By M. M. Wong, D. E. Couch, G. M. Martinez

The Bureau of Mines electrowon hafnium metal with an average oxygen content of' 150 ppm at 700°C from an electrolyte containing 27 wt pct LiCl, 62 wt pct RbCl, and 11 wt pct HfC14. The average anode and cathode current efficiencies were 90 pct at anode and initial cathode current densities of 86 amp per sq ft. Haf-nium metal with an average oxygen content of 440 ppm was electrowon at 800oC from an electrolyte containing 90 wt pct KC1 and 10 wt pct HfCl4. The average anode and cathode current efficiencies were similar to those obtained in the LiCL-RbCl-HfCl, electrolyte. The chlorine gas given off at the graphite anode was vented through either a silica or a graphite tube to prevent cell corrosion. THE current method for the commercial production of high-purity hafnium is the thermal decomposition of Hfl4.1 The iodide method is not adaptable to continuous process techniques. Nettle, Hiegel, and Baker2 studied the electrorefining of hafnium from hafnium sponge containing 800 ppm oxygen. They failed to obtain hafnium with 600 ppm oxygen in their initial deposits and obtained AEC specification for oxygen only after 75 pct of the soluble hafnium had been removed from the electrolyte. Calculations using their data indicated this was approximately 4 lb of hafnium. The electrolyte was then used to produce approximately 3 lb of hafnium with a low oxygen content. However, no data are shown concerning the amount of anode material initially used or what percent of it was dissolved, therefore, results are not suitable for evaluation of a continuous operation. In general, it was not possible to consistently obtain low oxygen content metal with the electrolytes described by Nettle, Hiegel, and Baker. Wong, Hiegel, and Martinez3 investigated the electrorefining process for hafnium and showed that even by strict control of electrolyte composition only relatively low oxygen reduction could be obtained. The oxygen contained in the hafnium anode material tended to transfer to the cathode deposit and only a limited purification was possible. Both the "iodide" and the "electrorefining" processes depend upon hafnium sponge as a starting material. The sponge is normally produced by magnesium reduction of HfC14 ' and does not meet AEC specifications for hafnium metal. Since only 30 pct of the anode feed could be utilized3 in the electrorefining cells, the Bureau of Mines developed an electrowinning process. HfC14 was used as the feed material for the electro-winning process described in this report. Many of the electrolytes used in the electrorefining studies3 ap- peared to be suitable carrier-electrolytes for HfC14. However, in the initial studies on electrowinning, it was desirable to use electrolytes that had low solidus temperatures and could be operated over a wide temperature range to investigate parameters of the process. Therefore, electrolytes containing LiC1, NaC1, KC1, RbC1, CsC1, and HfC14, in various combinations were explored. EQUIPMENT Chlorinator. Hafnium carbide was chlorinated to produce HfC14 in the batch-type chlorination shown in Fig. 1. Chlorination temperatures were measured with a thermocouple placed in the center of the HfC charge. A flow meter was used to monitor the helium and chlorine. The exhaust side of the silica chlorina-tor tube was equipped with a flask for collecting organic material released during the initial heating of the HfC. The temperature of an internal heater, which extended from the HfC14 condensing flask to the hot end of the chlorinator, was adjusted to prevent the HfC14 from condensing before entering the collection flask. Helium and excess chlorine were exhausted through the lid of the collection flask to an aqueous NaOH solution. Sublimer. Initial studies were conducted using a sublimer, Fig. 2, made by placing a 13/8-in. OD nickel thimble 11 in. long, inside a 11/2-in. ID nickel bell 12 in. long, and locking it in place. This unit was loaded with HfC14 and partially immersed in the molten electrolyte for sublimation directly into the electrolyte. In another sublimer shown in Fig. 3, the HfC14 was contained in a "resin reaction flask". Quartz wool, previously heated to 600aC, secured between two nickel wire screens, was placed just above the HfC14 powder. The lid contained a vacuum outlet, a gage, an argon inlet, and an air-cooled pipe for condensing the HfC14. This sublimer was evacuated and heated. The sublimation temperature was not critical and the sublimer operated satisfactorily at all temperatures between 250" and 350°C. Electrolytic Cell. The electrolyte chamber, Fig. 4, was made of mild steel 8-in. schedule 20 pipe, 30 in. long. The exterior was metallized with a Ni-Cr alloy. The electrolytes were contained in a 16 gage nickel or iron liner with a nickel heat shield on top. The cell was heated by a resistance furnace. A 21/2-in. ID by 25 in. long air lock was connected to one port of a two-port cell cover assembly through a slide valve. The cover assembly of the air lock was electrically insulated from the cell and was equipped with a rubber sleeve that provided for the passage of the cathode lead. This allowed the cathode deposits to be removed and a new nickel cathode to be introduced without allowing air to enter the cell. A tube-rod assembly was bolted to the other port on the cell cover assembly and was sealed by a packing seal. The tube-rod assembly consists of a graphite

