ALTHOUGH the open-hearth charge contributes CO, C02, H2, and water vapor to the combustion gases and absorbs oxygen from them, in the main the thermal effects in the melting charge and molten bath can be considered independently of those in fuel combustion; the latter then is regarded simply as the source of the net heat required to finish a heat of steel. First of all, it should be remembered that a large percentage of the heat supplied to the bath is furnished by oxidation of the various elements in the charge itself. If this charge consisted of 80 to 100 per cent of hot metal and the oxidation were accomplished by blowing in air or oxygen, as in the bessemer converter, the net heat absorption would be negative; that is, the bath would contribute part of the heat required to keep the melting chamber hot, in addition to that contained in the finished steel and slag. - In actual open-hearth practices, probably the nearest approach to this is in the duplex furnace, charged with bessemer-blown metal and some hot metal, where very little heat is required to complete the refining and nearly all the heat energy from fuel combustion is used to keep the roof and walls of the melting chamber up to around 2900 to 3000 F (1600 to 1650 C), so that the bath will not cool off during the refining. The other extreme is with all-cold charges containing around 80 per cent steel scrap and 20 per cent cast iron or cold pig iron, in which case a very large proportion of the heat in the bath at tap is supplied from the fuel combustion. THERMAL EFFECTS IN MELTING In a typical heat, the fuel furnishes about four million British thermal units per ton of steel produced. The heat required for the metallurgical processes is not easily defined in useful manner but it ranges downward from about one million Btu, depending not only on the charge but on the manner of calculation. In any event, this requirement appears small in comparison with the

Jan 1, 1951

By R. G. Davies

Isothermal annealing of quenched Fe3Al reveals that the superlattice forms by the nucleation and growth of ordered domains. The activation energy for isothermal ordering and initial domain growth is -29 keal per mole, which is thought to he the activation energy for vacancy migration. Domain growth, in the absence of excess vacancies, has an activation energy of -100 keal per mole. A maximum in the hardness is observed when the structure consists Of ordered domains, -35-4 in size, growing into a short-range ordered matrix and, also as a function of degree of order, S, with an infinite domain size at S = 0.4 to 0.5. It is proposed that both maxima are due to a transition from deformation by unit dislocations to deformation by superdislocntions. FE-AL alloys containing more than -23 at. pet Al, when quenched from above the critical temperature for the Fe3A1 type of order, always contain the maximum possible amount of FeAl (B2) type of order' (see Fig. 1). Thus when the Fe3A1 superlattice forms, in a 25 at, pet A1 alloy, it does so from an imperfect FeAl structure. The formation of the Fe3Al superlattice has been the subject of several recent X-ray,1, 2 electrical-resistivity,3"6 and dilatometric3 investigations. McQueen and Kuczynski3 concluded that the isotherma1 ordering of Fe3Al, after quenching from 800°C (T,, the critical temperature for order, is 55O°C), takes place by the nucleation and growth of ordered domains. However, Feder and Cahn4 found that the isothermal ordering was complex but more like a homogeneous nucleation process than a nucleation and growth process. Lawley and Cahn2 reported that the degree of order is a continuous function of temperature which is a characteristic of a homogeneous nucleation process. Thus, the evidence is conflicting as to the nature of the Fe3Al ordering reaction. Lipson7 was the first to suggest that ordered domains should exist in the Fe3A1 structure since, as

Jan 1, 1964

By Jack Washburn

The c axis indentations in zinc crystals were shown to undergo 100 pct strain recovery on heating. The mode of deformation and the details of the polygonization and collapse of indentations were found to be consistent with a number of predictions of dislocation theory. IT has been observed that indentations of the type made by Jillson in zinc crystals can, under certain conditions, be macle to shrink in size and even completely disappear on heating the crystal, Fig. 1. The details of the process are interesting in that they afford a simple experimental illustration of several predictions of dislocation theory. The indentations were made as shown in Fig. 2 by dropping a 0.2 g indenter with a hemispherical point on a cleavage face of a. zinc crystal. Such indentations can be made through relatively great thicknesses in the c-axis direction. The material close to the struck surface, where mechanical twinning and complex distortion occurred, was removed by cleavage. The remaining crystal, which was about 1 cm thick, contained a dent that was accurately round and almost the same size on both top and bottom surfaces. The indentation had the form of a flat cone of half angle approximately 89°, having a rounded apex and a rounded intersection with the unde-formed part of the crystal. The mode of deformation was primarily slip on the three equivalent systems in the basal plane. Six types of dislocation loop (plus and minus in each of the three directions) as shown in Fig. 3 are required by the geometry of the indentation. The maximum shear strain in the radial direction amounted to approximately 2.5 pct. Slip was distributed in the usual, microscopically nonuniform, manner among the possible parallel slip planes. When an indentation was made close to a (2110) surface, three separate sets of interpenetrating slip bands appeared as shown schematically in Fig. 3. A small biaxial tension strain in the plane of (0001) is also a geometrical necessity for the formation of an indentation. If the sides of the dent are tilted l° with respect to the undeformed surrounding crystal, and the surround-

