Institute of Metals - Iron and Steel - Mineral Industry - Industrial Minerals Year ?Division - Petroleum Division ? Division - Coal Division - Education Division -Division 1918 W M CORSE 1919 1920 W. H BASSETT 1921 1922 W B PRICE RALPH ARNOLD 1923 E DEGOLYER 1924 G K ELLIOTT 1925 F JULIUS FOHS 1926 PAUL D MERICA 1927 JOHN M LOvEJOY 1928 S SKOWRONSKI A W AMBROSE RALPH H SWEETSER

Jan 1, 1952

[EDMUND M. WISE, Chairman ROBERT H. LEACH, Past-Chairman D. K. CRAMPTON, Vice-Chairman CARL E. SWARTZ, Vice-Chairman W. M. CORSE, Treasurer LOUIS JORDAN, Secretary 29 West 39th St., New York, N. Y. Executive Committee 1941 1942 E. A. ANDERSON FRANCES H. CLARK D. L. COLWELL W. L. FINK W. P. SYKES J. T. NORTON 1943ERIC R. JETTE LOUIS W. KEMPF GEORGE SACHS]

Jan 1, 1940

By C. M. Wayman, S. R. Rauze

It was recently reported' that the initial transformation in (100) iron whiskers grown in the bcc condition can be nucleated on heating in regions of the whisker which are not necessarily the hottest. Although this behavior was observed1 several times, its sporadic nature precluded any documentation other than occasional visual observations during hot-stage optical-microscope heating experiments. The purpose of this communication is to report how, in one instance, the a-y transformation in such a (100) iron whisker was initiated in a region which was clearly at a lower temperature than an adjacent region which did not transform at all.

Jan 1, 1967

By Arthur F. Taggart

The following conclusions on the work of the Hardinge mill are based on data furnished to the writer by the Hardinge Conical Mill Co. in the form of the mesh cards hereto appended. Energy units (E. U.) and relative mechanical efficiencies (R. M. E.) are computed by the "volume method" of Stadler.' Screen apertures used are the average apertures of testing screeps of the meshes given. i . Card 122. June 28, 1912. Vipond Porcupine Mines Co., Ltd., Schumacher, Ont., Canada. Ore from mill bin. Gangue, quartz and basalt. 4.5 ft. by 13 in. ball mill, Capacity, 48 tons per 24 hr. Charge, 4,000 lb. balls. Speed, 33 rev. per minute. Horsepower, 15 to 17. Water, 100 per cent. by weight. (50 per cent. ?) Product deslimed and oversise reground in pebble mill, see Card 113. Feed to mill through 2-in. mesh. Mesh Feed, Per Cent. Discharge, Per Cent.. + 1in. 5.50 ....... + 3/4. 28.00 + in. 30.00 ...... + 1/4in. 19.72 ....... + 10 10.87 2.10 + 20 2.42 8.00 -20 3.51 .....,. + 40 ....... 22.68 + 60 ...___ 10.50 4-80 ....... 11.80 + 100 ....... 3.90 -100 ....... 40.15

Jan 1, 1916

By O. P. Quist, S. H. Carpenter

The internal friction of single-crystal LiF has been investigated as a function of crystal orientation, while simultaneously applying a static compressive load. Three different crystal orientations were used, these being samples with the (100), (110), and (111) directions along the sample length. Results show the internal friction measured to be similar in appearance but different in magnitude for the (100) and (110) samples. With both orientations, application of a static stress caused an increase in the amplitude-independent damping, which recovered with time. The amplitude-dependent damping was found to first decrease with load up to the yield stress and then increase rapidly. Samples of the (111) orientation were found to have no measurable internal friction even when loaded up to 3.0 kg per sq mm. These results are discussed in terms of current theories of internal friction in ionic crystals. This paper presents the results of an investigation of the dislocation mobility and dislocation motion in high-purity single-crystal LiF at applied stress levels up to the yield stress. Internal friction measurements of the dislocation damping while simultaneously applying a static compressive load was the experimental technique used. LiF crystals much prefer to slip on the (110) set of slip planes. However, with a suitable stress distribution they can be forced to slip on the {100} set of slip planes.' For both sets of slip planes the slip direction is the same, namely (110). The object of this investigation was to try and learn more about the dynamical properties of dislocations on the different slip systems in LiF crystals. EXPERIMENTAL PROCEDURE Dislocation damping was measured, in terms of the log decrement, using a five-component marx2 composite piezoelectric oscillator. The apparatus used allows one to measure the dislocation damping while simultaneously applying a static compressive load on the sample. A schematic of the apparatus used is shown in Fig. 1 and a complete discussion of its construction and operation is given elsewhere.3 All measurements were made at room temperature with a longitudinal resonant frequency of approximately 50 kc per sec. Damping measurements were made using longitudinal vibrations with strain amplitudes from up to 10. Static loads up to 3.0 kg per sq mm were applied to the sample while the damping was being measured. Samples used in this investigation were high-purity single crystals of LiF purchased from the Harshaw Chemical Co. All samples were approximately of an in. square and were hand-ground in length to one-half wavelength to match the resonant frequency of the driver and gage quartz crystals. Samples of three different crystallographic orientations were used, namely, crystals with the (loo), (110), and (111) direction parallel to their length. The magnitude of the damping is a direct measure of the area on the slip planes swept out by dislocations during a complete oscillatory cycle. With a sample of the (100) orientation the maximum applied shear stress, due to longitudinal vibrations, is on the (110) slip planes with zero shear stress on the (100) slip planes. Thus, damping measured from a (100) sample is due entirely to dislocation motion taking place on the (110) set of slip planes. Similarly, for a sample of the (111) orientation there is zero shear stress on the (110) set of slip planes and the damping measured from a sample of this orientation is due entirely to dislocation motion on the (100) set of slip planes. Samples of the (110) orientation will have a component of shear stress on both sets of slip planes and