Jan 1, 1970

By R. W. Gurry

In the course of a series of measurements of the rate of diffusion of carbon in austenite at about 960°C. (1760°F.) and III0°C. (2030°F.), it became necessary to determine carbon concentration when austenite is saturated with graphite, because of indications that the hitherto accepted value of the solubility of graphite in this temperature range is too low. Specimens of carbonyl iron were saturated at temperature in a hydrogen-toluene atmosphere which was in equilibrium with graphite. The carbon conteDt of the steel was measured either by combustion or by the loss of weight after substantially complete decarburization in an atmosphere of hydrogen saturated at room temperature with water vapor. The absence of carbide or graphite as a phase at temperature was demonstrated by microscopic examination of saturated specimens that had been drastically quenched, The mean result of concordant ments-—taeats-is-^that gamma iron saturated with respect to graphite contains 1.39 per cent carbon at 957°C .(i755°F.) and 1.89 per cent at III0°C. (2030°F.). These two values, plotted along with what appears from the literature to be the best value (0.69 per cent) at the iron-graphite eutec-toid temperature (738°C. or I360°F.), yield a curve that is almost linear, and which, continued upward through a short interval, leads to a limiting solubility of 1.98 per cent at the iron-graphite eutectic temperature II35°C. (2075°F.) instead of the commonly accepted value of about 1.7 per cent. Experimental Procedure The samples of carbonyl iron, with the exception of those for microscopic examination, were cylinders 3.8 cm. long, 0.475 cm. in diameter. They were placed in a graphite holder and suspended in a vertical furnace, the temperature of which was controlled precisely by means of the resistance of the platinum winding.' In the empty furnace the range of temperature over a distance of 4 cm. at the heat center was 9°C. (I6°F.) but at a given location the temperature remained within +o.5°C. (o.9°F.); it was measured by inserting a platinum-rhodium couple calibrated at the melting point of palladium, 1555°C. Since the presence of the sample probably improved the uniformity of temperature, it was decided to consider the average temperature of the sample to be 3°C. lower than the maximum measured in the empty furnace with the same setting of the controller. Data were obtained in the vicinity of two temperatures, 960°C. (I760°F.) and III0°C. (2030°F.). The samples for microscopic examination, 2.2 cm. long, 0.475 cm. in diameter, were suspended individually on pure iron wire; for these no temperature correction was applied. The carburizing gas passed into the furnace was dry, oxygen-free hydrogen saturated at room temperature with toluene; this quickly produced on the