Jan 1, 1957

By W. E. Mitchell

The ore that is being treated by the present plant lies between the leached zone, or capping, and the mixed sulfide and oxide zone. The principal copper minerals are chalcanthite (CuS04.5H20), brochantite (CuSO4.3Cu (OH)2 and atacamite, (CuC12.3Cu (OH)2). There are, in addition, some other minerals such as cuprite and kröhnkite (CuS04. Na2S04.2H20). These minerals, with many others, occur in a greatly crushed granodiorite rock. most of the copper-bearing minerals occur in the cracks and veinlets, but there are disseminated values and it is probably the relative proportion of these that accounts for some otherwise unexplainable variations in extraction. The entire mineralization of the ore is complex and varies with depth. This variation, the problems presented thereby, and the effect of various constituents of the ore will be taken up in detail. An analysis of :in unweighted composite of the ore treated during 1927 follows: I'Lr Cent. Per Cent. Per Cent. Cu............... 1.58 S................. 2.10 Mo............ 0.01 SiO? ............. 66.10 HNO3 ........0.03 As............ 0.005 Fe.......... 1.41 C1 .............. 0.05 Sb............. 0.005 CnO ..... 0.20 Na................ 0.80 Ba............ 0.01 A1203 .......... 17.70 KI.............. 4.80 H20............ 0.70 mgO.............. 0.68 Mn............... 0.07 0 in sulfates. . . . 3.94 Total..... 100.19 The most important constituents of the ore, as indicated by experience to date, are: (1) The total copper content; (2) the acid-insoluble copper; (3) the acid-making copper mineral, mainly the chalcanthite; (4) the chlorine; (5) the nitrates; (6) the soluble iron; (7) the soluble molybdenum. The total copper content needs no discussion. In Table 1, the values are weighted averages calculated from individual charge analyses. The acid-insoluble copper directly affects the extraction, as the present leach recovers practically no acid-insoluble copper. In Table 1 the values are unweighted averages of the analyses of monthly composite samples. The acid-making copper mineral affects the amount of copper that can be dissolved from the ore without neutralizing acid in the solution. The

Jan 1, 1930

By J. A. Solomon, H. E. Shafer

As a result of the great demand for metallic aluminum and the scarcity of domestic bauxite, numerous processes have been proposed and developed to extract the oxide of this metal (Al2o3) from clays, shales, and other low-grade raw materials.1-4 An exploratory study was made to extract alumina with sulfuric acid from relatively impure coal-associated draw-slate and to establish an optimum calcination temperature for maximum recovery. Draw-slate is the term used to describe the hard, slaty material directly overlying many coal seams and may range from a few inches to a few feet in thickness. Alumina content of these draw-slates may range from as low as 15% to over 35%. Although the following results are limited in scope, some of the data should prove beneficial for further work. Coal-associated clay, shale, and gob heretofore have been considered nuisance products; any successful alumina extraction process would greatly enhance the worth of these almost limitless resources. This research demonstrated that an optimum calcination temperature for alumina extraction could be established for a coal-associated draw-slate and that this temperature was lower than those suggested in previous work with unspecified clay types. It should be noted that slightly higher acid concentrations and somewhat finer particle sizes were used in this series of tests as compared to previous work. EXPERIMENTAL WORK Essentially, alumina extraction proceeded in four steps: 1) grinding, 2) calcining, 3) acid leaching, and 4) precipitating of aluminum sulfate. An initial series of reference tests to determine the optimum temperature of solubility for alumina was run using relatively pure kaolin. Kaolin forming clays are hydrous aluminum silicates of the approximate composition 2H2O A12O3 2SiO and kaolinite is the mineral that predominates in most kaolins. 5 The kaolin was ground to -30 mesh and subsequently calcined at temperatures ranging from 100°C to 700°C. Each sample was calcined for 1 hr in a muffle furnace and in turn subjected to sulfuric-acid leaching (H2SO4, 9 molar) for a 2-hr period. The filtrates were analyzed for the amount of dissolved alumina recovered.637 Also, each sample of leached or barren residue was