Jan 1, 1969

By M. E. Fine, A. A. Henderson

Investigation of the tensile properties of silver based aluminum alloy crystals was undertaken because it appeared attractive for studying strengthening effects due to Suzuki locking with minimum complication. Yield drops were observed in all alloy crystals (1, 2. 3. 4, and 6 at. pct Al) after strain aging at room temperature. No yield drops were found in similarly grown and tested silver crystals. The yield effects are attributed to Suzuki locking but the major portion of the solid solution strengthening to other mechanisms. INVESTIGATION of the tensile properties of single crystds of silver alloyed with aluminum was undertaken because it appeared to be a system in which segregation at stacking faults associated with partial dislocations1 would be the dominant factor in anchoring dislocations. First, silver and aluminum have closely similar atomic sizes and thus solute atom locking of a dislocation due to elastic interactions should be unimportant. Second, while both X-ray2 and thermodynamic3 investigations show short-range ordering in silver-based aluminum alloys, the degree of local order is quite small (X-ray measurements give v = EAB - 1/2(EAA + EBB) = - 0.025 ev and thermodynamic measurements give v r -0.007 ev) and should not be important in strengthening dilute alloys. Third, the stacking fault energy of silver is probably low (as indicated by the profusity of annealing twins) and is very likely diminished further and quite rapidly by aluminum additions since the A1-Ag phase diagram shows a stable hexagonal phase at only 25 at. pct Al. Also, a careful investigation in this laboratory4 has shown that the ratio of twin to normal grain boundaries in recrystallized alloys increases with aluminum content. Thus, with minimum complication from other factors, Ag-A1 alloys seem attractive for studying strengthening effects due to segregation at stacking faults of extended dislocations. EXPERIMENTAL METHOD Single crystals measuring 250 by 5 by 1.5 mm of pure Ag (99.99 pct) and Ag-A1 alloys (A1 of 99.999 pct purity) of nominal compositions* 1, 2, 3, 4, and 6 at. pct were grown in high-purity graphite molds from the melt under a dynamic vacuum (1 x l0-5 mm Hg). The technique consisted of moving a furnace having a hot zone (which melted about 0.5 cm of alloy) over a horizontal, evacuated quartz tube con- taining the mold and alloy at a rate of 3/8 in. per hr. Chemical analysis showed roughly the first inch of the crystal to be solute poor, the last inch solute rich; and the center section uniform in composition within the sensitivity of the analytical method (± 0.2 at. pct Al). The center section of the crystal was cut into five specimens. Gage lengths of reduced cross section, measuring from 1.5 to 2 cm in length, were mechanically introduced by means of jeweler&apos;s files and fine abrasive cloth with the crystal firmly held in polished steel guides. One-third of the cross section was then removed by etching and electro-polishing, the crystals were all subsequently annealed for several days at 850°C in a dynamic vacuum (<1 x 10-5 mm Hg) and furnace cooled to 200°C. The crystal orientations were determined using the usual back-reflection Laue technique. The Laue spots were sharp and of the same size as the incident beam. However, microscopic examination showed the crystals to contain substructures with subgrains of the order of a micron in diameter. The details of this substructure are presently under investigation. Tensile testing was done with a table model Instron using a cross-head speed of 0.002 in. per min. For testing at various temperatures the following media were used: 1) 415oK, hot ethylene glycol; 2) 296ºK, air, acetone, water; 3) 273ºK, ice water; 4) 258ºK, ethylene glycol "ice" in ethylene glycol; 5) 200°K, dry ice in acetone; 6) 77ºK, liquid nitrogen. EXPERIMENTAL RESULTS A) Yield Behavior—A portion of an interrupted stress-strain curve for a 6 at. pct A1 crystal of the indicated orientation tested at room temperature is shown in Fig. 1. Initially, at (a), there is a small, gradual yield drop of about 10 mg per sq mm2. However, on stopping the test, and aging for a few minutes at (b), a sharp yield drop is found. Aging for longer times at (c) and (dl results in larger yield drops (and larger AT&apos;S). At, defined in Fig. 1, is usually larger than the yield drop by about 20 pct; however, this increase in the lower yield is transient since extrapolations of the flow stress curves join as may be seen from Fig. 1. (Both Laue and low-angle scattering photographs revealed no evidence of precipitation in a strain-aged 6 at. pct A1 crystal.)