Jan 1, 1942

By R. W. Gurry

In the course of a series of measurements of the rate of diffusion of carbon in austenite at about 960°C. (1760°F.) and III0°C. (2030°F.), it became necessary to determine carbon concentration when austenite is saturated with graphite, because of indications that the hitherto accepted value of the solubility of graphite in this temperature range is too low. Specimens of carbonyl iron were saturated at temperature in a hydrogen-toluene atmosphere which was in equilibrium with graphite. The carbon conteDt of the steel was measured either by combustion or by the loss of weight after substantially complete decarburization in an atmosphere of hydrogen saturated at room temperature with water vapor. The absence of carbide or graphite as a phase at temperature was demonstrated by microscopic examination of saturated specimens that had been drastically quenched, The mean result of concordant ments-—taeats-is-^that gamma iron saturated with respect to graphite contains 1.39 per cent carbon at 957°C .(i755°F.) and 1.89 per cent at III0°C. (2030°F.). These two values, plotted along with what appears from the literature to be the best value (0.69 per cent) at the iron-graphite eutec-toid temperature (738°C. or I360°F.), yield a curve that is almost linear, and which, continued upward through a short interval, leads to a limiting solubility of 1.98 per cent at the iron-graphite eutectic temperature II35°C. (2075°F.) instead of the commonly accepted value of about 1.7 per cent. Experimental Procedure The samples of carbonyl iron, with the exception of those for microscopic examination, were cylinders 3.8 cm. long, 0.475 cm. in diameter. They were placed in a graphite holder and suspended in a vertical furnace, the temperature of which was controlled precisely by means of the resistance of the platinum winding.' In the empty furnace the range of temperature over a distance of 4 cm. at the heat center was 9°C. (I6°F.) but at a given location the temperature remained within +o.5°C. (o.9°F.); it was measured by inserting a platinum-rhodium couple calibrated at the melting point of palladium, 1555°C. Since the presence of the sample probably improved the uniformity of temperature, it was decided to consider the average temperature of the sample to be 3°C. lower than the maximum measured in the empty furnace with the same setting of the controller. Data were obtained in the vicinity of two temperatures, 960°C. (I760°F.) and III0°C. (2030°F.). The samples for microscopic examination, 2.2 cm. long, 0.475 cm. in diameter, were suspended individually on pure iron wire; for these no temperature correction was applied. The carburizing gas passed into the furnace was dry, oxygen-free hydrogen saturated at room temperature with toluene; this quickly produced on the

Jan 1, 1942

Jan 1, 1915

By Horace L. Wells

The gravimetric determination of titanium in irons and steels is extremely difficult. It may be well, therefore, to call the attention of those members of the Institute who are interested in the chemistry of iron to a colorimetric! method, which I have slightly elaborated to adapt it to the case under consideration. Schön * discovered that hydrogen peroxide produces, in certain solutions of titanic acid, a very intense color similar to that of ferric

Jan 1, 1886

Elected Died 1895 *ABBOTT, AI ATTHUR 1908 1882 *ABBOTT, ARTHUR V 1906 1905 * ABE, MASAYOSHI 1909 1903 * ADAMS, CHARLES C. 1905 1906 * ADAMS, JOHN C. 1913 1905 * ADAMS, WILLAMS 1909 1903 * ADAMS, W. EDWARDS 1910 1884 *ADDY, MATTHEW 1896 1906 * AFFLECK, WILLIAM A. 1911 1889 * AKERS, WILLIAMS A. 1906 1905 * ALABASTER, RUPPERT C. 1911 1899 * ALBERGER, LOUIS R. 1911 1894 *ALLEN R B 1896 1905 * ALLEN, R. SCOTT 1906 1874 * AMIOT, H. 1892 1886 *AMSLER, CARL 1894 1898 ** ANDRSON, JOHN W 1905 1895 *ÅNGSTROM, CARL 1901 1887 * ARCHBALD, JAMES 1910 1900 * ARLETT, GEORGE H 1906 1895 *ARMSTRONG, JOHN F 1898 1882 *ARNOLDS, HUGO 1886 1875 *ASHBURNER, CHARLES A 1889 1872 *ASIIBURNER, WILLIAM 1887 1883 *ATKINS, C M , JR 1885

Jan 1, 1917

By C. Chamberlain

The Telfer Project, Australia's newest, largest, and most remote gold mine treats 480 kt of ore grading 9.33 g/t derived from open pit mining operations. Coarse gold is recovered by gravity concentration with jigs and further upgraded wing a continuous strake launder table, and by amalgamation. Remaining gold is recovered in a cyanide circuit and incorporates flat bottom air agitators, counter current decantation (CCD) and stellar filters for clarification and precipitate removal. Overall recovery into a bullion averages 98%. The mill incorporates a number of design features that allow for maximum efficiency and security wing a minimum number of operation personnel.