Jan 1, 1968

By Shiou-Chuan Sun, R. F. Wesner, J. D. Morgan

FOR successful electrostatic separation, the behavior of the component minerals of the tested ore under various conditions should be known. In the course of investigation, it was found that these are difficult to measure accurately by the presently available methods. The method used by Johnson1 is handicapped by the fact that particles in the extreme front and rear end of the falling stream are difficult to control or observe accurately. Furthermore, this method is not applicable when the tested sample consists of more than one mineral. The deflection method, as reported by Fraas,' is inadequate to show the differential amounts of mineral particles deposited at the various horizontal positions under the grounded roll of the separator. This weakness is further noted when the tested sample contains more than one mineral. The purpose of this paper is to introduce a new method capable of measuring the behavior of mineral particles under various conditions, and of defining the optimum condition for separation. The main factors which influence the behavior of mineral particles in electrostatic separation are also described. dividing gauge and the two attached collecting chutes of a Johnson separator.~ This distribution analyzer consists of sixty or more 1.0-cm wide cells as shown in part in fig. 1; it has been fully described in a previous article." Except where otherwise stated, the testing procedure used in this paper is as follows: (a) calculate the weight of feed for a l-min run at a constant feed rate of one layer of closely packed particles falling on the grounded roll; (b) weigh and dry the feed at 100°C for 12 hr; (c) place the top of the distribution analyzer level 4 cm below the bottom of the grounded roll, so that the cells are longitudinally parallel to the grounded roll and the zero edge of a suitable cell is directly under the front vertical tangent to the grounded roll (see fig. 1); (d) with the charged roll at a negative potential of 15.5 kv, the dry hot sample is introduced into the feed chute at a constant feed rate; and (e)

Jan 1, 1951

By Shiou-Chuan Sun, R. F. Wesner, J. D. Morgan

FOR successful electrostatic separation, the behavior of the component minerals of the tested ore under various conditions should be known. In the course of investigation, it was found that these are difficult to measure accurately by the presently available methods. The method used by Johnson1 is handicapped by the fact that particles in the extreme front and rear end of the falling stream are difficult to control or observe accurately. Furthermore, this method is not applicable when the tested sample consists of more than one mineral. The deflection method, as reported by Fraas,' is inadequate to show the differential amounts of mineral particles deposited at the various horizontal positions under the grounded roll of the separator. This weakness is further noted when the tested sample contains more than one mineral. The purpose of this paper is to introduce a new method capable of measuring the behavior of mineral particles under various conditions, and of defining the optimum condition for separation. The main factors which influence the behavior of mineral particles in electrostatic separation are also described. dividing gauge and the two attached collecting chutes of a Johnson separator.~ This distribution analyzer consists of sixty or more 1.0-cm wide cells as shown in part in fig. 1; it has been fully described in a previous article." Except where otherwise stated, the testing procedure used in this paper is as follows: (a) calculate the weight of feed for a l-min run at a constant feed rate of one layer of closely packed particles falling on the grounded roll; (b) weigh and dry the feed at 100°C for 12 hr; (c) place the top of the distribution analyzer level 4 cm below the bottom of the grounded roll, so that the cells are longitudinally parallel to the grounded roll and the zero edge of a suitable cell is directly under the front vertical tangent to the grounded roll (see fig. 1); (d) with the charged roll at a negative potential of 15.5 kv, the dry hot sample is introduced into the feed chute at a constant feed rate; and (e)