Jan 1, 1962

By A. W. H. Morris, G. H. Laurie, J. N. Pratt

Using- galvanic cells of the form Sn(liq)/Sn" (LiCl-KC1-SnCl,)/Sn-Ag (alloy), measurements have been made of relative thermodynamic properties of the a, C, E, and liquid phases of the Ag-Sn alloy system. Partial heats of solution of the components in the liquid alloys lzave also been observed by direct cal-orimetric measurement in an isoperibol calorimeter. The thermodynanzic quantities are disczlssed in relation to structural and other properties and the existence of anomalous minor fluctuations in the partial heats and entropies of solution in liquid alloys is tentatively suggested. In the course of a recent electro motive-force study of the thermodynamic properties of Sn-Ag-Pd liquids,&apos; some measurements were also performed on the Ag-Sn binary system. Most previous thermodynamic studies of this system have been concerned with the liquid state. Measurements confined to the limiting heat of solution of silver in liquid tin have been made by many calorimetric workers2 while high-temperature calorimetric measurements of the heats of formation of the full range of liquid alloys are reported in the early work of Kawakami~ (1323°K) and more recently by Wittig and Gehrin~(1248°K). Electromotive-force studies on liquid alloys have been made by Yanko, Drake, and Hovorka&apos; (606" to 686°K; 86 to 99.4 at. pct Sn) and by Frantik and Mc Donald&apos; (900°K; 30 to 90 at. pct Sn). The only known measurements on the solid state are of heats of formation of the a, £, and c phases; these values were obtained using tin-solution calorimetry, at 723"K, by Kleppa,~ whose investigation also yielded heats of formation of liquid alloys containing more than 64 at. pct Sn. The present experiments on the Ag-Sn alloys include a re-examination of the liquid phase and, because of the dearth of free-energy data for the solid state, attempted measurements on the a, c, and E phases. The principal new feature of electromotive-force results obtained for the liquid phase was an indication of anomalous fluctuations in the partial heats and entropies of solution of tin at certain compositions. However, since the values for these thermodynamic quantities were determined from the temperature coefficients of cell potentials, which are commonly subject to considerable error, confirmation by calorimetric measurements was considered desirable. A detailed investigation of the partial heats of solution of the components in the binary liquids was made using a liquid metal solution calorimeter. I) GALVANIC CELL STUDIES a) Experimental Details. Measurements were made, as a function of alloy composition and temperature, of the potentials of reversible galvanic cells of the form: ~n(liq)/~n++/~n-Ag (solid or liquid alloy) Details of the apparatus and experimental techniques have been given elsewhere.&apos; so that a brief account will suffice here. Molten salt, 58 mole pct LiC1-42 mole pct KC1, containing small amounts (1 to 2 mole pct) of stannous chloride was used as the electrolyte. The salts were dehydrated by pre-electrolysis and vacuum -drying techniques. Cells were established under an argon atmosphere by immersing tin and alloy electrodes in the molten salt contained in a large silica tube, heated in a vertical resistance furnace. The tube was sealed at the top by a head plate provided with openings permitting the simultaneous insertion of six electrodes, a central thermocouple sheath, and connections to vacuum and argon lines. Temperatures were controlled to *0.2"C over prolonged periods, with maximum variation over the electrodes at any time of 0.l°C. Temperatures were measured with a standardized Pt/13 pct Rh-Pt couple. The electromotive force of this and the cell potentials were measured on a Cambridge Vernier potentiometer and short-period galvanometer. Alloys were prepared from Pass "S" tin (99.999 pct) and Johnson-Matthey high-purity silver (99.999 pct) by melting in evacuated silica capsules and quenching in cold water. For liquid phase experiments, pieces of the resulting alloys were remelted into prepared silica electrode units, while solid electrodes were prepared by remelting into 3-mm bore tubing, inserting a cleaned molybdenum lead wire, and quenching to produce uniform rods about 3 cm in length, with soundly attached leads. In all cases remelting was done under an argon atmosphere. The solid electrodes were subsequently annealed in evacu ated silica tubes for 14 days at about 20°C below the solidus and quenched. Analyses showed that these techniques produced uniform electrodes with no significant change from weighed out compositions. b) Results and Discussion. Measurements were made on about forty alloys in the solid and liquid states, over varying ranges of temperature between 550" and 1050°K. Stable, mutually consistent, and reproducible electromotive-force data were obtained with most liquid alloys and these are shown in Fig. 1. Investigations were extended below the liquidus tem-

Jan 1, 1967

By Amitava Gangulee, Michael B. Bever

The order-disorder transition in Ag-Mg alloys in the range 17 to 26 at. pct Mg was investigated and some thermodynamic, electrical and mechanical properties of ordered Ag-Mg alloys were measured. A modification of the phase diagram is proposed on the basis of measured transition temperatures. The stability of the ordered structure is analyzed in terms of the quasichemical theory. Kinetic aspects of the order-disorder transition were also investigated. The energies of ordering at 273°K of Ag-Mg alloys were measured by liquid metal solution calorimetry. The electrical resistivities and the tensile Properties of the ordered alloys were measured. The exothermic energy of ordering increased with magnesium concentration up to the composition Ag3Mg; it is discussed in terms of the quasichemical theory. Pronounced order hardening was observed and can be explained by several strengthening mechanisms, which are particularly effective because of a change in crystal structure associated with the ordering transition. IN silver-rich solid solutions containing approximately 17 to 26 at. pct Mg, long- range ordering may occur during appropriate therma1 treatments. Clare-brough and Nicholas1 first detected such long-range order in the solid solution of composition Ag3Mg and suggested that the unit cell of the superlattice contained 256 atoms. x-ray2 and electron diffraction3 investigations confirmed the occurrence of long-range order, but indicated a shifted Ll2-type structure. On the basis of recent X-ray measurements the crystal structure of ordered Ag3Mg has been confirmed as type D023.4 The present paper is concerned with the order-disorder transition in silver-rich Ag-Mg solid solutions and some thermodynamic, electrical, and mechanical properties of the ordered alloys. The effects of short-range order on the properties of silver-rich solid solutions containing up to 26 at. pct Mg are discussed in a concurrent paper.5 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Specimens of Ag-Mg alloys containing from 18 to 26 at. pct Mg were prepared in the form of 1.0-mm-diam wires as described in Section 1.1 of Ref. 5. Disordered specimens were prepared by annealing at 773°K for 1 hr and quenching into iced brine. Ordered specimens were prepared by annealing at 773°K for 1 hr and slowly cooling to room temperature over a period of 15 days. The specimens were stored at 78°K. 1.2) Resistivity Measurements. Electrical resistivi- ties were measured by a potentiometric method.&apos; Equilibrium values were obtained at several temperatures. The kinetics of ordering were investigated by following the time-dependent changes of the resistivity of initially disordered specimens during annealing. The specimens were enclosed in copper capsules and immersed in salt pots; the heating up was accelerated by injecting preheated helium into the capsules. 1.3) Calorimetry. The energies of ordering of the alloys were measured in a tin solution calorimeter as the difference between the heat effects of additions of completely ordered and disordered specimens of the same composition. The procedure and the method of calculation have been described.6 Magnesium was used for thermal compensation in most calorimetric runs in order to improve the accuracy.677 1.4) Mechanical Tests. Tensile tests were carried out with wire specimens at room temperature as described in Section 1.5 of Ref. 5. Microhardness measurements were also made.? 2) RESULTS AND DISCUSSION The characteristics of the order-disorder transition of silver-rich Ag-Mg solid solutions will be discussed first. Some thermodynamic, electrical, and mechanical properties of the ordered alloys will then be considered and compared with the corresponding properties of dis-disordered alloys. 2.1) The Order-Disorder Transition. 2.1.1) Thermodynamic and Structural Aspects. The transition temperatures Tt were determined from discontinuities in the slope of the equilibrium resistivity vs temperature curves. Normalized curves for three compositions are shown in Fig. 1. The transition temperature increases with the magnesium concentration and reaches a maximum at the stoichiometric composition Ag3Mg. The transition temperature of the alloy Ag3Mg was measured as 665° ± 2°K and compares with published values of 660°,1 663°,8 and 66°k.3 In the slopes of the resistivity vs temperature curves of alloys containing 22.2 and 22.5 at. pct Mg, discontinuities were observed at two temperatures. Such upper and lower discontinuities indicate a two-phase field. A modified form of the published phase diagram9 is shown in Fig. 2. A two-phase field was found only on the low-magnesium side of the composition Ag3Mg. On the high-magnesium side, the existence of a two-phase field could not be established because of insufficient resolution, but such a field must be present. This part of the phase diagram can be made complete by a eutec-toid-type reaction a = (a&apos; + ß). The existence of a boundary between the two-phase fields (a + ß) and (a&apos; + ß) is also in accord with published lattice parameters.3 The crystal structure of ordered Ag3Mg (type Do23)