Jan 1, 1983

By E. J. Nielsen, P. R. Strutt

A study has been made of the progressive changes in the distribution of etch-pit structures occurring during high-temperature creep in copper + 7 wt pct Al single crystals oriented with a [113] tensile axis. The two equally stressed glide systems with the highest Schmid factor would be expected to form subboundaries of the type predicted by Kear.2 The alignments of etch-pits on sections parallel to different (111} planes consistent with these types of boundaries were not observed. However, they were consistent with planar subboundaries (on a macroscopic scale). From an analysis of Amelinckx1 it may be shown that stable cross-grid dislocation boundaries may form in the primary slip planes. These boundaries form when dislocations with a Burgers vector not in the slip plane move into the plane by combination of climb and glide. THE geometry of subboundaries formed by the interaction of dislocations of two glide systems has been analyzed by Amelinckx,1 and the particular types produced by deforming fee crystals are predicted by ear.' In this paper types of boundaries which may be formed when climb as well as glide occur are discussed as this is relevant in high-temperature creep. It is assumed in the present investigation that the etch-pits observed in Cu + 7 wt pct A1 on surfaces parallel to {111} planes delineate the sites of dislocations. Although there is no direct evidence for this previous work on a-Cu/Al single crystals by Mitchell, Chevrier, Hockey, and Mon-aghan,3 would show this assumption to be reasonable. The alignments of etch-pits which form during creep are studied on sections parallel to each {111) plane. It is then deduced that these alignments are consistent with a specific type of planar subboundary. The Cu + 7 wt pct A1 single crystals had a [113] tensile axis and Fig. 1(a) shows schematically the relation of the slip planes and slip directions (as represented by tetrahedron ABCD) with reference to the tensile axis. The two equally stressed glide systems with the maximum Schmid factor namely ß-AD and (a-BD, from the analysis of Kear,2 would be expected to form the boundaries shown in Fig. l(a) and (b), also Fig. 5(a) and (b). EXPERIMENTAL PROCEDURE The a-Cu/Al single crystals were grown and annealed in a "gettered" argon atmosphere. Chemical analysis showed the aluminum content to be uniform in each crystal and the difference between crystals was maintained to an accuracy of ± 0.25 wt pct. The initial dislocation density and mean subgrain diameter after annealing was -106 cm-2 and 250 µ, respectively. Surfaces parallel to (111) planes were produced by specially developed electrolytic machining processes. The {111} faces were next electropolished for 5 min in a solution consisting of 25 g chromium trioxide, 113 ml glacial acetic acid and 40 ml water; the applied potential was 8 v. Dislocation etch-pits were revealed using l an etchant described by 1 ml bromine, 45 ml HCl, and - 250 ml water. RESULTS In crystals strained into secondary creep at higher stresses (443 and 750 g - mm-2 at 650° C aligned rows of etch-pits parallel to slip plane traces were evident in sections parallel to the (1111, (ill), and (111) planes, see Fig. 3. As well as the longitudinal alignments in Fig. 3, well formed randomly oriented arrays indicative of an equiaxed subgrain structure are evident. At the lower stresses (100 to 230 g . mm-2) only an equiaxed structure formed during creep. The sections in Fig. 3 are from a crystal crept for 70 hr at 650°C with a CRSS of 443 g.mm-2. Two identically oriented crystals were also deformed at the same temperature and stress for 5 min and 4 hr. In the crystal crept for 5 min, the etch-pits were randomly distributed with no tendency for directional alignment, see Fig. 2(a). As shown in Fig. 2(b) aligned arrays were evident after 4 hr creep but they were not nearly so well defined as in Fig. 3. The alignments (parallel to the arrows) in Fig. 3 are consistent with the existence of boundaries in the two main slip planes a and ß. The way in which this is deduced is seen by reference to Fig. l(c), where the existence of boundaries in the a and ß planes is verified by sectioning parallel to a,ß, and d. The (111) and ß(111) planes intersect the d(111) plane along BC [101 ] and AT [011] and alignments parallel to [101] and [011] are clearly evident in Fig. 3(c) in a section parallel to the d(111) plane. Similarly the a, and ß planes in Fig. l(a) intersect each other along DC [110] and hence there will be an alignment parallel to [110 ] in sections parallel to the a-plane and the ß-plane; this is evident in Fig. 3(a) and Fig. 3(b). It is interesting to note that alignments of etch-pits consistent with the boundaries predicted by Kear2 were not observed; see Figs. l(a) and l(b). The geometry of boundaries in {111} planes as shown in Fig. l(c) is discussed later. In Fig. 4(a) the individual etch-pits are resolved and the alignments are exactly parallel to the slip trace direction [101]. However, in some areas alignments deviate away from the slip trace direction by as much as 10 to 15 deg, this is evident in Fig. 4(b), and in Fig.