Jan 1, 1951

By J. E. Hilliard

Various methods are given for estimating the number per unit volume and average size of convex particles from measurements on a projection through a slice of the structure. The determination of the size distribution is considered specifically for spherical particles. The results are applicable to any type of transmission microscopy and also to the correction of measurements made by reflected light on semitransparent materials. WITH the advent of electron transmission microscopy, the metallurgist is confronted with the problem of relating a projected image to the three-dimensional properties of the structure. This paper deals with the estimation of the number per unit volume and size of particles dispersed in a matrix. The case of convex particles will first be treated (the results will be applicable as approximations to particles of more general shape) and then spherical particles will be considered specifically. The latter represent a special case frequently encountered in practice and one which is also amenable to a calculation of the effect of overlap on the observed particle-size distribution. Although the present treatment was prompted by the needs of the electron microscopist, the results are applicable to transmission studies with any type of radiation. In addition, they can be used in the analysis of semitransparent materials by reflected light, the depth of light penetration corresponding to the thickness of the slice or section used in the transmission studies. 1) CONVEX PARTICLES 1.1) General Expression for N,. We will suppose that a "center" (such as the center of mass) is assigned to each particle. The convention used for defining the center is immaterial providing it does not depend on the orientation or location of the particle. Consider a slice through the structure having a pair of parallel faces a distance t apart. It will be assumed that the slice is randomly located with respect to its perpendicular distance from some fixed point, but it is not necessary to assume that its orientation is random. Our problem is to deduce the relationship between the number of par- ticle images seen on an orthogonal projection through the slice with the number, Nv, of particles per unit volume in the original structure.* *Symbols are listed in the Table. The expected number of particles with centers lying within the slice is Nvt per unit area. In addition, there will be elements in the slice contributed by particles whose centers lie without. The number of such elements will be the same as the number of intersections occurring on a two-dimensional plane through the structure; namely N~K, where K is the mean distance, Fig. 1, between tangent planes to a particle averaged over all particles, i.e., Where Ni is the number of particles of class i having the same shape and size, and pi (4, 8) is the probability that an i particle will have a given orientation with respect to the slice. If the particles are randomly oriented, then K is independent of the orientation of the slice and equal to the mean cali-per diameter. The total number of particle elements in the slice is therefore Nv(t + K) per unit area, but fewer will be seen as separate images on the projection plane because of overlap. If MA is the number of elements "lost" by overlap, the number of images per unit area will be NA = Nv(t + K) -MA 121 MA is a function of the slice thickness and must vanish at t = 0. As t increases, NA at first increases, reaches a maximum, and thereafter decreases as the overlap term MA becomes predomi-

Jan 1, 1962

By R. G. Jones, W. L. Kinney, R. E. Schilson, R. S. Wilson, G. A. Clark, H. Suralo

This paper discusses the results of the Fry conventional or cocurrent in situ combustion test, which was conduct-ed in a 3.3-acre inverted five-spot. The depth of the formation was between 880 and 936 ft; the oil had a specific gravity of 28.6° APl and a viscosity of about 40 cp at the reservoir temperature of 65°F. Preceding the combustion test, air injection tests were conducted which, in conjunction with geological studies, were used to evaluate the characteristics of the reservoir. Combustion was initiated on Oct. 13, 1961, with ignition being accomplished by a 40 kw electrical heater. The test phase of the project ended on Oct. 1, 1963. During the test, the average air injection rate was 1,520.-000 scf/D. Throughout the test, production of all fluids— gas, oil, and water—was monitored. Cumulative oil production credited to the project was 100,586 bbl. The cumulative air-oil ratio was 11,500 scf/bbl oil, and the oxygen uti1ization efficiency was 87 per cent. INTRODUCTION The Marathon Oil Co. conducted a successful in situ combustion test, beginning Aug. 22, 1961, at the Fry unit, Crawford County, 111. The purpose of the project was to test the feasibility of cocurrent in situ combustion as a means of oil recovery in the Fry type reservoir. Interest in in situ combulstion as an oil recovery tool has been stimulated mostly by the existence of large reserves of heavy viscous crudes with low expected recovery, usually less than 10 per cent. These are the so-called unrecoverable reserves, and most combustion tests to date have been conducted in this type of reservoir.1-4 In contrast, the Fry combustion test was conducted in a reservoir with a relatively high gravity oil having a relatively low viscosity. This paper discusses the performance of the test. The geology of the reservoir and the field operations are discussed in separate papers.5 TEST SITE The Fry combustion test was carried out in a 3.3-acre inverted five-spot portion of a lenticular body of Robinson sandstone. Net sand was 50 ft thick, porosity averaged 19.7 per cent, oil saturation was 68 per cent of pore volume, and water saturation was 20 per cent of pore volume. The oil in place was estimated at 1,040 bbl/acre-foot, or 171,600 bbl within the 3.3-acre pattern. The water in place was 326 bbl/acre-foot, or 53,800 bbl. The oil has a specific gravity of 28.7° API and a viscosity of 40 cp at the reservoir temperature of 65°F. AIR INJECTION PERFORMANCE Air injection took place in two phases, the phases separated by ignition of the reservoir. In the pre-ignition phase, air injection tests were conducted in the summers of 1960 and 1961. These indicated that the Fry reservoir was confined, and a high return rate of injected air could be expected. This proved to be an outstanding characteristic of the project, as cumulative gas production was 95.3 per cent of the air injected. The difference between the cumulative air injected and the total gas produced can be largely accounted for by the quantity of air stored in the reservoir. An estimated 16 X 10 cf of air remained in the burned-out portion of the reservoir and an indeterminate amount of gas was stored in the unburned but pressurized reservoir. Hence, a complete material balance of gases would account for nearly 100 per cent of the air injected. At times during the test, the daily gas production rate was 98 per cent of the daily air injection rate. Fig. 1 presents the air injection history of the Fry com-