Jan 1, 1969

By M. Gell, G. R. Leveran

The high- and low-cycle fatigue properties of the nickel-base superalloy, Mar-MBOO, in columnar-grained and single-crystal forms were determined at room temperature. It was found that the fatigue lives of these materials were greatly affected by the size of preexisting cracks in MC-type carbides contained in the micro structure. Most of the data falls on two curves given by: (zN)&apos;/A€= K, where Nf is the number of cycles to failure, Af is the total strain range, and K is a function of carbide size. No difference was observed in the fatigue behavior of the columnar-grained and single-crystal materials for the same MC carbide size. Matrix slip and crack initiation occurred at precracked MC carbides and, to a lesser extent, at micropores. Fatigue crack propagation was mainly in the Stage I mode, i.e., on cry stallo graPhic slip planes. The Stage I fracture in these materials was unusual in that distinct features were observed on the fracture surfaces. In high-cycle fatigue, these features resembled those commonly observed on the cleavage fracture surfaces of bcc and hcp materials. Yet, in this study, the cracks propagated slowly in a cyclic manner. In low-cycle fatigue, the Stage I facets contained equiaxed dimples, similar to those observed on the tensile fracture surfaces of ductile materials. These observations indicate that both local normal and shear stresses are involved in these Stage I fractures. A model is proposed to explain these results based on the weakening of the cohesive energy of the active slip planes by reversed shear deformation and the fracture of the bonds across the weakened planes by the local normal stress. RECENT developments in casting technology have produced cast nickel-base superalloys in columnar -grained and single-crystal forms.1&apos;2 The tensile and creep properties of the nickel-base superalloy, Mar-M200, cast in these forms have been shown to be superior to the corresponding properties of the conventionally cast polycrystalline material.lp2 This improvement in properties results, in part, from the elimination of grain boundaries in the single crystals and the alignment of the grain boundaries parallel to the stress axis in the columnar-grained castings. As part of a program to evaluate the fatigue properties of nickel-base superalloys cast in single-crystal and columnar-grained forms, a study has been made of the cyclic deformation and fracture of Mar-M2OO at room temperature. M. fiFl I .hininr Mpmher AIMF ic ^pninr Rocoarrh Accn^iata anH I) EXPERIMENTAL PROCEDURE The composition range of Mar-Ma00 in weight percent is: 8 to 10 Cr, 9 to 11 Co, 11.5 to 13.5 W, 0.75 to 1.25 Cb, 1.75 to 2.25 Ti, 4.75 to 5.25 Al, 0.01 to 0.02 B, 0.03 to 0.08 Zr, 0.07 to 0.12 C, bal. Ni. All of the castings met the above specifications. The castings were solutionized for 1 to 4 hr at 2250°F followed by aging at 1600°F for 32 hr which resulted in a 0.2 pct offset yield stress of 150,000 psi at room temperature. The microstructure of the material consisted of cuboidal, coherent particles of ordered, fcc Ni3(A1,Ti) (commonly designated y&apos;), approximately 0.3 p on edge, distributed in an fcc y solid-solution matrix. MC carbides together with shrinkage and gas micropores were also distributed throughout the materials. The MC carbides and micropores were located preferentially in the interdendritic interstices, as well as in the grain boundaries in the columnar-grained castings. The (100) direction of all the single crystals and the common (100) axis of the grains in the columnar materials were aligned within about 5 deg of the specimen axis. Fatigue testing was carried out in the high-cycle (HCF) and low-cycle (LCF) fatigue regions, with the major difference being gross yielding of the specimen occurred during the first cycle in the LCF region. This division also corresponded with the more usual one in which the life of a specimen in LCF is less than lo4 cycles and that in HCF is greater than lo4 cycles. The designs of the high-cycle fatigue and low-cycle fatigue specimens are shown in Figs. l(a) and (c), respectively. The gage sections of both HCF and LCF specimens were electropolished prior to testing. The HCF specimens were tested in an MTS, closed-loop, hydraulic fatigue machine at 10 cps in air. The specimens were cycled between a tensile stress of 5000 psi and a maximum tensile stress which ranged from 35,000 to 125,000 psi, Fig. l(b). The LCF specimens were cycled under strain control from zero to a maximum tensile strain, Fig. l(d), in a Wiedemann-Baldwin testing machine. The experimental procedure has been described elsewhere.3&apos;4 Both HCF and LCF tests were interrupted periodically in order to replicate the development of slip and cracking at the specimen surface. This was accomplished by placing plastic replicating tape around the gage section of the specimen while the specimen was in the mahine. The size of the MC carbides for all specimens was measured on a polished longitudinal section through the gage section after fatigue testing. The method of measurement consisted of carefully scanning the entire polished section in order to locate the largest MC carbides. Photographs were then taken of the six longest carbides oriented approximately normal to the