Jan 1, 1969

By John Freeman

THIS paper relates entirely to the casting of brass under fluid pressure in steel dies. Die castings of metals and alloys of low melting point have been available for many years but the development of brass die castings has been relatively recent, occurring within the past five years. The successful development of brass die castings has resulted from the availability of alloy steels that would give satisfactory life as dies and the development of suitable die-casting machines. The melting point of copper is 1084° C. (1983° F.) and of a high brass about 900° C. (1652° F.), as compared to 327.5° C. (621.5° F.) for lead, 419.4° C. (786.7° F.) for zinc and 658.7° C. (1217.7° F.) for aluminum, temperatures that are indicative of the casting temperatures required for the various types of alloys, of which the melting points are somewhat lower than those of the pure metals.

Jan 1, 1935

YEAR OF ELECTION 1913. FRANK DAWSON ADAMS, Montreal, Canada. 1938. HENRY CORT HAROLD CARPENTER, London England 1933. KARL EIKERS New York, N. Y. 1922. FEDERICO GIOLITTI Torino, Italy. 1906. SIR ROBERT A. HADFIELD London, England. 1921. FRANK WILLIAM HARBORD London, England. 1917. HERBERT HOOVER Washington, D. C. 1931. WALDEMAR LINDGREN Cambridge, Mass. 1921. C. McDERMID London, England. 1913. EZEQUIEL ORDONEZ Mexico City, Mexico. 1935. ROBERT PEELE New York, N. Y. 1938. A.M. PORTEVIN Paris France 1937. JOHN V.W. REYNDERS, New York, N. Y. 1937. GEORGE S. RICE Washington, D. C. 1911. ROBERT H. RICHARDS Cambridge, Mass. 1934. T.A. RICKARD Victoria, B.C., Canada

Jan 1, 1939

LEHIGH UNIVERSITY On April 25, the Mining and Geological Society of Lehigh University held a meeting and elected. the following officers for the college year 1918-1919: C. S. SCHUBERT, President, C. G. GILMAN, Vice-president, H. TSAI, Secretary, E. D. HOLLINSHEAD, Treasurer, C. N. TOMLINSON, A. A. KORVES, Curators. After a short business meeting the Society was favored by three interesting and instructive talks. Mr. C. A. Bonine spoke on the "U. S. Geological Survey" and showed a number of beautiful lantern slides; Mr. R. Rosenbaum read a paper on "Geodes;" and Prof. B. L. Miller presented a brief discussion on "War Minerals." H. TSAI, Secretary.

Jan 7, 1918

By A. K. Sinha

The market for thermal coal has recently been growing rapidly and it is projected to continue to do so in the foreseeable future. Both the national and international markets often demand high-Btu low-sulfur thermal coal in order to minimize the cost of utilization and meet the environmental restrictions. High quality thermal coal can be prepared to compete in the utility market by desulfurizing the high-Btu midwestern coal and blending it with low-sulfur western coal which is usually low in Btu content. The methods that can be used for optimizing the coal preparation plant operating parameters for physically desulfurizing coal are presented.