Jan 1, 1966

By George S. Ansell, John B. Hudson, Stephen A. Koffler

The permeability of hydrogen through the a phase of palladium has been measured by a low pressure permeation technique under conditions such that bulk diffusion was the rate-controlling process. The observed permeability is described by the equation: J = 1.80 x 1O-3 P½exp(-3745)/RT) cc(stp)/sec/cm2/en over a range of hydrogen pressure, P, from 2.9 x 10-5 m Hg to 5.0 x 10-3 cm Hg, and over a temperature range, T, from 300" to 709°K. The fact that the permeability shows a square root dependence on pressure and a reciprocal dependence on thickness was taken as evidence that bulk diffusion, rather than surface reactions, was the rate-controlling process. The permeability data were used in conjunction with the solubility data of Salmon et al., to determine the diffusivity of hydrogen through palludium as: D = 4.94 x 10-3 exp(-5745/RT) cm2/sec There was no influence of sub structural defects observed over the temperature range employed. From the permeability data obtained, coupled with grain size measurements, it was concluded that the ratio of grain boundary diffusivity to bulk diffusivity was less than 105 over the range of temperature investigated. THE diffusive mass transport of hydrogen in the a phase of palladium has been studied previously by numerous investigators.' In spite of the large amount of attention this system has received, there is not good agreement between the results obtained in different investigations.' This is due in part to the fact that the mass transport was surface-limited during some of these studies, rather than being diffusion-controlled3-5 The reason for the disagreement in other cases is not clear. These studies made use of such techniques as rate of absorption from solutions6 and gases,' electrochemical potential,8 time lag,' and permeation10,11 to determine the mass transport behavior. Of these, the gas permeability technique is the only method which allows an easy test to determine if diffusion is the rate-controlling mechanism, thus eliminating the uncertainty regarding the limiting transport processes inherent in the other techniques. The two most recent permeability studies are those of Toda10 and Davis." Toda determined the permeability of hydrogen in the a phase of palladium over the temperature range from 170" to 290°C, and over the pressure range from 36 to 630 mm Hg utilizing a steady-state gas-permeability technique. Toda's result was: J = 1.41 x 10-3 P½ exp(-3220/RT) where J = specific permeability in cc(stp)/sec/cm2/cm, P½ = square root of the inlet pressure in (cm Hg)½, R = Universal gas constant, and T = temperature in deg Kelvin. Davis11 also employed a steady-state gas-permeability technique over the temperature range from 200" to 700°C and over the pressure range from 0.02 to 760 mm Hg. His result for the permeability of hydrogen in the a phase of palladium was: J = 3.15 x 10-3 P½ exp(-A440/RT) In the range of overlapping temperature for these two investigations, the values of the specific permeability calculated from the above two equations differ by a factor of about 1.8. In the present investigation, the permeation of hydrogen in the a phase of palladium was determined over a wide temperature range, 27" to 436oC, and over the pressure range from 2.9 x 10-5 to 5.0 x 10-3 cm Hg. This temperature range overlaps that of the previous investigations of Toda and Davis, but also covers the lower temperature range which has never before been investigated. The lower pressure range used here avoided the interaction between the dissolved hydrogen atoms observed at higher hydrogen concentrations.' MATERIALS The as-received palladium specimens were cold rolled from a casting and were supplied as 5.08 cm discs of 0.508 and 0.762 mm thickness. According to J. Bishop and Company specifications, the composition of the discs was 99.95 pct Pd, the balance being Cu, Ag, Au, and Ir. In order to obtain samples of varying grain size, the as-received discs were then heat treated. Sample 1 was treated for eight minutes in a nitrogen atmosphere at 810°C and then air-cooled. Sample D was heated first to 550°C in helium. The helium atmosphere was then immediately replaced by hydrogen and the temperature was slowly raised to 1220°C and held for 22 hr. The sample was then cooled to 550°C where the hydrogen was replaced by helium and the disc was further furnace-cooled to room temperature. Sample H was given the same heat treatment, only with hydrogen substituted for helium below 550°C. The reason that hydrogen was not used throughout the entire annealing cycle for samples D and H was to prevent the distortion encountered by low-temperature cycling in hydrogen observed by Darling." After these heat treatments were completed, the