Jan 1, 1969

By A. Kelly, S. Sato

Tensile tests have been performed on aluminum single crystals of 99.99 pct purity at 196°K. The resolved shear stress when the stress-strain curve becomes concave to the strain axis depends on orientation, being always higher for crystals with an initial orientation close to the sides of the unit triangle. Observations have been made, with the optical microscope, of the appearance of slip lines on polished surfaces of the crystals. Particular attention has been paid to the first appearance of cross-slip. It is confirmed that marked cross-slip is first seen when the stress-strain curve becomes concave to the strain axis. Measurements are reported of the lengths of the slip lines observed on top and side faces of the crystals at various stages of the deformation. The lengths of the slip lines vary inversely as the flow stress for all crystals, independent of crystal orientation. From measurements of the lengths and separations of the slip traces it is possible to estimate the number of dislocations which are annihilated at each cross-slip site. It is concluded that the annihilation of screw dislocations of opposite sign is the most important cross-slip process occurring. FRIEDEL1 recently pointed out that the stress-strain curve of many pure metals of face-centered-cubic structure can be considered as composed of three stages. Plastic flow commences with a region showing a small rate of hardening which is approximately linear. This has been called "easy glide*. It is followed by a region of more rapid hardening in which the slope of the curve is again approximately constant and this, in turn, is superseded by a final part of the curve which is concave to the strain axis. Following Diehl2 we may designate these regions as stages I, II, and III respectively. The onset of stage 111 occurs at lower stresses at higher temperatures. The appearance of the slip lines formed during these various stages has been described by a number of workers?-5* The object of the present work was to make detailed observations of the lengths and separations of slip lines for a number of crystals of different orientations deformed at the same temperature and strain rate. Although much previous work has been published on the deformation of aluminum single crystals the importance of measurements of these quantities has only recently been realized—they are essential for experimental tests of recent theories of work hardening.&apos; 9 In aluminum, deformed at room temperature, stage 11 of the stress-strain curve is very weakly marked, as the stress for the onset of stage 111 is attained soon after the end of easy glide. In the present experiments it was decided to use a temperature lower than room temperature so that stage II of the curve was better developed. However, at temperatures as low as 90°K slip lines are not measured easily with the optical microscope.5 For this reason 1960k was chosen as a suitable temperature. Even at 1960k however, stage III of the curve commences at glide strains of 6 to 10 pct and hence

Jan 1, 1960

By D. D. Pollock, D. I. Finch

PREVIOUS work&apos; on a four-component system (Cu-Mn-Ni-Fe) resulted in the development of consistent relationships between the chemical composition and the electrical properties of these manganin-type alloys. The present study was undertaken to develop alloys with temperature coefficients of resistivity and thermoelectric properties more desirable than those of the manganin type, and to determine whether the relationships which had been found for the Cu-Mn-Ni-Fe alloys could be extended to five-and six-component alloy systems. PREPARATION OF ALLOYS The five- and six-component alloys were made from OFHC copper rod, ARMCO iron, electrolytic nickel, manganese cathode chip, and special high-purity aluminum and indium. A Cu-Mg master was used for deoxidation. The compositions of these materials are given in Table I. The alloys were melted and cast as indicated previously,&apos; except that no cover was used and the melts were teemed. EXPERIMENTAL PROCEDURE The finished wire size of 0.0808 in. diam was again selected for the reason that the test specimens would be self-supporting, thus eliminating any extraneous effects which might have been introduced by winding smaller diameter wire on spools or forms. The following tests were performed on the finished wires: A) Chemical Analyses—All of the components of these alloys were determined by premium gravimetric methods. The principle residual impurity contained in these alloys is 0.008 pct Mg (by weight), maximum. Tables II and 111 present the mean analyses computed from at least four determinations of each constituent. B) Electrical Characteristics—The test procedures forthe determination of the thermal emf vs copper, resistivity, and the resistance-temperature relationship are given in detail in Ref. 1. It was also shown that the resistance-temperature relationship is of the form Pt = P,n + At -B/2, [1] where P, is the resistance at t C expressed in percent of a given standard resistance, P, is this per- 0 centage at 0°C, and A and B are constants for a given, properly treated, composition. The results of the electrical tests are also given in Tables II and 111. INTERPRETATION OF DATA The modified Linde2 formula, known to be valid for dilute binary solid solutions, was applied to the complex Cu-Mn-Ni-Fe type alloys. This relationship is of the form where Ap is the increase in resistivity. Zb the valence of the solute, Zn the valence of the solvent, and K and K are designations assigned by Robinson and Dorn3 to the constants for the periodic group to which solute element belongs. The units of K, are -cm per valence difference squared per at. pct; those of K2 are pa-cm per at. pct. For the sake of brevity, these units are not repeated in the following discussion. Calculations were made to determine if this formula was accurate for five-component systems. No experimental studies were made of the Cu-In and Cu-A1 binary systems. The effects of indium additions upon the resistivity of copper are given by Linde. These data, along with those of the effects of Mn and Fe, permitted the calculation of the effects of Al.