Jan 1, 1985

The Second Pan-American Scientific Congress will be held under the auspices of the United States Government in Washington, D. C., Dec. 27, 1915, to Jan. 8, 1916. The organization officers are John Barrett, LL. D., Director General of the Pan-American Union, Secretary General; Glen Levin Swiggett, Ph. D., Assistant Secretary General; the headquarters of the Congress are the Pan-American Union, Washington, D. C. The program of the Congress is divided into nine main Sections, which are given below with the name of the Chairman of each Section: 1. Anthropology, William H. Holmes, B. S., Smithsonian Institution, Washington. 2. Astronomy, Meteorology, and Seismology, Robert S. Woodward, Ph. D., Carnegie Institution, Washington, D. C. 3. Conservation of National Resources, Agriculture, Irrigation and Forestry, George M. Rommel, B. S., Bureau of Animal Industry, Department of Agriculture, Washington, D. C. 4. Education, P. P. Claxton, LL. D., Bureau of Education, Washington, D. C.

Jan 12, 1915

By G. R. Belton, Y. K. Rao

A galvanic cell, using liquid MgCl2 or MgC12-CaC12 mixtures as the electrolyte, has been used to determine activities in Mg-A1 liquid alloys between 700' and 880°C. The incovporation of a chlorine electrode in the cell also allowed measurements to be made of the standard free energy of formation of MgCl2(l). The results are shown to be in good agreement with thermo-chetrlical values from the literature, and this is taken as evidence that the small, known solubility of magnesium in iMgCl2 introduces no significant error in galcanic cell measurements. Within experimental error, the activity coefficients and relative partial molar enthalpies at 800°C are shown to be represented by the following "subregular" solution equations: logy~~ =-0.68(1 -xMgj3 log yAL =-1.02(1 - XMf + 0.68(1 - XMf H.M = -4400(1 - %)3 / cal Mg 7Ag' HZ =-6600(1 - xA1)' + 4400(1 - XMf cal SCHNEIDER and toll' have used a transpiration technique to measure the vapor pressures of magnesium over Mg-A1 alloys between 544" and 594°C. amsstad,' however, has since suggested that the extrapolation to zero flow rate, used by these authors in interpreting their apparent pressure vs flow rate data, gives unreliable results. Rogers, Tomlinson, and Richardson,3 in interpreting the results of solution equilibria between Mg-A1 alloys and liquid MgC12, also considered the measurements of Schneider and Stoll to be unreliable and preferred to derive activities for the alloys from the earlier boiling point determinations of ~eit~ebel~ and the partial molar heats recommended by Kubaschewski and ~atterall.~ These latter heats were based substantially on the early calorimetric work of Kawa-kami but, unfortunately, his work on other systems has sometimes been found to be inaccurate.7 Rogers et al., in the above-mentioned paper,3 tentatively concluded that the most likely species responsible for the limited solubility (0.3 mole pct at 800°C) of magnesium in MgC12 were Mg° (neutral) and Mg2++. Two more recent studies8,9 have supported Mg2++ as the soluble species. In the present study, activities in Mg-A1 alloys have been determined by means of a galvanic cell involving liquid MgCl2 or MgC12CaCl, mixtures as the electrolyte. Since the reactive nature of magnesium precluded simple Faraday yield experiments, a chlorine electrode was incorporated in the cell in order that the performance of the cell could be checked by measurements of the heat and free energy of formation of MgC12. This procedure was considered necessary since it has been suggested1' that the solubility of a metal in a molten salt might introduce electronic conductivity; also, previous determinations of the standard electrode potential for MgC12 differed by as much as 70 mv11-13 EXPERIMENTAL Materials. Analyses of the materials used in preparing the alloys and the electrolyte mixtures are presented in Table I. The alloys were prepared by induction melting weighed amounts of the metals in a graphite crucible held under an argon atmosphere. Pure anhydrous magnesium chloride was prepared by heating the mixture MgCl, . 6H20 +NH4C1(1:1) to 650°C, followed by melting under dry argon. The melting point of the dry MgC12 was found by differential thermal analysis to be 714.8oC, which compares well with the accepted value of 714C.14 This agreement was taken to be an indication of the high purity of the dried salt. Table I. Compositions of Materials, wt pn Impurity Mg Al MgCI2 CaCI, Ba - - 0.005 Ca - - 0.010 Cu 0.02 0.02 Fe - 0.10 0.001 0.010 Pb 0.01 - 0.001 0.005 Mn 0.15 0.001 Si - 0.10 Sr - - 0.005 MBSO* - 0.040 ARGON TUNGSTEN CHLORINE LEAD—411 11 II ALUMINA 'A I / ave GRAPHITE on irA~_ ( ^"l ROD MAGNESIUM S>ILICA~^ /, OR ALLOY-. I /A] ___________ -«^- _ ELECTROLYTE I y FRITTED DISCS Fig. l—Arrangement of chlorine and metal electrodes in electrolytic cell.