Jan 1, 1970

By AIME AIME

AT a joint meeting of the Tulsa Geological Society and the Mid-Continent Section of the A; I. M. E., held at Tulsa on March 21, the history of unit development in the Kettle- man Hills field was discussed. Robert C. Patterson? Super- visor for the U. S. Geological Survey at Taft, Calif., was the speaker. An abstract of some of his remarks follows: On July 1, 1923, curtailment agreement for two years was made between the operators of North Dome Kettleman and the U. S. Department of the Interior. In this it was agreed to consider a plan of unit development, or other cooperate method of developing the structure. As a result, Kettleman North Dome Association was incorporated in December, 1930, as a non-profit cooperative corporation under the laws of California. Approved in January, 1931, by California Oil and Gas Supervisor and by Secretary of Interior. On Feb. 10, 1931, it became an active organization through election of executive officers and eleven- directors. General manager chosen. Association started to function April 1, 1931. Assumed control of 10,800 acres of proved and semi-proved land, as shown in Table 1.

Jan 1, 1932

By Y. Baskin

Solid-solubility relationships in the Pseudobinary systems UAS-UP, UAs-US. UAS-UC, aid UAs-UN were investigated. The first two systems exhibit complete mutual solubility, whereas the component compounds in the other two systenzs are immiscible. The above information, together with solid-solubility data joy six additional pseudobinary systems , were analyzed for compliance wilh the Hurrze-Rothery rules for rnetallic systems. The relative size difference of the component nonmetal atoms was found to be the dopainant jactor determining the extent of solid solubility between the NaC1-type uranium compounds. The anionic and covalent radii of the nonmetal atoms appear to be inadequate for these systems, but compuled radii based on rare earth compounds yield consistent results for the uranium compounds. THE actinide elements, like metallic elements of the transition and rare earth series, readily form binary compounds with nonmetallic elements of groups IV, V, and VI of the periodic table. Of particular importance are the NaC1-type equiatomic compounds with carbon, nitrogen, sulfur, phosphorus, and arsenic. The uranium members of this family of compounds have high melting points, are essentially stoichiometric, and exhibit various amounts of mutual solubility. Thus, they are of interest for investigating the factors governing the extent of solid solubility. Previous investigators have determined the solid-solubility limits in the pseudobinary systems between the compounds UC, UN, US, and UP. Anselin et a1 .' reported complete miscibility in the system UC-UN. Baskin and shalek 2 and Allbutt et a1.3 reported that UP and US exhibit complete mutual solubility. Shalek and white4 reported partial miscibility in the system US-UC. At 1800°C the maximum solubility of UC in US is 40 mol pct, but that of US in UC is 4 rnol pct. shalek5 found limited solubility in the system US-UN; the maximum solubility of UN in US is 11 rnol pct at 1800°C, while that of US in UN is only 0.3 mol pct. White and askin 6 found very limited miscibility in the system UP-UC at 1800°C. Approximately 7 mol pct UC is soluble in UP, but there is no solubility of UP in the monocarbide. Phase relations in the pseudo-binary system UN-UP were investigated by askin.' Approximately 0.7 mol pct UN is soluble in UP at 1800°C, while UP is immiscible in UN. The present study was carried out to explore the extent of terminal solubility in the systems UAs-UC, UAs-UN, UAs-US, and UAs-UP. This information, combined with existing data, provided a sufficient basis on which to determine the factors governing solid solubility in pseudobinary systems containing NaC1-type uranium conpounds. I) EXPERIMENTAL 1) Materials. The compounds UC and UN were obtained from the Kerr-McGee Corp. and United Nuclear Co., respectively. The US, UP, and UAs were synthesized by reacting finely divided uranium with H2 S, pH3, or AsH3 gas at low temperature (300° to 500°C), followed by homogenization in a vacuum at moderately high temperatures (1400° to 1700°c).8-10 The materials were essentially stoichiometric, with the exception of UC, which exhibited a C/U ratio of 1.05. Oxygen was the major contaminant in these compounds, ranging from 0.05 wt pct in US to 0.30 wt pct in UC, and it was generally combined with uranium to form UO2. The UO2 content in these materials was usually of the order of 1 wt pct, and did not exceed 2 wt pct. Furthermore, no evidence was found for a high-temperature reaction between uranium dioxide and any of the compounds. Chemical analyses of equilibrated compositions in the systems UAs-UP and UAs-US showed that the non-metal atom to uranium ratios averaged about 1.01, and that the oxygen contents ranged from 0.06 to 0.22 pct. However, the small deviations from stoichiome-try or the presence of minor oxygen impurities do not invalidate the conclusions to be drawn from this study. 2) Experimental Procedures. The component compounds in powdered from were blended in the desired proportions for 5 hr in the ball mill that consisted of stainless-steel balls in a plastic container. Chemical analyses indicated very little metallic pickup from the blending operation and virtually no increase in oxygen content. The pellets were pressed in a 0.270-in.-diam steel die under 40,000 psi pressure. One wt pct of stearic acid dissolved in CCl 4 served both as a binder and as a die lubricant. Chemical analyses revealed that the stearic acid left no carbon residue in the sintered samples. The pellets were sintered in vacuum in an unsealed tantalum crucible. The temperature, measured with a calibrated optical pyrometer, was maintained at 1800" + 30°C for 3 hr. This was sufficient time for attaining equilibrium as no change occurred in either the lattice parameters or the sharpness of the X-ray patterns when samples were annealed for longer periods of time. The pellets were cooled with the furnace. Debye-Scherrer powder patterns were taken at room temperature with a 114.59-mm-diam Norelco powder camera and CuKor radiation (CuGI = 1.5405A). Unit cell dimensions were determined from a Nelson-Riley extrapolation to the high-angle reflections. The values for were precise to k 0.001A. 11) RESULTS X-ray and met allographic investigation revealed that complete mutual solid solubility exists in the pseudobinary systems UAs-UP and UAs-US. The lattice parameter vs composition plots, Fig. 1, show a