Jan 1, 1959

By Robert J. Hite, Samuel S. Adams

Potash, the generic term for a variety of potassium-bearing minerals, ores, and refined products (Table 1), owes its importance as an industrial mineral to the potassium requirement of growing plants. The term potash originally referred to potassium carbonate produced by the leaching of wood ashes. This process, for which the first US patent was issued in 1790, was the basis for the largest United States chemical industry in the early nineteenth century. The agricultural use of potash soon eclipsed the chemical applications following the German discovery in 1840 that potassium is essential to plant growth. The initial discoveries of large deposits of soluble potassium minerals, essential for agriculture applications, were made in 1857 in Germany and in 1914 in the United States. More than 90% of the 27.5 Mt K20 produced in the world in 1980 (Searls, 1981) was derived from marine evaporite deposits and approximately 90% was used in fertilizers. The potassium content of an ore, mineral, or product is customarily expressed as % K20, a unit of measure which is neither a natural nor synthetic compound of potassium (1.0% K is equivalent to 1.2046% K2O). Geology Potassium, the seventh most abundant element in the earth&apos;s crust, is present in silicate minerals in igneous, sedimentary and metamorphic rocks. Potassium is also a major constituent of many surface and subsurface brines (Table 2). Economic potash deposits are essentially restricted, however, to widespread, thick accumulations of marine chloride evaporite deposits. These deposits yield high grade, large tonnage ore bodies, many of which are amenable to low cost mining and beneficiation. The products from these deposits are, moreover, ideal for use in fertilizer because of the high relative solubility of the potassium chloride and sulfate evaporite minerals. World potash production and reserves for such deposits so vastly overshadow other sources of potassium that the following discussion will be limited largely to potash deposits in marine evaporites with brief reference to certain potash-rich brines. Approximately 85% of current domestic production is from bedded salt deposits and much of the balance is from brines. Marine evaporite deposits are accumulations of salt minerals deposited in structural sedimentary basins through the evaporation of seawater or mixtures of seawater and other brines. The salt minerals are precipitated in assemblages and sequences of assemblages as determined by the compositions of the brines and the solubility relations in the salt systems (D&apos;Ans, 1933). The evaporation of seawater normally yields carbonate minerals as the first precipitates (Table 3). Further evaporation and concentration of the brine leads to the precipitation, in succession, of sulfate, chloride, and supersaline mineral assemblages including the salts of potassium and magnesium. The common minerals, ores, and products of potassium deposits are listed in Table 1. Many potash deposits contain accessory evaporite minerals together with a variety of detrital and authigenic silicates (Braitsch, 1971). The structural basins within which marine evaporites occur are of two main types: (a) cratonic basins formed by broad epirogenic movements (for example, the Michigan Basin of the midwestern United States and the Permian Zechstein Basin of eastern Europe), and (b) grabens, commonly related to continental

Jan 1, 1983

By N. L. Hancox

Previous researchers have used the cutting and rejoining model to represent a porous body when attempting to place Archie&apos;s law on a theoretical basis and calculate rock permeabilities (F = Ø-m, where F = formation factor, = - porosity and m = a constant). In using the model, a porous solid is assumed to consist of sections with parallel sides containing straight. continuous pores of total porosity 4 (pore to total volume or, for a homogeneous body, pore to total area). The joining of pores at an interface between two sections is assumed to be random which results in a common pore area Ø2. This reduced area Ø2 is then taken as that area which limits electrical conduction or fluid flow in the body. Agreement between experimental results and results calculated using a model is not always good Because of this, various modifications of the model are presented — for instance, the random nature of the joining is questioned. Formation factor measurements on specially constructed porous specimens are described in this paper. it is concluded that the common pore area limits flow completely only if sections containing straight pores are very thin, and that, in most natural materials, the common pore area at an interface must be greater than that given by random joining. However, the model is still useful in permeability calculations, provided that the fractional area limiting flow is determined from formation factor measurements. INTRODUCTION Two important properties of porous media are permeability k, which describes the ease with which a fluid can flow through a porous medium, and formation factor F, defined as the ratio of the resistivity of a saturated specimen to the resistivity of the saturating liquid which describes the electrical properties of the saturated material. k is defined by Darcy&apos;s law,l k= µqL/P Ae . . . . . . . . . . . . . . . [1] where µ = liquid viscosity, q = flow rate, L = length of specimen, p = pressure across the specimen and = - the effective area over which flow occurs, F is given experimentally by Archie&apos;s law,2 F = Ø-m ,..............(2) where 4 is porosity defined as the pore to total volume or, for a homogeneous body, the pore to total area; and m lies between 1.3 for loose sand and 2 for cemented sand. Consider a porous body of total cross-sectional area A and length L, saturated with a liquid of resistivity R and with an effective area for conduction of Ae. Then, from the definition of F given previously, F=A/Ae , ................(3) or, from Eqs. 2 and 3, Ae = A Øm ..............(4) Thus, in any attempt to calculate k or F, some assumptions must be made concerning the pore structure of the body and a value derived for A,. To determine Ae, Childs and George3 and Wyllie and Gardner4 suggested an elementary statistical representation often referred to as the cutting and rejoining model of a porous body. The body is assumed to be composed of two or more parallel-sided sections of porosity 4, containing straight, continuous pores with a common pore area of Ø2 at an interface between two sections. The value is given by a random joining of the pores in either section. Two such sections,