Jan 1, 1970

By G. Willard Quick

TENSILE tests of rail steels at elevated temperatures'' have shown that certain rails, in addition to having low ductility in the well-known bluebrittle range in the neighborhood of 200° C., have marked reduction in elongation and reduction of area in the temperature range from 400° to 700° C. This range of low ductility was called "the secondary brittle range" and the phenomenon, "secondary brittleness." The question naturally arises as to whether this property of the steels would be shown by impact tests performed in the same range of temperature. If so, the impact test, as suggested by Gillett3 would be a simpler and quicker method for the routine examination of steels at elevated temperature than the tensile test. A number of investigators have reported results of impact tests on steels at elevated temperatures, in which the energy absorbed decreased with increase of temperature above 200° or 300° C. Langenberg4 performed Charpy impact tests on several steels at temperatures ranging from room temperature up to 1000° F. (538° C). His results showed an increase in the energy absorbed in specimens tested in the range from room temperature to 200° or 300° C. and then a gradual decrease in the range, 300° to 538° C., the maximum temperature used. Greaves and Jones5

Jan 1, 1932

[Appalachian Petroleum Section: James M. Kimbrough, chairman; John H. Adair, first vice-chairman; Walter L. Diddle, second vice-chairman; Byron M. Finch, secretary-treasurer. Balcones Section: Robert V. West, chairman; Frank W. Jessen, first vice-chairman; Zane V. Morgan, second vice-chairman; Brantley G. Myers, secretary-treasurer. Meets 4th Wed., Petroleum Club (San Antonio) or Terrace Dining Room (Austin) Billings Petroleum Section: Charles B. Evans, chairman; L. M. Lyon, first vice-chairman; Gordon E. Lansford, second vice-chairman; Fred. A. Haddenhorst, secretary-treasurer. Meets 3rd Tues., Billings Petroleum Club. California Coastal Section: Robert L. Richardson, chairman; David K. Hayward, first vice-chairman; W. Jackson Bransford, secretary; William N. Harwell, treasurer. Meets 3rd Thurs., Pierport Inn, Ventura. Caracas Petroleum Section: Edwin A. Moo re, chairman;. Jose Cirigliano, vice-chairman; Frank B. Davis, secretary; Robert N. Powers, treasurer. Meets 2nd Tues., Caracas Theater Club.]