Jan 1, 1968

By AIME AIME

THE first meeting" of the Iron and Steel Division was held Tuesday afternoon, Feb. 17, with nearly 100 men present and C. B. Murray as chairman. This was a round table discussion of iron ore beneficiation and of its relation to blast-furnace operations, and only one paper was presented, by Clyde E. Williams. Mr. Williams discussed the future of the Lake Superior district in its relation to the iron and steel industry. He stated that although estimates had shown that the total life of the present known iron ore reserves of the Lake Superior district was 20 to 30 years and that many believed that as a result of this depletion foreign ores would be brought to the Atlantic Seaboard, thus causing a displacement of the steel industry to the East, he believed that the Lake Superior district would continue to be the important producer of iron ore used in this country for decades beyond the predicted time before the exhaustion of the present known reserves. He described the three general types of ores that required concentration and pointed out the needs for research and the proper methods to be used in processes for the beneficiation of these low-grade materials. He discussed the effects of fine concentrates and the use of agglomerated ores in the blast furnace. This general summary led to interesting and valuable discussion on the various economic, ore-dressing, and blast-furnace problems in large-scale development of beneficiation. Perry Harrison described recent developments in sintering and the properties of iron ore sinter. T. B. Counselman and W. H. Coghill discussed the merits of classification of iron ore previous to tabling. Robert Faulkner and J. E. Little described the beneficiation plant of the Bethlehem Steel Corporation.

Jan 1, 1931

By I. H. Warren, E. Devuyst

A review of the physical and chemical aspects of the direct leaching of metal oxides has been given and com- pared to recent data of the authors and co-workers. The physical aspects, including the anisotropy of the dissolution, the hydration and the zero point of charge of some metal oxides are discussed first and then the kinetics of the dissolution of metal oxides are considered. A general mechanism of the leaching of oxides which describes most of the observed results is proposed.

Jan 1, 1973

United Engineering Trustees, Inc. H. G. MOULTON, 40 A. L. QUENEAU, '38 ALBERT ROBERTS, '39 The Engineering Foundation GEORGE D. BARRON, '40 A. L. QUENEAU, '38 Engineering Societies Library Board H. K. MASTERS, '38' A. B. PARSONS, Ex-officio F. F. SHARPLESS, '37

Jan 1, 1936

By Bain, Edgar C.