Jan 1, 1969

By Bruce Chalmers, D. C. Larson

Aluminum crystals with longitudinal-axis orientations of (111) . (110), and (100) were deforined in tension and annealed. The conditions of deformation were controlled so that the re crystallization nuclei originated in either the heavily deformed regions at saw cuts {artificial nucleation) or in the lightly deformed matrix (spontaneous nucleation). The artificial-nucleatioln experiments showed that in lightly deformed (110) and (100) crystals low-angle twist boundaries are most mobile, while in (111> crystals and heavily deformed (110) and (100) crystals high-angle tilt boundaries with near (111) rotations are favored. The spontaneous-nucleation experiments showed the existence of preferred orientations in the (111) crystals. The nonrandomness of the grain orientations is quantitatively determined through a comparison with the results which would he obtained from a randowl set of grain ovientations. PREVIOUS recrystallization studies have been performed on single crystals deformed in tension.1 7 The crystals used in these studies usually had random tensile-axis orientations and the extent of deformation was not a primary consideration. The present study concerns the recrystallization of single crystals with tensile-axis orientations of (Ill), (110), and (100). The emphasis of this work is on the influence of the tensile-axis orientation and the degree of deformation on both the nucleation and growth processes. The multiple-slip orientations were chosen because secondary slip or slip intersection promotes nucleation.1,5,8 These crystals recrystallize at lower strains than the crystals which are oriented for single slip. Also, the greatest variation in deformation behavior is exhibited by the multiple-slip orientations. The stress-strain curves for crystals with tensile-axis orientations of (111) are higher than the stress-strain curves for poly-crystals, and the stress-strain curves for crystals with tensile-axis orientations of (100) are lower (at large strains) than the stress-strain curves for the crystals which deform initially in single slip.g The recrystallization nuclei originated in either 1) the homogeneously* deformed matrix of the crys- tals or 2) the heavily and inhomogeneously deformed regions at saw cuts. The nuclei will be referred to hereafter as spontaneous and artificial nuclei, respectively. The two terms do not imply a difference in the nature of the nuclei; they imply simply a difference in the mode of introduction of the nuclei. During spontaneous nucleation very few (always less than ten) grains nucleate, while during artificial nucleation large numbers of grains nucleate. Only a fraction of the artificially nucleated grains penetrate very far into the deformed matrix during annealing. The grains that penetrate the farthest into the deformed matrix will be referred to as the dominant grains. EXPERIMENTAL PROCEDURE The thirty-five crystals used in this investigation were grown from the melt in milled graphite boats at a rate of 1.6 cm per hr. The crystals had dimensions of approximately 6 by 12 by 80 or 6 by 6 by 80 mm and the aluminum was of 99.992 pet purity. The as-grown crystals were annealed at 610°C for 24 hr and furnace-cooled. They were then heavily etched and electropolished in a solution of five parts methanol to one part perchloric acid. The crystal orientations were obtained by back-reflection Laue photographs and were accurate to ±2 deg. The tensile-axis orientations were (loo), (110), and (111). Two of the side faces of the (111) crystals were (110) lanes. The (110) crystals had both {100) and {110) side faces and the (100) crystals had (100) side faces. The crystals were deformed at a strain rate of 0.003 per min. Shear stress and shear strain were obtained by multiplying and dividing the tensile stress and strain, respectively, by the Schmid factor, m. For the (111) crystals m = 0.272 and for the (110) and the (100) crystals m = 0.408. The Schmid factor is effectively constant during deformation for all orientations. The deformed crystals were sawed into 1-in.-long specimens while the crystals were totally enclosed in a graphite boat. The sawing was performed very carefully in order to limit the plastic deformation to the sawed regions. The specimens were electropolished in the solution mentioned above to remove the sawed-end deformation as well as controlled amounts of surface material. A special stainless-steel grip was used to hold the specimens during the electropolishing treatment. The gripping faces were flat, with no teeth, to prevent the introduction of extraneous de-

Jan 1, 1964

By David A. Thomas, John F. Peck

Sam Leber (General Electric Refractory Metals Laboratory)—I think that the authors should differentiate between the curved grains obtained by swaging and the crumpled grains produced by drawing. This can be seen most easily in the transverse sections of Fig. 2d, and is also apparent in Fig. 2c. This difference in structure indicates that the mode of deformation shou1d affect the texture, since the cylindrical texture should be maintained or even increased by the curved grains developed by swaging. Drawing, on the other hand, crumples the grains. This should convert the cylindrical texture into a normal fiber texture. This has been substantiated by a comparison of tungsten wires fabricated by similar drawing and swaging schedules. Although cylindrical textures have been detected in drawn iron wires, they were weak in comparison to tungsten wires which included swaging as part of the fabrication process. It should also be noted that large curved surfaces developed by swaging are concentric with the surface. The postulated (100) surface of these crystals would be confirmed by a (100) cylindrical texture, as was observed in tungsten. The preservalion of the (100) cylindrical texture by swaging would maintain the <100> direction in the radial position required for easy flow. This might provide a partial explanation for the decreased rate of work hardening observed in the swaged wire. J. F. Peck and D. A. Thomas (authors&apos; reply) — The authors appreciate Dr. Leber&apos;s comments on the differences in textures, microstructures, and properties of swaged and drawn wires. The evidence of the prominence and persistence of the cylindrical texture in swaged bee wires seems quite consistent with our microstructural observations and interpretations. We are presently engaged in further work to correlate the development of texture and micro-structure in drawn bee metals.