Jan 1, 1961

MONTANA SECTION FREDERICK LAIST, Chairman F. W. BACORN, Vice-chairman E. B. YOUNG, Secretary-Treasurer, 52G Hennesy Building, Butte, Mont. C. H. CLAPP C. D. DEMOND The Montana Section held its annual meeting at the Silver Bow Club, Butte, Mont., on Friday, Feb. 7. The technical session was preceded by a dinner at which 54 members and guests were seated. N. B. Braly presided at the dinner and the, business and technical sessions. The officers whose names are noted above were elected for the ensuing year. H. B. Pulsifer presented a paper on The Metallurgy of Aluminum and Magnesium; it was discussed by C. H. Clapp and F. A. Linforth. J. C: Horgan presented a paper on The Manufacture of High Explosives and their Use in Metal Mines; it was discussed by C. W. Morse, J. J. Carrigan, and C. W. Goodale. The matter of reformed spelling as proposed in a circular letter coming from Palo Alto, Calif., was discussed, after which the Secretary was instructed to write to Secretary Stoughton and ask that when the matter is opened for discussion in New York he present the emphatic protest of the Montana Section against the alleged reforms in spelling. E. B. YOUNG, Secretary.

Jan 4, 1919

By C. W. Parmelee

THE ideal fuel for burning ceramic wares is the one that, among other characteristics, has little or no sulfur. For that reason wood was long considered the most desirable fuel but its high cost has practically eliminated its used except in regions where it is very abundant or other circumstances warrant its choice. The fuels commonly employed are natural and producer gas, oil, and coal. The last named is undoubtedly the most important, not only in this country but abroad. Occasionally anthracite is used but the larger part is bituminous. The quality of the coal used depends on the kind and the value of the products being manufactured. For some materials, such as common brick, hollow block, etc., the quality of the coal is of less importance than in the manufacture of polychrome terra cotta, pottery, porcelain, etc. It is obvious that in burning clays that contain notable amounts of pyrite, marcasite or gypsum, as is the case with many common clays, the sulfur content of the fuel is of much less importance. The permissible amount of sulfur in the coal used will depend on the kind of product being manufactured. "A good sample' of coal commonly used in pottery ovens has something like this quantity of sulfur." PER CENT. Total sulfur 1.20 Sulfur in the ash 0.11 Volatile sulfur a 1.09

Jan 9, 1919

By Charles Austin

IN an earlier series of studies on 18-8 stainless steel at 600°, 700°, and 800°C.1 one pretreatment was used throughout; viz., 15 min. in hydrogen at 950°C., followed by an air quench. Several manufacturers of this alloy since have expressed doubt as to the suitability of the temperature employed, recommending instead the more customary Strauss treatment as promising superior results. In this subsequent investigation on the effects of the temperature of pretreatment several interesting points have arisen, which are described in this paper. Previous work on our equipment had shown a marked difference between alloys of "similar chemical composition" that had been manu-factured by different companies. Accordingly, one mill-bar length was selected from which to prepare all specimens. It could then be assumed that any marked differences in creep characteristics would be due to effects resulting from variations in the pretreatment of the alloy. The material was furnished by the Allegheny-Ludlum Steel Co. in the form of 5/16-in, dia. rod, finished by air cooling from a mill anneal at 1950°F. (1066°C.). It was analyzed only for the elements shown: carbon, 0,07 per cent; chromium, 18.73; nickel, 9.46; manganese, 0.40. Three pretreating temperatures were chosen, the specimens being held for 15 min. in hydrogen at either: (1) 1150°C., to conform to the recom-mended Strauss treatment; (2) 950°C., to compare with the results of previous tests; or (3) 750°C., to initiate precipitation of carbides in the material before testing. As the test cross sections were only 1/8 -in. dia., air cooling followed the annealing treatment. These treatments per-mitted two direct comparisons: (1) between the 1150° and 950°C. treat-ments to indicate the effect of grain size when all carbides were probably in solution at the start of the test; and (2) between the 950° and 750°C. treatments to indicate the effect of carbide "nucleation" for similar grain sizes.

Jan 1, 1940

By H. Conrad, K. Janowski, G. Stone

The available data on the dynamics of plastic flow of sapphire indicate that the deformation rate in the temperature range .from 900° to 1700°C can be expressed either as A number of investigators1-10 have established that sapphire deforms plastically above 900°C, the most common mode of deformation being slip on the basal plane in the [1120] direction. Under certain conditions and at temperatures above 1500°C, slip

Jan 1, 1965