load-deflection graphs. The peak loads and ultimate deflections for the fixed end beams were considerably larger than for the simply supported beams for the various types of fibre considered. None of the beams tested, however, were able to sustain load at relatively constant value beyond the peak load. The panel tests showed that 40 mm and 50 mm long steel fibre and 30 mm, 40 mm and 50 mm long monofilament polypropylene fibre reinforcement gave shotcrete the same ductility as mesh.

Jan 1, 1998

By R. Scott

This article describes and evaluates the establishment of Kuyasa Mining including the search for a suitable deposit, the ongoing lack of finance, and market constraints. Despite the dramatic initial growth and success of their Ikhwezi Colliery near Delmas, Mpumalanga, Kuyasa?s experiences offer some sobering arguments for significant changes to mineral rights ownership, the attitude of financial institutions and government policy if South Africa is to have a dynamic and successful junior and small-scale mining sector.

Jan 1, 1998

By N. D. L. Burger

A low noise blast hole drilling system was developed to limit the risk of noise-induced hearing impairment in mining operations. Noise- induced hearing loss has been identified as a major occupational health risk in SA mines. The noise generated by pneumatic percussion drills is a major contributor to such noise-induced hearing loss. This motivated the South African Safety in Mines Research Advisory Committee (SIMRAC) to commission the development of a low noise rock drill system. The system had to be designed, manufactured, tested and demonstrated in a simulated underground mining environment. The specification required noise levels below 90 dBA. Other important design considerations were ease of manual transport, setting up and operation. The primary design concept was to encapsulate a standard SecoS215 pneumatic rock drill in a composite material tube. The tube is pushed onto the rock face by a pneumatic cylinder and is sealed at the rock face by an elastic seal. The drill is pulled towards the rock face by a rope and pulley mechanism fitted inside the tube. This mechanism is powered by a second pneumatic cylinder. The actions of moving and setting the drill require two persons. However, the team can carry out the drilling function itself on several drills simultaneously because of the self-thrusting design. The drill is supported by two camlocks. The exhaust (air containing dust, water, rock debris, oil and grease) is removed from the encapsulating tubes via an exhaust tube to the end of the stope. In this way exhaust noise and air pollutants are disposed of away from personnel. Tests were conducted in a test stope. Noise levels of under 90 dBA were achieved, thereby attaining the primary design specification. This was achieved without materially compromising ease of handling. Penetration rate was somewhat improved compared to that of the standard drill, so that productivity could be maintained. Keywords: Drill, rock drill, quiet, noise, mine, underground.

Jan 1, 2004

By André de Jager, Henk Ludik

Navachab Mine experiences difficulties with pit wall stability in certain areas of the mine. The main reason for the instability is the fact that the geology comprises many joints and faults. Blasting, without impacting negatively on the stability of the pit walls, poses a major challenge. The mine has installed a technologically advanced seismic monitoring system with monitoring sensors positioned at various locations and depths throughout the pit. The electronic data recording system records all relevant information on a continuous basis with early warning signals in cases of potential danger. From the information recorded by this micro-seismic system it was established that the energy release into the high-wall is predominantly influenced by the mining rate, water content and mining tempo and to a lesser extent by the blasting operations. To limit the negative effects of blast vibrations, the use of Electronic Delay Detonators (EDDs) was introduced. The optimal delays were determined through signature trace analysis. The vibrations obtained during blasts initiated by means of electronic delay detonators were monitored and compared to those traditionally obtained when standard pyrotechnic delay detonators had been used. The measured vibration data indicated an improvement of 25% to 100% drop in vibration amplitude compared. The accuracy and programmability of EDDs presented huge potential for blast optimization in terms of limiting the vibrations without compromising fragmentation. The whole project was conducted over a twelve week period with some 4000 EDDs. The average size of a blast was in the order of 350 holes using about 40kg explosives per hole, which equates to 14,000 kg explosives over 12 different blasts. The paper deals in detail with the blast optimization process with regard to: - determining the rock response time; - establishing the signature traces; - analyzing the wave interference patterns; - predicting the direction of constructive and destructive wave interferences; - optimizing of the inter-hole and inter-row delay periods; - measuring the ground vibrations. The results obtained during electronic blasting are compared to those obtained during pyrotechnic blasting. Comparisons are being made with regard to the following: - ground vibration measurements; - pit wall stability measurements; - blast safety.

Jan 1, 2006