Jan 1, 1962

CONTENTS KANSAS-H. S. BRYANT 3 TEXAS, EXCEPT GULF COAST-M. C. CHENEY 14 GULF COAST-L. P. TEAS 21 TEXAS PANHANDLE-W. E. HUBBARD 29 LOUISIANA, ARKANSAS AND MISSISSIPPI L H. K. SHEARER 37 ROCKY MOUNTAINS-R. C. COFFIN 43 CALIFORNIA-V. H. WILHELM 51 MICHIGAN AND THE TRENTON FIELDS OF OHIO AND INDIANA-M. G. GULLEY 65 ILLINOIS, WESTERN KENTUCKY AND WESTERN INDIANA-A. H. BELL . . . 73

Jan 1, 1932

By AIME AIME

AN outstanding session of the Annual February Meeting was one held under the joint auspices of several groups on Tuesday afternoon, Feb. 22, as a symposium on the question of preserving peace in the postwar era through the control of the supply of sundry minerals vital to the Axis nations. D. H. McLaughlin and R. C. Allen were associate chairmen. And C.K. Leith led the discussion.

Jan 1, 1944

By David J. Reddish, Barry N. Whittaker

The characteristics of surface ground strains due to longwall mining are reviewed with special reference to U.K. coal mining observations. The current empirical method of estimating ground strain is discussed. A method of determining surface ground strain above a longwall extraction is described whereby strain can be accurately represented along a line in any direction. The discussion is supported with examples of its application to common subsidence engineering problems.

Jan 1, 1984

Alfred Noble Joint Prize Committee F B Foley, &apos;56 American Documentation Institute F B Foley, &apos;56 American Geological Institute J L Gillson, Nov &apos;56, H A Meyerhoff, Nov &apos;57 Committee on Government Relations J L Gillson, &apos;56 American Power Conference Paul R Nichols, &apos;56 American Standards Association Mining Standards Board E R Borcherdt, Jan &apos;58, Otto Herres, Jan &apos;58 Alternates E W Bullard, Dec &apos;56, and J K Richardson, Dec &apos;56

Jan 1, 1956

By N. Mungan, F. W. Smith, J. L. Thompson

Adsorption of polymers and transport, rheology and oil recovery efficiency of their solutions were studied in the laboratory to evaluate the use of polymers in waterflood-ing. While a tenfold mobility reduction was obtained with polymer concentrations as low as 0.05 per cent by weight, the mobility reduction depended on the type of polymer, molecular weight, salinity and pH of water, crude oil and capillary properties of the porous media. Choice of a suitable polymer and a workable concentration will have to be tailored for each application. Little reduction in the residual oil saturation can be expected from polymer flooding. Improvement in the volumetric sweep efficiency is possible hut the extent of the improvement can best be evaluated by properly designed field testing. Some aspects of the field use of polymer floods are discussed. INTRODUCTION Waterflooding is a simple, inexpensive secondary recovery method and is being used widely. Innumerable laboratory studies have been made to unravel the fundamentals of the displacement of oil by water and to find the ways of most efficient oil recovery. These studies and a great many field case histories have revealed that the prime cause of poor oil recovery is the inefficient and incomplete sweep of reservoir volume by the injected water. Sweep efficiency is affected by many factors of which the mobility ratio is an important one. Mobility ratio M is defined here as the ratio of water to oil mobilities: M = (k»/y,r)/(k,JJJJ........(1) In Eq. I, the permeabilities are the effective permeabilities and depend on fluid saturations and, hence, change during the different depletion stages in a flood. A wide practice is to use the effective water permeability at residual oil saturation and the effective oil permeability at interstitial water saturation in Eq. 1. If the mobility ratio is greater than one, the mobility ratio is unfavorable and water, being more mobile than oil, would finger through the oil zone resulting in poor oil recovery efficiency. If the mobility ratio is favorable (one or less) the displacement of oil by water occurs more or less in a pistonlike fashion. In some waterfloods. the mobility ratio is unfavorable and any additives by which the mobility of water can be decreased would favor more efficient oil recovery. The thing to bear in mind, however, is whether or not the improvement in oil recovery is sufficient to more than pay out the cost of the additives needed. For example, materials like sugars, alcohols and glycerine reduce water mobility by thickening the water, but the cost of material requirement precludes any field application. For an additive to be useful in water-flooding, it must bring about a large reduction in water mobility at low concentrations; it must be adsorbed only negligibly; and it must not completely plug up the formation. Some synthetic organic polymers have shown promise of meeting these requirements and have been used in the field.&apos;-W owever, no in-depth studies of the rheological, adsorption and oil displacement characteristics of polymer solutions have been reported. The present work is a study of these properties. EXPERIMENTAL In this work, concentrations are given on a weight per volume basis; 0.5 per cent concentration means 0.5 gm of polymer is dissolved in enough water (or NaCl solution) to make 100 ml. A bactericide, usually 0.1 to 0.2 per cent by volume of 38 per cent formaldehyde solution, was used in the polymer solutions. The NaCl solution was 30,000 ppm. Some properties of the polymers studied are given in Table I. Physical properties of all cores used are in Table 2. Flow behavior of polymer solutions was studied by three consecutive flow tests in cores. First, water (or brine) was injected at constant rate of about 1 ft/D to obtain the water mobility. Then, filtered polymer solution (prepared in water or brine) was flowed through the core. Since the rate was constant, increase in the pressure drop across the core reflects decrease in the mobility. Finally, the core was flooded with water (or brine) to study recovery of mobility. The Alundum cores which were used in

Jan 1, 1967