THE results are presented of an investigation to discover the fundamental atomic conditions existing in Corson's high-copper alloys hardenable by means of silicide solution and reprecipitation. The study attracted the writer because it offered a very convenient example of the general type of hardenable alloys exemplified by duralumin. Sykes' iron-tungsten and iron-molybdenum alloys and the hardenable lead-antimony. SUMMARY OF RESULTS AND CONCLUSIONS In brief, the investigation shows that very perfect crystallinity exists in the solid solutions prepared at high temperature to contain as much dissolved silicide as possible. The lattice parameter of copper is altered very little by the amount of cobalt, nickel or chromium, and silicon dissolved. The hardening by drawing at a temperature to initiate precipitation of excess silicon and metal produces a remarkable change in the atomistics of the solid solution. The old perfection of crystallinity in the solid solution is destroyed and the new atomic spacings are of variable magnitude even in one grain, and a condition in a measure resembling that found in martensite is observed. Were no particles whatever precipitated by the drawing action, still ample causes for hardness would be in evidence in the solid solution alone. The lack of plane continuity in the crystal grains would oppose slip in a very effective manner. Complete annealing restores the crystalline perfection in large measure. In these alloys even the most sensitive methods failed to reveal the characteristic pattern of the silicide precipitated by the anneal, but this was largely to be expected as the amount is relatively small.

Jan 1, 1927

By R. E., Head

THE use of lime in flotation has become so general in recent years that its functions are familiar to plant operators. The conditions and phenomena described in this paper are of interest because they are directly associated with the use of lime as a reagent and the resulting formation of lime scale worth nearly $1 per pound for its gold content. It is not known to what extent lime scale is common in flotation plants where lime is used, but as several occurrences have been re- ported, its existence is not limited to one particular plant. In November, 1927, the author's attention was drawn to a lime scale that formed on the sides of Callow flotation cells in the Walker Mining Co. mill at Spring Gar- den, Cal. The scale was described as an accumulation of hard material that built up on the sides of both the rougher and cleaner cells and in some instances attained a thickness of 2 in. The lime scale builds up in the cleaner cell at the rate of about 1/10 in. per month, or slightly more than ?12 in. during six months' operation. The rate of growth in the rougher cells is slower, and about 3/s in. of scale forms in six months. Analyses' of typical lime scale samples are as follows:

Jan 1, 1928

Executive Committee. ROBERT H. RICHARDS, Chairman. ALBERT SAUVEUR, Vice-Chairman. TIMOTHY W. SPRAGUE. HENRY A. WENTWORTH. AUGUSTUS H. EUSTIS, Secretary, 131 State St., Boston, Mass. The twelfth meeting of the Boston Section was held at the Engineers' Club, 2 Commonwealth Ave., Boston, on Monday evening, May 5, 1913, fifteen members and three guests being present. The meeting was called to order by Vice-Chairman Albert Sauveur, who introduced the speaker of the evening, Utley Wedge, of Ardmore, Pa. Mr. Wedge read his paper on the chloridizing roasting of copper ores, which he illustrated with a stereopticon, and which will be published in full by the Institute. After Mr. Wedge had closed his paper, which was received with great interest by all the members, the following discussion took place: Professor Hofman said that iron was formerly thought to ho essential to the Henderson process, but that it is not absolutely essential. Mr.Wedge said that, as far as he. knew, the presence of some sulphates was an abso¬lute necessity, and that line ores can be worked satisfactorily, although lime has an effect on the subsequent leaching. He added that the low fuel consumption of the latest Wedge furnace is a result of direct application of the combustion gases to the ore. Ten per cent. of fuel was needed with the muffle furnace. By direct firing he has been able to reduce the fuel needed to from 2 to 4 per cent. In the latest types of furnaces the gases from the upper hearth are not used. There is doubtless some temperature at which the loss. from copper chloride volatilization becomes serious, but in practice on Rio Tinto ores troublesome losses are not experienced. The copper apparently does not become volatile at. the temperatures where we would expect that it would. There are doubtless ores in which there would be serious danger from losses from this source. The latest furnaces do not use the high temperatures that were needed in the former single-hearth Wedge furnaces.

Jan 7, 1913

By W. L. Saunders

THE world's greatest producing area is, geographically, in the midland region of North America about the Great Lakes. This area, with but one- third of the nation's population, produces, with the exception of tobacco and cotton, three-quarters of the principal staples. It provides the surplus or export grain, meats, dairy products, steel and leading minerals. The social and political condition of a nation is determined by its industrial efficiency, and the share of the commerce of the world obtained by a nation is fixed more by the economy of its transportation than by any other factor. It is an economic maxim that: The total cost is the cost of production plus transportation cost. The cost of carrying 1000 tons by water or 100 tons by rail is equal, over the same distance

Jan 1, 1921

Jan 1, 1910